HIGH EFFICIENCY RADIATION-INDUCED TRIGGERING FOR SET-ONCOMMAND
COMPOSITIONS AND METHODS OF USE
BACKGROUND
[0001] The present invention generally relates to hydrocarbon
exploration and production operations, such as subterranean cementing
operations, and more particularly to compositions and methods that allow for
greater control over the setting of fluids or slurries used during such operations.
[0002] Natural resources such as oil and gas located in a subterranean
formation can be recovered by drilling a wellbore down to the subterranean
formation, typically while circulating a drilling fluid in the wellbore. After the
wellbore is drilled, a string of pipe, e.g., casing, can be run in the wellbore. The
drilling fluid is then usually circulated downwardly through the interior of the
pipe and upwardly through the annulus between the exterior of the pipe and the
walls of the wellbore, although other methodologies are known in the art.
[0003] Hydraulic cement compositions are commonly employed in the
drilling, completion and repair of oil and gas wells. For example, hydraulic
cement compositions are utilized in primary cementing operations whereby
strings of pipe such as casing or liners are cemented into wellbores. In
performing primary cementing, a hydraulic cement composition is pumped into
the annular space between the walls of a wellbore and the exterior surfaces of a
pipe string disposed therein to harden. After the cement is placed within the
wellbore, a period of time is needed for the cement to cure and obtain enough
mechanical strength for drilling operations to resume. This down time is often
referred to as "wait-on-cement", or WOC. The WOC time ranges from a few
hours to several days, depending on the difficulty and criticality of the cement
job in question. It is desirable to reduce the WOC time, so that the crew can
recommence the drilling operation, and thus reduce the total time and cost of
operations. I f operations are resumed prior to the cement obtaining sufficient
mechanical strength, the structural integrity of the cement can be compromised.
As such, systems generally are over-engineered to have very long setting (or
thickening) times in order to ensure that the mix remains fluid until all of the
cementitious material is in place, which can result in excessive WOC.
BRIEF DESCRIPTION OF THE DRAWINGS
[0004] The following figures are included to illustrate certain aspects of
the present invention, and should not be viewed as exclusive embodiments. The
subject matter disclosed is capable of considerable modifications, alterations,
combinations, and equivalents in form and function, as will occur to those skilled
in the art and having the benefit of this disclosure.
[0005] FIG. 1 illustrates a cross sectional side view of a wellbore.
[0006] FIG. 2 illustrates a cross sectional side view of an electron beam
energy source used in a wellbore for subjecting the sealant composition to a
radiation dose according one embodiment of the present disclosure.
DETAILED DESCRIPTION
[0007] The present invention generally relates to hydrocarbon
exploration and production operations, such as subterranean cementing
operations, and more particularly to compositions and methods that allow for
greater control over the setting of fluids or slurries used during such operations
by curing cement compositions with radiation.
[0008] The use of, for example, bremsstrahlung radiation in doses in
the sub-1000 gray range generated by electron accelerators, has significant
advantages. At 10-50%, the efficiency ( E of photons out over electrical E in) of
electron-to-bremsstrahlung photon production is much higher than that of most
other ionizing particles, such as neutrons and protons. For many competing
methods of high energy photon production, the efficiency of photon production is
2-4 orders of magnitude greater. As a result, the problems associated with
excess heat production and large energy requirements are minimized.
[0009] Further, the use of electron accelerators t o generate
bremsstrahlung radiation does not require a supply of precursor fuel, such as
deuterium or tritium due to the abundance of electrons in matter.
[0010] The present invention relates generally to wellbore operations
involving fluids or slurries, and more particularly, to fluids or slurries that contain
accelerating agents and/or retarders that can be released, activated and/or
deactivated on command to provide thickening to the fluid or slurry. The fluids
or slurries referred to herein can be any suitable for wellbore operations, drilling,
completion, workover or production operations. The fluids may include various
types of sealants, such as resins, cements, settable muds, lost circulation fluids,
conformance fluids, and combinations thereof. One embodiment of the present
invention relates to wellbore cementing operations, and more particularly, to
methods of sealing in wellbores using cementitious compositions that contain
polymerizable additives that can be subjected to radiation doses of from about 1
gray to about 1000 grays to form a seal.
[0011] Referring to FIG. 1, a cross sectional side view of an
embodiment of a wellbore 2 is illustrated. Surface casing 4, having a wellhead 6
attached, is installed in the wellbore 2 . Casing 8 is suspended from the wellhead
6 to the bottom of the wellbore 2 . An annulus 10 is defined between casing 8
and the wellbore 2. Annulus flow line 12 fluidly communicates with annulus 10
through the wellhead 6 and/or surface casing 4 with an annulus valve 14. Flow
line 16 is connected to the wellhead 6 to allow fluid communication with the
inner diameter of casing 8 and a casing valve 18. At the lower most end of
casing 8 the casing is open to the wellbore 2 or has circulation ports in the walls
of casing 8 (not shown) to allow fluid communication between the annulus 10
and the inner diameter of casing 8 .
