Specification
[Title of the Invention] EXHAUST GAS TREATMENT METHOD AND EXHAUST
GAS TREATMENT FACILITY
[Technical Field of the Invention]
[0001]
The present invention relates to an exhaust gas treatment method and an
exhaust gas treatment facility.
Priority is claimed on Japanese Patent Application No. 2013-153536, filed on
July 24, 2013, the content of which is incorporated herein by reference.·
[Related Art] ·
[0002]
Slag (steelmaking slag), which is produced using a conve1ter or the like
through desulfurization, dephosphorization, or decarburization refinement in a
steelmaking step, contains a large amount ofCaO. Therefore, the expansibility of the
steelmaking slag is high, and the volume stability ofthe steelmaking slag is poor.
Thus, in the related art, the reuse of the steelmaking slag as a cement raw material, an
aggregate, or the like has been limited. However, recently, in order to promote the
recycling of resources, valuable materials such as Fe or P must be separated and
collected from the steelmaking slag and that the steelmaking slag is reformed into
high-quality slag to be reused. To that end, in the related art, various slag treatment
methods are proposed.
[0003]
For example, Patent Document 1 discloses a slag treatment method including:
a first step of obtaining modified slag by adding iron and steel slag to molten iron and
steel in a melting furnace, adding heat and a reducing material to modify the iron and
- 1 -
steel slag, and causing Fe, Mn, and Pin the iron and steel slag to move to the molten
iron and steel; and second and third steps of sequentially oxidizing Mn and P in the
molten iron and steel to move to the modified slag and sequentially extracting high-Mn
slag and high-P slag.
[0004]
Patent Document 2 discloses a method including: charging iron and steel slag
containing higher than 5 wt% of iron oxide into a steel bath containing lower than 1.5
wt% of carbon; obtaining the steel bath containing higher than2.0 wt% of carbon by
introducing carbon or a carbon carrier into the steel bath to carburize the steel bath;
and reducing oxides in the iron and steel slag. In this method, when the iron and steel
slag is charged into the steel bath, the iron and steel slag react vigorously with the steel
bath. As a result, the foaming of the iron and steel slag (slag foaming) may occur, or
the iron and steel slag may overflow from the furnace. In order to suppress slag
foaming and overflowing, the carbon content of the steel bath is decreased before
charging the iron and steel slag into the steel bath. As a result, when the iron and
steel slag is charged into the steel bath, the reaction rate between the iron and steel slag
and the steel bath decreases. As described above, in a state where the reaction rate
between the iron and steel slag and the steel bath decreases, the carbon content of the
steel bath increases, and then the iron and steel slag is reduced.
[0005]
In addition, Non-Patent Document 1 discloses the results of a slag reduction
test in which steelmaking slag powder, carbon powder, and slag reforming material
powder are charged into an electric furnace. Further, Patent Document 3 discloses a
method of collecting valuable metals from molten slag, the method including: reducing
molten slag, which is produced through non-ferrous metal refining, into a
- 2 -
carbonaceous reducing material in an open direct current electric furnace; and
separating the molten slag into a metal layer and a slag layer.
[0006]
In addition, in a reforming method disclosed in Patent Document 4, in order to
melt and modify low-fluidity steelmaking slag having a low temperature, a surface of
the steelmaking slag is mechanically stirred before (or after) adding or thermally
spraying a reforming material to the low-fluidity steelmaking slag which is
accommodated in a container. A mixed layer of the steelmaking slag and the
reforming material is heated using a heating burner to obtain molten slag, and this
molten slag is discharged li'om the container to be solidified.
[Prior Att Document]
[Patent Document]
[0007]
[Patent Document 1] Japanese Unexamined Patent Application, First
Publication No. 852-033897
[Patent Document 2] Published Japanese Translation No. 2003-520899 of
the PCT International Publication
[Patent Document 3) Australian Patent No. AU-B-20553/95
[Patent Document 4] Japanese Unexamined Patent Application, First
Publication No. 2005-146357
[Non-Patent Document]
[0008]
[Non-Patent Document 1] Scandinavian Journal of Metallurgy 2003; 32: p.
7 to 14
[Disclosure of the Invention]
- 3 -
[Problems to be Solved by the Invention]
[0009]
However, in the slag treatment method described in Patent Document 1, since
the reduction treatment is performed using a convet1er, the molten iron and steel and
the iron and steel slag are strongly stirred. Therefore, when the carbon concentration
. in the molten iron and steel is high during the charging of the iron and steel slag into
the steel bath, the iron and steel slag is brought into contact with the molten iron and
steel. As a result, a reaction between the iron and steel slag and the steel bath is
promoted, and slag foaming occurs. In order to avoid the occmTence of slag foaming,
the iron and steel slag is charged into the molten iron and steel having a low carbon
concentration. Next, in order to promote the reduction reaction, carbon is charged
into the steel bath to increase the carbon concentration in the molten iron and steel.
Therefore, it is necessary to repeat batch processing. That is, in order to obtain slag
having a necessary component composition, it is necessary to repeat batch processing
(slag reduction treatment, and oxidation and extraction treatment ofMn and P) a
plurality of times. Therefore, working efficiency and productivity decrease.
[0010]
Likewise, in the slag reduction method described in Patent Document 2, the
reduction treatment is performed using a converter. Therefore, in order to increase or
decrease the carbon concentration in molten iron and to reduce the iron and steel slag,
it is necessary to repeat batch processing such as decarburization heating and
carburization reduction. Therefore, working efficiency and productivity decrease.
[0011]
On the other hand, in the reduction test described in Non-Patent Document 1,
a ground product of solidified cold steelmaking slag is a treatment target. In the
- 4 -
method described in Patent Document 3, solidified cold slag is a treatment target. In
order to reduce cold slag, a step of heating and melting the cold slag is necessary.
Therefore, the energy consumption rate increases due to the addition of the step.
[0012]
As described above, in the method of the related art in which hot steelmaking
slag is recycled tln·ough batch processing (Patent Documents 1 and 2), there is a
problem in that the working efficiency and productivity of the slag treatment are low.
On the other hand, in the method of the related art in which cold steelmaking slag is
heated and melted to be recycled (Non-Patent Document 1 and Patent Document 3),
there is a problem in that the energy consumption rate required for the slag treatment
mcreases.
[0013]
Therefore, the present inventors thoroughly studied a method capable of:
treating molten steelmaking slag (hereinafter referred to as "molten slag"), which is
produced in a steelmaking step, without solidification in order to reduce the energy
consumption rate; and continuously reducing molten slag in order to improve working
efficiency and productivity.
[0014]
When molten slag is charged into molten iron in an electric furnace, the
energy consumption rate can be limited as compared to a case where cold slag is
heated and melted. However, when molten slag is charged into molten iron in an
electric furnace, a phenomenon occurs in which the molten slag reacts rapidly with the
molten iron and boils (slag foaming). When slag foaming occurs, a phenomenon may
occur in which the molten slag overflows from the electric furnace (overflowing).
Accordingly, in order to prevent overflowing, it is necessary to limit the occurrence of
- 5 -
slag foaming which causes overflowing.
[0015]
In a reducing furnace (for example, converter), a reduction reaction is
promoted due to a reaction between molten slag and molten iron, and C in the molten
iron reduces FeO in the molten slag. Therefore, in order to improve reducing power,
it is necessary to repeat decarburization and carburization. Therefore, working
efficiency decreases. On the other hand, in a reduction reaction in an electric furnace,
a reaction between iron (FeO) and carbon (C) in molten slag is more predominant than
a reaction between the molten slag and molten iron. Accordingly, it was found that,
in a case where an electric furnace is used, even when the C concentration in molten
iron is low at about 1.5 mass%, molten slag can be reduced without carburization, and
working efficiency can be improved. Therefore, it is considered that the use of an
electric furnace instead of a reducing furnace be one of the measures to limit the
occurrence of slag foaming during the charging of molten slag.
[0016]
However, there may be a case where the C concentration in molten iron is
high in an electric furnace. Therefore, the present inventors performed a thorough
investigation and repeated an experiment regarding a method, even in the above case,
capable of limiting the occurrence of slag foaming during the charging of molten slag;
and appropriately reducing molten slag with high working efficiency without
decarburization and carburization.
[0017]
As a result, it was found that, from the viewpoint of limiting the occurrence of
slag foaming during the charging of molten slag to prevent the occurrence of
overflowing, it is preferable that the following methods described in (a) and (b) are
- 6 -
adopted.
(a) Fluid molten slag having a high temperature is temporarily held in a slag
holding furnace, which is atTanged adjacent to an electric furnace, without directly
charging the molten slag to the electric furnace. The molten slag is slowly poured
from the slag holding furnace into the electric furnace while adjusting the pouring rate
of the molten slag so as to prevent the above-described overflowing.
(b) A molten slag layer (preferably, inert reducing slag layer) as a buffer zone
is formed on a molten iron layer in the electric furnace in advance, and the molten slag
is poured from the slag holding furnace to the molten slag layer.
[0018]
In this way, using the slag holding furnace, molten slag is poured onto the
molten slag layer in the electric furnace while adjusting the pouring rate of the molten
slag. As a result, the occurrence of rapid slag foaming can be limited during the
pouring of molten slag, and molten slag can be continuously reduced in the electric
fumace without performing decarburization and carburization.
[0019]
However, in the above-described electric furnace, exhaust gas containing CO
and the like and dust are produced during the reduction treatment of molten slag. In
order to prevent the exhaust gas or the dust fi·om leaking, it is necessary to maintain a
negative internal pressure of the electric furnace. Howeve1~ the emission rate of
exhaust gas in the electric furnace varies depending on, for example, the pouring rate
of molten slag or the progress of a slag reduction treatment. Therefore, in a case
where the exhaust rate of exhaust gas is constant, when the emission rate of exhaust
gas increases, the internal pressure of the electric furnace increases and a negative
internal pressure may not be maintained. In addition, when the emission rate of
- 7 -
exhaust gas decreases, the internal pressure of the electric furnace decreases
significantly, and an excess amount of dust may be sl1cked into an exhaust path. On
the other hand, for example, a configuration of adjusting the exhaust rate of exhaust
gas using a damper or the like to adjust the internal pressure of the electric fhrnace may
be considered. However, it is not necessarily easy to finely control the opening of the
damper according to the emission rate of exhaust gas.
[0020]
The present invention has been made in consideration of the above-described
problems, and an object thereof is to provide an exhaust gas treatment method and an
exhaust gas treatment facility, capable of easily adjusting the internal pressure of an
electric furnace according to a variation in the emission rate of exhaust gas in the
electric furnace in which molten slag is reduced.
[Means for Solving the Problem]
[0021]
The present invention adopts the following means to solve the abovedescribed
problems and to achieve the above-described object.
