[0001]The present invention relates to a hot-stamped article. Priority is claimed on
Japanese Patent Application No. 2019-101987, filed May 31, 2019, the content of which
is incorporated herein by reference.
[Background Art]
10 [0002]
In recent years, there has been a demand for the weight reduction of automotive
bodies from the viewpoint of environmental protection and resource saving, and the
application of high-strength steel sheets to automotive parts has been accelerating.
Automotive parts are manufactured by press forming, and an increase in the strength of
15 steel sheets does not only increase forming loads but also degrades formability, which
creates a problem with the formability of high-strength steel sheets into parts with a
complicated shape. In order to solve such a problem, the application of hot stamping
techniques, in which a steel sheet is heated to a high temperature in an austenite region
where the steel sheet softens and then formed by pressing, is underway. Hot stamping is
20 drawing attention as a technique in which a quenching treatment is carried out in a die at
the same time as pressing, thereby satisfying both formability into automotive parts and
the securement of the strength of automotive parts.
[0003]
However, in hot-stamped articles of the related art manufactured by hot
25 stamping, a hard structure (mainly martensite) is formed throughout the entire region in
1

the sheet thickness direction, and thus the deformability is poor. In order to obtain
superior collision properties in automotive parts, there is a need to enhance the impact
energy absorption capability. When deformation modes at the time of collision are
taken into account, there is a need to enhance deformability, particularly, bendability.
5 [0004]
Patent Document 1 discloses a technique in which the cooling rate from
finishing rolling through coiling in a hot rolling process is controlled to control the
crystal orientation difference in bainite to become 5° to 14°, thereby improving
deformability such as stretch-flangeability.
10 [0005]
Patent Document 2 discloses a technique in which manufacturing conditions for
finishing rolling through coiling in a hot rolling process are controlled to control the
strength of a specific crystal orientation group out of ferrite crystal grains, thereby
improving local deformability.
15 [0006]
Patent Document 3 discloses a technique in which a heat treatment is carried out
on a steel sheet for hot stamping to form ferrite in the surface layer, thereby reducing the
number of pores that are generated in the interface between ZnO and the steel sheet or
the interface between ZnO and a Zn-based plating layer during heating before hot
20 pressing and improving perforation corrosion resistance or the like.
[0007]
However, in the above-described techniques, there are cases where a sufficient
strength and sufficient bendability cannot be obtained.
[Citation List]
25 [Patent Document]
2

[0008]
[Patent Document 1]
PCT International Publication No. WO 2016/132545
[Patent Document 2]
5 Japanese Unexamined Patent Application, First Publication No. 2012-172203
[Patent Document 3]
Japanese Patent No. 5861766
[Non-Patent Documents]
[0009]
10 [Non-Patent Document 1]
T. Ungar and three coauthors, Journal of Applied Crystallography (1999), Volume 32 (pp. 992 to 1002) [Summary of the Invention]
[Problems to be Solved by the Invention]
15 [0010]
The present invention has been made in consideration of the problem of the
related art, and an objective of the present invention is to provide a hot-stamped article
having excellent strength and excellent bendability.
[Means for Solving the Problem]
20 [0011]
The present inventors carried out intensive studies regarding a method for solving the above-described problem and consequently obtained the following findings. [0012]
The present inventors carried out studies regarding the bendability of hot-
25 stamped articles. As a result, the present inventors found that, when the metallographic
3

structure of a surface layer region, which is a region from a surface to a depth of 50 μm,
of a base steel sheet that configures a hot-stamped article includes 80.0% or more of
martensite and 8.0% or more of residual austenite in terms of area percentage and the
concentration of Ni in the surface layer region is 8 mass% or more, the bendability of the
5 hot-stamped article improves.
[0013]
Furthermore, the present inventors found that, in order to obtain the above-
described metallographic structure in the surface layer region of the base steel sheet that
configures the hot-stamped article, in the surface layer region in the steel sheet for hot
10 stamping before hot stamping, it is necessary to set the average dislocation density to 4 ×
1015 m/m3 or more, to set the proportion of the crystal grains of one or more kinds of
unauto-tempered martensite and lower bainite to 15.0% or more in terms of area
percentage, and to carry out hot stamping under a predetermined condition.
[0014]
15 The present invention has been made by further progressing studies based on the
above-described findings, and the gist thereof is as described below.
[1] A hot-stamped article according to one aspect of the present invention having
a base steel sheet containing, as chemical components, by mass%,
C: 0.15% or more and less than 0.70%,
20 Si: 0.005% or more and 0.250% or less,
Mn: 0.30% or more and 3.00% or less,
sol. Al: 0.0002% or more and 0.500% or less,
P: 0.100% or less,
S: 0.1000% or less,
25 N: 0.0100% or less,
4

Nb: 0% or more and 0.150% or less,
Ti: 0% or more and 0.150% or less,
Mo: 0% or more and 1.000% or less,
Cr: 0% or more and 1.000% or less,
5 B: 0% or more and 0.0100% or less,
Ca: 0% or more and 0.0100% or less, and
REM: 0% or more and 0.30% or less with a remainder including Fe and impurities and
a plating layer on a surface of the base steel sheet, the plating layer being
10 attached to a single surface in an amount of 10 g/m2 or more and 90 g/m2 or less and
having a Ni content of 10 mass% or more and 25 mass% or less with a remainder including Zn and impurities,
in which a metallographic structure of a surface layer region that is a region
from the surface of the base steel sheet to a depth of 50 μm includes 80.0% or more of
15 martensite and 8.0% or more of residual austenite in terms of area percentage, and
the concentration of Ni in the surface layer region is 8 mass% or more.
[2] The hot-stamped article according to [1] may further contain, in the base
steel sheet, as chemical components, by mass%, one or more selected from the group
consisting of
20 Nb: 0.010% or more and 0.150% or less,
Ti: 0.010% or more and 0.150% or less,
Mo: 0.005% or more and 1.000% or less,
Cr: 0.005% or more and 1.000% or less,
B: 0.0005% or more and 0.0100% or less,
25 Ca: 0.0005% or more and 0.0100% or less, and
5

REM: 0.0005% or more and 0.30% or less. [Effects of the Invention] [0015]
According to the above-described aspect of the present invention, it is possible
5 to provide a hot-stamped article having excellent strength and excellent bendability.
[Embodiment for implementing the Invention] [0016]
In a hot-stamped article according to the present embodiment, the
metallographic structure of a surface of a base steel sheet that configures the hot-stamped
10 article, in other words, a surface layer region that is a region from the surface of the base
steel sheet after hot stamping to a depth of 50 μm includes 80.0% or more of martensite
and 8.0% or more of residual austenite in terms of area percentage, and the concentration
of Ni in the surface layer region is 8 mass% or more. Such characteristics make it
possible to obtain a hot-stamped article having excellent strength and excellent
15 bendability. In the present embodiment, the expression “having excellent strength”
refers to the fact that the (maximum) tensile strength is 1500 MPa or higher. [0017]
As a result of intensive studies, the present inventors found that a hot-stamped
article having the above-described metallographic structure can be obtained by the
20 following method.
[0018]
As a first stage, in a hot rolling process, cooling is initiated within five seconds
from the end of finishing rolling in a manner that the average cooling rate on the surface
of the base steel sheet reaches 80 °C/s or faster, and the base steel sheet is cooled to a
25 temperature region of lower than 500°C and coiled. Even after coiled, the base steel
6

sheet is continuously cooled with water to room temperature (approximately 40°C or
lower). As described above, compared with the related art, the average cooling rate is
set to be fast and the coiling temperature is set to be low, whereby it is possible to
suppress the generation of a carbide, ferritic transformation, and bainitic transformation.
5 This makes it possible in the metallographic structure of the surface layer region in the
steel sheet for hot stamping to set the proportion of the crystal grains of one or two kinds of unauto-tempered martensite and lower bainite to 15.0% or more in terms of area percentage and to set the average dislocation density of the surface layer region to 4 ×
1015 m/m3 or more.
10 [0019]
As a second stage, a Zn-based plating layer containing 10 to 25 mass% of Ni is formed on the surface of the base steel sheet such that the amount attached to the single surface reaches 10 to 90 g/m2, thereby producing a steel sheet for hot stamping. [0020]
15 As a third stage, the average heating rate of heating before hot stamping is
controlled, thereby diffusing Ni in the plating layer disposed on the surface of the base
steel sheet into the surface layer region of the base steel sheet.
[0021]
Usually, in hot-rolled steel sheets having a high dislocation density that contain
20 0.15 mass% or more of C, have a metallographic structure including martensite, and are
not tempered, ductility, toughness, and hydrogen embrittlement resistance deteriorate. Additionally, in the case of carrying out cold rolling after coiling, since the above-described hot-rolled steel sheets do not have excellent ductility, cracking is likely to occur. Therefore, it is usual that the above-described hot-rolled steel sheets are
25 tempered after hot rolling and before post processes. In order to improve the
7