[0012] A cement composition can be pumped down the casing 8 and
circulated up the annulus 10 while fluid returns are taken from the annulus 10
out annulus flow line 12, in a typical circulation direction. Alternately, the
cement composition can be pumped into the annulus 10 from annulus flow line
12 while fluid returns are taken from the inner diameter of casing 8 through flow
line 16. Thus, fluid flows through wellbore 2 in a reverse circulation direction.
[0013] In an alternate method a fluid composition, such as a cement
slurry, can be placed within the wellbore 2 and a sealed or filled tubular, such as
casing 8, can be lowered into the wellbore 2 such that the fluid composition is
displaced into the annulus 10 area, thereby placing the fluid composition within
the annulus 10 without pumping the fluid composition into the annulus 10. The
above method can be referred to as puddle cementing. The fluid composition can
be a drilling fluid placed within the wellbore after drilling operations are
complete.
[0014] In some embodiments, the sealant is subjected to a dose of
radiation from bremsstrahlung photons which result from decelerating electrons.
Bremsstrahlung radiation, or simply bremsstrahlung, is electromagnetic radiation
produced by a sudden slowing down or deflection of charged particles
(specifically electrons in this embodiment) passing through matter in the vicinity
of the strong electric fields of atomic nuclei Bremsstrahlung produces a
continuous X-ray spectra— .e., the resulting photons cover a whole range of
energy, from a maximum value downward through lower values all the way t o
zero. In generating bremsstrahlung, some electrons that collide with a material
target are decelerated to zero kinetic energy by a single head-on collision with a
nucleus, and thereby have a their energy of motion converted at once into
photon radiation of maximum energy. Other electrons from the same incident
beam come to rest after being decelerated many times by the positively charged
nuclei. Each deflection and subsequent scattering of the electrons gives rise to a
pulse of electromagnetic energy, or photon, of less than maximum energy. The
maximum energy of any one bremsstrahlung photon is the original kinetic
energy of the incoming charged particle, typically an electron in this
embodiment.
[0015] To generate bremsstrahlung, an electron accelerator may be
used. Electron beam bremsstrahlung-induced curing is a fast non-thermal
process which utilizes highly energetic electrons at controlled doses to produce
scattered photons that polymerize and crosslink polymeric materials. To produce
electrons with resulting bremsstrahlung photons that are most effective at
crosslinking, the electron accelerator in this embodiment should generate
electrons having an energy of about 0.5 MeV to about 20 MeV. I n other
embodiments, the electrons have an energy of about 0.1 MeV to about 50 MeV.
The maximum intensity of the electron accelerators which produce
bremsstrahlung photons may be large, over 1014/s. Further, the electron
accelerators may be geometrically modified to be accessible downwell. For
example, in some embodiments, a 5-6 MeV energy electron accelerator with an
average current of 10s of microamps (>10 14/s) and a tungsten target can induce
bulk gelation in some slurries in a few seconds.
[0016] Various electron accelerators are suitable for use in the present
invention. For example, on electron accelerator which includes a Cockcroft-
Walton voltage multiplying system that can make use of extra linear space
within a casing to amplify voltage up to the necessary several MeV level. This
system, which has a long, narrow shape makes it amenable to downhole utility.
Another suitable example of an electron accelerator is an RF cyclotron. Another
example of an electron accelerator technology for use in the present invention is
that of Wakefield technology. Wakefield technology exploits laser pulses to
evacuate electrons from small volumes of crystals. This allows other particles to
accelerate as the system returns to equilibrium.
[0017] One embodiment of the present invention is shown in Fig. 2.
Fig. 2 shows a cross sectional side view of an exemplary electron beam energy
source used in a wellbore for subjecting the sealant composition to a radiation
dose.
[0018] A tool wireline 401 supplies electrical power and communications
from the accelerator 500 to the surface of the wellbore. The tool wireline 401
also bears the mass of the accelerator 500 during transit up and down the
borehole.
[0019] The electron accelerator 500 comprises a housing 501 that
houses all the accelerator components. The housing 501 may have any
geometrical structure suitable for housing the components and for going
downwell in any type of geological formation 301.
[0020] The electron accelerator may include accelerator electrical power
components 561. These components may include devices for properly allocating
electrical power from the tool wireline 401 to the various power-using devices
throughout the accelerator 500.
[0021] An accelerator F electron acceleration component 581 may also
be included in the electron accelerator 500. The accelerator type may be
Cockcroft- Walton, radiofrequency, or Wakefield. The accelerator may also
include lasers. In addition, the accelerator 500 may have a characteristic radius.
The acceleration mechanism may involve plasma, RF induced electromagnetic
fields, capacitors and diodes or other mechanisms suitable for downwell
operations.
[0022] The accelerator 500 may also include cooling components 521.
The cooling component 521 could include cryogenic liquid with insulation. The
accelerator may also include communication components 541. These
components may include devices used to assist with communicating signals to
and from the tool wireline 401 to run the accelerator 500 properly.
