A Composition Containing A Polyolefin And A Stabilizer Mixture


Updated about 2 years ago

Abstract

A composition containingI) a polyolefin prepared by polymerization over a metallocene catalyst, and II) a stabilizer mixture comprising for examplewith n1 and n2 being a number from 2 to 25.

Information

Application ID 70/MAS/2000
Invention Field BIO-CHEMISTRY
Date of Application 2000-01-31
Publication Number 16/2007

Applicants

Name Address Country Nationality

Specification

The present invention relates to a composition containing a polyolefin prepared by polymerization over a metallocene catalyst, and a hindered amine light stabilizer system.
Hindered amine light stabilizer systems are described, for example, in US-A-4,863,981, US-A-5,719,217, EP-A-632,092, EP-A-741,163, EP-A-723,990, GB-A-2,267,499 and Research Disclosure 34,549 (January 1993). EP-A-814,127 discloses embrittlement-resistant polyolefin compositions. US-A-5,955,522 describes a process for the preparation of olefin polymers by polymerization over a transition metallocene catalyst with the addition of a sterically hindered amine.
In more detail, the present invention relates to a composition containing
I) a polyolefin prepared by polymerization over a metallocene catalyst, and
II) a stabilizer mixture comprising two different components-'&elected from the group of
components a), b) and c);


with A6 being hydrogen, Ci-C8alkyl, O-, -OH, -CH2CN, Ci-C18alkoxy, C5-Ci2cycloalkoxy, C3-C6alkenyl, C7-C9phenylalkyi unsubstituted or substituted on the phenyl by 1, 2 or 3 Ci-C4alkyl; or CrC8acyl,
A2 is C2-C18alkylene, C5-C7cycloalkylene or CrC4alkylenedi(C5-C7cycloalkylene), or
the radicals A1t A2 and A3, together with the nitrogen atoms to which they are attached, form
a 5- to 10-membered heterocyclic ring, or !
A4 and A5, together with the nitrogen atom to which they are attached, form a 5- to 10-membered heterocyclic ring, n! is a number from 2 to 50, and at least one of the radicals A1f A3, A* and A5 is a group of the formula (II);



in which A)4 is hydrogen, C1-C12 alkyl, C5-C12 cycloalkyl, C1-C4 alkyl-substituted C5-C12 cycloalkyl, phenyl, -OH- and/or C1-C10 alkyl-substituted phenyl, C7 -C9 phenylalkyl, C7-C9 phenylalkyl which is substituted on the phenyl radical by -OH and/or C1-C10 alkyl; or a group of the formula (II) as defined above, and
A15 has one of the meanings of A6;
with the provision that the group -N(A4)(A5) does not contain a cycloalkyl group when the stabilizer mixture comprises the two components a) and b).
Examples of alkyl having not more than 12 carbon atoms are methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, 2-ethylbutyl, n-pentyl, isopentyl, 1-methylpentyl, 1,3-di-methylbutyl, n-hexyl, 1-methylhexyl, n-heptyl, isoheptyl, 1,1,3,3-tetramethylbutyl, 1-methylheptyl, 3-methylheptyl, n-octyl, 2-ethylhexyl, 1,1,3-trimethylhexyl, 1,1,3,3-tetra-methylpentyl, nonyl, decyl, undecyl and dodecyl. A preferred meaning of A5 is Ci-Cg alkyl, e.g. C4-C8 alkyl. A preferred meaning of A6 and A15 is C1-C4 alkyl, in particular methyl. A preferred meaning of AI4 is C1-C4 alkyl, in particular butyl.
Examples of alkoxy containing not more than 18 carbon atoms are methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, pentoxy, isopentoxy, hexoxy, heptoxy, octoxy, decyloxy, dodecyloxy, tetradecyloxy, hexadecyloxy and octadecyloxy. C6-C12 Alkoxy, in particular heptoxy and octoxy, is one of the preferred meanings of A6 and A15.
Examples of C5-Q2 cycloalkyl are cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl and cyclododecyl. Cs-Cg cycloalkyl, especially cyclohexyl, is preferred.
C1-C4 alkyl-substituted C5-C12 cycloalkyl is for example methylcyclohexyl or dimethylcyclohexyl.

Examples of C5-C12cycloalkoxy are cyclopentoxy, cyclohexoxy, cycloheptoxy, cyclooctoxy, cyclodecyloxy, cyclododecyloxy and methylcyclohexoxy. C5-C8Cycloalkoxy, in particular cyclopentoxy and cyclohexoxy, is preferred.
Examples of C3-C6alkenyl are allyl, 2-methylallyl, butenyl and hexenyl. Alkenyls in which the carbon atom in the 1 -position is saturated are preferred, and allyl is particularly preferred.
Examples of CrCsacyl (aliphatic, cycloaliphatic or aromatic) are formyl, acetyl, propionyl, butyryl, pentanoyl, hexanoyl, heptanoyl, octanoyl and benzoyl. CrC8Alkanoyl and benzoyl are preferred. Acetyl is especially preferred.
-OH- and/or CrC10alkyl-substituted phenyl is for example methylphenyl, dimethylphenyl, trimethylphenyl, tert-butylphenyl or 3,5-di-tert-butyl-4-hydroxyphenyl.
Examples of C7-C9phenylalkyl are benzyl and phenylethyl.
C7-C9phenylalkyl which is substituted on the phenyl radical by -OH and/or by alkyl having up to 10 carbon atoms is, for example, methylbenzyl, dimethylbenzyl, trimethylbenzyl, tert-butylbenzyl or 3,5-di-tert-butyl-4-hydroxybenzyl.
Examples of alkylene containing not more than 18 carbon atoms are ethylene, propylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, octamethylene, decamethylene, dodecamethylene and octadecamethylene. A2 is for example C2-C8alkylene or C4-C8alkylene, in particular C2-C6alkylene, preferably hexamethylene. As is preferably ethylene and the radicals A10, An and Ai2 independently of one another are in particular C2-C4alkylene.
An example of C5-C7cycloalkylene is cyclohexylene.
Examples of C1-C4alkylenedi(C5-C7cycloalkylene) are cyclohexylene-methylene-cyclohexylene and cyclohexylene-isopropylidene-cyclohexylene.
Where the radicals A1f A2 and A3, together with the nitrogen atoms to which they are


Where the radicals A4 and A5, together with the nitrogen atom to which they are attached, form a 5- to 10-membered heterocyclic ring, the resulting ring is for example 1-pyrrolidyl, piperidino, morpholino, 1-piperazinyl, 4-methyM-piperazinyl, 1-hexahydroazepinyl, 5,5,7-trimethyl-1-homopiperazinyl or4,5,5,7-tetramethyl-1-homopiperazinyl. Morpholino is particularly preferred.
One of the preferred meanings of A4 is hydrogen, 2,2,6,6-tetramethyl-4-piperidyl or 1,2,2,6,6-pentamethyl-4-piperidyl.
Ai and A3 are preferably a group of the formula (II), in particular 2,2,6,6-tetramethyl-4-piperidyl or 1,2,2,6,6-pentamethyl-4-piperidyl.
A6 is preferably hydrogen, C1-C4alkyl, -OH, C6-C12alkoxy, C5-C8cycloalkoxy, allyl, benzyl or acetyl, in particular hydrogen or Ci-C4alkyl, e.g. hydrogen or methyl.
ni is preferably a number from 2 to 25.
n2 is preferably a number from 2 to 25, especially 2 to 20 or 2 to 10.
When the stabilizer mixture contains the two components a) and b), the group -N(A4)(A5) is preferably hydrogen, d-C^alkyl, a group of the formula (II) or morpholino.
When the stabilizer mixture contains the two components a) and b), the group -N(A4)(A5) is in particular


The compounds of components a), b) and c) are known and most of them are commercially available. The compounds of component a) can be prepared, for example, in analogy to the methods described in US-A-4,086,204, US-A-4,331,586 or EP-A-782,994. The compounds of component b) can be prepared, for example, in analogy to the method described in US-A-4,233,412. The compounds of component c) can be prepared, for example, in analogy to the method described in US-A-4,108,829.
Component a) is e.g. ®CHIMASSORB 944, ®CHIMASSORB 2020, ®CYASORB UV 3346 or ®DASTIB 1082, in particular ®CHIMASSORB 944, ®CHIMASSORB 2020 or®CYASORB UV 3346; component b) is preferably ®7fNUVIN 622; and component c) is preferably ®CHIMASSORB119.
When the stabilizer mixture contains the two components a) and b), component a) is different from ®DASTIB 1082.
The products disclosed in EP-A-782,994, which have a narrow molecular weight distribution with a well defined polydispersity Mw/Mn of 1.1 to 1.7 are also preferred as component a). EP-A-782,994 is equivalent to US Patent Application No. 08/756,225 filed on November 25, 1996, which is incorporated herein by reference.
A stabilizer mixture containing ®CHIMASSORB 944 and ®TINUVIN 622 is commercially available as ®TINUVIN 783 and a stabilizer mixture containing ®TINUVIN 622 and ®CHIMASSORB 119 is commercially available as ®TINUVIN 111. These mixtures are particularly preferred.
Further preferred embodiments relate to the following combinations of stabilizers:
1) the mixture of ®CHIMASSORB 944 and ®CHIMASSORB 119,
2) the mixture of ®CHIMASSORB 2020 and ®TINUVIN 622,

3) the mixture of ®CHIMASSORB 2020 and ®CHIMASSORB 119,
4) the mixture of ®CYASORB UV 3346 and ®TINUVIN 622,
5) the mixture of ®CYASORB UV 3346 and ®CHIMASSORB 119, and
6) the mixture of ®DASTIB 1082 and ®CHIMASSORB 119.
In general, the weight ratio of the two different components which form the Stabilizer mixture is 1:20 to 20:1, e.g 1:10 to 10:1, preferably 1:5 to 5:1, in particular 1:2 to 2:1.
The definition of the terminal groups which saturate the free valences in the compounds of the formulae (I) and (III) depend on the processes used for their preparation. The terminal groups can also be modified after the preparation of the compounds.

