FORM - 2
THE PATENTS ACT, 1970
(39 of 1970)
&
The Patents Rules, 2003


COMPLETE SPECIFICATION
(See Section 10 and Rule 13)
FABRIC TREATMENT METHOD AND COMPOSITION TO IMPART DIFFERENTIAL HYDROPHOBICITY

HINDUSTAN UNILEVER LIMITED, a company incorporated under
the Indian Companies Act, 1913 and having its registered office
at 165/166, Backbay Reclamation, Mumbai -400 020, Maharashtra, India
The following specification particularly describes the invention and the manner in which it is to be performed


WO 2008/058831

PCT/EP2007/061280

- 1 - ■
FABRIC TREATMENT METHOD AND COMPOSITION TO IMPART DIFFERENTIAL HYDROPHOBICITY
5 Technical Field
This invention relates to a method of treating a fabric with a rinse conditioner composition and thereafter subjecting a portion of the fabric to an activation step to cause 10 differential hydrophobicity, encouraging transport of water through the fabric. In one aspect the invention relates to compositions for use in such a method.
Background and Prior Art
15
The uncomfortable feel of clothes associated with - »
perspiration can take one of two forms depending on the level of sweat production. Under conditions of high sweat production, clothes can become saturated with sweat. Damp
20 areas of clothing then contact the skin causing discomfort through local cooling and cling.
Under conditions of low sweat production there is sweat /high humidity in any space between the skin and first layer 25 of clothing and within the clothing immediately adjacent the skin. Water vapour will gradually diffuse through the clothing into the surrounding air.
The textile literature identifies a high humidity level in
30 the space between the skin and the first layer of clothing
as one of the key drivers of discomfort under ambient, low
exercise conditions. Similarly, discomfort can arise from

WO 2008/058831

PCT/EP2007/061280

- 2 -
the build up of liquid water on the inside surface of apparel textiles. A known approach to this problem is to increase the rate of liquid water transport through textile by increasing the rate of wicking or wetting. This is-5 achieved by decreasing the contact angle of water on the fibre surface. This approach has the disadvantage of also increasing the total amount of water held in the textile. This leads to increased thermal conductivity and increased cling when these areas touch the skin. Both of these 10 effects increase the discomfort experienced in wear-It is known that certain materials, such as Zinc Oxide (ZnO) and Titanium Oxide (T1O2) have the ability to change between hydrophobic and hydrophilic properties under different 15 environmental conditions, see for example J. Am. Chem. Soc 2004, 126, 62-63 and Soft Matter 2005, 1, 55-61. There are various publications describing the effect of ZnO and Ti02 as hydrophobic/hydrophilic switchable surfaces. WO2004108S46 describes the use of Ti02 as a coating in combination with a 20 siloxane for an easy c.\ean surface and discloses that it can be applied to fabrics. US2005/0186371 Al discloses a gas permeable apparatus comprising a structure including a plurality of surfaces, at least another of the surfaces comprising electrets, at least one light source for exposing 25 the at least one of the surfaces comprising the
photocatalyst to light photons sufficient to activate the photocatalyst, the structure allowing for filtering particulates, wicking liquids, disinfecting, and deodarizing the surfaces. 30
Photocatalysts such as Ti02 are incorporated into the surfaces of apparel products such as goggles to decompose

WO 2008/058831

PCT/EP2007/061280

- 3 -
and oxidize absorbed chemicals on the photocatalyst surfaces with absorption of light with sufficient- energy to generate and electron hole pair in the photocatalyst. The electron hole pair leads to decomposition on surface contact with 5 water and subsequent reactive chemicals on the surface of the photocatalysts. The coated surfaces also can function as air filters, air vents, wicking surfaces, protective covers, layers, over underlying materials, and act as ultraviolet light protective filters for the underlying 10 materials and body.
The invention provides a method and composition for treating fabric with a rinse conditioner to increase transport of water through the fabric. 15
Summary of the Invention
According to one aspect of the invention there is provided a fabric softening composition comprising a fabric softening 20 compound and from 5 to 50 % by weight, preferably 5 to 25 % by weight of the composition of a material (HH material) capable of changing its hydrophobic./hydrophilic properties in response to an activation step.
25 According to a further aspect of the invention there is provided a method of treating a fabric to enhance the transport of water or water vapour therethrough, the method comprising rinsing the fabric in a composition as described above to deposit fabric conditioner and HH material thereon,
30 drying the fabric and before, after or simultaneously with the drying, subjecting a portion of the fabric tc an activation step to cause H.R material deposited in said

