FORM 2
THE PATENTS ACT, 1970 (39 of 1970) & THE PATENTS RULES, 2003
COMPLETE SPECIFICATION (See section 10, rule 13)
1. Title of the invention: CATALYST COMPOSITE AND PREPARATION THEREOF FOR
ISOMERIZATION OF PARAFFINS
2. Applicant(s)
NAME NATIONALITY ADDRESS
HINDUSTAN Indian Hindustan Petroleum Corporation
PETROLEUM Ltd, Petroleum House, 17
CORPORATION LTD. Jamshedji Tata Road, Churchgate,
Mumbai 400020, India
3. Preamble to the description
COMPLETE SPECIFICATION
The following specification particularly describes the invention and the manner in which it
is to be performed.

TECHNICAL FIELD [0001] The subject matter described herein relates in general to a catalyst composition for isomerization of paraffins comprising of at least one heteropoly acid and reduced graphene oxide. The invention also relates to a process for preparation of a catalyst composition for isomerization of paraffins. The invention further relates to a process for isomerization of paraffins using the catalytic composition.
BACKGROUND
[0002] Graphene is a two-dimensional pure carbon sheet possessing remarkable strength, electrical and thermal conductivity. One atom thick graphene sheet may be obtained by chemical exfoliation of graphite by Hummer’s Method or by chemical vapor deposition under controlled conditions. However graphene cannot be utilized as such because it is an unreactive and inert material without proper functionalization, on the other hand, reduced graphene oxide (rGO) is a reduced form of oxygenated graphene and is expected to be a very promising material to be used as a support in catalytic transformations owing to its remarkable properties such as high surface area, mechanical strength and thermal conductivity along with the potential to be utilized in the form of various nano and meso scale structures. The reduced graphene oxide sheets thus, can be functionalized and used as support for different organic transformations (Guerra et al., Appl. Catal A: Gen 2013; 468:474 467).
[0003]Phosphomolybdic acid (PMA) belongs to the class of materials called heteropoly acids which exist in one of the Keggin, Dawson or other structural forms. It is a highly acidic material and exhibits some very interesting properties such as pseudo-liquid behavior (Kozhevnikov IV. Chem Rev 1998; 98:198-171.), utility as catalyst in both homogeneous and heterogeneous phase (Kozhevnikov IV. J. Mol. Catal A: Chem 2007; 262:92-86.), low temperature activity and reversible structure evolution in the presence of water up to certain temperatures (Micek-Ilnicka A. J Mol. Catal A: Chem 2009; 308:14–1.) However PMA is a bulk material with very low surface area (<5 m2/g) and low mechanical strength thereby

limiting its applications. Recently, high resolution in situ and ex situ TEM studies have indicated that the crystallite size of platinum governs the nature of carbon deposited over the support as graphene sheets or carbon nanotubes (Peng et al., J. Catal. 2012; 286:29–22).
[0004]Monofunctional hybrid materials based on Keggin-type heteropolyacids supported on mesostructured silica were used in isomerization of n-hexane. The heteropolyacids, namely H3PW12O40 or H4SiW12O40, were immobilized onto SBA-15 type silica by incipient wetness impregnation. The resulting catalysts were thoroughly characterized by N2 adsorption–desorption isotherms, XRD, 31P NMR, TGA and FT-IR. These hybrid materials were active for the gas-phase isomerization of n-hexane (Pinto et al., Applied Catalysis A: General 483 (2014): 103-109.). In another study, isomerization of n-butane in the presence of hydrogen catalyzed by a bifunctional catalyst consisting of Pt and Cs2.5H0.5PW12O40 was examined mostly at 573 K. (Kyutae, et al., Journal of Molecular Catalysis A: Chemical 115.3 (1997): 449-455.)
[0005] Jin et al. reported a series of Ni–CsxH3-xPW12O40/SiO2 catalysts which were prepared by direct synthesis method and characterized by BET, XRD, in situ XRD, FT-IR, NH3-TPD, H2-TPR, and H2-TPD. The catalytic performance of the catalysts for the hydrocracking of n-decane with various concentrations of thiophene and pyridine was studied. (Jin, Hao, et al., Fuel 112 (2013): 134-139.) [0006]In another study, Cs-exchanged phosphotungstic acids (CsxH3-xPW12O40, x = 1–3) were examined as a catalyst for the hydrocracking of extra-heavy oil (vacuum residue, API gravity = 2.3°). (Eom, Hee-Jun, et al., Fuel 126 (2014): 263-270.)
SUMMARY
[0007] In an aspect of the present disclosure, there is provided a catalyst composition comprising at least one heteropoly acid and reduced graphene oxide. [0008]In an aspect of the present disclosure, there is provided a process for producing a catalyst composition, the process comprising; contacting at least one heteropoly acid with reduced graphene oxide to obtain a first solution; stirring the

