LAMINATE AND PRODUCTION METHOD THEREFOR Technical Field of the Invention [0001] The present invention relates to a laminate having a fibrous structure containing a water-soluble resin and a polylactic acid resin-containing layer which is optimum to use for medical applications such as wound-dressing membranes or adhesion-preventing membranes, and a production method therefor.. Background Art of the Invention [0002] In a surgical operation represented by abdominal surgery, plastic surgery, neurosurgery, etc., there is a problem of adhesion between organs as one of complications after operation. This is caused from the phenomenon wherein, when normal tissues having received injury due to drying and oxidation are stitched to each other to be closed in the operation, in a process of being self-healed by healing of wound, an adhesion phenomenon, namely, conjugation of the tissues of organs to each other which essentially must not happen, may be caused. It is said that an adhesion is caused at a high possibility in a surgical operation, the adhesion may lead a pain or a complication causing a serious symptom such as ileus or sterility. [0003] It is difficult to treat an adhesion once caused, with medicine. Further, there is also a case where ileus due to an adhesion is caused even after several years are passed after operation. It is considered that adhesion can be treated only by adhesion separation surgery which separates the adhesion part by conducting surgical operation again, and therefore, in a surgical operation, prevention of adhesions is extremely important. [0004] So far, as the treatment for preventing tissue adhesion or delay of healing after operation, a method for covering an exposed organ tissue with a piece of gauze dipped in a saline to prevent drying and oxidation has been employed. However, because an organ has an complicated and flexible property, the method has been origins causing problems such as ones that a sufficient covering cannot be carried out by gauze, that gauze becomes an obstacle relative to working for operation of a doctor, and that the possibility of leaving gauze in the body is increased because much gauze is used. [0005] From such reasons, as the materials having an effect for preventing adhesion or for preventing delay of healing, a method for using a silicone, "Teflon" (registered trademark), a polyurethane, an oxycellulose, and the like as an adhesion-preventing membrane has been employed in order to physically separate origin tissues, but, because these materials are non-bioabsorbable materials, they are left on the surface of the biological tissue, and not only they delay repair of the tissue but also they become origins causing infection and inflammation. [0006] In recent years, in order to solve such problems, adhesion-preventing materials using gelatin or collagen which can expect bioabsorbability are reported (for example, Patent documents 1 and 2). In a case where gelatin or collagen is used, however, there is a problem where it is difficult to remove telopeptide part having an antigenicity, and further, because there is a risk of an animal-derived infectious disease such as prion contamination, it is considered that it is better to avoid use to an organism. Moreover, it is considered that there are many cases where a crosslinking agent added in order to obtain strength and control degradability is not preferred for use in an organism. [0007] On the other hand, in a natural polymer, there is such a problem that it is low in strength though it is high in affinity with skin. Therefore, in a natural polymer, it has been necessary to ensure a strength by a material crosslinked with a crosslinking agent or by use of a reinforcement material or by wrapping with a gauze. However, in case where a reinforcement material is used, because there are many cases where the structure becomes complicated, it is not practical. [0008] Further, an adhesion-preventing material using a polysaccharide such as trehalose which is low in risk of infectious disease is also reported (for example, Patent document 3). However, in case of a material using a polysaccharide, it is poor in strength, and there is a problem that suture is difficult because of lack of strength. Further, even if suture is possible, it is difficult to maintain a sutured state for a certain period of time. [0009] Further, although an adhesion-preventing material using a hyaluronic acid is also reported (for example, Patent document 4), because of its poor adherence to an organ, the membrane and the organ are liable to be shifted from each other, and whereby an adhesion may be caused, and therefore, it is not always said that it has a satisfactory performance, and further, there is a problem that it is high in manufacturing cost because it is difficult to serve it to mass production. In order to strongly adhere the adhesion-preventing membrane to the organ and the like, although there are a method for using blood products and a method for using chemical substances, these methods include a problem that a high-quality management in viewpoints of hygiene and safety is required and it is difficult to be handled. [0010] Thus, although there are many reports relating to materials for preventing tissue adhesion, a material having a satisfactory performance as an adhesion-preventing material has not been obtained. Namely, a material, being hard to cause the above-described problems and capable of preventing adhesion until a tissue is recovered and maintaining a strength until the tissue is recovered, is required. [0011] On the other hand, with respect to a production method of a laminate having a fibrous structure (B) containing a water-soluble resin and a polylactic acid resin- containing layer (C) which is optimum to use for medical applications, although it is considered to apply the following conventional general production methods, there are the following problems in the conventional methods. [0012] For example, as a production method of a laminate, there is a dry laminating method for manufacturing a polylactic acid resin-containing layer (C) and a fibrous structure (B) separately and laminating the polylactic acid resin-containing layer (C) and the fibrous structure (B) using an adhesive (for example, Patent document 5). However, because an organic solvent is used, special waste liquid facility and exhaust equipment are required from the viewpoint of environmental load, and use of a protection device such as a gas mask is required in order to prevent health damage to an operator, and the like, and thus, many considerations are required in production activities. In addition, an organic solvent, which is low in contribution to performance of a final product, is used, at the production stage the solvent is evaporated and disposed outside the product, and the affection to the cost thereof is not low at all. [0013] Further, as a production method which does not use an organic solvent with respect to a production method of a laminate, there is an extrusion laminating method for delivering a molten resin onto a surface of a fibrous structure (B) produced in advance using an extruder and the like, and thereafter, solidifying it (for example, Patent document 6). However, there is a quality problem causing an appearance defect such as one that the fibrous structure collapses by heating and press contacting and the thickness is reduced. Moreover, in case where a resin low in thermal decomposition temperature is supplied to an extruder, there are problems such as ones that deterioration of the resin is caused, that a large amount of thermal energy is required for melting the resin, and further, that the environment for operation becomes a high temperature, etc. [0014] Further, as a production method which can reduce energy used for melting of a resin with respect to a production method of a laminate, there is a thermally laminating method for thermally fusing and press contacting a part of the contact portion of a polylactic acid resin-containing layer (C) and a fibrous structure (B) (for example, Patent document 7). However, there is a quality problem causing an appearance defect such as one that the fibrous structure collapses by heating and press contacting and the thickness is reduced. In particular, in case where the polylactic acid resin-containing layer (C) is a thin membrane, there is a quality problem that, if heat is too applied, it melts and the polylactic acid resin-containing layer (C) itself collapses. Further, there is a problem that a large amount of thermal energy is required for heating the polylactic acid resin-containing layer (C) and the fibrous structure (B), a heat-transfer boy such as a metal roller or plate used for heating is required to be elevated in temperature in advance before production, and the working efficiency thereof is bad by a reason such as an excessive time being required. [0015] Further, as a production method which can reduce a load due to heat or pressure applied to a fibrous structure (B) with respect to a production method of a laminate, there is a method for providing an adhesive layer between the fibrous structure (B) and a polylactic acid resin-containing layer (C) (for example, Patent document 8). However, there is a problem that the bending ability of the laminate is poor as compared with a single layer of the fibrous structure (B) because the thickness of the adhesive layer is great, thereby causing to damage the flexibility, or a problem that the adherence becomes poor on account of a small contact