WO 2006/010927 PCT/GB2005/002947
1
CURTAIN COATING PROCESS USING A HIGH SOLIDS CONTENT COMPOSITION, AND COATED PRODUCT
Field of Invention
The invention relates to a curtain coating process using a high solids content composition for coating a substrate web, and to a coated product.
Background of the Invention
In the manufacture of printing paper, pigmented coating compositions are applied by, for example, blade, bar, air-knife or reverse-roll type coating methods, usually at high speeds. However, the said coating methods are non-contoured (with the exception of air-knife coating method) onto rough substrates which means that any irregular substrate surface will lead to non-uniform coating thickness, which may result in irregularities during the printing process.
Curtain coating methods are now being developed in the paper industry for coating paper webs, to achieve uniformity in surface application which is a necessary condition for obtaining a good final print rendering.
Curtain coating processes are well known and widely used for the application of one or more liquid layers onto the surface of a moving support in the photographic industry. Indeed, this technology was developed for photographic films that require the deposit of many different coats, usually between 8 and 10, with severe constraints on the surface condition and also the thickness of applied coats. Curtain coating is a pre-metered coating process which means that only the required amount of coating liquid needed on the web is pumped through the coating head The curtain coating process is based on free flow on a surface from a coating head located above the surface to be coated. The support is coated by forming a freely-falling vertical curtain of liquid so that it impinges onto the support. A controlled relationship is maintained between the flow rate of the liquid and the speed at which the support is moved so that the curtain is stable and has a uniform flow rate across its width to obtain a layer of the coating onto the substrate. The coating head is defined using properties of the coating fluid, so as to obtain the most uniform possible coating film thickness in the running direction or the transverse direction of the machine.
One of the advantages of curtain coating is the superior quality and more uniform surface of the substrates, namely paper webs, that can be attained. Another advantage is the lack of contact between the coating head and the support, unlike contact coating processes such as blade and rod coating. This provides a

WO 2006/010927 PCT/GB2005/002947
2
means of eliminating forces applied on the support during coating, which causes web breakage in particular, and can have a non-negligible effect on the increase in the machine speed, and consequently can reduce production costs. Another advantage of curtain coating is the possibility of applying two or more coats simultaneously.
Despite many attempts to coat substrate webs with one or more coating layers using curtain coating processes, the main limiting factors to curtain coating remain the curtain stability and the air entrainment, which gives rise to the inclusion of air between the coating composition and the web leading to numerous bubbles and irregularities in the coating. Puddling of the curtain can also be an issue and lead to the formation of a heel at the curtain impingement zone, usually as a result of the coating fluid being too low in viscosity. This phenomenon can lead to coating non-uniformities, and can also induce air entrainment at relatively low web speeds. Highly viscous and elastic curtains tend to 'pull1 along the web, which can also lead to a non-uniform coating due to fluctuations at the curtain impingement zone. In curtain coating, uniform layer(s) are only obtained if the operational variables are held within fairly precise limits. These limits define the coating 'window'. One example is air entrainment, as described in US Patent No. 5,391,401 (Blake et al.). This patent describes a method to alleviate the issues of air entrainment. Therein is described an optimum relationship between viscosity and shear rate for curtain coating. The desired rheological profile promotes a low viscosity at the shear rates expected near the dynamic wetting line, where the coating wets the substrate, and a high viscosity at the much lower shear rates expected in the other regions of the flow. Coating composition can be increased in viscosity by the addition of thickening agents that interact with the binder, which has the effect of increasing the mix viscosity at low shear rate without substantially raising its viscosity at high shear rate, implying that a high viscosity at high shear rate is a disadvantage. Much of this work has been recorded for formulation containing binder, especially gelatine, along with silver halide grains for use in photographic applications. US Patent 5,393,571 (Suga et al.) describes the alleviation of air entrainment and puddling of the curtain coating by using a mix of viscosity superior to 90 mPa.s at low shear rate (10 s-1) onto a rough surface (0.3 urn). US Patent 6,099,913 (Clarke et al.) describes the formation of a coated layer adjacent to the substrate surface having a viscosity of 90 mPa.s to 220 mPas at a shear rate of 10000 s-1, which can form a free-falling curtain and allows for higher coating speeds to be attained without air entrainment. These applications are apparently