bendability and hydrogen embrittlement resistance of hot-rolled steel sheets, it is
important to improve the ductility of the surface layer region, and thus there are also
cases where a treatment for softening the surface layer region (for example, a surface
layer decarburization treatment) is carried out on the above-described steel sheets.
5 [0022]
In addition, usually, when steel sheets containing 0.15 mass% or more of C are hot-stamped, there are cases where the hot-stamped articles are not excellent in terms of bendability. [0023]
10 However, in the present embodiment, the metallographic structure of the surface
layer region in the steel sheet for hot stamping is put into a preferred state, and Ni in the plating layer disposed on the surface of the base steel sheet is diffused into the surface layer region of the base steel sheet by heating before hot stamping, whereby it is possible to improve the bendability or hydrogen embrittlement resistance of the hot-stamped
15 article even without tempering after hot stamping.
[0024]
The metallographic structure of the surface layer region in the steel sheet for hot stamping that is applied to the hot-stamped article according to the present embodiment includes 15.0% or more of the crystal grains of one or two kinds of unauto-tempered
20 martensite and lower bainite in terms of area percentage. Inside the crystal grains of
unauto-tempered martensite and lower bainite, the dislocation density is high, and these crystal grains have a small crystal grain size. Therefore, in the steel sheet for hot stamping according to the present embodiment, heating before hot stamping makes it easy for Ni contained in the plating layer to diffuse into the surface layer region through
25 crystal grain boundaries and dislocations in the surface layer region of the base steel
8

sheet as passages. Since Ni is an austenite-stabilizing element, when Ni in the plating
layer diffuses into the surface layer region of the base steel sheet to increase the
concentration of Ni in the surface layer region of the base steel sheet, residual austenite is
likely to remain in the surface layer region of the base steel sheet that configures the hot-
5 stamped article. The bendability of the hot-stamped article can be improved by causing
a predetermined amount of residual austenite to remain in the surface layer region of the
base steel sheet that configures the hot-stamped article using not only C but also Ni.
The present inventors found that, in order to diffuse Ni into the surface layer region of
the base steel sheet to cause a predetermined amount of residual austenite to remain in
10 the surface layer region of the base steel sheet that configures the hot-stamped article,
there is a need to set the average heating rate of heating before hot stamping to slower than 100 °C/s. When the average heating rate of heating before hot stamping is set to slower than 100 °C/s, Ni diffuses through not only crystal grain boundaries but also dislocations in the surface layer region of the base steel sheet as passages, which makes it
15 possible to uniformly diffuse Ni into the surface layer region.
[0025]
Hereinafter, the hot-stamped article according to the present embodiment and a method for manufacturing the same will be described in detail. First, reasons for limiting the chemical composition of the steel sheet that configures the hot-stamped
20 article according to the present embodiment will be described.
Numerical limitation ranges to be described below include the lower limit value and the upper limit value in the range. Numerical values with an expression of “less than” or “more than” do not include the numerical value in the numerical range. Regarding the chemical composition, “%” indicates “mass%” in all cases.
25 [0026]
9

The base steel sheet that configures the hot-stamped article according to the
present embodiment contains, as chemical components, by mass%, C: 0.15% or more
and less than 0.70%, Si: 0.005% or more and 0.250% or less, Mn: 0.30% or more and
3.00% or less, sol. Al: 0.0002% or more and 0.500% or less, P: 0.100% or less, S:
5 0.1000% or less, N: 0.0100% or less with a remainder including Fe and impurities.
[0027]
“C: 0.15% or more and less than 0.70%”
C is an important element for obtaining a tensile strength of 1500 MPa or higher
in the hot-stamped article. When the C content is less than 0.15%, martensite becomes
10 soft, and it is difficult to obtain a tensile strength of 1500 MPa or higher. In addition,
when the C content is less than 0.15%, the area rate of unauto-tempered martensite and
lower bainite decreases. Therefore, the C content is set to 0.15% or more. The C
content is preferably 0.20% or more and more preferably 0.30% or more. On the other
hand, when the C content is 0.70% or more, a coarse carbide is generated, breakage is
15 likely to occur, and the bendability and hydrogen embrittlement resistance of the hot-
stamped article deteriorate. Therefore, the C content is set to less than 0.70%. The C content is preferably 0.50% or less and more preferably 0.45% or less. [0028]
“Si: 0.005% or more and 0.250% or less”
20 Si is an element that is contained to secure hardenability. When the Si content
is less than 0.005%, the above-described effect cannot be obtained, and, in the steel sheet
for hot stamping, there are cases where the dislocation density decreases and cases where
unauto-tempered martensite and lower bainite cannot be obtained, which makes it
impossible to obtain a desired metallographic structure in the hot-stamped article.
25 Therefore, the Si content is set to 0.005% or more. Even when more than 0.250% of Si
10

is contained, the above-described effect is saturated, and thus the Si content is set to
0.250% or less. The Si content is preferably 0.210% or less.
[0029]
“Mn: 0.30% or more and 3.00% or less”
5 Mn is an element that contributes to improvement in the strength of the hot-
stamped article by solid solution strengthening. When the Mn content is less than 0.30%, the solid solution strengthening capability is poor, martensite becomes soft, and it is difficult to obtain a tensile strength of 1500 MPa or higher in the hot-stamped article. Therefore, the Mn content is set to 0.30% or more. The Mn content is preferably 0.50%
10 or more or 0.70% or more. On the other hand, when the Mn content is set to more than
3.00%, a coarse inclusion is generated in steel, breakage is likely to occur, and the bendability and hydrogen embrittlement resistance of the hot-stamped article deteriorate. Therefore, the upper limit is set to 3.00%. The Mn content is preferably 2.50% or less or 2.00% or less.
15 [0030]
“sol. Al (acid-soluble Al): 0.0002% or more and 0.500% or less”
Al is an element having an action of deoxidizing molten steel to make the steel sound (suppressing the generation of a defect such as a blowhole in steel). When the sol. Al content is less than 0.0002%, since molten steel is not sufficiently deoxidized, and
20 the above-described effect cannot be obtained, the sol. Al content is set to 0.0002% or
more. The sol. Al content is preferably 0.0010% or more or 0.0020% or more. On the other hand, when the sol. Al content exceeds 0.500%, a coarse oxide is generated in steel, and the bendability and hydrogen embrittlement resistance of the hot-stamped article deteriorate. Therefore, the sol. Al content is set to 0.500% or less. The sol. Al content
25 is preferably 0.400% or less or 0.300% or less.
11

[0031]
“P: 0.100% or less”
P is an element that is segregated in grain boundaries and degrades the strength
of the grain boundaries. When the P content exceeds 0.100%, the strength of grain
5 boundaries significantly decreases, and the bendability and hydrogen embrittlement
resistance of the hot-stamped article deteriorate. Therefore, the P content is set to
0.100% or less. The P content is preferably 0.050% or less. The lower limit of the P
content is not particularly limited. However, when the P content is decreased to lower
than 0.0001%, the dephosphorization cost increases significantly, which is not preferable
10 economically, and thus the lower limit of the P content may be set to 0.0001% in actual
operation. [0032]
“S: 0.1000% or less”
S is an element that forms an inclusion in steel. When the S content exceeds
15 0.1000%, a large amount of an inclusion is generated in steel, and the bendability and
hydrogen embrittlement resistance of the hot-stamped article deteriorate. Therefore, the
S content is set to 0.1000% or less. The S content is preferably 0.0050% or less. The
lower limit of the S content is not particularly limited. However, when the S content is
decreased to lower than 0.00015%, the desulfurization cost increases significantly, which
20 is not preferable economically, and thus the lower limit of the S content may be set to
0.00015% in actual operation. [0033]
“N: 0.0100% or less”
N is an impurity and an element that forms a nitride in steel to degrade the
25 toughness and hydrogen embrittlement resistance of the hot-stamped article. When the
12

N content exceeds 0.0100%, a coarse nitride is generated in steel to significantly degrade
the bendability and hydrogen embrittlement resistance of the hot-stamped article.
Therefore, the N content is set to 0.0100% or less. The N content is preferably 0.0075%
or less. The lower limit of the N content is not particularly limited. However, when
5 the N content is decreased to lower than 0.0001%, the denitrification cost increases
significantly, which is not preferable economically, and thus the lower limit of the N content may be set to 0.0001% in actual operation. [0034]
The remainder of the chemical composition of the base steel sheet that
10 configures the hot-stamped article according to the present embodiment is Fe and
impurities. As the impurity, exemplified is an element that is inevitably contained by accident from a steel raw material or a scrap and/or in a steel making process and is permitted to an extent that the properties of the hot-stamped article according to the present embodiment are not impaired.
15 [0035]
The Ni content of the base steel sheet that configures the hot-stamped article according to the present embodiment is less than 0.005%. Since Ni is an expensive element, in the present embodiment, it is possible to suppress the cost at a low level compared with a case where the Ni content is set to 0.005% or more by intentionally
20 including Ni.
[0036]
The base steel sheet that configures the hot-stamped article according to the present embodiment may contain the following elements as arbitrary elements. In a case where the following arbitrary elements are not contained, the amount thereof is 0%.
25 [0037]
13

“Nb: 0% or more and 0.150% or less”
Nb is an element that contributes to improvement in the strength of the hot-
stamped article by solid solution strengthening and thus may be contained as necessary.
In a case where Nb is contained, the Nb content is preferably set to 0.010% or more in
5 order to reliably exhibit the above-described effect. The Nb content is more preferably
0.035% or more. On the other hand, even when more than 0.150% of Nb is contained,
the above-described effect is saturated, and thus the Nb content is preferably set to
0.150% or less. The Nb content is more preferably 0.120% or less.
[0038]
10 “Ti: 0% or more and 0.150% or less”
Ti is an element that contributes to improvement in the strength of the hot-
stamped article by solid solution strengthening and thus may be contained as necessary.
In a case where Ti is contained, the Ti content is preferably set to 0.010% or more in
order to reliably exhibit the above-described effect. The Ti content is preferably
15 0.020% or more. On the other hand, even when more than 0.150% of Ti is contained,
the above-described effect is saturated, and thus the Ti content is preferably set to 0.150% or less. The Ti content is more preferably 0.120% or less. [0039]
“Mo: 0% or more and 1.000% or less”
20 Mo is an element that contributes to improvement in the strength of the hot-
stamped article by solid solution strengthening and thus may be contained as necessary.
In a case where Mo is contained, the Mo content is preferably set to 0.005% or more in
order to reliably exhibit the above-described effect. The Mo content is more preferably
0.010% or more. On the other hand, even when more than 1.000% of Mo is contained,
25 the above-described effect is saturated, and thus the Mo content is preferably set to
14