area of the adhesive layer with the fibrous structure (B). [0016] Furthermore, as a production method which does not provide an adhesive layer with respect to a production method of a laminate, there is a method of needle punching for physically fixing a fibrous structure (B) and a polylactic acid resin-containing layer (C) by stacking the fibrous structure (B) and the polylactic acid resin-containing layer (C) which are manufactured separately from each other, and pressing a needle to a plurality of places from a surface of the fibrous structure (B) or the polylactic acid resin-containing layer (C) to entangle the fibrous structure (B) and the polylactic acid resin-containing layer (C) to each other (for example, Patent document 9). However, because it is necessary to perforate the polylactic acid resin-containing layer (C), it cannot be used in case where it is required that passage of a liquid, a gas, or the like is interrupted by the layer, and further, in case where the polylactic acid resin-containing layer (C) is thin, there is a problem that it is greatly broken when the needle is penetrated therethrough. Prior art documents Patent documents [00171 Patent document 1: JP-A-2004-065780 Patent document 2: JP-A-2001-192337 Patent document 3: JP-A-2003-153999 Patent document 4: WO 2005/094915 Al Patent document 5: JP-A-2005-224981 Patent document 6: JP-A-2003-251749 Patent document 7: JP-A-2014-30825 Patent document 8: JP-A-2001 -145650 Patent document 9: JP-A-2014-94214 Summary of the Invention Problems to be solved by the Invention [0018] In consideration of the background of such conventional technologies, an object of the present invention is to provide a laminate laminated with a fibrous structure (B) containing a water-soluble resin and a polylactic acid resin-containing layer (C) which is optimum to use for medical applications such as wound-dressing membranes or adhesion-preventing membranes, which is excellent in biocompatibility and easy in handling ability, and which is excellent in economic efficiency. [0019] Further, another object of the present invention is to provide a method for producing a laminate, which is excellent in working efficiency and productivity when the above-described fibrous structure (B) containing a water-soluble resin and polylactic acid resin-containing layer (C) are laminated to each other, and which is low in environmental load, and in addition, which can produce a laminate excellent in appearance without breaking the polylactic acid resin-containing layer (C), in particular, which can enhance the appearance quality (wrinkle, unevenness in lamination, etc.) even in case where the polylactic acid resin-containing layer (C) is thin. Means for solving the Problems [0020] To achieve the above-described objects, a laminate according to the present invention has the following constitution. (1) A laminate having at least one polylactic acid resin-containing layer (C) with a thickness of 10 nm - 500 run on at least one surface of a fibrous structure (B) containing a waler-soluble resin (A). (2) The laminate according to (1), wherein at least one layer (D) containing a water-soluble resin (E) with a thickness of 0.01 urn - 15 rim is provided between the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin- containing layer (C). (3) The laminate according to (1) or (2), wherein a time required from a timing at that water is applied to one surface of the fibrous structure (B) containing a water-soluble resin (A) until a timing at that the water reaches another surface of the fibrous structure (B) is a range of 10 seconds to 5 minutes. (4) The laminate according to any one of (1) to (3), wherein the water-soluble resin (A) contains a polyvinyl alcohol and/or a pullulan. (5) The laminate according to any one of (2) to (4), wherein the water-soluble resin (E) contains a polyvinyl alcohol and/or a pullulan. (6) The laminate according to any one of (1) to (5), wherein an arcal weight of the fibrous structure (B) containing a water-soluble resin (A) is in a range of 1 g/m to 1,000 g/m2. (7) The laminate according to any one of (1) to (6), wherein a thickness of the fibrous structure (B) containing a water-soluble resin (A) is in a range of 0.3 u.m to 5,000 jim. (8) The laminate according to any one of (1) to (7), wherein the polylactic acid resin is one with an amount of poly-D-lactic acid in a range of 4 mol% to 50 mol%. [0021] Further, a method for producing a laminate according to the present invention has the following constitution. (9) A method for producing a laminate comprising the step of, when a fibrous structure (B) containing a water-soluble resin (A) and a polylactic acid resin-containing layer (C) are laminated, applying water or an aqueous solution to a joining surface of the fibrous structure (B) and the polylactic acid resin-containing layer (C). (10) The method for producing a laminate according to (9), wherein the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin- containing layer (C) are laminated at a condition being fixed onto respective flat plates. (11) The method for producing a laminate according to (9), wherein the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) are laminated by being nipped between two rollers. Effect according to the Invention [0022] The laminate according to the present invention is a laminate laminated with at least one polylactic acid resin-containing layer (C) on at least one surface of a fibrous structure (B) containing a water-soluble resin (A), since it is flexible and excellent in handling ability and the fibrous structure (B) containing a water-soluble resin (A) of a thick layer can be easily removed from the polylactic acid resin-containing layer (C) of a thin layer by means of an aqueous solution when it is applied to an adherend, it is excellent in followability, adherence and coatability relative to the adherend having a curved surface, and further, if a biodegradable component is selected, it exhibits excellent compatibility to organs such as skin and internal organs, and it is optimal for use in materials for external use on the skin, such as wound-dressing materials, adhesion-preventing materials, and skin care products. [0023] Further, by providing at least one layer (D) containing a water-soluble resin (E) between the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C), the adhesive property between the polylactic acid resin-containing layer (C) and the fibrous structure (B) containing the water-soluble resin (A) can be improved, the laminate can be more stabilized relatively to a stress from outside, and the handling ability as a laminate can be improved. [0024] Further, since materials for forming the laminate are a polylactic acid resin and a water-soluble resin, the laminate can be inexpensively served to a mass production, and it is excellent in economic efficiency. [0025] Moreover, since the polylactic acid resin-containing layer (C) after being removed with the fibrous structure (B) containing a water-soluble resin (A) by means of water or an aqueous solution is transparent, a surface stuck with it is not conspicuous, and therefore, it can be applied not only to surgery operation but also to sticking to a skin, and also to use as a plaster. [0026] Furthermore, loading or sustained release of various chemicals is possible using the polylactic acid resin-containing layer (C) as a base material, and the laminate can be used also as a drug delivery system. [0027] Further, in the method for producing a laminate according to the present invention, when the above-described fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) are laminated, water or an aqueous solution is applied to a joining surface of the fibrous structure (B) and the polylactic acid resin-containing layer (C) (here, as a method for applying water or the aqueous solution, for example, there are methods such as spraying, coating and dropping, and it is preferred to apply it by spraying.), thereby laminating the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C), and therefore, as compared with conventional production methods, it is extremely simple, and excellent in working efficiency, and further, it is a production method small in environmental load. [0028] By providing at least one layer (D) containing a water-soluble resin (E) between the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C), as compared with conventional production methods, the lamination of the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) becomes easy. [0029] Further, in case where the thickness of the layer (D) containing a water-soluble resin (H) is in a range of 0.01 urn - 15 urn, as compared with conventional production methods, the appearance quality (unevenness in lamination, etc.) can be improved, the yield is enhanced and the cost competitiveness is excellent, and therefore, such a condition is preferred. In case where the thickness of the layer (D) containing a water-soluble resin (E) is less than 0.01 u,m, there is a possibility that the appearance quality (unevenness in lamination, etc.) is poor, and in case of more than 15 |im, there is a possibility that the cost competitiveness is poor. [0030] As the lamination method in the method for producing a laminate according to the present invention, by laminating the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) at a condition being fixed onto respective separate flat plates, or by laminating the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) by being nipped between two or more rollers, a laminate