If X is halogen, it is advantageous to replace it, for example, by -OH or an amino group. Examples of amino groups which may be mentioned are pyrrolidin-1 -yl, morpholino, -NH2, -N(C1-C8alkyl)2 and -N(A)(CrC8alkyl) in which A is hydrogen or a group of the formula (II).
In the compounds of the formula (III), the terminal group bonded to the 2,2,6,6-tetramethyl-4-oxy-1-piperidyl radical is for example hydrogen or -CO-As-COOQ with Q being e.g. methyl,

ethyl or propyl, and the terminal group bonded to the diacyl radical is for example -OQ or a group

A preferred embodiment relates io a composition wherein "
AT, A3, A4 and A5 independently of one another are hydrogen, CVCaalkyl, C5-C8cycloalkyl,
methyl-substituted C5-C8cycloalkyl, phenyl, C7-C9phenylalkyl or a group of the formula (II), or
the radicals A4 and A5, together with the nitrogen atom to which they are attached, form a
6-membered heterocyclic ring,
A2 is C2-C10alkylene, and
rii is a number from 2 to 25;
A7 is hydrogen or methyl,
A8 is ethylene; and
n2 is a number from 2 to 25; and
A9 and A13 independently of one another are hydrogen or C1-C4alkyl,
A10, An and A12 independently of one another are C2-C6alkylene, and
A14 is hydrogen, CrC6alkyl, C5-C8cycloalkyl, methyl-substituted C5-C8cycloalkyl, phenyl,
C7-C9phenylalkyl or a group of the formula (II).
A particularly preferred embodiment relates to a composition wherein component a) is at least one compound of the formula (1-1), (I-2), (I-3) or (I-4);

Polyolefins prepared by polymerization over a metallocene catalyst, more detailed a transition metallocene catalyst, are commercially available. They are also known under the name "metallocene polyolefin". One example is ®Luflexen.
Catalyst systems based on a transition metallocene complex have made it possible to prepare either polymers with a particularly narrow molecular weight distribution or (co)polymers with a particular structure. These systems can be either homogeneous catalyst systems or supported catalysts. More details on the possible catalyst systems can be found, for example, in EP-A-563,917, EP-A-578,838, US-A-4,659,685, US-A-5,240,894 and WO-A-92/333.
Some representative explanations directed to metallocene catalysts and the polyolefins prepared by polymerization over those catalysts are given in the following.
The olefins which can be polymerized over a metallocene catalyst are in particular ethylene and oc-olefins, for example propylene, 1-butene, 4-methyl-1-pentene, 5-methyl-1-hexene, isohexene, isooctene, cycloolefins (cyclopentadiene (monomeric or dimeric) or norbornene) or styrene, and mixtures of olefins, for example ethylene-propylene or propylene mixed with minor amounts of higher oc-olefins. In this case preference is given to C2- or C3 olefins and their copolymers.
The transition metallocene catalysts are, for example, compounds of the formula (A)
{[(Ri)(R2M)a]an+an/q[LQm]q} (A)
in which a is 1 or 2 and n and q independently of one another are each an integer from 1 to 4, M is the cation of a monovalent to tetravalent metal from group IVb to Vllb, VIII or lb of the Periodic Table of the Elements, m is an integer corresponding to the valency of L + q, Q is a halogen atom, L is a divalent to heptavalent metal or nonmetal, R, is a rc-arene and R2 is a rc-arene or the anion of a rc-arene. Particularly suitable rc-arenes Ri and R2 are aromatic groups having 6 to 24 carbon atoms or heteroaromatic groups having 3 to 30 carbon atoms, it being possible for these groups to be substituted one or more times by identical or different monovalent radicals, such as halogen atoms, preferably chlorine or bromine atoms, or

CrCsalkyl, CVCsalkoxy, cyano, CrCsalkylthio, C2-C6monocarboxylic acid alkyl ester, phenyl, C2-C5alkanoyl or benzoyl groups. These rc-arene groups can be monocyclic, fused polycyclic or unfused polycyclic systems, where in the latter systems the rings can be linked directly or via bridging members such as -S- or -0-. R2 as the anion of a rc-arene can be an anion of a rc-arene of the abovementioned type, for example the indenyl anion and, in particular, the cyclopentadienyl anion, it being possible for these anions too to be substituted one or more times by identical or different monovalent radicals such as Ci-CBalkyl, C2-C6monocarboxylic acid alkyl ester, cyano, C2-C5alkanoyl or benzoyl groups.
The alkyl, alkoxy, alkylthio, monocarboxylic acid alkyl ester and alkanoyl substituents can be straight-chain or branched. Typical alkyl, alkoxy, alkylthio, monocarboxylic acid alkyl ester and alkanoyl substituents are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, n-pentyl, n-hexyl and n-octyl, methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, n-hexyloxy and n-octyloxy, methylthio, ethylthio, n-propylthio, isopropylthio, n-butylthio, n-pentylthio and a-bexylthio, carboxylic acid methyl, ethyl, n-propyl, isopropyl, n-butyl and n-pentyl ester, and acetyl, propionyl, butyryl and valeroyl. Among these, preference is given to alkyl, alkoxy, alkylthio and monocarboxylic acid alkyl ester groups having 1 to 4 carbon atoms, in particular 1 or 2 carbon atoms, in the alkyl moieties, and to alkanoyl groups having 2 or 3 carbon atoms. Preferred substituted rc-arenes or anions of substituted rc-arenes are those containing one or two of the abovementioned substituents, especially chlorine or bromine atoms, methyl, ethyl, methoxy, ethoxy, cyano, carboxylic acid methyl or ethyl ester groups and acetyl groups.
The n-arenes P^ and R2 can be identical or different. Suitable heteroaromatic rc-arenes are systems containing S, N and/or O atoms. Heteroaromatic rc-arenes containing S and/or O atoms are preferred.
Examples of suitable rc-arenes are benzene, toluene, xylenes, ethylbenzene, methoxybenzene, ethoxybenzene, dimethoxybenzene, p-chlorotoluene, chlorobenzene, bromobenzene, dichlorobenzene, acetylbenzene, trimethylbenzene, trimethoxybenzene, naphthalene, 1,2-dihydronaphthalene, 1,2,3,4-tetrahydronaphthalene, methylnaphthalenes, methoxynaphthalenes, ethoxynaphthalenes, chloronaphthalenes, bromonaphthalenes, biphenyl, indene, biphenylene, fluorene, phenanthrene, anthracene, 9,10-dihydroanthracene, triphenylene, pyrene, naphthacene, coronene, thiophene, chromene, xanthene,

thioxanthene, benzothiophene, naphthothiophene, thianthrene, diphenylene oxide, diphenylene sulfide, acridine and carbazole.
If a is 2, R2 is preferably in each case the anion of a rc-arene and M is in each case the same metal atom.
Examples of anions of substituted rc-arenes are the anions of methyl-, ethyl'-, n-propyl- and n-butylcyclopentadiene, the anions of dimethylcyclopentadiene, of cyclopentadienecarboxylic acid methyl and ethyl ester, and also of acetylcyclopentadiene, propionylcyclopentadiene, cyanocyclopentadiene and benzoylcyclopentadiene. Preferred anions are the anion of unsubstituted indene and, in particular, that of unsubstituted cyclopentadiene.
Preferably, a is 1, R2 is benzene, toluene, xylene, methoxybenzene, chlorobenzene, p-chlorotoluene, naphthalene, methylnaphthalene, chloronaphthalene, methoxynaphthalene, biphenyl, indene, pyrene or diphenylene sulfide and R2 is the anion of cyclopentadiene, acetylcyclopentadiene or indene or is benzene, toluene, xylene, trimethylbenzene, naphthalene or methylnaphthalene.
Particularly preferred complexes of the formula (A) are those in which a is 1, RT is r|6-pyrene or ri6-naphthalene and R2 is the anion of ri5-cyclopentadiene, n is preferably 1 or 2, in particular 1, and q is preferably 1. M is for example Ti2+, Ri3+, Ti4+, Zr+, Zr2+, Zr3+, Zr4+, Hf+, Hf2+, Hf3+, Hf4+, Nb+, Nb2+, Nb3+, Cr+, Mo+, Mo2\ W+, W2+, Mn\ Mn2+, Re+, Fe2+, Co2+, Co3+, Ni2+ or Cu2+. M is preferably a titanium, zirconium or hafnium cation, especially a titanium or zirconium cation, and with particular preference is Ti4+ or Zr4+.
Examples of suitable metals or nonmetals L are Sb, Fe, Sn, Bi, Al, Ga, In, Ti, Zr, Sc, V, Cr, Mn and Cu; lanthanides such as Ce, Pr and Nd or actinides such as Th, Pa, U or Np. Particularly suitable nonmetals are B, P and As. L is preferably P, As, B or Sb, with P being particularly preferred.
Complex anions [Lqm]q" are, for example, BF4", PF6\ AsF6", SbF6", FeCL,', SnCI6", SbCI6" and BiCI6". The particularly preferred complex anions are SbF6", BF4", AsF6" and PF6".
The compounds of the formula (A) can be prepared by methods known per se, for example by reacting a compound of the formula (B)

