Description
METHOD OF POLYMERIZING CYCLIC OLEFINS AND VINYL OLEFINS, COPOLYMER PRODUCED BY THE METHOD AND
OPTICAL ANISOTROPIC FILM COMPRISING THE SAME
Technical Field
[ 1 ] The present invention relates to a method of copolymerizing cyclic olefins and
vinyl olefins, a copolymer produced by the method, and an optical anisotropic film comprising the same. More particularly, the present invention relates to a method of copolymerizing cyclic olefins and vinyl olefins in a high yield, a high heat resistant copolymer produced by the method, and an optical anisotropic film comprising the copolymer.
Background Art
[2] Inorganic materials such as silicon oxides or nitrides have been mainly utilized in
the information and electronic industries. R ecent technical developments and demands for compact and high efficiency devices need new high performance materials. In this respect, a great deal of attention has been paid to polymers which have desirable physicochemical properties such as low dielectric constant and moisture absorption rate, high adhesion to metals, strength, thermal stability and transparency, and a high
glass transition temperature (Tg > 250 °C).

[3] Examples of resins for optical components, which are generally used, include a
methacrylic resin, polycarbonate, polyimide, and the like. However, these resins are not suitable for high performance optical components due to disadvantages such as low thermal stability, high birefringence, and coloration.
[4] Recently, polyacrylate, polyethersulfone (PES), polynorbornene (PNB), and cy-
cloolefin copolymer (COC), which have a T gof 100 °C or greater, a transmittance of
90% or more, low birefringence, and a low moisture absorption property, appeared as alternative polymers. These polymers consist of primarily a carbonyl group as a polar group and an aromatic or cyclic olefin portion as a non-polar group, and may further include fluorine (F) in order to improve physical properties such as a heat resistance, a refractive index, and a moisture absorption property.
[5] PES is an amorphous and heat resistant engineering plastic which includes diaryl
sulfone as a backbone and has a high Tg of approximately 225 °C and a strong resistance to thermal aging. PNB is made of norbornene derivatives and has a high Tg of approximately 300 °C , a transparency of 92% or greater, and a low birefringence. COC (or COP) consists of a cyclic olefin and an ethylene backbone and has a Tg of 100-200 °C , a high transparency, and a low birefringence, and can be subjected to

extrusion and injection molding. And these have higher transparency, heat resistance, and chemical resistance and much lower birefringence and moisture absorption rate than conventional olefin polymers. Thus, this polymer can be applied to various applications, e.g., optical components such as mobile phone earner a lens, CD/DVD pickup lens, LCD light guide panel and POFs (plastic optical fibers), electronic and information components such as capacitor films and low-dielectrics, and medical components such as low-absorbent syringes, blister packagings, etc.
[6] Meanwhile, polyacrylate has very high hardness and adhesion and high
transparency, and thus is widely used in an optical field such as glass substitutes.
[7] Thus, when norbornene is copolymerized with acrylate, a new polymer having
features to be applicable to broader field can be obtained. However, a polar vinyl olefin monomer is generally polymerized through a radical or anionic initiator, whereas a norbornene monomer is addition-polymerized by a late transition metal catalyst such as Ni or Pd. Due to such a contrary polymerization characteristic of the two monomers, their direct copolymerization is difficult to carry out.
[8] In the early days, norbornene and polar vinyl olefin were copolymerized by radical
polymerization, in which the content of norbornene in the copolymer is very low ( < 5.5 % by weight) (Morris et al., U.S. Patent No. 3,536,681; Starmer et al., U.S. Patent No. 3,679,490). Thereafter, copolymerization of norborene and acrylate using a palladium catalyst was reported, but a polymerization yield is low or it is difficult to obtain reproducible polymerization results (Goodall et al., U.S. Patent No. 6,303,724; Sen et al., U.S. Patent No. 6,111,041 and U.S. Patent No. 6,593,440).
[9] Therefore, there has been a demand for a new method of producing a copolymer of
norbornene and vinyl olefin with a high molecular weight and a high yield.
Disclosure of Invention
Technical Solution
[10] The present invention provides a method of copolymerizing cyclic olefins and
polar vinyl olefin monomers with a high molecular weight and a high yield.
[11] The present invention also provides a copolymer, which has a low dielectric
constant, a high glass transition temperature, a high thermal and oxidative stability , toughness, a high chemical resistance and adhesion to metal, and thus can be used in electronic components.
[12] The present invention also provides an optical film which has a high transparency
and controllable refractive index, and thus can be used as a polarizer protective film, an adhesive film, and an optical anisotropic compensation film, and in a LCD display.
[13] According to an aspect of the present invention, there is provided a method of
copolymerizing cyclic olefins and polar vinyl olefins, which includes:

