FORM 2
THE PATENTS ACT, 1970
(39 of 1970)
&
THE PATENTS RULES, 2003
COMPLETE SPECIFICATION (See section 10, rule 13)
“PHOTOELECTROCHEMICAL CELL AND ENERGY SYSTEM USING SAME”
PANASONIC CORPORATION, a Japanese Corporation of 1006, Oaza Kadoma, Kadoma-shi, Osaka 571-8501, Japan
The following specification particularly describes the invention and the manner in which it is to be performed.

DESCRIPTION
PHOTOELECTROCHEMICAL CELL AND ENERGY SYSTEM USING SAME
5 TECHNICAL FIELD
[0001] The present invention relates to a photoelectrochemical cell in which water is decomposed by irradiation with light and to an energy system using the photoelectrochemical cell.
10 BACKGROUND ART
[0002] There is a conventionally known technique for decomposing water by irradiating a semiconductor material that acts as a photocatalyst with light to obtain hydrogen and oxygen (see, for example, Patent Literature l). There is another known technique for rendering the surface of a base material hydrophilic by
15 coating the surface of the base material with the semiconductor material (see, for example, Patent Literature 2).
[0003] Patent Literature 1 discloses a method in which an n-type semiconductor electrode and a counter electrode are disposed in an electrolyte and the surface of the n-type semiconductor electrode is irradiated with light, so that hydrogen and
20 oxygen are obtained from the surfaces of both electrodes. Specifically, Patent
Literature 1 describes that a Ti02 electrode, a ZnO electrode, a CdS electrode, and the like can be used as the n'type semiconductor electrode. [0004] Patent Literature 2 discloses a hydrophilic member. This hydrophilic member is formed of a base material and a coating layer formed on the surface of
25 the base material. The coating layer has a titanium oxide layer that contains titanium oxide particles, and an island-shaped portion that is disposed on the titanium oxide layer and that is made of a second photocatalytic material other than titanium oxide. Specifically, Patent Literature 2 describes the use, as the second photocatalytic material, of a material having potentials at the bottom of the
30 conduction band and the top of the valence band on a more positive side relative to the standard hydrogen electrode potential (i.e., a more negative side relative to the vacuum level) than titanium oxide.
[0005] There is also proposed a photocatalytic thin film that exhibits highly efficient photocatalytic performance under natural light (see Patent Literature 3).
35 This photocatalytic thin film is a film obtained by injecting ions of at least one of
metals such as Nb, V and Cr into a photocatalytic thin film formed on a base. This film is a gradient film in which the band gap or the potential gradient changes in

the thickness direction.
[0006] Furthermore, there is also proposed a technique for producing hydrogen by irradiating a multilayer thin film photocatalyst with light (see Patent Literature 4). This multilayer thin film photocatalyst is formed by disposing a first compound 5 semiconductor layer and a second compound semiconductor layer having a band gap different from that of the first compound semiconductor layer sequentially on an electrically conductive base material. Hydrogen is produced by immersing this multilayer thin film photocatalyst in a solution containing hydrogen sulfide and then irradiating this multilayer thin film photocatalyst with light.
10
JP51(1976)-123779A JP 2002-234105 A JP 2002-143688 A JP 2003-154272 A
CITATION LIST Patent Literature [0007] Patent Literature 1 Patent Literature 2
15 Patent Literature 3
Patent Literature 4
SUMMARY OF INVENTION
Technical Problem
20 [0008] However, the method described in Patent Literature 1 suffers from a
problem of a low quantum efficiency for the water-splitting reaction by irradiation with light. This is because it is highly probable that holes and electrons generated by photoexcitation disappear due to recombination thereof before being used for the electrolytic reaction of water.
25 [0009] Patent Literature 2 describes that, among electrons and holes generated by photoexcitation, the electrons transfer to the conduction band of the second photocatalytic material and the holes transfer to the valence band of the titanium oxide, so that the electron-hole pairs are separated, which decreases the probability of the recombination of the holes and electrons. However, in Patent Literature 2,
30 there is no description about the energy state to be set at the junction plane
between the titanium oxide and the second photocatalytic material. When the junction plane between the titanium oxide and the second photocatalytic material forms a Schottky junction, Schottky barriers are formed at the junction plane in the conduction band and the valence band. At this time, among the electrons and
35 holes generated by photoexcitation, the electrons are confined by the Schottky
barrier in the conduction band at the junction plane. On the other hand, the holes are accumulated around the junction plane of the valence band by the Schottky

barrier that serves as a hole stopper in the valence band at the junction plane. Therefore, the configuration disclosed in Patent Literature 2 has a problem that the probability of recombination of electrons and holes is increased, compared to the case where the titanium oxide and the second photocatalytic material each are used 5 independently
[0010] The photocatalyst thin film described in Patent Literature 3 is made into a gradient film by metal ion doping. However, this configuration has been developed for the purpose of extending the utilized region to the visible light region and improving the light-use efficiency by making a photocatalyst thin film into a
10 gradient film. Therefore, in Patent Literature 3, there is no description about the photocatalytic energy state to be set in the gradient film. This means that the optimization of charge separation and the like is not performed in this photocatalyst thin film. [0011] A multilayer thin film photocatalyst described in Patent Literature 4 has a
15 structure in which two semiconductors, CdS and ZnS, each having a band gap
different from the other, are joined, and the semiconductor ZnS further is joined to an electrically conductive base material Pt. Patent Literature 4 describes that since these materials with different band gaps are joined, electrons can transfer to the semiconductor ZnS, and further to the electrically conductive base material Pt
20 along the gradient of the band gaps, and therefore can be coupled easily to hydrogen ions on the electrically conductive base material, which facilitates the generation of hydrogen (Paragraphs [0026] and [0027] in Patent Literature 4). However, in this multilayer thin film photocatalyst, no consideration is given to the Fermi level (vacuum reference level) of each of the materials. Accordingly, although this
25 configuration allows the electrons to transfer along the gradient of the band gaps, it hardly allows the electrons to transfer smoothly
[0012] In view of such conventional problems, it is an object of the present invention to provide a photoelectrochemical cell capable of efficient charge separation between electrons and holes generated by photoexcitation and thus
30 improving the quantum efficiency of the hydrogen evolution reaction by irradiation with light. It is a further object of the present invention to provide an energy system using such a photoelectrochemical cell.
Solution to Problem 35 [0013] In order to achieve the above objects, the present invention provides a
photoelectrochemical cell including: a semiconductor electrode including a conductor and a semiconductor layer disposed on the conductor; a counter electrode connected

electrically to the conductor; an electrolyte in contact with surfaces of the semiconductor layer and the counter electrode; and a container accommodating the semiconductor electrode, the counter electrode and the electrolyte. In this photoelectrochamical cell, a band edge level Ecs of a conduction band, a band edge 5 level Evs of a valence band, and a Fermi level EFS in a surface near-field region of the semiconductor layer, and a band edge level ECJ of a conduction band, a band edge level EVJ of a valence band, and a Fermi level EFJ in a junction plane near-field region of the semiconductor layer with the conductor satisfy, relative to a vacuum level, Ecs - EFs > ECJ - EFj, EFS - Evs < EFJ - EVJ, ECJ > -4.44 eV, and EVs < "5.67 eV,
10 and the Fermi level EFS in the surface near-field region of the semiconductor layer and the Fermi level EFJ in the junction plane near-field region of the semiconductor layer with the conductor satisfy, relative to the vacuum level, -5.67 eV < EFS < "4.44 eV and -5.67 eV < EFJ < -4.44 eV, respectively. [0014] The present invention further provides an energy system including^ the
15 photoelectrochemical cell of the present invention; a hydrogen storage, connected to the photoelectrochemical cell by a first pipe, for storing hydrogen generated inside the photoelectrochemical cell; and a fuel cell, connected to the hydrogen storage by a second pipe, for converting the hydrogen stored in the hydrogen storage into electricity.
20
Advantageous Effects of Invention
[0015] The photoelectrochemical cell of the present invention makes it possible to achieve efficient charge separation between electrons and holes generated by photoexcitation. Thus, the photoelectrochemical cell of the present invention
25 makes it possible to improve the quantum efficiency of the hydrogen evolution
reaction by irradiation with light. Since the energy system of the present invention is provided with such a photoelectrochemical cell, efficient power supply is achieved.
BRIEF DESCRIPTION OF DRAWINGS
30 [0016] Fig. 1 is a schematic view illustrating a configuration of the photoelectrochemical cell of Embodiment 1 of the present invention.
Fig. 2 is a conceptual diagram indicating a band structure of a conductor, a first semiconductor layer and a second semiconductor layer, before being joined, which constitute a semiconductor electrode in the photoelectrochemical cell of 35 Embodiment 1 of the present invention.
Fig. 3 is a conceptual diagram indicating a band structure of the conductor, the first semiconductor layer and the second semiconductor layer, after being joined,