(!)According to an aspect of the present invention, there is provided an
exhaust gas treatment method in a slag treatment process in which molten slag
produced in a steelmaking step is charged into a slag holding furnace, the molten slag
is poured from the slag holding furnace into an electric furnace, which accommodates
a molten iron layer and a molten slag layer formed on the molten iron layer, the molten
slag is continuously reduced in the electric furnace, and valuable materials in the
molten slag are collected into the molten iron layer, the method including: burning a
combustible component in exhaust gas by causing the exhaust gas, which is produced
in the electric furnace, to flow into the slag holding furnace and supplying oxygen-
- 8 -
containing gas into the slag holding furnace; causing the burned exhaust gas to flow
from the slag holding furnace to a suction device tln·ough an exhaust gas pipe;
adjusting an intemal pressure of the electric furnace by introducing external air into the
exhaust gas pipe tln·ough an opening pmtion provided in the middle of the exhaust gas
pipe; and changing an area of the opening pmtion depending on a variation in the
internal pressure of the electric furnace by using an opening area changing unit
provided in the opening pm1ion.
[0022)
(2) The exhaust gas treatment method according to (1) may further include:
cooling the exhaust gas in the exhaust gas pipe by introducing external air into the
exhaust gas pipe through an external air introduction port provided between the
opening portion and the suction device.
[0023]
(3) The exhaust gas treatment method according to (2) may futther include:
changing a flow rate of the external air, which is introduced tln·ough the external air
introduction pm1, depending on a variation in temperature of the exhaust gas in the
exhaust gas pipe between the opening portion and the suction device.
[0024]
(4) According to another aspect of the present invention, there is provided an
exhaust gas treatment facility for a slag treatment process in which molten slag
produced in a steelmaking step is charged into a slag holding furnace, the molten slag
is poured fi"om the slag holding furnace into an electric furnace, which accommodates
a molten iron layer and a molten slag layer formed on the molten iron layer, the molten
slag is continuously reduced in the electric furnace, and valuable materials in the
molten slag are collected into the molten iron layer, the facility including: an oxygen
- 9 -
supply unit that supplies oxygen-containing gas into the slag holding furnace; an
exhaust gas pipe that is connected to the slag holding furnace; a suction device that
sucks exhaust gas in the slag holding fhrnace through the exhaust gas pipe; an opening
portion that is provided in the middle of the exhaust gas pipe; a pressure detecting unit
that detects an internal pressure of the electric furnace; and an opening area changing
unit that changes an area of the opening portion depending on a variation in the
internal pressure of the electric furnace, in which the internal pressure of the electric
furnace is adjusted by causing exhaust gas, which is produced in the electric furnace, to
flow into the slag holding furnace, burning a combustible component in the exhaust
gas using the oxygen-containing gas in the slag holding furnace, exhausting the burned
exhaust gas through the exhaust gas pipe, and introducing external air into the exhaust
gas pipe through the opening portion.
[0025]
(5) In the exhaust gas treatment facility according to ( 4), the opening area
changing unit may include a sleeve that is provided around the exhaust gas pipe and
slides along an axial direction of the exhaust gas pipe so as to cover at least a pmtion
of the opening pmtion.
[0026]
(6) The exhaust gas treatment facility according to ( 4) or (5) may further
include: an external air introduction port that is provided in the exhaust gas pipe
between the opening portion and the suction device.
[0027]
(7) The exhaust gas treatment facility according to (6) may further include: a
temperature detecting unit that detects a temperature of exhaust gas in the exhaust gas
pipe between the opening portion aud the suction device; and an external air flow rate
- I 0 -
control unit that controls a flow rate of external air, which is introduced tln·ough the
external air introduction pmt, depending on the detected temperature.
[Effects of the Invention]
[0028]
According to the aspects, the internal pressure of the electric furnace can be
easily adjusted according to a variation in the emission rate of exhaust gas in the
electric furnace in which molten slag is reduced.
[Brief Description of the Drawings]
[0029]
FIG. 1 is a flowchart showing a slag treatment process according to a first
embodiment of the present invention.
FIG. 2 is a schematic diagram showing an overall configuration of a slag
treatment facility according to the first embodiment of the present invention.
FIG. 3 is a vertical cross-sectional view showing a slag holding furnace
(holding posture) according to the first embodiment of the present invention.
FIG. 4 is a ve1tical cross-sectional view showing the slag holding fi.Jrnace
(pouring posture) according to the first embodiment of the present invention.
FIG. 5 is a schematic diagram showing a configuration of an exhaust gas
treatment facility according to the first embodiment of the present invention.
FIG. 6 is a schematic diagram showing a configuration of an exhaust gas
treatment facility according to a second embodiment of the present invention.
FIG. 7 is a flowchart showing an example of a control method of a pressure
indicating controller according to the second embodiment of the present invention.
FIG. 8 is a flowchart showing an example of a control method of a
temperature indicating controller according to the second embodiment of the present
- 11 -
invention.
FIG. 9A is a graph showing a relationship between an emission rate of exhaust
gas (emission rate of exhaust gas g 1 in an electric furnace 1) and an elapsed time in a
slag pouring step according to an example of the present invention.
FIG. 9B is a graph showing a relationship between a slit width (width of a slit
58) and the elapsed time in the slag pouring step according to the example of the
present invention.
FIG. 9C is a graph showing a relationship between an internal pressure ofthe
electric furnace I and the elapsed time in the slag pouring step according to the
example of the present invention.
FIG. 1 OA is a graph showing a relationship between an exhaust gas
temperature (temperature of exhaust gas g3) and the elapsed time in the slag pouring
step according to the example of the present invention.
FIG. I OB is a graph showing a relationship between a damper opening
(opening of a damper 65) and the elapsed time in the slag pourin:g step according to the
example of the present invention.
FIG. IIA is a graph showing a relationship between the emission rate of
exhaust gas (emission rate of exhaust gas gl in the electric furnace I) and the elapsed
time in an interval step according to the example of the present invention.
FIG. JIB is a graph showing a relationship between the slit width (width of
the slit 58) and the elapsed time in the interval step according to the example of the
present invention.
FIG. 11 Cis a graph showing a relationship between the internal pressure of
the electric furnace 1 and the elapsed time in the interval step according to the example
of the present invention.
- 12 -
[Embodiments of the Invention]
[0030]
Hereinaftet~ the details of a preferred embodiment of the present invention
will be described with reference to the accompanying drawings. In this specification
and the drawings, components having practically the same function are represented by
the same reference numerals, and a description thereof will not be repeated.
[0031]
[1. First Embodiment]
[ 1.1. Summaty of Slag Treatment Process]
First, the summary of a slag treatment process according to a first
embodiment of the present invention will be described with reference to FIG. 1. FIG.
1 is a flowchatt showing the slag treatment process according to the first embodiment
of the present invention.
[0032]
As shown in FIG. 1, molten iron is produced using a blast fumace in att
ironmaking step (S 1 ), and molten steel is refined using a converter or the like in a
steelmaking step (S2). This steelmaking step (S2) includes a desulfurization step (S3 ),
a dephosphorization step (S4), and a decarburization step (S5) of removing sulfur,
phosphorus, carbon, and the like fi·om the molten iron. In addition, the steelmaking
step (S2) includes: a secondary refining step (S6) of removing gas such as hydrogen or
sulfi.tr and the like remaining in the molten steel to adjust components; and a casting
step (S7) of casting molten steel in a continuous caster.
[0033]
In the steelmaking step (S2), molten iron is refined in a converter by using a
flux containing calcium oxide as a major component. At this time, oxides are
- 13 -
produced by oxidizing C, Si, P, Mn, and the like in molten iron with oxygen which is
blown into the converter. Slag is produced by bonding these oxides to calcium oxide.
In addition, in the desulfurization step (S3), the dephosphorization step (S4), and the
decarburization step (S5), various kinds of slags ( desulfurization slag,
dephosphorization slag, and decarburization slag) are produced.
[0034]
Hereinaftet~ the slags produced in the steelmaking step (S2) will be
collectively called "steelmaking slag". The steelmaking slag includes desulfurization
slag, dephosphorization slag, and decarburization slag. In addition, hereinafter,
steelmaking slag which is in a molten state and has a high temperature will be referred
to as "molten slag". Likewise, desulfurization slag, decarburization slag, and
dephosphorization slag which are in a molten state will be referred to as "molten
desulfurization slag", "molten dephosphorization slag", and "molten decarburization
slag", respectively.
[0035]
In the slag treatment step (S 1 0), the molten slag produced in the steelmaking
step (S2) is transported from the convet1er to an electric furnace and is continuously
reduced, melted, and reformed in the electric furnace. As a result, valuable materials
(valuable elements such as Fe and P) in the molten slag are collected into a molten iron
layer as a layer positioned below a molten slag layer. At this time, in the electric
furnace, for example, a treatment of reducing oxides such as Fe and Pin the molten
slag, a treatment of separating iron powder (iron) from the molten slag, or a treatment
of adjusting the basicity of the molten slag is performed.
[0036]
As a result, high-phosphorus molten iron containing phosphorus and the like
- 14 -
is separated and collected from the molten slag. In addition, the molten slag as the
steelmaking slag is reduced and reformed, and high-quality reducing slag
corresponding to blast furnace slag is collected. This reducing slag has lower
expansibility than the steelmaking slag and thus can be effectively recycled for, for
example, a cement raw material, a fine aggregate, or a ceramic product.
[0037]·
Further, the dephosphorization treatment (S II) is performed on the highphosphorus
molten iron which is collected from the molten slag such that Pin the highphosphorus
molten iron is oxidized and moves into the molten slag. As a result, the
high-phosphorus molten iron is separated into high-phosphate slag and molten iron.
The high-phosphate slag can be recycled as, for example, a phosphate fertilizer or a
phosphate raw material. In addition, the molten iron is recycled in the steelmaking
step (S2) and is charged into the converter or the like.
[0038]
When molten iron, which is obtained by performing a desiliconization
treatment on molten iron tapped from a blast furnace, is used as molten iron
accommodated in the electric furnace, low silicon-molten iron is obtained by
performing the dephosphorization treatment (S II) on the high phosphorus molten iron
and can be recycled in the converter as it is.
[0039]
The above-described explanations are the summary of the slag treatment
process according to the embodiment. In this process, it is preferable that the molten
dephosphorization slag among various molten slags produced in the steelmaking step
(S2) is used as a treatment target. The molten dephosphorization slag has a lower
temperature than the molten decarburization slag and contains a large amount of iron
- 15 -
powder and phosphoric acid. Therefore, the molten dephosphorization slag is melted
and reformed not in the oxidation treatment but in the reduction treatment. As a
result, the collection efficiency of valuable elements (for example, Fe and P) is
improved. Therefore, in the following description, an example in which the molten
dephosphorization slag is used as a treatment target will be described. However, the
molten slag according to the present invention is not limited to the molten
dephosphorization slag, and an arbitrary steelmaking slag such as molten
desulfurization slag or molten decarburization slag produced in the steelmaking step
(S2) can be used.
[0040]
[1.2. Configuration of Slag Treatment Facility]
Next, a slag treatment facility for realizing the above-described slag treatment
process will be described with reference to FIG. 2. FIG. 2 is a schematic diagram
showing an overall configuration of the slag treatment facility according to the first
embodiment of the present invention.
[0041]
As shown in FIG. 2, the slag treatment facility includes an electric furnace 1
and a slag holding furnace 2 that is arranged diagonally above the electric furnace 1.