further excellent in appearance quality and cost competitiveness can be obtained, and therefore, such a method is preferred. [0031] In addition, by using an aqueous solution containing a water-soluble resin for spraying, the shape of the liquid drops, after the aqueous solution is sprayed from a sprayer until it reaches the surfaces of the fibrous structure (B) containing a water-soluble resin (A) and/or the polylactic acid resin-containing layer (C) and/or the layer (D) containing a water-soluble resin (E), can be stabilized, and a laminate excellent in appearance quality can be obtained, and therefore, such a condition is preferred. [0032] Such a method for producing a laminate according to the present invention is optimal, in particular, for production of medical products such as wound-dressing materials or adhesion-preventing materials and materials for external use on the skin such as skin care products, and further, also suitable for production of hygiene products and the like such as surgical gowns, antibacterial mats, poultices, stupes, artificial skins, diapers, sanitary items, gauze, first-aid adhesive tapes, cleaning supplies and masks. Brief explanation of the drawings [0033] [Fig. 1] Fig. 1 is a schematic diagram of a section showing an example of a laminate according to the present invention. [Fig. 2] Fig. 2 is a schematic diagram showing an example of a method for using a laminate according to the present invention. [Fig. 3] Fig. 3 is a schematic diagram showing rollers used for a method for producing a laminate according to an embodiment of the present invention. [Fig. 4] Fig. 4 is a schematic diagram showing a lamination method in Example 14 of the present invention. Embodiments for carrying out the Invention [0034] Hereinafter, the present invention will be explained in detail together with the embodiments. Where, in the present specification, a "film" is used as a term meaning a structural material having a two-dimensional extension, for example, as one including a sheet, a plate, a discontinuous membrane, etc. [0035] < Polylactic acid resin > The weight average molecular weight of the polylactic acid resin used in the present invention is preferably 30,000 or more, more preferably 50,000 or more, further preferably in a range of 80,000 to 400,000, and more preferably in a range of 100,000 to 500,000. Where, the weight average molecular weight referred to in present invention means a molecular weight determined with a chloroform solvent by gel permeation chromatography (GPC), and calculated by conversion method with polymethyl methacrylate (PMMA). By controlling the weight average molecular weight of the polytactic acid resin to be 30,000 or more, the mechanical properties of the polylactic acid resin-containing layer (C) according to the present invention, which contains such a polylactic acid resin, can be controlled to be excellent. [0036] The polylactic acid resin used in the present invention may be mixed with a homo-polylactie acid resin having a crystailinity and an amorphous homo-polylactic acid resin for the purpose of improving the solubility into a solvent at the time of preparing a coating liquid for a coating layer. In this case, the rate of the amorphous homo-polylactic acid resin may be decided within a range which does not damage the effects according to the present invention. Further, in case where a relatively high thermal resistance is desired to be provided to the polylactic acid resin-containing layer (C), at least one of the polylactic acid resins being used preferably includes a polylactic acid resin having an optical purity of 95% or more. [0037] It is preferred that the main component of the polylactic acid resin used in the present invention is poly-L-lactic acid (L body) and/or poly-D-lactic acid (D body). Here, the main component means that the content of the components originating from lactic acid is in a range of 70 mol% or more and 100 mol% or less relative to 100 mol% of all monomer components forming the polylactic acid resin, and a homo-polylactic acid resin substantially composed of only poly-L-lactic acid and/or poly-D-Iactic acid is preferably used. [0038] Further, the amount of poly-D-lactic acid of the polylactic acid resin used in the present invention is preferably in a range of 4 mol% to 50 mol%, and more preferably in a range of 6 mol% to 13 mol%. If the amount of poly-D-lactic acid is less than 4 mol%, the solubility into an organic solvent reduces and there is a possibility that it becomes difficult to make a coating material, and if more than 50 mol%, there is a possibility that it is hardly metabolized although there is an individual variation. [0039] The polylactic acid resin used in the present invention may be a copolymerized polylactic acid resin copolymerized with another monomer component having an ester forming function other than L-lactic acid and D-lactic acid. As a monomer component capable of being copolymerized, a hydroxycarboxylic acid such as glycolic acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 4-hydroxyvaleric acid, and 6-hydroxy-caproic acid, and in addition, compounds containing a plurality of hydroxyl groups in a molecule such as ethylene glycol, propylene glycol, butane diol, neopentyl glycol, polyethylene glycol, glycerin, or pentaerythritol, or derivatives thereof, and compounds containing a plurality of carboxylic groups in a molecule such as succinic acid, adipic acid, sebacic acid, fumaric acid, terephthalic acid, isophthalic acid, 2,6-naphthalene dicarboxylic acid, 5-sodium sulfoisophthalic acid, or 5-tetrabutylphosphonium sulfoisophthalic acid, or derivatives thereof, can be exemplified. Where, among the above-described copolymerized components, it is preferred to select a component having a biodegradabilily depending upon uses. It is preferred that these copolymerized components are contained at 40 mol% or less relative to 100 mol% of all monomer components forming the polylactic acid resin. [0040] As the method for producing a polylactic acid resin, though the details will be described later, a direct copolymerization from a lactic acid, a ring-opening copolymerization via a lactide, or the like, can be raised. [0041] From the viewpoint of suppressing reduction of strength due to hydrolysis, thereby providing a good durability (a long-term preservation property), the concentration of carboxylic end groups in the polylactic acid resin in the present invention is preferably 30 equivalents/10 kg or less, more preferably 20 equivalents/10 kg or less, and further preferably 10 equivalents/10" kg or less. If the concentration of carboxylic end groups in the polylactic acid resin is 30 equivalents/10 kg or less, because the concentration of carboxylic end groups, which also cause autocatalysis for hydrolysis, is sufficiently low, a practically good durability can be provided, and such a condition is preferred. The lower limit of the concentration of carboxylic end groups in the polylactic acid resin is not particularly restricted, and there is no problem even if it is as close to 0 equivalent as possible. [0042] As the method for controlling the concentration of carboxylic end groups in the polylactic acid resin at a condition of 30 equivalents/10" kg or less, for example, a method for controlling it by the catalyst or thermal history at the time of synthesis of the polylactic acid resin, a method for reducing the thermal history by lowering the processing temperature or shortening the heating time for forming it in a layered shape, a method for closing the ends of the carboxylic groups using a reaction type compound, etc., can be exemplified. [0043] In the method for closing the ends of the carboxylic groups using a reaction type compound, it is preferred that at least a part of the ends of the carboxylic groups in the polylactic acid resin are closed, and it is more preferred that all the ends are closed. As the reaction type compound, for example, condensation reaction type compounds such as aliphatic alcohols and amide compounds or additional reaction type compounds such as carbodiimide compounds, epoxy compounds and oxazoline compounds can be exemplified, and additional reaction type compounds are preferred from the viewpoint that excessive by-products are hardly generated at the time of reaction, and in particular, carbodiimide compounds are preferred from the viewpoint of reaction efficiency. [0044] In the polylactic acid resin-containing layer (C) in the present invention, for the purpose of improving the mechanical strength, an impact resistance improving agent may be eontaincd in a range of 2 mass% to 20 mass% relative to 3 00 mass% of the whole of the polylactic acid resin-containing layer (C). Preferably, it is in a range of 2.5 mass% to 15 mass%. As the content of the impact resistance improving agent increases, the improvement effect of the impact resistance increases, but, there is a possibility that a great improvement of mechanical properties cannot be achieved even if it is contained at a content over 20 mass%. [0045] As the impact resistance improving agent used for improving the impact resistance in the present invention, aliphatic polyesters or aliphatic aromatic polyesters other than the polylactic acid resin are preferred from the viewpoint that they have a good dispersibility in the polylactic acid resin and a higher effect can be obtained by a small amount thereof. [0046] The aliphatic polyesters or aliphatic aromatic polyesters other than the polylactic acid resin are not particularly limited, and