{[(Ri(R2M)a]an+an/q[X]q}

v-7;

with a salt of an anion
[LQmf
in which a, m, n, q, R^ R2, M and L are as defined under the formula (A) and [X]q' is an anion which is different from [LQm]q".
Both the compounds of the formula (B) and the compounds of the formula (C)
{[(R'i)(R2Ma]} (C)
in which a and M are as defined above and R', is a rc-arene or the anion of a rc-arene and R2 is an anion of a Tt-arene, can be prepared by reacting identical or different 7c-arenes in the presence of a Lewis acid with a salt of a metal from group IVb to Vllb, VIII or lb of the Periodic Table. The compounds of the formulae (A), (B) and (C) are also suitable for carrying out a ligand exchange, by reacting these compounds in the presence of a Lewis acid with a rc-arene which is different from Ri and/or R2, or RV In such cases, n is preferably 2 and particularly preferably 1.
Compounds of the formula (A) in which L is a metal can be prepared by reacting identical or different 7t-arenes in the presence of a Lewis acid with a suitable salt of a metal from group IVb to Vllb, VIII or lb of the Periodic Table of the Elements, for example a titanium, zirconium, chromium, manganese or, in particular, iron salt. Finally, compounds of the formula (A) can also be converted in a customary manner, by anion exchange, into complexes of the formula (A) with a different anion [LQm]q".
In a preferred embodiment the starting materials employed are uncharged 7t-complexes of the formula (C), for example ferrocene or bis(rj5-indenyl)iron(ll), and these starting materials are converted by ligand exchange into a complex of the formula (B), which is subsequently reacted with a salt of an anion [LQm]q\ The complex of the formula (B) obtained as intermediate in this procedure is normally not isolated.

Examples of suitable salts of anions [LQm]q" are alkali metal, alkaline earth metal or ammonium salts. It is preferred to use alkali metal salts, and particularly preferably sodium salts and potassium salts.
Examples of suitable Lewis acids for the reactions described above are Aldl3, AIBr3, BF3, SnCI4 and TiCI4, preferably AICI3. It can be advantageous to carry out the ligand exchange reaction with the addition of a reducing agent, for example aluminium or magnesium, to the reaction mixture, or to add a reducing agent, for example Na2S03 or ascorbic acid, to the reaction mixture subsequently. Aluminium is the preferred reducing agent. The ligand exchange reactions are expediently carried out in an inert organic solvent. Examples of suitable solvents are aliphatic or cycloaliphatic hydrocarbons such as octane, nonane, decane and cyclohexane. If desired, an excess of rc-arene can also be employed as solvent.
The reaction of the compounds of the formula (B) with a salt of an anion [LQm]q" and the anion exchange conversion of compounds of the formula (A) are expediently carried out in an aqueous or aqueous alcoholic medium, for example in mixtures of water and methanol or ethanol. The salts of the anions [LQm]q" are employed at least in stoichiometric amounts but preferably in excess.
For the polymerization, it is additionally possible to use a metallocene catalyst consisting of two principal components (A-1 and A-2).
Of these, component A-1 is a metallocene compound. It is possible in principle to employ any metallocene regardless of its structure and composition. The metallocenes can be either bridged or unbridged, and can have identical or different ligands. The compounds involved are those of the metals of groups IVb, Vb or Vlb of the Periodic Table, for example compounds of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten, preferably of zirconium, hafnium and titanium, especially zirconium.
Such metallocenes are known and are described, for example, in the following documents: EP-A-336,127, EP-A-336,128, EP-A-387,690, EP-A-387,691, EP-A-302,424, EP-A-129,368, EP-A-320,762, EP-A-284,707, EP-A-316,155, EP-A-351,392, US-A-5,017,714, J. Organomet, Chem., 342 (1988) 21.

Metallocenes worthy of emphasis are those of the general structure

in which
Mm+ is an m-valent cation of a metal of groups IVb, V or Vlb of the Periodic Table, for example titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum or tungsten, preferably zirconium, hafnium or titanium, especially zirconium; (C5H5.XRX) is a cyclopentadienyl ring substituted with from zero to five substituents R; x is zero, one, two, three, four or five; n is one or two;
each R, independently of the others, is a C1-C20 hydrocarbon radical, a CrC^o hydrocarbon radical substituted by one or more halogen atoms, a metalloid-substituted CrC2o hydrocarbon radical or halogen; or two adjacent radicals R are a C4-C20 ring; or, if n is 1, alternatively a radical By-JR'z.|.y, in which
J is an element of group Va of the Periodic Table of coordination number 3 or an element of group Via of the Periodic Table of coordination number 2, preferably N, P, O or S; each R', independently of the others, is a CrC20 hydrocarbon radical or a CrC20 hydro¬carbon radical which is substituted by one or more halogen atoms; z is the coordination number of the element J; y is zero or one;
B, if y is one, is a bridging member comprising an element of group IVA or VA of the Periodic Table, for example CrC20alkylene, a DiCrC20alkyl-, C7-C20alkylaryl- or DiC6-C20arylsilicon or germanium radical or an alkyl- or aryl-phosphine or amine radical; or R, if n is two, is a group selected from -M2(R10)(Ru)-, -M2(Rio)(Rn)-M2(R10)(Rii)--C(Rio)(Rii)-C(R10)(Rii)-, -O-M2(R10)(Rn)-O-, -C(R10)(Ri,)-, -O-M2(R10)(R,i)-, -C(R10)(R,i)-M2(Rio)(Rn), -B(R10)-, -AI(R10)-, -Ge-, -Sn-, -0-, -S-, -S(O)-, -S(0)2-, -N(R10)-, -C(O)-, -P(R10)-or -P(O)(R10)-; in which
R10 and Rn are identical or different and are a hydrogen atom, a halogen atom, a CrCioalkyl, CrC^fluoroalkyl, C6-C10aryl, C6-C10fluoroaryl, CrC10alkoxy, C2-C10alkenyl,

C7-C4oarylalkyl, C8-C40arylalkenyl or C7-C40alkylaryl group or R10and Rn, in each case with
the atoms which join them, form a ring, and
M2 is silicon, germanium or tin,
each Q, independently of the others, is hydrogen, a CrC50 hydrocarbon radical, a CrC50
hydrocarbon radical which is substituted with one or more electron-withdrawing groups, for
example halogen or alkoxy, or a metalloid-substituted CrCso hydrocarbon radical, the
metalloid being an element of group IVA of the Periodic Table, with the exception of
hydrocarbon radicals of the formula (C5H5.XRX); or two radicals Q are alkylidene, olefin,
acetylene or a cyclometallated hydrocarbon radical;
L is a neutral Lewis base, for example diethyl ether, tetrahydrofuran, dimethylaniline, aniline,
trimethylphosphine or n-butylamine; and
w is from 0 to 3.
The term metalloid refers, for example, to the elements silicon, germanium, tin and lead.

