Plated Steel Sheet

Abstract: The present invention provides a plated steel sheet which is characterized by comprising a base steel sheet and a plating layer that is formed on the surface of the base steel sheet, and which is also characterized in that: the plating layer has a specific chemical composition; the depth, in the sheet thickness direction from the interface between the base steel sheet and the plating layer, where the area fraction of pearlite is 0% to 20% is 3 µm to 100 µm; the area fraction of pearlite having a circle-equivalent diameter of 5 µm or more is 0% to 30% at the depth where the area fraction of pearlite is 0% to 20%; the adhesion amount of the plating layer is 20 g/m2 or more per surface; the plating layer has an oxide layer in the surface; and if the oxide layer is measured by XPS, the peak intensity ratio of (Al-O + Mg-O)/Zn-O is 3 or more.