1.000% or less. The Mo content is more preferably 0.800% or less. [0040]
“Cr: 0% or more and 1.000% or less”
Cr is an element that contributes to improvement in the strength of the hot-
5 stamped article by solid solution strengthening and thus may be contained as necessary.
In a case where Cr is contained, the Cr content is preferably set to 0.005% or more in
order to reliably exhibit the above-described effect. The Cr content is more preferably
0.100% or more. On the other hand, even when more than 1.000% of Cr is contained,
the above-described effect is saturated, and thus the Cr content is preferably set to
10 1.000% or less. The Cr content is more preferably 0.800% or less.
[0041]
“B: 0% or more and 0.0100% or less”
B is an element that is segregated in grain boundaries to improve the strength of
the grain boundaries and is thus contained as necessary. In a case where B is contained,
15 the B content is preferably set to 0.0005% or more in order to reliably exhibit the above-
described effect. The B content is preferably 0.0010% or more. On the other hand,
even when more than 0.0100% of B is contained, the above-described effect is saturated,
and thus the B content is preferably set to 0.0100% or less. The B content is more
preferably 0.0075% or less.
20 [0042]
“Ca: 0% or more and 0.0100% or less”
Ca is an element having an action of deoxidizing molten steel to make steel
sound. In order to reliably exhibit this action, the Ca content is preferably set to
0.0005% or more. On the other hand, even when more than 0.0100% of Ca is
25 contained, the above-described effect is saturated, and thus the Ca content is preferably
15

set to 0.0100% or less. [0043]
“REM: 0% or more and 0.30% or less”
REM is an element having an action of deoxidizing molten steel to make steel
5 sound. In order to reliably exhibit this action, the REM content is preferably set to
0.0005% or more. On the other hand, even when more than 0.30% of REM is contained, the above-described effect is saturated, and thus the REM content is preferably set to 0.30% or less.
In the present embodiment, REM refers to a total of 17 elements consisting of
10 Sc, Y, and lanthanoids, and the REM content refers to the total amount of these elements.
[0044]
The above-described chemical composition of the hot-stamped article may be
measured by an ordinary analysis method. For example, the chemical composition may
be measured using inductively coupled plasma-atomic emission spectrometry (ICP-
15 AES). C and S may be measured using an infrared absorption method after combustion,
and N may be measured using an inert gas melting-thermal conductivity method. The
chemical composition is preferably analyzed after the plating layer on the surface is
removed by machining.
[0045]
20 Next, the metallographic structure of the base steel sheet that configures the steel
sheet for hot stamping that is applied to the hot-stamped article according to the present
embodiment and the plating layer will be described.
[0046]

25 “In metallographic structure of surface layer region that is region from surface
16

of base steel sheet to depth of 50 μm, 15.0% or more of crystal grains of one or two kinds of unauto-tempered martensite and lower bainite in terms of area percentage are included and average dislocation density of surface layer region is 4 × 1015 m/m3 or more”
In the metallographic structure of the surface layer region that is a region from
5 the surface of the base steel sheet to a depth of 50 μm, the proportion of the crystal grains
of one or two kinds of unauto-tempered martensite and lower bainite is set to 15.0% or more in terms of area percentage, and the average dislocation density of the surface layer region is set to 4 × 1015 m/m3 or more, whereby it is possible to diffuse Ni in the plating layer into the surface layer region of the steel sheet by heating before hot stamping. The
10 upper limit of the average dislocation density of the surface layer region is not
particularly limited and the average dislocation density of the surface layer region may
be, for example, 5 × 1017 m/m3 or less or 1 × 1018 m/m3 or less.
[0047]
When the average heating rate of heating before hot stamping is set to slower
15 than 100 °C/s, Ni uniformly diffuses into the entire surface layer region, and it is possible
to set the area percentage of residual austenite in the surface layer region of the base steel sheet that configures the hot-stamped article to 8.0% or more. This makes it possible to improve the bendability of the hot-stamped article. [0048]
20 In order to obtain the above-described effect, the proportion of the crystal grains
of one or two kinds of unauto-tempered martensite and lower bainite in the surface layer region is set to 15.0% or more in terms of area percentage. The proportion of the crystal grains thereof is preferably 20.0% or more in terms of area percentage. From the viewpoint of suppressing the occurrence of cracking at the time of cold rolling in post
25 processes, the proportion of the crystal grains thereof may be set to 30.0% or more in
17

terms of area percentage. The upper limit of the proportion of the crystal grains of one
or two kinds of unauto-tempered martensite and lower bainite in the metallographic
structure of the surface layer region is not particularly limited and the proportion of the
crystal grains thereof may be, for example, 50% or less or 90% or less in terms of area
5 percentage. In addition, as a remaining structure other than the unauto-tempered
martensite and the lower bainite, the metallographic structure in the surface layer region may include one or more of ferrite, upper bainite, residual austenite, and martensite that has been auto-tempered. [0049]
10 The metallographic structure of the central portion of the base steel sheet is not
particularly limited, but is normally one or more of ferrite, upper bainite, lower bainite, martensite, residual austenite, an iron carbide, and an alloy carbide. Here, the central portion of the base steel sheet refers to a portion ranging from a position 0.2 mm apart from one surface of the base steel sheet in the sheet thickness central direction to a
15 position 0.2 mm apart from the other surface of the base steel sheet in the sheet thickness
central direction. [0050]
“Measurement of area fraction of crystal grains of unauto-tempered martensite and lower bainite”
20 A method for measuring the area fraction of the crystal grains of the unauto-
tempered martensite and the lower bainite in the surface layer region of the base steel sheet that configures the steel sheet for hot stamping that is applied to the hot-stamped article according to the present embodiment will be described. [0051]
25 First, a sample is cut out from an arbitrary position 50 mm or more apart from
18

the end face of the steel sheet for hot stamping such that a rolling-direction cross section
(sheet thickness section) perpendicular to the surface can be observed. While also
depending on a measuring instrument, the size of the sample is set to a size large enough
to observe approximately 10 mm in the rolling direction. A measurement surface of the
5 sample that corresponds to the above-described rolling-direction cross section is polished
using silicon carbide paper #600 to #1500, and then the measurement surface is mirror-finished using a liquid in which diamond powder having particle diameters of 1 to 6 μm is dispersed in a diluted solution such as alcohol or pure water. Next, the measurement surface is polished for eight minutes at room temperature using colloidal silica containing
10 no alkaline solution to remove strain present on the surface layer of the sample. After
that, the measurement surface is sputtered with argon ion beams using a cross section polisher manufactured by JEOL Ltd. At this time, the argon ion beams are radiated to the measurement surface from all directions using a specimen rotary holder manufactured by JEOL Ltd. for the purpose of suppressing the generation of streaky unevenness on the
15 measurement surface.
[0052]
At an arbitrary position of the measurement surface in the rolling direction, a 50 μm-long region from the interface between the plating layer and the surface of the base steel sheet to a depth of 50 μm is measured by the electron backscatter diffraction method
20 at measurement intervals of 0.1 μm, thereby obtaining crystal orientation information.
For the measurement, an instrument including a thermal field emission-type scanning electron microscope (JSM-7001F manufactured by JEOL Ltd.) and an EBSD detector (DVC 5-type detector manufactured by TSL) is used. At this time, the degree of vacuum in the instrument is set to 9.6 × 10-5 Pa or less, the accelerating voltage is set to
25 15 k V, the irradiation current level is set to 13, and the irradiation time of the electron
19

beam is set to 0.5 seconds/point. The obtained crystal orientation information is
analyzed using a “Grain Average Image Quality” function provided to software “OIM
Analysis (registered trademark)” accompanied by the EBSD analyzer. With this
function, it is possible to digitalize the definition of the crystal orientation information as
5 an IQ value and to discriminate a structure that is not auto-tempered. The unauto-
tempered martensite and the lower bainite have a poor crystallinity and thus have a small IQ value. A region showing an IQ value calculated to be 60000 or less with the “Grain Average Image Quality” function is defined as the unauto-tempered martensite and the lower bainite, and the area fraction thereof is calculated. The area percentage of the
10 crystal grains of the unauto-tempered martensite and the lower bainite in the surface layer
region is obtained by the above-described method. [0053]
“Measurement of average dislocation density”
Next, a method for measuring the average dislocation density in the surface
15 layer region will be described. The average dislocation density can be measured by the
X-ray diffraction method or transmission electron microscopic observation and is measured using the X-ray diffraction method in the present embodiment. [0054]
First, a sample is cut out from an arbitrary position 50 mm or more apart from
20 the end face of the base steel sheet. While also depending on a measuring instrument,
the size of the sample is set to a size of approximately 20 mm × 20 mm. The thickness of each of the front surface and rear surface of the sample is reduced by 25 μm using a mixed solution of distilled water (48%), a hydrogen peroxide solution (48%), and hydrofluoric acid (4%), thereby reducing the thickness by a total of 50 μm. Therefore,
25 regions 25 μm deep from the surfaces of the sample before the thickness reduction are
20