WO 2006/010927 PCT/GB2005/002947
3
suitable for photographic formulations generally containing gelatine and silver halide grains, which typically have a low solids content.
A second example of a limiting factor is curtain stability which is related to the ratio of inertial to surface tension forces (Weber number). This implies that higher flow rates and lower surface tensions are beneficial to curtain stability. However, in certain cases high flow rates are undesirable especially when high solid content mixes are used and lower coat weights are required.
Many typical paper coating compositions are highly pigmented and of high solids content and inherently are shear-thinning (pseudo-plastic) in nature. This type of rheology is useful for applications with blade, bar, reverse roll, slot or slide coating techniques. However, it has been observed that numerous pigmented paper coating formulations do not form a stable curtain at low flow rates (especially when Q, the flow rate per unit die length, is equal to or less than 104 m3/(s.m) for aqueous systems).
If the curtain coating method is to be used to coat high solid content paper formulations at low coat weights, this can only be achieved currently by utilising faster web speeds. However, at faster web speeds air entrainment becomes a real issue especially when coaling onto smooth, less porous substrates. Diluting the mix in order to run at slower web speeds is not an option. High solids mixes are preferred in the coating process as there is less demand on the drying capacity and it allows for lower grammage raw base (<80 g/m2) to be used, which can readily break during the process under high wet coating weights. Higher solid content mixes impart improved properties on the coated media, for example, higher gloss. Diluting mixes also lowers mix viscosity, which can lead to heel formation at the curtain impingement zone, if it becomes too low.
INVENTION
Thus, there is a requirement to generate coating formulations which can generate a stable curtain under low flow rates.
Described herein is an improved coating process for pigmented coalings which allows the coating 'window', including the curtain stability and coating uniformity, to be expanded. This means that the coating process can be run at a wider range of web speeds, reduced flow rates and, thus, lower corresponding wet lay down and dry coat weight, without destabilising the curtain. A further option allowed is the ability to coat onto smoother, coated substrates, which tend to give rise to the onset of air entrainment more readily than rougher substrates as the web

WO 2006/010927 PCT/GB2005/002947
4
speed is increased. This offers a greater flexibility with the entire coating process
and allows for a greater success in producing high quality coated substrates such
as paper, board and plastic webs.
This is achieved by the combined addition of a small quantity of a polymeric
additive (rheology modifier) and a non-ionic surfactant to the aqueous coating
composition. The former (i.e. rheology modifier) increases the viscosity of the
coating composition under mid to high shear rates, and the latter (i.e. non-ionic
surfactant) lowers the surface tension of the coating composition. Extensional
viscosity was influenced by the choice and quantity of rheology modifier.
The rheology modifier additives include anionic polyacrylamide / acrylate
polymers and ionic hydrophobic polyether types. The advantage of these
polymeric additives is that they can be added to the formulation in small quantities
(<2% dry weight) with no detrimental impact on the product properties (gloss,
opacity, colorimetric coordinates L*a*b*, stiffness, smoothness) or on print
performance (image quality, optical density, dry time). The surfactants are
preferably selected among non-ionic surfactants.
The combination of surfactant and rheology modifier seems to have a significant
influence upon extending the curtain coating 'window' of operation. There were
no signs that the increase in mid to high shear rate viscosity due to the presence of
the rheology modifiers had any influence on the onset of air-entrainment or
puddling at the coating impingement zone.
The invention provides a process of producing a free-falling curtain of an aqueous
pigmented composition having a high solids content at a flow rate per unit die
length values (Q) equal to or inferior to lxlO"4 m3/(s.m) for coating onto amoving
web.
The said composition contains a surfactant (which lowers the surface tension of
the composition) and a polymeric rheology modifier.
More particularly, the invention provides a curtain coating process for coating a
substrate with a stable curtain and a uniform coating at low flow rates wherein a
free-falling curtain of an aqueous composition comprising a high solids content is
coated onto a moving substrate at a flow rate per unit die length value (Q) equal to
or inferior to lX10-4m3/(s.m), the said high solids content composition comprising
a polymeric rheology modifier and a non-ionic surfactant.
The said rheology modifier is selected from the group comprising water phase
thickeners and associative thickeners, or a combination of the two.