concretely, a polyglycolic acid, a poly(3-hydroxybutyric acid), a po!y(4-hydroxybutyric acid), a poly(4-hydroxyvaleric acid), a poly(3-hydroxyhexanoic acid) or a polycaprolactone, a polyethylene adipate, a polyethylene succinate, a polybutylene succinate, a polybutylene succinate adipate, etc., can be exemplified. [0047] Furthermore, in order to improve the mechanical properties and maintain the biodegradability, a polybutylene succinate-based resin, which is an aliphatic polyester other than the polylactic acid resin, is preferably used. More preferably, a polybutylene succinate or a polybutylene succinate adipate, which is great in effect for improving mechanical properties and excellent in compatibility with the polylactic acid resin, is used. [0048] The weight average molecular weight of the polybutylene succinate-based resin used in the present invention is preferably in a range of 100,000 to 300,000. Where, the polybutylene succinate-based resin is prepared by polycondensation of 1,4-butane diol and succinic acid. [0049] The polylactic acid resin in the present invention can be prepared, for example, by the following method. As the raw material, a lactic acid component of L-lactic acid or D-lactic acid and the aforementioned hydroxycarboxylic acid other than the lactic acid component can be used together. Further, cyclic ester intermediates of the hydroxycarboxylic acid, for example, such as lactide or glycolide, can also be used as the raw material. Furthermore, dicarboxylic acids or glycols can also be used. [0050] The polylactic acid resin can be prepared by a method for directly dehydration condensing the above-described raw material or a method for ring-opening polymerizing the above-described cyclic ester intermediate. For example, in case where it is prepared by the direct dehydration condensation, a polymer having a high molecular weight can be prepared by polymerization by a method for serving the lactic acid or the lactic acid and the hydroxycarboxylic acid to azeotropic dehydration condensation preferably under the presence of an organic solvent, in particular, a phenylether-based solvent, preferably, by removing water from the solvent distillated by the azeotrope and returning the solvent controlled at a substantially dehydrated condition to the reaction system. [0051] Further, It is also known that a polymer having a high molecular weight can be prepared also by ring-opening polymerizing a cyclic ester intermediate such as lactide under a pressure-reduced condition, using a catalyst such as octyl tin. At that time, a polymer small in amount of lactide can be obtained by employing a method for adjusting the condition for removing the moisture component and the low-molecular compounds in the organic solvent at the time of heat reflux, a method for suppressing a depolymerization by deactivating the catalyst after the polymerization, a method for heat treating the prepared polymer, etc. [0052] The thickness of the polylactic acid resin-containing layer (C) in the present invention is controlled in a range of 10 nm to 500 nm from the viewpoint of the followability in shape to an adherend, and it is preferably in a range of 10 nm to 200 nm. If less than 10 nm, there is a possibility that it becomes difficult to maintain the shape, and if more than 500 nm, there is a possibility that wrinkles are generated when stuck to an adherend. [0053] Various kinds of additives may be contained in a range of 30 mass% or less relative to 100 mass% of the whole of the polylactic acid resin-containing layer (C) as long as the content is within a range which does not damage the effects according to the present invention. As the various kinds of additives, an antioxidant, a weather resistance agent, a thermal stabilizer, a lubricant, a nucleating agent, a ultraviolet absorber, a colorant, etc. can be used. The lower limit of the content of the additive is not particularly restricted, and there is no problem even if it is 0 mass% relative to 100 mass% of the whole of the polylactic acid resin-containing layer (C). Further, inorganic or organic particles may be contained in a range of 20 mass% or less relative to 100 mass% of the whole of the polylactic acid resin-containing layer (C) as long as the content is within a range which does not damage the transparency. For example, calcium carbonate, titanium oxide, silicon oxide, calcium fluoride, lithium fluoride, alumina, barium sulfate, zirconia, calcium phosphate, cross-linked polystyrene-based particles or metal nanoparticles, etc. can be used. The lower limit of the content of the inorganic or organic particles is not particularly restricted, and there is no problem even if it is 0 mass% relative to 100 mass% of the whole of the polylactic acid resin-containing layer (C). [0054] Further, a bioabsorbable material layer comprising gelatin, collagen, hyaluronic acid, chitosan, synthetic polypeptide, etc. may be further formed on at least one surface of the polylactic acid resin-containing layer (C) within a range which does not damage the effects according to the present invention. [0055] < Water-soluble resin (A), water-soluble resin (E)> The water-soluble resin (A) and water-soluble resin (E) are polymers which are soluble in an aqueous solution such as water, hot water, saline or glucose solution. Concretely, a polyvinyl alcohol or a copolymer thereof, polysaccharides such as a dextran, an agarose, a pullulan, a chitosan, a mannan, a carrageenan, an alginate, a starch group (oxidized starch, etherified starch, dextrin, etc.), an amylose, an amylopectin, a pectin, a lentinan, a hyaluronic acid, a hylan, a cellulose derivative (methyl cellulose, ethyl cellulose, carboxymethyl cellulose, carboxyethyl cellulose, hydoxyethyl cellulose, hydoxypropyl cellulose, etc.) etc., polypeptides such as a gelatin, a collagen, an elastin, an albumin, a hemoglobin, a transferrin, a globulin, a fibrin, a fibrinogen, a keratin sulphate, etc., copolymerized polyesters having a polar group such as a polyvinyl pyrrolidone, a sulfoisophthalic acid, etc., vinyl-based polymers such as a polyhydroxyethyl methacrylate or a copolymer thereof, acryl-based polymers, urethane-based polymers, ether-based polymers, etc., can be preferably exemplified. Further, polymers modifying these various polymers with a functional group such as a carboxylic group, an amino group, a methylol group, etc. can also be preferably used. In particular, a polyvinyl alcohol and a pullulan are preferred from the viewpoint of production cost, availability and hygiene. [0056] Polyvinyl alcohol is a saponificate of polyvinyl acetate, and the degree of saponification thereof is preferably in a range of 80 to 99.9 mol%, and more preferably in a range of 85 mol% o 98 mol%. In case where the degree of saponification of polyvinyl alcohol is more than 99.9 mol%, there is a possibility that the solubility of the obtained layer (D) containing a water-soluble resin (E) into water is reduced, but it can be used to the water-soluble resin (A) or the water-soluble resin (E) depending upon the purpose such as adjustment of the time of dissolution of the fibrous structure (B). Where, the polyvinyl alcohol in the present invention includes a polyvinyl alcohol copolymer. As the polyvinyl alcohol copolymer, the units of vinyl alcohol thereof are preferably in a range of 80 mol% to 98 mol%, and more preferably in a range of 85 mol% to 98 mol%. [0057] Where, the degree of saponification means a rate (mol%) of the mol number of the vinyl alcohol units relative to the total mol number of the structural units capable of being converted into vinyl alcohol units by saponification (typically, vinyl ester units) and the vinyl alcohol units contained in the polyvinyl alcohol or the copolymer thereof. Here, the degree of saponification can be determined based on JIS K6726:1994. [0058] With respect to pullulan, because of being advantageous in the points of availability and cost, usually, a pullulan, which is produced by cultivating an yeast such as genus oreobacidium in a culture medium containing starch decomposition products, can be advantageously used. For example, a pullulan sold by Hayashibara Co., Ltd. (trade name: "pullulan PI-20" and "pullulan PF-20") can be suitably used. However, it is not limited to these, and another pullulan product can also be used as long as the purpose of the present invention does not deviate. Further, as needed, a maltotriose, made as a derivative by modification or the like such as esterification at an arbitrary substitution degree, may be employed as a repeated unit. The weight average molecular weight of a pullulan used in the present invention is preferred to be usually 5,000 dallon or more, preferably 10,000 dalton or more and 1,000,000 dalton or less, more preferably 50,000 dalton or more and 500,000 dalton or less. Where, by selecting the weight average molecular weight or the molecular weight distribution of a pullulan, the layer (D) containing a water-soluble resin (E) can be controlled at a desired collapse speed. Although it is depending upon other components to be compounded, if the weight average molecular weight is less than 5,000 dalton, there is a possibility that it becomes difficult to form a sheet-like membrane, and if more than 1,000,000 dalton, there is a possibility that the dissolution speed into an aqueous solvent becomes too small. [0059] The average degree of polymerization of a water-soluble polymer forming the water-soluble resin (A) or water-soluble resin (E) is preferably in a range of 100 to 