Further details on metallocenes of the above type can also be found in WO-A-92/333.
For the isospecific polymerization of substituted olefins, for example propene, butene and styrene, and their copolymerization, including that with other olefins, the metallocenes which are of interest, especially zirconocenes, are those which carry indenyl derivatives as ligands. These are preferably the compounds of the following formula (1)


in which
Mi is a metal of group IVb, Vb or Vlb of the Periodic Table;
RT and R2 are identical or different and are a hydrogen atom, a d-C^alky!, d-doalkoxy,
C6-C10aryl, C6-C10aryloxy, C2-C10alkenyl, C7-C40arylalkyl, C7-C40alkylaryl, C8-C40arylalkenyl or
OH group or a halogen atom, and the radicals R3 are identical or different and are a
hydrogen atom, a halogen atom, a d-doalkyl group which can be halogenated, a C6-C10aryl
group, or a radical -NR2, -SR, -OSiR3, -SiR3 or PR2, in which R is a halogen atom, a
Ci-C10alkyl group or a C6-C10aryl group.
R4 to R8 are as defined for R3, or adjacent radicals R4 to R8 form, with the atoms connecting
them, an aromatic or aliphatic ring,
R9 is a group selected from -M2(R10)(Rn)-, -M2(R10)(Rii)-M2(R10)(R11)-, -C(R10)(Ru)-
C(R,o)(Rn)-, -O-M2(R10)(Rn)-O-, -C(R10)(R„)-, -O-M2(R10)(Rn)-, -C(R10)(Rii)-M2(R10)(R,i)-,
-B(R10)-, -AI(Rio)-, -Ge-, -Sn-. -0-, -S-, -S(O)-, -S(0)2-, -N(R10)-, -C(O)-, -P(R10)- or
-P(O)(R10)-; in which
R10 and Rt1 are identical or different and are a hydrogen atom, a halogen atom, a
Ci-C10alkyl, d-dofluoroalkyl, C6-C10aryl, C6-C10fluoroaryl, Crdoalkoxy, C2-C10alkenyl,
C7-C40arylalkyl, C8-C40arylalkenyl or C7-C40alkylaryl group or R10 and R11t in each case with
the atoms connecting them, form a ring, and
M2 is silicon, germanium or tin.

The 4,5,6,7-tetrahydroindenyl analogues corresponding to the compounds of the formula (1) are also of importance.
Preferably, in formula (1),
Mi is zirconium,
Ri and R2 are identical and are methyl or chlorine, especially chlorine,
R3 to R8 are hydrogen or CrC4alkyl,
R9 is -Si(R10)(Rn)-, -C(R10)(Rn)- or -C(R10)(Rii)-C(R10)(Rii)- and
R10 and Rn are identical or different and are CrC4alkyl or C6-C10aryl. In particular, R10 and
Rn are identical or different and are methyl or phenyl.
The indenyl and/or tetrahydroindenyl ligands in formula (1) are preferably substituted in the 2, 2,4, 4,7, 2,6, 2,4,6, 2,5,6, 2,4,5,6 or 2,4,5,6,7 positions, in particular in the 2,4,6 positions. The substituents are preferably a CrC4alkyl group such as methyl, ethyl or isopropyl. The 2 position is preferably substituted by methyl.
Also of particular importance are those compounds of the formula (1) in which the sub¬stituents in positions 4 and 5 of the indenyl radicals (R5 and R6) form, together with the atoms connecting them, a benzene ring. This fused ring system can likewise be substituted by radicals having the definitions of R3-R8. An example of such compounds I is dimethylsilanediylbis(2-methyl-4,5-benzoindenyl)zirconium dichloride.
The metallocenes of the formula (1) are particularly suitable for the preparation of high molecular weight polyolefins of high stereoregularity.
Also of particular importance are compounds of the formula (1) with (substituted) phenyl or naphthyl substituted in position 4.
For the syndiospecific polymerization of substituted olefins, for example propene, butene and styrene, and their copolymerization, including that with other olefins, the metallocenes of interest are those of the formula (2):

in which
MT is a metal of group IVb, Vb or Vlb of the Periodic Table;
Rt and R2 are identical or different and are a hydrogen atom, a CrCi0alkyl, CrC10alkoxy,
C6-C10aryl, C6-Ci0aryloxy, C2-C10alkenyl, C7-C40arylalkyl, C7-C40alkylaryl, C8-C40arylalkenyl or
OH group or a halogen atom, and the radicals R3 are identical or different and are a
hydrogen atom, a halogen atom, a d-C10alkyl group which can be halogenated, a C6-C10aryl
group, or a radical -NR2, -SR, -OSiR3, -SiR3 or PR2, in which R is a halogen atom, a
CrC10alkyl group or a C6-C10aryl group.
R4 to R8 are as defined for R3, or adjacent radicals R4 to R8 form, with the atoms connecting
them, an aromatic or aliphatic ring,
R9 is a group selected from -M2(R10)(Rn)-, -M2(R10)(Rii)-M2(R10)(Rii)-, -C(R10)(Rn)-
C(R,o)(Rii)-, -O-M2(R10)(Rn)-O-, -C(R10)(Rn)-, -O-M2(R10)(R„)-, -C(Rio)(Rii)-M2(R10)(Rn)-,
-B(R10)-, -AI(R10)-, -Ge-, -Sn-, -0-, -S-, -S(O)-, -S(0)2-, -N(R10)-, -C(O)-, -P(R10)- or
-P(O)(R10)-; in which
R10 and Rn are identical or different and are a hydrogen atom, a halogen atom, a
d-C^alkyl, Crdofluoroalkyl, C6-C10aryl, C6-C10fluoroaryl, d-d0alkoxy, C2-C10alkenyl,
d-C40arylalkyl, C8-doarylalkenyl or d-doalkylaryl group or R10 and Rn, in each case with
the atoms connecting them, form a ring, and
M2 is silicon, germanium or tin; and
R12 to R17 are as defined for R3.

Examples of metallocenes which can be used for the polymerization are the following compounds:
biscyclopentadienylzirconium dichloride, biscyclopentadienylzirconiumdimethyl, biscyclopentadienylzirconiumdiphenyl, biscyclopentadienylzirconiumdibenzyl, biscyclopentadienylzirconiumbistrimethylsilyl, bis(methylcyclopentadienyl)zifconium dichloride, bis(1,2-dimethylcyclopentadienyl)zirconium dichloride, bis(1,3-dimethyl-cyclopentadienyl)zirconium dichloride, bis(1,2,4-trimethylcyclopentadienyl)zirconium dichloride, bis(1,2,3-trimethylcyclopentadienyl)zirconium dichloride, bis(pentamethyl-cyclopentadienyl)zirconium dichloride, bisindenylzirconium dichloride, bis(tetrahydro-indenyl)zirconium dichloride, dimethylsilylbis-1-tetrahydroindenylzirconium dichloride, dimethylsilylbis-1 -(2-methyltetrahydroindenyl)zirconium dichloride, dimethylsilylbis-1 -(2,3,5-trimethylcyclopentadienyl)zirconium dichloride, dimethylsilylbis-1 -(2,4-dimethyl-cyclopentadienyl)zirconium dichloride, dimethylsilylbis-1-indenylzirconium dichloride, dimethylsilylbis-1 -indenylzirconiumdimethyl, dimethylgermylbis-1 -indenylzirconium dichloride, dimethylsilylbis-1 -(2-methylindenyl)zirconium dichloride, dimethylsilylbis-1 -(2-methyl-4-isopropylindenyl)zirconium dichloride, phenylmethylsilylbis-1 -(2-methylindenyl)-zirconium dichloride, dimethylsilylbis-1-(2-methyl-4-ethylindenyl)zirconium dichloride, ethylenebis-1-(4,7-dimethylindenyl)zirconium dichloride, phenyl(methyl)silylbis-1 -indenyl-zirconium dichloride, phenyl(vinyl)silylbis-1-indenylzirconium dichloride, diphenylsilylbis-1-indenylzirconium dichloride, dimethylsilylbis(1 -(2-methyl-4-tert-butylindenyl))zirconium dichloride, methylphenylsilylbis(1 -(2-methyl-4-isopropylindenyl))zirconium dichloride, dimethylsilylbis(1 -(2-ethyl-4-methylindenyl))zirconium dichloride, dimethylsilylbis(1 -(2,4-dimethylindenyl))zirconium dichloride, dimethylsilylbis(1-(2-methyl-4-ethylindenyl))-zirconium dichloride, dimethylsilylbis(2-methyl-4,6-diisopropylindenyl)zirconium di-chloride, dimethylsilylbis(2,4,6-trimethylindenyl)zirconium dichloride, methylphenylsilyl-bis(2-methyl-4,6-diisopropylindenyl)zirconium dichloride, 1,2-ethanediylbis(2-methyl-4,6-diisopropylindenyl)zirconium dichloride, dimethylsilyl(9-fluorenyl)(cyclopentadienyl)-zir-conium dichloride, diphenylsilyl(9-fluorenyl)(cyclopentadienyl)zirconium dichloride, diphenylmethylene(9-fluorenyl)cyclopentadienylzirconium dichloride, isopropylidene(9-fluorenyl)cyclopentadienylzirconium dichloride, phenylmethylmethylene(9-fluorenyl)-cyclopentadienylzirconium dichloride, isopropylidene(9-fluorenyl)(1 -(3-isopropyl)cyclo-pentadienyl)zirconium dichloride, isopropylidene(9-fluorenyl)(1-(3-methyl)cyclopenta-dienyl)zirconium dichloride, diphenylmethylene(9-fluorenyl)(1 -(3-methyl)cyclopenta-

dienyl)zirconium dichloride, methylphenylmethylene(9-fluorenyl)(1-(3-methyl)cyclopenta-
dienyl)zirconium dichloride, dimethylsilyl(9-fluorenyl)-(1 -(3-methyl)cyclopentadienyl)-
zirconium dichloride, diphenylsilyl(9-fluorenyl)-(1 -(3-methyl)cyclopentadienyl)zirconium
dichloride, diphenylmethylene(9-fluorenyl)(1-(3-tert-butyl)cyclopentadienyl)zirconium
dichloride and isopropylidene(9-fluorenyl)(1 -(3-tert-butyl)cyclopentadienyl)zirconium
dichloride. '
In the preparation of the catalyst, chiral metallocenes are preferably employed as a racemate. However, it is also possible to use the pure R or S form. Using these pure stereoisomeric forms, optically active polymer can be prepared. However, the meso form of the metallocenes should be separated off, since the polymerization-active centre (the metal atom) in these compounds is no longer chiral, owing to mirror symmetry at the central metal, and is therefore unable to produce highly tactic polymer. If the meso form is not separated off, atactic polymer is produced in addition to isotactic or syndiotactic polymers. For certain applications, for example flexible mouldings, or for the preparation of polyethylene grades, this may be entirely desirable. The stereoisomers are separated by methods known from the literature.