In addition, a slag ladle 3 is used in order to charge molten slag 4 into the slag holding
furnace 2. This slag ladle 3 can reciprocate between a convmter (not shown) used in
the steelmaking step (S2) and the slag holding furnace 2. The molten slag 4
discharged from the converter is charged into the slag ladle 3. The slag ladle 3
transports the molten slag 4 from the convetter to the slag holding furnace 2 and
charges the molten slag 4 into the slag holding fi.Jrnace 2. The slag holding furnace 2
can store and hold the molten slag 4. The held molten slag 4 is continuously or
- 16 -
intermittently poured into the electric fiJrnace 1.
[0042]
It is not necessary that the molten slag 4 held in the slag holding furnace 2 is
completely melted. It is only necessary that the molten slag 4 has fluidity so as to be
poured Jiom the slag holding furnace 2 into the electric furnace 1. That is, even when
a pmtion of the molten slag 4 is melted and the remaining portion thereof is solidified,
it is only necessary that the molten slag 4 has fluidity as a whole.
[0043]
The electric furnace 1 reduces and reforms the molten slag 4 using auxiliary
materials, for example, a reducing material such as a carbon material and a reforming
material. The electric furnace 1 is a reducing electric furnace for melting and
reducing the molten slag 4, for example, a fixed direct current electric furnace. A
shell of the electric furnace 1 includes a furnace bottom 11, a furnace wall 12, and a
furnace cover 13. A slag pouring pmt 14, through which the molten slag 4 is
introduced from the slag holding furnace 2, is formed on the furnace cover 13. In this
way, the electric furnace 1 has a closed stmcture except for the slag pouring pmt 14
such that the furnace internal space can be thermally insulated.
[0044]
At the center of the electric furnace 1, an upper electrode 15 and a furnace
bottom electrode 16 are arranged to be vertically opposite to each other. A voltage is
applied between the upper electrode 15 and the furnace bottom electrode 16 to
generate arc discharge between the upper electrode 15 and the furnace bottom
electrode 16. As a result, the molten slag 4 is reduced. As shown in FIG. 2, by
using a hollow electrode as the upper electrode 15, the auxiliary materials can be
charged into an arc. spot through the inside of the hollow electrode without separately
- 17 -
providing a raw material charging device.
[0045]
On the fhrnace wall12 ofthe electric furnace 1, a slag hole 17 for discharging
reducing slag and· a tap hole 18 for discharging molten iron are provided. The slag
hole 17 is mTanged at a height position corresponding to the molten slag layer 5 on the
molten iron layer 6. The tap hole 18 is arranged at a height position corresponding to
the molten iron layer 6 on the furnace bottom side.
[0046]
In addition, in FIG. 2, for example, raw supply devices 31, 32, and 33 are
provided in the electric furnace 1. The raw supply device 31 is provided to supply an
iron-containing material such as direct-reduced iron (DRI) into the electric furnace 1.
In addition, the raw supply device 33 is provided to supply a fine powdered ironcontaining
material (for example, FeO powder) such as dust powder containing iron
into the electric furnace 1 tlu·ough the upper electrode 15 (hollow electrode). As a
result, in the electric furnace 1, these iron-containing materials can be melted and
recycled. In addition, the raw supply device 32 is necessary to supply auxilimy
materials such as a reducing material and a reforming material required for the
reduction treatment of the molten slag 4.In this example, the auxiliaty materials are
supplied into the electric furnace I tlu·ough the upper electrode 15. As the reducing
material, for example, a fine powdered carbon material such as coke breeze, anthracite
culm, or graphite powder is used. In addition, the reforming material is an auxiliary
material for adjusting the concentration of Si02, Alz03, or .MgO contained in the
molten slag 4 as a major component. As such a reforming material, for example,
silica sand, flyash, .MgO powder, or waste refractory powder can be used.
[0047]
- 18 -
Next, the reduction treatment of the molten slag 4 in which the electric
fiunace having the above-described electric fimmce 1 is used will be described with
reference to FIG. 2.
[0048]
First, an appropriate amount of molten iron (for example, molten iron
transported from a blast furnace) is accommodated in advance in the electric furnace 1
as molten seed and the molten iron layer 6. The C concentration in the molten iron is
typically 1.5 mass% to 4.5 mass%. It was verified fi·om an experiment of the present
inventors that, in the electric furnace 1, the C concentration (mass%) in the molten iron
and the total Fe concentration (T. Fe; mass%) in the reduced molten slag 4 (reducing
slag) have a correlation with each other. For example, when the C concentration in
the molten iron is higher than 3 mass%, the reduction of oxides in the molten slag 4 is
promoted, and thus the total Fe concentration in the reducing slag can be reduced to be
1 mass% or lower. Accordingly, it is preferable that the C concentration in the molten
iron of the molten iron layer 6 is adjusted according to the total Fe concentration
required to reduce slag.
[0049]
Next, in a state where the electric furnace 1 is continuously operated by
supplying power thereto, the molten slag 4 is poured fi·om the slag holding furnace 2
into the electric furnace 1 in an amount corresponding to the reduction treatment
capability of the electric furnace I {for example, electricity supply per unit time in the
electric furnace I). The molten slag 4 poured into the electric furnace 1 forms the
molten slag layer 5 on the molten iron layer 6. Furthe1~ the auxiliary materials such
as the reducing material (carbon material) and the reforming material are also
continuously poured into the molten slag layer 5 in the electric furnace I, for example,
- 19 -
through the upper electrode 15. In addition, in the electric furnace I, the temperature
of the molten iron layer 6 is controlled to be, for example, 1400°C to 1550°C, and the
temperature of the molten slag layer 5 is controlled to be, for example, 1500°C to
l650°C. The temperature control can be realized by adjusting the supply rate of the
molten slag 4 or by adjusting the electricity supply to be within a range where the
electricity supply per unit time is constant.
[0050]
As a result, in the electric fi.Jrnace I, the reduction reaction of the molten slag
4 in the molten slag layer 5 is promoted due to arc heat generated between the upper
electrode 15 and the furnace bottom electrode 16. In this reduction treatment, oxides
(for example, FeO and PzOs) contained in the molten slag 4 are reduced by C of the
carbon material in the molten slag layer 5 to produce Fe and P. Fe and P move from
the molten slag layer 5 to the molten iron layer 6 (molten iron) on the furnace bottom
side. On the other hand, C of an excess amount of the carbon material is suspended
in the molten slag layer 5 without moving to the molten iron layer 6. In addition, in
the reduction treatment, the slag components in the molten slag 4 are reformed by the
reforming material.
[0051]
In the reduction treatment, FeO contained in the molten slag 4 which is
poured into the electric furnace I preferentially reacts with C of the carbon material in
the molten slag layer 5 before C contained in the molten iron in the molten iron layer 6
(refer to the following reaction formula (I)).
FeO+C--->Fe+COt (I)
That is, C of the charged carbon material is suspended in the molten slag layer
5 without moving to the molten iron layer 6. Therefore, the reduction reaction based
- 20 -
on the reaction formula (I) is not likely to occur at an interface between the molten
iron layer 6 and the molten slag layer 5. Therefore, in the molten slag layer 5, the
reduction reaction based on the reaction formula (I) preferentially progresses, and
reduced iron (Fe) which is ptoduced by the reduction reaction moves to the molten iron
layer 6.
[0052]
In this way, in the reduction treatment using the electric furnace I, the
reaction between FeO and C in the molten slag layer 5 is more predominant than the
reaction FeO in the molten slag layer 5 and C in the molten iron layer 6. Accordingly,
when the molten slag 4 is poured into the electric furnace 1, the molten slag layer 5 on
the molten iron layer 6 fimctions as a buffer zone for the reaction between the poured
molten slag 4 and the molten iron of the molten iron layer 6. Therefore, a rapid
reaction between the molten slag 4 and the molten iron can be limited.
[0053]
That is, by pouring the molten slag 4 into the molten slag layer 5 having a low
FeO concentration, the FeO concentration in the poured molten slag 4 can be reduced
by dilution, and direct contact between the poured molten slag 4 and the molten iron of
the molten iron layer 6 can be limited. Accordingly, when the molten slag 4 is poured
from the slag holding furnace 2 into the electric fi1rnace 1, the boiling phenomenon
(slag foaming) caused by a rapid reaction between the molten slag 4 and the molten
· iron can be limited. As a result, the phenomenon (overflowing) in which the molten
slag 4 overflows from the electric furnace I can be avoided.
[0054]
As described above, oxides contained in the molten slag 4 which is poured
into the molten slag layer 5 in the electric fim1ace I are reduced such that Fe and Pare
- 21 -
collected from the molten slag 4 into the molten iron layer 6, and the slag components
of the molten slag 4 are reformed. Accordingly, when the reduction treatment
progresses after the pouring of the molten slag 4, the components of the molten slag
layer 5 are gradually reformed from the molten slag 4 (steelmaking slag) into the
reducing slag (high-quality slag corresponding to blast furnace slag). The molten slag
layer 5 refmmed into the reducing slag functions as a buffer zone having a lower FeO
concentration. Therefore, when the molten slag 4 is newly poured fi·om the slag
holding furnace 2 into the molten slag layer 5, the occurrence of slag foaming can be
reliably limited.
[0055]
In addition, when the reduction treatment progresses, Fe moves into the
molten iron. Therefore, the thickness of the molten iron layer 6 gradually increases.
From the viewpoint of exhibiting the function as the buffer zone, the thickness
of the molten slag layer 5 is preferably 100 mm to 600 mm and more preferably 1 00
mm to 800 mm. Therefore, when the thickness of the molten slag layer 5 reaches a
predetermined value by pouring the molten slag 4 thereinto, the slag hole 17 is opened
to discharge the reducing slag ofthe molten slag layer 5 to the outside of the electric
furnace I. In addition, when the interface of the molten iron layer 6 approaches the
slag hole 17, the tap-hole .18 is opened to discharge the molten iron (for example, highp
molten iron) of the molten iron layer 6. In this way, the reducing slag is
intermittently discharged and collected from the slag hole 17 of the electric furnace I.
In addition, the molten iron is intermittently discharged and collected from the tap hole
18 of the electric furnace I. As a result, in the electric furnace 1, the reduction
treatment of the molten slag 4 can be continued without intetmption.
[0056]
- 22 -
In addition, during the operation ofthe electric furnace I (that is, during the
reduction treatment), oxides of the molten slag 4 are reduced using C of the carbon
material to produce high-temperature exhaust gas containing CO, H2, and the like.
For example, when iron oxide is reduced, CO gas is produced due to the reduction
reaction based on the reaction formula (1 ). This exhaust gas flows into the slag
holding furnace 2 through the slag pouring pmt 14 of the electric furnace I and is
discharged to the outside through the inside of the slag holding furnace 2 as an exhaust
path. By using the closed electric furnace 1 and using the slag holding furnace 2 as
an exhaust path for the exhaust gas as described above, the internal atmosphere of the
electric furnace I is maintained to be a reducing atmosphere containing, as major
components, CO gas produced by the reduction reaction and H2 produced from the
carbon material (reducing material). Accordingly, an oxidation reaction on the
surface of the molten slag layer 5 can be prevented.