WO 2008/058831

PCT/EP2007/061280

- 4 -
portion to undergo a change in its hydrophobic/hydrophilic properties.
The idea of the invention is to reduce the level of water 5 held in the region of the textile next to the skin, at the same time as facilitating the movement of water through the textile. This is achieved by creating different surface properties on fibres in different regions of the textile (either different regions of the garment, or different sides
10 of the textile). Areas of the textile which are close to the skin are made hydrophobic, while the areas of the textile which are away from the skin are made hydrophilic. In this manner it is possible to increase water transport without increasing the water holding properties of the
15 textile. Increasing water transport_while also decreasing
the amount of water held at the surface of the textile »
closest to the skin provides a beneficial effect. It is possible to maintain comfort for the wearer under conditions of low sweat production i.e. under low exercise conditions, 20 with warm climate etc, or at least delay the outset of
discomfort when the wearer is exposed to such conditions.
The key to this approach is to generate different local
fibre properties following uniform treatment of the textile
25 with a laundry product. By depositing the EH material onto
i-
the HH material is photosensitive and the outside of the garment is exposed to light, particularly UV light,the textile from the laundry treatment, areas which are '
close to the skin can be made hydrophobic, whereas areas of textile away from the skin may be rendered hydrophilic by an activation step. It is preferred the activation step uses 30 local environmental conditions. For example, in a preferred embodiment

WO 2008/058831

PCT/EP2007/061280

- 5 -
and is rendered hydrophilic, whilst the inside of the garment close to the skin and therefore shielded from the sunlight remains hydrophobic.
5 Hydrophobic/Hydrophilic Material
In principle any material which can be deposited on a fabric from a rinse conditioner which can "switch" properties from hydrophobic to hydrophilic or visa versa upon exposure to
10 certain conditions may be employed in the invention. The activation step causing the switch in properties may be based upon photosensitivity, pH change, temperature change, heat flow, change iii ionic strength, enzymatic activity etc. The most convenient activation step is based upon
15 photosensitivity, particularly UV light, since it is readily possible to expose the outside of a garment to sunlight, during wear and or drying, whilst shielding the inside of the garment.
20 Preferred HK materials are ZnO and Ti02 which can be drawn from a range of morphologies, shapes and aspect ratios. Particle linear dimensions should be in the range of 1 nm to 1000 nm.—Other suitable photosensitive materials include those which undergo:
25
1) structural rearrangement to increase nydrophilicity
(e.g. Ketoenol tautomerism or cis-irans isomerism
resulting in breaking intra-molecular hydrogen bonds and favouring inter-molecular hydrogen bonds); or 30
2) degradation to more polar species (e.g. UV unstable
dyes, or sunscreens).

WO 2008/058831

PCT/EP2007/061280

5
The HH materials are generally deposited to apply from 0.2 to 1 %, preferably 0.2 to 0.5 % by weight of the fabric after drying. The HH materials are generally present in an 5 amount of from 5 to 50 %, preferably 5 to 25 % by weight of the fabric softening composition.
Fabric Softening Compound
10 The fabric softening compound is preferably different from the HH material. Suitable fabric softening compounds are described below.
i) Oily sugar derivative 15
The oily sugar derivative is a liquid or soft solid
derivative of a cyclic polyol or of a reduced saccharide,
said derivative resulting from 35 to 100% of the hydroxy!
groups in said polyol or in said saccharide being esterified 20 or etherified. The derivative has two or more ester or
ether groups independently attached to a C8-C22 alkyl or
alkenyl chain.
The oily sugar derivatives of the invention are also 25 referred to herein as "derivative-CP" and "derivative-RS" dependent upon whether the derivative is a product derived from a cyclic polyol or from a reduced saccharide starting material respectively.
30 Preferably the derivative-CP and derivative-RS contain 35% by weight tri or higher esters, e.g. at least 40%.
-8MAY2QQ9I1