first solution to obtain a second solution; drying the second solution to obtain a dried paste; calcining the dried paste to obtain a catalyst composition. [0009]In an aspect of the present disclosure, there is provided a process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a catalyst composition in a reactor; wherein the catalyst composition comprises of at least one heteropoly acid in an amount in the range of 9% to 91% w/w of the total weight of the composition; and reduced graphene oxide acid in an amount in the range of 9% to 91% w/w of the total weight of the composition. [0010]These and other features, aspects, and advantages of the present subject matter will be better understood with reference to the following description and appended claims. This summary is provided to introduce a selection of concepts in a simplified form. This summary is not intended to identify key features or essential features of the claimed subject matter, nor is it intended to be used to limit the scope of the claimed subject matter.
BREIF DESCRIPTION OF ACCOMNAYING DRAWINGS [0011]The following drawings form part of the present specification and are included to further illustrate aspects of the present disclosure. The disclosure may be better understood by reference to the drawings in combination with the detailed description of the specific embodiments presented herein. [0012]Figure 1 depicts the scanning electron microscopy (SEM) image of conventional molybdophosphoric acid (MPA). [0013]Figure 2 depicts the scanning electron microscopy (SEM) image of molybdophosphoric acid (MPA) synthesized by hydrothermal route. [0014] Figure 3 depicts the scanning electron microscopic (SEM) image of molybdophosphoric acid (MPA) impregnated on reduced graphene oxide (rGO) at 25 oC without thermal treatment.
[0015]Figure 4 depicts the scanning electron microscopy (SEM) image of molybdophosphoric acid (MPA) impregnated on reduced graphene oxide (rGO) subjected to thermal treatment.

[0016]Figure 5 depicts the transmission electron microscopy (TEM) image of
molybdophosphoric acid (MPA) impregnated on reduced graphene oxide (rGO)
subjected to thermal treatment.
[0017]Figure 6 depicts the scanning electron microscopic (SEM) image of reduced
graphene oxide (rGO) assisted molybdophosphoric acid (MPA) synthesis post
thermal treatment.
[0018]Figure 7 depicts the transmission electron microscopic (TEM) image of
reduced graphene oxide (rGO) assisted molybdophosphoric acid (MPA) synthesis
subjected to thermal treatment.
DETAILED DESCRIPTION [0019] Those skilled in the art will be aware that the present disclosure is subject to variations and modifications other than those specifically described. It is to be understood that the present disclosure includes all such variations and modifications. The disclosure also includes all such steps, features, compositions and compounds referred to or indicated in this specification, individually or collectively and any and all combinations of any or more of such steps or features. Definitions:
[0020]For convenience, before further description of the present disclosure, certain terms employed in the specification, and examples are collected here. These definitions should be read in the light of the remainder of the disclosure and understood as by a person of skill in the art. The terms used herein have the meanings recognized and known to those of skill in the art, however, for convenience and completeness, particular terms and their meanings are set forth below.
[0021]The articles “a”, “an” and “the” are used to refer to one or to more than one (i.e., to at least one) of the grammatical object of the article. [0022]The terms “comprise” and “comprising” are used in the inclusive, open sense, meaning that additional elements may be included. Throughout this specification, unless the context requires otherwise the word “comprise”, and variations, such as “comprises” and “comprising”, will be understood to imply the

inclusion of a stated element or step or group of element or steps but not the exclusion of any other element or step or group of element or steps. [0023]The term “catalyst composite(s)” and “catalyst composition(s)” are used interchangeably in the present disclosure.
[0024]Ratios, concentrations, amounts, and other numerical data may be presented herein in a range format. It is to be understood that such range format is used merely for convenience and brevity and should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. [0025] In an embodiment of the present disclosure, there is provided a catalyst composition comprising at least one heteropoly acid and reduced graphene oxide. [0026] In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein at least one heteropoly acid is in an amount in the range of 9% to 91% w/w of the total weight of the composition; and reduced graphene oxide is in an amount in the range of 9% to 91% w/w of the total weight of the composition.
[0027]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the at least one heteropoly acid is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof. [0028]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the at least one heteropoly acid is in an amount in the range of 15% to 85% w/w of the total weight of the composition. [0029]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the at least one heteropoly acid is in an amount in the range of 15% to 30% w/w of the total weight of the composition. [0030]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the at least one heteropoly acid is in an amount in the range of 20% to 25% w/w of the total weight of the composition.

