IMPROVED PHASE CHANGE COMPOSITIONS
Field of the Invention
The present invention relates to phase change materials containing sodium acetate
trihydrate having improved homogeneity, a process for the preparation of said materials, and
their utility in phase change systems. More particularly, the present invention relates to the
use of phase change compositions comprising sodium acetate trihydrate, at least one alkali
soluble polymer for inhibition of sodium acetate anhydrous crystal formation in sodium
acetate trihydrate containing phase change materials, and at least one sodium acetate
trihydrate nucleation promoter.
Background of the Invention
There are many heating and cooling systems on the market and many of these are
reliant on fossil fuels. With the ever increasing demand for more environmentally friendly
systems various alternative systems based on sunlight or water have been proposed such
as for example photovoltaics, solar thermal electricity generators, hydroelectricity, wave
power and bio-fuels.
An issue common to all solar-driven renewable energy conversion devices, some
hydro-driven devices, and wind turbines is that they cannot operate "on demand", as the sun
does not always shine, the seas are not always high and the wind does not always blow.
This means that at some times these so-called intermittent renewable sources will generate
electricity which cannot be easily integrated into their corresponding local electricity grids,
and as such there have been a number of storage solutions proposed.
The thermal energy storage system, proposed in WO 2009/138771 converts surplus
electrical energy from intermittent renewable sources into heat or cool when available, store
the so-converted heat or cool in a thermal store, and then make it available as useful heat or
cool on demand using phase change materials (PCMs) to effect the energy conversion via
their inherent solid-liquid phase changing properties.
For practical application in domestic situations phase change materials capable of
supplying warm, or even hot, water that is just above the comfort level temperature of the
individual requiring the heated water are needed. In addition, phase change materials
suitable for such practical utility should achieve rates of heat transfer into and out of, their
phase changes, which are commensurate with domestic use, as well as deliver acceptable
levels of thermodynamic stability (efficiency).
l
Sodium acetate trihydrate, (SAT), has a solid-liquid phase change within the desired
temperature range for domestic utility. However, the practical applications of SAT as a
phase change material (PCM) are limited by the unique and incongruous manner in which it
melts, going from solid SAT, to a mixture of liquid SAT and a solid (sodium acetate/SA) at a
set temperature, 58°C. This inability to provide a fully liquid solution at 58°C is an issue
which is reflected in the thermodynamic stability of aqueous solutions upon initial heating,
as well as the thermodynamic stability of, re-formed, aqueous solutions provided following
re-heating after cooling in accordance with the normal heating / cooling cycles in phase
change systems.
This solid-formation on melting is a problem for use as SAT as a PCM because this
solid SA, once formed, would ordinarily be retained throughout the lifetime of the PCM in a
phase change system.
Previous attempts to overcome this issue via the utility of three dimensional crosslinked
polymers, such as cellulose based polymers and super absorbent polymers, to act as
solid supports have been unsuccessful because, independent of any apparent initial
reduction of solid formation, the underlying problem of solid sodium acetate formation is
unresolved, and over time solid sodium acetate will still precipitate out of solution, and
collect at the base of the PCM storage vessel irreversibly. For utility as a PCM, no solution
which has a finite lifetime is acceptable.
It is an object of at least one aspect of the present invention to obviate or mitigate at
least one or more of the aforementioned problems in relation to the utility of sodium acetate
trihydrate as a potential PCM for use in aqueous phase change systems.
It is an object of at least one aspect of the present invention to provide improved
phase change materials containing sodium acetate trihydrate having desirable homogeneity;
resistance to SA formation, which are suitable for use in phase change systems.
It is an object of at least one aspect of the present invention to provide improved
phase change materials containing sodium acetate trihydrate which can be heated, cooled
and re-heated in repeated cycles with retention of thermodynamic stability.
The Applicant has developed novel and inventive aqueous compositions for use as
phase change materials comprising: sodium acetate trihydrate; at least one alkali soluble
polymer for inhibition of sodium acetate anhydrous crystal formation in sodium acetate
trihydrate containing phase change materials; and at least one sodium acetate trihydrate
nucleation promoter. The Applicant has also developed a process for the preparation of said
improved phase change materials.
Summary of the Invention
The Applicant has developed novel and inventive phase change compositions
containing sodium acetate trihydrate as a phase change material.
Accordingly the present invention provides compositions containing sodium acetate
trihydrate as a phase change material comprising:
(a) sodium acetate trihydrate or sodium acetate anhydrous;
(b) at least one suitable alkali soluble polymer;
(c) at least one suitable nucleation promoter; and
(d) water.