which constitute the semiconductor electrode in the photoelectrochemical cell of Embodiment 1 of the present invention.
Fig. 4 is a schematic view illustrating a configuration of the
photoelectrochemical cell of Embodiment 2 of the present invention.
5 Fig. 5 is a schematic view illustrating a configuration of the
photoelectrochemical cell of Embodiment 3 of the present invention.
Fig. 6 is a schematic view illustrating a configuration of the photoelectrochemical cell of Embodiment 4 of the present invention.
Fig. 7 is a schematic view illustrating a configuration of the energy system 10 of Embodiment 5 of the present invention.
DESCRIPTION OF EMBODIMENTS
[0017] Hereinafter, the embodiments of the present invention are described in detail with reference to the drawings. The embodiments described below are
15 examples and the present invention is not limited to the following embodiments. Furthermore, in the following embodiments, the same members are indicated with identical numerals and the same descriptions thereof may be omitted. [0018] (Embodiment l)
The configuration of the photoelectrochemical cell according to Embodiment
20 1 of the present invention is described with reference to Fig. 1 to Fig. 3. Fig. 1 is a schematic view illustrating the configuration of the photoelectrochemical cell of the present embodiment. Fig. 2 is a conceptual diagram indicating a band structure of a conductor, a first semiconductor layer and a second semiconductor layer, before being joined, which constitute a semiconductor electrode in the photoelectrochemical
25 cell of the present embodiment. Fig. 3 is a conceptual diagram indicating a band structure of the conductor, the first semiconductor layer and the second semiconductor layer, after being joined, which constitute the semiconductor electrode in the photoelectrochemical cell of the present embodiment. In each of Figs. 2 and 3, the vertical axis indicates energy levels relative to the vacuum level
30 (unit: eV). Here, an embodiment in which n-type semiconductors are used for the first semiconductor layer and the second semiconductor layer that constitute the semiconductor electrode is described.
[0019] As illustrated in Fig. 1, a photoelectrochemical cell 100 of the present embodiment includes a semiconductor electrode 120, a counter electrode 130, an
35 electrolyte 140, and a container 110. The counter electrode 130 is an electrode paired with the semiconductor electrode 120. The electrolyte 140 contains water. The container 110 accommodates the semiconductor electrode 120, the counter

electrode 130 and the electrolyte 140, and has an opening.
[0020] The semiconductor electrode 120 and the counter electrode 130 are disposed inside the container 110 so that the surfaces thereof are in contact with the electrolyte 140. The semiconductor electrode 120 includes a conductor 121, a first 5 semiconductor layer 122 disposed on the conductor 121 and a second semiconductor layer 123 disposed on the first semiconductor layer 122. That is, the semiconductor electrode 120 in the present embodiment is a semiconductor electrode in which the first to Nth (N is an integer of 2 or more) semiconductor layers are formed on the conductor 121, and in this case, N is 2. In the present embodiment, a
10 semiconductor layer that constitutes the semiconductor electrode 120 includes the first semiconductor layer 122 and the second semiconductor layer 123 that are disposed in this order on the conductor 121. A portion of the container 110 facing the second semiconductor layer 123 of the semiconductor electrode 120 that is disposed inside the container 110 (which is, hereinafter, abbreviated as a light
15 incident portion 110a) is made of a material that transmits light, such as sunlight. [0021] The conductor 121 of the semiconductor electrode 120 is connected electrically to the counter electrode 130 by a conducting wire 150. Here, the counter electrode means an electrode that can exchange electrons with a semiconductor electrode without the intermediation of an electrolyte. Accordingly,
20 the counter electrode 130 in the present embodiment only have to be connected electrically to the conductor 121 that constitutes the semiconductor electrode 120. There is no limitation on the positional relationship and the like of the counter electrode 130 with the semiconductor electrode 120, [0022] Next, the band structure of the conductor 121, the first semiconductor layer
25 122 and the second semiconductor layer 123 in the semiconductor electrode 120 is described in detail.
[0023] As indicated in Fig. 2, the first semiconductor layer 122 and the second semiconductor layer 123 satisfy the following relationships, relative to the vacuum level-
30 Ec2" EF2 > Eci" EFI» EF2 " Ev2 < EFI " Evi» Eci > "4.44 eV; Ev2 < "5.67 eV; -5.67 eV < EFI < "4.44 eV; and
35 -5.67 eV < EF2 < "4.44 eV
where Eci is the band edge level of the conduction band of the first semiconductor layer 122, Evi is the band edge level of the valence band of the first semiconductor

layer 122, EFI is the Fermi level of the first semiconductor layer 122, Ec2 is the band edge level of the conduction band of the second semiconductor layer 123, Ev2 is the band edge level of the valence band of the second semiconductor layer 123, and EF2 is the Fermi level of the second semiconductor layer 123, respectively 5 [0024] That is, the semiconductor electrode 120 is set to satisfy the following (l) and (2):
(I) the difference value between the band edge level of the conduction band of the
second semiconductor layer 123 and the Fermi level of the second semiconductor
layer 123 is greater than that in the first semiconductor layer 122; and
10 (2) the difference value between the Fermi level of the first semiconductor layer 122 and the band edge level of the valence band of the first semiconductor layer 122 is greater than that in the second semiconductor layer 123.
[0025] Here, it is assumed that the first semiconductor layer 122 and the second semiconductor layer 123 are regarded as one semiconductor layer as a whole. In
15 this case, the second semiconductor layer 123 and the first semiconductor layer 122 can be regarded as the surface near-field region of the semiconductor layer and the junction plane near-field region thereof with the conductor 121, respectively Therefore, it can be said that the semiconductor electrode 120 of the present embodiment is set to satisfy the following (I) and (II), relative to the vacuum level:
20 (I) the difference value between the band edge level of the conduction band and the Fermi level in the surface near-field region of the semiconductor layer is greater than that in the junction plane near-field region of the semiconductor layer with the conductor; and
(II) the difference value between the Fermi level and the band edge level of the
25 valence band in the junction plane near-field region of the semiconductor layer with the conductor is greater than that in the surface near-field region of the semiconductor layer.
[0026] Furthermore, it can be said that the semiconductor electrode 120 of the present embodiment is set to satisfy the following (i) to (iv), relative to the vacuum
30 level:
(i) the band edge level ECJ of the conduction band in the junction plane near-field region of the semiconductor layer with the conductor is higher than -4.44 eV; (ii) the band edge level Evs of the valence band in the surface near-field region of the semiconductor layer is lower than -5.67 eV;
35 (0 the Fermi level EFJ in the junction plane near-field region of the semiconductor layer with the conductor satisfies -5.67 eV < EFJ < "4.44 eV; and (iv) the Fermi level EFS in the surface near-field region of the semiconductor layer