exposed. X-ray diffraction measurement is carried out on these exposed surfaces to
specify a plurality of diffraction peaks of body-centered cubic lattices. The average
dislocation density is analyzed from the half widths of these diffraction peaks, thereby
obtaining the average dislocation density of the surface layer region. Regarding the
5 analysis method, a modified Williamson-Hall method described in Non-Patent Document
1 is used. [0055]
“Plating layer being attached to single surface in amount of 10 g/m2 or more and 90 g/m2 or less and having Ni content of 10 mass% or more and 25 mass% or less with
10 remainder including Zn and impurity”
The steel sheet for hot stamping that is applied to the hot-stamped article according to the present embodiment has a plating layer on the surface of the base steel sheet that configures the steel sheet for hot stamping, the plating layer being attached to a single surface in an amount of 10 g/m2 or more and 90 g/m2 or less and having a Ni
15 content of 10 mass% or more and 25 mass% or less with a remainder including Zn and
impurities. This makes it possible to diffuse Ni into the surface layer region during heating and before hot stamping. [0056]
When the amount of the plating layer attached to a single surface is less than 10
20 g/m2 or the Ni content in the plating layer is less than 10 mass%, the amount of Ni that
concentrates in the surface layer region of the base steel sheet becomes small, and it is not possible to obtain a desired metallographic structure in the surface layer region after hot stamping. On the other hand, in a case where the amount attached to a single surface exceeds 90 g/m2 or the Ni content in the plating layer exceeds 25 mass%, Ni
25 concentrates excessively in the interface between the plating layer and the base steel
21

sheet, the adhesion between the plating layer and the base steel sheet deteriorates, it
becomes difficult for Ni in the plating layer to diffuse into the surface layer region of the
base steel sheet, and it is not possible to obtain a desired metallographic structure in the
hot-stamped article after hot stamping.
5 The amount of the plating layer attached to a single surface is preferably 30 g/m2
or more and more preferably 40 g/m2 or more. In addition, the amount of the Ni plating layer attached to a single surface is preferably 80 g/m2 or less and more preferably 60 g/m2 or less. [0057]
10 The amount of a plate attached in the steel sheet for hot stamping and the Ni
content in the plating layer are measured by the following methods.
The amount of the plate attached is measured by collecting a test piece from an arbitrary position in the steel sheet for hot stamping according to the testing method described in JIS H 0401: 2013. Regarding the Ni content in the plating layer, a test
15 piece is collected from an arbitrary position in the steel sheet for hot stamping according
to the testing method described in JIS K 0150: 2005, and the Ni content at a 1/2 position of the total thickness of the plating layer is measured, thereby obtaining the Ni content in the plating layer in the steel sheet for hot stamping. [0058]
20 The sheet thickness of the steel sheet for hot stamping that is applied to the hot-
stamped article according to the present embodiment is not particularly limited, but is preferably set to 0.5 to 3.5 mm from the viewpoint of the weight reduction of automotive bodies. [0059]
25 Next, the hot-stamped article according to the present embodiment will be
22

described. [0060]

“Metallographic structure of surface layer region that is region from surface of
5 base steel sheet to depth of 50 μm includes 80.0% or more of martensite and 8.0% or
more of residual austenite in terms of area percentage”
The metallographic structure of the surface layer region that is a region from the
surface of the base steel sheet that configures the hot-stamped article to a depth of 50 μm
includes 80.0% or more of martensite and 8.0% or more of residual austenite in terms of
10 area percentage, whereby it is possible to obtain excellent strength and excellent
bendability. As a remaining structure other than the martensite and the residual
austenite in the surface layer region, one or more of ferrite, upper bainite, and lower
bainite may be included.
[0061]
15 In a case where the proportion of the martensite is less than 80.0% in terms of
area percentage in the metallographic structure of the surface layer region, it is not
possible to obtain a desired strength in the hot-stamped article, and it is not possible to
apply the hot-stamped article to automotive parts or the like. The proportion of the
martensite is preferably 85.0% or more in terms of area percentage. The proportion of
20 the martensite may be set to 92.0% or less in terms of area percentage.
[0062]
In addition, when the proportion of the residual austenite is less than 8.0% in
terms of area percentage, the bendability of the hot-stamped article deteriorates. The
proportion of the residual austenite is preferably 10.0% or more in terms of area
25 percentage. There is no need to particularly limit the upper limit; however, in a case
23

where it is attempted to obtain a higher yield strength, the proportion of the residual
austenite may be set to 15.0% or less in terms of area percentage.
[0063]
Next, a method for measuring the metallographic structure of the surface layer
5 region will be described.
First, samples are cut out from an arbitrary position 50 mm or more apart from the end face of the hot-stamped article such that a rolling-direction cross section (sheet thickness cross section) perpendicular to the surface can be observed. While also depending on a measuring instrument, the size of the sample is set to a size large enough
10 to observe approximately 10 mm in the rolling direction. The area fractions of the
residual austenite and the martensite are measured using the samples collected by the
above-described method.
[0064]
“Measurement of area fraction of residual austenite”
15 A measurement surface of the sample that corresponds to the above-described
rolling-direction cross section is polished using silicon carbide paper #600 to #1500, and then the measurement surface is mirror-finished using a liquid in which diamond powder having particle diameters of 1 to 6 μm is dispersed in a diluted solution such as alcohol or pure water. Next, the measurement surface is polished for eight minutes at room
20 temperature using colloidal silica containing no alkaline solution to remove strain present
on the surface layer of the sample. At an arbitrary position of the measurement surface of the sample in the rolling direction, a 50 μm-long region from the surface of the base steel sheet to a depth of 50 μm is measured by the electron backscatter diffraction method at measurement intervals of 0.1 μm, thereby obtaining crystal orientation information.
25 For the measurement, an instrument including a thermal field emission-type scanning
24

electron microscope (JSM-7001F manufactured by JEOL Ltd.) and an EBSD detector
(DVC 5-type detector manufactured by TSL) is used. At this time, the degree of
vacuum in the instrument is set to 9.6 × 10-5 Pa or less, the accelerating voltage is set to
15 k V, the irradiation current level is set to 13, and the irradiation time of the electron
5 beam is set to 0.01 seconds/point. The area fraction of the residual austenite is
calculated from the obtained crystal orientation information using a “Phase Map” function provided to software “OIM Analysis (registered trademark)” accompanied by the EBSD analyzer, thereby obtaining the area fraction of the residual austenite in the surface layer region. A structure having an fcc structure as the crystal structure is
10 determined to be the residual austenite.
[0065]
“Measurement of area fraction of martensite”
A measurement surface of the sample (a sample different from the sample used for the measurement of the area fraction of the residual austenite) is polished using
15 silicon carbide paper #600 to #1500, then, the measurement surface is mirror-finished
using a liquid in which diamond powder having particle diameters of 1 to 6 μm is dispersed in a diluted solution such as alcohol or pure water, and Nital-etched. Next, a region within 50 μm from the end portion of the observation surface on a side toward the surface of the base steel sheet is observed as an observation visual field using a thermal
20 field emission-type scanning electron microscope (JSM-7001F manufactured by JEOL
Ltd.). The area fraction of martensite can be obtained as the total of the area fractions of tempered martensite and fresh martensite. The tempered martensite is an aggregate of lath crystal grains and is differentiated as a structure in which there are two or more extension directions of an iron carbide. The fresh martensite is not sufficiently etched
25 by Nital etching and thus can be differentiated from other structures that are etched.
25

Here, since the residual austenite is also, similar to the fresh martensite, not sufficiently
etched, the area percentage of the fresh martensite is obtained from the difference
between the area fraction of the structures that are not etched by Nital etching and the
area fraction of the residual austenite calculated above. The area fraction of the
5 martensite in the surface layer region is obtained by calculating the total of the area
percentages of the tempered martensite and the fresh martensite obtained by the above-described method. [0066]
“Concentration of Ni in surface layer region is 8 mass% or more”
10 The concentration of Ni in the surface layer region of the base steel sheet that
configures the hot-stamped article is 8 mass%. When the concentration of Ni in the
surface layer region is set to 8 mass% or more, the residual austenite in the surface layer
region is stabilized, and it is possible to increase the amount of the residual austenite in
the hot-stamped article. As a result, it is possible to improve the bendability of the hot-
15 stamped article. The concentration of Ni in the surface layer region is preferably 10
mass% or more and more preferably 12 mass% or more. In addition, the upper limit of
the concentration of Ni in the surface layer region is not particularly limited, and the
concentration of Ni may be, for example, 15 mass% or less or may be 20 mass% or less.
[0067]
20 “Method for measuring concentration of Ni in surface layer region”
A method for measuring the concentration of Ni in the surface layer region will be described.
First, a sample is cut out from an arbitrary position 50 mm or more apart from
the end face of the hot-stamped article. While also depending on a measuring
25 instrument, the size of the sample is set to a size of approximately 20 mm × 20 mm.
26