As demonstrated in the Examples hereinafter the Applicant has surprisingly found
that the compositions of the present invention which contain sodium acetate trihydrate as a
phase change material display unprecedented improvements in homogeneity and
thermodynamic stability properties than previously achievable using sodium acetate
trihydrate as a PCM. In particular the Applicant has found that the compositions of the
present invention which contain sodium acetate trihydrate as a phase change material are
resistant to the nucleation of crystalline sodium acetate on heating and cooling.
According to a further aspect the present invention provides for the use of the
compositions according to the invention as phase change materials suitable for use in phase
change systems.
The Applicant has also developed a novel process for the preparation of the
compositions according to the invention. According to a further aspect the present invention
provides a process for the preparation of compositions containing sodium acetate trihydrate
as a phase change material which comprises:
(a) mixing an aqueous solution comprising sodium acetate anhydrous with at least
one suitable alkali soluble polymer; and at least one nucleation promoter;
(b) heating the resultant mixture to provide a 58°C phase change material containing
sodium acetate trihydrate.
When sodium acetate trihydrate is used, the following steps are followed:
(a) heating the sodium acetate trihydrate to a temperature above 58°C; and
(b) mixing the sodium acetate trihydrate with at least one suitable alkali soluble
polymer; and at least one nucleation promoter.
BRIEF DESCRIPTION OF THE DRAWINGS
Embodiments of the present invention will now be described, by way of example
only, with reference to the accompanying drawings:
Figure 1 is a phase diagram of sodium acetate and water, showing the solubility limit
of sodium acetate in water, at about 58°C, is at about 58.0%, whereas the corresponding
sodium acetate trihydrate, which melts at 58°C, is made up of 60.28 % of SA and 39.72 % of
water, a value noticeable higher than the solubility limit at 58°C, as indicated by point 2 ;
Figure 2 is a proposed mechanism where the polymer interacts with the surface of
highly metastable sub-critical clusters of sodium acetate molecules to prevent, or block, their
further growth into crystallites, and hence precipitated material in due course, via a blocking
mechanism; and
Figure 3 is a representation of crystallisation temperatures obtained by aiding varying
levels of acetamide.
Detailed Description
The novel compositions according to the present invention are aqueous compositions
containing sodium acetate trihydrate, NaOAc-3H20 , also known as SAT, as a phase change
material. Any form of sodium acetate anhydrous, also known as SA, may be used in the
preparation the novel compositions containing SAT as a PCM in accordance with the
invention. For the avoidance of doubt this means that as all solid forms of NaOAc are
crystalline, and therefore any crystalline form may be used.
The level of sodium acetate anhydrous used in the preparation of the aqueous
compositions according to the invention is between about 40% to about 60% by weight of
the total composition. This corresponds to a relative amount of from about 66% to about
100% of sodium acetate trihydrate in the aqueous compositions of the invention. For the
avoidance of doubt the compositions according to the present invention are substantially
free-from, and are more preferably free-from solid anhydrous sodium acetate.
For the avoidance of doubt, where the actual or relative amounts of water in any
particular composition according to the invention described herein are not specified it should
be understood that the actual or relative amount of water required will be that sufficient to
reach either 100% of composition, either by weight or relative volume. Water may be used
either in purified, or distilled form, or from regular supply.
As indicated hereinbefore, despite having a phase change within the desired
temperature range for domestic heating purposes, the utility of sodium acetate trihydrate as
a potential PCM to-date has been hampered due to inherent melting incongruences. During
the melting process sodium acetate trihydrate changes from solid SAT, to a mixture of liquid
SAT and solid at a set temperature, 58°C. This is due to the formation of sodium acetate
anhydrous, NaOAc, or SA. For the avoidance of doubt, where the term sodium acetate, or
SA, is utilised herein it means sodium acetate anhydrous, as opposed to any hydrated form,
or the trihydrate, SAT in particular. As indicated by point 1, in Figure 1, a phase diagram of
sodium acetate and water, the solubility limit of sodium acetate in water, at about 58°C, is at
about 58.0%, whereas the corresponding sodium acetate trihydrate, which melts at 58°C, is
made up of 60.28 % of SA and 39.72 % of water, a value noticeable higher than the
solubility limit at 58°C, as indicated by point 2 , in Figure 1. When SA is formed during the
melting of aqueous SAT, a fully liquid state may be re-instated via the addition of more
water, to alter the composition to the composition of 58% SA, and solubilise SA anhydrous,
thereby providing a fully liquid material at 58°C. The so-produced solution is
thermodynamically stable, i.e. it is neither in the metastable zone, nor in the supersaturated
zone, thus no further solid material (SA) should crystallise out.