5,000, more preferably in a range of 200 to 2,500, and further preferably in a range of 400 to 1,800. Here, the average degree of polymerization means a number average degree of polymerization. If the average degree of polymerization is in this range, since a uniform coating layer is easily formed, the mechanical strength as the coating layer is high and it is excellent in re-solubility in an aqueous solution, such a condition is preferred. Where, the average degree of polymerization of polyvinyl alcohol mentioned in the present specification means an average degree of polymerization determined based on JIS K6726:1994. [0060] In the present invention, two kinds or more of water-soluble polymers having different average degrees of polymerization may be mixed and used. By this, in addition to high mechanical strength and re-solubility in an aqueous solution as a coating layer, a coating layer good also in adherence with the base material film and the polylactic acid resin can be obtained, and therefore, such a condition is preferred. [0061] It is preferred to mix and use two kinds or more of water-soluble polymers of a water-soluble polymer having a low average degree of polymerization of 100 to 800 and a water-soluble polymer having a high average degree of polymerization of 1,000 to 2,500. The water-soluble polymer having a low degree of polymerization preferably has an average degree of polymerization of 300 to 700. The water-soluble polymer having a high degree of polymerization preferably has an average degree of polymerization of 1,300 to 1,700. [0062] Various kinds of additives may be contained in a range of 30 mass% or less relative to 100 mass% of the whole of the water-soluble resin (A) or water-soluble resin (E) as long as the content is within a range which does not damage the effects according to the present invention. The lower limit is not particularly restricted, and there is no problem even if it is 0 mass%. As the various kinds of additives, an antioxidant, a weather resistance agent, a thermal stabilizer, a lubricant, a nucleating agent, a ultraviolet absorber, a colorant, etc. can be used. Further, inorganic or organic particles may be contained in a range of 20 mass% or less as long as the content is within a range which does not damage the effects according to the present invention. The lower limit is not particularly restricted, and there is no problem even if it is 0 mass%. For example, calcium carbonate, titanium oxide, silicon oxide, calcium fluoride, lithium fluoride, alumina, barium sulfate, zirconia, calcium phosphate, cross-linked polystyrene-based particles or metal nanoparticles, etc. can be used. [0063] In the present invention, a layer (D) containing a water-soluble resin (E) may be provided between the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C). By proving the layer (D) containing a water-soluble resin (E), the adhesive property between the fibrous structure (B) containing a water-soluble resin (A) and the polylactic acid resin-containing layer (C) is improved, the laminate is more stabilized against an external stress, and the handling ability as a laminate is improved. [0064] The thickness of the layer (D) containing a water-soluble resin (E) is preferably in a range of 0.01 Lim to 15 |xm, more preferably in a range of 1 u.m to 15 jim, from the viewpoints of the adhesive property to the fibrous structure (B) containing a water-soluble resin (A), the handling ability as a laminate, and the shape followability to an adherend. If it is thinner than 0.01 jam, there is a possibility that handling as a laminate becomes difficult because the adhesion with the fibrous structure (B) becomes weak, and if more than 15 uin, there is a possibility that wrinkles are generated when stuck to an adherend. or that it takes a time for being re-dissolved in water, it becomes hard to be separated from the biodegradable resin, and the adherence to an adherend is lowered. [0065] The fibrous structure (B) in the present invention includes, of course, one having a fabric form, and may be one formed from fibers having another form such as a strip¬like one, a string-like one or a yarn-like one. As a fabric, a woven fabric, a knitted fabric and a nonwoven fabric are preferred, and it may be a composite material. From the viewpoint of productivity, a nonwoven fabric is preferred. [0066] For example, in case of a nonwoven fabric, although the production is not particularly restricted, a fleece is formed using a dry method, a wet method, a melt blow method, a spun bond method, etc., and connection between fibers can be achieved using a chemical bond method, a thermal bond method, a needle punch method, a water complex method, etc. [0067] The average fiber diameter of the fibers used for the fibrous structure (B) in the present invention is preferably in a range of 0.001 um to 100 u.m from the viewpoints of dissolvability into water and fiber strength. By setting the average fiber diameter at 100 urn or less, sufficient flexibility and shape memory property can be provided, and therefore such a condition is preferred, and on the other hand, by setting the average fiber diameter at 0.001 jim or more, in the spinning the yarn can be stably formed, and if 0.1 u.m or more, the stability at the time of spinning can be enhanced, and therefore such a condition is preferred. [0068] The formation of the fiber used for the fibrous structure (B) in the present invention is not particularly restricted, it may be formed from one kind of polymer, and there is no problem that it is formed from two or more kinds of polymers. [0069] It is preferred that the areal weight of the fibrous structure (B) in the present invention (part except a reinforcing layer described later) is in a range of 1 g/m2 to 1,000 g/m . By controlling the above-described areal weight preferably at 10 g/m or more, more preferably at 15 g/m' or more, the formation stability and the dimensional stability of the fibrous structure (B) are excellent and occurrence of unevenness in processing and breakage due to elongation at the time of being laminated with the polylactic acid resin-containing layer (C) can be suppressed, and therefore, such a condition is preferred. On the other hand, by controlling the above-described areal weight preferably at 400 g/m" or less, more preferably at 150 g/m" or less, the handling at the time when the fibrous structure (B) is made in a form of a roll becomes easy, and further, the cushion property of the fibrous structure (B) is appropriately suppressed, and at the time of being laminated with the polylactic acid resin-containing layer (C), the pressing pressure can be appropriately maintained at the surface of the fibrous structure (B), thereby performing an efficient lamination processing, and therefore, such a condition is preferred. [0070] It is preferred that the thickness of the fibrous structure (B) in the present invention (thickness of part except a reinforcing layer described later) is in a range of 0.1 [im to 5,000 urn. By controlling the above-described thickness preferably at 50 (.im or more, more preferably at 100 u,m or more, the formation stability and the dimensional stability of the fibrous structure (B) are excellent and occurrence of unevenness in processing and breakage due to elongation at the time of being laminated with the polylactic acid resin-containing layer (C) can be suppressed, and therefore, such a condition is preferred. On the other hand, by controlling the above-described thickness preferably at 2,000 u,m or less, more preferably at 500 urn or less, the cushion property of the fibrous structure (B) is appropriately suppressed, and at the time of being laminated with the polylactic acid resin-containing layer (C), the pressing pressure can be appropriately maintained at the surface of the fibrous structure (B), thereby performing an efficient lamination processing, and therefore, such a condition is preferred. [0071] The fibrous structure (B) in the present invention contains a water-soluble resin. This is because by containing a water-soluble resin, as described later, the fibrous structure (B) can be easily dissolved with an aqueous solution such as water after being stuck to an adherend. Here, the water-soluble resin (A) is as being aforementioned. [0072] Concretely, with respect to the fibrous structure (B) in the present invention, it is preferred that the time required from a timing at that water (about 0.04 ml) is applied to one surface of the fibrous structure (B) until a timing at that the water reaches another surface of the fibrous structure (B) is a range of 10 seconds to 5 minutes. "The water reaches another surface" mentioned here means a condition where the fibers of another surface of the fibrous structure (B) are dissolved so that the form of the fibers cannot be maintained. If 10 seconds or more, since the handling under presence of moisture, blood, etc. can be facilitated, such a condition is preferred. In case of being used as a supporting material of an adhesion-preventing material, because a certain time is required until being stuck to a tissue, the time is preferably 30 seconds or more, particularly preferably 1 minute or more. On the other hand, if 5 minutes or less, since it can be quickly removed after being stuck to a tissue, such a condition is preferred. Although it is achieved to provide a water proof property for a long time by a method for making a layer comprising a water-insoluble polymer compound such as an outermost layer at a high areal weight or at a high