[0057]
[1.3. Configmation of Slag Holding Furnace]
Next, the configuration of the slag holding furnace 2 according to the
embodiment will be described in detail with reference to FIGS. 3 and 4. FIG. 3 is a
vertical cross-sectional view showing the slag holding furnace 2 (holding postme)
according to the embodiment. FIG. 4 is a vertical cross-sectional view showing the
slag holding furnace 2 (pouring posture) according to the embodiment.
[0058]
As shown in FIG. 3, the slag holding furnace 2 is a heat-resistant container
and has functions of holding the molten slag 4 having a high temperature and pouring
the molten slag 4 into the electric furnace I. The slag holding furnace 2 holds the
molten slag 4, has a structure in which the pouring rate of the molten slag 4 into the
- 23 -
electric furnace 1 can be adjusted, and fimctions as an exhaust path for the exhaust gas
produced from the electric furnace 1. The slag holding furnace 2 includes: a slag
holding furnace body 20 (hereinafter, referred to as "furnace body 20") for storing and
holding the molten slag 4; and a pouring hole pmiion 21 for pouring the molten slag 4
from the inside of the furnace body 20 into the electric furnace 1.
[0059]
The furnace body 20 is a closed container including a lower wall 22, a side
wall 23, and an upper wall 24 and has an internal space for storing the molten slag 4.
The lower wall 22 includes a shell 22a, a heat insulator 22b that is provided outside the
shell 22a, and a lining refractory 22c that is provided inside the shell 22a. Therefore,
the lower wall 22 has superior strength and heat resistance. The lining refractory is
also provided inside the side wall23 and the upper wall 24.
[0060]
A gas discharge port 25 and a slag pouring port 26 are provided on an upper
portion of the furnace body 20 on the furnace cover 27 side. The gas discharge port
25 is an exhaust port for discharging the exhaust gas of the electric furnace 1 and is
connected to an exhaust gas pipe 55 described below. A negative internal pressure of
the slag holding furnace 2 is maintained by a suction device such as a blower 56
connected to the exhaust gas pipe 55. The slag pouring port 26 is an opening for
pouring the molten slag 4 into the furnace body 20 from the slag ladle 3 provided
above the slag holding furnace 2. The openable furnace cover 27 is provided in the
slag pouring port 26. When the molten slag 4 is poured Jl'om the slag ladle 3 into the
fumace body 20, the furnace cover 27 is opened. On the other hand, while the molten
slag 4 is not poured from the slag ladle 3 into the fumace body 20, the furnace cover
27 is closed to close the slag pouring port 26. As a result, the permeation of external
- 24 -
c.·1 ~
air into the furnace body 20 can be prevented, and a constant internal temperature of
the furnace body 20 can be maintained.
[0061]
The pouring hole portion 21 is a cylindrical portion provided in the fiJrnace
body 20 on the electric furnace 1 side. The internal space of the pouring hole portion
21 is used as a slag pouring path 28 for pouring the molten slag 4 from the furnace
body 20 into the electric furnace 1. At a tip end of the pouring hole portion 21, a
pouring hole 29 connected to the slag pouring path 28 is provided. The length of the
slag pouring path 28 in the vettical direction of the slag holding furnace 2 and the
length of the slag pouring path 28 in the width direction ofthe slag holding furnace 2
(direction perpendicular to the plane of FIG. 3) are shorter than the size of the internal
space of the furnace body 20. The slag pouring path 28 is downwardly curved toward
the pouring direction. In addition, the internal space of the furnace body 20 gradually
becomes nan·ow toward the pouring hole pmtion 21 side. By setting the shapes of the
furnace body 20 and the pouring hole portion 21 to be as described above, the pouring
rate of the molten slag 4 can be accurately adjusted when the molten slag 4 is poured
from the inside of the furnace body 20 into the electric furnace 1.
[0062]
The pouring hole pottion 21 of the slag holding furnace 2 is connected to the
slag pouring pmt 14 of the electric furnace 1. As shown in FIGS. 3 and 4, the slag
pouring pmt 14 of the electric furnace 1 is larger than the pouring hole portion 21 of
the slag holding furnace 2. That is, in the embodiment, a connection structure is
adopted in which a tip end of the pouring hole portion 21 is inserted into the slag
pouring port 14 in a state where a gap is present between an outer wall surface of the
pouring hole portion 21 and an inner wall surface of the slag pouring pmt 14. The
- 25 -
connection structure between the pouring hole portion 21 and the slag pouring pmi 14
is not limited to this embodiment. For example, a connection structure in which the
pouring hole portion 21 and the slag pouring port 14 are air-tightly connected to each
other through bellows or the like, or a connection structure in which a gap between the
pouring hole pmiion 21 and the slag pouring pmi 14 is filled with a filler can be
adopted.
[0063]
According to the structure of the slag holding furnace 2, when the suction
device (refer to FIG. 5) such as the blower 56 is operated in a state where the furnace
cover 27 is closed, the internal pressure of the slag holding furnace 2 is negative.
When the internal pressure of the slag holding furnace 2 is negative, the slag holding
furnace 2 functions as an exhaust path for the exhaust gas produced from the electric
furnace 1. That is, as indicated by an arrow in FIG. 3, the exhaust gas containing CO,
H2, and the like produced due to the reduction treatment in the electric furnace 1 flows
into the furnace body 20 of the slag holding furnace 2, in which a negative internal
pressure is maintained, through the slag pouring port 14 of the electric furnace 1 and
the pouring hole portion 21 of the slag holding furnace 2. The negative internal
pressure of the slag holding furnace 2 is maintained. Therefore, even when external
air is introduced through the gap of the connection portion between the electric furnace
1 and the slag holding furnace 2, the exhaust gas in the electric furnace 1 does not leak
to the outside through the gap. Further, the exhaust gas flowing into the slag holding
furnace 2 is discharged from the gas discharge port 25 through the furnace body 20.
In this way, the exhaust gas discharged from the slag holding fi.Irnace 2 is treated by an
exhaust gas treatment facility (not shown) described below.
[0064]
- 26 -
In addition, a tilting device 40 is provided in a lower portion of the furnace
body 20 of the slag holding fi.unace 2. The tilting device 40 has a fi.mction of tilting
the slag holding furnace 2 toward the pouring hole pmiion 21 side to pour the molten
slag 4 from the inside of the furnace body 20 into the electric furnace 1 tlu·ough the
pouring hole pmiion 21. This tilting device 40 includes a cylinder 41, support
members 42 and 43, a tilting shaft 44, and a carriage 45.
[0065]
The cylinder 41 is configured of a hydraulic cylinder and generates power for
tilting the slag holding furnace 2. An upper end of the cylinder 41 is connected to a
position on the lower wall 22 of the furnace body 20 which is distant liom the electric
furnace I such that the slag holding fi.trnace 2 can be tilted toward the electric furnace
I side. A lower end of the cylinder 41 is connected to the top surface of the carriage
45. The tilting shaft 44 is provided below the pouring hole portion 21 of the slag
holding furnace 2 and functions as a central shaft of the tilting operation of the slag
holding furnace 2.. The support members 42 and 43 are connected to each other so as
to be pi votable around the tilting shaft 44. An upper end of the suppoti member 42 is
connected to a lower portion of the pouring hole pmiion 21. A lower end of the
support member 43 is connected to the top surface of the carriage 45. The slag
holding furnace 2 is tiltably supported by the cylinder 41, the support members 42 and
43, and the tilting shaft 44.
[0066]
Using the tilting device 40 having the above-described structure, the slag
holding furnace 2 can be tilted centering on the tilting shaft 44. As a result, the
posture of the slag holding furnace 2 can be changed to any one of the holding posture
(FIG. 3) and the pouring posture (FIG. 4). When the posture of the slag holding
- 27 -
furnace 2 is maintained at the holding posture, as shown in FIG. 3, the molten slag 4 is
held in the furnace body 20 without being poured from the slag holding furnace 2 into
the electric furnace 1. On the other hand, when the posture of the slag holding
furnace 2 is maintained at the pouring posture, as shown in FIG. 4, the molten slag 4 is
poured Ji'om the slag holding furnace 2 into the electric Jhrnace 1.
[0067]
When the posture of the slag holding furnace 2 is changed from the holding
posture to the pouring posture, the slag holding furnace 2 is tilted toward the electric
furnace 1 centering on the tilting shaft 44 by extending the cylinder 41 to lift up a rear
p011ion of the furnace body 20. As a result, as shown in FIG. 4, the position of the
pouring hole portion 21 is lower than the furnace body 20. Therefore, the molten slag
4 held in the furnace body 20 flows to the pouring hole portion 21 side and is poured
from the pouring hole 29 into the electric furnace 1 through the slag pouring path 28.
At this time, the pouring rate of the molten slag 4 can be adjusted by controlling the
extension length of the cylinder 41 to adjust the tilting angle of the slag holding
furnace 2.
[0068]
On the other hand, when the posture of the slag holding furnace 2 is changed
from the pouring posture to the holding posture, the height of the furnace body 20 on
the cylinder side returns to the height of the holding posture by shrinking the cylinder
41. As a result, as shown in FIG. 3, the position of the pouring hole portion 21 is
higher than the furnace body 20, and the liquid level of the molten slag 4 in the furnace
body 20 is lower than the slag pouring path 28. Therefore, the molten slag 4 is held
in the furnace body 20 without being poured into the electric furnace 1.
[0069]
- 28 -
In addition, the carriage 45 movably supports the tilting device 40. By
moving the slag holding furnace 2 backward or forward using the carriage 45, the
inspection, exchange, repair, and the like of the slag holding furnace 2 can be easily
performed.
[0070]
-By tilting the slag holding furnace 2 using the tilting device 40 as described
above, the molten slag 4 can be intermittently poured into the electric furnace 1, or the
pouring rate thereof can be adjusted. When the molten slag 4 is poured into the
electric furnace 1, it is preferable that the molten slag 4 is intermittently poured while
appropriately adjusting the pouring rate of the molten slag 4 (that is, the tilting angle of
the slag holding furnace 2) using the tilting device 40 such that the poured molten slag
4 does not. overflow due to a rapid reaction with the molten iron in the electric furnace
1. When the pouring rate of the molten slag 4 is fast during the pouring of the molten
slag 4, slag foaming occurs in the electric furnace 1, which may cause overflowing to
occur. In this case, it is preferable that the pouring of the molten slag 4 is temporarily
stopped by reducing the tilting angle of the slag holding furnace 2 using the tilting
device 40 or that the reaction between the molten slag 4 and the molten iron in the
electric furnace 1 is limited by reducing the pouring rate of the molten slag 4.
[0071]
In addition, the pouring rate of the molten slag 4 per unit time using the slag
holding furnace 2 is determined according to the reduction treatment capability of the
electric furnace 1. The reduction treatment capability of the electric furnace 1
depends on the electricity supply per unit time to the electric furnace 1, for example,
electricity consumed when a current flows by applying a voltage between the upper
electrode 15 and the furnace bottom electrode 16 in the electric furnace 1. Therefore,
- 29 -
the pouring rate of the molten slag 4 per unit time may be determined based on electric
energy which is calculated based on an electric power consumption rate required for
the reduction treatment of the molten slag 4, a voltage applied between the upper
electrode 1 5 and the furnace bottom electrode 16, and a cunent flowing between the
electrodes.