[0031]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
tungstophosphoric acid (TPA) in an amount in the range of 15% to 85% w/w of the
total weight of the composition.
[0032]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
tungstophosphoric acid (TPA) in an amount in the range of 15% to 30% w/w of the
total weight of the composition.
[0033]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
tungstophosphoric acid (TPA) in an amount in the range of 20% to 25% w/w of the
total weight of the composition.
[0034]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
molybdophosphoric acid (MPA) in an amount in the range of 15% to 85% w/w of
the total weight of the composition.
[0035]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
molybdophosphoric acid (MPA) in an amount in the range of 15% to 30% w/w of
the total weight of the composition.
[0036]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid is
molybdophosphoric acid (MPA) in an amount in the range of 20% to 25% w/w of
the total weight of the composition.
[0037]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the at least one heteropoly acid has a
general formula selected from the group consisting of HxAy[BD6O24].zH2O,
HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and HxAy[B5D30O110].zH2O, wherein
A is selected from a group consisting of alkali metal, alkali earth metal, post
transitional metal, ammonium salt, and phosphonium salt; B is selected from a
group consisting of P, Si, As, Ge, and D; D is selected from the group consisting of

Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Tc, Rh, Cd, In, Sn, Ta, W, and Re.
[0038]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the at least one heteropoly acid has a general formula of H3-yAyPW12O40, wherein y is 0 to 3,A is selected a group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Al, ammonium salt, phosphonium salt, Pd, Ag, Ni, Al, and Cu.
[0039]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the reduced graphene is in an amount in the range of 15% to 85% w/w of the total weight of the composition. [0040]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the reduced graphene is in an amount in the range of 70% to 85% w/w of the total weight of the composition. [0041]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, wherein the reduced graphene is in an amount in the range of 70% to 80% w/w of the total weight of the composition. [0042]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 9% to 91% w/w of the total weight of the composition and is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof; and the reduced graphene oxide is in an amount in the range of 9% to 91% w/w of the total weight of the composition. [0043]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 15% to 30% w/w of the total weight of the composition and is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof; and the reduced graphene oxide is in an amount in the range of 70% to 85% w/w of the total weight of the composition. [0044]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 20% to 30% w/w of the total weight of the composition and is selected

from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof; and the reduced graphene oxide is in an amount in the range of 70% to 80% w/w of the total weight of the composition. [0045]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 9% to 91% w/w of the total weight of the composition and has a general formula selected from the group consisting of HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and HxAy[B5D30O110].zH2O, wherein A is selected from a group consisting of alkali metal, alkali earth metal, post transitional metal, ammonium salt, and phosphonium salt; B is selected from a group consisting of P, Si, As, Ge, and D; D is selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Tc, Rh, Cd, In, Sn, Ta, W, and Re, and the reduced graphene oxide is in an amount in the range of 9% to 91% w/w of the total weight of the composition.
[0046]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 9% to 91% w/w of the total weight of the composition and has a general formula selected a group consisting of HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and HxAy[B5D30O110].zH2O, wherein A is selected a group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Al, ammonium salt, phosphonium salt, Pd, Ag, Ni, Al, and Cu; B is selected from a group consisting of P, Si, As, Ge, and D; D is selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Tc, Rh, Cd, In, Sn, Ta, W, and Re, and the reduced graphene oxide is in an amount in the range of 9% to 91% w/w of the total weight of the composition.
[0047]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 9% to 91% w/w of the total weight of the composition and has a general formula of H3-yAyPW12O40, wherein y is 0 to 3, A is Ni, and the reduced graphene oxide is in an amount in the range of 9% to 91% w/w of the total weight of the composition.

[0048]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 20% to 30% w/w of the total weight of the composition and has a general formula of H3-yAyPW12O40, wherein y is 0 to 3, A is Ni, and the reduced graphene oxide is in an amount in the range of 70% to 80% w/w of the total weight of the composition.
[0049] In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 15% to 85% w/w of the total weight of the composition and is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof; and the reduced graphene oxide is in an amount in the range of 15% to 85% w/w of the total weight of the composition. [0050]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 15% to 85% w/w of the total weight of the composition and has a general formula selected from the group consisting of HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and HxAy[B5D30O110].zH2O, wherein A is selected from a group consisting of alkali metal, alkali earth metal, post transitional metal, ammonium salt, and phosphonium salt; B is selected from a group consisting of P, Si, As, Ge, and D; D is selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Tc, Rh, Cd, In, Sn, Ta, W, and Re, and the reduced graphene oxide is in an amount in the range of 15% to 85% w/w of the total weight of the composition. [0051]In an embodiment of the present disclosure, there is provided a catalyst composition as described herein, the at least one heteropoly acid is in an amount in the range of 15% to 85% w/w of the total weight of the composition and has a general formula selected from the group consisting of HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and HxAy[B5D30O110].zH2O, wherein A is selected a group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Al, ammonium salt, phosphonium salt, Pd, Ag, Ni, Al, and Cu; B is selected from a group consisting of P, Si, As, Ge, and D; D is selected from the group consisting of Ti, V, Cr, Mn, Fe,

Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo, Tc, Rh, Cd, In, Sn, Ta, W, and Re, and the
reduced graphene oxide is in an amount in the range of 15% to 85% w/w of the
total weight of the composition.
[0052]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, the at least one heteropoly acid is in an amount in
the range of 20% to 25% w/w of the total weight of the composition and has a
general formula of H3-yAyPW12O40, wherein y is 0 to 3, A is Nickel, and the
reduced graphene oxide is in an amount in the range of 75% to 80% w/w of the
total weight of the composition.
[0053]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, the at least one heteropoly acid is a
tungstophosphoric acid in an amount of 23-25% w/w of the total weight of the
composition and has a general formula of H3-yAyPW12O40, wherein A is Ni and y is
2.5, and the reduced graphene oxide is in an amount of 70-80% w/w of the total
weight of the composition.
[0054]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, the at least one heteropoly acid is a
molybdophosphoric acid in an amount of 23-25% w/w of the total weight of the
composition and has a general formula of H3-yAyPW12O40, wherein A is Ni and y is
2.5, and the reduced graphene oxide is in an amount of 70-80% w/w of the total
weight of the composition.
[0055]In an embodiment of the present disclosure, there is provided a catalyst
composition as described herein, wherein the catalyst is used for isomerization of
paraffins.
[0056]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, the process comprising
contacting at least one heteropoly acid with reduced graphene oxide to obtain a first
solution; stirring the first solution to obtain a second solution; drying the second
solution to obtain a dried paste; calcining the dried paste to obtain a catalyst
composition.

[0057]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the first solution is
stirred for 8-20 hours at 70-100oC.
[0058]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the first solution is
stirred for 12 hours at 85oC.
[0059] In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the dried paste is
calcined at 200-400°C for a period of 2-6 hours.
[0060]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the dried paste is
calcined at 300°C for a period of 4 hours
[0061]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the at least one
heteropoly acid is selected from the group consisting of tungstophosphoric acid
(TPA), molybdophosphoric acid (MPA), and combinations thereof.
[0062]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the at least one
heteropoly acid has a general formula selected from the group consisting of
HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and
HxAy[B5D30O110].zH2O, wherein A is selected from a group consisting of alkali
metal, alkali earth metal, post transitional metal, ammonium salt, and phosphonium
salt; B is selected from a group consisting of P, Si, As, Ge, and D; D is selected
from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo,
Tc, Rh, Cd, In, Sn, Ta, W, and Re.
[0063]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the at least one
heteropoly acid has a general formula H3-yAyPW12O40.
[0064]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein A is selected from

the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Al, ammonium salt, phosphonium salt, Pd, Ag, Ni, Al, and Cu. [0065]In an embodiment of the present disclosure, there is provided a process for producing a catalyst composition as described herein, wherein the at least one heteropoly acid has a general formula H3-yAyPW12O40, and wherein y is 0 to 3. [0066]In an embodiment of the present disclosure, there is provided a process for producing a catalyst composition as described herein, wherein the at least one heteropoly acid has a general formula H3-yAyPW12O40, and wherein y is 2.5. [0067]In an embodiment of the present disclosure, there is provided a process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a catalyst composition in a reactor; wherein the catalyst composition comprises of at least one heteropoly acid in an amount in the range of 9% to 91% w/w of the total weight of the composition; and reduced graphene oxide in an amount in the range of 9% to 91% w/w of the total weight of the composition. [0068]In an embodiment of the present disclosure, there is provided a process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a catalyst composition in a reactor; wherein the catalyst composition comprises of at least one heteropoly acid in an amount in the range of 9% to 91% w/w of the total weight of the composition; and reduced graphene oxide in an amount in the range of 9% to 91% w/w of the total weight of the composition. [0069]In an embodiment of the present disclosure, there is provided a process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a catalyst composition in a reactor; wherein the catalyst composition comprises of at least one heteropoly acid in an amount in the range of 15% to 30% w/w of the total weight of the composition; and reduced graphene oxide in an amount in the range of 70% to 85% w/w of the total weight of the composition to obtain isoparaffins, olefins, naphthalenes, and aromatics..
[0070]In an embodiment of the present disclosure, there is provided a process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a catalyst composition in a reactor; wherein the catalyst composition comprises of at least one heteropoly acid in an amount in the range of 20% to 30% w/w of the total