Regarding the measurement of the concentration of Ni, an analysis is carried out in the
depth direction along the sheet thickness direction from the surface of the base steel sheet
by glow discharge optical emission spectrometry at 10 points on the surface of the
sample, the concentrations of Ni at positions 25 μm deep from the surface of the base
5 steel sheet in the sheet thickness direction are obtained, and the average value of the 10
points is calculated. The obtained average value is defined as the concentration of Ni in
the surface layer region.
[0068]
“Plating layer having amount attached to single surface of 10 g/m2 or more and
10 90 g/m2 or less and having Ni content of 10 mass% or more and 25 mass% or less with
the remainder including Zn and impurity”
The hot-stamped article according to the present embodiment has a plating layer on the surface of the base steel sheet that configures the hot-stamped article, the plating layer having an amount attached to a single surface of 10 g/m2 or more and 90 g/m2 or
15 less and having a Ni content of 10 mass% or more and 25 mass% or less with a
remainder including Zn and impurities. [0069]
When the amount of the plating layer attached to a single surface of the base steel sheet is less than 10 g/m2 or the Ni content in the plating layer is less than 10
20 mass%, the amount of Ni that concentrates in the surface layer region of the base steel
sheet becomes small, and it is not possible to obtain a desired metallographic structure in the surface layer region after hot stamping. On the other hand, in a case where the amount of the plating layer attached to a single surface of the base steel sheet exceeds 90 g/m2 or the Ni content in the plating layer exceeds 25 mass%, Ni concentrates
25 excessively in the interface between the plating layer and the base steel sheet, the
27

adhesion between the plating layer and the base steel sheet deteriorates, it becomes
difficult for Ni in the plating layer to diffuse into the surface layer region of the base steel
sheet, and it is not possible to obtain a desired metallographic structure in the hot-
stamped article.
5 The amount of the plating layer attached to a single surface of the base steel
sheet is preferably 30 g/m2 or more and more preferably 40 g/m2 or more. In addition, the amount of the Ni plating layer attached to a single surface of the base steel sheet is preferably 80 g/m2 or less and more preferably 60 g/m2 or less. [0070]
10 The amount of the plate attached in the hot-stamped article and the Ni content in
the plating layer are measured by the following methods.
The amount of the plate attached is measured by collecting a test piece from an arbitrary position in the hot-stamped article according to the testing method described in JIS H 0401: 2013. Regarding the Ni content in the plating layer, a test piece is collected
15 from an arbitrary position in the hot-stamped article according to the testing method
described in JIS K 0150: 2005, and the Ni content at a 1/2 position of the total thickness of the plating layer is measured, thereby obtaining the Ni content in the plating layer in the hot-stamped article. [0071]
20 Next, a preferred method for manufacturing the steel sheet for hot stamping that
is applied to the hot-stamped article according to the present embodiment will be described. [0072]

25 A steel piece (steel) that is to be subjected to hot rolling may be, for example, a
28

steel piece manufactured by a usual method such as a continuously cast slag or a thin slab
caster as long as the steel piece is manufactured by a normal method. Rough rolling
may also be carried out by a usual method and is not particularly limited.
[0073]
5 “Finishing rolling”
In the final rolling (final pass) of finishing rolling, it is necessary to carry out the finishing rolling in a temperature range of the A3 point or higher at a rolling reduction of smaller than 20%. When the finishing rolling is carried out at a temperature of lower than the A3 point or the rolling reduction is 20% or larger in the final rolling of the
10 finishing rolling, ferrite is formed in the surface layer region, and it is not possible to set
the proportion of the crystal grains of one or two kinds of the unauto-tempered martensite and the lower bainite to 15.0% or more in terms of area percentage. The A3 point is represented by Formula (1). [0074]
15 A3 point = 850 + 10 × (C + N) × Mn + 350 × Nb + 250 × Ti + 40 × B + 10 × Cr
+ 100 × Mo ∙∙∙ (1)
In Formula (1), C, N, Mn, Nb, Ti, B, Cr, and Mo indicate the amounts (mass%) of the individual elements. [0075]
20 “Cooling”
After the end of the finishing rolling, cooling at an average cooling rate of 80 °C/s or faster is initiated within five seconds, and the base steel sheet is cooled to a temperature range of lower than 500°C and coiled. In addition, even after coiled, the base steel sheet is continuously cooled with water to room temperature. In a case where
25 the cooling initiation time exceeds five seconds, a case where the average cooling rate is
29

slower than 80 °C/s, or a case where the coiling initiation temperature is higher than
500°C, ferrite, pearlite, and upper bainite are likely to be formed, and it is impossible to
set the proportion of the crystal grains of one or two kinds of the unauto-tempered
martensite and the lower bainite to 15.0% or more in terms of area percentage in the
5 surface layer region. The average cooling rate at this time is calculated from a change
in the temperature of the surface of the steel sheet and indicates an average cooling rate while the temperature reaches the coiling initiation temperature from the finishing rolling temperature. [0076]
10 “Plating”
On the hot-rolled steel sheet as it is or after cold rolling, a plating layer being attached to a single surface in an amount of 10 g/m2 or more and 90 g/m2 or less and having a Ni content of 10 mass% or more and 25 mass% or less with a remainder including Zn and impurities is formed to obtain the steel sheet for hot stamping. In a
15 case where cold rolling is carried out before plating, the rolling reduction in the cold
rolling is not particularly limited, but is preferably set to 40% to 60% from the viewpoint of the shape stability of the steel sheet. The manufacturing of the steel sheet for hot stamping may additionally include a well-known manufacturing method such as pickling or tempered rolling before the plating. However, when tempering is carried out at a
20 temperature of the Ms point - 15°C or higher, it is not possible to set the proportion of the
crystal grains of one or two kinds of the unauto-tempered martensite and the lower bainite to 15.0% or more in terms of area percentage and to set the average dislocation density to 4 × 1015 m/m3 or more in the surface layer region, and consequently, it is not possible to obtain a hot-stamped article having a desired metallographic structure.
25 Therefore, in a case where there is a need to carry out tempering before the plating for
30

the reason of a high C content or the like, the tempering is carried out at a temperature of
lower than the Ms point - 15°C. The Ms point is represented by Formula (2).
[0077]
Ms = 493 - 300 × C - 33.3 × Mn - 11.1 × Si - 22.2 × Cr - 16.7 × Ni - 11.1 × Mo
5 ∙∙∙ (2)
In Formula (2), C, Mn, Si, Cr, Ni, and Mo indicate the amounts (mass%) of the individual elements. [0078]
Next, a method for manufacturing the hot-stamped article according to the
10 present embodiment using the steel sheet for hot stamping manufactured by the above-
described method will be described. [0079]

The hot-stamped article is manufactured by heating the steel sheet for hot
15 stamping obtained as described above in a temperature range of 500°C or higher and the
A3 point or lower at an average heating rate of slower than 100 °C/s, then, holding the
steel sheet for hot stamping at a temperature of the A3 point or higher and the A3 point +
150°C or lower, hot-stamping the steel sheet for hot stamping such that the elapsed time
from the initiation of the heating to the initiation of forming reaches a predetermined
20 time or shorter, and cooling the steel sheet for hot stamping to room temperature.
In addition, in order to adjust the strength of the hot-stamped article, a softened
region may be formed by tempering a partial region or the entire region of the hot-
stamped article at a temperature of lower than the Ms point - 15°C.
[0080]
25 The steel sheet for hot stamping is heated in a temperature range of 500°C or
31

higher and the A3 point or lower at an average heating rate of slower than 100 °C/s, and
the elapsed time from the initiation of the heating to the initiation of the forming is set to
240 to 480 seconds, whereby it is possible to obtain a desired metallographic structure in
the surface layer region. This makes it possible to improve the bendability of the hot-
5 stamped article. The average heating rate is preferably slower than 80 °C/s. The
lower limit of the average heating rate is not particularly limited; however, in actual
operation, the average heating rate set to slower than 0.01 °C/s causes an increase in the
manufacturing costs. Therefore, the average heating rate may be set to 0.01 °C/s or
faster. The elapsed time from the initiation of the heating to the initiation of the forming
10 is preferably set to 280 seconds or longer and 320 seconds or shorter.
[0081]
The holding temperature during the hot stamping is preferably set to the A3 point + 10°C or higher. In addition, the holding temperature during the hot stamping is preferably set to the A3 point + 150°C or lower. In addition, the average cooling rate
15 after the hot stamping is preferably set to 10 °C/s or faster.
[Examples] [0082]
Next, examples of the present invention will be described. Conditions in the examples are examples of conditions adopted to confirm the feasibility and effect of the
20 present invention, and the present invention is not limited to these examples of
conditions. The present invention is capable of adopting a variety of conditions as long as the objective of the present invention is achieved without departing from the gist of the present invention. [0083]
25 Steel pieces manufactured by casting molten steel having a chemical
32

composition shown in Tables 1 and 2 were hot-rolled, cold-rolled, and plated under
conditions shown in Tables 3 and 4, thereby obtaining steel sheets for hot stamping
shown in Tables 3 and 4. The obtained steel sheets for hot stamping were hot-stamped
by carrying out a heat treatment shown in Tables 5 and 6, thereby obtaining hot-stamped
5 articles shown in Tables 5 and 6. A partial softened region was formed by irradiating a
part of the hot-stamped article with a laser, cooling the irradiated portion to lower than the Ms - 15°C, and tempering the irradiated portion.
Underlined values in the tables indicate that the values are outside the scope of
the present invention, the preferred manufacturing conditions are not satisfied, or
10 property values are not preferable.
33

[0084]
[Table 1]

Steel No. Chemical composition (mass%) with remainder of Fe and impurities A3 (°C) Note