WO 2006/010927 PCT/GB2005/002947
5
The said surfactant is selected from the group of alkyl aryl ethoxylates,
alkoxylated acetylenics, alkyl acetylenic diols, non-alkoxylated acetylenics,
secondary alcohol alkoxylates, and mixtures thereof.
The said composition comprises binders and coating pigments. In particular, the
binder is selected from a group consisting of copolymers of styrene, in particular
styrene-butadienes or styrene-acrylates, styrene-nialeic anhydrides, polyvinyl
alcohols, polyvinyl pyrrolidones, carboxymethyl celluloses, starches, proteins,
polyvinyl acetates, polyurethanes, polyesters, and mixtures thereof.
Preferably, the pigments are selected from calcium carbonates, kaolin, talc,
titanium dioxide, silica, alumina, boehmite alumina, barium sulphate, zinc oxide,
conductive pigments, aluminium silicate, and mixtures thereof.
The said aqueous composition has a high solids content more than or equal to 50%
in dry weight, preferably more than 60 %.
The concentration of the said rheology modifier in the composition is less than 5%
dry weight and preferably less than 1% dry weight, more preferably less than 0.5%
dry weight of the total composition dry weight.
The concentration of the said surfactant in the composition is less than 1% dry
weight and preferably less than 0.5% dry weight, more preferably less than 0.3%
dry weight of the total composition dry weight.
Preferably the viscosity of the said aqueous composition is between 50 and
200mPa.s at a shear rate of 1000 s-1, between 25 and 90 mPa.s at a shear rate of
10000 s-1, and between 20 and 75 mPa.s at a shear rate of 100 000 s-1, all sets of
data recorded at 25°C.
Preferably, the static surface tension of the, aqueous composition is less than
45mN/m.
Preferably, the dry coat weight coated onto the substrate is less than or equal to
12g/m2, preferably less than or equal to 10 g/m2.
According to the invention, the substrate is either a fibrous substrate such as a
paper or a board, or a plastic web.
Preferably, the curtain is coated onto a continuous paper web substrate which is
either a) non-coated or primed, b) pre-coated or pre-primed, c) pre-coated and
subsequently calendered.
In particular, when the substrate is a paper substrate, the grammage of the said
paper substrate before coating is less than or equal to 150g/m2, more particularly
less than or equal to SO g/m2.
The free-falling curtain is comprised of one or more layers.

WO 2006/010927 PCT/GB2005/002947
6
According to a particular embodiment of the invention, the free-falling curtain is
comprised of two layers of aqueous composition with a high solids content as
above described.
According to another aspect of the invention there is provided a coated product
including a substrate and a substantially uniform coating on the substrate, the
coating comprising a high solids content composition including a polymeric
rheology modifier and a non-ionic surfactant
The invention provides a paper or plastic support (web or sheet) obtained from this
process, in particular a high gloss paper.
EXAMPLES:
Examples of rheology modifiers utilised are outlined in Table 1 and examples of surfactants utilised are outlined in Table 2.
Table 1.
Rheology Company Polymer Type Mode of Major Feature
Modifier Activity
Sterocoll BASF Anionic water-in-oil Water phase Mid-shear rate
BL emulsion of an thickener viscosity-build,
acrylamide-acrylic acid Extensional
copolymer viscosity build
Rheolate Elementis Hydrophobic ethoxylated Associative High-shear rate
212 polyurethane thickener viscosity-build
Rheolate Elementis Polyether polyol Associative High-shear rate
350 thickener viscosity-build
Rheolate Elementis Hydrophobic modified Water phase / Low/mid-shear
425 alkali swellable Associative rate viscosity-
polyacrylate thickener build
Rheovis CIBA Anionic Water phase High/mid shear
802 polyacrylamide/acrylate thickener rate viscosity-
build
Mowiol KuraTay Polyvinyl alcohol Water phase High/raid shear
40-88 thickener rate viscosity-
build.
Extensional
| viscosity build

WO 2006/010927 PCT/GB2005/002947
7

Substrate
150 g/m2 clay-coated substrate composing of 130 g/m2 raw paper base with 20g/m2 clay coating calendered at l0N/m using a 2-nip steel roller calender stack at 600m/min. The physical properties of the coated paper substrate are shown in Table" 3.

EXAMPLES
Example 1 (Comparative)
Calcium carbonate pigments (85 parts) were dispersed in water. A latex binder (15 parts) was added to the formulation and the mix was allowed to stir for 0.5h. The solids content of the formulation was recorded at 64.7%.
Example 2 (Comparative)
Calcium carbonate pigments (84.8 parts) were dispersed in water. A latex binder (14.97 parts) was added to the formulation and the mix was allowed to stir for 0.5h. Surfynol CT211 (0.23 parts) was added to the mix and allowed to stir for a further 0.5h. The solids content of the formulation was recorded at 65.5%.