[14] contacting cyclic olefm monomers and polar vinyl olefm monomers with a catalyst
system including:
[15] i) a compound represented by formula (1) containing a group 13 element; and
[16] ii) a radical initiator composed of an azo compound represented by formula (2) or a
peroxide compound represented by formula (3):
[17] M(R°)n1 (OR1)n2 (X)n3 (1)
[18] where M is a group 13 element; O is an oxygen atom; each of nl, n2, and n3 is in-
dependently an integer of 0-3 and nl+n2+n3=3; each of R° and R1 is independently a hydrogen atom; a linear or branched C1-20 alkyl, alkenyl, or vinyl; a C5-12 cycloalkyl optionally substituted by a hydrocarbon; a C6-40 aryl optionally substituted by a hy-drocarbon; or a linear or branched C1-20 alkyl or aryl containing 1-10 hetreo atoms such as N, O, and halogen atoms; and X is a halogen atom;
[19] A1-N=N-A2 (2)
[20] where N is a nitrogen atom; and each of A and A is independently a hydrogen
atom; a linear or branched C1-20 alkyl, alkoxy, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hydrocarbon; a C6-40 aryl optionally substituted by a hy-
drocarbon; or a linear or branched C1-20 alkyl, alkoxy, alkenyl, aryl, or cycloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group, an ether group, or an amide group;
[21] B1-O-O-B2(3)
[22] where O is an oxygen atom; and each of B and B is independently a hydrogen
atom; a linear or branched C1-20 alkyl, alkoxy, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hydrocarbon; a C6-40 aryl optionally substituted by a hy-drocarbon; or a linear or branched C1-20 alkyl, alkoxy, alkenyl, aryl, or cycloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group, an ether group, or an amide group.
[23] According to another aspect of the present invention, there is provided a copolymer
having good physical properties, produced by the above method.
[24] According to another aspect of the present invention, there is provided a polarizing
protective film, an adhesive film, an optical anisotropic film, an optical compensation film, and a LCD display module.
[25] When the copolymerization method according to an embodiment of the present
invention is used, cyclic olefins and polar vinyl olefms can be copolymerized with a high yield using a catalyst system composed of a compound containing a group 13 element and a radical initiator. The copolymer produced by the method has good physical properties, including high transparency, adhesion to metals or other polymers, thermal stability and strength, and a low dielectric constant. Thus, the optical film including the copolymer can be used as a polarizer protective film, an adhesive film,

and an anisotropic compensation film, and in a LCD display module.
[26] The inventors of the invention found that when cyclic olefin monomers and polar
vinyl olefin monomers are contacted with a catalyst system composed of a compound containing a group 13 element and an azo compound (or peroxide compound), a copolymer having high transparency and optical anisotropy is obtained in a high yield.
Advantageous Effect
[21J According to the copolymerization method, a cyclic olefin and a polar vinyl olefin
can be effectively copolymerized using a catalyst system composed of a compound containing a group 13 element and a radical initiator. The resulting copolymer is transparent, has sufficient adhesion to metals or other polymers, thermal stability and strength, and exhibits a low dielectric constant sufficient to be used as insulating electronic materials. Thus, the optical film including the copolymer can be used as a polarizer protective film, an adhesive film, an anisotropic film, and a compensation film, and in a LCD display.
Description of Drawings
[28] FIG. 1 is a 'H NMR spectrum of a norbornene-methyl acrylate copolymer;
[29] FIG. 2 is a :H NMR spectrum of a butyl norbornene-methyl acrylate copolymer;
[30] FIG. 3 is a !H NMR spectrum of a norbornene-methyl methacrylate copolymer;
[31] FIG. 4 is a 'H NMR spectrum of a norbornene-methyl acrylate-styrene terpolymer;
[32] FIG. 5 is a DSC (differential scanning calorimetry) thermodiagram of a
norbornene-methyl acrylate copolymer;
[33] FIG. 6 is a DSC thermodiagram of a norbornene-methyl methacrylate copolymer;
and
[34] FIG. 7 is a DSC thermodiagram of a norbornene-methyl acrylate-styrene
terpolymer.
Mode for Invention
[35] In the present invention, a cyclic olefin monomer, a polar vinyl olefin monomer,
and a catalyst are dissolved in a solvent and mixed to polymerize as in a conventional polymerization method. A catalyst system to be contacted with the monomers includes a compound represented by formula (1), containing a group 13 element and a radical initiator composed of an azo compound represented by formula (2) (or a peroxide compound represented by formula (3)).
[36] The cyclic olefin monomer is represented by formula (4)
(Figure Removed)



(4)
[37] where m is an integer of 0-4; R2, R3, R4, and R5 may be a nonpolar functional
group selected from a hydrogen atom, a halogen atom, a linear or branched C alkyl, alkenyl, or vinyl, a C cycloalkyl optionally substituted by a hydrocarbon, a C aryl
5-12 6-40
optionally substituted by a hydrocarbon, a C aralkyl optionally substituted by a hy-
7-15
drocarbon, or a C alkynyl; or a polar functional group selected from the group consisting of -(CH 2) n C(O)OR6, -(CH 2 ) n OC(O)R6, -(CH ^) n OC(O)OR6, -(CH ^) ^ C(O)R6, -(CH2 )n OR6, -(CH2 O)n -OR6" -(CH2 )n C(O)-O-C(O)R6, -(CH2 )n C(O)NH2, -(CH2)n C(O)NHR6, -(CH2 )n C(O)N(Rfi )2, -(CH2 )n NH,, -(CH°2 )n NHR6, -(CH2) N(R6)2, -(CH2)n OC(O)NH2 , -(CH2) n OC(O)NHR6, -(CH 2)° OC(O)N(R6 )2 ,°-(CH2/ C(O)C1, -(CH2 )n SR6, -((CH 2 ) n ] SSR6, -(CH2 )n SO2R6, -(CH ) SO2R6, -(CH ) OSO R6, -(CH )n SO R6', -°(CH )n OSO R6, -(CH^) B(R^) °, -(CH 2 ) n B(OR6") -(CH ) n B(R2& )(OR), -(CH 2 ) n 2N=C=S,3-(CH 2\ ' " NCO, -(CH 2) n N(R6 )C(=O)R6, -(CH 2 ) n N(R6 )C(=O)(OR6), -(CH 2) n CN, -(CH 2) n N02, -(CH2 )n P(R6 )2, -(CH2 )n P(ORn )2, -(CH2 )n P(R6 )(OR6), -(CH2 )n P(=0)(R6) ,-(CH 2 ) n P(=0)(OR6)2 ,and-(CH 2 ) n P(=O)(R6 )(OR6);