[0023] Attached to the acceleration component 581 is an electron beam
port 591. This location is where the accelerated electrons 601 are expelled from
the acceleration electronics and put on a trajectory to impinge upon the high Z
target 701. The accelerated electrons in the present disclosure may have a
kinetic energy of from about 0.5 MeV and about 20 MeV. In other embodiments,
the accelerated electrons have a kinetic energy of from about 0.1 MeV to about
50 MeV. The electrons may be accelerated in a direction parallel to the axis of
the accelerator geometry.
[0024] An electron beam rastoring device 621 may be included to shape
the trajectory of the electrons 601 to depart from straight lines, to impinge on
the high Z target 701. The rastoring device 621 could include an electromagnet.
In other embodiments, the electron accelerator 500 may forego the use of the
rastoring device 621 and instead align the high Z target 701 with the electron
beam port, or increase the size of the area of the high Z target 701. In order to
optimize device utility, it is desirable t o create a trajectory for the accelerated
electrons whereby they impinge upon the high Z target 701 at angles that are as
perpendicular to the casing 101 as feasible so as to minimize the path length of
the bremsstrahlung photons 801 though the casing 101 and the material
surrounding the accelerator such as mud, pressurized water and other materials.
As such, the plane of the surface of the high Z target 701 might be angled with
respect to the radial plane of the accelerator and borehole.
[0025] During use of the accelerator 500 in the borehole, the
accelerator 500 may pass downward though the borehole in order to set the
cement slurry. I n the example shown in Fig. 2, the accelerator 500 has set the
cement 201 in the upper portion of the borehole, whereas the cement below the
accelerator 500 has not yet been irradiated, and as such, is yet to be cured
cement slurry 202. However, instead of passing downward, in other
embodiments, the accelerator 500 could be lowered to the bottom of the
borehole and then pulled upwards with the tool wireline 401 to set the cement
slurry from the bottom upward.
[0026] Any cement suitable for use in subterranean applications may be
suitable for use in the present invention. The cementitious compositions
disclosed herein generally include water and a cement component such as
hydraulic cement, which can include calcium, aluminum, silicon, oxygen, and/or
sulfur that sets and hardens by reaction with the water. Examples of hydraulic
cements include but are not limited t o Portland cements (e.g., Classes A, C, G,
and H Portland cements), pozzolana cements, gypsum cements, phosphate
cements, high alumina content cements, silica cements, high alkalinity cements,
and combinations thereof. Cements including shale, cement kiln dust or blast
furnace slag also may be suitable for use in the present invention. In certain
embodiments, the shale may include vitrified shale. In certain other
embodiments, the shale may include raw shale (e.g., unfired shale), or a
mixture of raw shale and vitrified shale.
[0027] The sealant may include a polymerizable additive capable of
undergoing polymerization when subjected to radiation. The polymerizable
additive may be present in an amount of about 0.01% to about 25% by weight
of the cement composition. In other embodiments, the polymerizable additive is
in an amount of about 1 to about 15%.
[0028] The polymerizable additive may include one selected from
alkeneoxides, vinyl pyrrolidones, vinyl alcohols, acrylamides, vinyl methyl
ethers, isobutylenes, fluoroelastomers, esters, tetrafluoroethylenes, acetals,
propylenes, ethylenes, methylpentenes, methylmethacrylates, fluorinated
ethylene propylenes, derivatives thereof and combinations thereof.
[0029] The sealant may also include a crosslinking agent capable of
crosslinking a polymer formed by the polymerization of the polymerizable
additive. For example, the crosslinking agent may include at least one selected
from the group consisting of a poly(ethylene glycol) diacrylates, a poly(ethylene
glycol) dimethacrylates, trimethylolpropane triacrylates (TMPTA), ethoxylated
TMPTAs, trimethylolpropane trimethacrylates, trimethylolpropanetriacrylates,
hexanediol diacrylates, N,N-methylene bisacrylamides, hexanedioldivinylethers,
triethyleneglycol diacrylates, pentaeritritoltriacrylates, tripropyleneglycol
diacrylates, l,3,5-triallyl-l,3,5-triazine-2,4,6(lH,3H,5H)-triones, 2,4,6-
triallyloxy-l,3,5-triazines, alkoxylated bisphenol A diacrylates, derivatives
thereof, and combinations thereof.
[0030] The sealant or cement compositions used in the present
invention can further include a set retarder. Set retarding admixtures lengthen
the time at which the fluid or slurry composition remains a fluid. These
retarding admixtures consequently allow a fluid or slurry, such as cement, to be
pumped along long distances without the effect of premature setting. A broad
variety of set retarders may be suitable for use in the fluid or slurry
compositions used in the present invention. For example, the set retarder may
include, inter alia, phosphonic acid, phosphonic acid derivatives, lignosulfonates,
salts, sugars, carbohydrate compounds, organic acids, carboxymethylated
hydroxyethylated celluloses, synthetic co- or ter-polymers including sulfonate
and carboxylic acid groups, and/or borate compounds. In certain embodiments,
the set retarders used in the present invention are phosphonic acid derivatives,
such as those described in U.S. Pat. No. 4,676,832, the entire disclosure of
which is incorporated herein. Examples of suitable borate compounds include,
but are not limited to, sodium tetraborate and potassium pentaborate.