satisfies -5.67 eV < EFS < "4.44 eV.
[0027] A common material used as the conductor 121 has a higher Fermi level than the band edge level of its conduction band. Therefore, the difference value between the band edge level of the conduction band of the conductor 121 and the Fermi level 5 thereof (the band edge level of the conduction band - the Fermi level) is a negative value. That is, the above difference value in the conductor 121 is greater than that in the first semiconductor layer 122. Therefore, electrons transfer smoothly from the first semiconductor layer 122 to the conductor 121, as is the case with the transfer from the second semiconductor layer 123 to the first semiconductor layer
10 122, As a result, the hydrogen production efficiency is further improved. [0028] Furthermore, in the present embodiment, the Fermi level EFC of the conductor 121 is higher than the band edge level Eci of the conduction band of the first semiconductor layer 122, and higher than -4,44 eV. As used herein, a level "higher than -4.44 eV" relative to the vacuum level is equivalent to a level "lower
15 than 0V" relative to the standard hydrogen electrode potential. Therefore, the
Fermi level of the conductor 121 is lower than 0V, which is the reduction potential of water. As a result, hydrogen ions are reduced efficiently on the surface of the counter electrode 130 that is connected electrically to the conductor 121, so that hydrogen is generated efficiently.
20 [0029] Furthermore, in the semiconductor electrode 120, the band edge level Ev2 of the valence band of the second semiconductor layer 123 that is disposed in contact with the electrolyte 140 is lower than -5.67 eV. As used herein, a level "lower than ■5.67 eV" relative to the vacuum level is equivalent to a level "higher than 1.23 V" relative to the standard hydrogen electrode potential. Therefore, the band edge
25 level Ev2 of the valence band of the second semiconductor layer 123 is higher than 1.23 V, which is the oxidation potential of water. As a result, water is oxidized efficiently on the surface of the second semiconductor layer 123, so that oxygen is generated efficiently [0030] When the first semiconductor layer 122 and the second semiconductor layer
30 123 are in contact with the electrolyte at a pH of about 7 and a temperature of 25°C, it is desirable that their Fermi levels EFI and EF2 be set to satisfy -5.67 eV < EFI < ■4.44 eV and -5.67 eV < EF2 < "4.44 eV, respectively, relative to the vacuum level. When a device is designed so that the Fermi levels EFI and EF2 of the first semiconductor layer 122 and the second semiconductor layer 123 fall within these
35 ranges, the device can generate hydrogen using water in the form of almost fresh water. [0031] Next, the conductor 121, the first semiconductor layer 122 and the second

semiconductor 123 are joined to one another. In this case, at the junction plane between the first semiconductor layer 122 and the second semiconductor layer 123, carriers transfer so that the Fermi levels of these layers coincide, as indicated in Fig. 3. This results in bending of the band edge. At this time, the band edge level Ec2 5 of the conduction band, the band edge level Ev2 of the valence band, and the Fermi level EF2 of the second semiconductor layer 123 and the band edge level Eci of the conduction band, the band edge level Evi of the valence band, and the Fermi level EFI of the first semiconductor layer 122 satisfy the relationships of Ec2 " EF2 > Eci" EFI and EF2 " Ev2 < EFI " Evi, relative to the vacuum level. Therefore, no Schottky
10 barrier is formed at the junction plane between the first semiconductor layer 122 and the second semiconductor layer 123.
[0032] In the photoelectrochemical cell 100 of the present embodiment, it is desirable that the Fermi level EF2 of the second semiconductor layer 123, the Fermi level EFI of the first semiconductor layer 122, the Fermi level EFC of the conductor
15 121, and the Fermi level EFS of the electrolyte 140 be set to satisfy EFS > EFC > EFI > EF2. Therefore, no Schottky barrier is formed at the junction planes between the first semiconductor layer 122, the second semiconductor layer 123, the conductor 121, and the electrolyte 140. As a result, higher hydrogen production efficiency is achieved.
20 [0033] Also at the junction plane between the conductor 121 and the first
semiconductor layer 122, carriers transfer so that their Fermi levels coincide. This causes bending of the band edge around the junction plane of the first semiconductor layer 122. In the present embodiment, the Fermi level EFC of the conductor 121 is set higher than the Fermi level EFI of the first semiconductor layer
25 122, relative to the vacuum level. Therefore, the junction between the conductor 121 and the first semiconductor layer 122 is an ohmic contact. In the present embodiment, the Fermi level EFC of the conductor 121 is set higher than the Fermi level EFI of the first semiconductor layer 122 in order to generate hydrogen more efficiently. However, it is not limited to this. Even if the Fermi level EFC of the
30 conductor 121 is lower than the Fermi level EFI of the first semiconductor layer 122, it is possible to generate hydrogen.
[0034] Desirably, the Fermi level EFS of the electrolyte 140 satisfies the relationship of EFS > EFC > EFI > EF2. However, even if this relationship is not satisfied, it is possible to generate hydrogen.
35 [0035] When the above-mentioned semiconductor electrode 120 is placed in contact with the electrolyte 140, the band edge level Ec2 of the conduction band and the band edge level Ev2 of the valence band around the surface of the second

semiconductor layer 123 are raised at the interface between the second semiconductor layer 123 and the electrolyte 140. Thus, a space charge layer is formed around the surface of the second semiconductor layer 123. [0036] As a comparative embodiment, an embodiment in which the difference value 5 between the band edge level of the conduction band of the second semiconductor layer and the Fermi level of the second semiconductor layer is smaller than that in the first semiconductor layer, relative to the vacuum level, is assumed. In this case, a square well potential is developed in the band edge level of the conduction band inside the second semiconductor layer due to the bending of the band edge of the
10 conduction band around the surface of the second semiconductor layer and the difference in the band edge level of the conduction band between the first semiconductor layer and that of the second semiconductor layer. This square well potential causes the electrons to be accumulated inside the second semiconductor layer. As a result, the probability of the recombination between the electrons and
15 holes generated by photoexcitation increases.
[0037] In contrast, in the photoelectrochemical cell 100 of the present embodiment, the difference value between the band edge level of the conduction band of the second semiconductor layer 123 and the Fermi level of the second semiconductor layer 123 is set greater than that in the first semiconductor layer 122. Accordingly,
20 no square well potential as mentioned above occurs in the band edge level of the conduction band inside the second semiconductor layer 123. Therefore, the electrons are not accumulated inside the second semiconductor layer 123 and can transfer toward the side of the first semiconductor layer 122. As a result, the efficiency of charge separation is improved significantly.
25 [0038] As another comparative embodiment, an embodiment in which the
difference value between the Fermi level of the first semiconductor layer 122 and the band edge level of the valence band of the first semiconductor layer 122 is smaller than that in the second semiconductor layer 123, relative to the vacuum level, is assumed. In this case, a square well potential is developed in the band
30 edge level of the valence band inside the second semiconductor layer due to the bending of the band edge of the valence band around the surface of the second semiconductor layer and the difference in the band edge level of the valence band between the first semiconductor layer and the second semiconductor layer. This square well potential causes the holes that have been generated inside the second
35 semiconductor layer by photoexcitation to transfer separately in the interface direction with the electrolyte and in the interface direction with the first semiconductor layer.

