LITHOGRAPHIC PRINTING PLATE PRECURSOR AND PLATE MAKING METHOD THEREOF

FIELD OF THE INVENTION
The present invention relates to a lithographic printing plate precursor and a plate making method using the same. More particularly  it relates to a lithographic printing plate precursor capable of undergoing a direct plate making by image exposure with laser and a plate making method comprising exposing and developing the lithographic printing plate precursor.

BACKGROUND OF THE INVENTION
In general  a lithographic printing plate has a surface composed of an oleophilic image area and a hydrophilic non-image area. Lithographic printing is a printing method comprising supplying alternately dampening water and oily ink on the surface of lithographic printing plate  making the hydrophilic non-image area a dampening water-receptive area (ink unreceptive area) and depositing the oily ink only on the oleophilic image area by utilizing the nature of water and oil to repel with each other  and then transferring the ink to a printing material  for example  paper.
In order to produce the lithographic printing plate  a lithographic printing plate precursor (PS plate) comprising a hydrophilic support having provided thereon an oleophilic image-forming layer (image-recording layer) has heretofore been broadly used. Ordinarily  a lithographic printing plate is obtained by conducting plate making by a method of exposing the lithographic printing plate precursor through an original  for example  a lith film  and then treating the exposed lithographic printing plate precursor to remove the image-recording layer in the unnecessary non-image area by dissolving with a an alkaline developer or an organic solvent thereby revealing a surface of the hydrophilic support to form the non-image area while leaving the image-recording layer in the image area.
In the hitherto known plate making process of lithographic printing plate precursor  after the exposure  the step of removing the unnecessary image-recording layer by dissolving  for example  with a developer is required. However  it is one of the subjects to simplify such an additional wet treatment as described above. As one means for the simplification  it has been desired to conduct the development with a nearly neutral aqueous solution or simply with water.
On the other hand  digitalized technique of electronically processing  accumulating and outputting image information using a computer has been popularized in recent years  and various new image outputting systems responding to the digitalized technique have been put into practical use.
Correspondingly  attention has been drawn to a computer-to-plate technique of carrying the digitalized image information on highly converging radiation  for example  laser light and conducting scanning exposure of a lithographic printing plate precursor with the light thereby directly preparing a lithographic printing plate without using a lith film. Thus  it is one of the important technical subjects to obtain a lithographic printing plate precursor adaptable to the technique described above.
Based on the background described above  adaptation of plate making operation to both simplification and digitalization has been demanded strongly more and more than ever before.
However  since the development processing ordinarily comprises three steps of developing with an aqueous alkali solution having pH of 10 or more  washing of the alkali agent with a water-washing bath and then treating with a gum solution mainly comprising a hydrophilic resin as described above  an automatic developing machine per se requires a large space and problems of the environment and running cost  for example  disposal of the development waste liquid  water-washing waste liquid and gum waste liquid still remain. Therefore  the decrease in alkali concentration of developer and the simplification of processing step have been further strongly required from both aspects of the consideration for global environment and the adaptation for space saving and low running cost.
For instance  a developing method with an alkali solution having pH from 10 to 12.5 and containing a nonionic surfactant is proposed in JP-A-2002-91016 (the term “JP-A” as used herein means an “unexamined published Japanese patent application”). However  since the photosensitive composition contains an alkali-soluble polymer  there is a problem in that the development can not be conducted with a developer having pH lower than the value defined.
A method of preparing a lithographic printing plate comprising exposing with laser of 350 to 450 nm a lithographic printing plate precursor having an image-forming layer containing (A) a sensitizing dye having an absorption maximum at a wavelength range from 350 to 450 nm  (B) a hexaarylbiimidazole compound  (C) a polymerizable compound  (D) a hydrophobic binder polymer and (E) a chain transfer agent and a protective layer in this order and then removing the protective layer and the unexposed area of the image-forming layer by rubbing the surface of the lithographic printing plate precursor with a rubbing member in an automatic processor equipped with the rubbing member in the presence of a developer having pH from 2 to 10 is described in JP-A-2007-58170.
A plate making method of a lithographic printing plate comprising exposing imagewise a lithographic printing plate precursor having a photopolymerizable layer on support having a hydrophilic surface or having a hydrophilic layer provided thereon by a plate setter and then treating with a gum solution an image-forming layer of the lithographic printing plate precursor in a gumming unit of an automatic developing machine to remove the unexposed area of the image-forming layer is described in WO 2005/111727.
A lithographic printing plate precursor using a star polymer is described in JP-A-2004-317543. There is described that development property and printing durability are improved by using the star polymer.
In order to improve on-press development property of a lithographic printing plate precursor capable of undergoing on-press development and printing durability  use of a star polymer in an image-recording layer is described in JP-A-2007-249036. Although the lithographic printing plate precursor exhibits high on-press development property and printing durability  there is no description with respect to a lithographic printing plate precursor of an alkali development type.
A lithographic printing plate precursor containing a polymer having a repeating unit containing an ethylenically unsaturated bond and a repeating unit containing a functional group capable of interacting a surface of support is described in JP-A-2005-125749. However  the technique is insufficient in stain resistance and development property.

SUMMARY OF THE INVENTION
An object of the present invention is to provide a negative lithographic printing plate precursor which provides high printing durability and stain resistance and exhibits excellent development property and a plate making method of the negative lithographic printing plate precursor.
As a result of the intensive investigations for achieving the object described above  the inventors have found that a lithographic printing plate precursor excellent in all of printing durability  stain resistance and development property can be obtained by using a star polymer in an undercoat layer to complete the invention.
The present invention includes the following items.
(1) A negative lithographic printing plate precursor comprising a support and an image-recording layer  wherein a layer containing a star polymer is provided between the support and the image-recording layer.
(2) The negative lithographic printing plate precursor as described in (1) above  wherein the layer containing a star polymer is an undercoat layer.
(3) The negative lithographic printing plate precursor as described in (1) above  wherein the layer containing a star polymer is a layer formed by hydrophilizing treatment of a surface of the support.
(4) The negative lithographic printing plate precursor as described in any one of (1) to (3) above  wherein the image-recording layer is a layer containing a polymerization initiator and a polymerizable compound.
(5) The negative lithographic printing plate precursor as described in any one of (1) to (4) above  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton.
(6) The negative lithographic printing plate precursor as described in (5) above  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton via sulfide bonds respectively.
(7) The negative lithographic printing plate precursor as described in (6) above  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton via sulfide bonds respectively and which is obtained by polymerization of an ethylenically unsaturated monomer in the presence of a multifunctional thiol.
(8) The negative lithographic printing plate precursor as described in any one of (1) to (7) above  wherein the star polymer has a hydrophilic group in the polymer chain thereof.
(9) The negative lithographic printing plate precursor as described in any one of (1) to (8) above  wherein the star polymer has a group adsorbing to a surface of the support in the polymer chain thereof.
(10) The negative lithographic printing plate precursor as described in (8) or (9) above  wherein the star polymer has a crosslinkable group in the polymer chain thereof.
(11) The negative lithographic printing plate precursor as described in any one of (1) to (10) above  wherein a protective layer is provided on the image-recording layer.
(12) The negative lithographic printing plate precursor as described in any one of (1) to (11) above  which is capable of printing  after image exposure with laser  by supplying at least any of printing ink and dampening water on a printing machine to remove an unexposed area of the image-recording layer.
(13) The negative lithographic printing plate precursor as described in any one of (1) to (11) above  which is capable of removing  after image exposure with laser  an unexposed area of the image-recording layer with a developer having pH from 2 to 14.
(14) The negative lithographic printing plate precursor as described in (11) above  which is capable of removing  after image exposure with laser  the protective layer and an unexposed area of the image-recording layer with one bath of a developer having pH from 2 to 14.
(15) A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as described in (12) above with laser  and then supplying at least any of printing ink and dampening water to the exposed negative lithographic printing plate precursor on a printing machine to remove an unexposed area of the image-recording layer.
(16) A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as described in (13) above with laser  and then removing an unexposed area of the image-recording layer with a developer having pH from 2 to 14.
(17) A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as described in (14) above with laser  and then removing the protective layer and an unexposed area of the image-recording layer with one bath of a developer having pH from 2 to 14.
According to the invention  the object described above can be achieved by using a star polymer in an undercoat layer. The functional mechanism of the invention is not quite clear but it is estimated as follows. It is believed that due to the star shape of polymer  adsorption power to the support and adhesion power to the image-recording layer are increased to improve the printing durability. It is also believed that since the support can be covered by not a line but a plane  hydrophilicity is increased so that the stain resistance after development is improved. It is further believed that permeation of developer into the whole lithographic printing plate precursor is accelerated so that the development property is improved.
According to the present invention  a negative lithographic printing plate precursor which provides high printing durability and stain resistance and exhibits excellent development property and a plate making method of the negative lithographic printing plate precursor can be provided.

BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 is a view schematically showing a star polymer according to the invention.
Fig. 2 is a view explaining a structure of an automatic development processor (A).
Fig. 3 is a view explaining a structure of an automatic development processor (B).
[Description of reference numerals and signs]
61: Rotating brush roller
62: Backing roller
63: Transport roller
64: Transport guide plate
65: Spray pipe
66: Pipe line
67: Filter
68: Plate supply table
69: Plate discharge table
70: Developer tank
71: Circulating pump
72: Lithographic printing plate precursor
11: Transporting path
100: Automatic development processor
200: Pre-heating unit
300: Developing unit
400: Drying unit
202: Machine casing
204: Heating unit
208: Heating chamber
210: Skewer roller
212: Transporting inlet
214: Heater
216: Circulation fan
218: Transporting outlet
302: Insertion unit
304: Insertion roller pair
306: Processing tank
306a: Processing tank margin
308: Developing tank (filled with a developer)
310: Outer panel
312: Slit type insertion slot
316: Submerged roller pair
318: Carrying-out roller pair
322: Brush roller pair
324: Shielding cover
326: Brush roller pair
330: Spray pipe
(*which is constructed to supply a developer in the developing tank 308 sucked by a pump (not shown) and the developer is ejected from the spray pipe 330 in the developing tank 308)
334: Slit type path-through slot
336: Liquid temperature sensor
338: Liquid level meter
332: Partition board
342: Guide member
344: Guide roller
402: Support roller
404: Discharge slot
406: Transport roller pair
408: Transport roller pair
410  412: Duct
414: Slit hole
50: External tank (developer storage)
51: Overflow aperture
52: Upper limit liquid level meter
53: Lower limit liquid level meter
54: Filter unit
55: Developer supply pump
C1: First circulation pipeline
C2: Second circulation pipeline
71: Water tank for replenishment (water storage)
72: Water-replenishing pump
C3: Circulation pipeline for water replenishment

DETAILED DESCRIPTION OF THE INVENTION
(A) Star polymer
The star polymer for use in the invention is a polymer having a main chain structure as shown in the schematic view of Fig. 1. It has a structure in which one terminal of polymer chain P1 is connected to central skeleton A and is different from a graft polymer in which one terminal of a polymer chain is connected to a polymer chain.
The star polymer for use in the invention may be any star polymer as far as it has the structure described above. The star polymer includes a star polymer obtained by a coupling method or an anion growing method described in Shin Jikken Kagaku Koza  Kobunshi Kagaku I (New Experimental Chemistry Course  Polymer Chemistry I)  pages 208 to 210  edited by The Chemical Society of Japan  a star polymer obtained by a synthesis method wherein a polymerization is conducted under light irradiation using a compound having a dithiocarbamate group and/or a compound having xanthate group as an initiator described in JP-A-10-279867  and a star polymer obtained by a conventional radical polymerization using a multifunctional thiol as a chain transfer agent.
The star polymer according to the invention is a polymer in which polymer chains are branched from a central skeleton via sulfide bonds and which is obtained by polymerization of an ethylenically unsaturated monomer in the presence of a multifunctional thiol from the standpoint of ease in synthesis and performances of the polymer obtained. Specifically  a polymer having a hub portion which is a residue of a three or higher functional thiol as a central structure is preferred. In the idealized structure  a main chain of an addition polymer extends from each thio part of the hub portion and thus  three or more main chains extend from the thio parts. Specifically  the central skeleton A has preferably a structure represented by formula (1) shown below.
Formula (1):

In formula (1)  A1 represents a trivalent or higher valent organic group  and n represents an integer of 3 or more. Specific examples of A1 include trivalent or higher valent organic groups having structures shown below and trivalent or higher valent organic groups composed of combination of two or more of structures shown below. n is preferably an integer from 3 to 10  more preferably an integer from 3 to 8  and particularly preferably an integer from 3 to 6.

[Central skeleton of polymer from which polymer chains are branched via sulfide bonds]
As the multifunctional thiol for use in the preparation of the star polymer according to the invention  any compound having three or more thiol groups in its molecule is suitably used. A multifunctional thiol having from 3 to 10 functional groups is preferred  a multifunctional thiol having from 3 to 8 functional groups is preferred  and multifunctional thiol having from 3 to 6 functional groups is particularly preferred. The multifunctional thiol includes Compound A to Compound F described below.
(Compound A)
Compound A is a compound obtained by a method of reacting a sulfuration agent  for example  thiourea  potassium thiocyanate or thioacetic acid with an electrophilic agent  for example  a halide or a sulfonic acid ester of an alcohol  followed by various treatments. Specific examples of Compound A include compounds set forth below  but the invention should not be construed as being limited thereto.

(Compound B)
Compound B is a compound obtained by a dehydration condensation reaction between a multifunctional alcohol and a carboxylic acid having a thiol group. Among them  a compound obtained by a dehydration condensation reaction between a multifunctional alcohol having from 3 to 10 functional groups and a mono-carboxylic acid having one thiol group is preferred.
Specific examples of the multifunctional alcohol include cyclohexanetriol (3)  glycerol (3)  2-hydroxymethyl-1 3-propanediol (3)  1 1 1-tris(hydroxymethyl)ethane (3)  1 2 4-butanetriol (3)  trimethylolpropane (3)  1 2 3-trihydroxyhexane (3)  1 2 6-trihydroxyhexane (3)  1 2 3-heptanetriol (3)  pyrogallol (3)  1 2 4-benzenetriol (3)  phloroglucinol (3)  1 1 1-tris(4-hydroxyphenyl)ethane (3)  1 3 5-tris(2-hydroxyethyl)isocyanurate (3)  pentaerythritol (4)  threitol (4)  erythritol (4)  xylulose (4)  ribulose (4)  quebrachitol (5)  adonitol (5)  arabitol (5)  xylitol (5)  catechin (5)  epicatechine (5)  inositol (6)  sorbitol (6)  mannitol (6)  iditol (6)  dulcitol (6)  dipentaerythritol (6) and tripentaerythritol (8). The number shown in parentheses above denotes a number of the functional groups.
Of the multifunctional alcohols  cyclohexanetriol (3)  glycerol (3)  2-hydroxymethyl-1 3-propanediol (3)  1 1 1-tris(hydroxymethyl)ethane (3)  trimethylolpropane (3)  phloroglucinol (3)  1 1 1-tris(4-hydroxyphenyl)ethane (3)  1 3 5-tris(2-hydroxyethyl)isocyanurate (3)  pentaerythritol (4)  catechin (5)  epicatechin (5)  inositol (6)  dipentaerythritol (6) and tripentaerythritol (8) are preferred  cyclohexanetriol (3)  2-hydroxymethyl-1 3-propanediol (3)  1 1 1-tris(hydroxymethyl)ethane (3)  trimethylolpropane (3)  phloroglucinol (3)  1 1 1-tris(4-hydroxyphenyl)ethane (3)  1 3 5-tris(2-hydroxyethyl)isocyanurate (3)  pentaerythritol (4)  catechin (5)  epicatechin (5)  inositol (6)  dipentaerythritol (6) and tripentaerythritol (8) are more preferred  and 1 3 5-tris(2-hydroxyethyl)isocyanurate (3)  pentaerythritol (4)  catechin (5)  epicatechin (5)  inositol (6)  dipentaerythritol (6) and tripentaerythritol (8) are particularly preferred.
Specific examples of the mono-carboxylic acid having one thiol group include mercaptoacetic acid  3-mercaptopropionic acid  2-mercaptopropionic acid  3-mercaptoisobutyric acid  N-acetylcysteine  N-(2-mercaptopropionyl)glycine and thiosalicylic acid.
Of the compounds  mercaptoacetic acid  3-mercaptopropionic acid  2-mercaptopropionic acid  3-mercaptoisobutyric acid  N-acetylcysteine and N-(2-mercaptopropionyl)glycine are preferred  3-mercaptopropionic acid  2-mercaptopropionic acid  3-mercaptoisobutyric acid  N-acetylcysteine and N-(2-mercaptopropionyl)glycine are more preferred  and 3-mercaptopropionic acid  3-mercaptoisobutyric acid  N-acetylcysteine and N-(2-mercaptopropionyl)glycine are particularly preferred.
Specific examples of Compound B include compounds set forth below  but the invention should not be construed as being limited thereto.

TABLE 1
Multifunctional Alcohol Carboxylic Acid Having Thiol Group
Mercaptoacetic Acid 3-Mercaptopropionic Acid 2-Mercaptopropionic Acid 3-Mercaptoisobutyric Acid N-Acetylcysteine N-(2-Mercaptopropionyl)glycine Thiosalicylic Acid
Cyclohexanetriol (3) SB-1 SB-2 SB-3 SB-4 SB-5 SB-6 SB-7
Glycerol (3) SB-8 SB-9 SB-10 SB-11 SB-12 SB-13 SB-14
2-Hydroxymethyl-1 3-propanediol (3) SB-15 SB-16 SB-17 SB-18 SB-19 SB-20 SB-21
1 1 1-Tris(hydroxymethyl)ethane (3) SB-22 SB-23 SB-24 SB-25 SB-26 SB-27 SB-28
1 2 4-Butanetriol (3) SB-29 SB-30 SB-31 SB-32 SB-33 SB-34 SB-35
Trimethylolpropane (3) SB-36 SB-37 SB-38 SB-39 SB-40 SB-41 SB-42
1 2 3-Trihydroxyhexane (3) SB-43 SB-44 SB-45 SB-46 SB-47 SB-48 SB-49
1 2 6-Trihydroxyhexane (3) SB-50 SB-51 SB-52 SB-53 SB-54 SB-55 SB-56
1 2 3-Heptanetriol (3) SB-57 SB-58 SB-59 SB-60 SB-61 SB-62 SB-63
Pyrogallol (3) SB-64 SB-65 SB-66 SB-67 SB-68 SB-69 SB-70
1 2 4-Benzenetriol (3) SB-71 SB-72 SB-73 SB-74 SB-75 SB-76 SB-77
Phloroglucinol (3) SB-78 SB-79 SB-80 SB-81 SB-82 SB-83 SB-84
1 1 1-Tris(4-hydroxyphenyl)ethane (3) SB-85 SB-86 SB-87 SB-88 SB-89 SB-90 SB-91
1 3 5-Tris(2-hydroxyethyl)isocyanurate (3) SB-92 SB-93 SB-94 SB-95 SB-96 SB-97 SB-98
Pentaerythritol (4) SB-99 SB-100 SB-101 SB-102 SB-103 SB-104 SB-105
Threitol (4) SB-106 SB-107 SB-108 SB-109 SB-110 SB-111 SB-112
Erythritol (4) SB-113 SB-114 SB-115 SB-116 SB-117 SB-118 SB-119
Xylulose (4) SB-120 SB-121 SB-122 SB-123 SB-124 SB-125 SB-126
Quebrachitol (5) SB-127 SB-128 SB-129 SB-130 SB-131 SB-132 SB-133
Adonitol (5) SB-134 SB-135 SB-136 SB-137 SB-138 SB-139 SB-140
Arabitol (5) SB-141 SB-142 SB-143 SB-144 SB-145 SB-146 SB-147
Xylitol (5) SB-148 SB-149 SB-150 SB-151 SB-152 SB-153 SB-154
Catechin (5) SB-155 SB-156 SB-157 SB-158 SB-159 SB-160 SB-161
Epicatechine (5) SB-162 SB-163 SB-164 SB-165 SB-166 SB-167 SB-168
Inositol (6) SB-169 SB-170 SB-171 SB-172 SB-173 SB-174 SB-175
Sorbitol (6) SB-176 SB-177 SB-178 SB-179 SB-180 SB-181 SB-182
Mannitol (6) SB-183 SB-184 SB-185 SB-186 SB-187 SB-188 SB-189
Iditol (6) SB-190 SB-191 SB-192 SB-193 SB-194 SB-195 SB-196
Dulcitol (6) SB-197 SB-198 SB-199 SB-200 SB-201 SB-202 SB-203
Dipentaerythritol (6) SB-204 SB-205 SB-206 SB-207 SB-208 SB-209 SB-210
Tripentaerythritol (8) SB-211 SB-212 SB-213 SB-214 SB-215 SB-216 SB-217