[38] R6 is a hydrogen atom, a linear or branched C1-20 alkyl, alkenyl, or vinyl, a C5-12
cycloalkyl optionally substituted by a hydrocarbon, a C6-40 aryl optionally substituted
by a hydrocarbon, a C7-15 aralkyl optionally substituted by a hydrocarbon, or a C3-20 alkynyl; and,
[39] n is an integer of 0-10; when R2, R3, R4, and R5 are may be a polar functional
group, a hydrogen atom, or a halogen atom, R2 and R3 , or R4 and R5 can be connected to each other to form a C1-10 alkylidene group, or R2 or R3 can be connected

to one of R4 and R5 to a saturated or unsaturated C4-12 cyclic group or an C 6-17 aromatic
ring compound.
[40] The polar vinyl olefin monomer is represented by formula (5):
(Figure Removed)

v

(5)
[41] where at least one of R and R is a polar functional group selected from the group
consisting of -(CH 2) n C(O)OR9, -(CH 2) n OC(O)R9, -(CH 2) n OC(O)OR9, -(CH ) C(O)R9,-(CH ) OR9,-(CH O) -OR9"! -(CH 2) n C(O)-O-C(O)R9,-(CH 2) n
2 n 2 n
C(O)NH2,-(CH2)nC(O)NHR9,-(CH2)nC(O)N(R9)2,-(CH 2) n NH2-(CH 2) n NHR9,-(CH2)nN(R9)2,-(CH2)nOC(OD)NH ,-(CH ) OC(O)NHR9,-(CH 2) n OC(O)N(R9)2,-(CH 2) nC(0)C1,-(CH2)nSR9,-(CH2)]sSR9,-(CH ) SO V, -(CH 2) n SO R9,-(CH 2) n OSO R9,-(CH 2) n SO R'.-(CH 2) n OSO R°9,-(CH )
3 2 n
B(R ) ,-(CH 2) n B(OR ),,-(CH 2) n B(R9)(OR ),-(CH,) N=C=S,-(CH 2) n NCO,-(CH2)nN(R9)C(=d)R9,-(CH 2) n N(R9 )C(=O)(OR9), -(CH 2) n CN.(CH 2) n NO ,-(CH 2) n P(R9) ,-(CH 2) n P(OR) ,-(CH 2) n P(R9 )(OR9), -(CH 2) n
P(=O)(R ) ,-(CH 2) n P(=O)(OR ) ,and-(CH 2) n P(=O)(R9 )(OR9);
[42] the remaining substituent is a hydrogen atom, a halogen atom, a linear or branched
C1-20 alkyl, alkenyl, or vinyl, a C5-12 cycloalkyl optionally substituted by a hydrocarbon, a C 6-40 aryl optionally substituted by a hydrocarbon, a C7-15 aralkyl optionally
substituted by a hydrocarbon, or a C3-20 alkynyl; n is an integer of 0-10; and R9 is a
hydrogen atom, a linear or branched C1-20 alkyl, alkenyl, or vinyl, a C5-12 cycloalkyl optionally substituted by a hydrocarbon, a C 6-40 aryl optionally substituted by a hy-
drocarbon, a C aralkyl optionally substituted by a hydrocarbon, or a C3-20 alkynyl.
[43] Meanwhile, the cyclic olefin monomer may be a non-polar cyclic olefin monomer
or a mixture of a polar cyclic olefin monomer and a cyclic olefin monomer.
[44] The solvent used in the polymerization method may be an organic solvent such as
dichloromethane (CH Cl), dichloroethane (CH2C1CH2 Cl), chloroform, benzene,
toluene, or chlorobenzene (C6 H 5Cl). An amount of the solvent used is preferably
0.5-10 folds, more preferably 1-8 folds, most preferably 2-4 folds, relative to the volume of a monomer to be addition polymerized. When the amount of the solvent is lower than 0.5 folds, gel is formed and post-treatment become an indispensable. When the amount of the solvent is higher than 10 folds, the polymerization yield is low. Without such a solvent, bulk polymerization may be carried out. In this case, the reaction solution is gellated or hardened during the polymerization, which can bring about an after-treatment problem.
[45] A polymerization temperature may be in the range of 20-150 °C , and may be
varied to change the polymerization conditions during the reaction. When the poly-merization temperature is lower than 20 °C , the catalyst is not activated and the polymerization yield is low. When the polymerization temperature is higher than 150 °C , the catalyst may be decomposed due to thermal instability.
[46] In the polymerization method, the cyclic olefin monomer and the polar vinyl olefin
monomer are not limited to only two monomers and may include a combination of two cyclic olefin monomers, which have different functional groups, and a polar vinyl olefin monomer, or a combination of two polar vinyl olefin monomers, which have different functional groups, and a cyclic olefin monomer.
[47] The copolymer may further include a non-polar vinyl olefin monomer in addition
to the cyclic olefin monomer and a polar vinyl monomer. The non-polar vinyl olefin monomer may be represented by formula (6):
(Figure Removed)
(6)
[48] where m is an integer of 0-4; and each of R1 and R is a hydrogen atom, a halogen
atom; a linear or branched C alkyl, alkenyl, or vinyl; a C cycloalkyl optionally substituted by a hydrocarbon; a C aryl optionally substituted by a hydrocarbon; a C aralkyl optionally substituted by a hydrocarbon; or a C alkynyl.
[49] In the polymerization method, it is preferable that the compound represented by
formula (1) containing a group 13 element is the compound represented by formula (7), and the radical initiator is the azo compund represented by formula (2):
[50] Al (R°) (OR1) (X) (7)
nl n2 n3
[51] where Al is an aluminium atom; O is an oxygen atom; each of nl, n2, and n3 is in-
dependently an integer of 0-3 and nl+n2+n3=3; each of R and R is independently a hydrogen atom; a linear or branched C alkyl, alkenyl, or vinyl; a C cycloalkyl optionally substituted by a hydrocarbon; a C aryl optionally substituted by a hy-
o-40
drocarbon; or a linear or branched C alkyl or aryl containing 1-10 hetreo atoms such
as N, 0, and halogen atoms; and X is a halogen atom;
[52] A -N=N-A (2)
[53] where N is a nitrogen atom; and each of A and A is independently a hydrogen
atom; a linear or branched C1-20 alkyl, alkoxy, alkenyl, or vinyl; a C5-12 cycloalkyl
optionally substituted by a hydrocarbon; a C aryl optionally substituted by a hy-
6-40
drocarbon; or a linear or branched C1-20 alkyl, alkoxy, alkenyl, aryl, or cycloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group, an ether group, or an amide group;
[54] The copolymer produced by the method according to an embodiment of the present
invention may include 0.1-99.9 mol% of a polar vinyl olefin monomer and have a weight average molecular weight (Mw) of 10,000 or greater. When the Mw of the copolymer is less than 10,000, it is difficult to produce a film. The copolymer may have a glass transition temperature (Tg) of 100 °C or greater. When the Tg of the