WO 2008/058831

PCT/EP2007/061280

_ 7 _
Preferably 35 to 85% most preferably 30 to 80%, even more
preferably 45 to 75%, such as 45 to 70% of the hydroxyl
groups in said cyclic polyol or in said reduced saccharide
are esterified or etherified to produce the derivative-CP
5 and derivative-RS respectively.
For the derivative-CP and derivative-Rs, the tetra, penta etc prefixes only indicate the average degrees of esterification or etherification. The compounds exist as a 10 mixture of materials ranging from the monoester to the fully esterified ester. It is the average degree of esterification as determined by weight that is referred to herein.
15 The derivative-C? and derivative-RS used do not have
substantial crystalline character at 2o°C. Instead they are preferably in a liquid or soft solid state, as hereinbelow defined, at 20°C.
20 The starting cyclic polyol or reduced saccharide material is esterified or etherified with Cs-C22 alkyl or alkenyl chains to the appropriate extent of esterication or etherification so that the derivatives are in the requisite liquid or soft solid state. These chains may contain unsaturation,
25 branching or mixed chain lengths.
Typically the derivative-CP or derivative-RS has 3 or more, preferably 4 or more, for example 3 to 8, e.g. 3 to 5, ester or ether groups or mixtures thereof. it is preferred if two 30 or more of the ester or ether groups of the derivative-CP
and derivative-RS are independently of one another attached

WO 2008/058831

PCT/EP2007/061280

- 8 -
to" a C8 to C22 alkyl or alkenyl chain. The alkyl or alkenyl groups may be branched or linear carbon chains.
The derivative-CPs are preferred for use as the oily sugar 5 derivative. Inositol is a preferred cyclic polyol, and Inositol derivatives are especially preferred.
In the context of the present invention the terms derivative-CP and derivative-RS encompass all ether or ester 10 derivatives of all forms of saccharides, which fall into the above definition, and are especially preferred for use. Examples of preferred saccharides for the derivative-CP and derivative-Rs to be derived from are monosaccharides and disB.ccharid^s.
Examples of monosaccharides include xylose, arabinose, galactose, fructose, sorbose and glucose. Glucose is especially preferred. An example of a reduced saccharide is sorbitan. Examples of disaccharides include maltose, 20 lactose, cellobiose and sucrose. Sucrose is especially preferred.
If the derivative-CP is based on a disaccharide it is preferred if the disaccharide has 3 or more ester or ether 25 groups attached to it. Examples include sucrose tri, tetra and penta esters.
Where the cyclic polyol is a reducing sugar it is advantageous if each ring of the derivative-CP has one ether 30 group, preferably at the C] position. Suitable examples of such compounds include methyl glucose derivatives.

WO 2008/058831 PCT/EP200 7/061280
- 9 - ■
Examples of suitable der-ivative-CPs include esters of" alkyl(poly)glucosides, in particular alkyl glucoside esters having a degree of polymerisation from 1 to 2.
5 The HLB of the derivative-CP and derivative-RS is typically between 1 and 3.
The derivative-CP and derivative-RS may have branched or linear alkyl or alkenyl chains (of varying degrees of 10 branching), mixed chain lengths and/or unsaturation. Those having unsaturated and/or mixed alkyl chain lengths are preferred.
One or more of the alkyl or alkenyl chains (independently 15 attached to the ester or ether groups.) may contain at least one unsaturated bond. '
For example, predominantly unsaturated fatty chains may be attached to the ester/ether groups, e.g. those attached may 20 be derived from rape o:l, cotton seed oil, soybean oil, oleic, tallow, palmitoleic, linoleic, erucic or other sources of unsaturated vegetable fatty acids.
The alkyl or alkenyl chains of the derivative-CP and 25 derivative-RS are preferably predominantly unsaturated, for example sucrose tetratallowate, sucrose tetrarapeate, sucrose tetraoleate, sucrose tetraesters of soybean oil or cotton seed oil, ceilobiose tetraoleate, sucrose trioleate, sucrose triapeate, sucrose pentaoleate, sucrose 30 pentarapeate, sucrose hexaoleate, sucrose hexarapeate,
sucrose triesters, pentaesters and hexaesters of soybean oil or cotton seed oil, glucose trioleate, glucose tetraoleate,