density, or the like, in this case, since the feeling tends to become hard, the time is preferably 3 minutes or less, and particularly preferably 2 minutes or less. [0073] Further, in the fibrous structure (B) in the present invention, for the purpose of improving the formation stability and the dimensional stability of the fibrous structure (B), a structure may be employed wherein a reinforcing layer is provided to a surface of the fibrous structure (B) opposite to the joining surface between the fibrous structure (B) and the polylactic acid resin-containing layer (C). As the reinforcing layer, can be employed a woven fabric, a knitted fabric, a nonwoven fabric (including a paper), a plastic film, a metal thin film, etc. [0074] A treatment such as pressing may be performed to the fibrous structure (B) in the present invention. The press treatment may be performed at any time between processes from a process for obtaining a nonwoven fabric to a process after joining with (he polylactic acid resin-containing layer (C). In order (o enhance the setting property at the time of pressing, a heat pressing is preferably employed. [0075] A base material in the item of a method for producing a laminate described later will be explained. A base material used in the present invention is used as a base material used for forming the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C), or as a base material used for forming a single layer of the polylactic acid resin-containing layer (C). [0076] The base material used in the present invention is preferably a film comprising a polymer material. As the material of a base material film, for example, exemplified are a polyolefin such as polyethylene and polypropylene, a polyester such as polyethylene terephthalate, polybutylene terephthalate and polyethylene-2,6-naphthalate, a polyamide such as nylon 6 and nylon 12, polyvinyl chloride, ethylene-vinyl acetate copolymer or a saponificate thereof, polystyrene, polycarbonate, polysulfone, polyphenylene oxide, polyphenylene sulfide, aromatic polyamide, polyimide, polyamideimide, cellulose, cellulose acetate, polyvinylidene chloride, polyacrylonitrile, polyvinyl alcohol, and copolymers thereof. From the viewpoint of ensuring an adherence with the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C), and a uniform thickness as a film to be laminated, as the material of a base material film, a polyester such as polyethylene terephthalate, or a polyolefin such as polypropylene, is preferred. Because the wetting tension at surface is high, a polyester such as polyethylene terephthalate is particularly preferred. [0077] It is more preferred to perform a surface treatment, such as a corona discharge treatment, a flame treatment, a plasma treatment or a ultraviolet irradiation treatment, to the base material film before forming the layer (D) containing a water-soluble resin (E)or the polylactic acid resin-containing layer (C) as a coating layer. [0078] Although the base material film may be any of a non-oriented film, a uniaxially oriented film and a biaxially oriented film, a biaxially oriented film is preferred from the viewpoint of dimensional stability and mechanical properties. [0079] Further, various kinds of additives may be contained in the base material film. For example, an antioxidant, a weather resistance agent, a thermal stabilizer, a lubricant, a nucleating agent, a ultraviolet absorber, a colorant, etc. can be contained. Further, inorganic or organic particles may be contained at a content which does not remarkably damage the surface smoothness. For example, talc, kaolinile, calcium carbonate, titanium oxide, silicon oxide, calcium fluoride, lithium fluoride, alumina, barium sulfate, zirconia, mica, calcium phosphate, cross-linked polystyrene-based particles, etc. can be contained. [0080] The average particle diameter of the above-described particles is preferably in a range of 0.001 |xm to 10 fim, and more preferably in a range of 0.003 jim to 5 jam. Here, the average particle diameter means a particle diameter determined by taking a photograph at a magnification of 10,000 times to 100,000 times using a transmission-type electron microscope or the like and calculating in a manner of number average. [0081] Furthermore, these base material films are preferably transparent. The total light transmittance of a base material film is preferably 40% or more, further preferably 60% or more, and there is no problem even if the upper limit is close lo 100% as much as possible. The haze of a base material film is preferably 20% or less, and more preferably 15% or less. If the haze is more than 20%, there is a possibility that inspection by an optical inspection machine with respect to impurities contained in the laminated layer (D) containing a water-soluble resin (E) and polylactic acid resin-containing layer (C) becomes difficult. The lower limit of the haze is not particularly restricted, and there is no problem even if it is as close to 0% as possible. [0082] Although the thickness of the base material film is not particularly restricted, it is preferably in a range of 2 um lo 1,000 fim, and more preferably in a range of 10 jim to 500 u.m from the viewpoint of economy. [0083] Production method> Next, a typical production method of a laminate according to the present invention will be described. [0084] [Method for producing a laminate] Although the method for producing a laminate in the present invention is not particularly restricted, for example, the following method can be employed. (1) A laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C), or a single layer of the polylactic acid resin-containing layer (C) is formed on a base material film which becomes a base material. (2) The formed polylactic acid resin-containing layer (C) (or, the laminated layer of the polylactic acid resin-containing layer (C) and the layer (D) containing a water-soluble resin (E) in case where the layer (D) containing a water-soluble resin (E) is present) is delaminated from the base material film. (3) The formed and delaminated layer and the fibrous structure (B) containing a water-soluble resin (A) are stuck and laminated to each other, and fixed to each other. At this lamination, water or an aqueous solution is provided between the formed and delaminated layer and the fibrous structure (B) (for example, provided by spraying). [0085] [Method for making a single layer of a polylactic acid resin-containing layer (C)] Although the method for making a single layer of a polylactic acid resin-containing layer (C) is not particularly restricted, for example, the following methods can be considered. (1) A method for mechanically delaminating the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) from the base material film, and thereafter, obtaining a single layer of the polylactic acid resin-containing layer (C) by dissolving the layer (D) containing a water-soluble resin (E) into an aqueous solution, thereby removing it. (2) A method for dipping the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) in an aqueous solution, and dissolving the layer (D) containing a water-soluble resin (E) and removing it, thereby obtaining a single layer of the polylactic acid resin-containing layer (C). Here, as the aqueous solution, although various aqueous solutions such as saline and glucose solution can be used, in particular, water is preferably used. (3) A method for laminating the polylactic acid resin-containing layer (C) onto a base material film having a smooth surface, and obtaining a single layer of the polylactic acid resin-containing layer (C) by mechanically delaminating the polylactic acid resin-containing layer (C) from the base material film. However, since there is a possibility that the polylactic acid resin-containing layer (C) is thin and the processing becomes difficult, or that a defect such as a pinhole is liable to occur, if possible, it is preferably made through a condition of the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C). [0086] [Method for making a laminated layer of a polylactic acid resin-containing layer (C) and a layer (D) containing a water-soluble resin (E)] 1. Lamination of a layer (D) containing a water-soluble resin (E) and a polylactic acid resin-containing layer (C): On one surface of a base material, a layer (D) containing a water-soluble resin (E) and a polylactic acid resin-containing layer (C) are laminated in this order. [0087] Although the lamination method is not particularly restricted, a gravure coating, a direct lip coating, a slot coating, a comma coating, an ink jet, a silk screen printing, etc. can be exemplified. Although the base material is not particularly restricted, a glass plate, a metal plate, a plastic film, etc. can be exemplified, and from the viewpoint of economy, it is desired to use a plastic film as the base material film, and in particular, a plastic film having a surface smoothness is desired. [0088] In case where a biaxially oriented film of a polyester such as polyethylene terephthalate or a polyolefin such as polypropylene is used as the base material, any method of off-line coating for coating after the film formation process of the biaxially oriented film and in-line coating for coating in the film formation process of the biaxially oriented film may be used. [0089] In case where in-line coating is used, it is preferred to perform the coating before the film is thermoset. The thermosetting means that a film is crystallized by heat treating the oriented film at a condition keeping the film