[0072]
An oxygen gas supply nozzle 51 shown in FIGS. 3 and 4 will be described
below in detail as the configuration ofthe exhaust gas treatment facility.
[0073]
[1.4. Configuration of Exhaust Gas Treatment Facility]
Next, the exhaust gas treatment facility which is incidental to the slag
treatment facility will be described with reference to FIG. 5. FIG. 5 is a schematic
diagram showing a configuration of the exhaust gas treatment facility according to the
embodiment.
[0074]
As shown in FIG. 5, THE exhaust gas treatment facility SO includes: the
oxygen gas supply nozzle 51 that is provided in the slag holding furnace 2; the exhaust
gas pipe 55 that is connected to the gas discharge port 25 of the slag holding furnace 2;
the blower 56 that sucks the exhaust gas in the slag holding furnace 2 though the
exhaust gas pipe 55; and a dust collector 57 that is provided at an end point of the
exhaust gas pipe 55 after. the blower 56. The blower 56 is an example of the suction
device according to the embodiment of the present invention. In another embodiment,
a suction device other than the blower 56 may be used.
[0075]
As described above, exhaust gas g 1 containing CO and the like, which are
- 30 -
produced by the reduction reaction of iron oxide in the electric fumace I, is caused to
flow into the slag holding furnace 2 tln·ough the slag pouring port I 4 of the electric
furnace I. The oxygen gas supply nozzle 5 I is an oxygen supply unit that supplies
oxygen gas into the slag holding furnace 2. As a result, in the slag holding furnace 2,
combustion (oxidation reaction) based on the following reaction formula (2) occurs
such that CO is changed into C02• Here, the supply rate of oxygen gas using the
oxygen gas supply nozzle 51 is appropriately controlled according to the emission rate
of CO gas in the electric furnace I. As a result, CO gas which is a combustible
component in the exhaust gas g I can be completely burned. C02 gas which is
produced by completely burning CO gas contained in the exhaust gas gl is discharged
as exhaust gas g2 from the gas discharge port 25 into the exhaust gas pipe 55.
2CO+Or->2COz ... (2)
[0076]
In the embodiment, in order to completely burn CO gas in the exhaust gas gl,
an analyzer 52 is provided at a position of the exhaust gas pipe 55 adjacent to the gas
discharge p01t 25 of the slag holding furnace 2. This analyzer 52 is connected to a
concentration indicating controller 53. The analyzer 52 analyzes components of the
exhaust gas g2 in the exhaust gas pipe 55 to calculate the CO concentration and the 0 2
component. The concentration indicating controller 53 controls the supply rate of
oxygen gas to the oxygen gas supply nozzle 51 according to the CO concentration and
the Oz concentration measured by the analyzer 52. More specifically, the
concentration indicating controller 53 controls the supply rate of oxygen gas to the
oxygen gas supply nozzle 51 using a valve 54 or the like such that the CO
concentration in the exhaust gas pipe 55 is substantially 0% and that the 0 2
concentration in the exhaust gas pipe 55 is a value which is higher than 0% and is as
- 31 -
close to 0% as possible.
[0077]
For example, when the CO concentration measured by the analyzer 52 is
higher than 0%, the concentration indicating controller 53 increases the supply rate of
oxygen gas to the oxygen gas supply nozzle 51. As a result, CO gas is completely
bumed in the slag holding furnace 2 and is prevented from flowing into the exhaust gas
pipe 55. In addition, when the 0 2 concentration measured by the analyzer 52 is
higher than 0% and exceeds a predetermined allowable range, the concentration
indicating controller 53 reduces the supply rate of oxygen gas to the oxygen gas supply
nozzle 51. As a result, the slag holding furnace 2 is prevented from being
unnecessarily cooled by the supply of an excess amount of oxygen gas. For example,
it is preferable that the allowable range ofthe 0 2 concentration be set to be 5% or
lower.
[0078]
When the molten slag 4 starts to be poured from the slag holding furnace 2
into the electric furnace 1, or when the pouring rate of the molten slag 4 increases, the
concentration indicating controller 53 may increase the supply rate of oxygen gas to
the oxygen gas supply nozzle 51 to prepare for an increase in the CO gas produced
from the electric fumace 1. . Information relating to the pouring rate of the molten slag
4 may be provided to the concentration indicating controller 53, for example, ii"01n a
control unit (not shown) for controlling the tilting angle of the slag holding furnace 2
to control the pouring rate of the molten slag 4. In addition, instead of the
concentration indicating controller 53, an operator which monitors an output value of
the analyzer 52 and a pouring state of the molten slag 4 may manually operate the
oxygen gas supply nozzle 51 to control the supply rate of oxygen gas as described
- 32 -
above.
[0079]
The oxygen gas supplied from the oxygen gas supply nozzle 51 is an example
of the oxygen-containing gas according to the embodiment of the present invention.
The oxygen-containing gas may be gas containing oxygen, for example, oxygen gas
containing only oxygen as in the case of the embodiment or mixed gas containing
oxygen gas and another gas (for example, nitrogen gas).
[0080]
As described above, the exhaust gas gl produced fi·om the electric furnace 1 is
discharged into the slag holding furnace 2, and the exhaust gas g2 in the slag holding
furnace 2 is sucked by the blower 56 tlu·ough the exhaust gas pipe 55. The internal
pressure of the electric furnace 1 is adjusted to be negative by the blower 56 sucking a
sufficient amount of exhaust gas g3 on an exit side of the exhaust gas pipe 55. As
described above, in order to prevent the exhaust gas g1 containing CO and dust from
leaking and to prevent an excess amount of dust from being sucked into the slag
holding furnace 2 or the exhaust gas pipe such as the exhaust gas pipe 55, it is
preferable that a negative internal pressure of the electric furnace 1 be maintained
within an appropriate range. However, the emission rate of the exhaust gas g1 in the
electric furnace l varies depending on, for example, the pouring rate of the molten slag
4 or the progress of the reduction treatment. Therefore, it is necessary to adjust the
internal pressure of the electric furnace 1 according to the emission rate of the exhaust
gas gl.
In the embodiment, a slit 58 is provided in the middle of the exhaust gas pipe
55 as a unit that adjusts the internal pressure of the electric furnace 1 to be negative in
an appropriate range under the above-described conditions.
- 33 -
[0081]
The slit 58 is an opening portion which is formed by cutting the entire
periphery of the exhaust gas pipe 55 or a portion of the entire periphery into a slit
shape. In the slit 58, the exhaust gas g2 in the exhaust gas pipe 55 is in contact with
external air. Since the negative intemal pressure of the exhaust gas pipe 55 is
maintained in the exhaust gas pipe 55 by the blower 56, external air (symbol air1 in
FIG. 5) flows into the exhaust gas pipe 55 through the slit 58. Accordingly, the
exhaust gas g3, which is sucked by the blower 56 in an exhaust gas pipe 55b of the rear
stage of the slit 58, contains: the exhaust gas g2 which has been discharged from the
slag holding furnace 2 through the exhaust gas pipe 55a of the front stage of the slit 58;
and the external air air1 which has flown from the slit 58. The slit 58 is formed with
a sufficiently small width (opening area) in which the negative internal pressure of the
exhaust gas pipe 55 can be maintained.
[0082]
Here, it was verified from an experiment of the present inventors that the flow
rate of the external air air1 flowing from the slit 58 into the exhaust gas pipe 55 varies
complementarily to the flow rate of the exhaust gas g2 flowing to the slit 58 through
the inside of the exhaust gas pipe 55a. For example, in a case where the air intake
rate of the exhaust gas g3 using-the blower 56 is 100 Nm3/h, when the flow rate of the
exhaust gas g2 is 80 Nm3/h, the flow rate of the external air air 1 is 20 Nm3 /h. In
addition, in the same case, when the flow rate ofthe exhaust gas g2 is 70 Nm3 /h, the
flow rate of the external air air! is 30 Nm3/h.
[0083]
When the emission rate of the exhaust gas g 1 in the electric furnace 1
increases due to the action of the slit 58, the flow rate of the exhaust gas g2 flowing
- 34 -
through the exhaust gas pipe 55a also increases. Therefore, the flow rate of the
external air air! flowing from the slit 58 decreases. Therefore, most of the suction
force of the exhaust gas g3 obtained by the blower 56 functions as the suction force of
the exhaust gas g2. As a result, a high capability to exhaust the exhaust gas g1 from
the electric furnace I can be maintained. Therefore, when the amount of the exhaust
gas g1 increases irrespective of conditions under which the suction force of the blower
56 is constant, an increase in the internal pressure of the electric furnace 1 can be
prevented. On the other hand, when the emission rate of the exhaust gas g1 in the
electric fumace 1 decreases, the flow rate of the exhaust gas g2 flowing tlu·ough the
exhaust gas pipe 55a also increases. Therefore, the flow rate of the external air air!
flowing from the slit 58 increases. Therefore, most of the suction force of the exhaust
gas g3 obtained by the blower 56 is distributed to the exhaust gas g2 and the external
air air!. As a result, the capability to exhaust the exhaust gas g1 from the electric
furnace 1 can be limited. Therefore, when the amount of the exhaust gas g 1
decreases irrespective of conditions under which the suction force of the blower 56 is
constant, a decrease in the internal pressure of the electric furnace 1 can be prevented.
As described above, in the exhaust gas treatment facility 50 according to the
embodiment, a substantially constant negative internal pressure of the electric furnace
1 can be maintained.
[0084]
On the other hand, by providing a damper in, for example, the exhaust gas
pipe 55 instead ofthe slit 58, the air intake rate of the exhaust gas using the blower 56
can be adjusted. However, in this case, complicated control of finely adjusting the
opening of the damper according to the emission rate of the exhaust gas g 1 is necessary.
In the embodiment, the external air air! is introduced by providing an opening portion
- 35 -
such as the slit 58 in the middle of the exhaust gas pipe 55. As a result, the air intake
rate of the exhaust gas g2 using the blower 56 is adjusted. As described above, the
flow rate of the external air airl flowing from the slit 58 is automatically adjusted
according to the flow rate of the exhaust gas g2. Therefore, control of finely
changing the opening ofthe slit 58 is unnecessary.
[0085]
In the above description of the embodiment of the present invention, the slit
58 provided through the entire periphery of the exhaust gas pipe 55 has been described
as an example of the opening portion through which the external air air I is introduced
into the exhaust gas pipe 55. However, the examples of the opening portion are not
limited to the slit 58. For example, in another embodiment, a hole having an arbitrary
shape such as a circular shape or a rectangular shape may be provided as an opening
portion through a portion of the peripheral surface of the exhaust gas pipe 55, for
example, a range of 1/3 or 1/4 of the entire periphery.
[0086]
[2. Second Embodiment]
Next, an exhaust gas treatment facility according to a second embodiment of
the present invention will be described. The configurations of the second
embodiment are substantially the same as those of the first embodiment except for
configurations described below. Therefore, a detailed description of the same
components as those of the first embodiment will not be repeated.