Of the specific examples shown in Table 1  SB-1 to SB-34  SB-36 to SB-48  SB-50 to SB-55  SB-57 to SB-62  SB-64 to SB-69  SB-71 to SB-76  SB-78 to SB-111  SB-113 to SB-118  SB-120 to SB-125  SB-127 to SB-132  SB-134 to SB-139  SB-141 to SB-146  SB-148 to SB-153  SB-155 to SB-181  SB-183 to SB-188  SB-190 to SB-195  SB-197 to SB-202 and SB-204 to SB-217 are preferred  SB-1 to SB-6  SB-9 to SB-13  SB-15 to SB-20  SB-22 to SB-27  SB-36 to SB-41  SB-78 to SB-83  SB-85 to SB-90  SB-92 to SB-97  SB-99 to SB-104  SB-155 to SB-160  SB-162 to SB-167  SB-169 to SB-174  SB-204 to SB-209 and SB-211 to SB-216 are more preferred  and SB-2 to SB-6  SB-16 to SB-20  SB-23 to SB-27  SB-37 to SB-41  SB-79 to SB-83  SB-86 to SB-90  SB-93 to SB-97  SB-100 to SB-104  SB-156 to SB-160  SB-163 to SB-167  SB-170 to SB-174  SB-205 to SB-209 and SB-212 to SB-216 are particularly preferred.
Since the multifunctional thiols described above have a long distance between the thiol groups and a small steric hindrance  the desired star structure can be formed.
(Compound C)
Compound C is a compound obtained by a dehydration condensation reaction between a multifunctional amine and a carboxylic acid having a thiol group. Among them  a compound obtained by a condensation reaction between a multifunctional amine having from 3 to 10 functional groups and a mono-carboxylic acid having one thiol group is preferred.
Specific examples of the multifunctional amine include diethylenetriamine (3)  N-(2-aminoethyl)-1 3-propanediamine (3)  N-(3-aminopropyl)-1 3-propanediamine (3)  spermidine (3)  bis(hexamethylene)triamine (3)  4-(aminomethyl)-1 8-octanediamine (3)  triethylenetetramine (4)  1 4 7 11-tetraazaundecane (4)  N N’-bis(3-aminopropyl)ethylenediamine (4)  N N’-bis(2-aminoethyl)-1 3-propanediamine (4)  N N’-bis(3-aminopropyl)-1 3-propanediamine (4)  spermine (4)  tris(2-aminoethyl)amine (3)  tetraethylenepentamine (5)  pentaethylenehexamine (6)  1 4 7-triazacyclononane (3)  1 5 9-triazacyclododecane (3)  cyclene (4)  1 4 8 11-tetraazacyclotetradecane (4)  1 4 8 12-tetraazacyclopentadecane (4)  hexacyclene (6)  3 3’-diaminobenzidine (4) and 1 2 4 5-benzenetetramine (4).
Of the multifunctional amines  4-(aminomethyl)-1 8-octanediamine (3)  triethylenetetramine (4)  1 4 7 11-tetraazaundecane (4)  N N’-bis(3-aminopropyl)ethylenediamine (4)  N N’-bis(2-aminoethyl)-1 3-propanediamine (4)  N N’-bis(3-aminopropyl)-1 3-propanediamine (4)  spermine (4)  tris(2-aminoethyl)amine (3)  tetraethylenepentamine (5)  pentaethylenehexamine (6)  cyclene (4) and hexacyclene (6) are preferred  4-(aminomethyl)-1 8-octanediamine (3)  tris(2-aminoethyl)amine (3)  tetraethylenepentamine (5)  pentaethylenehexamine (6)  cyclene (4) and hexacyclene (6) are more preferred  and tetraethylenepentamine (5)  pentaethylenehexamine (6)  cyclene (4) and hexacyclene (6) are particularly preferred.
Specific examples of the carboxylic acid having a thiol group include the carboxylic acids described for Compound B above. Specific examples of Compound C include compounds set forth below  but the invention should not be construed as being limited thereto.
TABLE 2
Multifunctional Amine Carboxylic Acid Having Thiol Group
Mercaptoacetic Acid 3-Mercaptopropionic Acid 2-Mercaptopropionic Acid 3-Mercaptoisobutyric Acid N-Acetylcysteine N-(2-Mercaptopropionyl)glycine Thiosalicylic Acid
Diethylenetriamine (3) SC-1 SC-2 SC-3 SC-4 SC-5 SC-6 SC-7
N-(2-Aminoethyl)-1 3-propanediamine (3) SC-8 SC-9 SC-10 SC-11 SC-12 SC-13 SC-14
N-(3-Aminopropyl)-1 3-propanediamine (3) SC-15 SC-16 SC-17 SC-18 SC-19 SC-20 SC-21
Spermidine (3) SC-22 SC-23 SC-24 SC-25 SC-26 SC-27 SC-28
Bis(hexamethylene)triamine (3) SC-29 SC-30 SC-31 SC-32 SC-33 SC-34 SC-35
4-(Aminomethyl)-1 8-octanediamine (3) SC-36 SC-37 SC-38 SC-39 SC-40 SC-41 SC-42
Triethylenetetramine (4) SC-43 SC-44 SC-45 SC-46 SC-47 SC-48 SC-49
1 4 7 11-Tetraazaundecane (4) SC-50 SC-51 SC-52 SC-53 SC-54 SC-55 SC-56
N N’-Bis(3-aminopropyl)ethylenediamine (4) SC-57 SC-58 SC-59 SC-60 SC-61 SC-62 SC-63
N N’-Bis(2-aminoethyl)-1 3-propanediamine (4) SC-64 SC-65 SC-66 SC-67 SC-68 SC-69 SC-70
N N’-Bis(3-aminopropyl)-1 3-propanediamine (4) SC-71 SC-72 SC-73 SC-74 SC-75 SC-76 SC-77
Spermine (4) SC-78 SC-79 SC-80 SC-81 SC-82 SC-83 SC-84
Tris(2-aminoethyl)amine (3) SC-85 SC-86 SC-87 SC-88 SC-89 SC-90 SC-91
Tetraethylenepentamine (5) SC-92 SC-93 SC-94 SC-95 SC-96 SC-97 SC-98
Pentaethylenehexamine (6) SC-99 SC-100 SC-101 SC-102 SC-103 SC-104 SC-105
1 4 7-Triazacyclononane (3) SC-106 SC-107 SC-108 SC-109 SC-110 SC-111 SC-112
1 5 9-Triazacyclododecane (3) SC-113 SC-114 SC-115 SC-116 SC-117 SC-118 SC-119
Cyclene (4) SC-120 SC-121 SC-122 SC-123 SC-124 SC-125 SC-126
1 4 8 11-Tetraazacyclotetradecane (4) SC-127 SC-128 SC-129 SC-130 SC-131 SC-132 SC-133
1 4 8 12-Tetraazacyclopentadecane (4) SC-134 SC-135 SC-136 SC-137 SC-138 SC-139 SC-140
Hexacyclene (6) SC-141 SC-142 SC-143 SC-144 SC-145 SC-146 SC-147

Of the compounds shown in Table 2  SC-1 to SC-6  SC-8 to SC-13  SC-15 to SC-20  SC-22 to SC-27  SC-29 to SC-34  SC-36 to SC-111  SC-113 to SC-118  SC-120 to SC-132  SC-134 to SC-139 and SC-141 to SC-147 are preferred  SC-37 to SC-41  SC-44 to SC-48  SC-51 to SC-55  SC-58 to SC-62  SC-65 to SC-69  SC-72 to SC-76  SC-79 to SC-83  SC-86 to SC-90  SC-93 to SC-97  SC-100 to SC-104  SC-121 to SC-125 and SC-142 to SC-146 are more preferred  and SC-37 to SC-41  SC-86 to SC-90  SC-93 to SC-97  SC-100 to SC-104  SC-121 to SC-125 and SC-142 to SC-146 are particularly preferred.
Since the multifunctional thiols described above have a long distance between the thiol groups and a small steric hindrance  the desired star structure can be formed.
(Compound D)
Compound D is a compound obtained by a dehydration condensation reaction between a compound having a hydroxy group and an amino group and a carboxylic acid having a thiol group  and preferably a compound obtained by a dehydration condensation reaction between a multifunctional alcoholamine having from 3 to 10 functional groups of hydroxy group and amino group and a mono-carboxylic acid having one thiol group is preferred.
Specific examples of the multifunctional alcoholamine include diethanolamine (3)  serinol (3)  diisopropanolamine (3)  2-amino-2-ethyl-1 3-propanediol (3)  2-amino-2-methyl-1 3-propanediol (3)  tris(hydroxymethyl)aminomethane (4)  bishomotris (4)  1 3-diamino-2-hydroxypropane (3)  2-(2-aminoethylamino)ethanol (3)  N N’-bis(2-hydroxyethyl)ethylenediamine (4)  1 3-bis[tris(hydroxymethyl)methylamino]propane (8)  1-amino-1-deoxy-D-sorbitol (6)  N-methyl-D-glucamine (6)  2 3-diaminophenol (3)  4-aminoresorcinol (3)  norphenylephrine (3)  octopamine (3)  synephrine (3)  3 4-dihydroxybenzylamine (3)  3-hydroxytyramine (3)  norepinephrine (4)  5-hydroxydopamine (4) and 6-hydroxydopamine (4).
Of the multifunctional alcoholamines  serinol (3)  2-amino-2-methyl-1 3-propanediol (3)  tris(hydroxymethyl)aminomethane (4)  bishomotris (4)  1 3-diamino-2-hydroxypropane (3)  N N’-bis(2-hydroxyethyl)ethylenediamine (4)  1 3-bis[tris(hydroxymethyl)methylamino]propane (8)  1-amino-1-deoxy-D-sorbitol (6)  N-methyl-D-glucamine (6)  norepinephrine (4)  5-hydroxydopamine (4) and 6-hydroxydopamine (4) are preferred  and tris(hydroxymethyl)aminomethane (4)  bishomotris (4)  N N’-bis(2-hydroxyethyl)ethylenediamine (4)  1 3-bis[tris(hydroxymethyl)methylamino]propane (8)  1-amino-1-deoxy-D-sorbitol (6)  N-methyl-D-glucamine (6)  norepinephrine (4)  5-hydroxydopamine (4) and 6-hydroxydopamine (4) are particularly preferred.
Specific examples of the carboxylic acid having a thiol group include the carboxylic acids described for Compound B above. Specific examples of Compound D include compounds set forth below  but the invention should not be construed as being limited thereto.

TABLE 3
Multifunctional Alcoholamine Carboxylic Acid Having Thiol Group
Mercaptoacetic Acid 3-Mercaptopropionic Acid 2-Mercaptopropionic Acid 3-Mercaptoisobutyric Acid N-Acetylcysteine N-(2-Mercaptopropionyl)glycine Thiosalicylic Acid
Diethanolamine (3) SD-1 SD-2 SD-3 SD-4 SD-5 SD-6 SD-7
Serinol (3) SD-8 SD-9 SD-10 SD-11 SD-12 SD-13 SD-14
Diisopropanolamine (3) SD-15 SD-16 SD-17 SD-18 SD-19 SD-20 SD-21
2-Amino-2-ethyl-1 3-propanediol (3) SD-22 SD-23 SD-24 SD-25 SD-26 SD-27 SD-28
2-Amino-2-methyl-1 3-propanediol (3) SD-29 SD-30 SD-31 SD-32 SD-33 SD-34 SD-35
Tris(hydroxymethyl)aminomethane (4) SD-36 SD-37 SD-38 SD-39 SD-40 SD-41 SD-42
Bishomotris (4) SD-43 SD-44 SD-45 SD-46 SD-47 SD-48 SD-49
1 3-Diamino-2-hydroxypropane (3) SD-50 SD-51 SD-52 SD-53 SD-54 SD-55 SD-56
2-(2-Aminoethylamino)ethanol (3) SD-57 SD-58 SD-59 SD-60 SD-61 SD-62 SD-63
N N’-Bis(2-hydroxyethyl)ethylenediamine (4) SD-64 SD-65 SD-66 SD-67 Sd-68 SD-69 SD-70
1 3-Bis[tris(hydroxymethyl)methylamino]propane (8) SD-71 SD-72 SD-73 SD-74 SD-75 SD-76 SD-77
1-Amino-1-deoxy-D-sorbitol (6) SD-78 SD-79 SD-80 SD-81 SD-82 SD-83 SD-84
N-Methyl-D-glucamine (6) SD-85 SD-86 SD-87 SD-88 SD-89 SD-90 SD-91
2 3-Diaminophenol (3) SD-92 SD-93 SD-94 SD-95 SD-96 SD-97 SD-98
4-Aminoresorcinol (3) SD-99 SD-100 SD-101 SD-102 SD-103 SD-104 SD-105
Norphenylephrine (3) SD-106 SD-107 SD-108 SD-109 SD-110 SD-111 SD-112
Octopamine (3) SD-113 SD-114 SD-115 SD-116 SD-117 SD-118 SD-119
Synephrine (3) SD-120 SD-121 SD-122 SD-123 SD-124 SD-125 SD-126
3 4-Dihydroxybenzylamine (3) SD-127 SD-128 SD-129 SD-130 SD-131 SD-132 SD-133
3-Hydroxytyramine (3) SD-134 SD-135 SD-136 SD-137 SD-138 SD-139 SD-140
Norepinephrine (4) SD-141 SD-142 SD-143 SD-144 SD-145 SD-146 SD-147
5-Hydroxydopamine (4) SD-148 SD-149 SD-150 SD-151 SD-152 SD-153 SD-154
6-Hydroxydopamine (4) SD-155 SD-156 SD-157 SD-158 SD-159 SD-160 SD-161

Of the compounds shown in Table 3  SD-1 to SD-6  SD-8 to SD-20  SD-22 to SD-27  SD-29 to SD-62  SD-64 to SD-97  SD-99 to SD-104  SD-106 to SD-111  SD-113 to SD-118  SD-120 to SD-125  SD-127 to SCD-132  SD-134 to SD-139 and SD-141 to SD-161 are preferred  SD-9 to SD-13  SD-30 to SD-34  SD-37 to SD-41  SD-44 to SD-48  SD-51 to SD-55  SD-65 to SD-69  SD-72 to SD-76  SD-79 to SD-83  SD-86 to SD-90  SD-142 to SD-146  SD-149 to SD-153 and SD-156 to SD-160 are more preferred  and SD-37 to SD-41  SD-44 to SD-48  SD-65 to SD-69  SD-72 to SD-76  SD-79 to SD-83  SD-86 to SD-90  SD-142 to SD-146  SD-149 to SD-153 and SD-156 to SD-160 are particularly preferred.
Since the multifunctional thiols described above have a long distance between the thiol groups and a small steric hindrance  the desired star structure can be formed.
(Compound E)
Compound E is a compound obtained by a dehydration condensation reaction between a multifunctional carboxylic acid and an alcohol having a thiol group. Among them  a compound obtained by a dehydration condensation reaction between a multifunctional carboxylic acid having from 2 to 10 functional groups and an alcohol having one or more thiol groups is preferred.
Specific examples of the multifunctional carboxylic acid include oxalic acid (2)  malonic acid (2)  methylmalonic acid (2)  succinic acid (2)  methylsuccinic acid (2)  glutaric acid (2)  adipic acid (2)  pimelic acid (2)  suberic acid (2)  azelaic acid (2)  sebacic acid (2)  tricarballylic acid (3)  1 2 3 4-butanetetracarboxylic acid (4)  aconitic acid (3)  hexafluoroglutaric acid (2)  malic acid (2)  tartaric acid (2)  citric acid (3)  diglycolic acid (2)  3 6-dioxaoctanedicarboxylic acid (2)  tetrahydrofuran-2 3 4 5-tetracarboxylic acid (4)  mercaptosuccinic acid (2)  thioglycolic acid (2)  2 2’ 2’’ 2’’’-[1 2-ethanediylidenetetrakis(thio)]tetrakisacetic acid (4)  1 3 5-cyclohexanetricarboxylic acid (3)  1 2 3 4-cyclobutanetetracarboxylic acid (4)  1 2 3 4 5 6-cyclohexanehexacarboxylic acid (6)  1 2-phenylenediacetic acid (2)  1 2-phenylenedioxydiacetic acid (2)  homophthalic acid (2)  1 3-phenylenediacetic acid (2)  4-carboxyphenoxyacetic acid (2)  1 4-phenylenediacetic acid (2)  1 4-phenylenedipropionic acid (2)  phthalic acid (2)  isophthalic acid (2)  terephthalic acid (2)  1 2 3-benzenetricarboxylic acid (3)  1 2 4-benzenetricarboxylic acid (3)  1 3 5-benzenetricarboxylic acid (3)  1 2 4 5-benzenetetracarboxylic acid (4)  mellitic acid (6) and 1 4 5 8-naphthalenetetracarboxylic acid (4).
Of the multifunctional carboxylic acids  tricarballylic acid (3)  1 2 3 4-butanetetracarboxylic acid (4)  aconitic acid (3)  citric acid (3)  tetrahydrofuran-2 3 4 5-tetracarboxylic acid (4)  mercaptosuccinic acid (2)  2 2’ 2’’ 2’’’-[1 2-ethanediylidenetetrakis(thio)]tetrakisacetic acid (4)  1 3 5-cyclohexanetricarboxylic acid (3)  1 2 3 4-cyclobutanetetracarboxylic acid (4)  1 2 3 4 5 6-cyclohexanehexacarboxylic acid (6)  1 2-phenylenediacetic acid (2)  1 2-phenylenedioxydiacetic acid (2)  1 3-phenylenediacetic acid (2)  1 4-phenylenediacetic acid (2)  1 4-phenylenedipropionic acid (2)  phthalic acid (2)  isophthalic acid (2)  terephthalic acid (2)  1 3 5-benzenetricarboxylic acid (3)  1 2 4 5-benzenetetracarboxylic acid (4)  mellitic acid (6) and 1 4 5 8-naphthalenetetracarboxylic acid (4) are preferred  and tricarballylic acid (3)  1 2 3 4-butanetetracarboxylic acid (4)  tetrahydrofuran-2 3 4 5-tetracarboxylic acid (4)  mercaptosuccinic acid (2)  2 2’ 2’’ 2’’’-[1 2-ethanediylidenetetrakis(thio)]tetrakisacetic acid (4)  1 3 5-cyclohexanetricarboxylic acid (3)  1 2 3 4-cyclobutanetetracarboxylic acid (4)  1 2 3 4 5 6-cyclohexanehexacarboxylic acid (6)  1 3 5-benzenetricarboxylic acid (3)  1 2 4 5-benzenetetracarboxylic acid (4)  mellitic acid (6) and 1 4 5 8-naphthalenetetracarboxylic acid (4) are particularly preferred.
Specific examples of the alcohol having a thiol group include 2-mercaptoethanol (1)  1-mercapto-2-propanol (1)  3-mercapto-1-propanol (1)  3-mercapto-2-butanol (1)  2 3-dimercapto-1-propanol (2) and 4-hydroxythiophenol (1). Of the alcohols having a thiol group  2-mercaptoethanol (1)  3-mercapto-1-propanol (1) and 2 3-dimercapto-1-propanol (2) are preferred  2-mercaptoethanol (1) and 3-mercapto-1-propanol (1) are more preferred  and 3-mercapto-1-propanol (1) is particularly preferred.
Specific examples of Compound E include compounds shown in Tables 4 and 5 below  but the invention should not be construed as being limited thereto.