As explained hereinbefore, such a re-instated liquid solution comprising water and
sodium acetate trihydrate is not suitable for use as a phase change agent because, it is not
capable of being cooled and reheated to provide a thermodynamically stable homogeneous
liquid. As demonstrated in the Examples hereinafter, the Applicant has found when such a
solution is cooled down and seeded with some sodium acetate trihydrate, a solid sample of
sodium acetate trihydrate is formed. Applicant has also found that when such a cooled
solution is heated up to 58°C again, a solution with some solid sodium acetate anhydrous,
SA, is formed i.e. the solution is not in fact in thermodynamic equilibrium.
Mixing and/or agitation would return the composition to its thermodynamic
equilibrium, a homogenous solution; however without such mechanism, as in this invention,
a homogenous solution does not prevail.
As illustrated in Figure 1, crystalline sodium acetate trihydrate melts to form sodium
acetate anhydrous and a concentrated solution of aqueous sodium acetate. In simple terms,
and in accordance with general chemical practise, the addition of more water added would
be expected to dissolve this additional sodium acetate (the anhydrous solid). More
accurately, this extra water would be expected to dilute the concentrated solution comprising
sodium acetate anhydrous and water, which in turn would enable the solid sodium acetate
anhydrous to dissolve into it. Most surprisingly, the Applicant has demonstrated that this
does not occur in practise, and further that the resistance to dissolution of the anhydrous
solid is in fact unaltered due to the additional water level.
Without wishing to be bound to any particular theory it is postulated herein that,
during the melting process, molecules of sodium acetate trihydrate dissociate incongruently,
and also that there is rapid exchange between the sodium acetate in the liquid phase and
the sodium acetate in the solid phase. The solid sodium acetate anhydrous molecules are
thought to initially be present in small clusters. Such small clusters are thought to possibly
contain hundreds of molecules of SA, and are not considered to be crystalline. It is further
proposed herein that as any one of these clusters increases in size it can eventually attain
the critical cluster size, or threshold size, required to become a crystallite. It is further
proposed herein that such crystallites, grouping together, form the dense crystals of sodium
acetate that are observed as the unwanted solid precipitated material in the aforementioned
Example. The Applicant has observed that the formation of solid precipitate, during the
melting process, occurs too quickly for the dissolution of additional water to have any
significant impact.
The Applicant has resolved this issue of non-homogeneous liquid formation in
aqueous phase change materials containing sodium acetate trihydrate via the provision of
PCMs containing NaOAc- 3H20 which are resistant to the formation of NaOAc crystallites via
the utility of one or more particular alkali soluble polymers.
Without being bound to any particular theory it is thought that the particular polymers
utilised in the PCMs containing sodium acetate trihydrate according to the present invention
composition provide resistance to the formation of precipitated NaOAc in aqueous
NaOAc- 3H20 solutions via a combination of effects including: viscosity effects; crystal habit
modifying behaviour; 3D-lattice effects. As such, the one or more alkali soluble polymers
suitable for use herein may also be referred to as SA crystal inhibitors, or inhibitors of the
formation of crystalline SA from aqueous solutions.
At one level by harnessing the ability of these particular polymers to increase the
viscosity of solutions it is believed that at least some of the sodium acetate anhydrous
formed during the melting process may remain suspended long enough to dissolve and
thereby reduce the potential for SA precipitation from solution, and subsequent collection
within the phase change system equipment during use. It is also proposed herein that use
of these particular polymers would provide solid sodium acetate having a significantly
increased effective surface area in solution, versus that previously possible (for SA only
aqueous systems) when the solid is amassed at the base and only the top of this solid layer
is in contact with the solution. It is further proposed herein that even dispersal of the solid
sodium acetate in this more viscous solution for an extended period of time, may increase
the dissolution rate and thereby reduce the rate at which the anhydrous form of sodium
acetate could form, and potentially may prevent formation altogether.
Polymers suitable for use in the novel compositions herein containing SAT as PCMs
in accordance with the first or further aspects of the invention as detailed herein are soluble
in aqueous alkaline solution. As defined herein polymers suitable for use herein are soluble
in aqueous alkaline solutions having a pH in excess of about pH 8 . More particularly
polymers suitable for use herein are soluble in highly alkaline aqueous solution having a pH
of about pH 9 , such as aqueous sodium acetate solution. The compositions herein include
one or more polymers, as defined herein, wherein each polymer may be independently
present at levels of from about 0.1% to about 10%, from about 0.2% to about 4%, from about
0.5% to about 2% are utilised in the aqueous compositions according to the present
invention.