WO 2006/010927 PCT/GB2005/002947
8
Example 3 (Invention)
Calcium carbonate pigments (84.62 parts) were dispersed in water. A latex binder (14.94 parts) was added to the formulation and the mix was allowed to stir for 0.5h. Surfynol CT211 (Air Products) (0.23 parts) was added to the mix and allowed to stir for a further 0.5h. 0.21 parts of Sterocoll BL (BASF) was added at the end of the formulation. The mix was stirred for a further 0.5h. The solids content of the formulation was recorded at 65.08%.
Example 4 (Invention)
Calcium carbonate pigments (84.44 parts) were dispersed in water. A latex binder (14.90 parts) was added to the formulation and the mix was allowed to stir for 0.5h. Surfynol CT211 (0.23 parts) was added to the mix and allowed to stir for a further 0.5h. 0.42 parts of Rheovis 802 (CIBA) was added at the end of the formulation. The mix was stirred for a further 0.5h. The solids content of the formulation was recorded at 65.0%.
Example 5 (Invention)
Calcium carbonate pigments (84.44 parts) were dispersed in water. A latex binder (14.9 parts) was added to the formulation and the mix was allowed to stir for 0.5h. Surfynol CT211 (0.23 parts) was added to the mix and allowed to stir for a further 0.5h. 0.42 parts of Mowiol 40-88 (Kuraray) was added at the end of the formulation. The mix was stirred for a further 0.5h. The solids content of the formulation was recorded at 63.5%.
Example 6 (Invention)
Calcium carbonate pigments (90.52 parts) were dispersed in water. A latex binder (8.42 parts) was added to the formulation and the mix was stirred. Surfyaol CT211 (0.27 parts) was added to the mix. 0.03 parts of a defoamer was added to the mix, followed by the addition of 0.41 parts of Mowiol 4-98 (as a rheology modifier) (Kuraray) and 0.05 parts of Sterocoll BL (BASF), agitation was performed between each component addition. The mix pH was adjusted to 10.3 with sodium hydroxide. The solids content of the formulation was recorded at 65.5%.

WO 2006/010927 PCT/GB2005/002947
9
Results and Discussion
Example 1 did not contain either the surfactant or rheology modifier and a curtain could only be formed at a Q (flow rate per unit die length) value of 1.8x10 m3/(s.m). The static surface tension was measured at 45 mN/m. At a web speed of 400 m/min this corresponded to a dry coat weight of 26.6 g/m2 which is far greater than the coat weight requirement of <10 g/m3 for coated paper of good quality (image quality and dry time) for off-set printing. However, the coating was unstable at the impingement zone, possible due to air entrainment, and a poor coating uniformity was obtained. The viscosity of the mix at a shear rate of 100s" was 125mPa.s, at a shear rate of 1000 s-1 was 37rnPa.s, at a shear rate of 10 000 s-1 was 14mPa.s, and at a shear rate of 100 000 s-1 was 13mPa.s. Example 2 involved the addition of the non-ionic surfactant to Example 1 which allowed for the curtain to form at a much reduced flow-rate per unit die length (Q= 9.26x10-5m3/(s.m), in comparison to Example 1. This is due to the lowering of the surface tension of the mix to 35 mN/m. This allows for a dry coat weight of 14.0 g/m2 to be attained, which is much lower than in the absence of surfactant but higher than the target 10 g/m2. The viscosity of the mix at a shear rate of 100s-1 was 142mPa.s, at a shear rate of 1000 s-1 was 43mPa.s, at a shear rate of 10 000 s-1 was 18mPa,s, and at a shear rate of 100 000 s-1 was 18mPa.s. Example 3 involved the addition of the surfactant and rheology modifier (Sterocoll BL) to Example 1, which yielded a stable curtain at a flow rate per unit die length, Q, of 6.73xl0"5 m3/(s.m). This yielded a dry coat weight of 9.4g/m2 which was within the target required. The static surface tension is increased over Example 1 (rheology modifiers tend to raise the surface tension), to 40 mN/m. However, the flow rate required for curtain stability is lower than that in Example 1. A uniform coating profile was obtained until a speed of 600 m/min was reached, where the onset of air entrainment occurred. The viscosity of the mix at a shear rate of 100s-1 was 438raPa.s, at a shear rate of 1000s-1 was 107mPa.s, at a shear rate of 10 000s-1 was 50mPa,s, and at a shear rate of 100 000 s-1 was 48mPa.s. Example 4 involved the addition of the surfactant and rheology modifier (Rheovis 802) to Example 1, which yielded a stable Gurtain at a flow rate per unit die length, Q, of 6.17xl0"5 m3/(s.m). This yielded a dry coat weight of 8.5g/m2 which was within the target required. The static surface tension is increased over Example 1 (rheology modifiers tend to raise the surface tension), to 37 mN/m. However, the flow rate required for curtain stability is again lower than that in Example 1. A uniform coating profile was obtained until a speed of 600m/min was reached,