TABLE 4
Multifunctional Carboxylic Acid Alcohol Having Thiol Group
2-Mercaptoethanol 1-Mercapto-2-propanol 3-Mercapto-1-propanol 3-Mercapto-2-butanol 2 3-Dimercapto-1-propanol 4-Hydroxythiophenol
Oxalic acid (2) - - - - SE-1 -
Malonic acid (2) - - - - SE-2 -
Methylmalonic acid (2) - - - - SE-3 -
Succinic acid (2) - - - - SE-4 -
Methylsuccinic acid (2) - - - - SE-5 -
Glutaric acid (2) - - - - SE-6 -
Adipic acid (2) - - - - SE-7 -
Pimelic acid (2) - - - - SE-8 -
Suberic acid (2) - - - - SE-9 -
Azelaic acid (2) - - - - SE-10 -
Sebacic acid (2) - - - - SE-11 -
Tricarballylic acid (3) SE-12 SE-13 SE-14 SE-15 SE-16 SE-17
1 2 3 4-Butanetetracarboxylic acid (4) SE-18 SE-19 SE-20 SE-21 SE-22 SE-23
Aconitic acid (3) SE-24 SE-25 SE-26 SE-27 SE-28 SE-29
Hexafluoroglutaric acid (2) - - - - SE-30 -
Malic acid (2) - - - - SE-31 -
Tartaric acid (2) - - - - SE-32 -
Citric acid (3) SE-33 SE-34 SE-35 SE-36 SE-37 SE-38
Diglycolic acid (2) - - - - SE-39 -
3 6-Dioxaoctanedicarboxylic acid (2) - - - - SE-40 -
Tetrahydrofuran-2 3 4 5-tetracarboxylic acid (4) SE-41 SE-42 SE-43 SE-44 SE-45 SE-46
Mercaptosuccinic acid (2) SE-119 SE-120 SE-121 SE-122 SE-47 SE-123
Thioglycolic acid (2) - - - - SE-48 -
2 2’ 2’’ 2’’’-[1 2-Ethanediylidenetetrakis(thio)]tetrakisacetic acid (4) SE-49 SE-50 SE-51 SE-52 SE-53 SE-54

TABLE 5
Multifunctional Carboxylic Acid Alcohol Having Thiol Group
2-Mercaptoethanol 1-Mercapto-2-propanol 3-Mercapto-1-propanol 3-Mercapto-2-butanol 2 3-Dimercapto-1-propanol 4-Hydroxythiophenol
1 3 5-Cyclohexanetricarboxylic acid (3) SE-55 SE-56 SE-57 SE-58 SE-59 SE-60
1 2 3 4-Cyclobutanetetracarboxylic acid (4) SE-61 SE-62 SE-63 SE-64 SE-65 SE-66
1 2 3 4 5 6-Cyclohexanehexacarboxylic acid (6) SE-67 SE-68 SE-69 SE-70 SE-71 SE-72
1 2-Phenylenediacetic acid (2) - - - - SE-73 -
1 2-Phenylenedioxydiacetic acid (2) - - - - SE-74 -
Homophthalic acid (2) - - - - SE-75 -
1 3-Phenylenediacetic acid (2) - - - - SE-76 -
4-Carboxyphenoxyacetic acid (2) - - - - SE-77 -
1 4-Phenylenediacetic acid (2) - - - - SE-78 -
1 4-Phenylenedipropionic acid (2) - - - - SE-79 -
Phthalic acid (2) - - - - SE-80 -
Isophthalic acid (2) - - - - SE-81 -
Terephthalic acid (2) - - - - SE-82 -
1 2 3-Benzenetricarboxylic acid (3) SE-83 SE-84 SE-85 SE-86 SE-87 SE-88
1 2 4-Benzenetricarboxylic acid (3) SE-89 SE-90 SE-91 SE-92 SE-93 SE-94
1 3 5-Benzenetricarboxylic acid (3) SE-95 SE-96 SE-97 SE-98 SE-99 SE-100
1 2 4 5-benzenetetracarboxylic acid (4) SE-101 SE-102 SE-103 SE-104 SE-105 SE-106
Mellitic acid (6) SE-107 SE-108 SE-109 SE-110 SE-111 SE-112
1 4 5 8-Naphthalenetetracarboxylic acid (4) SE-113 SE-114 SE-115 SE-116 SE-117 SE-118

Of the compounds shown in Tables 4 and 5  SE-12  SE-14  SE-16  SE-18  SE-20  SE-22  SE-24  SE-26  SE-33  SE-35  SE-41  SE-43  SE-45  SE-119  SE-121  SE-47  SE-49  SE-51  SE-53  SE-55  SE-57  SE-59  SE-61  SE-63  SE-65  SE-67  SE-69  SE-71  SE-83  SE-85  SE-89  SE-91  SE-95  SE-97  SE-99  SE-101  SE-103  SE-105  SE-107  SE-109  SE-111  SE-113  SE-115 and SE-117 are preferred  and SE-12  SE-14  SE-18  SE-20  SE-41  SE-43  SE-119  SE-121  SE-49  SE-51  SE-55  SE-57  SE-61  SE-63  SE-67  SE-69  SE-95  SE-97  SE-101  SE-103  SE-107  SE-109  SE-113 and SE-115 are more preferred.
Since the multifunctional thiols described above have a long distance between the thiol groups and a small steric hindrance  the desired star structure can be formed.
(Compound F)
Compound F is a compound obtained by a dehydration condensation reaction between a multifunctional carboxylic acid and an amine having a thiol group. Among them  a compound obtained by a dehydration condensation reaction between a multifunctional carboxylic acid having from 2 to 10 functional groups and an amine having one or more thiol groups is preferred.
Specific examples of the multifunctional carboxylic acid include the multifunctional carboxylic acids described above. Specific examples of the amine having one or more thiol groups include 2-aminoethanethiol  2-aminothiophenol  3-aminothiophenol and 4-aminothiophenol  and 2-aminoethanethiol and 4-aminothiophenol are preferred  and 2-aminoethanethiol is more preferred.
Specific examples of Compound F include compounds set forth below  but the invention should not be construed as being limited thereto.

TABLE 6
Multifunctional Carboxylic Acid Amine Having Thiol Group
2-Aminoetyhanetiol 2-Aminothiophenol 3-Aminothiophenol 4-Aminothiophenol
Tricarballylic acid (3) SF-1 SF-2 SF-3 SF-4
1 2 3 4-Butanetetracarboxylic acid (4) SF-5 SF-6 SF-7 SF-8
Aconitic acid (3) SF-9 SF-10 SF-11 SF-12
Citric acid (3) SF-13 SF-14 SF-15 SF-16
Tetrahydrofuran-2 3 4 5-tetracarboxylic acid (4) SF-17 SF-18 SF-19 SF-20
Mercaptosuccinic acid (2) SF-21 SF-22 SF-23 SF-24
2 2’ 2’’ 2’’’-[1 2-Ethanediylidenetetrakis(thio)]tetrakisacetic acid (4) SF-25 SF-26 SF-27 SF-28
1 3 5-Cyclohexanetricarboxylic acid (3) SF-29 SF-30 SF-31 SF-32
1 2 3 4-Cyclobutanetetracarboxylic acid (4) SF-33 SF-34 SF-35 SF-36
1 2 3 4 5 6-Cyclohexanehexacarboxylic acid (6) SF-37 SF-38 SF-39 SF-40
1 2 3-Benzenetricarboxylic acid (3) SF-41 SF-42 SF-43 SF-44
1 2 4-Benzenetricarboxylic acid (3) SF-45 SF-46 SF-47 SF-48
1 3 5-Benzenetricarboxylic acid (3) SF-49 SF-50 SF-51 SF-52
1 2 4 5-benzenetetracarboxylic acid (4) SF-53 SF-54 SF-55 SF-56
Mellitic acid (6) SF-57 SF-58 SF-59 SF-60
1 4 5 8-Naphthalenetetracarboxylic acid (4) SF-61 SF-62 SF-53 SF-64

Of the compounds shown in Table 6  SF-1  SF-4  SF-5  SF-8  SF-9  SF-13  SF-17  SF-20  SF-21  SF-24  SF-25  SF-28  SF-29  SF-32  SF-33  SF-36  SF-37  SF-40  SF-41  SF-45  SF-49  SF-52  SF-53  SF-56  SF-57  SF-60  SF-61 and SF-64 are preferred  and SF-1  SF-5  SF-17  SF-21  SF-25  SF-29  SF-33  SF-37  SF-49  SF-53  SF-57 and SF-61 are more preferred.
Since the multifunctional thiols described above have a long distance between the thiol groups and a small steric hindrance  the desired star structure can be formed.
Of the multifunctional thiols described above  Compounds A to E are preferred  Compounds A  B  C and E are more preferred  and Compounds A  B and C are particularly preferred  from the standpoint of the printing durability and development property.
[Polymer chain]
The polymer chain of the star polymer according to the invention includes a polymer chain of a known vinyl-based polymer  (meth)acrylic acid-based polymer or styrene-based polymer  which can be produced by radical polymerization  and a polymer chain of a(meth)acrylic acid-based polymer is particularly preferred.
[Hydrophilic group]
The polymer chain of the star polymer according to the invention may contain a repeating unit having a hydrophilic group as a copolymerization component in order to increase hydrophilicity of the surface of support and improve the development property. Specific examples of the hydrophilic group are set forth below.

In the formulae above  M1 represents a hydrogen atom  a metal atom or an ammonium group. X+ denotes a group represented by –N+R1R2-  -S+R1-  -I+- or –P+R1R2-. R1 and R2 each independently represents a hydrogen atom or a straight-chain or branched alkyl group having from 1 to 6 carbon atoms  or R1 and R2 may be combined with each other to forma ring. R3 represents a straight-chain or branched alkylene group having from 1 to 6 carbon atoms and is preferably an ethylene group. R4 represents a hydrogen atom or an alkyl group having from 1 to 12 carbon atoms. n represents an integer from 1 to 100 and is preferably from 1 to 30. R5 represents a hydrogen atom or an alkyl group having from 1 to 12 carbon atoms. L represents a single bond or a divalent connecting group comprising from 1 to 60 carbon atoms  from 0 to 10 nitrogen atoms  from 0 to 50 oxygen atoms  from 1 to 100 hydrogen atoms and from 0 to 20 sulfur atoms. More specifically  the divalent connecting group includes those formed by a combination of structural units shown below.

In the structures above  Ra and Rb each represents a hydrogen atom  an alkyl group having from 1 to 20 carbon atoms  an aryl group having from 6 to 20 carbon atoms or a halogen atom. n represents an integer from 1 to 4.
According to the invention  specifically  the repeating unit having a hydrophilic group is preferably represented by formula (B1) shown below.

In formula (B1)  Ra to Rc each independently represents a hydrogen atom  an alkyl group having from 1 to 6 carbon atoms or a halogen atom. L has the same meaning as defined above. W represents a hydrophilic group and its preferred embodiment is the same as described above. W is preferably a group containing a polyalkylene oxy group  and particularly preferably a group containing a polyethylene oxy group.
Specific examples of the repeating unit having a hydrophilic group for use in the invention are set forth below  but the invention should not be construed as being limited thereto.







[Adsorbing group to surface of support]
According to a preferred example of the polymer chain for use in the invention  the polymer chain contains a repeating unit having at least one functional group capable of interacting with a surface of the support as a copolymerization component in order to increase an adhesion property to the support. The functional group capable of interacting with a surface of the support includes  for example  a group capable of undergoing interaction  for example  forming an ionic bond or a hydrogen bond or undergoing polar interaction  with metal  a metal oxide  a hydroxy group or the like present on the support subjected to anodizing treatment or hydrophilizing treatment is exemplified. Specific examples of the functional group capable of interacting with a surface of the support are set forth below.

In the formulae above  R5 to R7 each independently represents a hydrogen atom  an alkyl group having from 1 to 10 carbon atoms  an alkynyl group having from 2 to 10 carbon atoms  an alkenyl group having from 2 to 10 carbon atoms or an aryl group having from 6 to 15 carbon atoms  and M1 and M2 each independently represents a hydrogen atom  a metal atom included in alkali metal or alkaline earth metal or an ammonium group. From the standpoint of the stain resistance and printing durability  the functional group capable of interacting with a surface of the support is preferably a carboxylic acid group  a sulfonic acid group  a phosphoric acid ester group or a salt thereof or a phosphonic acid group or a salt thereof. In view of further improvement in the stain resistance  a phosphoric acid ester group or a salt thereof or a phosphonic acid group or a salt thereof is more preferred  and a phosphonic acid group or a salt thereof is most preferred.
According to the invention  specifically  the repeating unit having at least one functional group capable of interacting with a surface of the support is preferably represented by formula (B2) shown below.

In formula (B2)  Ra to Rc and L have the same meanings as those defined in formula (B1) respectively. Q represents a functional group capable of interacting with a surface of the support and its preferred embodiment is the same as described above.
Specific examples of the repeating unit having at least one functional group capable of interacting with a surface of the support for use in the invention are set forth below  but the invention should not be construed as being limited thereto.

[Crosslinkable group]
The polymer chain of the star polymer for use in the invention preferably further contains a repeating unit having a crosslinkable group as a copolymerization component. The crosslinkable group as used herein means a group capable of crosslinking the polymer chain in the process of a radical polymerization reaction which is caused in the image-recording layer  when the lithographic printing plate precursor is exposed to light. The crosslinkable group is not particularly restricted as long as it has such a function and includes  for example  an ethylenically unsaturated bond group  an amino group or an epoxy group as a functional group capable of undergoing an addition polymerization reaction. Also  a functional group capable of forming a radical upon irradiation with light may be used and such a crosslinkable functional group includes  for example  a thiol group and a halogen atom. Among them  the ethylenically unsaturated bond group is preferred. Of the ethylenically unsaturated bond groups  a (meth)acryloyl group or an allyl group is preferred  and a (meth)acryloyl group is particularly preferred.
In the polymer chain according to the invention  for example  a free radical (a polymerization initiating radical or a propagating radical in the process of polymerization of the polymerizable compound) is added to the crosslinkable functional group to cause an addition-polymerization between the polymer chains directly or through a polymerization chain of the polymerizable compound  as a result  crosslinkage is formed between the polymer chains to effect curing. Alternatively  an atom (for example  a hydrogen atom on the carbon atom adjacent to the crosslinkable functional group) in the polymer chain is withdrawn by a free radical to produce a polymer radical and the polymer radicals combine with each other to form crosslinkage between the polymer chains to effect curing.
The content of the crosslinkable group (content of the radical polymerizable unsaturated double bond determined by iodine titration) in the polymer chain for use in the invention is preferably from 0.01 to 10.0 mmol  more preferably from 0.05 to 9.0 mmol  most preferably from 0.1 to 8.0 mmol  based on 1 g of the star polymer.
According to the invention  specifically  the repeating unit having at least one crosslinkable group is preferably represented by formula (B3) shown below.

In formula (B3)  Ra to Rc and L have the same meanings as those defined in formula (B1) respectively. K represents a crosslinkable group and its preferred embodiment is the same as described above. Specific examples of the repeating unit having a crosslinkable group for use in the invention are set forth below  but the invention should not be construed as being limited thereto.

(Other repeating unit)
The polymer chain of the star polymer for use in the invention may be a polymer chain of a copolymer containing a repeating unit (hereinafter  simply referred to as an “other repeating unit” in some cases) other than the repeating units described above. As the other repeating unit  repeating units derived from conventionally known various monomers are exemplified.
The polymer chain for use in the invention may contain a polymerization unit of an alkyl or aryl ester of (meth)acrylic acid  a polymerization unit of a (meth)acrylamide or a derivative thereof  a polymerization unit of an a-hydroxymethylacrylate or a polymerization unit of a styrene derivative in addition to the polymerization unit having an acid group and the polymerization unit having a crosslinkable group described above.
The alkyl group of the alkyl ester of (meth)acrylic acid is preferably an alkyl group having from 1 to 5 carbon atoms or an alkyl group having from 2 to 8 carbon atoms and the substituent described above  and more preferably a methyl group. The aralkyl ester of (meth)acrylic acid includes  for example  benzyl (meth)acrylate.
The (meth)acrylamide derivative includes  for example  N-isopropylacrylamide  N-phenylmethacrylamide  N-(4-methoxycarbonylphenyl)methacrylamide  N N-dimethylacrylamide and morpholinoacrylamide.
The a-hydroxymethylacrylate includes  for example  ethyl a-hydroxymethylacrylate and cyclohexyl a-hydroxymethylacrylate. The styrene derivative includes  for example  styrene and 4-tert-butylstyrene.
Specific examples of the star polymer for use in the invention are set forth below  but the invention should not be construed as being limited thereto.
Polymer chains used in the specific examples are shown below.

TABLE 7: P-1 to P-50
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No. % by Mole*1
P-1 SA-3 0.5 C-1 10
P-2 SA-4 0.5 C-1 9.5
P-3 SA-5 0.5 C-1 9.2
P-4 SA-6 0.5 C-1 8.9
P-5 SA-7 0.5 C-1 8.8
P-6 SA-8 0.5 C-1 8.7
P-7 SB-030 0.5 C-1 10.6
P-8 SB-065 0.5 C-1 10.6
P-9 SB-210 0.5 C-1 7.9
P-10 SB-009 0.5 C-1 10.6
P-11 SB-036 0.5 C-1 9.3
P-12 SB-099 0.5 C-1 9.1
P-13 SB-204 0.5 C-1 8.1
P-14 SB-002 0.5 C-1 10.6
P-15 SB-007 0.5 C-1 9.1
P-16 SB-079 0.5 C-1 10.6
P-17 SB-093 0.5 C-1 9.4
P-18 SB-094 0.5 C-1 9.3
P-19 SB-100 0.5 C-1 9.0
P-20 SB-101 0.5 C-1 9.1
P-21 SB-156 0.5 C-1 10.6
P-22 SB-170 0.5 C-1 10.6
P-23 SB-205 0.5 C-1 9.4
P-24 SB-206 0.5 C-1 8.0
P-25 SB-207 0.5 C-1 8.4
P-26 SB-208 0.5 C-1 8.3
P-27 SB-209 0.5 C-1 8.4
P-28 SB-212 0.5 C-1 10.6
P-29 SC-002 0.5 C-1 11.0
P-30 SC-044 0.5 C-1 11.2
P-31 SC-037 0.5 C-1 10.9
P-32 SC-086 0.5 C-1 11.3
P-33 SC-093 0.5 C-1 10.8
P-34 SC-100 0.5 C-1 10.7
P-35 SE-056 0.5 C-1 8.0
P-36 SE-058 0.5 C-1 8.3
P-37 SE-059 0.5 C-1 7.8
P-38 SE-085 0.5 C-1 8.1
P-39 SE-014 0.5 C-1 8.0
P-40 SE-020 0.5 C-1 8.1
P-41 SE-243 0.5 C-1 8.3
P-42 SE-051 0.5 C-1 8.5
P-43 SE-055 0.5 C-1 7.9
P-44 SE-057 0.5 C-1 7.9
P-45 SE-063 0.5 C-1 7.8
P-46 SE-069 0.5 C-1 8.0
P-47 SE-097 0.5 C-1 8.2
P-48 SE-103 0.5 C-1 8.0
P-49 SE-109 0.5 C-1 8.1
P-50 SE-115 0.5 C-1 8.1

*1: Equivalent of SH group when the monomer is taken as 100.