Examples of suitable organic acids include, inter alia, gluconic acid and tartaric
acid. Generally, the set retarder is present in the fluid or slurry compositions
used in the present invention in an amount sufficient to delay the setting of the
fluid or slurry composition in a subterranean formation for a desired time. More
particularly, the set retarder may be present in the fluid or slurry compositions
used in the present invention in an amount of from about 0.1% to about 10%
bwoc. In certain embodiments, the set retarder is present in the fluid or slurry
compositions used in the present invention in an amount of from about 0.5% to
about 4% bwoc.
[0031] The set retarders of the current invention may include a
sensitizer-containing retarder, such as a boron-containing retarder. The
sensitizer can be made from a material having a strong radiation absorption
property. The sensitizer can also be a scintillator material. The sensitizer can
be any material that increases the capture efficiency of the ionizing radiation
within the slurry. This sensitizer-containing retarder, also referred to as a
sensitized retarder, can be a boron-containing retarder, also referred to as a
boronated retarder, may include a wide variety of set retarders, including the set
retarders disclosed herein, wherein the selected set retarder, or combination or
set retarders, additionally includes at least one boron atom. As discussed in the
immediately preceding paragraph, sugars and/or carbohydrates can be used as a
retarder in the setting of a cement composition. In an embodiment, the retarder
is a sensitized sugar or carbohydrate. In a more specific embodiment, the
sensitized retarder is boronated glucose. I n an even more specific embodiment,
the boronated glucose is represented by 3-0-(o-Carborany-l-ylmethyl)-Dglucose,
as presented in U.S. Pat. No. 5,466,679, to Soloway et al.
[0032] The compositions of the present invention may also include a set
accelerator. The accelerator aids in overcoming possible delays caused by the
set retarders by shortening the setting time of the fluid or slurry composition. A
broad variety of set accelerators may be suitable for use in the fluid or slurry
compositions used in the present invention, the set accelerator may include any
component that reduces the setting time of a cement composition. For example,
the set accelerator may include alkali and alkali earth metal salts, silicate salts,
aluminates and amines, such as triethanolamine. In an embodiment, the set
accelerator is a calcium salt. The calcium salt may be selected from the group
consisting of calcium formate, calcium nitrate, calcium nitrite and calcium
chloride. In a specific embodiment, the set accelerator is calcium chloride. The
set accelerator may be present in the fluid or slurry compositions used in the
present invention in an amount of from about 0 .1% to about 20% bwoc. In
certain embodiments, the set accelerator is present in the cement compositions
used in the present invention in an amount of from about 4% to about 12%
bwoc.
[0033] Methods of this invention for isolating a wellbore or a portion of
a wellbore may include placing a sealant composition including a polymerizable
additive, pumping the sealant composition containing the polymerizable additive
into a wellbore penetrating a subterranean formation, and subjecting the sealant
composition to a radiation dose of from about 1 gray to about 1000 grays, so as
to form a seal therein. In other embodiments, the sealant composition may be
subjected to a radiation dose of from about 5 grays to about 500 grays.
[0034] Methods of this invention may include preparing a cement
composition comprising : hydraulic cement, a polymerizable additive, and
sufficient water to form a slurry; placing the cement composition into the
wellbore; and subjecting the cement composition to a radiation dose of from
about 1 gray to about 1000 grays to activate setting of the cement composition.
In other embodiments, the cement composition may be subjected to a radiation
dose of from about 5 grays to about 500 grays.
[0035] In an embodiment, a set retarder and/or a set accelerator or
oxidizing agent are/is added to the cement mixture before water is added to the
mixture. I n another embodiment, the set retarder and/or the set accelerator or
oxidizing agent are/is added to the cement mixture after water has been added
to the mixture. In yet another embodiment, set retarder is added before the set
accelerator or oxidizing agent. In yet another embodiment, the set accelerator
is added before the set retarder. In a further embodiment, the set accelerator
and/or set retarder is/are added during the mixing of the cement and water.
[0036] In an embodiment, once the cementitious composition
containing the set retarder and/or set accelerator or oxidizing agent is obtained,
the slurry is then placed in the wellbore, such as in a wellbore/casing annulus.
Upon the placement of the slurry containing the set retarder and/or set
accelerator or oxidizing agent in the wellbore, the cement particles and the set
retarder and/or set accelerator or oxidizing agent should be substantially
uniformly mixed with the cement particles in the cement slurry.
[0037] In a further embodiment, a set retarder as well as both a set
accelerator and oxidizer are added to the fluid or slurry. Upon being exposed to
the ionizing radiation, both the set accelerator and oxidizer are released. The
simultaneous destruction of the retarder by the oxidizer and the acceleration of
cement hydration by the set accelerator provide rapid set.