for the cyclic type, in which formulae (3) and (4) the radicals R can be identical or different and are a CrCealkyl group, a C6-C18aryl group, benzyl or hydrogen, and p is an integer from 2 to 50, preferably from 10 to 35.
The radicals R are preferably identical and are methyl, isobutyl, n-butyl, phenyl or benzyl, particularly preferably methyl.
Where the radicals R are different, they are preferably methyl and hydrogen, methyl and isobutyl or methyl and n-butyl, with the content of hydrogen or isobutyl or n-butyl preferably being 0.01-40 % (number of radicals R).
The aluminoxane can be prepared by known methods in various ways. One of the methods, for example, is the reaction of an aluminium hydrocarbon compound and/or a hydridoaluminium-hydrocarbon compound with water (in gaseous, solid or liquid form or else in bound form, for example as water of crystallization) in an inert solvent (for example toluene). To prepare an aluminoxane with different alkyl groups R, two different aluminium trialkyls (AIR3 + AIR'3), in accordance with the desired composition and reactivity, are reacted with water (cf. S. Pasynkiewicz, Polyhedron 9 (1990) 429 and EP-A-302,424).
The precise structure of the aluminoxanes of the formulae (3) and (4) is unknown.
Regardless of the manner of their preparation, all aluminoxane solutions share the feature of a varying content of unreacted aluminium starting compound, which is present in free form or as an adduct.
b) Ion exchange compounds
Ion exchange compounds are compounds comprising a cation, which reacts irreversibly with a ligand of component A-1, and a noncoordinating anion, which is bulky, labile and chemically inert. Combining components A-1 and A-2 produces an ion pair formed from the cation of A-2 and a ligand of A-1. Examples of cations of component A-2 are Bransted acids, such as ammonium ions, or reducible Lewis acids, such as Ag+ or ferrocene ions.
The aluminoxane which can be used as component A-2 can also be produced in the course of the preparation of a supported catalyst from trimethylaluminium.

In addition to homogeneous catalyst systems, the metallocenes can also be used as heterogeneous catalysts. In this case the catalyst is applied to an inorganic or organic carrier by methods known to the person skilled in the art from the literature. Inorganic carrier materials are preferably silica gels; further details on this can be found, for example, in US-A-5,240,894.
Examples of organic carrier materials are microporous polymeric carriers which are obtainable commercially (e.g. the ®Accurel grades from AKZO, such as ®Accurel-PE, ®Accurel-PP, ®Accurel-PA-6 or ®Accurel-PA-12 with a voids content of about 75 % by volume). The pore size of the ®Accurel materials is 0.5-5 \im (PP), 1.0-5 |xm (HDPE), or 0.5-3^m(PA-6andPA-12).
The microporous polymeric carrier is advantageously dried beforehand, for example by treatment with aluminium alkyl solutions, then washed and rendered inert under a protective gas.
The preferred procedure for this is first to react the aluminoxane in an appropriate solvent, for example pentane, hexane, heptane, toluene or dichloromethane, with at least one metallocene, by intensive mixing, for example by stirring. The reaction temperature is preferably from -20 to +120°C, in particular 15-40°C. The molar ratio of aluminium to transition metal M of the metallocene is preferably between 10:1 and 10,000:1, in particular between 100:1 and 2000:1. The reaction time is in general between 5 and 120 minutes, preferably 10-30 minutes. The reaction is preferably operated with an aluminium concentration of more than 0.01 mol/litre, in particular more than 0.5 mol/litre. The reaction is carried out under inert conditions.
In place of the aluminoxane it is also possible to use a mixture of an aluminoxane with a further aluminium alkyl compound, for example trimethyl-, triethyl- or triisobutylaluminium, for the described reaction with the metallocene.
After the reaction has taken place it is possible, for example, to remove part of the solvent under vacuum or, following concentration, to replace the solvent by a different solvent. The solution thus prepared is reacted in a suitable manner with the microporous polymeric

carrier. In this context, the carrier is added at least in an amount whose total pore volume is able to take up the solution from the previous reaction. The reaction referred to in the second sentence of this paragraph is preferably carried out at temperatures of between -20 and +20°C, in particular 15-40°C, by intense mixing, for example by stirring or treatment with ultrasound. Thorough homogenization should be accomplished. In this context, the exchange of the inert gas of the pore volume can be accelerated by brief evacuation, for example.
In principle, the supported catalyst can also be prepared in a one-pot reaction, i.e. all three starting components are reacted with one another simultaneously in an appropriate solvent/suspension medium. In this context, the amount of the polymeric carrier should preferably be calculated such that it is able to take up the entire volume of liquid.
The catalyst can be metered into the polymerization system in suspended form, in an inert suspension medium such as, for example, heptane, n-decane, hexane or diesel oil, or else in dry form, possibly after removal of the remaining solvent by a drying step carried out, for example, under vacuum.
The catalyst can advantageously be prepolymerized in the gaseous phase, in the liquid monomer or in suspension in which case it is possible to omit the addition of a further organoaluminium compound.
Polymerization with these catalysts can be carried out by known methods in liquid or gaseous phase. The liquid phase may, for example, be an aliphatic hydrocarbon or the liquid monomer itself. The metallocene catalysts can also be employed as a mixture with other types of catalyst, for example Ziegler or Phillips catalysts. At the end of the polymerization the catalyst is destroyed, for example by adding water (vapour), wet nitrogen, carbon dioxide or alcohol.
Metallocene polyolefins are further described in "New Trends in Polyolefin Catalysts and Influence on Polymer Stability" (Rolf Mulhaupt; the Twelfth Annual International Conference on Advances in the Stabilization and Controlled Degradation of Polymers, held in Luzern, Switzerland, 21-23 May 1990, pages 181 to 196 of the conference papers).

According to a preferred embodiment of the present invention the polyolefin prepared by polymerization over a metallocene catalyst is polyethylene or polypropylene.
A further preferred embodiment of the present invention relates to a composition which additionally contains a polyolefin not prepared by polymerization over a metallocene catalyst.
Such polyolefins are for example prepared
a) by radical polymerization (normally under high pressure and at elevated
temperature); or
b) by catalytic polymerization over a Phillips
or Ziegler (-Natta) catalyst.
Low density polyethylene (LDPE; prepared by radical polymerization), linear low density polyethylene (LLDPE; prepared by catalytic polymerization over a Ziegler (-Natta) catalyst) and high density polyethylene (HDPE; prepared by catalytic polymerization over a Phillips catalyst) are particularly preferred.
The weight ratio between the polyolefin prepared by polymerization over a metallocene catalyst to the polyolefin not prepared by polymerization over a metallocene catalyst is for example 1:10 to 10:1.
A further embodiment of this invention is a method for stabilizing a polyolefin prepared by polymerization over a metallocene catalyst, which comprises incorporating into said polyolefin a stabilizer mixture as defined above.
The two components of the stabilizer mixture can be used in various proportions depending on the nature of the polyolefin to be stabilized, on the end use and on the presence of other additives.
In general, it is appropriate to use, for example, 0.01 to 5 % by weight of each of the two components of the stabilizer mixture, relative to the weight of the polyolefin to be stabilized, preferably 0.01 to 2 %, in particular 0.025 to 1 %.