In addition, polymers suitable for use herein have one or more carboxylic acid groups
and may be utilised as acids, or as acid salts. For the avoidance of doubt the term polymer
as used herein includes both polymers of repeated singular monomeric units, and co
polymers comprised of mixed monomeric units having varying repeating patterns.
A group of preferred polymers for use herein are polymers having repeating units of
general formula I :
and salts thereof
wherein z is 10 to 1,000;
n = 1 to 10 to 1,000; and wherein m = 0 to 1,000
wherein the ratio of n : m is in the range of from about X: Y and wherein the
molecular weight of the polymer is in the range of from about P to about Q,
X is independently selected from groups based on the following monomers: ethylene,
acrylic acid, methyl methacrylate, acrylamide, ethyl methacrylate, ethacrylic acid, ethyl oxide,
diallyldimethylammonium chloride, vinylpyrrolidone, N-isopropylacrylamide, styrene, maleic
acid and mixtures thereof,
Y is independently selected from groups based on the following monomers: ethylene,
acrylic acid, methyl methacrylate, acrylamide, ethyl methacrylate, ethacrylic acid, ethyl oxide,
diallyldimethylammonium chloride, vinylpyrrolidone, N-isopropylacrylamide, styrene, maleic
acid and mixtures thereof,
A group of preferred polymers according to general formula I for use herein have
monomeric repeating units of general formula II.
I I
and salts thereof wherein n , m and z are as defined hereinbefore
wherein the ratio of n : m is about 1 : 2 and wherein the molecular weight is in the
range of from about 1,000 to 1,000,000.
Preferred polymers of general formula I I for use herein are either acids or acid salts,
more particularly either acids or metal acid salts, and especially acids or sodium, potassium
or zinc acid salts. The copolymer of methacrylic acid and methyl methacrylate,
poly(methacrylic acid co-methyl methacrylate) having a molecular weight of from about
500,000 to about 1,000,000, and the sodium, potassium or zinc salts thereof are polymers
within general formulae I , I I and III, and are particularly suited for use herein.
Another group of preferred polymers for use herein according to general formula I for
use herein have repeating units of general formula III:
and metal salts thereof selected from sodium or potassium, and
wherein z and n are as defined herein before.
A preferred polymer of formula III for use herein is poly(methacrylic acid), particularly
the sodium salt, preferably in 30 or 40% aqueous solution wherein the polymer has an
average molecular weight of about 10,000 or 4-6,000
Thus, the present invention provides compositions as defined hereinbefore wherein
the one or more alkaline soluble polymers are selected from general formulae I I or III and
mixtures thereof each independently present at a level of from about at levels of from about
0.1% to about 10%, from about 0.2% to about 4%, from about 0.5% to about 2%. In
addition, there are provided compositions as defined hereinbefore wherein the polymer is:
the copolymer of methacrylic acid and methyl methacrylate, poly(methacrylic acid co-methyl
methacrylate) having a molecular weight of from about 500,000 to about 1,000,000, or a
sodium, potassium or zinc salts thereof; the poly(methacrylic acid), or the sodium salt having
an average molecular weight of about 10,000, and wherein either polymer may be
independently present at a level of from about at levels of from about 0.1% to about 10%,
from about 0.2% to about 4%, from about 0.5% to about 2%. According to a further aspect
the present invention provides a composition having either one or the above two polymers at
the levels defined above.
The improved PCM compositions according to the present invention containing SAT
as a PCM have been demonstrated to form homogeneous liquids without the need to add
excessive additional water, which is in stark contrast to the precipitated systems observed
without polymers. However it is the demonstrated improvements in both homogeneity and
thermodynamic stability following cooling and re-heating, between the SAT containing PCM
systems of the invention with polymers, when compared to the behaviour displayed by
sodium acetate trihydrate without polymers which are truly revolutionary.
Without being bound to any particular theory it is proposed herein that phenomenal
abilities observed for the various different SAT / polymer systems tested for the delivery
unprecedented inhibition of nucleation in aqueous sodium acetate trihydrate systems is due
to a consistent, underlying technical effect common to them all. Whilst the precise
mechanism of crystal nucleation inhibition in these systems is unknown, it is proposed herein
that the polymer interacts with the surface of highly metastable sub-critical clusters of
sodium acetate molecules to prevent, or block, their further growth into crystallites, and
hence precipitated material in due course, via a blocking mechanism. Figure 2 provides a
proposed illustration of this mechanism.