[0038] In an embodiment, the ionizing radiation is introduced by an
ionizing radiation emitter located at a point within the wellbore. In another
embodiment, an ionizing radiation emitter located at the surface introduces the
ionizing radiation directed downward into the wellbore. I n another embodiment,
a radiation source is lowered into the wellbore, such as on a wireline, and the
ionizing radiation is emitted. The radiation source can be shielded to not emit
the ionizing radiation other than when the shielding is removed. For example, a
radiation source can be shielded at the surface when personnel could otherwise
be exposed. Once the ionizing radiation source is placed in the wellbore and
radiation can safely be emitted, the shield can be removed or opened, such as
by an electronically activated signal transmitted from the surface down the
wireline to the shield. I n an embodiment, the radiation emitter can emit ionizing
radiation as it is lowered down the wellbore and as it is pulled up the length of
the wellbore. In a further embodiment, two or more ionizing radiation emitters
are separately lowered to two or more depths, such that two or more depths of
the wellbore may be subject to the ionizing radiation simultaneously.
[0039] In an embodiment, the ionizing radiation is introduced under the
control of a technician in the field. The technician, engineer, or other on-site
employee, can have the control over the emission of the ionizing radiation by
imputing a signal that causes a release of the ionizing radiation from an emitter.
In this embodiment, the ionizing radiation is released on demand from the
technician in the field. The ionizing radiation can be released by a control
system having parameters such as timer, flow meter, temperature sensor, or the
like. In another embodiment, the lowering and/or emitting of the ionizing
radiation source is triggered by a timing mechanism. I n a further embodiment,
the lowering and/or emitting of the radiation source is triggered by a flow meter
that detects the amount of the cement mixture delivered into the wellbore.
[0040] As mentioned above, the ionizing radiation of the current
invention can be under the control of technicians in the field. The release of the
ionizing radiation emissions act as a trigger in the sense that the radiation can
destroy the sensitized retarder, thus allowing the setting of the cement slurry t o
proceed. The release of the ionizing radiation may also act as a trigger when the
ionizing radiation emissions act to release the set accelerator or oxidizing agent,
or both, into the cement slurry. Once the set accelerator or oxidizing agent is
released, it is dispersed into the cement slurry and reacts with the slurry or
retarder, resulting in the acceleration of the setting process. Therefore,
technicians in the field can trigger the thickening of the cement slurry. This
triggering process puts the thickening of the cement slurry under the control of
technicians in the field and can result in a decrease in the time needed to wait
on cement (WOC) in the drilling and completion of a wellbore.
[0041] The term "cementitious composition" as may be used herein
includes pastes (or slurries), mortars, and grouts, such as oil well cementing
grouts, shotcrete, and concrete compositions including a hydraulic cement
binder. The terms "paste", "mortar" and "concrete" are terms of art: pastes are
mixtures composed of a hydratable (or hydraulic) cement binder (usually, but
not exclusively, Portland cement, Masonry cement, Mortar cement, and/or
gypsum, and may also include limestone, hydrated lime, fly ash, granulated
blast furnace slag, and silica fume or other materials commonly included in such
cements) and water; "mortars" are pastes additionally including fine aggregate
(e.g., sand), and "concretes" are mortars additionally including coarse aggregate
(e.g., crushed rock or gravel). The cement compositions described in this
invention are formed by mixing required amounts of certain materials, e.g., a
hydraulic cement, water, and fine and/or coarse aggregate, as may be required
for making a particular cementitious composition.
[0042] The term "set accelerator" can include any component, which
reduces the setting time of a cement composition. For example, the set
accelerator may include alkali and alkali earth metal salts, such as a calcium
salt. The calcium salt may include calcium formate, calcium nitrate, calcium
nitrite or calcium chloride.
[0043] The term "encapsulating layer" as used herein can mean any
form of coating or binding wherein most of the material being encapsulated is
enclosed within the layer and that the dissipation of the material is substantially
restricted by the layer. It does not mean that all of the material being
encapsulated is enclosed within the layer or that the material being encapsulated
cannot leak through the encapsulating layer.
[0044] The term oxidizer can include any component which is capable
of degrading the retarder present. These include, but are not limited to alkaline
earth and zinc salts of peroxide, perphosphate, perborate, percarbonate; calcium
peroxide, calcium perphosphate, calcium perborate, magnesium peroxide,
magnesium perphosphate, zinc perphosphate; calcium hypochlorite, magnesium
hypochlorite, chloramine T, trichloroisocyanuric acid, trichloromelamine,
dichloroisocynaurate dihydrate, anhydrous dichloroisocynaurate; and mixtures
thereof.
[0045] The term "radiation tolerance" as used herein is the amount of
ionizing radiation that a material can withstand without noticeable or measurable
degradation.
[0046] The term "retarder" or "set retarder" can include boronated or
non-boronated forms of phosphonic acid, phosphonic acid derivatives,
lignosulfonates, salts, sugars, carbohydrate compounds, organic acids,
carboxymethylated hydroxyethylated celluloses, synthetic co- or ter-polymers
including sulfonate and carboxylic acid groups, and/or borate compounds.