TABLE 8: P-51 to P-63
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No. % by Mole*1
P-51 SF-025 0.5 C-1 8.4
P-52 SF-033 0.5 C-1 8.5
P-53 SF-037 0.5 C-1 8.4
P-54 SF-049 0.5 C-1 8.6
P-55 SF-053 0.5 C-1 8.7
P-56 SF-057 0.5 C-1 8.1
P-57 SF-061 0.5 C-1 8.4
P-58 SD-002 0.5 C-1 8.4
P-59 SD-030 0.5 C-1 8.5
P-60 SD-037 0.5 C-1 8.4
P-61 SA-8 0.5 C-2 8.4
P-62 SA-8 0.5 C-3 8.5
P-63 SA-8 0.5 C-4 8.4

TABLE 9: P-64 to P-76
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No. % by Mole*1 Hydrophilic Repeating Unit (A) Adsorbing Repeating Unit (B) Crosslinkable Repeating Unit (C) Molar Ratio of (A)/(B)/(C)
P-64 SA-8 0.25 - - 100/0/0 15.0
P-65 SA-8 0.5 - - 100/0/0 8.0
P-66 SA-8 1 - - 100/0/0 4.0
P-67 SA-8 0.25 - - 100/0/0 13.0
P-68 SA-8 0.5 - - 100/0/0 7.0
P-69 SA-8 1 - - 100/0/0 3.5
P-70 SA-8 0.25 - - 0/100/0 15.0
P-71 SA-8 0.5 - - 0/100/0 7.0
P-72 SA-8 1 - - 0/100/0 3.6
P-73 SA-8 0.25 - 90/10/0 16.0
P-74 SA-8 0.5 - 80/20/0 8.0
P-75 SA-8 1 - 70/30/0 4.2
P-76 SA-8 0.25 - 65/35/0 12.0

TABLE 10: P-77 to P-89
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No. % by Mole*1 Hydrophilic Repeating Unit (A) Adsorbing Repeating Unit (B) Crosslinkable Repeating Unit (C) Molar Ratio of (A)/(B)/(C)
P-77 SA-8 0.5 - 60/40/0 7.9
P-78 SA-8 1 - 55/45/0 3.6
P-79 SA-8 0.25 - 80/20/0 14.5
P-80 SA-8 0.5 - 80/20/0 8.6
P-81 SA-8 1 - 80/20/0 3.8
P-82 SA-8 0.25 - 80/20/0 13.5
P-83 SA-8 0.5 80/10/10 7.5
P-84 SA-8 1 80/10/10 3.6
P-85 SA-8 0.25 80/10/10 17.3
P-86 SA-8 0.5 80/10/10 6.5
P-87 SA-8 1.5 80/10/10 4.2
P-88 SA-8 0.25 80/10/10 14.0
P-89 SA-8 0.5 80/10/10 7.0

TABLE 11: P-90 to P-96
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No. % by Mole*1 Hydrophilic Repeating Unit (A) Adsorbing Repeating Unit (B) Crosslinkable Repeating Unit (C) Molar Ratio of (A)/(B)/(C)
P-90 SA-8 1.5 - 80/0/20 3.0
P-91 SA-8 0.25 80/5/15 15
P-92 SA-8 0.5 80/7/13 7.8
P-93 SA-8 1.5 80/9/11 4.5
P-94 SA-8 0.25 80/11/9 15
P-95 SA-8 0.5 80/13/7 8.0
P-96 SA-8 1.5 80/15/5 3.7

TABLE 12: P-97 to P-100
Polymer No. Central Skeleton Polymer Chain Mw
(x 104)
No.*3 % by Mole*2
P-97 SG-1 0.5 C-1 7.0
P-98 SG-2 0.5 C-1 9.0
P-99 SG-3 0.5 C-1 9.0
P-100 SG-4 0.5 C-1 6.0

*2: (Equivalent of central skeleton x number of branched chain) when the monomer is taken as 100.
*3: Structures of SG-1 to SG-4 are shown below.

* indicates a position connecting to a terminal of the polymer chain.

The star polymer according to the invention can be synthesized by radical polymerization using a multifunctional thiol  living radical polymerization using a multivalent dithiocarbamate compound  radical polymerization using a multivalent radical initiator or anion polymerization using an anion polymerization initiator having plural anion-generating sites.
The weight average molecular weight (Mw) of the star polymer according to the invention is preferably from 5 000 to 500 000  more preferably from 10 000 to 250 000  and particularly preferably from 20 000 to 150 000. In the range described above  the development property and printing durability are improved.
The star polymers according to the invention may be used only one kind or two or more kinds in combination. Also  it can be used together with a conventional straight-chain type binder.
[Undercoat layer]
The undercoat layer according to the invention means a layer provided between the support and the image-recording layer of the lithographic printing plate precursor.
In the case of using the star polymer in the undercoat layer according to the invention  the star polymer is ordinarily used by diluted it with a solvent. The solvent includes water and an organic solvent  for example  methanol  ethanol  propanol  isopropanol  ethylene glycol  hexylene glycol  THF  DMF  1-methoxy-2-propanol  dimethylacetamide or dimethylsulfoxide  and is particularly preferably water or an alcohol. The solvents may be used as a mixture.
The concentration of a coating solution for undercoat layer is preferably from 0.001 to 10% by weight  more preferably from 0.01 to 5% by weight  and still more preferably from 0.05 to 1% by weight. The undercoat layer may contain a surfactant described hereinafter  if desired.
The coating amount (solid content) of the undercoat layer is preferably from 0.1 to 100 mg/m2  and more preferably from 3 to 30 mg/m2.
Various methods can be used for the coating of the undercoat layer. Examples of the method include bar coater coating  spin coating  spray coating  curtain coating  dip coating  air knife coating  blade coating and roll coating.
The undercoat layer according to the invention may contain a chelating agent  a secondary or tertiary amine  a polymerization inhibitor or a compound containing an amino group or a functional group having polymerization inhibition ability and a group capable of interacting with a surface of aluminum support (for example  1 4-diazabicyclo[2 2 2]octane (DABCO)  2 3 5 6-tetrahydroxy-p-quinone  chloranil  sulfophthalic acid  hydroxyethylethylenediaminetriacetic acid  dihydroxyethylethylenediaminediacetic acid or hydroxyethyliminodiacetic acid) in addition to the star polymer described above in order to prevent the occurrence of stain due to the lapse of time.
The content of the star polymer according to the invention in the undercoat layer is preferably from 5 to 100% by weight  more preferably from 10 to 100% by weight  particularly preferably from 15 to 100% by weight  based on the total solid content of the undercoat layer.
[Support]
A support for use in the lithographic printing plate precursor according to the invention is not particularly restricted as long as it is a dimensionally stable plate-like hydrophilic support. Particularly  an aluminum plate is preferred. In advance of the use of an aluminum plate  the aluminum plate is preferably subjected to a surface treatment  for example  roughening treatment or anodizing treatment. The roughening treatment of the surface of the aluminum plate is conducted by various methods and includes  for example  mechanical roughening treatment  electrochemical roughening treatment (roughening treatment of electrochemically dissolving the surface) and chemical roughening treatment (roughening treatment of chemically dissolving the surface selectively). With respect to the surface treatments  methods described in Paragraph Nos. [0241] to [0245] of JP-2007-206217 are preferably used.
The support subjected to the roughening treatment and anodizing treatment may be subjected to a hydrophilizing treatment in order to increase hydrophilicity of the surface of support. According to the invention  the support is subjected to a hydrophilizing treatment with a solution containing the star polymer described above to provide a layer containing the star polymer between the support and the image-recording layer. In this case  the undercoat layer may not be necessarily provided.
In the case of conducting the hydrophilizing treatment of the support with a solution containing the star polymer  the support is treated by immersing it in a solution formed by diluting the star polymer with a solvent. The solvent includes water and an organic solvent  for example  methanol  ethanol  propanol  isopropanol  ethylene glycol  hexylene glycol  THF  DMF  1-methoxy-2-propanol  dimethylacetamide or dimethylsulfoxide  and is particularly preferably water or an alcohol. The solvents may be used as a mixture. The content of the star polymer in the solution used in the immersion treatment is preferably from 0.001 to 10% by weight  and more preferably from 0.01 to 3% by weight. The immersion time is preferably from 5 seconds to 10 minutes  and more preferably from 60 seconds to 2 minutes. The solution temperature at the immersion treatment is preferably from 20 to 100?C  and more preferably from 50 to 90?C.
The attachment amount (solid content) of the star polymer onto the surface of support is preferably from 0.1 to 100 mg/m2  and more preferably from 3 to 30 mg/m2.
The hydrophilizing treatment without using the star polymer includes  for example  an alkali metal silicate treatment method wherein the support is subjected to an immersion treatment or an electrolytic treatment in an aqueous solution  for example  of sodium silicate  a method of treating with potassium fluorozirconate  a method of treating with polyvinylphosphonic acid and a method of treating with polyacrylic acid. A method of immersion treatment in an aqueous solution  for example  of sodium silicate or a method of immersion treatment in an aqueous polyvinylphosphonic acid solution is preferably used.
The center line average roughness of the support is preferably from 0.10 to 1.2 µm. In the range described above  good adhesion property to the image-recording layer and good printing durability and good resistance to stain are achieved.
The color density of the support is preferably from 0.15 to 0.65 in terms of the reflection density value. In the range described above  good image-forming property due to prevention of halation at the image exposure and good aptitude for plate inspection after development are achieved.
The thickness of the support is preferably from 0.1 to 0.6 mm  more preferably from 0.15 to 0.4 mm  and still more preferably from 0.2 to 0.3 mm.

[Image-recording layer]
The image-recording layer according to the invention is a negative image-recording layer wherein the imagewise exposed area remains after development to from an image area at printing. In particular  an image-recording layer of polymerization type containing (B) a polymerization initiator and (C) a polymerizable compound is preferred.
(B) Polymerization initiator
The image-recording layer contains a polymerization initiator (hereinafter  also referred to as an initiator compound). In the invention  a radical polymerization initiator is preferably used.
As the initiator compound in the invention  initiator compounds known to those skilled in the art can be used without limitation. Specifically  the initiator compound includes  for example  a trihalomethyl compound  a carbonyl compound  an organic peroxide  an azo compound  an azide compound  a metallocene compound  a hexaarylbiimidazole compound  an organic boron compound  a disulfone compound  an oxime ester compound  an onium salt compound and a iron arene complex. Among them  at least one compound selected from the hexaarylbiimidazole compound  onium salt compound  trihalomethyl compound and metallocene compound is preferred  and the hexaarylbiimidazole compound or the onium salt compound is particularly preferred. Two or more kinds of the polymerization initiators may be appropriately used in combination.
The hexaarylbiimidazole compound includes  for example  lophine dimers described in European Patents 24 629 and 107 792 and U.S. Patent 4 410 621  specifically  2 2’-bis(o-chlorophenyl)-4 4’ 5 5’-tetraphenylbiimidazole  2 2’-bis(o-bromophenyl)-4 4’ 5 5’-tetraphenylbiimidazole  2 2’-bis(o p-dichlorophenyl)-4 4’ 5 5’-tetraphenylbiimidazole  2 2’-bis(o-chlorophenyl)-4 4’ 5 5’-tetra(m-methoxyphenyl)biimidazole  2 2’-bis(o o’-dichlorophenyl)-4 4’ 5 5’-tetraphenylbiimidazole  2 2’-bis(o-nitrophenyl)-4 4’ 5 5’-tetraphenylbiimidazole  2 2’-bis(o-methylphenyl)-4 4’ 5 5’-tetraphenylbiimidazole and 2 2’-bis(o-trifluoromethylphenyl)-4 4’ 5 5’-tetraphenylbiimidazole.
The hexaarylbiimidazole compound is particularly preferably used together with a sensitizing dye having an absorption maximum in a wavelength range from 300 to 450 nm.
The onium salt compound preferably used in the invention includes a sulfonium salt  an iodonium salt and a diazonium salt. Particularly  a diaryliodonium salt or a triarylsulfonium salt is preferably used. The onium salt compound is particularly preferably used together with an infrared absorbing agent having an absorption maximum in a wavelength range from 750 to 1 400 nm.
In addition  polymerization initiators described in Paragraph Nos. [0071] to [0129] of JP-A-2007-206217 are preferably used.
The polymerization initiators are preferably used individually or in combination of two or more thereof according to the invention.
The amount of the polymerization initiator used in the image-recording layer according to the invention is preferably from 0.01 to 20% by weight  more preferably from 0.1 to 15% by weight  still more preferably from 1.0 to 10% by weight  based on the total solid content of the image-recording layer.
(C) Polymerizable compound
The polymerizable compound for use in the image-recording layer according to the invention is an addition-polymerizable compound having at least one ethylenically unsaturated double bond and it is selected from compounds having at least one  preferably two or more  terminal ethylenically unsaturated double bonds. The polymerizable compound has a chemical form  for example  a monomer  a prepolymer  specifically  a dimer  a trimer or an oligomer  or a mixture thereof. Examples of the monomer include unsaturated carboxylic acids (for example  acrylic acid  methacrylic acid  itaconic acid  crotonic acid  isocrotonic acid or maleic acid) and esters or amides thereof. Preferably  esters of an unsaturated carboxylic acid with a polyhydric alcohol compound and amides of an unsaturated carboxylic acid with a polyvalent amine compound are used. An addition reaction product of an unsaturated carboxylic acid ester or amide having a nucleophilic substituent  for example  a hydroxy group  an amino group or a mercapto group  with a monofunctional or polyfunctional isocyanate or epoxy compound  or a dehydration condensation reaction product of the unsaturated carboxylic acid ester or amide with a monofunctional or polyfunctional carboxylic acid is also preferably used. Moreover  an addition reaction product of an unsaturated carboxylic acid ester or amide having an electrophilic substituent  for example  an isocyanate group or an epoxy group  with a monofunctional or polyfunctional alcohol  amine or thiol  or a substitution reaction product of an unsaturated carboxylic acid ester or amide having a releasable substituent  for example  a halogen atom or a tosyloxy group with a monofunctional or polyfunctional alcohol  amine or thiol is also preferably used. In addition  compounds in which the unsaturated carboxylic acid described above is replaced by an unsaturated phosphonic acid  styrene  vinyl ether or the like can also be used. These compounds are described in references including JP-T-2006-508380 (the term “JP-T” as used herein means a published Japanese translation of a PCT patent application)  JP-A-2002-287344  JP-A-2008-256850  JP-A-2001-342222  JP-A-9-179296  JP-A-9-179297  JP-A-9-179298  JP-A-2004-294935  JP-A-2006-243493  JP-A-2002-275129  JP-A-2003-64130  JP-A-2003-280187 and JP-A-10-333321.
Specific examples of the monomer  which is an ester of a polyhydric alcohol compound with an unsaturated carboxylic acid  include  as an acrylic acid ester  for example  ethylene glycol diacrylate  1 3-butanediol diacrylate  tetramethylene glycol diacrylate  propylene glycol diacrylate  trimethylolpropane triacrylate  hexanediol diacrylate  tetraethylene glycol diacrylate  pentaerythritol tetraacrylate  sorbitol triacrylate  isocyanuric acid ethylene oxide (EO) modified triacrylate and polyester acrylate oligomer. As a methacrylic acid ester  for example  tetramethylene glycol dimethacrylate  neopentyl glycol dimethacrylate  trimethylolpropane trimethacrylate  ethylene glycol dimethacrylate  pentaerythritol trimethacrylate  bis[p-(3-methacryloxy-2-hydroxypropoxy)phenyl]dimethylmethane and bis[p-(methacryloxyethoxy)¬phenyl]dimethylmethane are exemplified. Specific examples of the monomer  which is an amide of a polyvalent amine compound with an unsaturated carboxylic acid  include methylene bisacrylamide  methylene bismethacrylamide  1 6-hexamethylene bisacrylamide  1 6-hexamethylene bismethacrylamide  diethylenetriamine trisacrylamide  xylylene bisacrylamide and xylylene bismethacrylamide.
Urethane type addition-polymerizable compounds produced using an addition reaction between an isocyanate and a hydroxy group are also preferably used and specific examples thereof include vinylurethane compounds having two or more polymerizable vinyl groups per molecule obtained by adding a vinyl monomer containing a hydroxy group represented by formula (A) shown below to a polyisocyanate compound having two or more isocyanate groups per molecule  described in JP-B-48-41708 (the term “JP-B” as used herein means an “examined Japanese patent publication”).
CH2=C(R4)COOCH2CH(R5)OH (A)
wherein R4 and R5 each independently represents H or CH3.
Also  urethane acrylates as described in JP-A-51-37193  JP-B-2-32293  JP-B-2-16765  JP-A-2003-344997 and JP-A-2006-65210  urethane compounds having an ethylene oxide skeleton described in JP-B-58-49860  JP-B-56-17654  JP-B-62-39417  JP-B-62-39418  JP-A-2000-250211 and JP-A-2007-94138  and urethane compounds having a hydrophilic group described in U.S. Patent 7 153 632  JP-T-8-505958  JP-A-2007-293221 and JP-A-2007-293223 are preferably used.
Details of the method of using the polymerizable compound  for example  selection of the structure  individual or combination use or an amount added  can be appropriately determined in accordance with the characteristic design of the final lithographic printing plate precursor. The polymerizable compound is used preferably in a range from 5 to 75% by weight  more preferably in a range from 25 to 70% by weight  particularly preferably in a range from 30 to 60% by weight  based on the total solid content of the image-recording layer.

(D) Binder polymer
In the image-recording layer according to the invention  a binder polymer can be used for the purpose of improving film strength of the image-recording layer. The binder polymer which can be used in the invention can be selected from those heretofore known without restriction  and a polymer having a film-forming property is preferred. Among them  an acrylic resin  a polyvinyl acetal resin and a polyurethane resin are preferred.
As the binder polymer preferable for the invention  a polymer having a crosslinkable functional group for improving film strength of the image area in its main chain or side chain  preferably in its side chain  as described in JP-A-2008-195018 is exemplified. Due to the crosslinkable functional group  crosslinkage is formed between the polymer molecules to facilitate curing.
As the crosslinkable functional group  an ethylenically unsaturated group  for example  a (meth)acryl group  a vinyl group  an allyl group or a styryl group or an epoxy group is preferred. The crosslinkable functional group can be introduced into the polymer by a polymer reaction or copolymerization. For instance  a reaction between an acrylic polymer or polyurethane having a carboxyl group in its side chain and glycidyl methacrylate or a reaction between a polymer having an epoxy group and a carboxylic acid containing an ethylenically unsaturated group  for example  methacrylic acid can be utilized.
The content of the crosslinkable group in the binder polymer is preferably from 0.1 to 10.0 mmol  more preferably from 1.0 to 7.0 mmol  most preferably from 2.0 to 5.5 mmol  based on 1 g of the binder polymer.
It is also preferred that the binder polymer for use in the invention further contains a hydrophilic group. The hydrophilic group contributes to impart the development property to the image-recording layer. In particular  coexistence of the crosslinkable group and the hydrophilic group makes it possible to maintain good balance between the printing durability and the development property.
The hydrophilic group includes  for example  a hydroxy group  a carboxyl group  an alkylene oxide structure  an amino group  an ammonium group  an amido group  a sulfo group and a phosphoric acid group. Among them  an alkylene oxide structure containing from 1 to 9 alkylene oxide units each having 2 or 3 carbon atoms is preferred. In order to introduce a hydrophilic group into the binder polymer  a monomer having the hydrophilic group may be copolymerized.
According to the invention  for example  in the case of development with an aqueous alkaline solution  the hydrophilic group is particularly preferably an acid group  for example  a carboxylic acid group or a sulfonic acid group. In the case of conducting the development with dampening water and/or printing ink on a printing machine  the hydrophilic group is particularly preferably that having a polyoxyethylene structure.
In order to control the ink receptivity  an oleophilic group  for example  an alkyl group  an aryl group  an aralkyl group or an alkenyl group may be introduced into the binder polymer according to the invention. Specifically  an oleophilic group-containing monomer  for example  an alkyl methacrylate may be copolymerized.
The weight average molecular weight (Mw) of the binder polymer according to the invention is preferably 2 000 or more  more preferably 5 000 or more  and still more preferably from 10 000 to 300 000.
According to the invention  a hydrophilic polymer  for example  polyacrylic acid or polyvinyl alcohol described in JP-A-2008-195018 may be used  if desired. Further  an oleophilic binder polymer is used together with a hydrophilic binder polymer.
The content of the binder polymer is preferably from 5 to 90% by weight  more preferably from 5 to 80% by weight  still more preferably from 10 to 70% by weight  based on the total solid content of the image-recording layer.
Specific examples of the binder polymer (for the image-recording layer of on-press development type and for the image-recording layer to be developed with an aqueous alkaline solution) used in the invention are set forth below  but the invention should not be construed as being limited thereto.
As the binder polymer for the image-recording layer of on-press development type  (1) to (11) shown below are exemplified.