WO 2006/010927 PCT/GB2005/002947
10
where the onset of air entrainment occurred. The viscosity of the mix at a shear rate of 100s-1 was 355mPa.s, at a shear rate of 1000s-1 was 80mPa.s, at a shear rate of 10 000 s -1 was 28 mPa.s, and at a shear rate of 100 000 s"3 was 24 mPa.s. Example 5 involved the addition of the surfactant and Mowiol 40-88 polyvinyl alcohol to Example 1, which yielded a stable curtain at a flow rate per unit die length, Q, of 7.86xlO"5 m3/(s.m). This yielded a dry coat weight of 10.0 g/m2 which was within the target required. The static surface tension is increased over Example 1 to 42 mN/m. However, the flow rate required for curtain stability is lower than in Example 1. A uniform coating profile was obtained until a speed of 600 m/min was reached, where the onset of air entrainment occurred. The viscosity of the mix at a shear rate of 100 s-1 was 161wiPa.s, at a shear rate of 1000 s-1 was l24mPa.s, at a shear rate of 10 000 s-1 was 77mPa.s, and at a shear rate of 100 000 s"1 was 34mPa.s.
Example 6 involved the addition of the surfactant and a dual rheology modifier system (Sterocoll BL + Mowiol 4-98) to a latex binder and calcium carbonate coating mix. A stable curtain at a flow rate per unit die length Q of 9,45x10" m3/(s.m) was formed and the static surface tension value was of 35.5 mN/m. A uniform coating profile was obtained without air entrainment at a line speed of 600m/min. The coated paper obtained presents good print performance. The dry coat weight was of 10.0g/m2. Hie viscosity of the mix at a shear rate of 100s-1 was 255 mPa,s, at a shear rate of 1000 s-1was 78mPa,s, at a shear rate of 10 000 s-1 was 37mPa.s, and at a shear rate of 100 000 s-1 was 29mPa.s. Viscosity results at the various shear rates for each mix are summarised in Table 4.

Effective extensional viscosity does not appear to impact on curtain stability (see the results in Table.5). .Example 3 shows a high extensional viscosity of 174mPa.s

WO 2006/010927 PCT/GB2005/002947
11
at 100 000 s-1 and Example 4 shows a low extensional viscosity of 4mPa.s at the same shear rate, yet the minimum flow rate obtained for curtain stability is slightly lower for the latter.


Test Methods
Viscosity - was measured using a Brookfield RVT viscometer. The spindle speed
selected was l00rpm. Spindle size was either sp2 or sp3. The temperature of the
mix was recorded during the measurement of viscosity.
Density - was measured using a l00mL Pycnometer. The temperature was
recorded during the measurement of the density.
pH - was measured using; an HI 9024 Microcomputer pH meter (Hanna
Instruments). The temperature was recorded during the measurement of the pH.
Solids (%) - was measured using a CEM Labwave 9000 Microwave
Moisture/Solids Analyzer.