weight of the composition; and reduced graphene oxide in an amount in the range
of 70% to 80% w/w of the total weight of the composition to obtain isoparaffins
selectively more than 20%.
[0071]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins comprising contacting the paraffins and hydrogen with a
catalyst composition in a reactor; wherein the catalyst composition comprises of at
least one heteropoly acid in an amount in the range of 20% to 30% w/w of the total
weight of the composition; and reduced graphene oxide in an amount in the range
of 70% to 80% w/w of the total weight of the composition to obtain naphthalenes
selectively more than 20%.
[0072]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins comprising contacting the paraffins and hydrogen with a
catalyst composition in a reactor; wherein the catalyst composition comprises of at
least one heteropoly acid in an amount in the range of 20% to 30% w/w of the total
weight of the composition; and reduced graphene oxide in an amount in the range
of 70% to 80% w/w of the total weight of the composition to obtain naphthalenes
and isoparaffins selectively more than 40%.
[0073]In an embodiment of the present disclosure, there is provided a process for
producing a catalyst composition as described herein, wherein the catalyst
composition is at least one heteropoly acid in an amount in the range of 15% to
85% w/w of the total weight of the composition, and support material in an amount
in the range of 15% to 85% w/w of the total weight of the composition.
[0074]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid is in an amount in the range of 15% to 30% w/w of the total weight of the
composition.
[0075]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the reduced graphene oxide
is in an amount in the range of 70% to 85% w/w of the total weight of the
composition.

[0076]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the catalyst composition is
23-25% w/w tungstophosphoric acid (TPA), and 70-80 % w/w reduced graphene
oxide.
[0077]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid is selected from the group consisting of tungstophosphoric acid (TPA),
molybdophosphoric acid (MPA), and combinations thereof.
[0078]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid has a general formula selected from the group consisting of
HxAy[BD6O24].zH2O, HxAy[BD12O40].zH2O, HxAy[B2D18O62].zH2O, and
HxAy[B5D30O110].zH2O, wherein A is selected from a group consisting of alkali
metal, alkali earth metal, post transitional metal, ammonium salt, and phosphonium
salt; B is selected from the group consisting of P, Si, As, Ge, and D; D is selected
from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Zr, Nb, Mo,
Tc, Rh, Cd, In, Sn, Ta, W, and Re.
[0079]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid has a general formula H3-yAyPW12O40.
[0080]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein A is selected a group
consisting of Li, Na, K, Rb, Cs, Mg, Ca, Al, ammonium salt, phosphonium salt, Pd,
Ag, Ni, Al, and Cu.
[0081]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid has a general formula H3-yAyPW12O40, and wherein y is 0 to 3.
[0082]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the at least one heteropoly
acid has a general formula H3-yAyPW12O40, and wherein y is 2.5.

[0083]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the paraffin is a refinery
feedstock such as straight run naphtha, cracked run naptha and fcc naphtha.
[0084]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the paraffin is C5 to C10
linear paraffin.
[0085]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein hydrogen is passed over the
catalyst composition at a rate of 10-100 mL/min.
[0086] In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein feedstock is fed at a rate of
0.05 mL/min.
[0087]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the process is carried out at
a temperature in the range of 150-300°C.
[0088]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the process is carried out at
a temperature of 250°C.
[0089]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the process is carried out at
a pressure in the range of 5-50 bar.
[0090]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the process is carried out at
a pressure of 30 bar.
[0091]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the paraffin weight hourly
space velocity is in the range of 0.01 to 10 hr-1.
[0092]In an embodiment of the present disclosure, there is provided a process for
isomerization of paraffins as described herein, wherein the paraffin weight hourly
space velocity is 2 hr-1.

[0093]Although the subject matter has been described in considerable detail with reference to certain embodiments thereof, other embodiments are possible.
EXAMPLES
[0094]The following examples are given by way of illustration of the present invention and should not be construed to limit the scope of present disclosure. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are intended to provide further explanation of the claimed subject matter.
Example 1
[0095]Preparation of rGO
[0096]Synthesis of Graphene oxide (GO): Graphene oxide was synthesized by improved synthesis of graphene oxide, a 9:1 mixture of concentrated H2SO4/H3PO4 (360:40 mL) was added to a mixture of graphite flakes (3.0 g, 1 wt equiv) with a purity of 99.8% was purchased from Sigma Aldrich. The mixture was and left for aging for 3 days. KMnO4 (18.0 g, 6 wt equiv) was added to the mixture post aging producing a slight exotherm to 35-40 °C. The reaction was then heated to 50 °C and stirred for 48 h. The reaction was cooled to room temperature and poured onto ice (400 mL) with 30% H2O2 (3 mL) AR Grade. The mixture was filtered through polyester filter. The filtrate was centrifuged (8000 rpm for 15 min), and the supernatant was decanted away. The remaining solid material was then washed in succession with 200 mL of water, 200 mL of 30% HCl (37% fuming), and 200 mL of ethanol. The material remaining after this extended multiple-wash process was coagulated with 200 mL of ether. The solid obtained on the filter was vacuum-dried overnight at room temperature, obtaining 5.8 g of product. [0097]Synthesis of Exfoliated Graphite Oxide (XGO): Aqueous colloids of XGO were prepared by dispersing 1.0 g GO into 500 mL of distilled water by ultrasonication and centrifugation for 2 hr to remove any unexfoliated GO. The XGO was dried at 45°C for 24 h.