The Applicant has found that even when the polymeric systems herein are seeded
with SA, to in effect force the formation of solid material, the so-formed solid material is very
different in both appearance and behaviour to that observed in the corresponding solid
material formed in non-polymeric systems. It is in this impact upon the behaviour of the
resultant solid, which suggests that the solid may exist in a different structural habit, and that
the polymers act as crystal habit modifiers.
Whilst these modified polymer containing aqueous solutions of sodium acetate are
indeed most surprisingly and desirably resistant to SA formation, they are not suitable for
utility as PCMs because, as has been most clearly demonstrated both by the experiments
and results discussed herein and as the SA phase diagram of Figure 1, sodium acetate
trihydrate does not readily nucleate, even in supersaturated solutions. This means that a
nucleating agent is required to promote the nucleation of the sodium acetate trihydrate from
the aqueous solution.
Nucleating agents, as defined herein are also known as nucleators, or nucleation
promoters. In some cases, the effective pairing of a particular material with a particular
nucleating agent can be the result of iso-structural similarities between the nucleator and the
salt hydrate in their crystalline forms, and indeed this is the case with many known-pairs.
For example strontium chloride hexahydrate acts as a nucleator for calcium chloride
hexahydrate, and sodium tetraborate decahydrate acts as a nucleator for sodium sulfate
decahydrate and in each pairing they have very similar molecular packing in their respective
crystalline forms.
For sodium acetate trihydrate identification of a suitable nucleator is a more
challenging matter. Whilst disodium hydrogen phosphate (DSP) and tetrasodium
pyrophosphate (TSPP) have been identified as potential nucleators for SAT their mechanism
of action remains unknown. (T Wada and R Yamamoto "Studies on salt hydrates for latent
heat storage. 1. Crystal nucleation of sodium acetate trihydrate catalyzed by tetrasodium
pyrophosphate decahydrate, Bulletin of the Chemical Society of Japan. Volume 55, page
3603, 1982; T Wada, R Yamamoto and Y Matsuo "Heat storage capacity
of sodium acetate trihydrate during thermal cycling", Solar Energy. Volume 33, pages 373 to
375, 1984; and H Kimura, "Nucleating agents for sodium acetate trihydrate", Journal of the
Japanese Association of Crystal Growth. Volume 9 , issue 3 , page 73, 1982.)
Furthermore there is an acknowledged so-called deactivation of these nucleators at
high temperatures which undermines their potential for consideration as potential pairs for
SAT PCMs for use in phase change systems because by their nature PCMs are intended for
long-term use, and require on-demand, reliable activation throughout the anticipated
heating/cooling/re-heating cycles therefor.
Surprisingly the Applicant has identified a particular hydrate of disodium hydrogen
phosphate, the dihydrate, to be the active nucleating species for SAT, and has also
demonstrated that utility of this hydrate in aqueous polymeric solutions containing SAT as
detailed hereinbefore provides compositions highly suited for use as PCMs in phase change
systems. The compositions according to the present invention typically contain one or more
nucleation promoters each independently present at a level of from about 0.1% to about 5%,
from about 0.2% to about 3%, from about 0.5% to about 2%.
Thus the present invention additionally provides compositions containing sodium
acetate trihydrate as a phase change material comprising:
(a) from about 48 to about 60% of sodium acetate anhydrous;
(b) from about 0.1% to about 10% of at least one suitable alkali soluble polymer;
(c) from about 0.1% to about 5% of at least one suitable nucleation promoter; and
(d) water to balance.
Alternatively, when sodium acetate trihydrate is used, the composition above
changes to:
(a) from about 80% to about 100% of sodium acetate trihydrate;
(b) from about 0.1% to about 10% of at least one suitable alkali soluble polymer;
(c) from about 0.1% to about 5% of at least one suitable nucleation promoter; and
(d) water to balance.
Whilst any material capable of nucleating SAT is suitable for use herein, preferred
materials which both nucleate SAT and retain their effectiveness at high temperatures are
particularly suited for use in the compositions for use as PCMs according to the present
invention. Such materials include: disodium hydrogen phosphate (DSP); tetrasodium
pyrophosphate (TSPP); and hydrated forms thereof. Particular materials suitable for use
herein are disodium hydrogen phosphate dihydrate, and tetrasodium pyrophosphate
decahydrate. Thus, the present invention provides compositions as defined hereinbefore
wherein the nucleation promoters are disodium hydrogen phosphate (DSP); tetrasodium
pyrophosphate (TSPP); and hydrated forms thereof each independently present at a level of
from about 0.1% to about 5%, from about 0.2% to about 3%, from about 0.5% to about 2%.