The stabilizer mixture or the individual components can be incorporated into the polyolefin by known methods, for example by dry mixing in the form of powder, or wet mixing in the form of solutions or suspensions or also in the form of a masterbatch which contains the individual components in a concentration of 2.5 to 25 % by weight; in such operations, the polyolefin can be used in the form of powder, granules, solutions, suspensions or eveVi in the form of latices.
The stabilizer mixture or the individual components can be added before, during or after the polymerization or crosslinking. Furthermore, they can be incorporated in the polyolefin in the pure form or encapsulated in waxes, oils or polymers.
Before incorporation, the individual components of the stabilizer mixture can also be mixed with one another in a melt or can be extruded with one another.
The polyolefin stabilized with the stabilzer mixture can be used for the production of mouldings, films, tapes, monofilaments, fibres, surface coatings and the like.
If desired, other conventional additives for polyolefins, such as antioxidants, UV absorbers, nickel stabilizers, pigments, fillers, plasticizers, corrosion inhibitors and metal deactivators, can be added to the polyolefin containing the stabilizer mixture described above.
Examples of such conventional additives are listed in the following.
1. Antioxidants
1.1. Alkylated monophenols, for example 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-di-methylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-bu-tyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(a-methylcyclohexyl)-4,6-dimethyl-phenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-tert-butyl-4-meth-oxymethylphenol, nonylphenols which are linear or branched in the side chains, for example, 2,6-di-nonyl-4-methylphenol, 2,4-dimethyl-6-(1 '-methylundec-1 '-yl)phenol, 2,4-dimethyl-6-(1 '-methylheptadec-1'-yl)phenol, 2,4-dimethyl-6-(1'-methyltridec-1'-yl)phenol and mixtures there¬of.

1.2. Alkylthiomethylphenols, for example 2,4-dioctylthiomethyl-6-tert-butylphenol, 2,4-dioctyl-thiomethyl-6-methylphenol, 2,4-dioctylthiomethyl-6-ethylphenol, 2,6-di-dodecylthiomethyl-4-nonylphenol.
1.3. Hydroquinones and alkylated hydroquinones, for example 2,6-di-tert-butyl-4-methoxy-phenol, 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octade-cyloxyphenol, 2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-bu-tyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyphenyl stearate, bis-(3,5-di-tert-butyl-4-hy-droxyphenyl) adipate.
1.4. Tocopherols, for example a-tocopherol, p-tocopherol, y-tocopherol, 8-tocopherol and mixtures thereof (Vitamin E).
1.5. Hydroxyiated thiodiphenvl ethers, for example 2,2'-thiobis(6-tert-butyl-4-methylphenol), 2,2'-thiobis(4-octylphenol), 4,4'-thiobis(6-tert-butyl-3-methylphenol), 4,4'-thiobis(6-tert-butyl-2-methylphenol), 4,4'-thiobis-(3,6-di-sec-amylphenol), 4,4'-bis(2,6-dimethyl-4-hydroxyphe-nyl)disulfide.
1.6. Alkylidenebisphenols. for example 2,2'-methylenebis(6-tert-butyl-4-methylphenol), 2,2'-methylenebis(6-tert-butyl-4-ethylphenol), 2,2'-methylenebis[4-methyl-6-(oc-methylcyclohexyl)-phenol], 2,2'-methylenebis(4-methyl-6-cyclohexylphenol), 2,2'-methylenebis(6-nonyl-4-me-thylphenol), 2,2'-methylenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(4,6-di-tert-butylphe-nol), 2,2'-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis[6-(a-methylbenzyl)-4-nonylphenol], 2,2'-methylenebis[6-(a,a-dimethylbenzyl)-4-nonylphenol], 4,4'-methylenebis-(2,6-di-tert-butylphenol), 4,4'-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methyl-phenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydr-oxy-2-methyl-phenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3'-tert-butyl-4'-hydroxyphenyl)butyrate], bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadiene, bis[2-(3'-tert-butyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate, 1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis-(3,5-di-tert-butyl-4-hydroxyphenyl)propane, 2,2-bis-(5-tert-butyl-4-hydroxy2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1,5,5-tetra-(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane.

1.7. 0-, N- and S-benzvl compounds, for example 3,5,3',5'-tetra-tert-butyl-4,4'-dihydroxydi-benzyl ether, octadecyl-4-hydroxy-3,5-dimethylbenzylmercaptoacetate, tridecyl-4-hydroxy-3,5-di-tert-butylbenzylmercaptoacetate, tris(3,5-di-tert-butyl-4-hydroxybenzyl)amine, bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithioterephthalate, bis(3,5-di-tert-butyl-4-hydroxy-benzyl)sulfide, isooctyl-3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate. '
1.8. Hydroxvbenzvlated malonates, for example dioctadecyl-2,2-bis-(3,5-di-tert-butyl-2-hy-droxybenzyl)-malonate, di-octadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)-malonate, di-dodecylmercaptoethyl-2,2-bis-(3,5-di-tert-butyl-4-hydroxybenzyl)malonate, bis[4-(1,1,3,3-te-tramethylbutyl)phenyl]-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate.
1.9. Aromatic hvdroxvbenzyl compounds, for example 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxy-benzyl)-2,4,6-trimethylbenzene, 1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetrame-thylbenzene, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol.

1.10. Triazine Compounds, for example 2,4-bis(octylmercapto)-6-(3,5-di-tert-butyl-4-hydroxy-anilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-tri-azine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,3,5-triazine, 2,4,6-tris-(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine, 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxyben-zyl)isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate, 2,4,6-tris-(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1,3,5-triazine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxy-phenylpropionyl)-hexahydro-1,3,5-triazine, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl)iso-cyan urate.
1.11. Benzvlphosphonates, for example dimethyl-2,5-di-tert-butyl-4-hydroxybenzylphospho-nate, diethyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl3,5-di-tert-butyl-4-hy-droxybenzylphosphonate, dioctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, the calcium salt of the monoethyl ester of 3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid.
1.12. Acylaminophenols, for example 4-hydroxylauranilide, 4-hydroxystearanilide, octyl N-(3,5-di-tert-butyl-4-hydroxyphenyl)carbamate.

1.13. Esters of (H3,5-di-tert-butvl-4-hvdroxyphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethy¬lene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl) isocyanurate, N,N'-bis(hy-droxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylol-propane, 4-hydroxymethyl-1 -phospha-2,6,7-trioxabicyclo[2.2.2]octane.
1.14. Esters of (H5-tert-butvl-4-hvdroxv-3-methvlphenyl)propionic acid with mono- or poly¬hydric alcohols, e.g. with methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanedi¬ol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl) isocyanurate, N,N'-bis-(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethyl-olpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.
1.15. Esters of fH3,5-dicvclohexvl-4-hvdroxyphenvl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, tri¬ethylene glycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)ox-amide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hy-droxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.
1.16. Esters of 3.5-di-tert-butvl-4-hydroxvphenvl acetic acid with mono- or polyhydric alco¬hols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)ox-amide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hy-droxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.
1.17. Amides of B-(3,5-di-tert-butvl-4-hvdroxvphenyl)propionic acid e.g. N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxy-phenylpropionyl)trimethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazide, N,N'-bis[2-(3-[3,5-di-tert-butyl-4-hydroxyphenyl]propionyloxy)ethyl]oxamide (Nau-gard®XL-1 supplied by Uniroyal).

1.18. Ascorbic acid (vitamin C)
1.19. Aminic antioxidants, for example N,N'-di-isopropyl-p-phenylenediamine, N,N'-di-sec-bu-tyl-p-phenylenediamine, N,N'-bis(1,4-dimethylpentyl)-p-phenylenediamine, N,N'-bis(1 -ethyl-3-methylpentyl)-p-phenylenediamine, N,N'-bis(1 -methylheptyl)-p-phenylenediamine, N,N'-dicy-clohexyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-'bis(2-naphthyl)-p-phenylenediamine, N-isopropyl-N'-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N'-phe-nyl-p-phenylenediamine, N-(1 -methylheptyl)-N'-phenyl-p-phenylenediamine, N-cyclohexyl-N'-phenyl-p-phenlenediamine, 4-(p-toluenesulfamoyl)diphenylamine, N,N'-dimethyl-N,N'-di-sec-butyl-p-phenylenediamine, diphenylamine, N-allyldiphenylamine, 4-isopropoxydiphenylamine, N-phenyl-1 -naphthylamine, N-(4-tert-octylphenyl)-1 -naphthylamine, N-phenyl-2-naphthyl-amine, octylated diphenylamine, for example p,p'-di-tert-octyldiphenylamine, 4-n-butylamino-phenol, 4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylaminophenol, 4-octa-decanoylaminophenol, bis(4-methoxyphenyl)amine, 2,6-di-tert-butyl-4-dimethylaminomethyl-phenol, 2,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, N,N,N',N'-tetramethyl-4,4'-diaminodiphenylmethane, 1,2-bis[(2-methylphenyl)amino]ethane, 1,2-bis(phenylamino)-propane, (o-tolyl)biguanide, bis[4-(1',3'-dimethylbutyl)phenyl]amine, tert-octylated N-phenyl-1-naphthylamine, a mixture of mono- and dialkylated tert-butyl/tert-octyldiphenylamines, a mixture of mono- and dialkylated nonyldiphenylamines, a mixture of mono- and dialkylated dodecyldiphenylamines, a mixture of mono- and dialkylated isopropyl/isohexyldiphenyl-amines, a mixture of mono- und dialkylated tert-butyldiphenylamines, 2,3-dihydro-3,3-di-methyl-4H-1,4-benzothiazine, phenothiazine, a mixture of mono- und dialkylated tert-butyl/-tert-octylphenothiazines, a mixture of mono- und dialkylated tert-octyl-phenothiazines, N-allylphenothiazin, N,N,N',N'-tetraphenyl-1,4-diaminobut-2-ene, N,N-bis(2,2,6,6-tetramethyl-piperid-4-yl-hexamethylenediamine, bis(2,2,6,6-tetramethylpiperid-4-yl)sebacate, 2,2,6,6-tetramethylpiperidin-4-one, 2,2,6,6-tetramethylpiperidin-4-ol.
2. UV absorbers and light stabilisers
2.1. 2-(2'-Hvdroxvphenvl)benzotriazoles, for example 2-(2'-hydroxy-5'-methylphenyl)-benzo-triazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(5'-tert-butyl-2'-hydroxyphe-nyl)benzotriazole, 2-(2'-hydroxy-5'-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl- 2'-hydroxy-5'-methylphe-nyl)-5-chloro-benzotriazole, 2-(3'-sec-butyl-5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'-