[0098]Synthesis of Reduced Graphene Oxide (rGO): The rGO was prepared by dispersing 400 mg XGO into 800 mL of distilled water and treating GO with hydrazine hydrate and maintaining the solution at 100oC for 24 hours.
Example 2
[0099]Preparation of composites: Following three methodologies were used to synthesize composites:
a) Conventional MPA synthesis: Phosphomolybdic acid was obtained by dissolving ammoniumheptamolybdate (AMH) in water, mixed slowly with dilute ortho-phosphoric acid solution such that a Mo/P ratio of 12 was maintained. Concentrated HCl was added drop wise to the above solution until the formation of yellow precipitate had stopped. The obtained yellow precipitate was dried overnight (12h) at 100oC and calcined at 350oC for 4 hours. The SEM images shown in Figure 1 indicate a cuboidal morphology. The SEM images shown in Figure 2 indicate rosette morphology for this class of heteropoly acids upon hydrothermal treatment.
(b) MPA was synthesized and impregnated on rGO followed by hydrothermal treatment. Phosphomolybdic acid (PMA) was impregnated over rGO by traditional wet impregnation method where a solution of rGO in water is mixed with as synthesized MPA under stirring for 2 hours at 25°C, and subsequently subjected to hydrothermal treatment at 85°C for 12 hours. The final material was filtered and dried at 100oC for 8 h. The SEM images shown in Figure 3 indicate crystals were found to be embedded over the nano sheets of rGO. However, upon hydrothermal treatment, Figure 4 indicates MPA crystals were found to be embedded within the nano sheets of rGO.
(c) rGO Assisted MPA Synthesis: A dilute solution of AMH was impregnated on rGO prior to the conventional PMA synthesis. The solution was mixed slowly with dilute ortho-phosphoric acid solution such that a Mo/P ratio of 12 was maintained. Concentrated HCl was added drop wise to the above solution until the formation of yellow precipitate had stopped. Subsequently the mixture was subjected to hydrothermal treatment at 85oC for 12 hours. The obtained greenish grey

precipitate was dried overnight (12h) at 100oC and calcined at 350oC for 4 hours. Figure 6 indicates MPA crystals are embedded within the nano sheets of rGO as shown in the inset indicating the restricted morphological changes. Figure 7 showing TEM images also confirm the embedding of MPA inside rGO sheets. Table 1 below details morphological features of different MPA-rGO composites synthesized with the aforementioned methods, wherein MPA stands for molybdophosphoric acid and rGO stands for reduced graphene oxide.
Table 1

S.No. Type Temperature (oC) Observations (Morphological)
1. Pure MPA Synthesis 25 Hexagonal
2. Pure MPA Synthesis 85 Rosette
3. MPA Impregnated on rGO 25 Cuboidal
4. MPA Impregnated on rGO 85 Cuboidal embedded within sheets of rGO
5. rGO Assisted MPA Synthesis 25 Cuboidal embedded within sheets of rGO
6. rGO Assisted MPA Synthesis 85 Cuboidal particles
embedded
within sheets of rGO
restricted the rosette
morphology formation.

[00100]Thus, MPA synthesized at lower temperature was found to have a hexagonal structure, which on thermal/hydrothermal treatments transformed to rosette morphology.
[00101]The cuboidal crystals of MPA impregnated on rGO were found to be cuboidal/hexagonal/spherical. However, thermal treatment of MPA impregnated on rGO did not result in rosette morphology.
[00102]The synthesis of MPA carried out with rGO as support with loading precursors in rGO resulted only in cuboidal/spherical/hexagonal crystals embedded within the rGO sheets confirmed by HRTEM, FESEM and elemental mapping. Further confirmation was obtained by carrying out the catalytic activity of paraffin isomerization. The presence of MPA within the nano sheets of rGO provides superior catalytic performance exhibited by metal-HPA-rGO composite compared to the control experiments (metal-rGO composite).
Example 3
Preparation of Metal-rGO composite:
[00103]Platinum was impregnated over rGO by traditional wet impregnation
method where a solution of platinum salt (platinum nitrate; 0.029 g) in water (10
mL) is mixed with rGO (5 g) under stirring for 2 hours at 25°C, and subsequently
subjected to thermal treatment at 200°C for 4 hours. The final material was filtered
and dried at 100oC for 8 h to obtain CAT 1 with 0.3% of Pt and 100% of rGO.
[00104]Preparation of Metal – MPA – rGO composite: [00105] 12-phosphotungstic acid (Aldrich) was dried at 100 °C to remove the physically adsorbed water before use. Ni(NO3)2 (Aldrich 99.9%) was used as received. NiyH3-yPW12O40 samples (y=2.5) was prepared by drop wise addition of predetermined amounts of a Ni(NO3)2 aqueous on HPW at room temperature. A greenish white precipitate formed, and the solution was stirred for 2 h for uniform mixing. The solvent was vacuum dried and further left to dry overnight at room temperature evaporate the water. Fine greenish white powder was obtained by oven-drying the materials in air at 100°C. The powder was calcined at 300 degrees for 4 hrs. The synthesized Ni-HPW was impregnated by adding a known weight of Ni-HPW on the rGO support and stirred for 12 h at 85oC. The solution was vacuum