copolymer is lower than 100 °C , the thermal stability of film becomes poor.
[55] The copolymer may be a copolymer blend which further includes at least one of a
cyclic olefin monomer, a polar vinyl olefin monomer, a non-polar vinyl olefin monomer, or a copolymer of a cyclic olefin monomer and a polar vinyl olefin.
[56] The copolymer produced in accordance with the method of the present invention is
transparent, has sufficient adhesion to metals or polymers containing different polar functional groups, thermal stability and strength, and exhibits a low dielectric constant sufficient to be used as insulating electronic materials. The copolymer has a desirable adhesion to substrates of electronic components without requiring a coupling agent, and at the same time, a sufficient adhesion to metal substrates, e.g., Cu, Ag and Au. Further, the copolymer exhibits a desirable optical properties so that it can be used in electronic components such integrated circuits (ICs), printed circuit boards, multichip modules, and the like.
[57] Thus, the copolymer prepared by the present invention has high transparency,
molecular weight in the range of 10,000 -1,000,000 and the glass transition temperature in the range of 100 -200 oC which lead to afford to good moldability for a plastic lens. The plastic lens can be formed by various molding methods such as injection molding, compression molding, extrusion molding or injection compression molding. In the injection compression molding, generally, the cylinder temperature is 150 to 300 °C and the mold temperature is 50 to 150 °C.
[58] In addition, an optical film according to an embodiment of the present invention
can be used as a polarizer protective film due to good heat resistance and strength, and has sufficient adhesion to polyvinylalcohol (PVA) to be attached to a polyvinylalcohol polarizer. Even when corona discharge, glow discharge, flame treatment, acid treatment, alkaline treatment, UV irradiation, or coating, if necessary, is performed on the optical film, its transparency, etc. is not reduced.
[59] The copolymer of the present embodiment can be used to produce an optical
anisotropic film capable of controlling a birefringence, which could not be produced with the conventional method. A conformational unit of a general cyclic olefin has one or two stable rotation states, and thus can achieve an extended conformation such as polyimide having a rigid phenyl ring as a backbone. When a monomer having a polar functional group is introduced into a norbornene-based polymer with an extended form, the interaction between molecules increases compared to polymers having compact conformations, and thus packing of molecules has a directional order, thereby producing optical and electronic anisotropy.
[60] The birefringence can be controlled according to the type and the amount of polar
functional group in the copolymer of a cyclic olefin polymer and a polar vinyl olefin. In particular, the birefringence in a direction through the film thickness is easily

controlled, and thus the polymer of the present embodiment can be used to produce an optical compensation film for various modes of liquid crystal display (LCD).
[61] The optical anisotropic film can be prepared by solution casting or melting, or can
be prepared with a blend of one or more copolymers of cyclic olefms and polar vinyl olefins.
[62] In order to prepare a film by solution casting, it is preferable to introduce a
copolymer of a cyclic olefm and a polar vinyl olefin in a solvent in amount of 5-95% by weight, and preferably 10-60% by weight, and stirring the mixture at room temperature. The viscosity of the prepared solution is preferably 100-10,000 cps, and more preferably 300-8000 cps for solution casting. To improve mechanical strength, heat resistance, light resistance, and manipulability of the film, additives such as a plasticizer, an anti-deterioration agent, a UV stabilizer or an antistatic agent can be added.
[63] The optical anisotropic film thus prepared has a retardation value (R ) of 70 to

1000 nm, as defined by the following Equation 1 :

(Figure Removed)
[64] where n is a refractive index of an in-plane fast axis measured at 550 nm, n is a
refractive index toward thickness direction measured at 550 nm, and d is a film
thickness.
[65] The optical anisotropic film has clear picture quality at a wide viewing angle and
can improve contrast when a driving cell is on or off, and thus can be used as an
optical compensation film for LCD.
[66] In particular, the optical anisotropic film has an optical axis perpendicular to a plate
and meets a refractive index requirement of n @ n > n , in which n is a refractive
x y z x
index of an in-plane slow axis, n is a retractive index of an in-plane fast axis, and n is
a refractive index toward thickness direction , and thus can be used as a negative C-
plate type optical compensation film. Thus, the optical anisotropic film can achieve a general liquid crystal mode of LCD which meets a refractive index requirement of n @ n < n , in which n , n , and n are as defined above, when a voltage is on or off.
y z x y z
[67] Hereinafter, the present invention will be described in more detail with reference to
the following Examples. However, these Examples are given for the purpose of illustration and are not to be construed as limiting the scope of the invention.
[68] Examples
[69] In the following Preparation Examples and Examples, all operations handling
compounds sensitive to air or water were carried out using standard Schlenk technique