C Si Mn P S sol. Al N Nb Ti Mo Cr B Ca REM

1 0.16 0.250 1.10 0.006 0.0020 0.030 0.0026 0.130 865 Invention steel
2 0.44 0.250 1.80 0.010 0.0090 0.400 0.0040 0.03 858 Invention steel
3 0.23 0.250 1.20 0.010 0.0100 0.030 0.0050 0.020 0.200 860 Invention steel
4 0.08 0.220 0.81 0.008 0.0009 0.044 0.0026 851 Comparative steel
5 0.16 0.150 0.71 0.011 0.0006 0.043 0.0037 851 Invention steel
6 0.31 0.250 0.80 0.015 0.0011 0.041 0.0039 853 Invention steel
7 0.36 0.180 0.81 0.005 0.0005 0.045 0.0037 853 Invention steel
8 0.44 0.250 0.71 0.015 0.0007 0.034 0.0042 853 Invention steel
9 0.67 0.190 0.71 0.014 0.0003 0.037 0.0035 855 Invention steel
10 0.78 0.250 0.90 0.014 0.0011 0.031 0.0026 857 Comparative steel
11 0.36 0.002 0.86 0.005 0.0003 0.041 0.0032 853 Comparative steel
12 0.38 0.007 0.83 0.005 0.0011 0.050 0.0030 853 Invention steel
13 0.37 0.210 0.72 0.011 0.0007 0.030 0.0041 853 Invention steel
14 0.37 0.240 0.90 0.015 0.0007 0.047 0.0037 853 Invention steel
15 0.37 0.150 0.15 0.005 0.0003 0.035 0.0030 851 Comparative +steel
16 0.44 0.170 0.44 0.007 0.0005 0.049 0.0029 852 Invention steel
17 0.36 0.240 0.82 0.010 0.0011 0.035 0.0038 853 Invention steel
18 0.37 0.180 1.29 0.007 0.0010 0.030 0.0028 855 Invention steel
19 0.37 0.150 1.99 0.009 0.0005 0.035 0.0042 857 Invention steel
20 0.38 0.170 2.89 0.007 0.0005 0.046 0.0037 861 Invention steel
21 0.38 0.150 3.15 0.012 0.0009 0.036 0.0042 862 Comparative steel
22 0.38 0.240 0.82 0.0004 0.0007 0.045 0.0026 853 Invention steel
34

23 0.36 0.160 0.90 0.009
24 0.36 0.150 0.77 0.094
25 0.37 0.190 0.84 0.123
26 0.36 0.200 0.75 0.009
27 0.37 0.150 0.81 0.013
28 0.37 0.190 0.89 0.008
29 0.36 0.230 0.80 0.007
30 0.36 0.190 0.72 0.006
[0085]
0.0006 0.030 0.0038 853 Invention steel
0.0010 0.043 0.0033 853 Invention steel
0.0010 0.033 0.0032 853 Comparative steel
0.0002 0.047 0.0045 853 Invention steel
0.0003 0.031 0.0029 853 Invention steel
0.0022 0.044 0.0032 853 Invention steel
0.0900 0.049 0.0030 853 Invention steel
0.1334 0.045 0.0025 853 Comparative steel

[Table 2]

Steel No. Chemical composition (mass%) with remainder of Fe and impurities A3 (°C) Note

C Si Mn P S sol. Al N Nb Ti Mo Cr B Ca REM

31 0.38 0.230 0.79 0.013 0.0008 0.0001 0.0027 853 Comparative steel
32 0.38 0.160 0.85 0.010 0.0009 0.0003 0.0033 853 Invention steel
33 0.35 0.200 0.72 0.014 0.0007 0.0029 0.0042 853 Invention steel
34 0.37 0.160 0.73 0.006 0.0006 0.031 0.0026 853 Invention steel
35 0.35 0.240 0.83 0.009 0.0008 0.494 0.0034 853 Invention steel
36 0.37 0.240 0.84 0.011 0.0007 0.581 0.0040 853 Comparative steel
37 0.37 0.220 0.89 0.007 0.0007 0.035 0.0001 853 Invention steel
38 0.38 0.150 0.89 0.009 0.0008 0.038 0.0073 853 Invention steel
39 0.38 0.190 0.71 0.007 0.0007 0.039 0.0090 853 Invention steel
40 0.36 0.210 0.73 0.008 0.0003 0.035 0.0160 853 Comparative steel
41 0.37 0.230 0.87 0.009 0.0006 0.031 0.0025 0.012 857 Invention steel
42 0.36 0.170 0.70 0.009 0.0009 0.046 0.0030 0.032 864 Invention steel
43 0.37 0.220 0.73 0.008 0.0004 0.033 0.0038 0.120 895 Invention steel
44 0.37 0.230 0.90 0.009 0.0011 0.044 0.0044 0.013 857 Invention steel
35

45 0.35 0.170 0.89 0.011 0.0007 0.043 0.0028 0.036 862 Invention steel
46 0.36 0.170 0.88 0.007 0.0004 0.031 0.0033 0.140 888 Invention steel
47 0.36 0.210 0.80 0.005 0.0003 0.037 0.0035 0.006 854 Invention steel
48 0.37 0.200 0.78 0.009 0.0010 0.031 0.0026 0.012 854 Invention steel
49 0.38 0.160 0.82 0.015 0.0009 0.031 0.0041 0.980 951 Invention steel
50 0.36 0.230 0.77 0.011 0.0008 0.043 0.0038 0.006 853 Invention steel
51 0.35 0.160 0.70 0.005 0.0006 0.047 0.0026 0.009 853 Invention steel
52 0.37 0.250 0.83 0.006 0.0010 0.033 0.0039 0.960 863 Invention steel
53 0.37 0.150 0.70 0.015 0.0008 0.031 0.0044 0.0006 853 Invention steel
54 0.36 0.230 0.86 0.005 0.0003 0.050 0.0044 0.0011 853 Invention steel
55 0.36 0.160 0.74 0.015 0.0006 0.034 0.0044 0.0090 853 Invention steel
56 0.36 0.160 0.78 0.015 0.0006 0.037 0.0039 0.0080 853 Invention steel
57 0.36 0.190 0.80 0.010 0.0006 0.034 0.0027 0.28 853 Invention steel
58 0.14 0.110 0.84 0.011 0.0008 0.036 0.0031 851 Comparative steel
59 0.20 0.210 1.32 0.012 0.0007 0.028 0.0027 853 Invention steel
[0086]
[Table 3]

Steel No. Steel sheet No. Finishing rolling Cooling Coiling Cold rolling Heat
treatment
before
plating Steel sheet for hot stamping Note

Final
rolling
reduction
of
finishing
rolling (%) Finishing
rolling
temperature
(°C) Time
until
initiation
of
cooling
(s) Cooling
rate
(°C/s) Coiling
initiation
temperature
(°C) Rolling
reduction
(%) Heating
temperature
(°C) Amount
of plate
attached
(g/m2) Ni content
in
plating
layer
(mass
%) Average dislocation
density (1014 m/m3) Unauto-martensite and lower bainite (area%) Sheet
thickness
(mm)

1 1 6 910 3 38 571 41 N/A 39 15 1 4.9 1.6 Comparative steel
2 2 5 921 2 32 596 40 N/A 55 12 29 2.1 1.6 Comparative steel
36

3 3 5 934 3 51 397 50 773 41 12 21 6.3 1.6 Comparative steel
4 4 9 954 1 126 372 53 N/A 56 15 3 9.8 1.6 Comparative steel
5 5 6 884 4 115 369 58 N/A 50 17 41 18.4 2.0 Invention steel
6 6 8 917 2 133 345 45 N/A 41 17 96 21.2 1.9 Invention steel
7 7 10 901 1 123 330 44 N/A 54 25 187 21.9 1.5 Invention steel
8 8 10 897 4 103 266 49 N/A 57 16 345 18.5 1.7 Invention steel
9 9 6 924 1 115 261 53 N/A 40 17 948 21.3 1.6 Invention steel
10 10 10 898 1 115 316 43 N/A 53 18 1120 24.7 1.3 Comparative steel
11 11 8 905 1 142 292 55 N/A 48 18 155 18.1 1.3 Comparative steel
12 12 5 887 4 118 353 60 N/A 58 15 230 19.9 1.6 Invention steel
13 13 5 926 3 146 390 47 N/A 48 15 223 22.3 1.6 Invention steel
14 14 9 890 3 134 283 55 N/A 46 15 219 17.6 1.8 Invention steel
15 15 8 933 1 123 329 53 N/A 58 18 11 3.7 1.6 Comparative steel
16 16 6 885 4 115 329 52 N/A 51 17 372 22.0 1.3 Invention steel
17 17 9 900 3 133 379 45 N/A 43 18 157 22.7 1.2 Invention steel
18 18 7 876 4 134 250 42 N/A 52 17 184 16.6 1.7 Invention steel
19 19 10 942 1 105 315 59 N/A 50 17 229 20.3 1.9 Invention steel
20 20 10 960 3 125 273 49 N/A 45 17 217 22.4 2.0 Invention steel
21 21 5 895 2 147 343 41 N/A 45 17 192 24.4 1.6 Comparative steel
22 22 8 931 3 123 354 43 N/A 60 17 178 20.3 1.8 Invention steel
23 23 10 961 1 138 272 48 N/A 47 15 159 18.4 2.0 Invention steel
24 24 10 955 2 124 330 45 N/A 60 15 189 18.9 1.2 Invention steel
37

25 25 5 901 1 104 310 50 N/A 58 15 237 20.9 1.6 Comparative steel
26 26 5 892 4 134 329 52 N/A 60 16 206 21.2 1.2 Invention steel
27 27 10 938 3 104 251 41 N/A 52 17 164 19.2 1.5 Invention steel
28 28 7 953 1 149 372 60 N/A 50 18 172 23.4 1.8 Invention steel
29 29 10 943 1 126 382 41 N/A 53 17 201 21.5 1.6 Invention steel
30 30 7 948 1 148 260 44 N/A 51 16 237 16.9 1.2 Comparative steel
31 31 5 895 1 115 328 52 N/A 46 16 152 18.5 1.8 Comparative steel
32 32 6 918 1 126 341 52 N/A 40 15 214 22.4 1.2 Invention steel
33 33 6 885 4 106 314 47 N/A 43 18 181 18.0 1.5 Invention steel
34 34 5 883 3 149 266 45 N/A 46 15 156 19.9 1.8 Invention steel
35 35 6 947 1 131 387 57 N/A 51 15 151 22.3 1.9 Invention steel
36 36 8 877 3 109 291 47 N/A 47 15 206 16.1 1.6 Comparative steel
37 37 9 947 2 118 365 45 N/A 52 16 171 21.4 1.7 Invention steel
38 38 6 924 4 145 393 45 N/A 46 15 212 23.1 1.8 Invention steel
39 39 9 938 3 143 354 51 N/A 60 16 173 22.2 1.2 Invention steel
40 40 5 943 1 144 395 40 N/A 60 16 220 23.7 1.8 Comparative steel
[0087]
[Table 4]