In addition, there are provided compositions as defined hereinbefore wherein the nucleation
promoters are disodium hydrogen phosphate dihydrate and tetrasodium pyrophosphate
decahydrate and wherein the total level of these promoters is from about 0.5% to about 5%,
from about 0.2% to about 2.5%, from about 0.5% to about 2%.
In addition to the polymer and the nucleation promoter the compositions according to
the invention may additionally comprise a further agent to modify the melting point of SAT
when in use as a PCM. Any suitable agent capable of providing a desirable melting point
modification can be used, for the avoidance of doubt melting point modification, means a
lowering of the melting and crystallisation point. Such modifying agents may be utilised at a
relative concentration level of from about 1% to about 25%, 5% to about 25%, from about
10% to about 20%, from about 2% to about 10% of the total mass. Example agents for
lowering the melting point of SAT in the compositions herein include: metal salts such as
ithium acetate dihydrate; and organic compounds such as acetamide and trimethylolethane
which could also include non-metal salts, e.g. ammonium acetate.
Thus the present invention additionally provides compositions containing sodium
acetate trihydrate as a phase change material comprising:
(a) from about 35% to about 60% of sodium acetate anhydrous;
(b) from about 0.1% to about 10% of at least one suitable alkali soluble polymer;
(c) from about 0.1% to about 5% of at least one suitable nucleation promoter;
(d) from about 1% to about 95% of an optional melting point depressing agent; and
(e) water to balance.
Preferred herein are compositions wherein the lithium acetate dihydrate is utilised as
a melting point depressing agent at levels of from about 1% to about 25%, from about 5% to
about 25%, from about 10% to about 20%.
Lithium acetate dihydrate is 64.67% LiOAc and 35.33% water, values below copied
from above but x by 64,67.
Preferred herein are compositions wherein the lithium acetate anhydrous is utilised
as a melting point depressing agent at levels of from about 0.65% to about 16.17%, from
about 3.23% to about 16.17%, from about 6.47% to about 12.93%.
The melting point may also be depressed by addition of acetamide and
trimethylolethane.
The compositions of the invention containing SAT as a PCM can be made according
to a process comprising:
(a) mixing an aqueous solution comprising sodium acetate anhydrous with at least
one suitable alkali soluble polymer; at least one nucleation promoter, and at least
one melting point depressing agent;
(b) heating the resultant mixture to provide a 58°C phase change material containing
sodium acetate trihydrate.
According to a preferred process herein the from 35% to about 60% of sodium
acetate anhydrous, from about 0.1% to about 10% in total of suitable alkali soluble
polymer(s), from about 0.1% to about 5% in total of one or more nucleation promoter are
utilised and optionally from about 1% to about 25% of melting point depressing agent may
be included in the mixing stage. An example of this process is found in Example 3
hereinafter.
According to a preferred process herein the from 35% to about 60% of sodium
acetate anhydrous, from about 0.1% to about 10% in total of suitable alkali soluble
polymer(s), from about 0.1% to about 5% in total of one or more nucleation promoter are
utilised and optionally from about 1% to about 95% of melting point depressing agent may
be included in the mixing stage.
Alternatively the polymer may be formed in situ in the molten (heated) aqueous SAT
mixture, in which instance the relevant monomers would be added into the aqueous solution
and polymerisation would be initiated. Therefore, the PCM can be made in either the heat
battery enclosure before including the heat exchanger and sealing it or the PCM can be
made in an external vessel and then poured into the enclosure containing heat exchanger.
The following non-limiting examples provided in the Experimental results hereinafter
are representative of the PCM compositions according to the invention, as are the processes
for their preparation.
Experimental Results
Example 1: Addition of polymer 1 to aqueous sodium acetate to prevent precipitation
1% (2g) of a poly(methacrylic acid co-methyl methacrylate) 2:1 copolymer having a
molecular weight of 500,000- 1,000,000 (available from Fluka, as Polyacrylic acid, cas
25086-15-1 (labelled medium viscosity, mr -500,000-1,000,000, copolymer of methacrylic
acid and methyl methacralate) was added with stirring to a well-mixed 198g aqueous
solution of sodium acetate (available from VWR International Ltd. (UK) as sodium acetate
anhydrous 99%) at a concentration of 58.24% (17.002 mol dm 3) at from about 60 to about
70°C and then allowed to cool down to room temperature (RT).
At RT a homogenous liquid was observed which is in stark contrast to the same
solution but without any polymer where significant of precipitation of sodium acetate was
observed. Further, cycling experiments were preformed throughout a temperature range of
between about 25 to about 80°C which confirmed that the beneficial effects observed for
polymer-assisted solution were consistent across the range tested. In addition, further
experiments confirmed that sodium acetate could only be initiated to form with seeding at
RT.