at a temperature higher than the stretching temperature and lower than the melting point of the film. Therefore, a coating applied to a non-oriented film, a film after uniaxial stretching in the longitudinal direction or the transverse direction, or a film after biaxial stretching is preferred. A coating applied to a film immediately after uniaxial stretching is more preferred, and it is further preferred to further stretch the film in one or more axial directions and thermoset it. As the method for drying a coating layer, a heated roll contacting method, a heat medium (air, oil, etc.) contacting method, an infrared heating method, a microwave heating method, etc. can be utilized. [0090] As the method for forming a coating layer on the base material film by off¬line coaling, from the point of being able to coat a thin layer at a high speed, a method for gravure coating, reverse coating, spray coating, kiss coating, comma coating, die coating, knife coating, air knife coating or metering bar coating a solution prepared by dispersing a component of a coating layer in various kinds of solvents is preferred. The base material film is more preferably applied before coating with a adherence promoting treatment of, for example, a corona discharge treatment in air, in nitrogen gas, or under an atmospheric condition of nitrogen/carbon dioxide mixed gas or another gas, a plasma treatment under a pressure reduced condition, a flame treatment, a ultraviolet treatment, etc. Furthermore, an anchoring treatment may be applied using an anchoring treatment agent such as a urethane resin, an epoxy resin or a polyethylene inline. [0091] It is preferred that the drying of the coating layer of the layer (D) containing a water-soluble resin (E) is performed within a range of 60°C to 180°C in case of off¬line coating, and within a range of 80°C to 250°C in case of in-line coating. The time for drying is preferably in a range of 1 second to 60 seconds, more preferably in a range of 3 seconds to 30 seconds. [0092] It is preferred that the drying of the coating layer of the polylactic acid resin is performed within a range of 60°C to 310°C in case of off-line coating, and within a range of 80°C to 1S0°C in case of in-line coating. The time for drying is preferably in a range of 1 second to 60 seconds, more preferably in a range of 3 seconds to 30 seconds. [0093] 2. Isolation of layer (D) containing a water-soluble resin (E) from base material: Next, by mechanical delamination at the interface between the base material and the layer (D) containing a water-soluble resin (E), the layer (D) containing a water-soluble resin (E) or the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) is obtained. [0094] 3. Fixing of laminated layer to supporting material: Further, the obtained single layer or laminated layer is set such that the polylactic acid resin-containing layer (C) and (he supporting material come into contact with each other. Although the supporting material is not particularly restricted, a glass plate, a metal plate, a plastic film, etc. can be exemplified, and from the viewpoint of economy, it is preferred to use a plastic film as the supporting material, in particular, a plastic film having a surface release property. [0095] 4. Dissolution of surface of layer (D) containing a water-soluble resin (E) or fibrous structure (B): Next, an aqueous solution is applied to the layer (D) containing a water-soluble resin (E) or the fibrous structure (B) containing a water-soluble resin (A) to dissolve a part of the surface layer. Further, the layer (D) containing a water-soluble resin (E) may be completely removed by this process. [0096] Although the aqueous solution is not particularly restricted, a purified water, an alcohol aqueous solution, a mineral dispersion, a chemical dispersion, etc. can be exemplified, and from the viewpoint of economy, a purified water is desired. [0097] 5. Fixing of fibrous structure (B) containing a water-soluble resin (A): Although the lamination method of the single layer or the laminated layer and the fibrous structure (B) is not particularly restricted, there are a method for spraying water or an aqueous solution to the surface of the layer (D) containing a water-soluble resin (E) in the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) or to the surface of the fibrous structure (B) to dissolve it, and bringing the dissolved surface into contact with a surface side of one of the respective layers containing a water-soluble resin to weld the respective surfaces; a method for spraying water or an aqueous solution to the surface of the single layer of the polylactic acid resin-containing layer (C) after forming the single layer of the polylactic acid resin-containing layer (C), thereafter, bringing it into contact with the fibrous structure (B), and dissolving the surface of the fibrous structure (B) contacted to the polylactic acid resin-containing layer (C) to bond them; and the like. [0098] [Method for spraying water or aqueous solution] Although the above-described spraying method of water or aqueous solution is not particularly restricted, it may be able to uniformly and broadly disperse a liquid at a fine form using a sprayer such as a spray or a shower, and for example, an accumulator spray method, a nozzle spray method (two-fluid nozzle, three fluid nozzle or four -fluid nozzle), an Inkjet method, etc., can be used. [0099] [Lamination method] As the lamination method in the present invention, the following two kinds of methods are preferred. Lamination method A: lamination method wherein the fibrous structure (B) and the single layer of the polylactic acid resin-containing layer (C) or the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) are laminated at a condition being fixed onto separated respective flat plates. Lamination method B: lamination method wherein the fibrous structure (B) and the single layer of the polylactic acid resin-containing layer (C) or the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) are stuck to each other and laminated by being nipped between two rollers. [0100] [Coating material containing water-soluble resin (A) or water-soluble resin (E)] A coating material containing a water-soluble resin (A) or a water-soluble resin (E) can be used when the laminated layer of the layer (D) containing a water-soluble resin (E) and the polylactic acid resin-containing layer (C) is laminated with the fibrous structure (B) containing a water-soluble resin (A). [0101 j As the coating material containing a water-soluble resin (A) or a water-soluble resin (E), a solution uniformly dissolved with components is preferred. As its solvent, water or a mixed solution of water and a lower alcohol is preferably used. It is more preferred to use a mixed solution of water and a lower alcohol. [0102] The concentration of solid components of the coating material containing a water-soluble resin (A) or a water-soluble resin (E) is preferably 1.0 mass% or more and 15 mass% or less, from the viewpoint of productivity such as viscosity, drying efficiency and coatability of the coating material. If a high-concentration coating material more than 15 mass% is used, the viscosity of the solution becomes too high, and there is a possibility that it becomes difficult to control the thickness of the layer (D) containing a water-soluble resin (E). In case where a low-concentration coating material less than 1,0 mass%, a method for adding a low-boiling point solvent having a high volatility and a compatibility with water to the solvent of the coating material, a method for performing the drying of the coating layer at a temperature of water boiling point or higher, or the like, is employed. [0103] Further, in order to provide an application ability, another water-soluble organic compound as a third component may be contained in the mixed solvent as long as its content is within a range at which the stability of the coaling material containing a water-soluble resin (A) or a water-soluble resin (E) can be maintained. As the water-soluble organic compound, for example, alcohols such as methanol, ethanol, n-propanol and isopropanol, glycols such as ethylene glycol and propylene glycol, glycol derivatives such as methyl cellosolvc, ethyl cellosolve and n-bulyl cellosolve, polyhydric alcohols such as glycerin and wax groups, ethers such as dioxane, esters such as ethyl acetate, ketones such as methyl ethyl ketone, etc. can be raised. Further, the pH of the dispersion is preferably in a range of 2 to 11 from the point of stability of the solution. [0104] [Coating material containing polylactic acid resin] As the coating material containing a polylactic acid resin, a solution uniformly dissolved with components is preferred. Although its solvent is not particularly restricted, it is preferred to use at least a sole solvent or a solution mixed with two or more kinds selected from the group consisting of butyl alcohol, chloroform, cyclohexane, acetonitrile, dichloromethane, dichloroethane, ethyl acetate, ethyl ether, dipropyl ether and toluene. From the viewpoint of productivity and handling ability, ethyl acetate is particularly preferred. [0105] Although the solid-component concentration of the coating material containing a polylactic acid resin is not particularly restricted, it is preferably 1.0 mass% or more and 10 mass% or less, from the viewpoint of the productivity such as viscosity, drying efficiency and coatability of the coating material. [0106] Further, in order to provide an application ability, another