As the binder polymer for the image-recording layer to be developed with an aqueous alkaline solution  for example  alkali-soluble binders described in Paragraph Nos. [0119] to [0123] of JP-A-2008-64786 are used.
(Sensitizing dye)
The image-recording layer according to the invention preferably contains a sensitizing dye. The sensitizing dye can be used without particular limitation as far as it absorbs light at the image exposure to form the excited state and provides energy to the polymerization initiator described above with electron transfer  energy transfer or heat generation thereby improving the polymerization initiation function. Particularly  a sensitizing dye having an absorption maximum in a wavelength range from 300 to 450 nm or from 750 to 1 400 nm is preferably used.
Examples of the sensitizing dye having an absorption maximum in a wavelength range from 300 to 450 nm include merocyanine dyes  benzopyranes  coumarins  aromatic ketones  anthracenes  styryls and oxazoles.
Of the sensitizing dyes having an absorption maximum in a wavelength range from 300 to 450 nm  a dye represented by formula (2) shown below is more preferable in view of high sensitivity.
Formula (2):

In formula (2)  A represents an aryl group which may have a substituent or a heteroaryl group which may have a substituent  X represents an oxygen atom  a sulfur atom or =N(R3)  and R1  R2 and R3 each independently represents a monovalent non-metallic atomic group  or A and R1 or R2 and R3 may be combined with each other to form an aliphatic or aromatic ring.
The formula (2) will be described in more detail below. R1  R2 and R3 each independently represents a monovalent non-metallic atomic group  preferably a hydrogen atom  a substituted or unsubstituted alkyl group  a substituted or unsubstituted alkenyl group  a substituted or unsubstituted aryl group  a substituted or unsubstituted heteroaryl group  a substituted or unsubstituted alkoxy group  a substituted or unsubstituted alkylthio group  a hydroxy group or a halogen atom.
Specific examples of such a sensitizing dye preferably used include compounds described in Paragraph Nos. [0047] to [0053] of JP-A-2007-58170  Paragraph Nos. [0036] to [0037] of JP-A-2007-93866 and Paragraph Nos. [0042] to [0047] of JP-A-2007-72816.
Further  sensitizing dyes described in JP-A-2006-189604  JP-A-2007-171406  JP-A-2007-206216  JP-A-2007-206217  JP-A-2007-225701  JP-A-2007-225702  JP-A-2007-316582 and JP-A-2007-328243 are also preferably used.
The sensitizing dyes may be used only one kind or in combination of two or more kinds thereof.
Next  the sensitizing dye having an absorption maximum in a wavelength range from 750 to 1 400 (hereinafter  also referred to as an “infrared absorbing agent”) preferably used in the invention is described in detail below. The infrared absorbing agent used is preferably a dye or a pigment.
As the dye  commercially available dyes and known dyes described in literatures  for example  Senryo Binran (Dye Handbook) compiled by The Society of Synthetic Organic Chemistry  Japan (1970) can be used. Specifically  the dyes includes azo dyes  metal complex azo dyes  pyrazolone azo dyes  naphthoquinone dyes  anthraquinone dyes  phthalocyanine dyes  carbonium dyes  quinoneimine dyes  methine dyes  cyanine dyes  squarylium dyes  pyrylium salts and metal thiolate complexes.
Of the dyes  cyanine dyes  squarylium dyes  pyrylium dyes  nickel thiolate complexes and indolenine cyanine dyes are particularly preferred. Further  cyanine dyes and indolenine cyanine dyes are more preferred. As particularly preferable examples of the dye  cyanine dyes represented by formula (a) shown below are exemplified.
Formula (a)

In formula (a)  X1 represents a hydrogen atom  a halogen atom  -N(R9)(R10)  -X2-L1 or a group shown below. R9 and R10  which may be the same or different  each represents an aromatic hydrocarbon group having from 6 to 10 carbon atoms  which may have a substituent  an alkyl group having from 1 to 8 carbon atoms or a hydrogen atom or R9 and R10 may be combined with each other to from a ring  and preferably represents a phenyl group. X2 represents an oxygen atom or a sulfur atom  L1 represents a hydrocarbon group having from 1 to 12 carbon atoms  an aromatic cyclic group containing a hetero atom or a hydrocarbon group having from 1 to 12 carbon atoms and containing a hetero atom. The hetero atom as used herein means a nitrogen atom  a sulfur atom  an oxygen atom  a halogen atom or a selenium atom. In the group shown below  Xa- has the same meaning as Za- defined hereinafter. Ra represents a hydrogen atom or a substituent selected from an alkyl group  an aryl group  a substituted or unsubstituted amino group and a halogen atom.

R1 and R2 each independently represents a hydrocarbon group having from 1 to 12 carbon atoms. In view of the preservation stability of a coating solution for image-recording layer  it is preferred that R1 and R2 each represents a hydrocarbon group having two or more carbon atoms. Also  R1 and R2 may be combined with each other to form a ring and in case of forming the ring  to form a 5-membered or 6-membered ring is particularly preferred.
Ar1 and Ar2  which may be the same or different  each represents an aryl group which may have a substituent. Preferable examples of the aryl group include a benzene ring group and a naphthalene ring group. Preferable examples of the substituent include a hydrocarbon group having 12 or less carbon atoms  a halogen atom and an alkoxy group having 12 or less carbon atoms. Y1 and Y2  which may be the same or different  each represents a sulfur atom or a dialkylmethylene group having 12 or less carbon atoms. R3 and R4  which may be the same or different  each represents a hydrocarbon group having 20 or less carbon atoms  which may have a substituent. Preferable examples of the substituent include an alkoxy group having 12 or less carbon atoms  a carboxyl group and a sulfo group. R5  R6  R7 and R8  which may be the same or different  each represents a hydrogen atom or a hydrocarbon group having 12 or less carbon atoms. From the standpoint of the availability of raw materials  a hydrogen atom is preferred. Za- represents a counter anion. However  Za- is not necessary when the cyanine dye represented by formula (a) has an anionic substituent in the structure thereof and the neutralization of charge is not needed. Preferable examples of the counter ion for Za- include a halide ion  a perchlorate ion  a tetrafluoroborate ion  a hexafluorophosphate ion and a sulfonate ion  and particularly preferable examples thereof include a perchlorate ion  a hexafluorophosphate ion and an arylsulfonate ion in view of the preservation stability of a coating solution for image-recording layer.
Specific examples of the cyanine dye represented by formula (a) preferably used in the invention include compounds described in Paragraph Nos. [0017] to [0019] of JP-A-2001-133969  Paragraph Nos. [0012] to [0021] of JP-A-2002-23360 and Paragraph Nos. [0012] to [0037] of JP-A-2002-40638  preferably compounds described in Paragraph Nos. [0034] to [0041] of JP-A-2002-278057 and Paragraph Nos. [0080] to [0086] of JP-A-2008-195018  and particularly preferably compounds described in Paragraph Nos. [0035] to [0043] of JP-A-2007-90850.
Further  compounds described in Paragraph Nos. [0008] to [0009] of JP-A-5-5005 and Paragraph Nos. [0022] to [0025] of JP-A-2001-222101 are also preferably used.
The infrared absorbing dyes may be used only one kind or in combination of two or more kinds thereof and may be used together with an infrared absorbing agent other than the infrared absorbing dye  for example  a pigment. As the pigment  compounds described in Paragraph Nos. [0072] to [0076] of JP-A-2008-195018 are preferred.
The amount of the sensitizing dye added is preferably from 0.05 to 30% by weight  more preferably from 0.1 to 20% by weight  most preferably from 0.2 to 10% by weight  based on the total solid content of the image-recording layer.
(F) Other components of image-recording layer
Into the image-recording layer according to the invention  various additives can be further incorporated  if desired. Examples of the additive include a surfactant for progressing the development property and improving the surface state of coated layer  a microcapsule for providing good compatibility between the development property and printing durability  a hydrophilic polymer for improving the development property and dispersion stability of microcapsule  a coloring agent or print-out agent for visually distinguishing the image area from the non-image area  a polymerization inhibitor for preventing undesirable thermal polymerization of the radical polymerizable compound during the production or preservation of the image-recording layer  a hydrophobic low molecular weight compound  for example  a higher fatty acid derivative for avoiding polymerization inhibition due to oxygen  a fine inorganic particle for increasing strength of the cured layer in the image area  a fine organic particle  a hydrophilic low molecular weight compound for improving the development property  a co-sensitizer or chain transfer agent for increasing sensitivity  and a plasticizer for improving plasticity. As the additives  known compounds are used and  for example  compounds described in Paragraph Nos. [0161] to [0215] of JP-A-2007-206217  Paragraph No. [0067] of JP-T-2005-509192  Paragraph Nos. [0023] to [0026] and [0059] to [0066] of JP-A-2004-310000 are used. With respect to the surfactant  surfactants which may be added to a developer described hereinafter may be used.
The image-recording layer preferably contains a chain transfer agent. The chain transfer agent is defined  for example  in Kobunshi Jiten (Polymer Dictionary)  Third Edition  pages 683 to 684  edited by The Society of Polymer Science  Japan (2005). As the chain transfer agent  for example  compounds having SH  PH  SiH or GeH in their molecules are used. The compound donates a hydrogen to a low active radical species to generate a radical or is oxidized and then deprotonized to generate a radical.
In the image-recording layer according to the invention  a thiol compound (for example  a 2-mercaptobenzimidazole  a 2-mercaptobenzothiazole  a 2-mercaptobenzoxazole  a 3-mercaptotriazole or a 5-mercaptotetrazole) is preferably used.
The content of the chain transfer agent is preferably from 0.01 to 20 parts by weight  more preferably from 1 to 10 parts by weight  most preferably from 1 to 5 parts by weight  per 100 parts by weight of the total solid content of the image-recording layer.
The image-recording layer according to the invention may contain a hydrophilic low molecular weight compound in order to improve the on-press development property. As the hydrophilic low molecular weight compound  a polyol compound  an organic sulfate compound  an organic sulfonate compound and a betaine compound are preferred.
Specific examples of the organic sulfonate compound include an alkylsulfonate  for example  sodium n-butylsulfonate  sodium n-hexylsulfonate  sodium 2-ethylhexylsulfonate  sodium cyclohexylsulfonate or sodium n-octylsulfonate; an alkylsulfonate containing an ethylene oxide chain  for example  sodium 5 8 11-trioxapentadecane-1-sulfonate  sodium 5 8 11-trioxaheptadecane-1-sulfonate  sodium 13-ethyl-5 8 11-trioxaheptadecane-1-sulfonate or sodium 5 8 11 14-tetraoxatetracosane-1-sulfonate; an arylsulfonate  for example  sodium benzenesulfonate  sodium p-toluenesulfonate  sodium p-hydroxybenzenesulfonate  sodium p-styrenesulfonate  sodium isophthalic acid dimethyl-5-sulfonate  sodium 1-naphtylsulfonate  sodium 4-hydroxynaphtylsulfonate  disodium 1 5-naphthalenedisulfonate or trisodium 1 3 6-naphthalenetrisulfonate. The salt may also be a potassium salt or a lithium salt.
The organic sulfate compound includes a sulfate of alkyl  alkenyl  alkynyl  aryl or heterocyclic monoether of polyethylene oxide. The number of ethylene oxide unit is preferably from 1 to 4. The salt is preferably a sodium salt  a potassium salt or a lithium salt.
As the betaine compound  a compound wherein a number of carbon atoms included in a hydrocarbon substituent on the nitrogen atom is from 1 to 5 is preferred. Specific examples thereof include trimethylammonium acetate  dimethylpropylammonium acetate  3-hydroxy-4-trimethylammoniobutyrate  4-(1-pyridinio)butyrate  1-hydroxyethyl-1-imidazolioacetate  trimethylammonium methanesulfonate  dimethylpropylammonium methanesulfonate  3-trimethylammonio-1-porpanesulfonate and 3-(1-pyridinio)-1-porpanesulfonate.
The amount of the hydrophilic low molecular weight compound added to the image-recording layer is preferably from 0.5 to 20% by weight  more preferably from 1 to 10% by weight  based on the total solid content of the image-recording layer.
In order to improve the ink receptivity  an oil-sensitizing agent  for example  a phosphonium compound  a nitrogen-containing low molecular weight compound or an ammonium group-containing polymer can be used in the image-recording layer according to the invention. The oil-sensitizing agent is effective in case of the image-recording layer capable of undergoing on-press development.
In particular  in the case where an inorganic stratiform compound is incorporated into a protective layer  the oil-sensitizing agent functions as a surface covering agent of the inorganic stratiform compound and prevents deterioration of the ink receptivity during printing due to the inorganic stratiform compound.
As preferred examples of the phosphonium compound  phosphonium compounds described in JP-A-2006-297907 and JP-A-2007-50660 are exemplified. Specific examples of the phosphonium compound include tetraphenylphosphonium bromide and 1 9-bis(triphenylphosphonio)nonane naphthalene-2 7-disulfonate.
As the nitrogen-containing low molecular weight compound  an amine salt and a quaternary ammonium salt are exemplified. Also  an imidazolinium salt  a benzimidazolinium salt  a pyridinium salt and a quinolinium salt are exemplified. Of the nitrogen-containing low molecular weight compounds  the quaternary ammonium salt and pyridinium salt are preferably used. Specific examples the nitrogen-containing low molecular weight compound include tetrabutylammonium hexafluorophosphate  dodecyltrimethylammonium p-toluenesulfonate  benzyltriethylammonium hexafluorophosphate  benzyldimethyloctylammonium hexafluorophosphate and benzyldimethyldodecylammonium hexafluorophosphate.
As the ammonium group-containing polymer  polymers described in JP-A-2009-208458  for example  2-(trimethylammonio)ethyl methacrylate p-toluenesulfonate/3 6-dioxaheptyl methacrylate copolymer  2-(trimethylammonio)ethyl methacrylate hexafluorophosphate /2-ethylhexyl methacrylate copolymer or 2-(butyldimethylammonio)ethyl methacrylate hexafluorophosphate/3 6-dioxaheptyl methacrylate copolymer are exemplified.
The content of the oil-sensitizing agent is preferably from 0.01 to 30.0% by weight  more preferably from 0.1 to 15.0% by weight  still more preferably from 1 to 10% by weight  based on the total solid content of the image-recording layer.
(Formation of image-recording layer)
The image-recording layer according to the invention is formed by dispersing or dissolving each of the necessary components described above in a solvent to prepare a coating solution and coating the solution. The solvent used include  for example  methyl ethyl ketone  ethylene glycol monomethyl ether  1-methoxy-2-propanol  2-methoxyethyl acetate  1-methoxy-2-propyl acetate and ?-butyrolactone  but the invention should not be construed as being limited thereto. The solvents may be used individually or as a mixture. The solid content concentration of the coating solution is preferably from 1 to 50% by weight.
The coating amount (solid content) of the image-recording layer on the support after the coating and drying is preferably from 0.3 to 3.0 g/m2. Various methods can be used for the coating. Examples of the method include bar coater coating  spin coating  spray coating  curtain coating  dip coating  air knife coating  blade coating and roll coating.
[Protective layer]
In the lithographic printing plate precursor according to the invention  a protective layer (oxygen-blocking layer) is preferably provided on the image-recording layer in order to prevent diffusion and penetration of oxygen which inhibits the polymerization reaction at the time of exposure. As a material for use in the protective layer  any water-soluble polymer and water-insoluble polymer can be appropriately selected to use. The polymers may be used in combination of two or more thereof  if desired. Specifically  for example  polyvinyl alcohol  a modified polyvinyl alcohol  polyvinyl pyrrolidone  a water-soluble cellulose derivative and poly(meth)acrylonitrile are exemplified. Among them  a water-soluble polymer compound relatively excellent in crystallizability is preferably used. Specifically  when polyvinyl alcohol is used as a main component  the particularly preferred results can be obtained in the fundamental characteristics  for example  oxygen-blocking property and removability by development.
Polyvinyl alcohol for use in the protective layer may be partially substituted with ester  ether or acetal as long as it contains unsubstituted vinyl alcohol units for achieving the necessary oxygen-blocking property and water solubility. Also  polyvinyl alcohol may partly have other copolymer component. Polyvinyl alcohol is obtained by hydrolysis of polyvinyl acetate. Examples of the polyvinyl alcohol include those having a hydrolysis degree of 69.0 to 100% by mole and a polymerization repeating unit number of 300 to 2 400. Specific examples thereof include PVA-102  PVA-103  PVA-105  PVA-110  PVA-117  PVA-117H  PVA-120  PVA-124  PVA-124H  PVA-CS  PVA-CST  PVA-HC  PVA-203  PVA-204  PVA-205  PVA-210  PVA-217  PVA-220  PVA-224  PVA-235  PVA-217EE  PVA-217E  PVA-220E  PVA-224E  PVA-403  PVA-405  PVA-420  PVA-424H  PVA-505  PVA-617  PVA-613  PVA-706 and L-8 (produced by Kuraray Co.  Ltd.). The polyvinyl alcohols can be used individually or as a mixture. According to a preferred embodiment  the content of polyvinyl alcohol in the protective layer is from 20 to 95% by weight  and more preferably from 30 to 90% by weight.
Also  known modified polyvinyl alcohol can be preferably used. Particularly  an acid-modified polyvinyl alcohol having a carboxylic acid group or a sulfonic acid group is preferably used. Specifically  modified polyvinyl alcohols described in JP-A-2005-250216 and JP-A-2006-259137 are preferably exemplified.
When the polyvinyl alcohol is used as a mixture with other material  as the other material mixed  a modified polyvinyl alcohol  polyvinyl pyrrolidone or a modified product thereof is preferred from the viewpoint of the oxygen-blocking property and removability by development. The content thereof in the protective layer is ordinarily from 3.5 to 80% by weight  preferably from 10 to 60% by weight  and more preferably from 15 to 30% by weight.
As other component of the protective layer  glycerin  dipropylene glycol or the like can be added in an amount corresponding to several % by weight of the material for the protective layer to provide flexibility. Further  an anionic surfactant  for example  sodium alkylsulfate or sodium alkylsulfonate  an amphoteric surfactant  for example  alkylaminocarboxylate and alkylaminodicarboxylate  or a nonionic surfactant  for example  polyoxyethylene alkyl phenyl ether can be added in an amount of several % by weight of the material for the protective layer.
Further  it is also preferred to incorporate an inorganic stratiform compound into the protective layer of the lithographic printing plate precursor according to the invention for the purpose of improving the oxygen-blocking property and property for protecting the surface of image-recording layer. Of the inorganic stratiform compounds  fluorine-based swellable synthetic mica  which is a synthetic inorganic stratiform compound  is particularly useful. Specifically  inorganic stratiform compounds described in JP-A-2005-119273 are preferably exemplified.
Further  protective layers described in U.S. Patent 3 458 311  JP-B-55-49729  JP-A-2008-15503  JP-A-2008-89916 and Paragraph Nos. [0211] to [0261] of JP-2008-139813 are preferably used.
The coating amount of the protective layer is preferably in a range from 0.05 to 10 g/m2 in terms of the coating amount after drying. When the protective layer contains the inorganic stratiform compound  it is more preferably in a range from 0.1 to 5 g/m2  and when the protective layer does not contain the inorganic stratiform compound  it is more preferably in a range from 0.5 to 5 g/m2.
[Backcoat layer]
A backcoat layer can be provided on the back surface of the support after conducting the surface treatment to the surface of support or forming the undercoat layer on the surface of support  if desired.
The backcoat layer preferably includes  for example  a coating layer comprising an organic polymer compound described in JP-A-5-45885 and a coating layer comprising a metal oxide obtained by hydrolysis and polycondensation of an organic metal compound or an inorganic metal compound described in JP-A-6-35174. Among them  use of an alkoxy compound of silicon  for example  Si(OCH3)4  Si(OC2H5)4  Si(OC3H7)4 or Si(OC4H9)4 is preferred since the starting materials are inexpensive and easily available.
[Plate making method]
The plate making method of the lithographic printing plate precursor according to the invention is preferably a method including at least a step of imagewise exposing the lithographic printing plate precursor (hereinafter  also referred to as a “exposure step”) and a step of development processing of the lithographic printing plate precursor with a processing solution (hereinafter  also referred to as a “development step”).

Although the lithographic printing plate precursor for use in the invention can be subjected to image recording by a method of scanning exposure of digital data by laser  for example  visible laser or infrared laser or a method of exposing through a transparent original having an image recorded using a light source  for example  a halogen lamp or a high pressure mercury lamp  the method of scanning exposure of digital data by laser  for example  visible laser or infrared laser is preferred.
The wavelength of the exposure light source is preferably from 300 to 450 nm or from 750 to 1 400 nm. In case of exposing with light of 300 to 450 nm  the lithographic printing plate precursor having an image-recording layer containing a sensitizing dye having an absorption maximum in such a wavelength range is used. In case of exposing with light of 750 to 1 400 nm  the lithographic printing plate precursor containing an infrared absorbing agent which is a sensitizing dye having an absorption maximum in such a wavelength range is used. As the light source of 300 to 450 nm  a semiconductor laser is preferably used. As the light source of 750 to 1 400 nm  a solid laser or semiconductor laser emitting an infrared ray is preferably used. The exposure mechanism may be any of an internal drum system  an external drum system and a flat bed system.