hydroxy-4'-octyloxyphenyl)benzotriazole, 2-(3',5'-di-tert-amyl-2'-hydroxyphenyl)benzotriazole,
2-(3',5'-bis-(a,a-dimethylbenzyl)-2'-hydroxyphenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-
5'-(2-octyloxycarbonylethyl)phenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyl-
oxy)-carbonylethyl]-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-
methoxycarbonylethyl)phenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-meth-
oxycarbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2ioctyloxycarbonyl-
ethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)carbonylethyl]-2'-hydroxy-phenyl)benzotriazole, 2-(3'-dodecyl-2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-isooctyloxycarbonylethyl)phenylbenzotriazole, 2,2'-methylene-bis[4-(1,1,3,3-tetramethylbutyl)-6-benzotriazole-2-ylphenol]; the transesterification product of 2-[3'-tert-bu-tyl-5'-(2-methoxycarbonylethyl)-2'-hydroxyphenyl]-2H-benzotriazole with polyethylene glycol
300; [R-CH2CH—COO-CH2CH2-^- where R = 3'-tert-butyl-4'-hydroxy-5'-2H-benzotri-
azol-2-ylphenyl, 2-[2'-hydroxy-3'-(a,a-dimethylbenzyl)-5'-(1,1,3,3-tetramethylbutyl)-phenyl]-benzotriazole; 2-[2'-hydroxyr3i:(.1,1,3,3-tetramethylbutyl)-5'-(a,a-dimethylbenzyl)-phenyl]ben-zotriazole.
2.2. 2-Hydroxybenzophenones, for example the 4-hydroxy, 4-methoxy, 4-octyloxy, 4-decyl-oxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy and 2'-hydroxy-4,4'-dimethoxy derivatives.
2.3. Esters of substituted and unsubstituted benzoic acids, as for example 4-tertbutyl-phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoyl resorcinol, bis(4-tert-butylben-zoyl) resorcinol, benzoyl resorcinol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzo-ate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert-butyl-4-hydroxyben-zoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate.
2.4. Acrvlates, for example ethyl a-cyano-P,p-diphenylacrylate, isooctyl a-cyano-p,(3-diphe-nylacrylate, methyl a-carbomethoxycinnamate, methyl a-cyano-p-methyl-p-methoxy-cinna-mate, butyl a-cyano-p-methyl-p-methoxy-cinnamate, methyl cc-carbomethoxy-p-methoxycin-namate and N-(p-carbomethoxy-p-cyanovinyl)-2-methylindoline.
2.5. Nickel compounds, for example nickel complexes of 2,2'-thio-bis-[4-(1,1,3,3-tetramethyl-butyl)phenol], such as the 1:1 or 1:2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldithiocarbamate,

nickel salts of the monoalkyl esters, e.g. the methyl or ethyl ester, of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphe-nyl undecylketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxypyrazole, with or with¬out additional ligands.
2.6. Oxamides. for example 4,4'-dioctyloxyoxanilide, 2,2'-diethoxyoxanilicfe, 2,2'-dioctyloxy-5,5'-di-tert-butoxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butoxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2'-ethoxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butoxanilide, mixtures of o- and p-methoxy-disubstituted oxanilides and mixtures of o- and p-ethoxy-disubstituted oxanilides.
2.7. 2-(2-HvdroxvphenvO-1,3.5-triazines. for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2,4-bis(2-hydroxy-4-propyl-oxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxy-propoxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-octyloxy-propyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxy-phenyl]-4,6-bis(2,4-dimethylphenyl)-
1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxy-propoxy)phenyl]-4,6-bis(2,4-dimethyl-phenyl)-1,3,5-triazine, 2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1,3,5-triazine, 2-(2-hy-droxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine, 2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hy-droxy-propoxy)phenyl]-1,3,5-triazine, 2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine, 2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine.
3. Metal deactivators, for example N,N'-diphenyloxamide, N-salicylal-N'-salicyloyl hydrazine, N,N'-bis(salicyloyl) hydrazine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl) hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyl dihydrazide, oxanilide, isophthaloyi dihydrazide, sebacoyl bisphenylhydrazide, N,N'-diacetyladipoyl dihydrazide, N,N'-bis(salicyl-oyl)oxalyl dihydrazide, N,N'-bis(salicyloyl)thiopropionyl dihydrazide.

4. Phosphites and phosphonites, for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phos¬phite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)-pentaerythritol diphosphite, diisodecyloxypentaerythritol diphos¬phite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis(2?,4,6-tris(tert-butyl-phenyl)pentaerythritol diphosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butyl-phenyl) 4,4'-biphenylene diphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenz-[d,g]-1,3,2-dioxaphosphocin, bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite, 6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-di-benz[d,g]-1,3,2-dioxaphosphocin, 2)2',2"-nitrilo[triethyltris(3,3',5,5'-tetra-tert-butyl-1,1 '-biphe-nyl-2,2'-diyl)phosphite], 2-ethylhexyl(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2,2'-diyl)phosphite, 5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane.



5, Hydroxvlamines. for example, N,N-dibenzylhydroxylamine, N.N-diethylhydroxylamine,
N,N-dioctylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine, N,N-
dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine, N-hexadecyl-N-octadecylhydrox-
ylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamine derived from
hydrogenated tallow amine.
6. Nitrones, for example, N-benzyl-alpha-phenyl-nitrone, N-ethyl-alpha-methyl-nitrone, N-oc-
tyl-alpha-heptyl-nitrone, N-lauryl-alpha-undecyl-nitrone, N-tetradecyl-alpha-tridcyl-nitrone, N-

hexadecyl-alpha-pentadecyl-nitrone, N-octadecyl-alpha-heptadecyl-nitrone, N-hexadecyl-al-pha-heptadecyl-nitrone, N-ocatadecyl-alpha-pentadecyl-nitrone, N-heptadecyl-alpha-hepta-decyl-nitrone, N-octadecyl-alpha-hexadecyl-nitrone, nitrone derived from N,N-dialkylhydroxyl-amine derived from hydrogenated tallow amine.
7. Thiosvnergists, for example, dilauryl thiodipropionate or distearyl thiodiprbpionate.
8. Peroxide scavengers, for example esters of (3-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercaptobenzimidazole or the zinc salt of 2-mercapto-benzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis(p-dodecylmercapto)propionate.
9. Polvamide stabilisers, for example, copper salts in combination with iodides and/or phos¬phorus compounds and salts of divalent manganese.

10. Basic co-stabilisers, for example, melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids for example calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ricinoleate and potassium palmitate, antimony pyrocatecholate or zink pyrocatecholate.
11. Nucleating agents, for example, inorganic substances such as talcum, metal oxides such as titanium dioxide or magnesium oxide, phosphates, carbonates or sulfates of, preferably, alkaline earth metals; organic compounds such as mono- or polycarboxylic acids and the salts thereof, e.g. 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid, sodium succinate or sodium benzoate; polymeric compounds such as ionic copolymers (ionomers). Especially preferred are 1,3:2,4-bis(3',4'-dimethylbenzylidene)sorbitol, 1,3:2,4-di(paramethyldibenzyli-dene)sorbitol, und 1,3:2,4-di(benzylidene)sorbitol.
12. Fillers and reinforcing agents, for example, calcium carbonate, silicates, glass fibres, glass bulbs, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, car¬bon black, graphite, wood flour and flours or fibers of other natural products, synthetic fibers.