dried and calcined at 300oC for 4h. Table 2 below details the composition of different catalyst composites of the present disclosure, wherein MPA stands for molybdophosphoric acid, HPA stands for heteropoly acid and rGO stands for reduced graphene oxide.
Table 2

Sample No Metal (Ni); Value of Y Compound Ratio(Metal HPA): rGO Type of HPA
CAT 2 2.5 3:10 TPA
CAT 2 2.5 3:10 TPA
CAT 3 2.5 3:10 MPA
CAT 3 2.5 3:10 MPA
Preparation of Ni-TPA-rGO (CAT 2)
[00106] 0.3784 g of nickel nitrate was dissolved in 10 ml distilled water. The solution was transferred to a round bottom flask containing 1.5g of tungstophosphoric acid (TPA). This mixture has 0.07641 g of Ni which contributes to 4.0677% of total mixture of (0.3784 g of Nickel Nitrate+1.5 g of TPA=1.878g total mixture). The round bottom flask was kept for stirring in the vacuum rotavapor BUCCI till the temperature of the bath attains 70°C. The solvent was evaporated from the sample using vacuum rotavapour. The dried sample was then calcined at 350°C for 4 hours.
[00107]1.5 g of the above synthesized composite was dissolved in 10 ml of water (This mixture has 0.061005 g of Ni and 1.4349g of TPA). This solution was transferred to a round bottom flask containing 5 g of rGO. This composite has 0.30226g of Nickel Nitrate, 1.4349 g of TPA and 5 g of rGO contribute to 0.9385%Ni-22.075%TPA-76.9865%rGO.The round bottom flask was kept for stirring in the vacuum rotavapor BUCCI till the temperature of the bath attains 70°C. The solvent was evaporated from the sample using vacuum rotavapour. The dried sample was then calcined at 350°C for 4 hours.

[00108] Catalyst formation: The catalysts were pelletized using a Retsch PP25 pellet press with 20 bar pressure. The pelletized catalysts were coarse ground to US Test Sieve 850/600 µm.
Preparation of Ni-MPA-rGO (CAT-3)
[00109] 0.5974 g of nickel nitrate was dissolved in 10 ml distilled water. The solution was transferred to a round bottom flask containing 1.5g of molybdophosphoric acid (MPA). This mixture has 0.12058 g of Ni which contributes to 5.749 % of total mixture of (0.5974 g of nickel nitrate+1.5 g of TPA=2.094 g total mixture). The round bottom flask was kept for stirring in the vacuum rotavapor BUCCI till the temperature of the bath attains 70°C. The solvent was evaporated from the sample using vacuum rotavapour. The dried sample was then calcined at 350°C for 4 hours.
[00110]1.5 g of the above synthesized composite was dissolved in 10 ml of water (This mixture has 0.0862 g of nickel nitrate and 1.4137g of MPA). This solution was transferred to a round bottom flask containing 5 g of rGO. This composite has 0.0862g of nickel nitrate, 1.4137 g of MPA and 5 g of rGO contribute to 1.853%Ni-21.749%MPA-78.2507%rGO.The round bottom flask was kept for stirring in the vacuum rotavapor BUCCI till the temperature of the bath attains 70°C. The solvent was evaporated from the sample using vacuum rotavapour. The dried sample was then calcined at 350°C for 4 hours. [00111] Catalyst formation: The catalysts were pelletized using a Retsch PP25 pellet press with 20 bar pressure. The pelletized catalysts were coarse ground to US Test Sieve 850/600 µm
Example 4
[00112]Process for isomerization of paraffins: Table 3 below details the isomerizing activity of a reference catalyst, wherein TPA stands for tungstophosphoric acid and rGO stands for reduced graphene oxide.
Table 3

Sample No Metal
(Pt/Ni);
Value of Y Compound
Ratio(Metal HPA):
rGO Type of HPA Catalyst Composition Composition in Weights Temp. (oC) Conversion (%) Isoparaffin Se le ctivity Products forme d