[0039] In contrast, in the photoelectrochemical cell 100 of the present embodiment, the difference value between the Fermi level of the first semiconductor layer 122 and the band edge level of the valence band of the first semiconductor layer 122 is set greater than that in the second semiconductor layer 123. Accordingly, no 5 square well potential as mentioned above occurs in the band edge level of the
valence band inside the second semiconductor layer 223. Therefore, the holes are not accumulated inside the second semiconductor layer 123 and can transfer toward the interface direction with the electrolyte. As a result, the efficiency of charge separation is improved significantly.
10 [0040] The photoelectrochemical cell 100 of the present embodiment causes band bending but forms no Schottky barrier at the interface between the first semiconductor layer 122 and the second semiconductor layer 123. As a result, among the electrons and holes generated by photoexcitation inside the second semiconductor layer 123, the electrons transfer to the conduction band of the first
15 semiconductor layer 122, and the holes transfer in the valence band toward the interface direction with the electrolyte. Therefore, an efficient charge separation between the electrons and holes is achieved without being blocked by Schottky barriers. This reduces the probability of the recombination between the electrons and holes generated by photoexcitation inside the second semiconductor layer 123.
20 As a result, the quantum efficiency of the hydrogen evolution reaction by irradiation with light is improved.
[0041] Furthermore, in the photoelectrochemical cell 100 of the present embodiment, the Fermi level of the conductor 121 is set higher than the Fermi level of the first semiconductor layer 122. This configuration forms no Schottky barrier
25 also at the junction plane between the conductor 121 and the first semiconductor layer 122. Therefore, the electrons can transfer from the first semiconductor layer 122 to the conductor 121 without being blocked by Schottky barriers. This further reduces the probability of the recombination between the electrons and holes generated by photoexcitation inside the second semiconductor layer 123. As a
30 result, the quantum efficiency of the hydrogen evolution reaction by irradiation with light is further improved.
[0042] It should be noted that the Fermi level, the potential (band edge level) at the bottom of the conduction band, and the potential (band edge level) at the top of the valence band of each of the first semiconductor layer 122 and the second
35 semiconductor layer 123 can be calculated using the flat band potential and carrier concentration. The flat band potential and carrier concentration of a semiconductor can be determined from a Mott-Schottky plot obtained by

measurement using, as an electrode, the semiconductor to be measured. These energy levels can also be determined physically by ultraviolet photoelectron spectroscopy (UPS) or by measurement using an atmospheric photoelectron spectrometer (AC-3, Riken Keiki Co., Ltd.). 5 [0043] The potential (band edge level) at the top of the valence band of each of the first semiconductor layer 122 and the second semiconductor layer 123 can be calculated using the band gap and the potential at the bottom of the conduction band of each of the semiconductor layer 122 and the second semiconductor layer 123 calculated by the above-mentioned method. Here, the band gap of each of the
10 semiconductor layer 122 and the second semiconductor layer 123 can be obtained from the optical absorption edge observed in the measurement of the light absorption spectrum of the semiconductor to be measured.
[0044] The Fermi level of the conductor 121 can be determined, for example, by photoelectron spectroscopy.
15 [0045] Next, the material of each constituent member provided in the photoelectrochemical cell 100 of the present embodiment is described. [0046] First, the materials of the first semiconductor layer 122 and the second semiconductor layer 123 in the present embodiment are described. In the present embodiment, however, the case where n-type semiconductors are used is described.
20 [0047] N-type semiconductors whose band structures satisfy the above-described relationships can be selected for the first semiconductor layer 122 and the second semiconductor 123 layer. Therefore, there is no limitation on the materials for the first semiconductor layer 122 and the second semiconductor layer 123. Preferably, one selected from the group consisting of oxide, nitride and oxynitride is used as the
25 n-type semiconductors for the first semiconductor layer 122 and the second
semiconductor layer 123. With the use of these materials, the first semiconductor layer 122 and the second semiconductor layer 123 are prevented from dissolving in the electrolyte 140, in a state where the semiconductor electrode 120 is in contact with the electrolyte 140. Accordingly, the photoelectrochemical cell can operate
30 stably.
[0048] In the present embodiment, the junction between the conductor 121 of the semiconductor electrode 120 and the first semiconductor layer 122 is an ohmic contact. Accordingly, for the conductor 121, electrically conductive materials, such as ITO (Indium Tin Oxide) and FTO (Fluorine-doped Tin Oxide), or metals such as
35 Ti, Ni, Ta, Nb, Al and Ag, can be used, for example.
[0049] It is preferable that, in the surface of the conductor 121, the area that is not covered by the first semiconductor layer 122 be coated, for example, with an

insulating material such as a resin. With such a configuration, the conductor 121 can be prevented from dissolving in the electrolyte 140. [0050] A material with a low overvoltage is used preferably for the counter electrode 130. In the present embodiment, hydrogen is generated at the counter 5 electrode 130. Therefore, Pt, Au, Ag, Fe, or the like is used preferably as the counter electrode 130, for example.
[0051] Any electrolyte containing water can be used for the electrolyte 140. The electrolyte containing water may be acidic or alkali. In the case where a solid electrolyte is disposed between the semiconductor electrode 120 and the counter
10 electrode 130, the electrolyte 140 in contact with the surface of the second
semiconductor layer 123 of the semiconductor electrode 120 and the surface of the counter electrode 130 can be replaced by pure water for electrolysis. [0052] Next, the operation of the photoelectrochemical cell 100 of the present embodiment is described.
15 [0053] When the second semiconductor layer 123 of the semiconductor electrode 120 disposed inside the container 110 is irradiated with sunlight from the light incident portion 110a of the container 110 in the photoelectrochemical cell 100, electrons are generated in the conduction band and holes are generated in the valence band in the second semiconductor layer 123. The holes generated at this
20 time transfer toward the surface side of the second semiconductor layer 123.
Thereby, water is decomposed on the surface of the second semiconductor layer 123 according to the reaction formula (1) below, so that oxygen is generated. On the other hand, the electrons transfer toward the conductor 121 along the bending of the band edge of the conduction band at the interface between the second
25 semiconductor layer 123 and the first semiconductor layer 122 and at the interface between the first semiconductor layer 122 and the conductor 121. The electrons that have transferred to the conductor 121 transfer toward the side of the counter electrode 130 connected electrically to the semiconductor electrode 120 through the conducting wire 150. Thereby hydrogen is generated on the surface of the counter
30 electrode 130 according to the reaction formula (2) below. [0054] Formula (1):
4h++2H20 -> 02T+4H+ (1)
Formula (2):
4e"+4H+ -> 2H2T (2)
35

[0055] At this time, no Schottky barrier is formed at the junction plane between the first semiconductor layer 122 and the second semiconductor layer 123. Therefore, the electrons can transfer from the second semiconductor layer 123 to the first semiconductor layer 122 without being blocked. 5 [0056] Furthermore, no Schottky barrier is formed also at the junction plane
between the first semiconductor layer 122 and the conductor 121. Therefore, the electrons can transfer from the first semiconductor layer 122 to the conductor 121 without being blocked. This reduces the probability of the recombination between the electrons and holes generated by photoexcitation inside the second
10 semiconductor layer 123. As a result, the quantum efficiency of the hydrogen evolution reaction by irradiation with light is further improved. [0057] In the present embodiment, the case where n-type semiconductors are used for the semiconductor electrode 120 have been described. However, also in the case where p-type semiconductors are used, the same operational effects are obtained if
15 the band structures of the first semiconductor layer 122 and the second semiconductor layer 123 satisfy the relationships described in the present embodiment.
[0058] When p-type semiconductors are used, oxides, chalcogenides, sulfides, nitrides, oxynitrides, phosphides, and the like, containing barium, strontium,
20 calcium, zirconium, titanium, cerium, gadolinium, gallium, indium, yttrium, ytterbium, and/or scandium, as constituent elements, can be used for the first semiconductor layer 122 and the second semiconductor layer 123. [0059] As a p-type semiconductor for the first semiconductor layer 122, an oxide containing barium, zirconium, and indium, as constituent elements, is used
25 preferably. The use of such an oxide allows the Fermi level EFI of the first
semiconductor layer 122 to be set higher than -5.67 eV but lower than -4.44 eV, relative to the vacuum level. That is, the Fermi level of the first semiconductor layer 122 can be set higher than 0V but lower than 1.23 V, relative to the standard hydrogen electrode potential. The first semiconductor layer 122 may be an oxide of
30 barium, zirconium and indium, a composite oxide thereof, or a mixture of such oxide and composite oxide. The first semiconductor layer 122 may be the above-mentioned compound additionally containing metal ions other than indium ions. An oxide containing barium, zirconium, cerium, and indium, as constituent elements, also can be used suitably.
35 [0060] For example, the p-type semiconductor may contain at least one selected from perovskite-type oxide semiconductors represented by the following general formulae A and B^