Steel No. Steel sheet No. Finishing rolling Cooling Coiling Cold rolling Heat
treatment
before
plating Steel sheet for hot stamping Note

Final
rolling
reduction Finishing
rolling
temperature Time
until
initiation Cooling
rate
(°C/s) Coiling
initiation
temperature Rolling
reduction
(%) Heating
temperature
(°C) Amount of plate attached Ni
content
in Average
dislocation
density Unauto-martensite and lower bainite Sheet
thickness
(mm)

38

of
finishing
rolling (%) (°C) of
cooling
(s) (°C) (g/m2) plating
layer
(mass
%) (1014 m/m3) (area%)
41 41 9 921 2 114 394 58 N/A 45 16 169 23.1 2.0 Invention steel
42 42 9 898 1 106 330 48 N/A 58 15 229 18.9 1.8 Invention steel
43 43 10 952 4 131 376 55 N/A 59 15 233 23.2 1.6 Invention steel
44 44 5 902 4 119 291 52 N/A 45 16 219 19.7 1.2 Invention steel
45 45 6 929 4 131 342 42 N/A 42 18 223 22.4 1.5 Invention steel
46 46 10 929 3 117 316 54 N/A 58 17 219 21.5 2.0 Invention steel
47 47 9 896 4 149 269 55 N/A 42 17 226 17.5 1.5 Invention steel
48 48 10 928 2 110 331 46 N/A 48 17 223 20.5 1.8 Invention steel
49 49 9 987 2 102 386 58 N/A 58 17 176 23.4 1.3 Invention steel
50 50 5 953 2 109 343 43 N/A 42 17 198 19.7 1.6 Invention steel
51 51 9 928 4 101 316 46 N/A 51 15 216 19.2 1.6 Invention steel
52 52 10 939 4 106 338 56 N/A 60 16 197 21.5 1.6 Invention steel
53 53 5 936 4 144 276 57 N/A 49 17 239 19.9 1.9 Invention steel
54 54 10 876 1 104 315 51 N/A 40 18 211 18.3 1.4 Invention steel
55 55 9 944 2 108 338 40 N/A 54 16 209 21.6 1.7 Invention steel
56 56 9 883 3 138 344 50 N/A 44 15 181 22.6 1.7 Invention steel
57 57 9 916 4 127 263 47 N/A 46 16 166 18.9 1.5 Invention steel
7 58 7 887 7 137 255 40 N/A 54 25 21 8.9 1.9 Comparative steel
7 59 10 890 4 72 260 47 N/A 54 25 34 3.9 1.3 Comparative steel
7 60 9 900 2 88 379 54 N/A 54 25 213 19.7 1.8 Invention steel
39

7 61 6 946 2 176 325 47 N/A 54 25 216 21.3 1.4 Invention steel
7 62 8 963 2 113 536 56 N/A 54 25 28 1.8 1.8 Comparative steel
7 63 9 905 3 134 308 51 N/A 54 25 238 25.1 1.3 Invention steel
7 64 6 911 3 118 220 59 N/A 54 25 174 28.6 1.9 Invention steel
7 65 5 908 3 139 94 45 N/A 54 25 204 39.4 1.4 Invention steel
7 66 8 881 4 137 42 56 N/A 54 25 206 46.8 1.6 Invention steel
7 67 10 874 2 108 365 43 320 54 25 94 15.3 1.5 Invention steel
7 68 6 898 2 119 386 0 N/A 54 25 203 21.5 2.8 Invention steel
7 69 10 901 1 123 330 44 N/A 54 8 187 21.9 1.5 Comparative steel
7 70 10 901 1 123 330 44 N/A 54 11 187 21.9 1.5 Invention steel
2 71 40 901 5 82 418 51 N/A 47 15 2 3.1 1.4 Comparative steel
9 72 9 932 2 58 403 53 N/A 41 16 721 12.6 1.4 Comparative steel
58 73 8 946 3 87 486 49 N/A 55 14 29 44.4 1.6 Comparative steel
59 74 9 957 3 102 283 50 N/A 45 17 71 19.7 1.6 Invention steel
[0088]
[Table 5]
Heat treatment process during hot stamping Surface layer region Mechanical properties

Steel No. Steel sheet No. Manufacture No. Heating
rate
(°C/s) Holding
temperature
(°C) Elapsed time from initiation of
heating to initiation of forming (s) Tempering
temperature
(°C) Partial softened region Amount of plate attached (g/m2) Ni
content in
plating
layer
(mass%) Concentration of Ni (mass%) Martensite (area%) Residual
γ (area%) Tensile strength (MPa) Bending angle (°) Note
1 1 A1 6 901 296 N/A No 39 15 3 96.7 2.1 1503 48 Comparative steel
2 2 A2 48 889 303 N/A No 55 12 1 96.4 1.1 2403 33 Comparative steel
40

3 3 A3 23 906 305 N/A No 41 12 3 93.4 2.0 1618 45 Comparative steel
4 4 A4 4 903 319 N/A No 56 15 2 87.4 2.3 1001 - Comparative steel
5 5 A5 1 877 306 N/A No 50 17 13 85.5 12.4 1555 71 Invention steel
6 6 A6 4 909 284 N/A No 41 17 13 82.9 12.8 1867 68 Invention steel
7 7 A7 2 873 287 N/A No 54 25 18 86.5 13.2 2025 59 Invention steel
8 8 A8 13 867 297 N/A No 57 16 10 89.9 9.9 2520 51 Invention steel
9 9 A9 8 896 295 247 No 40 17 10 89.4 10.1 1716 65 Invention steel
10 10 A10 2 935 302 N/A No 53 18 11 85.3 10.8 1298 - Comparative steel
11 11 A11 15 894 318 N/A No 48 18 14 86.5 8.3 2208 41 Comparative steel
12 12 A12 10 946 292 N/A No 58 15 11 90.1 8.9 2022 52 Invention steel
13 13 A13 2 886 284 N/A No 48 15 11 84.9 10.3 1936 61 Invention steel
14 14 A14 12 904 313 N/A No 46 15 11 86.8 10.9 2134 66 Invention steel
15 15 A15 53 862 301 N/A No 58 18 3 60.9 4.5 1361 - Comparative steel
16 16 A16 68 902 306 N/A No 51 17 10 87.7 9.9 2544 50 Invention steel
17 17 A17 19 949 306 N/A No 43 18 8 87.5 8.6 2008 63 Invention steel
18 18 A18 9 881 307 N/A No 52 17 9 88.3 8.6 2163 57 Invention steel
19 19 A19 74 939 315 N/A No 50 17 14 82.9 13.0 2018 52 Invention steel
20 20 A20 23 911 316 N/A No 45 17 9 90.3 8.9 2101 51 Invention steel
21 21 A21 37 911 306 N/A No 45 17 15 81.7 14.9 2208 46 Comparative steel
22 22 A22 51 917 313 N/A No 60 17 15 81.5 15.3 1935 65 Invention steel
23 23 A23 33 898 285 N/A No 47 15 13 84.7 13.3 2111 61 Invention steel
24 24 A24 39 888 292 N/A No 60 15 12 85.4 11.6 1967 55 Invention steel
41

25
25 A25 34 870 305 N/A No 58 15 9 90.6 9.1 2043 42
26 26 A26 31 932 310 N/A No 60 16 13 84.3 13.3 2204 64
27 27 A27 72 918 286 N/A No 52 17 14 85.8 13.1 2062 65
28 28 A28 19 940 296 N/A No 50 18 10 87.3 10.6 2069 64
29 29 A29 15 864 284 N/A No 53 17 15 80.6 15.3 2068 58
30 30 A30 30 942 312 N/A No 51 16 16 82.2 15.1 2083 48
31 31 A31 33 941 302 N/A No 46 16 9 86.6 9.1 2170 38
32 32 A32 42 893 314 N/A No 40 15 13. 84.4 13.7 1981 57
33 33 A33 27 915 288 N/A No 43 18 14 84.0 14.3 2053 60
34 34 A34 17 889 287 N/A No 46 15 14 81.8 13.4 2040 62
35 35 A35 49 881 304 N/A No 51 15 14 83.3 13.6 1985 56
36 36 A36 23 888 282 N/A No 47 15 16 81.9 16.4 2045 46
37 37 A37 28 946 305 N/A No 52 16 9 86.6 9.2 2027 61
38 38 A38 13 921 295 N/A No 46 15 14 82.8 13.2 2096 55
39 39 A39 60 915 302 N/A No 60 16 12 83.7 11.9 2007 51
40 40 A40 65 925 305 N/A No 60 16 13 85.0 12.7 1988 45
[0089]

Comparative
steel Invention
steel Invention
steel Invention
steel Invention
steel Comparative
steel Comparative
steel Invention
steel Invention
steel Invention
steel Invention
steel Comparative
steel Invention
steel Invention
steel Invention
steel Comparative
steel