[0087]
[2. I. Configuration of Exhaust Gas Treatment Facility]
First, the exhaust gas treatment facility according to the embodiment
invention will be described with reference to FIG. 6. FIG. 6 is a schematic diagram
- 36 -
showing a configuration of the exhaust gas treatment facility according to the
embodiment.
[0088]
As shown in FIG. 6; in the exhaust gas treatment facility 60, not only the slit
58 but also a sleeve 61 are provided in the middle of the exhaust gas pipe 55. The
sleeve 61 is provided around the exhaust gas pipe 55 and slides along an axial direction
of the exhaust gas pipe 55 so as to cover at least a pmiion of the slit 58. As the sleeve
61 slides to cover the slit 58, the width of the slit 58 is narrowed, and the area of an
opening pmiion formed by the slit 58 decreases. Conversely, as the sleeve 61
covering the slit 58 slides to open the slit 58, the width of the slit 58 is widened, and
the area of an opening portion formed by the slit 58 increases. In this way, in the
embodiment, the sleeve 61 functions as an opening area changing unit that changes the
area of the opening portion formed by the slit 58.
[0089]
For example, when the inner diameter of the exhaust gas pipe 55 is 700 mm,
the area of the slit 58 covered with the sleeve 61 is the smallest, and when the slit 58 is
fully opened (opening: 100%), the width of the slit 58 is about 300 mm. When the
sleeve 61 slides and gradually covers the slit 58 from the above state, the width of the
slit 58 can be adjusted to be, for example, within a range of 50 mm to 300 mm. In
this example, in order to secure a clearance between the sleeve 61 and an end portion
of the exhaust gas pipe 5 Sa, the minimum width of the slit 58 is set to be not 0 nnn but
50 mm. However, in another embodiment, the sleeve 61 may fully cover the slit 58
so as to adjust the width of the slit 58 to be 0 mm. In addition, in FIG. 6, the sleeve
61 is provided on the exhaust gas pipe 55b side. However, the sleeve 61 may be
provided on the exhaust gas pipe 55a side.
- 37 -
[0090]
As described above in the first embodiment, by providing the slit 58, the
internal pressure of the electric furnace 1 is adjusted according to a variation in the
emission rate of the exhaust gas g 1 in the electric furnace 1. However, when the
width of the slit 58 is fixed as in the case of the first embodiment, there is a limit in the
allowable variation range in the emission rate of the exhaust gas gl. · For example, it
is assumed that, in a case where the air intake rate of the exhaust gas g3 using the
blower 56 is 100 Nm3/h, when the flow rate of the exhaust gas g2 flowing through the
exhaust gas pipe 55a is about 70 Nm3/h to 80 Nm3/h as described above in the first
embodiment, the internal pressure of the electric furnace 1 can be automatically
adjusted to be constant without changing the width of the slit 58. According to this
assumption, when the emission rate of the exhaust gas g 1 varies more largely (for
example, according to the assumption, when the flow rate of the exhaust gas g2
decreases to about 50 Nm3/h by the emission rate of the exhaust gas gl being largely
decreased), the flow rate of the external air air! flowing fi·om the slit 58 does not
exceed 50 Nm3/h. Accordingly, when the emission rate of the exhaust gas gl varies
largely, the suction force of the exhaust gas g3 using the blower 56 is concentrated on
the exhaust gas g2. Thus, the capability to exhaust the exhaust gas g 1 from the
electric furnace 1 is excessive, and there is a problem in that the internal pressure of
the electric furnace 1 decreases more than necessary.
[0091]
Therefore, in the embodiment, in the above-described case, the sleeve 61 is
slid such that the width of the slit 58 is widened and a larger amount ofthe external air
airl (in the above-described example, about 50 Nm3 /h) temporarily flows. As a result,
the internal pressure of the electric furnace 1 is prevented from decreasing more than
- 38 -
necessary. Next, when the flow rate of the exhaust gas g2 recovers to be, for example,
about 70 Nm3/h to 80 Nm3/h, the sleeve 61 is slid again such that the width of the slit
58 is narrowed and the flowing of the external air airl from the slit 58 is limited. As
a result, the capability to exhaust the exhaust gas gl from the electric furnace 1 is
maintained to be high, and thus the internal pressure of the electric furnace 1 can be
prevented fi·om increasing.
[0092]
In the embodiment, in order to adjust the width of the slit 58 as described
above, a pressure gauge 62 (pressure detecting unit) is provided in the electric furnace
1. The pressure gauge 62 is connected to the pressure indicating controller 63. The
pressure gauge 62 measures the internal pressure of the electric furnace 1. The
pressure indicating controller 63 controls the width of the slit 58 by sliding the sleeve
61 according to the internal pressure of the electric furnace 1 measured by the pressure
gauge 62. More specifically, when the internal pressure of the electric furnace 1 is
high, the pressure indicating controller 63 narrows the width of the slit 58 by
controlling a driving unit (not shown) to slide the sleeve 61. As a result, an increase
in the internal pressure of the electric furnace 1 is limited. In addition, when the
internal pressure of the electric furnace 1 is low, the pressure indicating controller 63
widens the width ofthe slit 58 by controlling the a driving unit to slide the sleeve 61.
As a result, a decrease in the internal pressure of the electric furnace 1 is limited. A
speci fie example of the sleeve control using the pressure indicating controller 63 will
be described below.
[0093]
When the molten slag 4 starts to be poured from the slag holding furnace 2
into the elec!ric furnace 1, or when the pouring rate of the molten slag 4 into the
- 39 -
electric furnace I increases, the pressure indicating controller 63 may slides the sleeve
61 and narrow the width of the slit 58 to prepare for an increase in the exhaust gas gl
produced from the electric furnace I. Information relating to the pouring rate of the
molten slag 4 may be provided to the pressure indicating controller 63, for example,
from a control unit (not shown) for controlling the tilting angle of the slag holding
furnace 2 to control the pouring rate.ofthe molten slag 4 .. Alternatively, instead of the
pressure indicating controller 63, an operator which monitors a measured value of the
pressure gauge 62 and a pouring state of the molten slag 4 may manually operate the
sleeve 61 to adjust the width of the slit 58 as described above.
[0094]
Fmther in the exhaust gas treatment facility 60, an external air introduction
pmt 64 may be provided through the exhaust gas pipe 55b provided between the slit 58
and the blower 56. Since the negative internal pressure of the exhaust gas pipe 55b is
maintained by the suction force of the blower 56, external air (air2) flows into the
exhaust gas pipe 55b through the external air introduction pmt 64. This external air
air2 is mixed with the exhaust gas g3 flowing through the exhaust gas pipe 55b, and
thus the exhaust gas g3 is cooled. Due to the action of the external air introduction
port 64, the temperature of the exhaust gas g3 flowing to the dust collector 57 tlu·ough
the blower 56 can be decreased to be within an appropriate range. Howeve1~ the
temperature of the exhaust gas g3 flowing tlu·ough the inside of the exhaust gas pipe
55b varies depending on the emission rate of the exhaust gas gl in the electric furnace
1, the flow rate of the external air air! flowing from the slit 58, and the like. The
amount of the external air air2 required to cool the exhaust gas g3 to an appropriate
temperature also varies depending on the emission rate of the exhaust gas g1, the flow
rate of the external air air 1, and the like.
- 40 -
[0095]
Therefore, a damper 65 for adjusting the flow rate of the external air air2 is
provided in the external air introduction port 64. At an exit of the exhaust gas pipe
55b on the blower 56 side, a thermometer 66 (temperature detecting unit) which
detects the temperature of the exhaust gas g3 in the exhaust gas pipe 55b is provided.
The opening of the damper 65 is controlled by a temperature indicating controller 67
connected to the thermometer 66. The damper 65 and the temperature indicating
controller 67 function as an external air flow rate control unit that controls the flow
rate of the external air air2, which is introduced through the external air introduction
port 64, depending on the temperature ofthe exhaust gas g3. More specifically, when
the temperature of the exhaust gas g3 in the exhaust gas pipe 55b is high, the
temperature indicating controller 67 controls the damper 65 such that the opening of
the damper 65 increases. As a result, the flow rate of the external air air2 increases,
which promotes the cooling of the exhaust gas g3. In addition, when the temperature
of the exhaust gas g3 is low, the temperature indicating controller 67 controls the
damper 65 such that the opening of the damper 65 decreases. As a result, the flow
rate of the external air air2 decreases, which limits the cooling of the exhaust gas g3.
Alternatively, the damper 65 may be completely closed to stop the flowing of the
external air air2 to the exhaust gas pipe 55b. In a case where the exhaust gas g3 is
sufficiently cooled without the introduction of the external air air2, it is preferable that,
when the temperature of the exhaust gas g3 is increased again by reducing the flow
rate of the external air air2, the external air air2 is caused to flow into the exhaust gas
pipe 55b so as to cool the exhaust gas g3. A specific example of the damper control
using the temperature indicating controller 67 will be described below.
[0096]
- 41 -
In addition, as in the case of other controllers, when the molten slag 4 starts to
be poured from the slag holding furnace 2 into the electric fiJrnace 1, or when the
pouring rate of the molten slag 4 into the electric furnace I increases, the temperature
indicating controller 67 may adjust the opening of the damper 65 to be large so as to
prepare for an increase in the exhaust gas g 1 produced from the electric furnace 1.
Information relating to the pouring rate of the molten slag 4 may be provided to the
temperature indicating controller 67, for example, from a control unit (not shown) for
controlling the tilting angle of the slag holding furnace 2 to control the pouring rate of
the molten slag 4. Alternatively, instead ofthe temperature indicating controller 67,
an operator which monitors a measured value of the thermometer 66 and a pouring
state of the molten slag 4 may manually operate the damper 65 to adjust the opening of
the damper 65 as described above.
[0097]
Further, in the exhaust gas treatment facility 60, when the external air
introduction port 64 is provided, it is preferable that a damper 68 for adjusting the
suction flow rate using the blower 56 is provided on the front stage (upper stream side)
of the blower 56. The opening of the damper 68 is controlled by a temperature
indicating controller 69 connected to the thermometer 66. More specifically, when
the temperature ofthe exhaust gas g3 in the exhaust gas pipe 55b increases, the
temperature indicating controller 69 controls the damper 68 such that the opening of
the damper 68 increases. As a result, the suction flow rate using the blower 56
increases. In addition, when the temperature of the exhaust gas g3 decreases, the
temperature indicating controller 69 controls the damper 68 such that the opening of
the damper 68 decreases. As a result, the suction flow rate using the blower 56
decreases. In the example of FIG. 6, the temperature indicating controller 67 and the
- 42 -
temperature indicating controller 69 are separately provided but may be integrated into
one controller.
[0098]
That is, when the temperature of the exhaust gas g3 increases, the exhaust gas
g3 expands. Therefore, the gas mass per unit volume decreases. As a result, since a
load on the blower 56 decreases, the suction flow rate using the blower 56 can be
increased. Accordingly, the suction flow rate using the blower 56 can be increased by
increasing the opening of the damper 68.