WO 2006/010927 PCT/GB2005/002947
12
Contact Angle - was measured with a FibroDAT 1100.
Surface Tension - was measured using a DC A 132 apparatus with a platinum
plate.
Paper Gloss - was measured using a gloss meter at a fixed angle of 75° (BYK
Gardner GmbH).
Paper Smoothness - was measured using a Bekk Smoothness Tester (Messmer
Instruments Ltd).
Air Permeability - was measured using a Bendtsen Tester (Lorentzen & Wettre)
Rheology - flow data was measured with a CV0120 High Resolution Rheometer
(Bohlin Instruments) using the parallel plate at a gap of 40 um at 25 +/- 0.1 °C.
The shear rate range was 10 to 100 000 s"1.
Effective Extensional viscosity - was measured on a Paar Automated High Shear
Viscometer HVA 6 with a capillary length of 10mm and 5 mm and a capillary
diameter of 0.6 mm.
Mix Preparation and Coating Method
All parts are expressed in dry weight by 100 parts in dry weight of the total composition.
So, the coating formulas in examples 1-6 are expressed in % dry weight (parts) of the total composition.
All formulations were mixed using a Greaves GM dispersing apparatus. The stirring was optimised to ensure good mixing but to avoid excessive air entrainment. The curtain head used was a slide-type with a width of 0.49m and a die gap of 300µm. The curtain coating head was equipped with edge guides with running water down each side, with a vacuum suction present to remove this water at the bottom of the edge guides. The catch pan also acts as a baffle - a mechanical barrier to limit air entrainment at the impingement zone. A suction vacuum can optionally be applied (0.3 bar) to reduce the movement across the web of the curtain at the impact zone and to limit further the onset of air entrainment. The curtain height was 100mm.
The coat weight of each coated sample is determined from the known volumetric flow rate of the pump delivering the mix to the curtain head, web speed, density and % solids of the mix, and curtain width. The coat weight is checked by placing a 100 cm2 coated and uncoated substrate sample in an oven at

WO 2006/010927 PCT/GB2005/002947
13
150°C for 10 min and measuring the difference in weight between the two samples.
Materials used in Formulations
Calcium carbonate pigments : ground calcium carbonate of which 95% (weight)
have an average particle size less than 2.5 µm. Solids at 78%.
Latex binder : an aqueous dispersion of a copolymer of styrene-butadiene. Solids
content are at 50%.
Mowiol 40-88 (Kuraray): the polyvinyl alcohol is 88% hydrolysed. The viscosity
of a 4% solution at 25°C is 40 cps as measured on a Brookfield RVT viscometer
(manufacturer's data). Used as a rheology modifier (water phase thickener) or as a
binder. The polyvinyl alcohol was used as a 10% solution obtained by heating the
polyvinyl alcohol granules with water at 95°C for 0.5h.
Rheovis 802: an anionic water-in-oil emulsion of a polyacrylamide/acrylate. Used
as .a rheology modifier (water phase thickener).
Mowiol 4-98 (KuraravV the polyvinyl alcohol is 98% hydrolysed. The viscosity
of a 4% solution at 25°C is 4.5 cps as measured on a Brookfield RVT viscometer
(manufacturer's data). Used as a rheology modifier (thickener) or as a binder. The
Mowiol 4-98 was used as a 25% solution obtained by heating the polyvinyl
alcohol granules with water at 95°C for 0.5h.

WO 2006/010927 PCT/GB2005/002947
CLAIMS
1. Curtain coating process; for coating substrates with a stable curtain and a
uniform coating at low flow rates wherein a free-falling curtain of an
aqueous composition comprising a high solids content is coated onto the
moving substrate at a flow rate per unit die length value (Q) equal to or
inferior to 10-4m3/(s.m), the said high solids content composition comprising
a polymeric rheology modifier and a non-ionic surfactant
2. Curtain coating process as claimed in claim 1, wherein the said rheology
modifier is selected from the group comprising water phase thickeners and
associative thickeners, and mixtures thereof.
3. Curtain coating process as claimed in claim 2, wherein the said water phase
thickeners are selected, among anionic polyacrylamide/acrylate polymers,
ionic hydrophobic polyether types and Polyvinyl alcohol, carboxymethyl
cellulose, hydroxyethyl cellulose, starch, protein derivate and alkali swellable
polyacrylate(s).
4. Curtain coating process as claimed in claim 2, wherein the said associative
thickeners are selected among hydrophobic ethoxylated polyurethanes and
polyether polyols.
5. Curtain coating process as claimed in claims 1 to 4, wherein the said
surfactant is selected from the group of alkyl aryl ethoxylates, alkoxylated
acetylenics, alkyl acetylenic diols, non-alkoxylated acetytenics, secondary
alcohol alkoxylates, and mixtures thereof.
6. Curtain coating process as claimed in any one of claims 1 to 5, wherein the
aqueous composition has a high solids content more than or equal to 50% dry
weight, preferably more than or equal to 60%.
7. Curtain coating process as claimed in any one of claims 1 to 6, wherein the
viscosity of the aqueous composition is between 50 and 200mPa.s at a shear
rate of 1000 s-1, between 25 and 90mPa.s at a shear rate of 10 000 s-1, and
between 20 and 75 mPa,s at a shear rate of 100000s"1, all sets of data
recorded at 25°C.