BaZri-xMx03-a (General Formula A) where M denotes at least one element selected from trivalent elements, x denotes a numerical value of more than 0 and less than 1 (preferably less than 0.5), and a denotes an amount of oxygen deficiency that is a numerical value of more than 0 5 and less than 1.5; and
BaZrxCeyMi-x-y03-a (General Formula B) where M denotes at least one element selected from trivalent elements, x denotes a numerical value of more than 0 and less than 1, y denotes a numerical value of more than 0 and less than 1, x + y < 1 is satisfied, and a denotes an amount of oxygen
10 deficiency that is a numerical value of more than 0 and less than 1.5.
[0061] An oxide containing barium, zirconium and indium as constituent elements or an oxide containing barium, zirconium, cerium and indium as constituent elements are also used suitably for the second semiconductor layer 123, as is the case with the first semiconductor layer 122. Furthermore, a material containing at
15 least one selected from semiconductors represented by the above general formula A and general formula B also can be used. The carrier concentration of the p-type semiconductor in the second semiconductor layer 123 preferably is lower than the carrier concentration of the p-type semiconductor in the first semiconductor layer 122. The p-type semiconductor in the second semiconductor layer 123 preferably is
20 one selected from the group consisting of oxide, nitride and oxynitride. With the use of these materials, the second semiconductor layer 123 is prevented from dissolving in the electrolyte 140, even if the second semiconductor layer 123 is irradiated with light in a state where the semiconductor electrode 120 is in contact with the electrolyte 140. Accordingly the photoelectrochemical cell can operate
25 stably.
[0062] When an oxide containing barium, zirconium and indium as constituent elements is used as a p-type semiconductor for the first semiconductor layer 123, an oxide containing, for example, barium, zirconium, cerium and indium as constituent elements can be used as a p-type semiconductor for the second semiconductor layer
30 123.
[0063] In the present embodiment, preferable examples of p-type semiconductors used to form a semiconductor layer include BaZro.95lno.os03-a, BaZro.9Ino.1O3a, BaZro.875lno.i2503-a> BaZr0.85lno.i503-a, BaZro.sIno.2O3a, BaZro.75lno.2s03-a, BaZro.8Gao.2O3a, BaZro.9Gao.1O3a, BaZro.8Gdo.2O3a, BaZro.9Gdo.1O3a, BaZro.8Yo.2O3a,
35 BaZro.4Ceo.4Ino.2O3a, and BaZro.6Ceo.2Ino.2O3a. Table 1 shows the band edge levels (Ec) of the conduction bands, the band edge levels (Ey) of the valence bands, and the Fermi levels (EF) of these p-type semiconductors. Table 1 also shows the difference

values (Ec _ EF) between the band edge levels of the conduction bands and the Fermi levels and the difference values (EF - Ev) between the band edge levels of the valence bands and the Fermi levels.
[0064] Table 1

P'type semiconductor Ec (eV) EC-EF (eV) EF (eV) Ev (eV) EF-Ev (eV)
BaZro.95lno.o503-a ■2.94 2.14 ■5.08 ■5.69 0.61
BaZro.9Ino.1O3a
■3.21 1.87 ■5.08 ■5.71 0.63
BaZro.875lno.l2503-a ■3.72 1.36 ■5.08 ■5.72 0.64
BaZro.ssIiio.isOs-a ■4.02 1.06 ■5.08 ■5.72 0.64
BaZro.8lno.2O3a
■4.29 0.79 ■5.08 ■5.74 0.65
BaZro.75lno.2503-a ■4.40 0.68 ■5.08 ■5.68 0.66
BaZro.8Grao.2O3a
•3.71 1.37 ■5.08 ■5.77 0.69
BaZro.9Grao.1O3a
■3.56 1.52 ■5.08 ■5.76 0.68
BaZro.8Grdo.203-a ■3.55 1.53 ■5.08 ■5.85 0.77
BaZro.9Gdo.i03-a ■3.04 2.04 ■5.08 ■5.84 0.76
BaZro.8Yo.2O3a
•4.07 1.01 ■5.08 ■5.87 0.79
BaZro.4Ceo.4Ino.2O3a
•3.85 1.23 ■5.08 ■5.85 0.77
BaZro.6Ceo.2Gdo.2O3a
■3.30 1.78 ■5.08 ■5.90 0.82
5
[0065] It should be noted that a configuration in which the semiconductor layer provided on the conductor includes the first semiconductor layer and the second semiconductor layer (i.e., a configuration in which two semiconductor layers are provided on the conductor) is shown in the present embodiment. However, the
10 configuration of the photoelectrochemical cell of the present invention is not limited to this. In the photoelectrochemical cell of the present invention, the semiconductor layer provided on the conductor may include the first to Nth (N is an integer of 2 or more) semiconductor layers that are disposed in this order on the conductor. Therefore, it also is possible to use a semiconductor electrode in which
15 three or more semiconductor layers are provided on a conductor. In the
configuration in which N semiconductor layers are provided on a conductor, two adjacent layers selected from the first to Nth semiconductor layers are referred to as the (K-l)th (K is an integer of 2 to N) semiconductor layer and the Kth semiconductor layer from the side of the conductor. In this case, the (K-l)th
20 semiconductor layer and the Kth semiconductor layer can be set to satisfy the following relationships, relative to the vacuum level: ECK " EFK > EC(K-D " EF(K-I)J EFK " EVK < EF(K-I) " EV(K-I)>* EC(K-I) > -4.44 eV;

EvK<-5.67eV;
■5.67 eV < EFCK-I) < "4.44 eV; and •5.67 eV ECJ ■ EFJJ EFS " Evs < EFJ " EvjJ ECJ > -4.44 eV; Evs <-5.67 eV; -5.67 eV < EFj < "4.44 eV; and
25 -5.67 eV< EFS < "4.44 eV
where ECJ is the band edge level of the conduction band in the junction plane near-field region of the semiconductor layer with the conductor, EVJ is the band edge level of the valence band in the junction plane near-field region of the semiconductor layer with the conductor, EFJ is the Fermi level in the junction plane near-field
30 region of the semiconductor layer with the conductor, Ecs is the band edge level of the conduction band in the surface near-field region of the semiconductor layer, Evs is the band edge level of the valence band in the surface near-field region of the semiconductor layer, and EFS is the Fermi level in the surface near-field region of the semiconductor layer, respectively.
35 [0067] Embodiment 2
The configuration of the photoelectrochemical cell according to Embodiment 2 of the present invention is described with reference to Fig. 4. Fig. 4 is a

schematic view illustrating the configuration of the photoelectrochemical cell of the present embodiment.
[0068] In a photoelectrochemical cell 200 of the present embodiment, a semiconductor electrode 220 includes a conductor 221, a first semiconductor layer 5 222 disposed on the conductor 221, and a second semiconductor layer 223 disposed on the first semiconductor layer 222. The semiconductor electrode 220 further includes an insulation layer 224 disposed on the surface of the conductor 221 opposite to the surface on which the first semiconductor layer 222 is disposed. The conductor 221, the first semiconductor layer 222 and the second semiconductor layer
10 223, respectively, have the same structures as those of the conductor 121, the first semiconductor layer 122 and the second semiconductor layer 123 in Embodiment 1. The insulation layer 224 is formed, for example, of resin or glass. This insulation layer 224 can prevent the conductor 221 from dissolving in the electrolyte 140. In the present embodiment, a configuration in which an insulation layer as mentioned
15 above is additionally provided on a semiconductor electrode including two
semiconductor layers as shown in Embodiment 1 is adopted. Such an insulation layer can be employed also for each of the semiconductor electrodes described in Embodiment 1, one including three or more semiconductor layers and the other including a semiconductor layer with a gradient composition.
20 [0069] Embodiments
The configuration of the photoelectrochemical cell according to Embodiment 3 of the present invention is described with reference to Fig. 5. Fig. 5 is a schematic view illustrating the configuration of the photoelectrochemical cell of the present embodiment.
25 [0070] In a photoelectrochemical cell 300 of the present embodiment, a
semiconductor electrode 320 includes a conductor 321, a first semiconductor layer 322 disposed on the conductor 321 and a second semiconductor layer 323 disposed on the first semiconductor layer 322. On the other hand, a counter electrode 330 is disposed on the conductor 321 (on the surface of the conductor 321 opposite to the
30 surface on which the first semiconductor layer 322 is disposed). The conductor 321, the first semiconductor layer 322 and the second semiconductor layer 323, respectively, have the same structures as those of the conductor 121, the first semiconductor layer 122 and the second semiconductor layer 123 in Embodiment 1. [0071] As is the case with the present embodiment, the configuration in which the
35 counter electrode 330 is disposed on the conductor 321 can eliminate the need for a conducting wire for connecting the semiconductor electrode 320 electrically to the counter electrode 330. This can eliminate the ohmic loss derived from the