organic compound as a third component may be contained in the solution as long as its content is within a range at which the stability of the coating material containing a polylactic acid resin can be maintained. [0107] [Method for preparing coating material] Although the methods for preparing the coating material containing a water-soluble resin (A) or a water-soluble resin (E) and for preparing the coating material containing a polylactic acid resin are not particularly restricted, in case where various kinds of additives such as cross-linking agent and particles are added within a range at which the effects according to the present invention are not damaged, it is preferred that the resin and the additives are dispersed uniformly in the coating material. As needed, may be employed a method for enhancing the solubility of the resin by raising the temperature of the solvent using a heater or the like, or a method for employing a mechanically forcible dispersion treatment using a device such as homo mixer, a jet agitor, a ball mill, a bead mill, a kneader, a sand mill or a three-roll mechanism. [0108] [Method for using laminate] In an operation for an abdominal cavity, it is more preferable than laparotomy to open a small hole on the abdominal cavity and perform the operation using an endoscope, because the invasiveness to the human body is smaller. In this case, a laminate is to be stuck to a target part through a thin cylindrical vessel such as a trocar. In such a case, since the laminate according to the present invention is good in passing property through the trocar and extensibility of the laminate after passing through the trocar, the laminate can particularly suitably used to an operation using an endoscope. ("Good in extensibility" mentioned here means that the laminate once pressed into a trocar can be easily extended to an original form by a forceps or the like after being passed through the trocar.) [0109] The laminate according to the present invention has a structure, for example, as shown in Fig. 1. Namely, it is a laminate 3 having at least one polylactic acid resin-containing layer (C) 2 with a predetermined thickness on at least one surface of a fibrous structure (B) 1 containing a water-soluble resin (A). [0110] As the method for using the laminate according to the present invention, a using method shown in Fig. 2 is exemplified as an example. Namely, it is a method for using the laminate for pressing the laminate 3 according to the present invention into a cylindrical vessel 5 using a pressing jig 4 from one opening of the vessel 5, sending the laminate 3 out of the other opening, after sticking the laminate 3 to a surface of an adherend 6, applying a liquid onto the laminate 3 to dissolve the fibrous structure (B) 1 (shown in Fig, 1), thereby removing the fibrous structure (B), and leaving the polylactic acid resin-containing layer (C) 2 (shown in Fig. 1) on the surface of the adherend 6. [0111] [Uses] The laminate according to the present invention can be suitably used for medical applications such as wound-dressing membranes or adhesion-preventing membranes capable of being used in an organism or even under an environment adhered with moisture. Examples [0112] Hereinafter, Examples and Comparative Examples (Examples 1-12 and Comparative Examples 1-8) with respect to the laminate according to the present invention and Examples and Comparative Examples (Examples 13-16 and Comparative Examples 9-13) with respect to the method for producing a laminate according to the present invention will be explained. First, the methods for evaluating the properties used in the present invention are as follows. [0113] (1) Areal weight of fibrous structure (B): The areal weight was determined based on the method described in JIS L 1096 8.3.2 (1999). [0114] (2) Thickness of laminate, fibrous structure (B), layer (D) containing water-soluble resin (E) and polylactic acid resin-containing layer (C): In case of being determined from a state of a laminate, first, a dial thickness gauge (supplied by OZAKI MFG.CO.,LTD., product name: "Peacock H", amount of scale: 0.01 mm, measurement force: 1.8N or less) was used, and an average value of 10 measurement points of each sample was determined to be a total thickness of the laminate. However, in case where the total thickness is less than 0.05 mm, a dial thickness gauge higher in accuracy (supplied by Teclock Corporation, type: SM-1201L, amount of scale: 0.001 mm, measurement force: 1.5N or less) was used. [0115] Next, in order to determine the thickness of each layer, a perpendicular section in the thickness direction was prepared by a microtome, and the section was observed using a scanning electron microscope (SEM, supplied by Keyence Corporation, VE-7800) and appropriately adjusting the magnification in a range of 2,500 times to 100,000 times so that each observed layer was put within 10% to 90% of the angle of visibility. The thickness of each layer was determined as an average of values measured al different 10 sections of an identical sample. In case where a thickness of each layer became 0.1 urn or less and it was difficult to observe by the above-described method, it was similarly observed using a high-resolution transmission electron microscope (supplied by JEOL Ltd., JEM-2100) and adjusting the magnification in a range of 500,000 times to 1,000,000 times. In case where the determination was still difficult even by the method, the thickness was determined by storing the observed image and appropriately enlarging the image (for example, by printing it at an A3 size or the like). The thickness of a fibrous structure (B) was determined as a thickness calculated by subtracting the thicknesses of a layer (D) containing water-soluble resin (E) and a polylactic acid resin-containing layer (C) from the total thickness of the laminate. Where, the thickness of a fibrous structure (B) in case having a reinforcing layer was determined as a thickness calculated by subtracting the thicknesses of a layer (D) containing water-soluble resin (E), a polylactic acid resin-containing layer (C) and the reinforcing layer from the total thickness of the laminate. Namely, the thickness of a fibrous structure (B) in case having a reinforcing layer means a thickness of only the fibrous structure (B) which does not include the thickness of the reinforcing layer. [0116] (3) Evaluation of dis solvability of fibrous structure (B): The height from a surface of a test piece to a tip of a burette was adjusted so as to become 3 0 mm. The timing when one drop of water was dropped from the burette to one surface of the test piece of a fibrous structure (B) was referred to as a starting time, the timing when the water permeated to another surface thereof and dissolved it was referred to as a finishing time, and a time required from the starting time until the finishing time was determined. The dissolution referred here means that the shape of the fibers cannot be maintained and collapses, and it is determined by observing from various directions. A case where the time required until the finishing of dissolution was 10 seconds or more and less than 5 minutes was determined to be Rank A, a case of 5 minutes or more was determined to be Rank B, and a case of less than 10 seconds was determined to be Rank C. [0117] (4) Workability: (a) Stickiness Two sheets of Si rubbers (supplied by Kyowa Industrial Co., Ltd., hardness: 20 degrees, 3 cm x 1 cm) were prepared, and purified water was sprayed onto the surfaces of the two sheets of Si rubbers so as to uniformly adhere thereto at an amount of 5 mg per each sheet under an environment of a temperature of 23 ± 5°C and a relative humidity of 65 ± 20%. [0118] Thereafter, a test piece of 5 cm x 5 cm was nipped by two sheets of wet Si rubbers for 1 second at a force of 5N, and was held in the air so that the longer sides of the Si rubbers were perpendicular to the ground, and when one Si rubber was fixed and the other Si rubber was exfoliated in the horizontal direction relative to the ground at a speed of 1.5 m/min., it was checked whether the test piece fell without being stuck to the Si rubber or not. A case where it separated from the Si rubber and fell was determined to be Rank A, a case where it stuck to the Si rubber and did not fall and a breakage did not occur in the test piece was determined to be Rank B, and a case where it stuck to the Si rubber and did not fall and a breakage occurred in the test piece was determined to be Rank C. [0119] (b) Trocar passing property: A test piece of 9 cm x 12 cm and a trocar used in a general laparoscopic surgery were used, and flexibility was evaluated at the following condition. Further, as the trocar and a sending-out rod, the following (i) and (ii) were used. In the sending out, the test piece was placed so that the polylactic acid resin-containing layer (C) side thereof was brought into contact with the hole part of the trocar, it was pressed into the trocar, it was evaluated whether the test piece could pass through the trocar, and further, after passing, whether the test piece could be extended to an original formation when extending it by hand. Further, supposing use during operation, a test wetting the inside of the trocar was also carried out. Where, with respect to a test piece which did not pass through the trocar, the extensibility could not be evaluated. [0120] (i) Trocar: supplied by Covidien Inc., "VERSAPORT" (registered trade mark) V2, 5 mm short (hole: cp5mm, cylinder length: 9 cm) Sending-out rod: acryl rod of