WO 2006/010927 PCT/GB2005/002947
15
8. Curtain coating process as claimed in any one of claims 1 to 6, wherein the
static surface tension of the aqueous composition is less than 45 mN/m.
9. Curtain coating process; as claimed in any one of claims 1 to 8, wherein the
aqueous composition comprises binders and pigments.
10. Curtain coating process; as claimed in claim 9, wherein the binder is selected
from a group consisting of copolymers of styrene in particular styrene-
butadiene or styrene-acrylates, styrene-maleic anhydrides, polyvinyl
alcohols, polyvinyl pyirrolidones, carboxymethyl celluloses, starch, protein,
polyvinyl acetates, polyurethanes, polyester, acrylic acid and mixtures
thereof.
11. Curtain coating process as claimed in claim 9 or claim 10, wherein the
pigment is selected from calcium carbonates, aluminium silicate, kaolin, talc,
titanium dioxide, silica, aluminas, boehmite alumina, barium sulphate, zinc
oxide, plastic pigments conductive pigments, and mixtures thereof.
12. Curtain coating process as claimed in any one of claims 1 to 9, wherein the
concentration of rheology modifier in the aqueous composition is less than
5% dry weight and preferably less than' 1% dry weight of the total
composition dry weight
13. Curtain coating process as claimed in any one of claims 1 to 10, wherein the
concentration of surfactant in the composition is less than 1% dry weight and
preferably less than 0.5% dry weight of the total composition dry weight.
14. Curtain coating process as claimed in any one of claims 1 to 13, wherein the
dry coat weight coated onto the substrate is less than or equal to 12g/m2,
preferably less than or equal to 10 g/m2.
15. Curtain coating process as claimed in any one of claims 1 to 14, wherein the
moving substrate is a fibrous substrate or a plastic substrate.
16. Curtain coating process as claimed in claim 15, wherein the fibrous substrate
is a paper or a board.

WO 2006/010927 PCT/GB2005/002947
16
17. Curtain coating process as claimed in claim 16, wherein the grammage of the
paper substrate before coating is less than or equal to 150g/mz, more
particularly less than or equal to 80 g/m2.
18. Curtain coating process as claimed in claims 16 to 17, wherein the curtain is
coated onto a continuous paper web which is either a) non-coated or primed,
b) pre-coated or pre-primed, c) pre-coated and subsequently calendered.
19. Curtain coating process as claimed in claim 15, wherein the moving substrate
is a plastic web or a film.
20. Curtain coating process as claimed in any one of claims 1 to 19, wherein the
free-falling curtain is comprised of one or more layers.
21. Curtain coating process as claimed in claim 20, wherein said free-falling
curtain comprises two layers of aqueous composition with a high solids
content.
22. A coated product including a substrate and a substantially uniform coating on
the substrate, the coating comprising a high solids content composition
including a polymeric rheology modifier and a non-ionic surfactant.
23. A coated product as claimed in claim 22, wherein the said rheology modifier
is selected from the group comprising water phase thickeners and associative
thickeners, and mixtures thereof.
24. A coated product as claimed in claim 22 or claim 23, wherein the said
surfactant is selected from the group of alkyl aryl ethoxylates, alkoxylated
acetylenics, alkyl acetylenic diols, non-alkoxylated acetylenics, secondary
alcohol alkoxylates, and mixtures thereof.
25. A coated product as claimed in any one of claims 22 to 24, wherein the
coating composition including binders and pigments.
26. A coated product as claimed in any one of claims 22 to 25, wherein the
concentration of rheology modifier in the coating composition is less than
5% dry weight and preferably less than 1% dry weight of the total
composition dry weight.

WO 2006/010927 PCT/GB 2005/00294 7
17
27. A coated product as claimed in any one of claims 22 to 26, wherein the dry
coat weight coated onto the substrate is less than or equal to 12g/m2,
preferably less than or equal to 10 g/m2.
28. A coated product as claimed in any one of claims 22 to 27, wherein the
substrate is a fibrous substrate or a plastic substrate.
29. A coated product as claimed in claim 28, wherein the substrate is a paper
substrate having a grammage, excluding the coating, of less than or equal to
150g/m2, more particularly less than or equal to 80 g/m2.