[0047] The term "set" as used herein refers to an increase in
mechanical strength of a fluid or slurry sufficient to perform a desired result,
such as to restrict movement of an item or impede fluid flow or pressure transfer
through a fluid. A cement may be referred to as set when it can restrict the
movement of a pipe, or impede fluid flow or pressure transfer, regardless of
whether the cement has cured to a fully solid composition. A fluid or slurry can
be referred to as set when it has thickened to a sufficient level that it achieves
the desired result, such as the isolation of a particular zone or the restriction of
fluid flow or pressure transfer, regardless of whether it has reached its final
consistency.
[0048] The present invention may also be useful for cement or concrete
in other applications, including infrastructure and building materials, where a
quick setting time can be obtained with the polymer system. Some specific
examples include rapid hardening of pre-cast units such as pipes, panels, and
beams, cast in-situ structures for bridges, dams, or roads, quick-set grout,
increased adhesion in cement, addition of water-resistant properties to cement,
decorative concrete, rapid concrete repair, production of cement board. Other
advantages over typical polymer-enhanced concrete systems include the ability
to use a wider variety of polymer species, including oligomers which are
significantly less volatile, combustible and toxic, and the elimination of initiators,
which are also toxic to humans and the environment.
[0049] Embodiments disclosed herein include:
[0050] Embodiment A: A method comprising : placing a sealant
composition comprising a polymerizable additive into a wellbore penetrating a
subterranean formation; and subjecting the sealant composition to a radiation
dose of from about 1 gray to about 1000 grays, so as to form a seal therein.
[0051] Embodiment B: A method comprising : preparing a cement
composition comprising : hydraulic cement, a polymerizable additive, and
sufficient water to form a slurry; placing the cement composition into the
wellbore; and subjecting the cement composition to a radiation dose of from
about 1 gray to about 1000 grays to activate setting of the cement composition.
[0052] Each of embodiments A and B may have one or more of the
following additional elements in any combination :
[0053] Element 1: the method wherein the radiation dose is from
bremsstrahlung photons that result from electron scattering, and where the
photons initiate setting of the sealant composition
[0054] Element 2 : the method wherein the polymerizable additive
comprises one selected from the group consisting of acrylate, methacrylate,
polyalkylene oxide, alkeneoxide, vinyl pyrrolidone, polyvinyl pyrrolidone,
acrylamido-methyl-propane sulfonate, vinyl alcohol, acrylamide, vinyl methyl
ether, isobutylene, a fluoroelastomer, an ester, tetrafluoroethylene, an acetal,
propylene, ethylene, methylpentene, methylmethacrylate, fluorinated ethylene
propylene, derivatives thereof, and combinations thereof.
[0055] Element 3 : the method wherein the sealant composition further
comprises a crosslinking agent capable of crosslinking a polymer formed by
polymerization of the polymerizable additive.
[0056] Element 4 : the method wherein the sealant composition further
comprises a crosslinking agent capable of crosslinking a polymer formed by
polymerization of the polymerizable additive and wherein the crosslinking agent
comprises one selected from the group consisting of a poly(ethylene glycol)
diacrylate, a poly(ethylene glycol) dimethacrylate, trimethylolpropane triacrylate
(TMPTA), ethoxylated TMPTA, trimethylolpropane trimethacrylate,
trimethylolpropanetriacrylate, hexanediol diacrylate, N,N-methylene
bisacrylamide, hexanedioldivinylether, triethyleneglycol diacrylate,
pentaeritritoltriacrylate, tripropyleneglycol diacrylate, l,3,5-triallyl-l,3,5-
triazine-2,4,6(lH,3H,5H)-trione, 2,4,6-triallyloxy-l,3,5-triazine, alkoxylated
bisphenol A diacrylate, derivatives thereof, and combinations thereof.
[0057] Element 5 : the method wherein the sealant composition is
selected from the group consisting of a resin, a cement, a settable mud, a lost
circulation fluid, a conformance fluid, and combinations thereof.
[0058] Element 6 : the method wherein the radiation dose is generated
by an electron accelerator.
[0059] Element 7 : the method wherein the radiation dose is generated
by an electron accelerator located downhole.
[0060] Element 8 : the method wherein the electron accelerator
generates electrons having an energy of about 0.5 MeV to about 50 MeV.
[0061] Element 9 : the method wherein the radiation dose is from about
5 grays to about 500 grays.
[0062] Element 10: the method wherein subjecting the sealant
composition to the radiation dose increases the mechanical strength of the
sealant composition.
[0063] Element 11 : the method wherein the polymerizable additive is
present in an amount of about 0.01% to about 25% by weight of the cement
composition or by weight of the sealant composition.
[0064] Element 12: the method wherein the cement composition
further comprises a set retarder.
[0065] Element 13: the method wherein the cement composition
further comprises a set retarder and wherein the set retarder is present in an
amount of about 0.1% to about 20% by weight of the cement composition.
[0066] By way of non-limiting example, exemplary combinations
applicable to A, B, C include, for example: combinations of A or B with Elements
1, 2, and 6; combinations of A or B with Elements 1, 4, and 7; combinations of A
or B with Elements 2, 8, and 9; etc.