[0099]
On the other hand, when the temperature of the exhaust gas g3 decreases, the
exhaust gas g3 shrinks. Therefore, the gas mass per unit volume increases. As a
result, a load on the blower 56 increases. In order to decrease the suction flow rate
using the blower 56, it is important to decrease the suction flow rate using the blower
by decreasing the opening of the damper 68 using the blower 56.
[0100]
[2.2. Example of Control Method]
(Control ofinternal Pressure of Electric Furnace)
FIG. 7 is a flowchart showing an example of a control method of the pressure
indicating controller 63 according to the second embodiment of the present invention.
As described above, the pressure indicating controller 63 adjusts the width of the slit
58 by sliding the.s1eeve 61 according to the internal pressure of the electric furnace 1
measured by the pressure gauge 62.
[0101]
As shown in FIG. 7, first, the pressure indicating controller 63 determines
whether or not the internal pressure of the electric furnace 1 exceeds a predetermined
- 43 -
upper limit value (Step SIOI). Here, when the internal pressure of the electric
furnace 1 exceeds the upper limit value, the pressure indicating controller 63 slides the
sleeve 61 to narrow the width of the slit 58 (Step S103). Therefore, the flow rate of
the external air air! flowing from the slit 58 decreases. As a result, since the
capability to exhaust the exhaust gas gl increases, the internal pressure of the electric
furnace I can be adjusted such that the internal pressure of the electric furnace 1 does
not exceed the upper limit value.
[0102]
When the internal pressure of the electric furnace 1 does not exceed the upper
limit value in Step SIOI, the pressure indicating controller 63 determines whether or
not the internal pressure of the electric furnace 1 falls below a predetermined lower
limit value (Step S 1 05). Here, when the internal pressure of the electric furnace 1
falls below the lower limit value, the pressure indicating controller 63 slides the sleeve
61 to widen the width ofthe slit 58 (Step S107). Therefore, the flow rate of the
external air air! flowing from the slit 58 increases. As a result, since the capability to
exhaust the exhaust gas gl is limited, the internal pressure ofthe electric furnace 1 can
be adjusted such that the internal pressure of the electric furnace 1 does not fall below
the lower limit value.
[0103]
When the internal pressure of the electric furnace 1 does not fall below the
lower limit value in Step Sl05,that is, when the internal pressure of the electric
furnace 1 is maintained in an appropriate range between the upper limit value and the
lower limit value, the pressure indicating controller 63 fixes the sleeve 61 and
maintains the width of the slit 58.
[0104]
- 44 -
(Control of Amount of External Air for Cooling Exhaust Gas)
FIG. 8 is a flowchart showing an example of a control method of the
temperature indicating controller 67 according to the second embodiment of the
present invention, As described above, the temperature indicating controller 67
adjusts the opening of the damper 65, which is provided in the external air introduction
pmi 64, according to the temperature ofthe exhaust gas g3 in the exhaust gas pipe 55b
measured by the thermometer 66.
[0105]
As shown in FIG. 8, first, the temperature indicating controller 67 determines
whether or not the temperature of the exhaust gas g3 exceeds a predetermined upper
limit value (Step S201 ). Here, when the exhaust gas temperature exceeds the upper
limit value, the temperature indicating controller 67 opens the damper 65 (Step S203).
Therefore, the flow rate of the external air air2 flowing from the external air
introduction pmi 64 increases. As a result, since the exhaust gas g3 is cooled by a
larger amount of the external air air2, the temperature of the exhaust gas g3 can be
adjusted such that the temperature of the exhaust gas g3 does not exceed the upper
limit value.
[0106]
As described above, when an increase in the temperature of the exhaust gas g3
is detected by the thermometer 66, the temperature indicating controller 69 controls the
damper 68 such that the opening of the damper 68 provided on the front stage of the
blower 56 increases. That is, when it is determined that the temperature of the
exhaust gas g3 in Step S201 exceeds the upper limit value, the opening of the damper
68 increases.
[0107]
- 45 -
~I
In addition, the exhaust gas g3 is cooled by the damper 65 being opened in
Step S203. That is, when an increase in the temperature of the exhaust gas g3 is
detected by the thermometer 66, the temperature indicating controller 67 controls the
damper 65 such that the opening of the damper 65 increases. Based on the result of
measuring the temperature of the exhaust gas g3 which is obtained from the
thermometer 66 by the operator, the damper 65 may be manually operated such that the
opening of the damper 65 is an appropriate value.
[0108]
When the temperature of the exhaust gas g3 does not exceed the upper limit
value in Step S20 I, the temperature indicating controller 67 fmther determines whether
or not the temperature of the exhaust gas g3 falls below a predetermined lower limit
value (Step S205). Here, when the temperature of the exhaust gas g3 falls below the
lower limit value, the temperature indicating controller 67 closes the damper 65 (Step
S207). Therefore, the flow rate of the external air air2 flowing from the external air
introduction port 64 decreases. As a result, since the effect of cooling the exhaust gas
g3 decreases, the temperature of the exhaust gas g3 cari be adjusted such that the
temperature of the exhaust gas g3 does not fall below the lower limit value.
[0109]
When the temperature of the exhaust gas g3 does not fall below the lower
limit value in Step S205, that is, when the temperature of the exhaust gas g3 is
maintained in an appropriate range between the upper limit value and the lower limit
value, the temperature indicating controller 67 maintains the opening ofthe damper 65.
[0110]
As described above, in the second embodiment, the sleeve 61 which can
change the width of the slit 58 is provided. As a result, even when a variation in the
- 46 -
emission rate of the exhaust gas gl is large, the internal pressure of the electric furnace
I can be adjusted to be an appropriate value. In the second embodiment, even a
variation in the emission rate of the exhaust gas gl is small, the internal pressure of the
electric furnace I can be automatically adjusted in a state where the width of the slit 58
is fixed as in the case of the first embodiment. Therefore, the emission rate of the
exhaust gas gl varies largely, and only when the internal pressure of the electric
furnace I actually statts to increase, the sleeve 61 may be slid to change the width of
the slit 58. Accordingly, for example, as compared to a case where the air intake rate
of the exhaust gas is adjusted using the damper or the like, the internal pressure of the
electric furnace I can be significantly easily controlled. In addition, even when the
emission rate of the exhaust gas gl and the flow rate of the external air air! flowing
from the slit 58 varies largely, the exhaust gas g3 cooled to an appropriate temperature
can be discharged from the blower 56 to the dust collector 57 by changing the opening
of the damper 65 provided in the external air introduction port 64.
[0111]
In the second embodiment, as an example of the opening area changing unit,
the sleeve 61 for adjusting the width ofthe slit 58, which is provided through the entire
periphery of the exhaust gas pipe 55, is used. However, the examples of the opening
area changing unit are not limited to the sleeve 61. For example, in another
embodiment, a slide cover may be provided to cover at least a part of a hole (opening
pmtion) having an arbitrary shape such as a circular shape or a rectangular shape
which is provided through a pmtion of the peripheral surface of the exhaust gas pipe
55, for example, a range of l/3 or 1/4 of the entire periphery. This cover can adjust a
proportion of the hole by being slid, for example, in a peripheral direction of the
exhaust gas pipe 55 or in an axial direction of the exhaust gas pipe 55.
- 47 -
~I
[0 112]
In addition, in FIG. 6, the concentration indicating controller 53, the pressure
indicating controller 63, the temperature indicating controller 67, and the temperature
indicating controller 69 are separately shown. Howeve1~ these controllers may be
integrated into one controller by, for example, using a computer.
In addition, it is preferable that the slit 58 and the sleeve 61 is arranged at a
position of the exhaust gas pipe 55 which is as close to the slag holding furnace 2 as
possible. As a result, control responsiveness of the internal pressure of the electric
furnace I can be improved. Fmiher, when the slit 58 is arranged at a position of the
exhaust gas pipe 55 close to the slag holding furnace 2, the exhaust gas gl having a
high temperature introduced from the slag holding furnace 2 into the exhaust gas pipe
55 is mixed with the external air air! introduced from the slit 58 into the exhaust gas
pipe 55. As a result, unburned gas contained in the exhaust gas gl can be burned in
the exhaust gas pipe 55.
In addition, the plural slits 58 may be provided along the exhaust gas pipe 55.
In this case, the total opening area of the plural slits 58 may be controlled by extending
a movable range of the sleeve 61 to control the position of the sleeve 61. In addition,
the total opening area of the plural slits 58 may be controlled by providing the sleeves
61 corresponding to. the plural slits 58 to control the position of each of the sleeves 61.
[Examples]
[0113]
Next, an example of the present invention will be described. The following
example is merely a condition example which is adopted to verify the operability and
effects of the present invention, and the present invention is not limited to conditions
of the following example.
- 48 -
[0114]
In the example of the present invention, a closed direct current electric
furnace was used as the electric furnace 1. As the molten slag 4, molten slag
discharged from a converter was used. The fluid molten slag 4 in a state of being
melted was poured into the slag holding furnace 2. Further, in the electric furnace 1,
the molten iron layer 6 formed of about 130 tons of molten steel was formed, and the
molten slag layer 5 having a thickness of about 200 mm formed of the reduced molten
slag 4 (that is, reducing slag) was present on the molten iron layer 6. Under this
condition, the molten slag 4 was intermittently poured from the slag holding furnace 2
into the molten slag layer 5 of the electric furnace l. More specifically, by changing
the posture of the slag holding furnace 2 fi·om the holding posture to the pouring
posture, a step (slag pouring step) of pouring 8.2 tons to 8.5 tons of the molten slag 4
into the electric furnace I was performed. After the posture of the slag holding
furnace 2 returned to the holding posture, a step (interval step) of maintaining the
holding posture for about 10 minutes was performed. By repeating the slag pouring
step and the interval step, the molten slag 4 in the electric furnace 1 was reduced. As
a result, the molten slag 4 was able to be continuously and stably reduced in the
electric furnace I without causing rapid slag foaming to occur during the slag pouring.
[0115]
(Slag Pouring Step)
FIG. 9A is a graph showing a relationship between an emission rate of exhaust
gas (emission rate of the exhaust gas g1 in the electric furnace 1) and an elapsed time
in the slag pouring step according to the example of the present invention. FIG. 9B is
a graph showing a relationship between a slit width (width of a slit 58) and the elapsed
time in the slag pouring step according to the example of the present invention. FIG.
- 49 -
~I
9C is a graph showing a relationship between an internal pressure of the electric
furnace 1 and the elapsed time in the slag pouring step according to the example of the
present invention. In the initial stage of the slag pouring step, in order to rapidly
progress the reduction reaction; as shown in FIG. 9A, the emission rate of the exhaust
gas g1 in the electric furnace 1 continuously increased from the start of the treatment to
a time tl. As a result, as shown in FIG. 9C, the internal pressure of the electric
furnace 1 reached a predetermined upper limit value (-10 Pa) at the time tl.
Therefore, the pressure indicating controller 63 slid the sleeve 61 such that the width
(opening) of the slit 58 was narrowed from 40% to 30% as shown in FIG. 9B.
Therefore, the flowing of the external air air! in the slit 58 was limited, and thus the
capability to exhaust the exhaust gas g1 using the blower 56 increased. As a result, as
shown in FIG. 9C, after the time tl, the internal pressure of the electric furnace 1
decreased from the upper limit value and then was maintained at a substantially
constant value (-20 Pa). In this way, as the internal pressure of the electric furnace 1
approached the upper limit value, the emission rate of the exhaust gas gl increased.