Example 2 : Addition of polymer 2 to aqueous sodium acetate to prevent precipitation
(0.66% with respect to only polymer) 22.6g of a 30% aqueous solution of
poly(methacrylic acid, sodium salt) having a molecular weight of 9,500 (available from Sigma
Adrich, UK, as Poly(methacrylic acid, sodium salt) solution average M -5,400, average
Mw -9,500 by GPC, 30 wt. % in H20 , cas 54193-36-1) was added to a 59.16% (17.66 mol
dm 3) aqueous solution of sodium acetate(1,000g) in accordance with the method of
Example 1 and then allowed to cool down to room temperature (RT).
Example 3 : Qualification that polymer systems provide homogeneous liquids at 58°C
Test samples containing various levels of polymers 1 and 2 , and varying initial
aqueous concentrations of sodium acetate, were left undisturbed at RT for several weeks.
Where sodium acetate were observed, it appeared as a large white mass taking up the
whole sample container. This mass is thought to be an intricate mixture of sodium acetate
and water, and yet had the appearance of a solid. When the sample container was
squeezed the mass was observed to be very soft. On careful stirring this mass was found to
appear as fine needle-like crystals and furthermore, heating such samples to 58°C resulted
in homogenous liquids, which were in agreement with the phase diagram of Figure 1, point
2 , as discussed hereinbefore.
In addition test samples were carefully seeded with sodium acetate were also left
undisturbed, and the resulting solid sodium acetate appeared as a large white mass taking
up the whole sample container. This mass is thought to be an intricate mixture of sodium
acetate and water, and yet had the appearance of a solid. When the sample container was
squeezed the mass was observed to be very soft. On careful stirring this mass was also
found to appear as fine needle-like crystals, and furthermore, on heating to 58°C, these
samples also provided in homogenous liquids, which were in agreement with the phase
diagram of Figure 1, point 2 .
This ability to form homogeneous liquids without the need to add excessive water is
in stark contrast to the precipitated systems observed without polymers. However the
observed improvements in both homogeneity and thermodynamic stability following cooling
and re-heating, between the systems of the invention with polymers and when compared to
sodium acetate trihydrate without polymers is truly revolutionary.
Example 4 : Identification of Active Nucleator for SAT in DSP
Variable temperature powder X-ray diffraction was utilised to identify the dihydrate of
disodium hydrogen phosphate as the active nucleator. Samples of sodium acetate trihydrate
with disodium hydrogen phosphate dihydrate were cooled and crystallisation of sodium
acetate trihydrate took place. Heating the sample to 90°C resulted in the transition from the
dihydrate to anhydrous disodium hydrogen phosphate. Subsequent cooling of this sample,
now containing SAT and anhydrous DSP to 25°C, did not return the anhydrous DSP to the
DSP dihydrate, and thus no crystallisation of sodium acetate trihydrate could take place.
Additional experiments were carried out to confirm that no deactivation of this system
occurs at the temperatures required for utility in compositions for use as PCMs, via either
seeding with sodium acetate trihydrate or the active nucleators. The results of these
experiments have confirmed that upon such seeding "reactivation" of the nucleators occurs
and their effectiveness is fully restored. This is in agreement with previous observations but
the Applicant is the first to understand and characterise the hitherto unexplained
phenomena.
Example 5 : Preparation of PCM Formulations containing SAT
Formulation 1 was prepared as follows sodium acetate anhydrous (134.1 kg, 1634.77
mol), water (94.6 kg, 5251.18 mol) and a polymethacrylic acid polymer (mol wt 9,500) as a
30% aqueous solution (5.3 kg), DSP (2.3 kg, 16.20 mol) and TSPP (2.3 kg, 8.65 mol) were
mixed together and heated to about 70°C. This resultant 58°C PCM produced via this
process has no anhydrous sodium acetate formation.
Formulation 2 was prepared as for Formulation 1. The resultant 50°PCM produced
also had no anhydrous sodium acetate formation.
Thus the PCMs according to the present invention are free from SA when viewed by
the naked eye and experimental techniques such as X-ray powder diffraction.