[0067] To facilitate a better understanding of the present invention, the
following examples of preferred or representative embodiments are given. In no
way should the following examples be read to limit, or to define, the scope of the
invention.
EXAMPLES
[0068] Example 1:
[0069] Cement slurry samples were prepared by mixing the following
ingredients: 400 grams of a class H cement (Lafarge, Joppa IL), 160 grams of
water (w/c = 0.40), 8.0% by weight of solids (bwos) acrylamide, 0.42%bwos
N,N-methylene-bis-acrylamide as a crosslinker, 0.50%bwos maltodextrin as a
set retarder, 0.50%bwos HR-25 as a set retarder, 0.20%bwos Diutan gum as a
rheology modifier, 0.10%bwos SnCI2 as an oxygen scavenger, and 1.0%bwos
SYLOID® RAD 2105 silica gel (Grace Performance Chemicals, USA).
[0070] The slurry was mixed for 45 seconds on a Waring blade mixer as
per the API mixing schedule. The slurry was split into two samples. One sample
was exposed for 20 seconds to bremsstrahlung radiation produced by focusing
an electron beam of 5-6MeV energy onto a tungsten target and placing the
sample in a vial at the other end of the tungsten target and thereby exposing
the sample to the bremsstrahlung photons. The other sample was not irradiated
and kept as a control. The control sample remained fluid. The irradiated sample
had been crosslinked and displayed a freestanding solid-like behavior.
[0071] Example 2 :
[0072] A cement/sand slurry was prepared similar to that of Example 1,
except that the 1% SYLOID RAD particles were not included, and 200 grams of
the class H cement was replaced with 200 mesh sand for a 50: 50 mixture of
cement and silica flour.
[0073] The slurry was mixed for 45 seconds on a Waring blade mixer as
per the API mixing schedule. The slurry was split into two samples. One sample
was exposed for 30 seconds to bremsstrahlung radiation produced by focusing
an electron beam of 5-6MeV energy onto a tungsten target and placing the
sample in a vial at the other end of the tungsten target and thereby exposing
the sample to the bremsstrahlung photons. The other sample was not irradiated
and kept as a control. The control sample remained fluid. The irradiated sample
had been crosslinked and displayed a freestanding solid-like behavior.
[0074] Example 3 :
[0075] Silica flour slurry samples were prepared by mixing the following
ingredients: 400 grams of SSA-1 silica flour (Halliburton, Houston, Texas) 168
grams of water (w/c = 0.42), 0.18wt% Ca(OH)2 per 100 grams water, 8.0% by
weight of solids (bwos) acrylamide, 0.42%bwos N,N-methylene-bis-acrylamide
as a crosslinker, 0.20%bwos Diutan gum as a rheology modifier, 0.10%bwos
SnCI 2 as an oxygen scavenger.
[0076] The slurry was mixed for 45 seconds on a Waring blade mixer as
per the API mixing schedule. The slurry was split into two samples. One sample
was exposed for 30 seconds to bremsstrahlung radiation produced by focusing
an electron beam of 5-6MeV energy onto a tungsten target and placing the
sample in a vial at the other end of the tungsten target and thereby exposing
the sample to the bremsstrahlung photons. The other sample was not irradiated
and kept as a control. The control sample remained fluid. The irradiated sample
had been crosslinked and displayed a freestanding solid-like behavior.
[0077] The samples demonstrate that bremsstrahlung radiation may be
utilized to solidify cement by irradiating a sample of polymerizable additive
contained in the cement.
[0078] Therefore, the present invention is well adapted to attain the
ends and advantages mentioned as well as those that are inherent therein. The
particular embodiments disclosed above are illustrative only, as the present
invention may be modified and practiced in different but equivalent manners
apparent t o those skilled in the art having the benefit of the teachings herein.
Furthermore, no limitations are intended to the details of construction or design
herein shown, other than as described in the claims below. It is therefore
evident that the particular illustrative embodiments disclosed above may be
altered, combined, or modified and all such variations are considered within the
scope and spirit of the present invention. The invention illustratively disclosed
herein suitably may be practiced in the absence of any element that is not
specifically disclosed herein and/or any optional element disclosed herein. While
compositions and methods are described in terms of "comprising," "containing,"
or "including" various components or steps, the compositions and methods can
also "consist essentially of" or "consist of" the various components and steps.
All numbers and ranges disclosed above may vary by some amount. Whenever
a numerical range with a lower limit and an upper limit is disclosed, any number
and any included range falling within the range is specifically disclosed. In
particular, every range of values (of the form, "from about a to about b," or,
equivalently, "from approximately a to b," or, equivalently, "from approximately
a-b") disclosed herein is to be understood to set forth every number and range
encompassed within the broader range of values. Also, the terms in the claims
have their plain, ordinary meaning unless otherwise explicitly and clearly defined
by the patentee. Moreover, the indefinite articles "a" or "an," as used in the
claims, are defined herein to mean one or more than one of the element that it
introduces. I f there is any conflict in the usages of a word or term in this
specification and one or more patent or other documents that may be
incorporated herein by reference, the definitions that are consistent with this
specification should be adopted.