30% 100%

Tetraamine Platinum N itrate / Nickel Nitrate HPA rGO

1 0.2214 3:10 - CAT 1 0.3% Pt-100%rGO 0.029772 - 5 250 5.02 32.072 Isoparaffins 1.61

Olefins 0.07

Naphthenes 0.75

Aromatics 2.58
2 2.5 3:10 TPA CAT2 1.1% Ni –
22.8% PTA –
76%rGO 1.2621 5 5 250 54.01 74.13 Isoparaffins 40.04

Olefins 0.33

Naphthenes 13.33

Aromatics 0.3
3 2.5 3:10 MPA CAT3 1.1% Ni – 22.8% PMA – 76% rGO 1.995 g 5 5 250 18.49 91.08 Isoparaffins 16.84

Olefins 0.11

Naphthenes 1.05

Aromatics 0.48
[00113]All catalysts were first reduced under a hydrogen flow of 35 ml/min at a temperature of 300 °C and atmospheric pressure. All catalytic evaluations were done after the reduction step in a fixed bed reactor at a temperature of 250° C, a pressure of 30 bar and under hydrogen flow of 35 ml/min and a nitrogen flow of 10 ml/min.
[00114]CAT1 has shown the least conversion at a value of 5.02% and only a 32% selectivity towards isomerization. Without being bound by theory, it is suggested that the low conversion and selectivity may be due to the presence of functional groups on the surface of reduced graphene oxide. CAT2, surprisingly, exhibits a conversion of 54.01% and a selectivity of 74.13% towards isomers. TPA is a highly acidic material and loading this material on rGO has increased the acidity of the composite altogether which explains the high activity of this catalyst compared to other catalysts. Surprisingly, CAT 2 shows significant selectivity towards naphthenes thereby leading to a decrease in selectivity towards isoparaffins. CAT3 has shown a conversion of 18.49 and a selectivity of 91.08% towards

isomerization. Surprisingly, the activity of CAT3 is lesser than activity of CAT2, however, PMA has shown a better selectivity towards isomerization and naphthenes are formed only to an extent of 1.05% on this catalyst. This behavior can be explained due to the moderate acidity of this material as compared to CAT2.
[00115]Although the subject matter has been described in considerable detail with reference to certain examples and implementations thereof, other implementations are possible. As such, the spirit and scope of the appended claims should not be limited to the description of the preferred examples and implementations contained therein.

I/We claim:
1. A catalyst composition comprising:
at least one heteropoly acid; and reduced graphene oxide acid.
2. The catalyst composition as claimed in claim 1, wherein at least one heteropoly acid is in an amount in the range of 15% to 85% w/w of the total weight of the composition.
3. The catalyst composition as claimed in claim 1, wherein the at least one heteropoly acid is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof.
4. The catalyst composition as claimed in claim 1, wherein the reduced graphene oxide is in an amount in the range of 15% to 85% w/w of the total weight of the composition.
5. The catalyst composition as claimed in claim 1, wherein the catalyst is used for isomerization of paraffins.
6. A process for producing a catalyst composition as claimed in claim 1, the process comprising;
contacting at least one heteropoly acid with reduced graphene oxide to obtain a first solution;
stirring the first solution for to obtain a second solution;
drying the second solution to obtain a dried paste;
calcining the dried paste to obtain a catalyst composition.
7. The process as claimed in claim 6, wherein the first solution is stirred for 8-
20 hours at 70-100oC.

8. The process as claimed in claim 6, wherein the dried paste is calcined at 200-400°C for a period of 2-6 hours
9. The process as claimed in claim 6, wherein the at least one heteropoly acid is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof.
10. A process for isomerization of paraffins comprising contacting the paraffins and hydrogen with a a catalyst composition in a reactor;
wherein the catalyst composition comprises of
at least one heteropoly acid in an amount in the range of 9% to 91% w/w of the total weight of the composition; and
reduced graphene oxide acid in an amount in the range of 9% to 91% w/w of the total weight of the composition.
11. The process as claimed in claim 10, wherein the at least one heteropoly acid is selected from the group consisting of tungstophosphoric acid (TPA), molybdophosphoric acid (MPA), and combinations thereof.
12. The process as claimed in claim 10, wherein the paraffin is a refinery feedstock such as straight run naphtha, cracked run naptha and fcc naphtha.
13. The process as claimed in claim 10, wherein the paraffin is C5 to C10 linear paraffin.
14. The process as claimed in claim 10, wherein hydrogen is passed over the catalyst composition at a rate of 10-100 mL/min.
15. The process as claimed in claim 10, wherein the process is carried out at a temperature in the range of 150-300°C.

16. The process as claimed in claim 10, wherein the process is carried out at a pressure in the range of 5-50 bar.
17. The process as claimed in claim 10, wherein the paraffin weight hourly space velocity is in the range of 0.1 to 10 hr-1.