Example 6 : Addition of acetamide to sodium acetate trihydrate to depress melting
Ratio of SAT to acetamide needed for mixes
a) Starting from the trihydrate form of sodium acetate:
95.53 wt% sodium acetate trihydrate (CAS 6131-90-4) with 2.17 wt% water with
2.30wt% of an aqueous solution of poly(methacrylic acid, sodium salt) (available from Sigma
Aldrich UK CAS 54193-36-1) was made up, and heated to 60-70 °C, whilst stirring, to create
a homogeneous mixture.
b) Starting from the anhydrous sodium acetate:
57.85 wt% sodium acetate (available from VWR International Ltd. as sodium acetate
anhydrous 99% CAS 127-09-3) with 39.84% water and 2.31 wt% aqueous solution of
poly(methacrylic acid, sodium salt) was heated to 60-70 °C whilst stirring, to create a
homogeneous mixture.
To depress the melting and freezing temperatures, this solution was added in varying
amounts with acetamide, as shown in the table above. Temperatures were recorded for the
melt and freeze (nucleated with a seed crystal) of the samples, and the range of depressions
is shown below. Crystallisation temperatures from 58°C to 28.5°C can be gained by adding
acetamide up to 70 molar %, whereupon the mix nears the eutectic point, after this point
freezing temperature increases. This is shown in Figure 3 .
Example 7 : Addition of trimethylolethane to sodium acetate tri hydrate to depress
melting point
Sodium acetate trihydrate solution was made as in the methods described in Example 1. To
make the mixture samples the SAT solution was added to TME as described in the table
below.
The mixtures can either be nucleated manually with a seed crystal, or 2wt% of a
nucleator, disodium hydrogen phosphate dihydrate. By increasing the content of
trimethyolethane from 0 to 40 molar %, the freezing point of the material has a range from
42°C to 58°C.

CLAIMS
A composition containing sodium acetate trihydrate as a phase change material
comprising:
(a) sodium acetate trihydrate or sodium acetate anhydrous;
(b) one or more suitable alkali soluble polymers;
(c) one or more suitable nucleation promoters; and
(d) water.
A composition according to claim 1, wherein the sodium acetate trihydrate is present
at a level of from about 80% to about 100% by weight of the composition.
A composition according to claim 1, wherein the sodium acetate anhydrous is
present at a level of from about 45% to about 60% by weight of the composition.
A composition according to claim 1 or 3 , wherein said one or more alkali soluble
polymers may be independently present at levels of from about 0.1% to about 10%
by weight of the composition.
A composition according to any of claims 1 to 4 , wherein said one or more alkali
soluble polymers is a polymer having general formula I .
A composition according to any of the preceding claims wherein said one or more
alkali soluble polymers is independently selected from: the copolymer of methacrylic
acid and methyl methacrylate, poly(methacrylic acid co-methyl methacrylate) having
a molecular weight of from about 500,000 to about 1,000,000, or a sodium,
potassium or zinc salt thereof; poly(methacrylic acid) having an average molecular
weight of about 10,000, or the sodium salt thereof; or a mixture thereof
A composition according to any of the preceding claims wherein said one or more
suitable nucleation promoters are each independently present at a level of from
about 0.1% to about 5% by weight of the composition.
A composition according to any of the preceding claims wherein said one or more
suitable nucleation promoters are independently selected from: disodium hydrogen
phosphate (DSP) and hydrated forms thereof; tetrasodium pyrophosphate (TSPP)
and hydrated forms thereof; and mixtures thereof.
9 . A composition according to any of the preceding claims wherein said the nucleation
promoters are disodium hydrogen phosphate dihydrate and tetrasodium
pyrophosphate decahydrate present at a total combined level of from about 0.5% to
about 5% by weight of the composition.
10. A composition according to any of the preceding claims additionally comprising an
agent for modifying the melting point of sodium acetate trihydrate at a level of from
about 1% to about 95% by weight of the composition.
11. A composition according to claim 10 wherein said agent is lithium acetate dihydrate.
12. A composition according to claim 10 wherein said agent is lithium acetate anhydrous.
13. A process for the preparation of compositions according to any of the preceding
claims containing sodium acetate trihydrate as a phase change material which
comprises:
(a) mixing an aqueous solution comprising sodium acetate anhydrous with at least
one suitable alkali soluble polymer; and at least one nucleation promoter;
(b) heating the resultant mixture to provide a 58°C phase change material containing
sodium acetate trihydrate; and
wherein said aqueous solution may optionally contain an agent for modifying the
melting point of sodium acetate.
14. A process according to claim 13 wherein the aqueous solution comprises: from about
40% to about 60% of sodium acetate anhydrous; from about 0.1% to about 10% of at
least one suitable alkali soluble polymer; from about 0.1% to about 5% of at least one
suitable nucleation promoter; from about 1% to about 25% of an optional melting
point depressing agent; and water to balance.
15. Use of a composition according to any of claims 1 to 10, or a composition obtainable
via the process of claims 11 or 12 as a phase change material.