After the exposure  the lithographic printing plate precursor for use in the invention is developed with water or an aqueous solution having pH from 2 to 14 (processing with developer) or developed with dampening water and ink on a printing machine (on-press development).
(Processing with developer)
The processing with developer is ordinarily practiced according to the following steps: (1) removing the non-image area with a developer  (2) conducting gumming solution treatment and (3) drying in a drying step. Although the lithographic printing plate precursor for use in the invention can be developed according to the conventional steps described above (conventional development)  it is preferred to conduct steps (1) and (2) simultaneously (simple development). In any of the development methods  a water washing step for removing a protective layer may be provided before step (1). The development of step (1) is conducted according to a conventional manner at temperature approximately from 0 to 60?C  preferably from 15 to 40?C  using  for example  a method wherein the imagewise exposed lithographic printing plate precursor is immersed in a developer and rubbed with a brush or a method wherein a developer is sprayed to the imagewise exposed lithographic printing plate precursor by a spray and the lithographic printing plate precursor is rubbed with a brush.
In case of the conventional development  a water washing step for removing an excess developer may be provided between step (1) and step (2). The developer used in step (1) is preferably a known alkali developer.
In case of the simple development  it is preferred that after the development and gumming treatment  an excess developer is removed using a squeeze roller and then drying is conducted.
The developer for use in the simple development is an aqueous solution having pH from 2 to 11. An aqueous solution containing water as the main component (containing 60% by weight or more of water) is preferred. In particular  an aqueous solution containing a surfactant (for example  an anionic  nonionic  cationic or amphoteric surfactant) or an aqueous solution containing a water-soluble polymer compound is preferred. An aqueous solution containing both the surfactant and the water-soluble polymer compound is also preferred. The pH of the developer is preferably from 5 to 10.7  more preferably from 6 to 10.5  and most preferably from 7.5 to 10.3.
The anionic surfactant for use in the developer for the simple development is not particularly limited and includes  for example  fatty acid salts  abietic acid salts  hydroxyalkanesulfonic acid salts  alkanesulfonic acid salts  dialkylsulfosuccinic acid salts  straight-chain alkylbenzenesulfonic acid salts  branched alkylbenzenesulfonic acid salts  alkylnaphthalenesulfonic acid salts  alkyldiphenylether (di)sulfonic acid salts  alkylphenoxy polyoxyethylene propylalkylsulfonic acid salts  polyoxyethylene alkylsulfophenyl ether salts  N-methylalkyl-N-oleyltaurine sodium salt  N-alkylsulfosuccinic acid monoamide disodium salts  petroleum sulfonic acid salts  sulfated castor oil  sulfated beef tallow oil  sulfate ester slats of fatty acid alkyl ester  alkyl sulfate ester salts  polyoxyethylene alkyl ether sulfate ester salts  fatty acid monoglyceride sulfate ester salts  polyoxyethylene alkyl phenyl ether sulfate ester salts  polyoxyethylene styryl phenyl ether sulfate ester salts  alkyl phosphate ester salts  polyoxyethylene alkyl ether phosphate ester salts  polyoxyethylene alkyl phenyl ether phosphate ester salts  partially saponified products of styrene-maleic anhydride copolymer  partially saponified products of olefin-maleic anhydride copolymer and naphthalene sulfonate formalin condensates. Of the compounds  alkylbenzenesulfonic acid salts  alkylnaphthalenesulfonic acid salts and alkyldiphenylether (di)sulfonic acid salts are particularly preferably used.
The cationic surfactant for use in the developer for the simple development is not particularly limited and conventionally known cationic surfactants can be used. Examples of the cationic surfactant include alkylamine salts  quaternary ammonium salts  alkylimidazolinium salts  polyoxyethylene alkyl amine salts and polyethylene polyamine derivatives.
The nonionic surfactant for use in the developer for the simple development is not particularly limited and includes  for example  polyethylene glycol type higher alcohol ethylene oxide adducts  alkylphenol ethylene oxide adducts  alkylnaphthol ethylene oxide adducts  phenol ethylene oxide adducts  naphthol ethylene oxide adducts  fatty acid ethylene oxide adducts  polyhydric alcohol fatty acid ester ethylene oxide adducts  higher alkylamine ethylene oxide adducts  fatty acid amide ethylene oxide adducts  ethylene oxide addacts of fat  polypropylene glycol ethylene oxide adducts  dimethylsiloxane-ethylene oxide block copolymers  dimethylsiloxane-(propylene oxide-ethylene oxide) block copolymers  fatty acid esters of polyhydric alcohol type glycerol  fatty acid esters of pentaerythritol  fatty acid esters of sorbitol and sorbitan  fatty acid esters of sucrose  alkyl ethers of polyhydric alcohols and fatty acid amides of alkanolamines. Of the compounds  those having an aromatic ring and an ethylene oxide chain are preferred and alkyl-substituted or unsubstituted phenol ethylene oxide adducts and alkyl-substituted or unsubstituted naphthol ethylene oxide adducts are more preferred.
The amphoteric surfactant for use in the developer for the simple development is not particularly limited and includes  for example  amine oxide type  for example  alkyldimethylamine oxide  betaine type  for example  alkyl betaine  and amino acid type  for example  sodium salt of alkylamino fatty acid. In particular  alkyldimethylamine oxide which may have a substituent  alkyl carboxy betaine which may have a substituent and alkyl sulfo betaine which may have a substituent are preferably used. Specific examples of the amphoteric surfactant include compounds described in Paragraph Nos. [0255] to [0278] and compounds represented by formula (2) in Paragraph No. [0256] of JP-A-2008-203359  compounds described in Paragraph Nos. [0028] to [0052] and compounds represented by formulae (I)  (II) and (VI) in Paragraph No. [0028] of JP-A-2008-276166 and compounds described in Paragraph Nos. [0022] to [0029] of JP-A-2009-47927.
Two or more of the surfactants may be used in combination. The content of the surfactant in the developer is preferably from 0.01 to 20% by weight  and more preferably from 0.1 to 10% by weight.
The water-soluble polymer compound for use in the developer for the simple development includes  for example  soybean polysaccharide  modified starch  gum arabic  dextrin  a cellulose derivative (for example  carboxymethyl cellulose  carboxyethyl cellulose or methyl cellulose) or a modified product thereof  pllulan  polyvinyl alcohol or a derivative thereof  polyvinyl pyrrolidone  polyacrylamide  an acrylamide copolymer  a vinyl methyl ether/maleic anhydride copolymer  a vinyl acetate/maleic anhydride copolymer  a styrene/maleic anhydride copolymer  polyvinylsulfonic acid or a salt thereof and polystyrenesulfonic acid or a salt thereof.
As the soybean polysaccharide  known soybean polysaccharide can be used. For example  as a commercial product  SOYAFIVE (trade name  produced by Fuji Oil Co.  Ltd.) is available and various grade products can be used. The soybean polysaccharide preferably used is that having viscosity in a range from 10 to 100 mPa/sec in the 10% by weight aqueous solution thereof.
As the modified starch  known modified starch can be used. The modified starch can be prepared  for example  by a method wherein starch  for example  of corn  potato  tapioca  rice or wheat is decomposed  for example  with an acid or an enzyme to an extent that the number of glucose residue per molecule is from 5 to 30 and then oxypropylene is added thereto in an alkali.
Two or more of the water-soluble polymer compounds may be used in combination. The content of the water-soluble polymer compound in the developer is preferably from 0.1 to 20% by weight  and more preferably from 0.5 to 10% by weight.
Into the developer for use in the simple development  a pH buffer agent may further be incorporated.
As the pH buffer agent according to the invention  any pH buffer agent exhibiting a pH buffer function at pH from 2 to 11 can be preferably used. In the invention  a weak alkaline buffer agent is preferably used and includes  for example  (a) a carbonate ion and a hydrogen carbonate ion  (b) a borate ion  (c) a water-soluble amine compound and an ion of the water-soluble amine compound  and combinations thereof. Specifically  for example  (a) a combination of a carbonate ion and a hydrogen carbonate ion  (b) a borate ion  or (c) a combination of a water-soluble amine compound and an ion of the water-soluble amine compound exhibits a pH buffer function in the developer to prevent fluctuation of the pH even when the developer is used for a long period of time. As a result  for example  the deterioration of development property resulting from the fluctuation of pH and the occurrence of development scum are restrained. The combination of a carbonate ion and a hydrogen carbonate ion is particularly preferred.
In order for a carbonate ion and a hydrogen carbonate ion to be present in the developer  a carbonate and a hydrogen carbonate may be added to the developer or a carbonate ion and a hydrogen carbonate ion may be generated by adding a carbonate or a hydrogen carbonate to the developer and then adjusting the pH. The carbonate or hydrogen carbonate used is not particularly restricted and it is preferably an alkali metal salt thereof. Examples of the alkali metal include lithium  sodium and potassium and sodium is particularly preferable. The alkali metals may be used individually or in combination of two or more thereof.
When the combination of (a) a carbonate ion and a hydrogen carbonate ion is adopted as the pH buffer agent  the total amount of the carbonate ion and hydrogen carbonate ion is preferably from 0.05 to 5 mole/l  more preferably from 0.1 to 2 mole/l  particularly preferably from 0.2 to 1 mole/l  in the developer.
The developer for use in the simple development may contain an organic solvent. As the organic solvent to be contained  for example  an aliphatic hydrocarbon (e.g.  hexane  heptane  Isopar E  Isopar H  Isopar G (produced by Esso Chemical Co.  Ltd.)  gasoline or kerosene)  an aromatic hydrocarbon (e.g.  toluene or xylene)  a halogenated hydrocarbon (methylene dichloride  ethylene dichloride  trichlene or monochlorobenzene) or a polar solvent is exemplified. Examples of the polar solvent include an alcohol (e.g.  methanol  ethanol  propanol  isopropanol  1-butanol  1-pentanol  1-hexanol  1-heptanol  1-octanol  2-octanol  2-ethyl-1-hexanol  1-nonanol  1-decanol  benzyl alcohol  ethylene glycol monomethyl ether  2-ethyoxyethanol  diethylene glycol monoethyl ether  diethylene glycol monohexyl ether  triethylene glycol monomethyl ether  propylene glycol monoethyl ether  propylene glycol monomethyl ether  polyethylene glycol monomethyl ether  polypropylene glycol  tetraethylene glycol  ethylene glycol monobutyl ether  ethylene glycol monobenzyl ether  ethylene glycol monophenyl ether  propylene glycol monophenyl ether  methyl phenyl carbinol  n-amyl alcohol or methylamyl alcohol)  a ketone (e.g.  acetone  methyl ethyl ketone  ethyl butyl ketone  methyl isobutyl ketone or cyclohexanone)  an ester (e.g.  ethyl acetate  propyl acetate  butyl acetate  amyl acetate  benzyl acetate  methyl lactate  butyl lactate  ethylene glycol monobutyl acetate  polyethylene glycol monomethyl ether acetate  diethylene glycol acetate  diethyl phthalate or butyl levulinate) and others (e.g.  triethyl phosphate  tricresyl phosphate  N-phenylethanolamine  N-phenyldiethanolamine  N-methyldiethanolamine  N-ethyldiethanolamine  4-(2-hydroxyethyl)morpholine  N N-dimethylacetamide or N-methylpyrrolidone). Two or more organic solvents may be used in combination.
Further  when the organic solvent is insoluble in water  it may be employed by being solubilized in water using a surfactant or the like. In the case where the developer contains an organic solvent  the concentration of the organic solvent is desirably less than 40% by weight in view of safety and inflammability.
The developer may contain a preservative  a chelating agent  a defoaming agent  an organic acid  an inorganic acid  an inorganic salt or the like in addition the components described above. Specifically  compounds described in Paragraph Nos. [0266] to [0270] of JP-A-2007-206217 are preferably used.
The developer described above can be used as a developer and a development replenisher for the exposed negative lithographic printing plate precursor and it is preferably applied to an automatic processor described hereinafter. In the case of conducting the development processing using an automatic processor  the processing solution becomes fatigued in accordance with the processing amount  and hence the processing ability may be restored using a replenisher or a fresh developer.
The development processing using the developer having pH from 2 to 11 according to the invention is preferably performed by an automatic processor equipped with a supplying means for the developer and a rubbing member. An automatic processor using a rotating brush roll as the rubbing member is particularly preferred. Further  the automatic processor is preferably provided with a means for removing the excess developer  for example  a squeeze roller or a drying means  for example  a hot air apparatus  subsequently to the development processing means.
Further  in the plate making process of preparing a lithographic printing plate from the lithographic printing plate precursor according to the invention  the lithographic printing plate precursor may be heated its entire surface before or during the exposure or between the exposure and the development  if desired. By the heating  the image-forming reaction in the image-recording layer is accelerated and advantages  for example  improvement in the sensitivity and printing durability and stabilization of the sensitivity are achieved. For the purpose of increasing the image strength and printing durability  it is also effective to perform entire after-heating or entire exposure of the image after the development. Ordinarily  the heating before the development is preferably performed under a mild condition of 150?C or lower. When the temperature is too high  a problem may arise sometimes in that the unexposed area is also cured. On the other hand  the heating after the development can be performed using very strong conditions. Ordinarily  the heat treatment is carried out in a temperature range from 100 to 500?C. When the temperature is too low  a sufficient effect of strengthening the image may not be obtained  whereas when it is excessively high  problems of deterioration of the support and thermal decomposition of the image area may occur sometimes.
(On-press development method)
The lithographic printing plate precursor according to the invention can also be subjected to the plate making by an on-press development method. The on-press development method includes a step in which the lithographic printing plate precursor is imagewise exposed and a printing step in which oily ink and an aqueous component are supplied to the exposed lithographic printing plate precursor without undergoing any development processing to perform printing  and it is characterized in that the unexposed area of the lithographic printing plate precursor is removed in the course of the printing step. The imagewise exposure may be performed on a printing machine after the lithographic printing plate precursor is mounted on the printing machine or may be separately performed using a platesetter or the like. In the latter case  the exposed lithographic printing plate precursor is mounted as it is on a printing machine without undergoing a development processing step. Then  the printing operation is initiated using the printing machine with supplying oily ink and an aqueous component and at an early stage of the printing the on-press development is carried out. Specifically  the image-recording layer in the unexposed area is removed and the hydrophilic surface of support is revealed therewith to form the non-image area. As the oily ink and aqueous component  printing ink and dampening water for conventional lithographic printing can be employed  respectively.
While either the dampening water or printing ink may be supplied at first on the surface of lithographic printing plate precursor  it is preferred to supply the printing ink at first in view of preventing the dampening water from contamination with the component of the image-recording layer removed.
Thus  the lithographic printing plate precursor according to the invention is subjected to the on-press development on an offset printing machine and used as it is for printing a large number of sheets.

EXAMPLES
The present invention will be described in more detail with reference to the following examples  but the invention should not be construed as being limited thereto. With respect to the polymer compounds used in the examples  unless otherwise particularly defined  a molecular weight means a weight average molecular weight (Mw) and a ratio of repeating units is indicated in mole percent.
Examples 1 to 6 and Comparative Example 1
I. Preparation of Lithographic printing plate precursors (1) to (7)
(1) Preparation of Support 1
An aluminum plate (material: JIS A 1050) having a thickness of 0.3 mm was subjected to a degreasing treatment at 50?C for 30 seconds using a 10% by weight aqueous sodium aluminate solution in order to remove rolling oil on the surface thereof and then grained the surface thereof using three nylon brushes embedded with bundles of nylon bristle having a diameter of 0.3 mm and an aqueous suspension (specific gravity: 1.1 g/cm3) of pumice having a median size of 25 µm  followed by thorough washing with water. The plate was subjected to etching by immersing in a 25% by weight aqueous sodium hydroxide solution of 45?C for 9 seconds  washed with water  then immersed in a 20% by weight aqueous nitric acid solution at 60?C for 20 seconds  and washed with water. The etching amount of the grained surface was about 3 g/m2.
Then  using an alternating current of 60 Hz  an electrochemical roughening treatment was continuously carried out on the plate. The electrolytic solution used was a 1% by weight aqueous nitric acid solution (containing 0.5% by weight of aluminum ion) and the temperature of electrolytic solution was 50?C. The electrochemical roughening treatment was conducted using an alternating current source  which provides a rectangular alternating current having a trapezoidal waveform such that the time TP necessary for the current value to reach the peak from zero was 0.8 msec and the duty ratio was 1:1  and using a carbon electrode as a counter electrode. A ferrite was used as an auxiliary anode. The current density was 30 A/dm2 in terms of the peak value of the electric current and 5% of the electric current flowing from the electric source was divided to the auxiliary anode. The quantity of electricity in the nitric acid electrolysis was 175 C/dm2 in terms of the quantity of electricity when the aluminum plate functioned as an anode. The plate was then washed with water by spraying.
The plate was further subjected to an electrochemical roughening treatment in the same manner as in the nitric acid electrolysis above using as an electrolytic solution  a 0.5% by weight aqueous hydrochloric acid solution (containing 0.5% by weight of aluminum ion) having temperature of 50?C and under the condition that the quantity of electricity was 50 C/dm2 in terms of the quantity of electricity when the aluminum plate functioned as an anode. The plate was then washed with water by spraying.
The plate was then subjected to an anodizing treatment using as an electrolytic solution  a 15% by weight aqueous sulfuric acid solution (containing 0.5% by weight of aluminum ion) at a current density of 15 A/dm2 to form a direct current anodized film of 2.5 g/m2  washed with water and dried to prepare Support 1.
The center line average roughness (Ra) of the support thus obtained was measured using a stylus having a diameter of 2 µm and found to be 0.51 µm.
(2) Formation of Undercoat layer
Coating solution (1) for undercoat layer shown below was coated on Support 1 by a bar and dried in an oven at 80?C for 10 seconds to prepare a support having an undercoat layer having a dry coating amount of 10 mg/m2.

Star polymer shown in Table 13 0.017 g
Methanol 9.00 g
Water 1.00 g

(3) Formation of Image-recording layer and Protective layer
Coating solution (1) for image-recording layer having the composition shown below was coated on the support having an undercoat layer described above by a bar and dried in an oven at 70?C for 60 seconds to form an image-recording layer having a dry coating amount of 1.1 g/m2. Coating solution (1) for protective layer having the composition shown below was coated on the image-recording layer using a bar so as to have a dry coating amount of 0.75 g/m2 and dried at 125?C for 70 seconds to form Lithographic printing plate precursors (1) to (7)  respectively.