or dry box technique. Nuclear magnetic resonance spectra were obtained using a Bruker 3 00 spectrometer . 1H NMR and 13C NMR were measured at 300 MHz and 75 MHz, respectively. A molecular weight and a molecular weight distribution of a polymer were determined by gel permeation chromatography (GPC) using standard polystyrene samples. Thermal analyses such as TGA (thermal gravimetric analysis) and DSC (differential scanning calorimetry) were carried out using TA Instrument (TGA 2050; heating rate lOK/min). Toluene was distilled and purified in potassium/ benzophenone.
[70] Preparation Example 1: Copolymerization of norbornene and methyl acrylate
[71] Norbornene (15.8 g, 168 mmol), methyl acrylate (10 mL, 112 mmol), and AIBN
(2,2'-azobisisobutyronitrile) (0.037 g, 0.22 mmol) were charged into a 250 mL Schlenk flask and dissolved in 30 mL of toluene. Ethylaluminum sesquichloride (0.277 g, 1.12 mmol) was charged into a 100 mL flask and dissolved in 20 mL of toluene. The toluene solution of ethylaluminum sesquichloride was slowly dropped to the 250 mL Schlenk flask at -70 °C . The reaction temperature was raised to 45 °C while stirring the mixture for 2 hours, and then the reaction was performed at 45 °C for 12 hours. The reaction solution turned to light green in color during the reaction. After the reaction was completed, the reaction solution was slowly dropped to 3000 cc of 5% v/v HC1-MeOH to precipitate a white polymer, which was filtered through a glass filter and dried in a vacuum oven at 70 °C for 12hours to obtain a norbornene-methyl acrylate copolymer (11.7 g: 58.2 % by weight based on the total weight of used monomers). The copolymer had a Tg of 140 °C , a molecular weight (Mw) of 46,600, and Mw/Mn of 1.99.
[72] ' H-NMR (300MHz in CDC13): 3.55 (br s, 3H), 2.5-1.5 (br m,13H)
[73] Preparation Example 2: Copolymerization of norbornene and methyl acrylate
[74] Diethylaluminium chloride(l .36 g, 1.12 mmol) was used instead of Ethylaluminum
sesquichloride used in Preparation Example 1. And, norbornene was copolymerized with methyl acrylate in the same way as the Preparation Example 1.
[75] Polymerization yield was 12. lg(60.2 % by weight based on the total weight of used
monomers). The copolymer had a molecular weight (Mw) of 68,000, and Mw/Mn of 2.12.
[76] Preparation Example 3: Copolymerization of norbornene and methyl acrylate
[77] Diethylaluminium ethoxide(1.15 g, 1.12 mmol) was used instead of Ethy-
laluminum sesquichloride used in Preparation Example 1. And, norbornene was
copolymerized with methyl acrylate in the same way as the Preparation Example 1.
[78] Polymerization yield was 12.5g(62.1 % by weight based on the total weight of used
monomers). The copolymer had a molecular weight (Mw) of 54,000, and Mw/Mn of 2.10.

[79] Preparation Example 4: Copolymerization of norbornene and methyl acrylate
[80] Norbornene (15.8 g, 168 mmol), methyl acrylate (10 mL, 112 mmol), and Di-
t-butylperoxide (0.32 g, 2.2 mmol) were charged into a 250 mL Schlenk flask and
dissolved in 30 mL of toluene. Ethylaluminum sesquichloride (0.277 g, 1.12 mmol)
was charged into a 100 mL flask and dissolved in 20 mL of toluene. The toluene
solution of ethylaluminum sesquichloride was slowly dropped to the 250 mL Schlenk
flask at -70 °C . The reaction temperature was raised to room temperature while stirring
the mixture for 2 hours, and then the reaction was performed at 80 °C for 12 hours.
After the reaction was completed, the reaction solution was slowly dropped to 3000 cc
of 5% v/v HCl-MeOH to precipitate a white polymer, which was filtered through a
glass filter and dried in a vacuum oven at 70 °C for 12hours to obtain a norbornene-
methyl acrylate copolymer (10.5 g: 52.0 % by weight based on the total weight of used
monomers). The copolymer had a molecular weight (Mw) of 38,500, and Mw/Mn of
2.29.
[81] Preaparation Example 5: Copolymerization of 2-butylnorbornene and methyl
acrylate
[82] 2-butylnorbornene (16.8 g, 112 mmol), methyl acrylate (5 mL, 56 mmol), and
AIBN (0.28 g, 1.68 mmol) were charged into a 250 mL Schlenk flask and dissolved in
30 mL of toluene. Ethylaluminum sesquichloride (15.2 g, 61.6 mmol) was charged into
a 100 mL flask and dissolved in 20 mL of toluene. The toluene solution of ethy
laluminum sesquichloride was slowly dropped to the 250 mL Schlenk flask at -70 °C .
The reaction temperature was raised to room temperature while stirring the mixture for
2 hours, and then the reaction was performed at 65 °C for 12 hours. The reaction
solution turned to light green in color during the reaction. After the reaction was
completed, the reaction solution was slowly dropped to 3000 cc of 5% v/v HCl-MeOH
to precipitate a white polymer, which was filtered through a glass filter and dried in a
vacuum oven at 70 °C for 12hours to obtain a 2-butyl norbomene-methyl acrylate
copolymer (5 g: 38.0 % by weight based on the total weight of used monomers). The
copolymer had a Tg of 100 °C , a molecular weight (Mw) of 8,180, and Mw/Mn of 3.2.
[83] ' H-NMR (300MHz in CDCl3): 3.64 (br s, 3H), 2.5-0.5 (br m,21H)
[84] Preparation Example 6: Copolymerization of norbornene and methyl methacrylate
[85] Norbornene (8.8 g, 93 mmol), methyl methacrylate (5 mL, 47 mmol), and AIBN
(0.23 g, 1.40 mmol) were charged into a 250 mL Schlenk flask and dissolved in 30 mL of toluene. Ethylaluminum sesquichloride (12.7 g, 51.4 mmol) was charged into a 100 mL flask and dissolved in 20 mL of toluene. The toluene solution of ethylaluminum sesquichloride was slowly dropped to the 250 mL Schlenk flask at -70 °C . The reaction temperature was raised to room temperature while stirring the mixture for 2 hours, and then the reaction was performed at 65 °C for 12 hours. The reaction solution