conducting wire, therefore further improving the quantum efficiency of the hydrogen evolution reaction by irradiation with light. Furthermore, with such a configuration, the semiconductor electrode 320 can be connected electrically to the counter electrode 330 by a simple and easy process. The present embodiment 5 shows a configuration in which the counter electrode 330 is disposed on the surface of the conductor 321 opposite to the surface on which the first semiconductor layer 322 is disposed. However, the counter electrode 330 is not limited to this configuration, and the counter electrode 330 can be disposed also on the same surface on which the first semiconductor layer 322 is disposed. In the present
10 embodiment, the above configuration in which a counter electrode is disposed on a conductor in a photoelectrochemical cell including two semiconductor layers as shown in Embodiment 1 is adopted. Such a configuration can be employed also for each of the semiconductor electrodes described in Embodiment 1, one including three or more semiconductor layers and the other including a semiconductor layer
15 with a gradient composition. [0072] Embodiment 4
The configuration of the photoelectrochemical cell according to Embodiment 4 of the present invention is described with reference to Fig. 6. Fig. 6 is a schematic view illustrating the configuration of the photoelectrochemical cell of the
20 present embodiment.
[0073] As indicated in Fig. 6, a photoelectrochemical cell 400 of the present embodiment includes a housing (container) 410, a semiconductor electrode 420, a counter electrode 430 and a separator 460. The separator 460 separates the inside of the housing 410 into two chambers: a first chamber 470 and a second chamber
25 480. An electrolyte 440 containing water is contained in each of the first chamber 470 and the second chamber 480.
[0074] The semiconductor electrode 420 is disposed at a position in contact with the electrolyte 440 inside the first chamber 470. The semiconductor electrode 420 includes a conductor 421, a first semiconductor layer 422 disposed on the conductor
30 421 and a second semiconductor layer 423 disposed on the first semiconductor layer 422. Furthermore, the first chamber 470 includes a first gas outlet 471 for discharging oxygen generated inside the first chamber 470 and a water inlet 472 for supplying water into the first chamber 470. A portion of the housing 410 that faces the second semiconductor layer 423 of the semiconductor electrode 420 disposed
35 inside the first chamber 470 (hereinafter, abbreviated as a light incident portion 410a) is made of a material that transmits light such as sunlight. [0075] On the other hand, the counter electrode 430 is disposed inside the second

chamber 480 at a position in contact with the electrolyte 440. The second chamber 480 includes a second gas outlet 481 for discharging hydrogen generated inside the second chamber 480.
[0076] The conductor 421 of the semiconductor electrode 420 is connected 5 electrically to the counter electrode 430 by a conducting wire 450.
[0077] The conductor 421, the first semiconductor layer 422 and the second semiconductor layer 423 of the semiconductor electrode 420 in the present embodiment, respectively, have the same structures as those of the conductor 121, the first semiconductor layer 122 and the second semiconductor layer 123 of the
10 semiconductor electrode 120 in Embodiment 1. Accordingly, the semiconductor electrode 420 has the same operational effects as those of the semiconductor electrode 120 of Embodiment 1. Furthermore, the counter electrode 430 and the electrolyte 440 respectively are the same as the counter electrode 130 and the electrolyte 140 in Embodiment 1.
15 [0078] The separator 460 is formed of a material that allows the electrolyte 440 to permeate itself and has a function of blocking gas generated inside each of the first chamber 470 and the second chamber 480. Examples of the material of the separator 460 include a solid electrolyte such as a solid polymer electrolyte. As the solid polymer electrolyte, an ion exchange membrane such as Nafion (registered
20 trademark) can be mentioned, for example. After the internal space of the
container is separated into two areas using such a separator, the electrolyte and the surface of the semiconductor electrode (i.e., the semiconductor layer) are made in contact in one of the areas while the electrolyte and the surface of the counter electrode are made in contact in the other area. With such a configuration, oxygen
25 and hydrogen generated inside the container can be separated easily.
[0079] It should be noted that the photoelectrochemical cell 400 using the semiconductor electrode 420 having the same structure as that of the semiconductor electrode 120 in Embodiment 1 is described in the present embodiment. However, it also is possible to use, for the photoelectrochemical cell 400, a semiconductor
30 electrode including three or more semiconductor layers or a semiconductor electrode including a semiconductor layer with a gradient composition, described also in Embodiment 1, instead of the semiconductor electrode 420. [0080] Embodiments
The configuration of the energy system according to Embodiment 5 of the
35 present invention is described with reference to Fig. 7. Fig. 7 is a schematic view illustrating the configuration of the energy system of the present embodiment. [0081] As indicated in Fig. 7, an energy system 500 of the present embodiment

includes the photoelectrochemical cell 400, a hydrogen storage 510, a fuel cell 520 and a storage battery 530.
[0082] The photoelectrochemical cell 400 is the photoelectrochemical cell described in Embodiment 4 and the specific configuration thereof is as illustrated in Fig. 6. 5 Therefore, detailed descriptions thereof are omitted.
[0083] The hydrogen storage 510 is connected to the second chamber 480 (see Fig. 6) of the photoelectrochemical cell 400 by a first pipe 541. The hydrogen storage 510 can be constituted, for example, by a compressor for compressing the hydrogen generated in the photoelectrochemical cell 400 and a high-pressure hydrogen tank
10 for storing the hydrogen compressed by the compressor.
[0084] The fuel cell 520 includes a power generator 521 and a fuel cell controller 522 for controlling the power generator 521. The fuel cell 520 is connected to the hydrogen storage 510 by a second pipe 542. The second pipe 542 is provided with a shutoff valve 543. For example, a solid polymer electrolyte fuel cell can be used as
15 the fuel cell 520.
[0085] The positive electrode and the negative electrode of the storage battery 530 respectively are connected electrically to the positive electrode and the negative electrode of the power generator 521 in the fuel cell 520 by a first line 544 and a second line 545. The storage battery 530 is provided with a capacity meter 546 for
20 measuring the remaining capacity of the storage battery 530. A lithium ion battery can be used as the storage battery 530, for example.
[0086] Next, the operation of the energy system 500 according to the present embodiment is described with reference also to Fig. 6. [0087] When the surface of the second semiconductor layer 423 of the
25 semiconductor electrode 420 disposed inside the first chamber 470 is irradiated with sunlight through the light incident portion 410a of the photoelectrochemical cell 400, electrons and holes are generated inside the second semiconductor layer 423. The holes generated at this time transfer toward the surface side of the second semiconductor layer 423. Thus, water is decomposed on the surface of the second
30 semiconductor layer 423 according to the above reaction formula (l), so that oxygen is generated.
[0088] On the other hand, the electrons transfer toward the conductor 421 along the bending of the band edge of the conduction band at the interface between the second semiconductor layer 423 and the first semiconductor layer 422 and at the
35 interface between the first semiconductor layer 422 and the conductor 421. The electrons that have transferred to the conductor 421 transfer toward the side of the counter electrode 430 connected electrically to the conductor 421 through the