Binder (1) shown below (weight average molecular weight: 60 000) 0.54 g
Polymerizable compound (1) shown below 0.48 g
(PLEX 6661-O  produced by Degussa Japan Co.  Ltd.)
Sensitizing dye (1) shown below 0.06 g
Polymerization initiator (1) shown below 0.18 g
Co-sensitizer (1) shown below 0.07 g
Dispersion of e-phthalocyanine pigment (1) 0.40 g
[pigment: 15 parts by weight; dispersing agent (allyl methacrylate/methacrylic acid (80/20) copolymer  Mw: 50 000): 10 parts by weight; solvent (cyclohexanone/methoxypropyl acetate/1-methoxy-2-propanol = 15 parts by weight/20 parts by weight/40 parts by weight)]
Thermal polymerization inhibitor 0.01 g
N-Nitrosophenylhydroxylamine aluminum salt
Fluorine-based surfactant (1) shown below (Mw: 13 000) 0.001 g
Polyoxyethylene-polyoxypropylene condensate
(PLURONIC L44  produced by ADEKA Corp.) 0.04 g
1-Methoxy-2-propanol 3.5 g
Methyl ethyl ketone 8.0 g

Binder (1) Sensitizing dye (1)

Mixture of the isomers described above
Polymerizable compound (1)

Polymerization initiator (1)

Co-sensitizer (1)

Fluorine-based surfactant (1)

Dispersion of mica (1) shown below 13.0 g
Polyvinyl alcohol (saponification degree: 98% by mole; polymerization degree: 500) 1.3 g
Sodium 2-ethylhexylsulfosuccinate 0.2 g
Vinyl pyrrolidone/vinyl acetate (1/1) copolymer (Mw: 70 000) 0.05 g
Surfactant (EMALEX 710  produced by Nihon-Emulsion Co.  Ltd.) 0.05 g
Water 133 g

(Preparation of Dispersion of mica (1))
To 368 g of water was added 32 g of synthetic mica (SOMASIF ME-100  produced by CO-OP Chemical Co.  Ltd.  aspect ratio: 1 000 or more) and the mixture was dispersed using a homogenizer until an average particle size (according to a laser scattering method) became 0.5 µm to prepare Dispersion of mica (1).
II. Evaluation of Lithographic printing plate precursor

(1) Condition of preparing standard lithographic printing plate
Each of Lithographic printing plate precursors (1) to (7) was subjected to imagewise exposure using a semiconductor laser of 405 nm having output of 100 mW in an exposure amount of 300 µJ/cm2.
Then  the exposed lithographic printing plate precursor was subjected to development processing in Automatic development processor (A) having a structure shown in Fig. 2 using Developer (1) having the composition shown below. Automatic development processor (A) was an automatic processor having two rotating brush rollers. The first brush roller was a brush roller having an outer diameter of 90 mm and being implanted with fiber of polybutylene terephthalate (bristle diameter: 200 µm  bristle length: 17 mm)  and the brush roller was rotated at 200 rpm (peripheral velocity at the tip of brush: 0.94 m/sec) in the same direction as the transporting direction of the lithographic printing plate precursor. The second brush roller was a brush roller having an outer diameter of 60 mm and being implanted with fiber of polybutylene terephthalate (bristle diameter: 200µm  bristle length: 17 mm)  and the brush roller was rotated at 200 rpm (peripheral velocity at the tip of brush: 0.63 m/sec) in the opposite direction to the transporting direction of the lithographic printing plate precursor. The transportation of the lithographic printing plate precursor was conducted at a transporting speed of 100 cm/min.
The developer was supplied on the surface of the lithographic printing plate precursor by showering from a spray pipe using a circulation pump. The tank volume for the developer was 10 liters. Thus  Standard lithographic printing plates (1) to (7) were prepared.
(2) Condition of preparing lithographic printing plate for evaluating development property
Each of Lithographic printing plate precursors (1) to (7) was subjected to the imagewise exposure in the same manner as in Condition of preparing standard lithographic printing plate and then subjected to the development processing in the same manner as in Condition of preparing standard lithographic printing plate except for variously changing the transporting speed of the lithographic printing plate precursor to prepare a lithographic printing plate for evaluating development property.
Developer (1)
Water 100.00 g
Benzyl alcohol 1.00 g
Polyoxyethylene naphthyl ether (average number of oxyethylene: n = 13) 1.00 g
Sodium salt of dioctylsulfosuccinate 0.50 g
Gum arabic 1.00 g
Ethylene glycol 0.50 g
Ammonium primary phosphate 0.05 g
Citric acid 0.05 g
Sodium carbonate 1.40 g
Sodium hydrogen carbonate 0.59 g

(pH of the developer was adjusted to 9.8 using phosphoric acid and sodium hydroxide)

The lithographic printing plate obtained was mounted on a printing machine (SOR-M  produced by Heidelberg) and printing was conducted at a printing speed of 6 000 sheets per hour using dampening water (EU-3 (etching solution  produced by FUJIFILM Corp.))/water/isopropyl alcohol = 1/89/10 (by volume ratio)) and TRANS-G (N) Black Ink (produced by Dainippon Ink & Chemicals  Inc.).

The development property  stain resistance and printing durability were evaluated in the manner described below. The results obtained are shown in Table 13.
(1) Stain resistance
Using the standard lithographic printing plate  the printing of 500 sheets was conducted under the condition described above. On the 500th sheet of the printed material  ink satin generated in the non-image area was visually observed to evaluate the stain resistance on a 1 to 10 bases  1 being a case where due to adhesion of ink the non-image area was almost stained and 10 being a case where the non-image area did not stained at all. In case this evaluation point is less than 9  it cannot be practically used as a lithographic printing plate.
(2) Printing durability
The printing was continued under the condition described above using the standard lithographic printing plate and a number of printed materials obtained until the ink density (reflection density) on the printing paper decreased by 0.1 from that at the initiation of printing was determined to evaluate the printing durability.
(3) Development property
With the lithographic printing plate for evaluating development property  cyan density of the non-image area was measured by a Macbeth densitometer. The transporting speed (cm/min) at which the cyan density of the non-image area became equivalent to cyan density of the aluminum support was determined to evaluate the development property.
TABLE 13
Lithographic Printing Plate Precursor Star Polymer Printing Durability
(sheets) Development Property (cm/min) Stain Resistance
Example 1 (1) P-1 8 x 104 105 10
Example 2 (2) P-2 9 x 104 105 10
Example 3 (3) P-3 9 x 104 115 10
Example 4 (4) P-4 9 x 104 120 10
Example 5 (5) P-5 10 x 104 150 10
Example 6 (6) P-6 10 x 104 145 10
Comparative Example 1 (7) Comparative Polymer C-1 7 x 104 100 7

Comparative polymer C-1 (Mw: 60 000)

Example 7 and Comparative Example 2
I. Preparation of Lithographic printing plate precursors (8) and (9)
(1) Preparation of Support 2
An aluminum plate of JIS A1050 having a thickness of 0.30 mm and a width of 1 030 mm was continuously subjected to surface treatment according to various processes (a) to (f) shown below. After each process and water washing  removal of liquid was conducted with a nip roller.
(a) Alkali etching treatment of the aluminum plate was conducted by spraying an aqueous solution having sodium hydroxide concentration of 26% by weight  aluminum ion concentration of 6.5% by weight and temperature of 70?C to dissolve the aluminum plate in an amount of 5 g/m2. Subsequently  the plate was washed with water.
(b) Desmut treatment of the aluminum plate was conducted by spraying an aqueous 1% by weight nitric acid solution (containing 0.5% by weight of aluminum ion) having temperature of 30?C. Subsequently  the plate was washed with water.
(c) Electrochemical surface roughening treatment of the aluminum plate was continuously conducted by applying 60 Hz alternating current voltage. The electrolytic solution used was an aqueous 1% by weight nitric acid solution (containing 0.5% by weight of aluminum ion and 0.007% by weight of ammonium ion) and the solution temperature was 30?C. The electrochemical surface roughening treatment was conducted using a trapezoidal rectangular wave alternating current where time (TP) for reaching the current to its peak from zero was 0.8 msec and a duty ratio was 1:1 as an alternating current source  and using a carbon electrode as a counter electrode. A ferrite was used as an auxiliary anode. The current density was 25 A/dm2 at the peak current  and the electric quantity was 250 C/dm2 in terms of the total electric quantity during the aluminum plate functioning as an anode. To the auxiliary anode  5% of the current flowing from the electric source was divided. Subsequently  the plate was washed with water.
(d) Alkali etching treatment of the aluminum plate was conducted at 35?C by spraying an aqueous solution having a sodium hydroxide concentration of 26% by weight and an aluminum ion concentration of 6.5% by weight to dissolve the aluminum plate in an amount of 0.2 g/m2. Thus  the smut component mainly comprising aluminum hydroxide formed in the precedent process of electrochemical surface roughening treatment using alternating current was removed and an edge portion of the pit formed was dissolved to smoothen the edge portion. Subsequently  the plate was washed with water.
(e) Desmut treatment of the aluminum plate was conducted by spraying an aqueous 25% by weight sulfuric acid solution (containing 0.5% by weight of aluminum ion) having temperature of 60?C. Subsequently  the plate was washed with water by spraying.
(f) Anodizing treatment of the aluminum plate was conducted in an aqueous solution having sulfuric acid concentration of 170 g/liter (containing 0.5% by weight of aluminum ion) at temperature of 33?C and an electric density of 5 A/dm2 for 50 seconds. Subsequently  the plate was washed with water. The amount of the anodic oxide film was 2.7 g/m2.
The surface roughness (Ra) of Support 2 thus-obtained was 0.27 (measuring instrument: SURFCOM having a stylus with a tip diameter of 2 µm  produced by Tokyo Seimitsu Co. Ltd. ).
(2) Formation of Undercoat layer
Coating solution (2) for undercoat layer shown below was coated on Support 2 by a wire bar and dried at 90?C for 30 seconds. The coating amount of the undercoat layer was 10 mg/m2.

Star polymer shown in Table 14 0.05 g
Methanol 27 g
Ion-exchanged water 3 g

(3) Formation of Image-recording layer
Coating solution (2) for image-recording layer shown below was prepared and coated on the support having an undercoat layer described above by a wire bar. Drying was conducted in a hot air drying apparatus at 115?C for 34 seconds to form an image-recording layer. The coverage of the image-recording layer after drying was 1.4 g/m2.

Phosphonium compound (A-6) 0.077 g
Infrared absorbing agent (IR-1) 0.074 g
Polymerization initiator (OS-12) 0.280 g
Additive (PM-1) 0.151 g
Polymerizable compound (AM-1) 1.00 g
Binder (BT-1) (Mw: 45 000) 1.00 g
Ethyl violet (C-1) 0.04 g
Fluorine-based surfactant 0.015 g
(MEGAFAC F-780-F  30% by weight methyl isobutyl ketone (MIBK) solution  produced by Dainippon Ink & Chemicals  Inc.)
Methyl ethyl ketone 10.4 g
Methanol 4.83 g
1-Methoxy-2-propanol 10.4 g

The structure of Phosphonium compound (A-6)  Polymerization initiator (OS-12)  Infrared absorbing agent (IR-1)  Additive (PM-1)  Polymerizable compound (AM-1)  Binder (BT-1) and Ethyl violet (C-1) are shown below.

(4) Formation of protective layer
An aqueous mixed solution (Coating solution (2) for protective layer) comprising synthetic mica (SOMASIF ME-100  8% by weight aqueous dispersion  produced by CO-OP Chemical Co.  Ltd.)  polyvinyl alcohol (PVA-205  produced by Kuraray Co.  Ltd.) and a surfactant (EMALEX 710  produced by Nihon-Emulsion Co.  Ltd.) was coated on the image-recording layer described above by a wire bar and dried in a hot air drying apparatus at 125?C for 75 seconds.
The content ratio of mica (solid content)/polyvinyl alcohol/surfactant in Coating solution (2) for protective layer was 16/82/2 (% by weight)  and the coating amount (coverage after drying) of the protective layer was 1.6 g/m2. Thus  Lithographic printing plate precursors (8) and (9) were prepared.
II. Evaluation of Lithographic printing plate precursor
The lithographic printing plate precursor obtained was exposed by TRENDSETTER 800II QUANTUM (produced by Creo Co.) at resolution of 2 400 dpi and a rotational number of an external drum of 200 rpm and output of 7 W. The exposure was conducted under conditions of 25?C and 50% RH. After the exposure  without conducting heat treatment and water washing  the exposed lithographic printing plate precursor was subjected to development processing using an automatic developing machine (LP-1310HII  produced by FUJIFILM Corp.) at a transporting speed (line speed) of 2 m/min and at development temperature of 30?C. The developer used was a solution prepared by diluting DH-N (produced by FUJIFILM Corp.) with water in a ratio of 1:4. The development replenisher used was a solution prepared by diluting FCT-421 (produced by FUJIFILM Corp.) with water in a ratio of 1:1.4. The finisher used was a solution prepared by diluting GN-2K (produced by FUJIFILM Corp.) with water in a ratio of 1:1.

Using the lithographic printing plate obtained by the plate making described above  the printing was conducted in the same manner as in Example 1 and a number of printed materials obtained until the ink density (reflection density) on the printing paper decreased by 0.1 from that at the initiation of printing was determined to evaluate the printing durability. The results obtained are shown in Table 14.

Using the lithographic printing plate obtained by the plate making described above  the stain resistance was also evaluated in the same manner as in Example 1. The results obtained are shown in Table 14.

With the lithographic printing plates obtained by changing the transporting speed (line speed) of the lithographic printing plate precursor in the automatic developing machine LP-1310HII  cyan density of the non-image area was measured by a Macbeth densitometer in the same manner as in Example 1. The transporting speed (cm/min) at which the cyan density of the non-image area became equivalent to cyan density of the aluminum support was determined to evaluate the development property. The results obtained are shown in Table 14.

TABLE 14
Lithographic Printing Plate Precursor Star Polymer Printing Durability
(sheets) Development Property (cm/min) Stain Resistance
Example 7 (8) P-61 2.5 x 104 150 10
Comparative Example 2 (9) Comparative Polymer C-2 1.5 x 104 100 8

Comparative polymer C-2 (Mw: 55 000)

Example 8 and Comparative Example 3
I. Preparation of Lithographic printing plate precursors (10) and (11)
(1) Preparation of Support 3
An aluminum plate (material: JIS A 1050  refining: H16) having a thickness of 0.24 mm was immersed in an aqueous 5% by weight sodium hydroxide solution maintained at 65?C to conduct a degreasing treatment for one minute  followed by washed with water. The degreased aluminum plate was immersed in an aqueous 10% by weight hydrochloric acid solution maintained at 25?C for one minute to neutralize  followed by washed with water. Subsequently  the aluminum plate was subjected to an electrolytic surface-roughening treatment with alternating current under condition of current density of 100 A/dm2 in an aqueous 0.3% by weight hydrochloric acid solution at 25?C for 60 seconds and then subjected to a desmut treatment in an aqueous 5% by weight sodium hydroxide solution maintained at 60?C for 10 seconds. The surface-roughened and desmuted aluminum plate was subjected to an anodizing treatment under condition of current density of 10 A/dm2 and voltage of 15 V in an aqueous 15% by weight sulfuric acid solution at 25?C for one minute and then subjected to a hydrophilizing treatment using an aqueous 1% by weight solution of the star polymer shown in Table 15 at 75?C to prepare Support 3. The surface roughness of the support was measured and found to be 0.44 µm (Ra indication according to JIS B0601).
(2) Formation of Image-recording layer
Coating solution (3) for image-recording layer having the composition shown below was coated on Support 3 described above using a bar and dried in an oven at 90?C for 60 seconds to form an image-recording layer having a dry coating amount of 1.3 g/m2.

Binder (2) (Mw: 50 000) shown below 0.04 g
Binder (3) (Mw: 80 000) shown below 0.30 g
Polymerizable compound (1) shown above 0.17 g
Polymerizable compound (2) shown below 0.51 g
Sensitizing dye (2) shown below 0.03 g
Sensitizing dye (3) shown below 0.015 g
Sensitizing dye (4) shown below 0.015 g
Polymerization initiator (1) shown above 0.13 g
Chain transfer agent 0.01 g
Mercaptobenzothiazole
Dispersion (2) of e-phthalocyanine pigment 0.40 g
(pigment: 15 parts by weight; dispersing agent (allyl methacrylate/methacrylic acid copolymer (weight average molecular weight: 60 000  copolymerization molar ratio: 83/17)): 10 parts by weight; cyclohexanone: 15 parts by weight)
Thermal polymerization inhibitor 0.01 g
N-Nitrosophenylhydroxylamine aluminum salt
Fluorine-based surfactant (1) shown above 0.001 g
1-Methoxy-2-propanol 3.5 g
Methyl ethyl ketone 8.0 g

Binder (2) (acid value: 85 mg KOH/g)

Binder (3) (acid value: 66 mg KOH/g)

Polymerizable compound (2)

Sensitizing dye (2)

Sensitizing dye (3)

Sensitizing dye (4)

(3) Formation of Protective layer
Coating solution (3) for protective layer having the composition shown below was coated on the image-recording layer described above using a bar so as to have a dry coating amount of 1.2 g/m2 and dried at 125?C for 70 seconds to form a protective layer  thereby preparing Lithographic printing plate precursors (10) and (11).

PVA-205 (partially hydrolyzed polyvinyl alcohol  produced by Kuraray Co.  Ltd. (saponification degree: 86.5 to 89.5% by mole; viscosity: 4.6 to 5.4 mPa•s in a 4% by weight aqueous solution at 20?C)) 0.658 g
PVA-105 (fully hydrolyzed polyvinyl alcohol  produced by Kuraray Co.  Ltd. (saponification degree: 98.0 to 99.0% by mole; viscosity: 5.2 to 6.0 mPa•s in a 4% by weight aqueous solution at 20?C)] 0.142 g
Vinyl pyrrolidone/vinyl acetate (1/1) copolymer (weight average molecular weight: 70 000) 0.001 g
Surfactant (EMALEX 710  produced by Nihon Emulsion Co.  Ltd.) 0.002 g
Water 13 g

(4) Exposure  Development and Printing
The lithographic printing plate precursor was subjected to image exposure by Violet semiconductor laser plate setter Vx9600 (equipped with InGaN semiconductor laser; emission: 405 nm ± 10 nm/output: 30 mW) produced by FUJIFILM Electronic Imaging  Ltd. The image drawing was conducted at a resolution of 2 438 dpi with halftone dots of 50% using an FM screen (TAFFETA 20  produced by FUJIFILM Corp.) under condition of a plate surface exposure amount of 0.05 mJ/cm2.
Then  the exposed lithographic printing plate precursor was subjected to development processing by Automatic development processor (B) having a structure shown in Fig. 3 using Developer (2) having the composition shown below at a transporting speed so as to regulate preheating time at 100?C of 10 seconds and immersion time (developing time) in the developer of 20 seconds. Also  for the purpose of evaluating the development property  the development was conducted with variously changing the immersion time.
The lithographic printing plate thus-obtained was mounted on a printing machine (SOR-M  produced by Heidelberg) and printing was conducted at a printing speed of 6 000 sheets per hour using dampening water (EU-3 (etching solution  produced by FUJIFILM Corp.))/water/isopropyl alcohol = 1/89/10 (by volume ratio)) and TRANS-G (N) Black Ink (produced by Dainippon Ink & Chemicals  Inc.).

Water 88.6 g
Nonionic surfactant (W-1) having structure
shown below
2.4 g
Nonionic surfactant (W-2) having structure
shown below
2.4 g
Nonionic surfactant (EMALEX 710  produced by
Nihon Emulsion Co.  Ltd.)
1.0 g
Phenoxypropanol 1.0 g
Octanol 0.6 g
N-(2-Hydroxyethyl)morpholine 1.0 g
Triethanolamine 0.5 g
Sodium gluconate 1.0 g
Trisodium citrate 0.5 g
Tetrasodium ethylenediaminetetraacetate 0.05 g
Polystyrenesulfonic acid (VERSA TL77 (30% solution) produced by Alco Chemical Inc.)
1.0 g
(pH was adjusted to 7.0 by adding phosphoric acid)

II. Evaluation of Lithographic printing plate precursor

The lithographic printing plate precursor was subjected to the image exposure and development processing as described above. After the development processing  the non-image area of the lithographic printing plate obtained was visually observed and the immersion time in the developer for which the image-recording layer did not remain to obtain good development property was determined to evaluate the development property.

As increase in the number of printed materials  the image of the image-recording layer formed on the lithographic printing plate was gradually abraded to cause decrease in the ink receptivity  resulting in decrease in ink density of the image on a printing paper. A number of printed materials obtained until the ink density (reflection density) decreased by 0.1 from that at the initiation of printing was determined to evaluate the printing durability.

The printing was conducted as described above and on the 3 000th sheet of the printed material  the stain resistance was evaluated according to the following criteria:
A: Ink stain was not observed in the non-image area.
B: Slight ink stain was observed in the non-image area.
TABLE 15
Lithographic Printing Plate Precursor Star Polymer Printing Durability
(sheets) Development Property (sec) Stain Resistance
Example 8 (10) P-62 9 x 104 20 A
Comparative Example 3 (11) Comparative Polymer C-2 7 x 104 30 B

Examples 9 to 68 and Comparative Example 4
I. Preparation of Lithographic printing plate precursors (12) and (72)
(1) Preparation of Support 4
In order to ensure the hydrophilicity of the non-image area  Support 1 described above was subjected to silicate treatment using a 2.5% by weight aqueous sodium silicate No. 3 solution at 60?C for 10 seconds and subsequently washed with water to obtain Support 4. The adhesion amount of Si was 10 mg/m2. The center line average roughness (Ra) of the support was measured using a stylus having a diameter of 2 µm and found to be 0.51 µm.
(2) Formation of Undercoat layer
Coating solution (3) for undercoat layer shown below was coated on Support 4 described above so as to have a dry coating amount of 20 mg/m2 to prepare a support having an undercoat layer.