[Table 6]

Tempering
temperature
(°C)
Bending angle (°)
N/A

Steel No. Steel sheet No.
41 41

Manufacture No.
A41

Heating
rate
(°C/s)
40

Heat treatment process during hot stamping
Holding
temperature
(°C)
Elapsed time from initiation of heating to initiation of forming (s)
912
319

Partial softened region
No

Amount Ni content
of plate in plating
attached layer
(g/m2) (mass%)
45 16

Surface layer region
Martensite (area%)
Concentration
of Ni
(mass%)
84.3
13

Residual γ (area%)
12.8

Mechanical properties
Tensile strength (MPa)
65
2207

Note
Invention

42

steel
42 42 A42 65 877 299 N/A No 58 15 10 86.9 10.7 2171 65 Invention steel
43 43 A43 70 984 302 N/A No 59 15 10 86.8 10.1 2124 63 Invention steel
44 44 A44 76 898 289 N/A No 45 16 9 89.0 8.6 2250 58 Invention steel
45 45 A45 55 944 319 N/A No 42 18 13 87.3 12.4 2044 62 Invention steel
46 46 A46 39 918 307 N/A No 58 17 15 81.6 16.0 2272 61 Invention steel
47 47 A47 57 885 320 N/A No 42 17 9 91.2 8.8 2217 61 Invention steel
48 48 A48 33 867 307 N/A No 48 17 9 90.5 8.8 2225 58 Invention steel
49 49 A49 49 1005 302 247 No 58 17 13 85.7 12.7 2265 61 Invention steel
50 50 A50 52 879 285 N/A No 42 17 13 82.2 13.1 2143 64 Invention steel
51 51 A51 47 871 305 N/A No 51 15 16 81.6 15.0 2247 64 Invention steel
52 52 A52 70 903 311 N/A No 60 16 12 84.1 11.5 2088 61 Invention steel
53 53 A53 69 925 299 N/A No 49 17 9 88.8 9.4 2109 60 Invention steel
54 54 A54 59 923 305 N/A No 40 18 14 83.6 13.7 1999 61 Invention steel
55 55 A55 63 898 304 N/A No 54 16 16 83.4 14.7 2045 63 Invention steel
56 56 A56 57 953 307 N/A No 44 15 9 90.4 8.5 2029 64 Invention steel
57 57 A57 61 939 294 N/A No 46 16 10 88.3 10.3 2102 60 Invention steel
7 58 A58 52 933 307 N/A No 54 25 4 84.3 2.9 2132 41 Comparative steel
7 59 A59 6 878 302 N/A No 54 25 5 85.5 4.1 2112 43 Comparative steel
7 60 A60 67 890 280 N/A No 54 25 8 86.4 8.9 1989 51 Invention steel
7 61 A61 44 942 320 N/A No 54 25 18 88.0 10.1 2132 71 Invention steel
7 62 A62 75 878 301 N/A No 54 25 2 84.5 3.8 2112 47 Comparative steel
7 63 A63 7 865 318 N/A No 54 25 18 84.8 15.1 1968 58 Invention
43

steel
7 64 A64 38 887 309 N/A No 54 25 20 82.1 15.8 1989 61 Invention steel
7 65 A65 31 882 299 N/A No 54 25 22 82.9 16.1 2009 69 Invention steel
7 66 A66 5 909 308 N/A No 54 25 23 84.7 15.1 2030 72 Invention steel
7 67 A67 21 917 284 N/A No 54 25 8 90.3 8.1 2132 56 Invention steel
7 68 A68 42 950 290 N/A No 54 25 13 86.7 12.1 2009 58 Invention steel
7 69 A69 75 914 319 N/A No 54 8 7 90.0 7.5 1948 46 Comparative steel
7 70 A70 70 943 313 N/A No 54 11 8 88.1 8.2 2037 52 Invention steel
7 7 A71 92 937 294 N/A No 54 25 12 89.3 10.1 2018 53 Invention steel
7 7 A72 105 935 306 N/A No 54 25 4 94.7 2.8 2079 48 Comparative steel
7 7 A73 30 779 314 N/A No 54 25 5 76.4 0.8 1323 - Comparative steel
7 7 A74 40 1040 303 N/A No 54 25 14 82.9 14.1 2110 34 Comparative steel
7 7 A75 87 891 227 N/A No 54 25 6 90.3 6.2 2171 37 Comparative steel
7 7 A76 26 947 523 N/A No 54 25 14 66.6 1.1 1599 38 Comparative steel
7 7 A77 10 891 304 N/A Yes 54 25 13 83.8 13.1 2129 61 Invention steel
2 71 A78 16 902 300 N/A No 47 15 1 71.1 3.3 2289 48 Comparative steel
9 72 A79 77 907 289 N/A No 41 16 6 94.1 3.8 2601 29 Comparative steel
58 73 A80 6 918 280 N/A No 55 14 8 91.7 8.1 1458 - Comparative steel
59 74 A81 3 922 291 N/A No 45 17 9 88.2 9.9 1521 69 Invention steel
44

[0090]
The metallographic structures, the average dislocation densities, and the
concentrations (amounts) of Ni of the steel sheets for hot stamping and the hot-stamped
articles were measured by the above-described measurement methods. In addition, the
5 mechanical properties of the hot-stamped articles were evaluated by the following
methods. [0091]
“Tensile strength”
Regarding the tensile strength of the hot-stamped article, a No. 5 test piece
10 described in JIS Z 2201: 2011 was produced from an arbitrary position in the hot-
stamped article, and the tensile strength was obtained according to the testing method
described in JIS Z 2241: 2011. In a case where the tensile strength was lower than 1500
MPa, the tensile strength was evaluated as failure, and a test described below was not
carried out.
15 [0092]
“Bendability”
The bendability of the hot-stamped article was evaluated by the following
method based on the VDA standard (VDA238-100) specified by Verband der
Automobilindustrie. In the present examples, displacement under the maximum load
20 that was obtained in a bending test was converted to an angle based on VDA, thereby
obtaining the maximum bending angle (°).
Test piece dimensions: 60 mm (rolling direction) × 60 mm (direction parallel to
sheet width direction) or 30 mm (rolling direction) × 60 mm (direction parallel to sheet
width direction)
25 Test piece sheet thickness: 1.0 mm (the front and rear surfaces were polished the
45

same amount, respectively)
Bending ridge: Direction parallel to sheet width direction
Testing method: Supported by rolls and pressed by a punch
Roll diameter: ϕ30 mm
5 Punch shape: Tip R = 0.4 mm
Distance between rolls: 2.0 × sheet thickness (mm) + 0.5 mm Pressing rate: 20 mm/min
Tester: SHIMADZU AUTOGRAPH 20 kN
[0093]
10 In a case where the maximum bending angle obtained by the above-described
method was 50° or more, the bendability was considered to be excellent and determined
to be a pass. However, in a case where the maximum bending angle was less than 50°,
the bendability was determined to be a failure.
[0094]
15 In Tables 5 and 6, in cases where the tensile strength was 1500 MPa or higher
and the bendability was pass (50° or more), the strength and the bendability were
considered to be excellent, and the steels were determined to be invention steel. In
cases where any one of the two performances described above was not satisfied, the
steels were determined to be a comparative steel.
20 [0095]
From Tables 5 and 6, it is found that hot-stamped articles having a chemical composition, a plate composition, and a metallographic structure within the scope of the present invention have excellent strength and excellent bendability.
On the other hand, it is found that hot-stamped articles having any one or more
25 of a chemical composition and a metallographic structure outside the scope of the present
46

invention are poor in terms of one or more of strength and bendability.
[Industrial Applicability]
[0096]
According to the present invention, it is possible to provide a hot-stamped article
5 having excellent strength and excellent bendability.

WE CLAIMS

A hot-stamped article comprising:
a base steel sheet containing, as chemical components, by mass%,
5 C: 0.15% or more and less than 0.70%,
Si: 0.005% or more and 0.250% or less,
Mn: 0.30% or more and 3.00% or less,
sol. Al: 0.0002% or more and 0.500% or less,
P: 0.100% or less,
10 S: 0.1000% or less,
N: 0.0100% or less,
Nb: 0% or more and 0.150% or less,
Ti: 0% or more and 0.150% or less,
Mo: 0% or more and 1.000% or less,
15 Cr: 0% or more and 1.000% or less,
B: 0% or more and 0.0100% or less, Ca: 0% or more and 0.0100% or less, and REM: 0% or more and 0.30% or less
with a remainder including Fe and impurities; and
20 a plating layer on a surface of the base steel sheet, the plating layer being
attached to a single surface in an amount of 10 g/m2 or more and 90 g/m2 or less and having a Ni content of 10 mass% or more and 25 mass% or less with a remainder including Zn and impurities,
wherein a metallographic structure of a surface layer region that is a region from
25 the surface of the base steel sheet to a depth of 50 μm includes 80.0% or more of
48

martensite and 8.0% or more of residual austenite in terms of area percentage, and a concentration of Ni in the surface layer region is 8 mass% or more.
2. The hot-stamped article according to Claim 1,
5 wherein the base steel sheet contains, as chemical components, by mass%, one
or more selected from the group consisting of
Nb: 0.010% or more and 0.150% or less,
Ti: 0.010% or more and 0.150% or less,
Mo: 0.005% or more and 1.000% or less,
10 Cr: 0.005% or more and 1.000% or less,
B: 0.0005% or more and 0.0100% or less,
Ca: 0.0005% or more and 0.0100% or less, and
REM: 0.0005% or more and 0.30% or less.