conducting wire 450. Thus, hydrogen is generated on the surface of the counter electrode 430 according to the above reaction formula (2).
[0089] At this time, no Schottky barrier is formed at the junction plane between the second semiconductor layer 423 and the first semiconductor layer 422, as is the 5 case with the semiconductor electrode 120 in Embodiment 1. Therefore, the electrons can transfer from the second semiconductor layer 423 to the first semiconductor layer 422 without being blocked. Furthermore, no Schottky barrier is formed also at the junction plane between the first semiconductor layer 422 and the conductor 421. Therefore, the electrons can transfer to the conductor 421
10 without being blocked. Accordingly the probability of the recombination between the electrons and holes generated by photoexcitation inside the first semiconductor layer 423 is reduced. As a result, the quantum efficiency of the hydrogen evolution reaction by irradiation with light is improved. [0090] Oxygen generated inside the first chamber 470 is discharged from the first
15 gas outlet 471 to the outside of the photoelectrochemical cell 400. On the other hand, hydrogen generated inside the second chamber 480 is supplied into the hydrogen storage 510 through the second gas outlet 481 and the first pipe 541. [0091] In generating power in the fuel cell 520, the shutoff valve 543 is opened according to signals from the fuel cell controller 522, so that the hydrogen stored
20 inside the hydrogen storage 510 is supplied to the power generator 521 of the fuel cell 520 through the second pipe 542.
[0092] The electricity generated in the power generator 521 of the fuel cell 520 is stored inside the storage battery 530 through the first line 544 and the second line 545. The electricity stored inside the storage battery 530 is supplied to households,
25 enterprises, and the like through a third line 547 and a fourth line 548.
[0093] According to the photoelectrochemical cell 400, it is possible to improve the quantum efficiency of the hydrogen evolution reaction by irradiation with light. Thus, the energy system 500 of the present embodiment provided with this photoelectrochemical cell 400 can provide an efficient power supply.
30 [0094] In the present embodiment, an energy system using the
photoelectrochemical cell 400 described in Embodiment 4 is exemplified. The same effects can be obtained also when the photoelectrochemical cells 100, 200 and 300 described in Embodiments 1 to 3 each are used.
35 EXAMPLES
[0095] Hereafter, examples of the present invention are described specifically. [0096] (Example 1)

As Example 1, a photoelectrochemical cell having the same configuration as that of the photoelectrochemical cell 200 indicated in Fig. 4 was produced. The photoelectrochemical cell of Example 1 is described below with reference to Fig. 4. [0097] The photoelectrochemical cell 200 of Example 1 was provided with a 5 rectangular glass container (container 110) with an opening in the upper part, the semiconductor electrode 220 and the counter electrode 130. The glass container 110 held therein 0.01 mol/L Na2S03 aqueous solution containing 0.01 mol/L Na2S as the electrolyte 140. [0098] The semiconductor electrode 220 was produced according to the following
10 procedure.
[0099] First, a 150 nnrthick ITO film (sheet resistance 10 £2/sq.) as the conductor 221 was formed by sputtering on a 1 cm-square glass substrate as the insulation layer 224. Next, a 300 nnrthick BaZro.sIno.2O3a film as the first semiconductor layer 222 was formed by electrodeposition on the conductor 221. Finally a 1
15 jim-thick BaZro.9Ino.1O3a film as the second semiconductor layer 223 was formed also by electrodeposition on the first semiconductor layer 222. The semiconductor electrode 220 was disposed so that the surface of the second semiconductor layer 223 faced the light incident surface 110a of the glass container 110. [OlOO] A platinum plate was used as the counter electrode 130. A portion of the
20 conductor 221 of the semiconductor electrode 220 was connected electrically to the
counter electrode 130 by the conducting wire 150. The current flowing between the
semiconductor electrode 220 and the counter electrode 130 was measured with an
ammeter.
[OlOl] (Comparative Example l)
25 The first semiconductor layer 222 was not provided on the conductor 221 but
a BaZro.9Ino.1O3a film as the second semiconductor layer 223 was provided thereon in the semiconductor electrode 220 of Example 1. Except for this point, a photoelectrochemical cell of Comparative Example 1 was produced by the same procedure as used for the photoelectrochemical cell 200 of Example 1.
30 [0102] (Comparative Example 2)
A l|im-thick film of titanium oxide, which is an n-type semiconductor, was provided instead of the BaZro.9Ino.1O3a film provided as the second semiconductor layer 223 in the semiconductor electrode 220 of Example 1. Except for this point, a photoelectrochemical cell of Comparative Example 2 was produced by the same
35 procedure as used in Example 1. [0103] (Comparative Example 3)
A l|im-thick CU2O film was provided as the second semiconductor layer 223

instead of the BaZro.9Ino.1O3a film in the semiconductor electrode 220 of Example 1.
Except for this point, a photoelectrochemical cell of Comparative Example 3 was
produced by the same procedure as used in Example 1.
[0104] (Example 2)
5 As Example 2, a photoelectrochemical cell having the same configuration as
that of the photoelectrochemical cell 100 indicated in Fig. 1 was produced. The
photoelectrochemical cell of Example 2 is described below with reference to Fig. 1.
[0105] In the photoelectrochemical cell 100 of the present example, a Ti substrate
was used as the conductor 121. The photoelectrochemical cell 100 of the present 10 example is different from the photoelectrochemical cell 200 of Example 1 in that a
500 nm-thick BaZro.8lno.2O3a film as the first semiconductor layer 122 was formed
by electrodeposition on the conductor 121, a glass substrate as an insulation layer
was not provided on the back surface of the conductor 121, and the back surface of
the conductor 121 was coated with fluororesin. Since the configuration of the 15 photoelectrochemical cell 100 of the present example is the same as that of the
photoelectrochemical cell 200 of Example 1 except for these differences, the
description thereof is omitted.
[0106] (Example 3)
As Example 3, a photoelectrochemical cell having the same configuration as 20 that of the photoelectrochemical cell 300 indicated in Fig. 5 was produced. The
photoelectrochemical cell of Example 3 is described below with reference to Fig. 5.
[0107] The semiconductor electrode 320 and the counter electrode 330 were
produced according to the following procedure.
[0108] As the conductor 321, a 1 cm-square Ti substrate was used. A 500 25 nm-thick BaZro.4Ceo.4Ino.2O3a film as the first semiconductor layer 322 was formed
by electrodeposition on this Ti substrate. Next, a 1 ^m-thick BaZro.9Ino.1O3a film as
the second semiconductor layer 323 was formed by electrodeposition on the first
semiconductor layer 322, in the same manner as in Example 1. Finally, a 10
nm-thick Pt film as the counter electrode 330 was formed by sputtering on the back 30 surface of the Ti substrate as the conductor 321. The semiconductor electrode 320
was disposed so that the surface of the second semiconductor layer 323 faced the
light incident surface 110a of the glass container 110.
[0109] (Example 4)
As Example 4, a photoelectrochemical cell including a semiconductor 35 electrode in which first to third semiconductor layers were provided in this order on
a conductor was produced. Specifically, the photoelectrochemical cell of Example 4
has a configuration in which the third semiconductor layer is additionally provided