WO 2008/058831

PCTVEP2007/061280

- 10 -
xylose trioleate, or sucrose tetra-,tri-, penta- or hexa-esters with any mixture of predominantly unsaturated fatty acid chains.
5 However some derivative-CPs and derivative-RSs may be based on alkyl or alkenyl chains derived from polyunsaturated fatty acid sources, e.g. sucrose tetralinoleate. It is preferred that most, if not all, of the polyunsaturation has been removed by partial hydrogenation if such 10 polyunsaturated fatty acid chains are used.
The most highly preferred liquid derivative-CPs and
derivative-RSs are any of those mentioned in the above three
paragraphs but where the polyunsaturation has been removed
15 through partial hydrogenation.
■ ,
Especially good results"are obtained when the alkyl and/or
alkenyl chains of the derivative-CPs and derivative-RSs are
obtained by using a fatty acid mixture (to react with the
starting cyclic polyol or reduced saccharide) which
20 comprises a mixture of tallow fatty acid and oleyl fatty acid in a weight ratio of 10:90 to 90:10, more preferably 25:75 to 75:25, most preferably 30:70 to 70:30. A fatty acid mixture comprising a mixture of tallow fatty acid and oleyl fatty acid in a weight ratio of 60:40 to 40:60 is most
25 preferred.
Especially preferred are fatty acid mixtures comprising a weight ratio of approximately 50wt% tallow chains and 50wt% oleyl chains. It is especially preferred that the fatty-acid mixture consists only of a mixture of tallow fatty acid 30 and oleyl fatty acid.

WO 2008/058831

PCT/EP2007/061280

- 11 -
Preferably 40% or more of the chains Qontain an unsaturated bond/ more preferably 50% or more, most preferably 60% or more e.g. 65% to 95%. 5
Other oily sugar derivatives suitable for use in the compositions include sucrose pentalaurate, sucrose pentaerucate and sucrose tetraerucate. Suitable materials include some of the Ryoto series available from Mitsubishi 10 Kagaku Foods Corporation.
The liquid or soft solid derivative-CPs and derivative-RSs are characterised as xiateriaJs having 3 solid:liqvid ratio of.between 50:50 and 0:100 at 20°C as determined by T2
15 relaxation time NMR, preferably between 43:57 and 0:100,
most preferably between 40:60 and 0:10o, such as, 20:80 and 0:100. The T2 NMR relaxation time is commonly used for characterising solid:liquid ratios in soft solid products such as fats and margarines. For the purpose of the present
20 invention, any component of the NMR signal with a T2 of less than 100 microsecond is considered to be a solid component and any component with T2 greater than 1Q0 microseconds is considered to be a liquid component.
25 The liquid or soft solid derivative-CPE and derivative-RSE can be prepared by a variety of methods well known to those skilled in the art. These methods include acylation of the cyclic poiyol or of a reduced saccharide with an acid chloride; trans-esterification of the cyclic poiyol or of a
30 reduced saccharide material with short chain fatty acid esters in the presence of a basic catalyst {e.g. KOH); acylation of the cyclic poiyol or of a reduced saccharide

WO 2008/058831

PCT/EP2007/061280

- 12 -
with an acid anhydride, and, acylation of the cyclic polyol or of a reduced saccharide with a fatty acid. Typical preparations of these materials are disclosed in US 4 386 213 and AU 14416/88 (Procter and Gamble). 5
When an oily sugar derivative is present the compositions preferably comprise between 0.5%-30% wt of the oily sugar derivatives, more preferably 1-20% wt, most preferably 1.5-20% wt, e.g. 3-15% wt %, based on the total weight of the 10 composition.
(ii) Cationic Fabric Softening Compounds
The preferred cationic fabric softening compound(s) are 15 those having two or more alkyl or alkenyl chains each having an average chain length equal to, or greater than Ce, especially Ci2-23 alkyl or alkenyl chains connected to a nitrogen atom. The alkyl or alkenyl groups are preferably connected via at least one ester link, more preferably via 20 two or more ester linkages.
The cationic fabric softening compounds may be ester-linked quaternary ammonium fabric softening compounds or non-ester linked quaternary ammonium fabric softening compouads. The
25 ester-linked quaternary ammonium fabric softening compounds are herein referred to as "the ester-softening compound". The non-ester linked quaternary ammonium fabric softening compounds are herein referred to as "the non-ester softening compound".
30