turned to light green in color during the reaction. After the reaction was completed, the reaction solution was slowly dropped to 3000 cc of 5% v/v HCl-MeOH to precipitate a white polymer, which was filtered through a glass filter and dried in a vacuum oven at 70 °C for 12 hours to obtain a norbornene-methyl methacrylate copolymer (0.3 g: 3.0 % by weight based on the total weight of used monomers). The copolymer had a Tg of 167 °C , a molecular weight (Mw) of 10,700, and Mw/Mn of 3.4.
[86] ' H-NMR (300MHz in CDCl3 3.60 (br s, 3H), 2.5-0.8 (br m,15H)
[871 Preparation Example 7: Polymerization of norbornene, styrene, and methyl acrylate
[88] Norbornene (10.5 g, 112 mmol), styrene (0.6 g, 5.6 mmol), methyl acrylate (5 mL,
56 mmol), and AIBN (0.028 g, 0.17 mmol) were charged into a 250 mL Schlenk flask and dissolved in 30 mL of toluene. Ethylaluminum sesquichloride (1.38 g, 5.6 mmol) was charged into a 100 mL flask and dissolved in 20 mL of toluene. The toluene solution of ethylaluminum sesquichloride was slowly dropped to the 250 mL Schlenk flask at -70 °C . The reaction temperature was raised to room temperature while stirring the mixture for 2 hours, and then the reaction was performed at 65 °C for 12 hours. The reaction solution turned to light green in color during the reaction. After the reaction was completed, the reaction solution was slowly dropped to 3000 cc of 5% v/v HC1-MeOH to precipitate a white polymer, which was filtered through a glass filter and dried in a vacuum oven at 70 °C for 12 hours to obtain a norbornene-styrene-methyl acrylate terpolymer (7.1 g: 66.7 % by weight based on the total weight of used monomers). The copolymer had a Tg of 120 °C , a molecular weight (Mw) of 228,000, and Mw/Mn of 16.
[89] ' H-NMR (300MHz in CDC13): 7.4-6.6 (br m, 5H), 3.8-3.1 (br m, 3H), 2.4-0.6 (br
m,16H)
[90] Examples 1-4: Preparation of optical anisotropic film
[91] Each of the p olymers prepared in Preparation Examples 1, 5-7 was mixed with a
solvent to form a coating solution as shown in Table 1. The coating solutions were cast on a glass substrate using a knife coater or a bar coater, and then the s ubstrate was dried at room temperature for 1 hour and further dried under a nitrogen atmosphere at 100 °C for 18 hours. The glass substrate was kept at -10 °C for 10 seconds and the film on the glass plate was peeled off with a knife to obtain a clear film having an uniform thickness. The thickness deviation of the film was less than 2%. The thickness and the light transmittance at 400-700 nm of the obtained films were shown in Table 1
[92] Table 1
(Table Removed)

[93] In Table 1, THF is tetrahydrofurane and MC is methylene chloride.
[94] Measurement of optical anisotropy
[95] For clear films produced in Examples 1-4, a refractive index n was measured using an Abbe refractometer, an in-plane retardation value Re was measured using an automatic birefringence analyzer (available from Oji Scientific Instrument; KOBRA-21 ADH), and a retardation value R was measured when the angle between incident

light and the film surface was 50 ° and a retardation value R between the direction

through the film thickness and the in-plane x-axis was calculated using Equation 2:

(Figure Removed)

[96] A refractive index difference (n -n ) and a refractive index difference (n -n ) were
x y y z
calculated by dividing R and R by the film thickness, (n -n ), R , R and (n -n ) of
e ft xyeth y z
each clear film were indicated in Table 2.
Table 2
(Table Removed)

[98] When films were covered with a triacetate cellulose film having n > n , R values
y z 8
of all cyclic olefin films increased, which indicates that R of a cyclic olefin film is
th
produced due to a negative birefringence (n > n ) in a direction through the film thickness.
[99] Example 5: Surface treatment and lamination with poly vinyl alcohol (PVA) polarization film
[100] The surface tension of the NB-MA copolymer film obtained from Example 1 was determined by measuring the contact angle and using Equations 3 and 4 (Wu, S.J. Polym. Sci. C Vol 34, P19, 1971):

(Figure Removed)

[101]
(Figure Removed)

[102] where γs is a surface tension of the film, γlv is a surface tension of liquid, γsl is a interfacial tension between the film and liquid, cos Ө is a contact angle, γd is a dispersion term of the surface tension, and γp is a polar term of the surface tension.
[103] When water was used, the contact angle was 74.3 ° and when methane was used, the contact angle was 33.5 °. A surface tension calculated from these values was 49.5
mN/m.
[104] The NB-MA copolymer film was subjected three times to a corona treatment at a current of 8 mA and a line speed of 6 m/min, and then the contact angle was measured. When water was used, the contact angle was 20.7 ° and when diode methane was used, the contact angle was 22 ". A surface tension calculated from these values was 76.9 mN/m.
[105] Within 30 minutes after the corona treatment, the film was roll laminated on a fully dried PVA polarization film in a 10% by weight PVA aqueous solution and dried at 80