In this case, by changing the width of the slit 58 from 40% to 30%, the internal
pressure of the electric furnace 1 was able to be automatically adjusted to be the
substantially constant value.
[0116]
However, as shown in FIG. 9A, after the time t1, the emission rate of the
exhaust gas g1 in the electric furnace 1 slatted to gradually decrease and continuously
decreased until a time t2. As a result, as shown in FIG. 9C, the internal pressure of
the electric fhrnace 1 started to decrease from the substantially constant value (-20 Pa)
and reached a predetermined lower limit value (-30 Pa) at the time t2. Therefore, the
pressure indicating controller 63 slid the sleeve 61 such that the width (opening) of the
- 50 -
slit 58 was widened again from 30% to 40% as shown in FIG. 9B. Therefore, the
flowing of the external air air! in the slit 58 was promoted, and thus the capability to
exhaust the exhaust gas g I using the blower 56 was limited. As a result, as shown in
FIG. 9C, after the timd2, the internal pressure of the electric furnace 1 increased from
the lower limit value and then was maintained again at the substantially constant value
( -20 Pa). In this way, as the internal pressure of the electric furnace I approached the
lower limit value, the emission rate of the exhaust gas gl decreased. In this case, by
changing the width of the slit 58 from 30% to 40%, the internal pressure of the electric
furnace 1 was able to be automatically adjusted to be the substantially constant value.
[0 117]
FIG. I OA is a graph showing a relationship between an exhaust gas
temperature (temperature of the exhaust gas g3) and the elapsed time in the slag
pouring step according to the example of the present invention. FIG. lOB is a graph
showing a relationship between a damper opening (opening of the damper 65) and the
elapsed time in the slag pouring step according to the example of the present invention.
As shown in FIG. 9B, in the slag pouring step according to the example of the present
invention, the width (opening) of the slit 58 was narrowed from 40% to 30% at the
time t 1. As a result, the proportion of the external air air 1 contained in the exhaust
gas g3 flowing through the exhaust gas pipe 55b decreased. Therefore, as shown in
FIG. lOA, the temperature of the exhaust gas g3largely increased after the time tl and
reached a predetermined upper limit value (90°C) at a time t3. Accordingly, as shown
in FIG. JOB, the temperature indicating controller 67 changed the opening of the
damper 65 from 50% to 70% at the time t3. Thus, due to an increase in the flow rate
of the external air air2 flowing from the external air introduction port 64, the exhaust
gas g3 was cooled by a larger amount of the external air air2. As a result, as shown in
- 51 -
~I
FIG. lOA, after the time t3, the temperature of the exhaust gas g3 decreased from the
upper limit value and was maintained in an appropriate range of lower than 90°C while
being slightly varied.
[0118]
However, as described above, at the time t2, the width of the slit 58 was
widened again from 30% to 40%. As a result, the proportion of the external air air!
contained in the exhaust gas g3 increased. That is, the exhaust gas g3 was cooled to
some extent by the external air air! flowing from the slit 58 and then was fmther
cooled by the external air air2 flowing fi·om the external air introduction pmi 64.
Therefore, as shown in FIG. lOA, the temperature of the exhaust gas g3 largely
increased after the time t2 and reached a predetermined lower limit value (70°C) at a
time t4. Accordingly, as shown in FIG. 1 OB, the temperature indicating controller 67
returned the opening of the damper 65 from 70% to 50% at the time t4. Thus, due to
a decrease in the flow rate of the external air air2, the exhaust gas g3 was prevented
from being excessively cooled. As a result, as shown in FIG. lOA, after the time t4,
the temperature of the exhaust gas g3 increased from the lower limit value and was
maintained again in an appropriate range of 70°C to 90°C.
[0119]
(Interval Step of Slag Pouring)
FIG. llA is a graph showing a relationship between the emission rate of
exhaust gas (emission rate of the exhaust gas gl in the electric furnace 1) and the
elapsed time in the interval step according to the example of the present invention.
FIG. llB is a graph showing a relationship between the slit width (width of the slit 58)
and the elapsed time in the interval step according to the example of the present
invention. FIG. 11 Cis a graph showing a relationship between the internal pressure
- 52 -
of the electric fhrnace 1 and the elapsed time in the interval step according to the
example of the present invention. After the slag pouring step, the reduction reaction
in the electric furnace 1 was stabilized in the interval step of stopping slag pouring.
However, even in-the intmval step, the reduction reaction was not completely uniform.
Therefore, as shown in FIG. llA, the emission rate of the exhaust gas gl in the electric
furnace 1 slightly varied, On the other hand, as shown in FIG. I I B, the width
(opening) of the slit 58 was fixed 40%. Even in this case, as shown in FIG. llC, the
internal pressnre of the electric furnace 1 measnred by the pressure gauge 62 was
substantially constant at -20 Pa. In this interval step, the opening of the damper 65
was maintained at 50%, and the temperature of the exhaust gas g3 was not largely
changed. Therefore, a relationship between the temperature of the exhaust gas g3 and
the opening of the damper 65 was not shown.
[0120]
From the above results, it was verified that, even when a variation in the
emission rate of the exhaust gas gl in the electric fl.1rnace 1 is relatively large, the
internal pressure of the electric fl.unace I can be adjusted to be substantially constant
by changing the width of the slit 58 depending on the internal pressure of the electric
furnace 1. In addition, it was also verified that, even when the temperature of the
exhaust gas g3 in the exhaust gas pipe 55b varies due to, for example, a variation in the
width of the slit 58, the temperature of the exhaust gas g3 can be adjusted to be
substantially constant by changing the opening of the damper 65 depending on the
temperatnre of the exhaust gas g3. Fmther, it was also verified that, when the
reduction reaction in the electric fl.mmce I was stable and a variation in the emission
rate of the exhaust gas, the internal pressure of the electric fl.1rnace I can be adjusted to
be substantially constant in a state where the width of the slit 58 is fixed.
- 53 -
[0121]
Hereinabove, the preferable embodiments of the present invention have been
described in detail with reference to the accompanying drawings. However, the
present invention is not limited to these embodiments. It is apparent that those having
ordinary skill in the technical field to which the present invention pe1tains can
conceive various alternation examples or modification examples within a scope of
technical ideas described in claims, and it would be understood that these examples
belong to the technical scope of the invention.
[Brief Description of the Reference Symbols]
[0122]
1: ELECTRIC FURNACE
2: SLAG HOLDING FURNACE
3: SLAG LADLE
4: MOLTEN SLAG
5: MOLTEN SLAG LAYER
6: MOLTEN IRON LAYER
14: SLAG POURING PORT
15: UPPER ELECTRODE
16: FURNACE BOTTOM ELECTRODE
17: SLAG HOLE
18:TAPHOLE
50, 60: EXHAUST GAS TREATMENT FACILITY
51: OXYGEN GAS SUPPLY NOZZLE
52: ANALYZER
53: CONCENTRATION INDICATING CONTROLLER
- 54 -
~I
55: EXHAUST GAS PIPE
56: BLOWER
57: DUST COLLECTOR
58: SLIT
61: SLEEVE
62: PRESSURE GAUGE
63: PRESSURE INDICATING CONTROLLER
64: EXTERNAL AIR INTRODUCTION PORT
65:DAMPER
66: THERMOMETER
67: TEMPERATURE INDICATING CONTROLLER
gl, g2, g3: EXHAUST GAS

[Document Type]
What is claimed is:
CLAIMS
1. An exhaust gas treatment method in a slag treatment process in which
molten slag produced in a steelmaking step is charged into a slag holding furnace, the
molten slag is poured from the slag holding furnace into an electric furnace, which
accommodates a molten iron layer and a molten slag layer formed on the molten iron
layer, the molten slag is continuously reduced in the electric furnace, and valuable
materials in the molten slag are collected into the molten iron layer, the method
comprising:
burning a combustible component in exhaust gas by causing the exhaust gas,
which is produced in the electric furnace, to flow into the slag holding fi.!rnace and
supplying oxygen-containing gas into the slag holding furnace;
causing the burned exhaust gas to flow from the slag holding furnace to a
suction device through an exhaust gas pipe;
adjusting an internal pressure of the electric furnace by introducing external
air into the exhaust gas pipe through an opening portion provided in the middle of the
exhaust gas pipe; and
changing an area of the opening portion depending on a variation in the
internal pressure of the electric furnace by using an opening area changing unit
provided in the opening pmiion.
2. The exhaust gas treatment method according to claim 1, fmiher
compnsmg:
cooling the exhaust gas in the exhaust gas pipe by introducing external air into
the exhaust gas .pipe through an external air introduction port provided between the
- 56 -
opening portion and the suction device.
3. The exhaust gas treatment method according to claim 2, fmiher
compnsmg:
changing a flow rate of the external air, which is introduced tluough the
external air introduction port, depending on a variation in temperature of the exhaust
gas in the exhaust gas pipe between the opening portion and the suction device.
4. An exhaust gas treatment facility for a slag treatment process in which
molten slag produced in a steelmaking step is charged into a slag holding furnace, the
molten slag is poured from the slag holding furnace into an electric furnace, which
accommodates a molten iron layer and a molten slag layer formed on the molten iron
layer, the molten slag is continuously reduced in the electric fumace, and valuable
materials in the molten slag are collected into the molten iron layer, the facility
comprising:
an oxygen supply unit that supplies oxygen-containing gas into the slag
holding furnace;
an exhaust gas pipe that is connected to the slag holding furnace;
a suction device that sucks exhaust gas in the slag holding furnace tlu·ough the
exhaust gas pipe;
an opening portion that is provided in the middle of the exhaust gas pipe;
a pressure detecting unit that detects an internal pressure of the electric
furnace; and
an opening area changing unit that changes an area of the opening portion
depending on a variation in the internal pressure of the electric furnace,
- 57 -
wherein the internal pressure of the electric furnace is adjusted by causing
exhaust gas, which is produced in the electric fmna<;e, to flow into the slag holding
fumace, burning a combustible component in the exhaust gas using the oxygencontaining
gas in the slag holding furnace, exhausting the bumed exhaust gas tluough
the exhaust gas pipe, and introducing external air into the exhaust gas pipe tluough the
opening pottion.
5. The exhaust gas treatment facility according to claim 4,
wherein the opening area changing unit includes a sleeve that is provided
around the exhaust gas pipe and slides along a!). axial direction of the exhaust gas pipe
so as to cover at least a portion of the opening portion.
6. The exhaust gas treatment facility according to claim 4 or 5, futther
compnsmg:
an extemal air introduction pott that is provided in the exhaust gas pipe
between the opening portion and the suction device.
\.
7. The exhaust gas treatment facility according to claim 6, further
comprising:
a temperature detecting unit that detects a temperature of exhaust gas in the
exhaust gas pipe between the opening portion and the suction device; and
an extemal air flow rate control unit that controls a flow rate of external air,
which is introduced tlu·ough the external air introduction pott, depending on the ·
detected temperature.