WO 2008/058831

PCT/EP2007/061280

- 13 -
Especially suitable compounds have two or more alkyl or alkenyl chains each having an average chain length equal to, or greater than Cn, more preferably, equal to or greater Ci6. Most preferably at least 50% of the total number of alkyl or 5 alkenyl chains have a chain length equal to, or greater than Cis.
It is advantageous for environmental treasons if the ester-softening compound is biologically degradable. It is also 10 preferred if the alkyl or alkenyl chains of the ester-softening compound are predominantly linear.
One preferred type of ester-softeninq compound is a quaternary ammonium material represented by formula (I): 15
20
0 0
l! II
25 wherein T is -O-C- or -C-0-; each R1 group is independently selected from C1-4, alkyl or hydroxyalkyl or C2-4 alkenyl groups; and wherein each R2 group is independently selected from C3-23 alkyl or alkenyl groups, X" is any suitable anion including a halide, acetate or lower aikosulphate ion, such
30 as chloride or methosulphate, n is 0 or an integer from 1-5, and m is from 1-5.

WO 2008/058831

PCT/EP2007/061Z80

- 14 -
Preferred materials of this class such as 1,2 bis[hardened tallowoyloxy]-3- trimethylammonium propane chloride and their method of preparation are, for example, described in US 4 137 180 (Lever Brothers). Preferably these materials 5 comprise small amounts of the corresponding monoester as described in US 4 137 180 for example 1-hardened tallowoyloxy -2-hydroxy 3-trimethylammonium propane chloride.
10 A second preferred type of ester-softening compound is represented by the formula (II) :
15 (II)
20 wherein T, R1, R2, n, and X" are as defined above.
In this class di{tallowoyloxyethyl) dimethyl ammonium chloride and methyl bis-[ethyl (tallowoyl)]- 2-hydroxyethyl ammonium methyl sulphate are especially preferred. The
25 tallow chains in these compounds may be hardened and may even be fully unsaturated, i.e. preferred compounds also include di(hardened tallowoyloxy ethyl) dimethyl ammonium chloride and methyl bis-[ethyl(hardened tallowoyl)]-2-hydroxyethyl ammonium methyl sulphate. Commercially
30 available compounds include those in the Tetranyl range (ex Kao) and Stepantex range (ex Stepan),

WO 2008/05S831

PCT/EF2007/061280

- 15 -
Also suitable are derivatives of the above formula where one or more of the (CH2)n chain (s) has at least one pendent alkyl chain e.g. a methyl chain. Examples include the cationic quaternary ammonium compounds described in 5 WO 39/35223 and WO 99/35120 (Witco).
Another preferred softening active is triethanolamine di-alkylester methosulphate (TEAQ). The iodine value of the parent fatty acid is preferably in the range of from 20 to 10 60, more preferably from 25 to 50, still more preferably
from 30 to 45, and most preferably from 30 to 42. Preferred mono-rdi-:tri-ester distribution ratios of these materials are in ehe range as follows:-
15 Mono: from 28 to 42 %, preferably 30 to 40 %, most
preferably 30 to 35 %
Di: from 45 to 60 %, preferably 50 to 55 %
Tri: from 5 to 25 %, preferably. 5 to 15 %, most preferably
from 6 to 10 %. 20
A third preferred type of ester-softening compound is a
quaternary ammonium material represented by the formula
(III) :
25
(
30
wherein X~ is as defined above, A is an (m+n) valent radical remaining after the removal of (m-fn) hydroxy groups from an