°C for 10 minutes. Then, the PVA polarization plate on which the NB-MA copolymer film was laminated exhibited excellent adhesion.
[106] Example 6: Preparation of plastic lens
[107] Each of the polymers prepared in Preparation Examples 1~4 was palletized with an
extruder under nitrogen atmosphere. The obtained pellets were injection compression molded with a mold for a spectacle concave lens at a cylinder temperature of 200 to 300 °C, at a mold temperature of 110 °C to obtain a lens. The obtained lens was tested under condition of 70 °C, 95% RH relative humidity for 24 hrs to show a good appearance and more than 90% light transmittance in the range of 400-700 nm.
Industrial Applicability
[108] According to the present invention, the resulting copolymer is transparent, has
sufficient adhesion to metals or other polymers, thermal stability and strength, and exhibits a low dielectric constant sufficient to be used as insulating electronic materials. Thus, the optical film including the copolymer can be used as a polarizer protective film, an adhesive film, an anisolropic film, and a compensation film, and in a LCD display.

Claims
[ 1 ] A method of copolymerizing cyclic olefins and polar vinyl olefins, comprising :
contacting a cyclic olecfin monomer and a polar vinyl olefin monomer with a catalyst system comprising:
i) a compound represented by formula (1) containing a group 13 element; and ii) a radical initiator composed of an azo compound represented by formula (2) or a peroxide compound represented by formula (3): M(R°) (OR1) (X) (1)
where M is a group 13 element; O is an oxygen atom;
each of nl, n2, and n3 is independently an integer of 0-3 and nl+n2+n3=3; each of R° and R1 is independently a hydrogen atom; a linear or branched C alkyl, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hy-drocarbon; a C6-40 aryl optionally substituted by a hydrocarbon; or a linear or branched C6-40 alkyl or aryl containing 1-10 hetreo atoms such as N, O, and halogen atoms; and X is a halogen atom; A1-N=N-A2 (2)where N is a nitrogen atom; and each of A and A is independently a hydrogen atom; a linear or branched C1-20 alkyl, alkoxy, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hy-drocarbon; a C6-40 aryl optionally substituted by a hydrocarbon; or a linear or branched C 1-20 alkyl, alkoxy, alkenyl, aryl, or cycloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group, an ether group, or an amide group;
B1-O-O-B2 (3)
where 0 is an oxygen atom; and
each of B and B is independently a hydrogen atom; a linear or branched C alkyl, alkoxy, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hy-drocarbon; a C6-40 aryl optionally substituted by a hydrocarbon; or a linear or branched v alkyl, alkoxy, alkenyl, aryl, or cycloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group, an ether group, or an amide group.
[2] The method of claim 1, wherein the cyclic olefin monomer is represented by
formula (4):
(Figure Removed)



(4)
1-20
where m is an integer of 0-4; R2 , R3 , R4 , and R5 may be a nonpolar functional group selected from a hydrogen atom, a halogen atom, a linear or branched C 1-20 alkyl, alkenyl, or vinyl, a C cycloalkyl optionally substituted by a hy-drocarbon, a C aryl optionally substituted by a hydrocarbon, a C aralkyl
6-40 7-15
optionally substituted by a hydrocarbon, or a C alkynyl; or a polar functional
group selected from the group consisting of -(CH ) C(O)OR6 , -(CH )
OC(O)R 6 , -(CH 2 ) n OC(0)OR 6 , -(CH2 )n C(0)R 6 ° -(CH 2 ) n OR 6 , -(CH ^ O) n -
ORfi,-(CH2)nC(O)-O-C(O)Rfi,-(CH2 )n C(O)NH9 , -(CH °) C(O)NHR~6 , -
(CH2 ) C(O)N(R6 ) , -(CH ) NH2 , -(CH2 )n NHR6 , -(CH ) N(R6 ) , -(CH
2 )n OC(O)NH2 , -(CH2 )n OC(6)NHR6 , -(CH2 )n OC(O)N(R6 )°2 , -(CH2 )n
C(O)C1, -(CH) SR6 , -(CH) SSR6
B(R5 )(OR6 ), -(CH ) N=C=S, -(CH ) NCO, -N(R6 )C(=O)(OR6 ), -(CHz )n )a P(R6 )(OR"5 P(=O)(R6 )(OR6
P(=0)(R6) ,-(CH ) P(=O)(OR6) ,and-(CH2)n

R6 is a hydrogen atom, a linear or branched C alkyl, alkenyl, or vinyl, a C

substituted by a hydrocarbon, a C7-15 aralkyl optionally substituted by a hy-drocarbon, or a C 3-20 alkynyl; and,
n is an integer of 0-10; when R2 , R3 , R4 , and R5 are may be a polar functional group, a hydrogen atom, or a halogen atom, R and R , or R and R can be connected to each other to form a C 1-10 alkylidene group, or R or R can be connected to one of R4 and R5 to a saturated or unsaturated C cyclic group or
4-12
an C aromatic ring compound.