13. Other additives, for example, plasticisers, lubricants, emulsifiers, pigments, rheology additives, catalysts, flow-control agents, optical brighteners, flameproofing agents, antistatic agents and blowing agents.
14. Benzofuranones and indolinones, for example those disclosed in U.S. 4,325,863; U.S. 4,338,244; U.S. 5,175,312; U.S. 5,216,052; U.S. 5,252,643; DE-A-43t6611; DE-A-4316622; DE-A-4316876; EP-A-0589839 or EP-A-0591102 or 3-[4-(2-acetoxyethoxy)-phenyl]-5,7-di-tert-butyl-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phe-nyl]benzofuran-2-one, 3,3'-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one], 5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphe-nyl)-5,7-di-tert-butyl-benzofuran-2-one, 3-(3,5-dimethyl-4-pivaloyloxyphenyi)-5,7-di-tert-butyl-benzofuran-2-one, 3-(3,4-dimethylphenyl)-5,7-di-tert-butyl-benzofuran-2-one, 3-(2,3-di-methylphenyl)-5,7-di-tert-butyl-benzofuran-2-one.
The weight ratio of the stabilizer mixture to the conventional additives can be for example 1:0.5 to 1:5.
The examples below illustrate the invention in greater detail. All percentages or parts are by weight, unless stated otherwise.



EXAMPLE 1: Light stabilization of metailocene polyethylene films.
100 parts of unstabilized metailocene polyethylene powder (density: 0.903 g/cm3,

10 % butene comonomer, melt flow index -5.0 g/10 minutes at 190°C and 2160 g) are homogenized at 180°C for 10 minutes in a Brabender plastograph with 0.02 parts of octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, 0.08 parts of tris(2,4-di-tert-butylphenyl) phospite, 0.1 part of Ca stearate and the amount of the light stabilizer system indicated in Tables 1 and 2. The material thus obtained is compression molded in a laboratory press between two aluminum foils for 6 minutes at 170°C to a 0.2 mm thick film which is quenched immediately in cold water. Samples of 60 mm x 25 mm are cut out of these 0.2 mm films and are exposed in a ®WEATHER-OMETER Ci 65 (black panel temperature 63 ± 2°C, without water-spraying). Periodically, these samples are removed from the exposure apparatus and their carbonyl content is measured with an infrared spectrophotometer.
The exposure time (T01) corresponding to the formation of a carbonyl absorbance of 0.1 is a measure for the stabilizing efficiency of the light stabilizer system. The values obtained are summarized in the following Tables 1 and 2.

EXAMPLE 2: Light stabilization of metallocene polypropylene films.
100 parts of unstabilized metallocene polypropylene powder (melt flow index
-20 g/10 minutes at 230°C and 2160 g) are homogenized at 200°C for 10 minutes in a
Brabender plastograph with 0.05 parts of pentaerythrityl-tetrakis{3-(3,5-di-tert-butyl-4-
hydroxyphenyl) propionate}, 0.1 part of tris(2,4-di-tert-butylphenyl) phosphite, 0.1 part of Ca

stearate and the amount of the light stabilizer system indicated in Table 3. The material thus
obtained is compression molded in a laboratory press between two aluminum foils for
6 minutes at 260°C to a 0.5 mm thick film which is cooled immediately to room temperature
in a water-cooled press. Samples of 60 mm x 25 mm are cut out of these 0.5 mm films and
are exposed in a ®WEATHER-OMETER Ci 65 (black panel temperature 63 ± 2°C, without
water-spraying). '
Periodically, these samples are removed from the exposure apparatus and their carbonyl content is measured with an infrared spectrophotometer.
The exposure time (T02) corresponding to the formation of a carbonyl absorbance of 0.2 is a measure for the stabilizing efficiency of the light stabilizer system. The values obtained are summarized in the following Table 3.

WE CLAIM:
1. A composition containing
I) a polyolefin prepared by polymerization over a metallocene catalyst, and
II) a stabilizer mixture comprising two different components selected from the group
of components a), b) and c);
component a) is at least one compound of the formula (I)

wherein
A], A3, A4 and A5 independently of one another are hydrogen, C1-C12 alkyl, C5-C12 cycloalkyl, C1-C4 alkyl-substituted C5-C12 cycloalkyl, phenyl, -OH- and/or CpCio alkyl-substituted phenyl, C7-C9 phenylalkyl, C7-C9 phenylalkyl which is substituted on the phenyl radical by -OH and/or CpCio alkyl; or a group of the formula (II),
HI)
with A6 being hydrogen, C1-Cg alkyl, O, -OH, -CH2CN, C|-C,8 alkoxy, Q-Cu cycloalkoxy, C3-C6 alkenyl, C7-C9 phenylalkyl unsubstituted or substituted on the phenyl by 1, 2 or 3 C1-C4 alkyl; dt C-Cg acyl,
A2 is C2-C18 alkylene, C5-C7 cycloalkylene or C1-C4 alkylenedi(C5-C7 cycloalkylene), or the radicals Ai, A2 and A3, together with the nitrogen atoms to which they are attached, form a 5- to 10-membered heterocyclic ring, or
A4 and A5, together with the nitrogen atom to which they are attached, form a 5- to 10-membered heterocyclic ring.

cycloalkyl, phenyl, -OH- and/or C|-Cio alkyl-substituted phenyl, C7-C9 phenylalkyl, C^
C9 phenylalkyl which is substituted on the phenyl radical by -OH and/or CpCio alkyl; or a
group of the formula (II) as defined above, and
Ai5 has one of the meanings of Ag;
with the provision that the group -N(A4)(A5) does not contain a cycloalkyl group when
the stabilizer mixture comprises the two components a) and b).
2. The composition according to claim 1 wherein As and A15 independently of one another are hydrogen or C1-C4 alkyl.
3. The composition according to claim 1 wherein Ai, A3, A4 and A5 independently of one another are hydrogen, CpCg alkyl, Cs-Cg cycloalkyl, methyl-substituted Cs-Cg cycloalkyl, phenyl, C7-C9 phenylalkyl or a group of the formula (II), or the radicals A4 and A5, together with the nitrogen atom to which they are attached, form a 6-membered heterocyclic ring,
A2 is C2-C10 alkylene, and
Ui is a number from 2 to 25;
Ay is hydrogen or methyl,
Ag is ethylene; and
n2 is a number from 2 to 25; and
A9 and A]3 independently of one another are hydrogen or C1-C4 alkyl,
Aio, All is and A12 independently of one another are C2-C6 alkylene, and
Ai4 is hydrogen, CpCg alkyl, Cj-Cg cycloalkyl, methyl-substituted Cj-Cg cycloalkyl,
phenyl, C7-C9 phenylalkyl or a group of the formula (II).


5. The composition according to claim 1 wherein the two different components of the stabilizer mixture are the components a) and b).
6. The composition according to claim 1 wherein the two different components of the stabilizer mixture are the components a) and c).
7. The composition according to claim 1 wherein the two different components of the stabilizer mixture are the components b) and c).


with Til being a number from 2 to 25.
10. The composition according to claim 1 wherein the polyolefm prepared by
polymerization over a metallocene catalyst is polyethylene or polypropylene.
11. The composition according to claim 1 comprising a polyolefm not prepared by
polymerization over a metallocene catalyst.
12. A composition substantially as hereinbefore described and exemplified.

Documents

Name Date
789.jpg 2011-09-02
0070-mas-2000 form-5.pdf 2011-09-02
0070-mas-2000 petition.pdf 2011-09-02
0070-mas-2000 form-26.pdf 2011-09-02
0070-mas-2000 form-3.pdf 2011-09-02
0070-mas-2000 others.pdf 2011-09-02
0070-mas-2000 form-19.pdf 2011-09-02
0070-mas-2000 form-1.pdf 2011-09-02
0070-mas-2000 correspondence-po.pdf 2011-09-02
0070-mas-2000 abstract.pdf 2011-09-02
0070-mas-2000 abstract-duplicate.pdf 2011-09-02
0070-mas-2000 claims.pdf 2011-09-02
0070-mas-2000 claims-duplicate.pdf 2011-09-02
0070-mas-2000 correspondence-others.pdf 2011-09-02
0070-mas-2000 description (complete)-duplicate.pdf 2011-09-02
0070-mas-2000 description (complete).pdf 2011-09-02
789.jpg 2011-09-02
0070-mas-2000 others.pdf 2011-09-02
0070-mas-2000 form-5.pdf 2011-09-02
0070-mas-2000 petition.pdf 2011-09-02
0070-mas-2000 abstract.pdf 2011-09-02
0070-mas-2000 form-3.pdf 2011-09-02
0070-mas-2000 form-26.pdf 2011-09-02
0070-mas-2000 form-1.pdf 2011-09-02
0070-mas-2000 correspondence-others.pdf 2011-09-02
0070-mas-2000 abstract-duplicate.pdf 2011-09-02
0070-mas-2000 claims.pdf 2011-09-02
0070-mas-2000 correspondence-po.pdf 2011-09-02
0070-mas-2000 claims-duplicate.pdf 2011-09-02
0070-mas-2000 description (complete).pdf 2011-09-02
0070-mas-2000 description (complete)-duplicate.pdf 2011-09-02
0070-mas-2000 form-19.pdf 2011-09-02

Orders

Applicant Section Controller Decision Date URL