WO 2008/058831

PCTVEP2007/061280

- 16 -
aliphatic polyol having p hydroxy groups and an atomic ratio of carbon to oxygen in the range of 1.0 to 3.0 and-up to 2 groups per hydroxy group selected from ethylene oxide and propylene oxide/ m is 0 or an integer from 1 to p-n, n is an 5 integer from 1 to p-m, and p is an integer of at least 2, 3 is an alkylene or alkylidene group containing 1 to 4 carbon atoms, R3, R4, R5 and R5 are, independently from each other, straight or branched chain Ci-C*e alkyl or alkenyl groups, optionally.with substitution by one or more functional 10 groups and/or interruption by at most 10 ethylene oxide
and/or propylene oxide groups, or by at most two functional groups selected from;
15
or R4 and R5 may form a ring system containing 5 or 6 atoms in the ring, with the proviso that the average compound 20 either has at least one R groip having 22-48 carbon atoms, or at least two R groups having 16-20 carbon atoms, or at least three R groups having 10-14 carbon atoms. Preferred compounds of this type are described in EP 638 639 (Akzo) .
25 The non-ester softening compound preferably has the alkyl or alkenyl chain lengths referred to above (in respect of the non-ester softening compounds).

WO 2008/058831

PCT/EP2007/061280

- 17 -
One preferred type of non-ester softening compound is a quaternary ammonium material represented by formula (IV):
(IV)
5
wherein each R1 group is independently selected from C1-4 alkyl, hydroxyalkyl or C2-4 alkenyi groups; each R group is independently selected from C3-23 alkyl or alkenyi groups, and X" is as defined above. 10
A preferred material of formula (IV) is di-hardened tallow-dimethyl ammonium chloride, sold under the Trademark ARQUAD 2HT by Akzo Nobel.
15 The compositions preferably comprise a total amount of between 0.5%wt-30% by weight of the cationic fabric softening compounds, preferably l%-25%, more preferably 1.5-22%, most preferably 2%-20%, based on the total weight of the composition.
20

WO 2008/058831

PCT/EP2007/0612SO

- 18 -
Non-Ionic Surfactant
A non-ionic surfactant may be present in order to stabilise the composition, or perform other functions such as 5 emulsifying any oil that may be present.
Suitable non-ionic surfactants include alkoxylated materials, particularly addition products of ethylene oxide and/or propylene oxide with fatty alcohols, fatty acids and 10 fatty amines.
Preferred materials are of the general formula:
R-Y- (CH2CH20)zH
15
Where R is a hydrophobic moiety, typically being an alkyl or alkenyl group, said group being linear or branched, primary or secondary, and preferably having from 8 to 25, more preferably 10 to 20, and most preferably 10 to 18 carbon
20 atoms; R may also be an aromatic group, such as a phenolic
group, substituted by an alkyl or alkenyl group as described above; Y is a linking group, typically being 0, CO.O, or CO.NfR1)/ where R1 is H or a Ci-4 alkyl group; and z represents the average number of ethoxylate (EO) units 25 present, said number being 8 or more, preferably 10 or more, more preferably 10 to 30, most preferably 12 to 25, e.g. 12 to 20.
Examples of suitable non-ionic surfactants include the 30 ethoxylates of mixed natural or synthetic alcohols in the "coco" or v-tallow" chain length. Preferred materials are condensation products of coconut fatty alcohol with 15-20

WO 2008/058831

PCT/EP2007/061280

- 19 -
moles of ethylene oxide and condensation products of tallow fatty alcohol with 10-20 moles of ethylene oxide.
The ethoxylates of secondary alcohols such as 3-hexadecanol, 5 2-octadecanol, 4-eicosanol, and 5-eicosanol may also be used. Exemplary ethoxylated secondary alcohols have formulae Ci2-EO(20); Ci4-EO(20); Ci4-EO(25); and C1G-EO(30). Especially preferred secondary alcohols are disclosed in PCT/EP2004/003992 and include Tergitol-15-S-3.
10
Polyol-based non-ionic surfactants may also be used, examples including sucrose esters {such as sucrose rrtonooleate) , alkyl polyglucosides {such as stearyl monoglucoside and stearyl triglucoside), and alkyl
15 polyglycerols.
Fatty Complexing Agent
A preferred additional component in the compositions of the 20 present invention is a fatty complexing agent. Such'agents typically have a Ca to C22 hydrocarbyl chain present as part of their molecular structure. Suitable fatty complexing agents include C3 to C22 fatty alcohols and C8 to C22 fatty acids; of these, the Cg to C22 fatty alcohols are most 25 preferred. A fatty complexing agent is particularly
valuable in compositions comprising a QAC having a single Ci2-28 group connected to the nitrogen head group, such as mono-ester associated with a TEA ester quat. or a softening agent of formula II, for reasons of product stability and 30 effectiveness.