[3] The method of claim 1 , wherein the polar vinyl olefin monomer is represented by
formula (5):
(Figure Removed)

(5) where
7 R
at least one of R and R is a polar functional group selected from the group consisting of -(CH 2 ) n C(O)OR 9 , -(CH2 ) n OC(O)R 9 , -(CH 2 ) n OC(O)OR 9 , -(CH ) C(O)R9,-(CH ) OR9,-(CH 2O)) -OR9,-(CH ) C(O)-O-C(O)R9 , (CH ) C(0)NH , -(CH 2 C(0)NHR 9 , -(CH ) C(O)N(R 9 ) , -(CH ) NH
OC(O)NHR9 , -(CH2 )n OC(O)N(R9 ) , -(CH ) C(0)C1, -(CH ) SR9
n
3 R9 , -(CH2 )n OSQ3 R9 , -(CH2 )n B(R9 )2 , -(CH2 )n B(OR9 )2 , -(CH2 ) B(R9 )(OR9 ), -(CH° ) N=C=S, -(CH2)nNCO, -(CH ) N(R9 )C(=O)R9 , -(CH ) N(R9)C(=O)(OR9), -(CH ) CN,"-(CH2)nNO .'-(CH ) P(R9 ) , -(CH )° P(OR9) ,-(CH ) P(R9)(OR9), -(CH )np(-O)(R9) , -(CH ) P(=0)(OR"9 )
2 2 n 2 n 2 2 n
,and-(CH ) P(=O)(R9 )(OR );

the remaining substituent is a hydrogen atom; a halogen atom; a linear or
branched C 1-20 alkyl, alkenyl, or vinyl; a C5-12 cycloalkyl optionally substituted by
a hydrocarbon; a C 1-20 aryl optionally substituted by a hydrocarbon; a C7-15 aralkyl
optionally substituted by a hydrocarbon; or a C 3-20 alkynyl;
n is an integer of 0-10; and
R9 is a hydrogen atom, a linear or branched C 1-20 alkyl, alkenyl, or vinyl, a C5-12
cycloalkyl optionally substituted by a hydrocarbon, a C aryl optionally
6-40
substituted by a hydrocarbon, a C7-15aralkyl optionally substituted by a hy-drocarbon, or a C alkynyl.
3-20
[4] The method of claim 1 , wherein the cyclic olefin monomer is a non-polar cyclic
olefin monomer or a mixture of a polar cyclic olefin monomer and a non-polar cyclic olefin monomer .
[5] The method of claim 1, wherein a polymerization temperature is in the range of
20-150°C.
[6] The method of claims 1, wherein the cyclic olefin monomer and the polar vinyl
olefin monomer comprise a combination of two cyclic olefin monomers having different functional groups and a polar olefin monomer, or a combination of two polar vinyl olefin monomers having different functional groups and a cyclic olefin monomer.

[7] The method of claim 1, wherein the copolymer further comprises a non-polar
vinyl olefin monomer represented by formula (6) in addition to the cyclic olefm monomer and the polar vinyl monomer:
(Figure Removed)
(6)
where
each of R and R is independently a hydrogen atom; a halogen atom; a linear or branched C 1-20alkyl, alkenyl, or vinyl; a C5-12cycloalkyl optionally substituted by a hydrocarbon; a C6-40aryl optionally substituted by a hydrocarbon; a C7-15 aralkyl optionally substituted by a hydrocarbon; or a C3-20 alkynyl.
[8] The method of claim 1, wherein the group 13 compound is the organoaluminium
compound represented by formula (7), and the radical initiator is the azo compund represented by formula (2): Al (R°) (OR1) (X) (7)
where Al is an aluminium atom; O is an oxygen atom; each of nl, n2, and n3 is independently an integer of 0-3 and nl+n2+n3=3; each of R0 and R1 is inde-pendently a hydrogen atom; a linear or branched C1-20 alkyl, alkenyl, or vinyl; a C
cycloalkyl optionally substituted by a hydrocarbon; a C6-40 aryl optionally substituted by a hydrocarbon; or a linear or branched C1-20 alkyl or aryl containing 1-10 hetreo atoms such as N, O, and halogen atoms; and X is a halogen atom; A-N=N-A (2)
where N is a nitrogen atom; and each of A and A is independently a hydrogen atom; a linear or branched C1-20 alkyl, alkoxy, alkenyl, or vinyl; a C 5-12 cycloalkyl optionally substituted by a hydrocarbon; a C6-40 aryl optionally substituted by a hydrocarbon; or a linear or branched C6-40 alkyl, alkoxy, alkenyl, aryl, or cy-
cloalkylhetero containing a cyano group, a carbonyl group, a carboxylic group,
an ether group, or an amide group;
[91 A copolymer produced by the method of any one of claims 1-8.
[10] The copolymer of claim 9, which comprises 0.1-99.9 mol% of a polar vinyl
olefin monomer.
[11] The copolymer of claim 9, which has a weight average molecular weight (Mw)
of 10,000 or greater.
[12] The copolymer of claim 9, which has a glass transition temperature (Tg) of 100

°C or greater.
[13] The copolymer of claim 9, which is a copolymer blend which further includes at
least one of a cyclic olefin monomer, a polar vinyl olefm monomer, a non-polar
vinyl olefm monomer, or a copolymer of a cyclic olefi n monomer and a polar
vinyl olefin.
[14] A polarizer protective film comprising a copolymer produced by the method of
any one of claims 1-8.
[15] An adhesive film comprising a copolymer produced by the method of any one of
claims 1-8.
[16] An optical anisotropic film comprising a copolymer produced by the method of
any one of claims 1-8.
[17] The optical anisotropic film of claim 16, which has a retardation value (R ) of 70
to 1000 nm, as defined by the following Equation 1 :

(Figure Removed)
where n is a refractive index of an in-plane fast axis measured at 550 nm, n is a

refractive index toward thickness direction measured at 550 nm, and d is a film
thickness.
[18] The optical anisotropic film of claim 16, which is a negative C-plate type optical
compensation film for liquid crystal display, satisfying a refractive index re-quirement of n @ n < n , in which n is a refractive index of an in-plane slow
axis, n is a refractive index of an in-plane fast axis, and n is a refractive index in

a direction through the film thickness.
[19] A liquid crystal display having a film comprising a copolymer produced by the
method of any one of claims 1-8.
[20] A plastic lens comprising a copolymer produced by the method of any one of
claims 1-8.