Star polymer shown in Table 16 0.18 g
Hydroxyethyliminodiacetic acid 0.10 g
Methanol 55.24 g
Water 6.15 g

(3) Formation of Image-recording layer
Coating solution (4) for image-recording layer having the composition shown below was coated on the undercoat layer formed as described above by a bar and dried in an oven at 100?C for 60 seconds to form an image-recording layer having a dry coating amount of 1.0 g/m2.
Coating solution (4) for image-recording layer was prepared by mixing Photosensitive solution (1) shown below with Microgel solution (1) shown below just before the coating  followed by stirring.

Binder (4) shown below 0.240 g
Infrared absorbing dye (1) having structure shown above 0.030 g
Radical polymerization initiator (2) having structure shown above 0.162 g
Radical polymerizable compound (Tris(acryloyloxyethyl) isocyanurate (NK ESTER A-9300  produced by Shin-Nakamura Chemical Co.  Ltd.)) 0.192 g
Hydrophilic low molecular weight compound (Tris(2-hydroxyethyl) isocyanurate) 0.062 g
Hydrophilic low molecular weight compound (1) having structure shown below 0.050 g
Oil-sensitizing agent (Phosphonium compound (1) having structure shown below) 0.055 g
Oil-sensitizing agent (Benzyl dimethyl octyl ammonium PF6 salt) 0.018 g
Oil-sensitizing agent (Ammonium group-containing polymer having structure shown below (reduced specific viscosity: 44 ml/g) 0.035 g
Fluorine-based surfactant (1) described above 0.008 g
Methyl ethyl ketone 1.091 g
1-Methoxy-2-propanol 8.609 g

Microgel (1) shown below 2.640 g
Distilled water 2.425 g

The structures of Binder (4)  Infrared absorbing dye (1)  Radical polymerization initiator (2)  Phosphonium compound (1)  Hydrophilic low molecular weight compound (1) and Oil-sensitizing agent (ammonium group-containing polymer) are shown below.

Infrared absorbing agent (1)

Radical polymerization initiator (2)

Phosphonium compound (1)

Hydrophilic low molecular weight compound (1)

Ammonium group-containing polymer

(Mw: 70 000)
Binder (4)

An oil phase component was prepared by dissolving 10 g of adduct of trimethylol propane and xylene diisocyanate (TAKENATE D-110N  produced by Mitsui Chemicals  Inc.)  3.15 g of pentaerythritol triacrylate (SR444  produced by Nippon Kayaku Co.  Ltd.) and 0.1 g of PIONIN A-41C (produced by Takemoto Oil & Fat Co.  Ltd.) in 17 g of ethyl acetate. As an aqueous phase component  40 g of a 4% by weight aqueous solution of polyvinyl alcohol (PVA-205  produced by Kuraray Co.  Ltd.) was prepared. The oil phase component and the aqueous phase component were mixed and emulsified using a homogenizer at 12 000 rpm for 10 minutes. The resulting emulsion was added to 25 g of distilled water and stirred at room temperature for 30 minutes and then at 50?C for 3 hours. The microgel liquid thus-obtained was diluted using distilled water so as to have the solid content concentration of 15% by weight to prepare Microgel (1). The average particle size of the microgel was measured by a light scattering method and found to be 0.2 µm.
(4) Formation of Protective layer
Coating solution (4) for protective layer having the composition shown below was coated on the image-recording layer described above by a bar and dried in an oven at 120?C for 60 seconds to form a protective layer having a dry coating amount of 0.15 g/m2  thereby preparing Lithographic printing plate precursors (12) to (72)  respectively.

Dispersion of inorganic stratiform compound (1) shown below 1.5 g
Aqueous 6% by weight solution of polyvinyl alcohol (CKS 50  sulfonic acid-modified  saponification degree: 99% by mole or more  polymerization degree: 300  produced by Nippon Synthetic Chemical Industry Co.  Ltd.) 0.55 g
Aqueous 6% by weight solution of polyvinyl alcohol (PVA-405  saponification degree: 81.5 % by mole  polymerization degree: 500  produced by Kuraray Co.  Ltd.) 0.03 g
Aqueous 1% by weight solution of surfactant (EMALEX 710  produced by Nihon Emulsion Co.  Ltd.) 0.86 g
Ion-exchanged water 6.0 g

To 193.6 g of ion-exchanged water was added 6.4 g of synthetic mica (SOMASIF ME-100  produced by CO-OP Chemical Co.  Ltd.) and the mixture was dispersed using a homogenizer until an average particle size (according to a laser scattering method) became 3 µm to prepare Dispersion of inorganic stratiform compound (1). The aspect ratio of the inorganic particle thus-dispersed was 100 or more.
II. Evaluation of Lithographic printing plate precursor

The lithographic printing plate precursor thus-obtained was exposed by LUXEL PLATESETTER T-6000III equipped with an infrared semiconductor laser produced by FUJIFILM Corp. under the conditions of a rotational number of an external drum of 1 000 rpm  laser output of 70% and resolution of 2 400 dpi. The exposed image contained a solid image and a 50% halftone dot chart of a 20 µm-dot FM screen.
The exposed lithographic printing plate precursor was mounted without undergoing development processing on a plate cylinder of a printing machine (LITHRONE 26  produced by Komori Corp.). Using dampening water (ECOLITY-2 (produced by FUJIFILM Corp.)/tap water = 2/98 (volume ratio)) and VALUES-G (N) Black Ink (produced by Dainippon Ink & Chemicals  Inc.)  the dampening water and ink were supplied according to the standard automatic printing start method of LITHRONE 26 to conduct printing on 100 sheets of TOKUBISHI ART paper (76.5 kg) at a printing speed of 10 000 sheets per hour.
A number of the printing papers required until the on-press development of the unexposed area of the image-recording layer on the printing machine was completed to reach a state where the ink was not transferred to the printing paper in the non-image area was measured to evaluate the on-press development property. The results obtained are shown in Table 16.

After performing the evaluation for the on-press development property described above  the printing was continued. As the increase in a number of printing papers  the image-recording layer was gradually abraded to cause decrease in the ink density on a printed material. A number of printed materials wherein a value obtained by measuring a halftone dot area rate of the 50% halftone dot of FM screen on the printed material using a Gretag densitometer decreased by 5% from the value measured on the 100th printed material of the printing was determined to evaluate the printing durability. The results obtained are shown in Table 16.

After performing the evaluation for the on-press development property described above  the printing was continued. On the 500th sheet of the printed material  ink satin generated in the non-image area was visually observed to evaluate the stain resistance on a 1 to 10 bases  1 being a case where due to adhesion of ink the non-image area was almost stained and 10 being a case where the non-image area did not stained at all. In case this evaluation point is less than 9  it cannot be practically used as a lithographic printing plate.

TABLE 16
Lithographic Printing Plate Precursor Star Polymer Printing Durability
(sheets) Development Property (sheets) Stain Resistance
Example 9 (12) P-1 4.70 x 104 8 10
Example 10 (13) P-2 4.66 x 104 8 10
Example 11 (14) P-3 4.79 x 104 9 10
Example 12 (15) P-4 4.76 x 104 9 10
Example 13 (16) P-5 5.00 x 104 8 10
Example 14 (17) P-6 4.94 x 104 8 10
Example 15 (18) P-7 4.67 x 104 8 10
Example 16 (19) P-8 4.61 x 10 4 8 10
Example 17 (20) P-9 4.69 x 10 4 9 10
Example 18 (21) P-10 4.71 x 10 4 8 10
Example 19 (22) P-11 4.77 x 10 4 10 10
Example 20 (23) P-12 4.75 x 10 4 9 10
Example 21 (24) P-13 4.74 x 10 4 10 10
Example 22 (25) P-14 4.93 x 10 4 9 10
Example 23 (26) P-15 4.97 x 10 4 8 10
Example 24 (27) P-16 4.84 x 10 4 10 10
Example 25 (28) P-17 4.89 x 10 4 8 10
Example 26 (29) P-18 4.91 x 10 4 8 10
Example 27 (30) P-19 4.82 x 10 4 9 10
Example 28 (31) P-20 4.81 x 10 4 10 10
Example 29 (32) P-21 4.80 x 10 4 8 10
Example 30 (33) P-22 4.86 x 10 4 10 10
Example 31 (34) P-23 4.87 x 10 4 8 10
Example 32 (35) P-24 4.83 x 10 4 8 10
Example 33 (36) P-25 4.85 x 10 4 9 10
Example 34 (37) P-26 4.99 x 10 4 9 10
Example 35 (38) P-27 4.95 x 10 4 10 10
Example 36 (39) P-28 4.98 x 10 4 8 10
Example 37 (40) P-29 4.63 x 10 4 8 10
Example 38 (41) P-30 4.77 x 10 4 10 10
Example 39 (42) P-31 4.96 x 10 4 8 10
Example 40 (43) P-32 4.92 x 10 4 9 10
Example 41 (44) P-33 4.88 x 10 4 8 10
Example 42 (45) P-34 4.90 x 10 4 10 10
Example 43 (46) P-35 4.25 x 10 4 11 10
Example 44 (47) P-36 4.30 x 10 4 11 10
Example 45 (48) P-37 4.40 x 10 4 12 10
Example 46 (49) P-38 4.35 x 10 4 11 10
Example 47 (50) P-39 4.60 x 10 4 12 10
Example 48 (51) P-40 4.47 x 10 4 11 10
Example 49 (52) P-41 4.57 x 10 4 13 10
Example 50 (53) P-42 4.42 x 10 4 13 10
Example 51 (54) P-43 4.53 x 10 4 12 10
Example 52 (55) P-44 4.50 x 10 4 13 10
Example 53 (56) P-45 4.48 x 10 4 12 10
Example 54 (57) P-46 4.41 x 10 4 13 10
Example 55 (58) P-47 4.54 x 10 4 12 10
Example 56 (59) P-48 4.44 x 10 4 12 10
Example 57 (60) P-49 4.59 x 10 4 13 10
Example 58 (61) P-50 4.46 x 10 4 11 10
Example 59 (62) P-51 4.15 x 10 4 13 10
Example 60 (63) P-52 4.21 x 10 4 13 10
Example 61 (64) P-53 4.23 x 10 4 13 10
Example 62 (65) P-54 4.18 x 10 4 13 10
Example 63 (66) P-55 4.24 x 10 4 14 10
Example 64 (67) P-56 4.15 x 10 4 13 10
Example 65 (68) P-57 4.22 x 10 4 14 10
Example 66 (69) P-58 4.00 x 10 4 15 10
Example 67 (70) P-59 4.07 x 10 4 14 10
Example 68 (71) P-60 4.05 x 10 4 15 10
Comparative Example 4 (72) Comparative Polymer C-1 3.0 x 104 20 8

Example 69 and Comparative Example 5
I. Preparation of Lithographic printing plate precursors (73) and (74)
Coating solution (5) for image-recording layer shown below was applied to an aluminum substrate subjected to brush graining  anodizing with phosphoric acid and hydrophilizing treatment by immersing in an aqueous 1% by weight solution of the star polymer shown in Table 17 at 75?C for one minute using a wire wound rod and dried in a Ranar conveyor oven set at 90?C for about 90 seconds. The dry coating amount of the image-recording layer obtained was 1.5 g/m2.

Urethane acrylate 2.48 g
Copolymer 1 13.53 g
Copolymer 2 3.97 g
Infrared absorbing dye (2) having structure shown below 0.13 g
Polymerization initiator (IRGACURE 250  produced by Ciba Specialty Chemicals  Inc.) 0.42 g
Mercapto-3-triazole 0.18 g
BYK 336 (produced by BYK-Chemie GmbH) 0.60 g
KLUCEL M (produced by Hercules Chemical Co.  Inc.) 3.31 g
n-Propanol 61.97 g
Ion-exchanged water 13.41 g

The compounds in the coating solution for image-recording layer above are shown below.
* Urethane acrylate: 80% by weight 2-butanone solution of urethane acrylate obtained by a reaction of DESMODUR N100 with hydroxyethyl acrylate and pentaerythritol triacrylate
* Copolymer 1: A mixture of 54 g of n-propanol and 16 g of deionized water was set in a 250-ml flask and heated to 70?C while purging with continuous nitrogen gas flow and stirring with a mechanical stirrer. A mixture of 54 g of n-propanol  16 g of deionized water  10 g of PEGMA  4.5 g of styrene  40.5 g of acrylonitrile and 0.32 g of VAZO-64 was prepared in a separate beaker and then added dropwise to the 250-ml flask over a period of 30 minutes. After 2.5 hours  0.16 g of VAZO-64 was added to the reaction mixture. The polymerization reaction was further continued for 2 hours. The polymer solution thus-obtained contained 21% by weight (solid content) of Copolymer 1.
* Copolymer 2: In 1-liter four-necked flask was set 384.1 g of 2-butanone and 8.5 g of PEGMA under nitrogen atmosphere  followed by heating to 80?C. A pre-mixture of 38.0 g of allyl methacrylate and 0.3 g of VAZO-64 was added thereto at 80?C over a period of 90 minutes. After the completion of the addition  0.13 g of VAZO-64 was further added to the reaction mixture. Then  0.13 g of VAZO-64 was further added twice. The polymer conversion rate based on nonvolatile component percent was more than 98%.
* PEGMA: Poly(ethylene glycol) methyl ether methacrylate as an aqueous 50% by weight solution  Mn ?2080  available from Sigma-Aldrich Corp. (St. Louis  Missouri)
* VAZO-64: 2 2’-Azobisisobutyronitrile  available from E. I. du Pont de Nemours and Co. (Wilmington  Delaware)
* Infrared absorbing dye (2): structure shown below

Infrared absorbing dye (2)
* IRGACURE 250: 75% by weight propylene carbonate solution of (4-methylphenyl)[4-(2-methylpropyl)phenyl]iodonium hexafluorophosphate  available from Ciba Specialty Chemicals (Tarrytown  New York)
* BYK 336: 25% by weight xylene/methoxypropyl acetate solution of modified dimethylpolysiloxane copolymer  available from Byk-Chemie USA Inc. (Wallingford  Connecticut)
* KLUCEL M: 2% by weight aqueous solution of hydroxypropyl cellulose (viscosity: 5 000 mPa•s) available from Hercules Inc.  Aqualon Division (Wilmington  Delaware)
Coating solution (5) for protective layer having the composition shown below was coated on the image-recording layer described above by a bar and dried in an oven at 120?C for 60 seconds to form a protective layer having a dry coating amount of 0.35 g/m2  thereby preparing Lithographic printing plate precursors (73) and (74)  respectively.

Dispersion of inorganic stratiform compound (1) shown above 1.5 g
Aqueous 6% by weight solution of polyvinyl alcohol (CKS 50  sulfonic acid-modified  saponification degree: 99% by mole or more  polymerization degree: 300  produced by Nippon Synthetic Chemical Industry Co.  Ltd.) 0.58 g
Aqueous 1% by weight solution of surfactant (EMALEX 710  produced by Nihon Emulsion Co.  Ltd.) 0.86 g
Ion-exchanged water 6.0 g

II. Evaluation of Lithographic printing plate precursor
With the lithographic printing plate precursor thus-obtained  the on-press development property  printing durability and stain resistance were evaluated in the manner shown below. The results obtained are shown in Table 17.

The lithographic printing plate precursor was subjected to exposure by TRENDSETTER 3244VX  produced by Creo Co.  equipped with a water-cooled 40 W infrared semiconductor laser under the conditions of output of 9W  a rotational number of an external drum of 210 rpm and resolution of 2 400 dpi. The exposed lithographic printing plate precursor was mounted without undergoing development processing on a plate cylinder of a printing machine (SOR-M  produced by Heidelberg). Using dampening water (a solution prepared by diluting CDS803 (produced by Tokyo Printing Ink Mfg. Co.  Ltd.) 50 times with tap water) and TRANS-G (N) Black Ink (produced by Dainippon Ink & Chemicals  Inc.)  after supplying the dampening water and ink printing was initiated at a printing speed of 6 000 sheets per hour.
A number of the printing papers required until the on-press development of the unexposed area of the image-recording layer on the printing machine was completed to reach a state where the ink was not transferred to the printing paper was measured to evaluate the on-press development property.

After ink reception on the image-recording layer in the image area  the image-recording layer was gradually abraded. With the progress of abrasion of the image-recording layer  the ink receptivity degraded to initiate decrease of ink density on printing paper. A number of printed materials obtained until the ink density (reflection density) decreased by 0.1 from that at the initiation of printing was determined to evaluate the printing durability.

After ink reception on the image-recording layer in the image area  the printing was continued. On the 500th sheet of the printed material  ink satin generated in the non-image area was visually observed to evaluate the stain resistance on a 1 to 10 bases  1 being a case where due to adhesion of ink the non-image area was almost stained and 10 being a case where the non-image area did not stained at all. In case this evaluation point is less than 9  it cannot be practically used as a lithographic printing plate.
TABLE 17
Lithographic Printing Plate Precursor Star Polymer Printing Durability
(sheets) Development Property (sheets) Stain Resistance
Example 69 (73) P-63 4.70 x 104 10 10
Comparative Example 5 (74) Comparative Polymer C-4 3.00 x 104 21 7

Comparative polymer C-4: Polyacrylic acid (Mw: 5 000)

WHAT IS CLAIMED IS:
1. A negative lithographic printing plate precursor comprising a support and an image-recording layer  wherein a layer containing a star polymer is provided between the support and the image-recording layer.

2. The negative lithographic printing plate precursor as claimed in Claim 1  wherein the layer containing a star polymer is an undercoat layer.

3. The negative lithographic printing plate precursor as claimed in Claim 1  wherein the layer containing a star polymer is a layer formed by hydrophilizing treatment of a surface of the support.

4. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 3  wherein the image-recording layer contains a polymerization initiator and a polymerizable compound.

5. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 4  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton.

6. The negative lithographic printing plate precursor as claimed in Claim 5  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton via sulfide bonds respectively.

7. The negative lithographic printing plate precursor as claimed in Claim 6  wherein the star polymer is a polymer in which from 3 to 10 polymer chains are branched from a central skeleton via sulfide bonds respectively and which is obtained by polymerization of an ethylenically unsaturated monomer in the presence of a multifunctional thiol.

8. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 7  wherein the star polymer has a hydrophilic group in a polymer chain thereof.

9. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 8  wherein the star polymer has a group adsorbing to a surface of the support in a polymer chain thereof.

10. The negative lithographic printing plate precursor as claimed in Claim 8 or 9  wherein the star polymer has a crosslinkable group in the polymer chain thereof.

11. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 10  which further comprises a protective layer so that the support  the image-recording layer and the protective layer are provided in this order.

12. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 11  which is capable of printing  after image exposure with laser  by supplying at least one of printing ink and dampening water on a printing machine to remove an unexposed area of the image-recording layer.

13. The negative lithographic printing plate precursor as claimed in any one of Claims 1 to 11  which is capable of removing  after image exposure with laser  an unexposed area of the image-recording layer with a developer having pH from 2 to 14.

14. The negative lithographic printing plate precursor as claimed in Claim 11  which is capable of removing  after image exposure with laser  the protective layer and an unexposed area of the image-recording layer with one bath of a developer having pH from 2 to 14.

15. A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as claimed in Claim 12 with laser  and supplying at least one of printing ink and dampening water to the exposed negative lithographic printing plate precursor on a printing machine to remove an unexposed area of the image-recording layer.

16. A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as claimed in Claim 13 with laser  and removing an unexposed area of the image-recording layer with a developer having pH from 2 to 14.

17. A plate making method of a negative lithographic printing plate precursor comprising exposing imagewise the negative lithographic printing plate precursor as claimed in Claim 14 with laser  and removing the protective layer and an unexposed area of the image-recording layer with one bath of a developer having pH from 2 to 14.

ABSTRACT

The invention is directed to a negative lithographic printing plate precursor including a support and an image-recording layer  wherein a layer containing a star polymer is provided between the support and the image-recording layer  and the star polymer is preferably a polymer in which from 3 to 10 polymer chains are branched from a central skeleton.