CLAIMS
The invention claimed is:
1. A method comprising :
placing a sealant composition comprising a polymerizable additive into a
wellbore penetrating a subterranean formation; and
subjecting the sealant composition to a radiation dose of from about 1
gray to about 1000 grays, so as to form a seal therein.
2. The method of claim 1, wherein the radiation dose is from
bremsstrahlung photons that result from electron scattering, and where the
photons initiate setting of the sealant composition.
3. The method of claim 1, wherein the polymerizable additive comprises
one selected from the group consisting of acrylate, methacrylate, polyalkylene
oxide, alkeneoxide, vinyl pyrrolidone, polyvinyl pyrrolidone, acrylamido-methylpropane
sulfonate, vinyl alcohol, acrylamide, vinyl methyl ether, isobutylene, a
fluoroelastomer, an ester, tetrafluoroethylene, an acetal, propylene, ethylene,
methylpentene, methylmethacrylate, fluorinated ethylene propylene, derivatives
thereof, and combinations thereof.
4 . The method of claim 2, wherein the sealant composition further
comprises a crosslinking agent capable of crosslinking a polymer formed by
polymerization of the polymerizable additive.
5. The method of claim 4, wherein the crosslinking agent comprises one
selected from the group consisting of a poly(ethylene glycol) diacrylate, a
poly(ethylene glycol) dimethacrylate, trimethylolpropane triacrylate (TMPTA),
ethoxylated TMPTA, trimethylolpropane trimethacrylate,
trimethylolpropanetriacrylate, hexanediol diacrylate, N,N-methylene
bisacrylamide, hexanedioldivinylether, triethyleneglycol diacrylate,
pentaeritritoltriacrylate, tripropyleneglycol diacrylate, l,3,5-triallyl-l,3,5-
triazine-2,4,6(lH,3H,5H)-trione, 2,4,6-triallyloxy-l,3,5-triazine, alkoxylated
bisphenol A diacrylate, derivatives thereof, and combinations thereof.
6. The method of claim 1, wherein the sealant composition is selected
from the group consisting of a resin, a cement, a settable mud, a lost circulation
fluid, a conformance fluid, and combinations thereof.
7. The method of claim 1, wherein the radiation dose is generated by an
electron accelerator.
8 . The method of claim 7, wherein the electron accelerator generates
electrons having an energy of about 0.5 MeV to about 50 MeV.
9 . The method of claim 1, wherein the radiation dose is from about 5
grays t o about 500 grays.
10. The method of claim 1, wherein subjecting the sealant composition to
the radiation dose increases the mechanical strength of the sealant composition.
11. A method comprising :
preparing a cement composition comprising : hydraulic cement, a
polymerizable additive, and sufficient water to form a slurry;
placing the cement composition into the wellbore; and
subjecting the cement composition to a radiation dose of from about 1
gray to about 1000 grays to activate setting.
12. The method of claim 11, wherein the polymerizable additive is
present in an amount of about 0.01% to about 25% by weight of the cement
composition.
13. The method of claim 11, wherein the cement composition further
comprises a set retarder.
14. The method of claim 13, wherein the set retarder is present in an
amount of about 0.1% to about 20% by weight of the cement composition.
15. The method of claim 11, wherein the radiation dose is from
bremsstrahlung photons that result from electron scattering, and where the
photons initiate setting of the cement composition.
16. The method of claim 11, wherein the polymerizable additive
comprises one selected from the group consisting of acrylate, methacrylate,
polyalkylene oxide, alkeneoxide, vinyl pyrrolidone, polyvinyl pyrrolidone,
acrylamido-methyl-propane sulfonate, vinyl alcohol, acrylamide, vinyl methyl
ether, isobutylene, a fluoroelastomer, an ester, tetrafluoroethylene, an acetal,
propylene, ethylene, methylpentene, methylmethacrylate, fluorinated ethylene
propylene, and combinations thereof.
17. The method of claim 11, wherein the cement composition further
comprises a crosslinking agent capable of crosslinking a polymer formed by
polymerization of the polymerizable additive.
18. The method of claim 17, wherein the crosslinking agent comprises
one selected from the group consisting of a poly(ethylene glycol) diacrylate, a
poly(ethylene glycol) dimethacrylate, trimethylolpropane triacrylate (TMPTA),
ethoxylated TMPTA, trimethylolpropane trimethacrylate,
trimethylolpropanetriacrylate, hexanediol diacrylate, N,N-methylene
bisacrylamide, hexanedioldivinylether, triethyleneglycol diacrylate,
pentaeritritoltriacrylate, tripropyleneglycol diacrylate, l,3,5-triallyl-l,3,5-
triazine-2,4,6(lH,3H,5H)-trione, 2,4,6-triallyloxy-l,3,5-tnazine, alkoxylated
bisphenol A diacrylate, derivatives thereof, and combinations thereof.
19. The method of claim 11, wherein the radiation dose is generated by
an electron accelerator located downhole.
20. The method of claim 19, wherein the electron accelerator generates
electrons having an energy of about 0.5 MeV to about 50 MeV.