WO 2008/058831

PCT/EP2007/061280

- 20 -
Preferred fatty acid complexing agents include hardened tallow fatty acid (available as Pristerene, ex Uniqema).
Preferred fatty alcohol complexing agents include Cis/Cis 5 fatty alcohols (available as Stenol and Hydrenol, ex Cognis, and Laurex CS, ex Albright and Wilson) and behenyl alcohol, a C22 fatty alcohol, available as Lanette 22, ex Henkel.
The fatty complexing agent may be used at from 0.1% to 10%, 10 particularly at from 0.2% to 5%, and especially at from 0.4 to 2% by weight, based on the total weight of the composition.
Perfume
15
The compositions of the invention typically comprise one or more perfumes. The perfume is preferably present in an amount from 0.01 to 10% by weight, more preferably 0.05 to 5% by weight, most preferably 0.5 to 4.0% by weight, based
20 on the total weight of the composition.
Viscosity Modifiers
The Fabric softening compositions may comprise viscosity 25 modifiers. Suitable viscosity modifiers are disclosed, for example, in WO 02/081611, US 2004/0214736, US 6827795, E? 0501714, US 2003/0104964, EP 0385749 and EP 331237.
Further Optional Ingredients 30
The compositions of the invention may contain one or more other ingredients. Such ingredients include preservatives

WO 2008/058831

PC17EP2007/061280

- 21 -
(e.g. bactericides), pH buffering agents, perfume carriers, fluorescers, colourants, hydrotropes, antifoaming agents, anti-redeposition agents, soil-release agents, electrolytes including polyelectrolytes, enzymes, optical brightening 5 agents, anti-shrinking agents, anti-wrinkle agents, anti-spotting agents, anti-oxidants, sunscreens, anti-corrosion agents, drape imparting agents, anti-static agents, ironing aids and dyes.
10 Product Use
The compositions of the present invention are preferably rinse conditioner compositions and may be used in the rinse cycle of a domestic laundry process. 15
The composition is preferably used in the rinse cycle of a home textile laundering operation, where, it may be added directly in an undiluted state to a washing machine, e.g. through a dispenser drawer or, for a top-loading washing 20 machine, directly into the drum. Alternatively, it can be diluted prior to use. The compositions may also be used in a domestic hand-washing laundry operation.
It is also possible, though less desirable, for the 25 compositions of the present invention to be used in industrial laundry.
The invention will be described with reference to the following Example.

WO 2008/058831
PCT/EP2007/061280
- 22 -
Example
Apparatus
5 Pad Mangle : Vertical laboratory padder VFM type ex. Werner Mathis AG
Darkened Drying frame
Light Source : Atlas Xenon Weatherometer S30QQ Bottle roller: Stuart Scientific Roller mixer SRTl 10 Spin dryer: Creda debonair spindryer
Materials
Fabric : 100% Polyester {Plain weave 122girf2)
15 100% Polyester (Knit 140girf2,)
100% cotton (jersey knit (175gm ~)
Treatments : ZnO nanopowder (ex. Sigma Aldrich)
20 Ti02 nanopowder(ex. Sigma Aldrich)
Fabric Softener Composition 1
Ti02 50.00
Cationic Fabric Softener (Stepantex UL 85) 6.34
25 Nonionic (Genapol C200) 0.19
Tallow alcohol (Stenol 1618) 0.50
Perfume 0.47
Water 42.50

WO 2008/058831

PCT/EP2007/061280

- 23 -
Procedure
Treatment
5 Samples of clean polyester or cotton were cut into 20cm x 10cm pieces
Fabric samples were treated with prototypes using a pad mangle or a bottle roller 10
Padded Samples
ZnO and Ti02 were each diluted to make a 1.0% w/w dispersion for pad application. 15
These 1.0 % dispersions were pad applied to the polyester at 100% pick-up.
This evenly delivered 1% on weight of xabric (o.w.f.) of the 20 metal oxide to the fabric
The Fabric Softener Composition 1 was diluted to make a 25% w/w dispersion for further dilution
25 This 25% dispersion was diluted to make 2% w/w dispersion for pad application.
The 2% w/w dispersion was pad applied to the knitted cotton at 100% pick-up. 30

WO 2008/058831

PCT/EP20Q7/061280

- 24 -
This evenly delivered 1.0% o.w.f. of the metal oxide and 0.12% o.w.f. of standard rinse conditioner active to the fabric.
Exhausted Sample
The Fabric Softener Composition 1 was diluted to make a 25% w/w dispersion for further dilution.
This 25% dispersion was diluted to make 0.25% w/w dispersion for exhaust application.
The 0.25% w/w dispersion placed in a bottle with a fabric s amp1e.
i
The bottle was rolled for 10 minutes to allow deposition to
take place.
The fabric sample was then spun for 1 minute in a domestic spin dryer.
This delivered 1.0% o.w.f. of the metal oxide and 0.12% o.w.f. of standard rinse conditioner active to the fabric if 100% of the material is deposited.
The treated fabric samples were allowed to dry in air within a darkened drying frame.
Light Exposure
The treated dried samples were then cut in half with half staying in the darkened crying frame.

WO 2008/058831

PCT/EP2007/061280

- 25 -
The other half were placed in the Atlas weatherometer mounting frames ready for light exposure. . . ..
The fabric samples were then exposed to a 2kW Xenon light 5 source for 3 hours with a relative humidity between 60-80%. Once the exposure was complete the polyester samples were assessed for their wetting behaviour.
Wetting Test 10
Exposed and unexposed samples were assessed for wetting.
Several 50p.l droplets were placed a :ross the surface of the fabric and the time taken from the droplets to fully 15 penetrate the surface was measured. !This was completed on both sides of the knitted polyester.
Results
20 Result shown as time taken to wet the surface against treatment.

[

WO 2008/058831

PCT/EP2007/061280

Woven Polyester

Treatments Wetting Time (seconds)
1% ZnO 600 +
1% ZnO + UV exposure 0
1% Ti02 600 +
1% Ti02 + UV exposure 0
Untreated 600 +
Untreated + UV exposure 600 +
Knitted Polyester
5

Treatments Wetting Time (seconds)
1% Ti02 500
1% Ti02 + Light exposure 0
1% Ti02 + Light exposure (RS)* 600
Untreated 600
Untreated + Light exposure 600
*(RS) Reverse side of exposed polyester

WO 2008/058831

PCT/EP2007/061280

Knitted Cotton

- 27 -

C4526 (C). WO (Amended 9 Sept 08)
- 28 -
CLAIMS

10
.15

1. A fabric softening composition comprising a fabric softening compound and from 5 to 50 % by weight, preferably 5 to 25 % by weight of the composition of a material (HH material) in which the HH material is hydrophobic but becomes hydrophilic upon exposure" to. light, particularly UV light wherein the fabric softening compound is selected from an oily sugar derivative, a quaternary ammonium compound having at -least two Ci2_2B groups connected to the nitrogen head group that may independently be alkyl or alkenyl groups, preferably being connected to the nitrogen head group by an ester link and mixtures thereof, and wherein the HH material comprises ZnO and/or Ti02.

20

A composition as claimed in claim 1 which additionally comprises one or more ingredients selected from perfume, non-ionic surfactant, fatty acid, fatty alcohol and viscosity modifier.

25
30

A method of treating a fabric to enhance the transport of water or water vapour therethrough, the method comprising rinsing the fabric in a composition as claimed in any preceding claim to deposit fabric conditioner and HH material thereon, drying the fabric and before, after or simultaneously with the drying, subjecting a portion of the fabric to an activation step to cause HH material deposited in said portion to undergo a change in its hydrophobic/hydrophilic properties.

AMENDED SHEET

C4526 (C) WO (Amended 9 Sept 08}
- 29 -
.4. A method as claimed in claim 3 in which the HH material-is ZnO and/or T1O2 and the activation step comprises exposure to UV light.
5. A method as claimed in claim 3 or claim 4 in which one side or portion of the fabric is subjected to said activation step.
Dated this 3th day of Hay 2009
HINDUSTAN UNILEVER LIMITED
(S. Venkatramani) Head of Patent Group, India