on the second semiconductor layer 223 in the semiconductor electrode 220 of the photoelectrochemical cell 200 indicated in Fig. 4. The photoelectrochemical cell of Example 4 is described below with reference to Fig. 4.
[0110] First, a 150 nm-thick ITO film (sheet resistance 10 £2/sq.) as the conductor 5 221 was formed by sputtering on a 1 cm-square glass substrate as the insulation layer 224. Next, a 300 nm-thick BaZro.sIno.2O3a film as the first semiconductor layer 222 was formed by electrodeposition on the conductor 221. Next, a 500 nm-thick BaZro.9Ino.1O3a film as the second semiconductor layer 223 was formed also by electrodeposition on the first semiconductor layer 222. Finally, a 1
10 jim-thick BaZro.gsIno.osOs-a film as the third semiconductor layer was formed also by electrodeposition on the second semiconductor layer 223. The semiconductor electrode 220 was disposed so that the surface of the third semiconductor layer faced the light incident surface 110a of the glass container 110. [0111] Since the configuration of the photoelectrochemical cell of Example 4 is the
15 same as that of the photoelectrochemical cell 200 of Example 1 except for these differences, the description thereof is omitted. [0112] (Example 5)
A photoelectrochemical cell of Example 5 was produced by the same procedure as used in Example 1, except that the materials of the first semiconductor
20 layer 222 and the second semiconductor layer 223 were replaced by n-type
semiconductors in the semiconductor electrode 220 of Example 1. As the first semiconductor layer 222, a 300 nm-thick Ti02 film was formed by electrodeposition. As the second semiconductor layer 223, a 500 nm-thick CdS film formed by sputtering on the first semiconductor layer 222 was used. The band edge level of
25 the conduction band of titanium oxide was -4.24 eV, the band edge level of the
valence band thereof was -7.44 eV, and the Fermi level thereof was -4.84 eV. The band edge level of the conduction band of CdS was -4.04 eV, the band edge level of the valence band thereof was -6.54 eV, and the Fermi level thereof was -5.24 eV. It should be noted that the values of the Fermi levels, the band edge levels of the
30 conduction bands, and the band edge levels of the valence bands are indicated
herein relative to the vacuum level. It should be noted that a vacuum level of -4.44 eV corresponds to a standard hydrogen electrode potential of 0 V. [0113] Tables 2 and 3 below indicate the materials, the Fermi levels (unit- eV), the band edge levels (unit: eV) of the conduction bands, and the band edge levels (unit:
35 eV) of the valence bands of the conductor, the p-type semiconductor and n-type
semiconductor used for the production of the semiconductor electrode in each of the photoelectrochemical cells of Examples 1 to 5 and Comparative Examples 1 to 3. It

should be noted that the Fermi levels of the semiconductors indicated herein are the values relative to the vacuum level. However, given that the pH value of the actually used electrolyte is about 7, the Fermi levels of the semiconductors are considered to be pulled down to the same level as the Fermi level of the electrolyte 5 at a pH of 7 and a temperature of 25°C by that Fermi level of the electrolyte.

[0114] Table 2

Conductor First
semiconductor
layer Second
semiconductor
layer Third
semiconductor
layer
Example 1 Material composition ITO BaZro.8lno.2O3a
BaZro.9Ino.1O3a
-

Fermi level -4.24 eV ■5.08 eV -5.08 eV ■

Conduction band - -4.29 eV -3.21 eV ■

Valence band - -5.74 eV -5.71 eV -
Example 2 Material composition Ti BaZro.8lno.2O3a
BaZro.9Ino.1O3a
-

Fermi level -4.33 eV -5.08 eV -5.08 eV ■

Conduction band - -4.29 eV -3.21 eV -

Valence band - -5.74 eV -5.71 eV -
Example 3 Material composition Ti BaZro.4Ceo.Jno.203-a BaZro.9Ino.1O3a
-

Fermi level ■4.33 eV -5.08 eV -5.08 eV -

Conduction band ■ -3.85 eV -3.21 eV -

Valence band - -5.85 eV -5.71 eV -
Example 4 Material composition ITO BaZro.8lno.2O3a
BaZro.9Ino.1O3a
BaZro.95lno.0503-a

Fermi level -4.24 eV -5.08 eV -5.08 eV -5.08 eV

Conduction band - -4.29 eV -3.21 eV -2.94 eV

Valence band ■ -5.74 eV -5.71 eV -5.69 eV
Example 5 Material composition ITO Ti02 CdS ■

Fermi level -4.24 eV -4.84eV -5.24 eV -

Conduction band - -4.24 eV -4.04 eV -

Valence band ■ -7.44 eV -6.54 eV -

[0115] Table 3

Conductor First
semiconductor
layer Second
semiconductor
layer
Comparative Example 1 Material composition ITO ■ BaZro.9Ino.1O3a

Fermi level ■4.24 eV - -5.08 eV

Conduction band - - -3.21 eV

Valence band - - -5.71 eV
Comparative Example 2 Material composition ITO BaZro.8lno.203-a Ti02

Fermi level -4.24 eV -5.08 eV -4.84eV

Conduction band - ■4.29 eV ■4.24 eV

Valence band - ■5.74 eV ■7.44 eV
Comparative Example 3 Material composition ITO BaZro.8lno.2O3a
Cu20

Fermi level -4.24 eV -5.08 eV ■4.99 eV

Conduction band ■ -4.29 eV -3.60 eV

Valence band - -5.71 eV ■5.62 eV
[0116] As seen from Table 2, in the semiconductor electrode in each of the photoelectrochemical cells of Examples 1 to 3, the band edge level of the conduction 5 band and the band edge level of the valence band of the second semiconductor layer, respectively were higher than the band edge level of the conduction band and the band edge level of the valence band of the first semiconductor layer. The Fermi level of the first semiconductor layer was the same as that of the second semiconductor layer. Therefore, a value obtained by subtracting the Fermi level of
10 the second semiconductor layer from the band edge level of the conduction band of the second semiconductor layer was greater than that in the first semiconductor layer. Furthermore, a value obtained by subtracting the band edge level of the conduction band of the second semiconductor layer from the Fermi level of the second semiconductor layer was smaller than that in the first semiconductor layer.
15 The Fermi levels of the semiconductors used in Examples 1 to 3 were -5.08 eV, which was within the range of -5.67 eV to -4.44 eV. The band edge levels of the conduction bands of the first semiconductor layers were higher than -4.44 eV. The

band edge levels of the valence bands of the second semiconductor layers were lower than -5.67 eV. Therefore, the photoelectrochemical cells of Examples 1 to 3 met the structural requirements of the semiconductor electrode of the present invention. [0117] The semiconductor electrode in the photoelectrochemical cell of Example 4 5 included the first to third semiconductor layers. The relationships between the band structures of two adjacent semiconductor layers (the third semiconductor layer and the second semiconductor layer, and the second semiconductor layer and the first semiconductor layer) satisfied the relationships between the semiconductor layers described in Embodiment 1. That is, the photoelectrochemical cell of
10 Example 4 corresponded to the cell including N = 3 semiconductor layers, among the photoelectrochemical cells including N semiconductor layers described in Embodiment 1.
[0118] In the photoelectrochemical cell of Example 5, n-type semiconductors were used for the first semiconductor layer and the second semiconductor layer. The
15 band edge level of the conduction band and the band edge level of the valence band of the second semiconductor layer, respectively, were higher than the band edge level of the conduction band and the band edge level of the valence band of the first semiconductor layer. The Fermi level of the first semiconductor layer was higher than that of the second semiconductor layer. Therefore, a value obtained by
20 subtracting the Fermi level of the second semiconductor layer from the band edge level of the conduction band of the second semiconductor layer was greater than that in the first semiconductor layer. Furthermore, a value obtained by subtracting the band edge level of the conduction band of the second semiconductor layer from the Fermi level of the second semiconductor layer was smaller than that
25 in the first semiconductor layer. The Fermi level of the first semiconductor layer and the Fermi level of the second semiconductor layer used in Example 5 were -4.84 eV and -5.24 eV, respectively, which were within the range of -5.67 eV to -4.44 eV. The band edge level of the conduction band of the first semiconductor layer was higher than -4.44 eV, and the band edge level of the valence band of the second
30 semiconductor layer was lower than "5.67 eV. Therefore, the photoelectrochemical cell of Example 5 met the structural requirements of the semiconductor electrode of the present invention.
[0119] In the semiconductor electrode in the photoelectrochemical cell of Comparative Example 3, a value obtained by subtracting the band edge level of the
35 valence band of the second semiconductor layer from the Fermi level of the second semiconductor layer was greater than that in the first semiconductor layer. Furthermore, the band edge level of the valence band of the second semiconductor

layer was higher than -5.67 eV. From these points, the photoelectrochemical cell of Comparative Example 3 did not meet the requirements of the photoelectrochemical cell of the present invention.
[0120] A simulated sunlight irradiation experiment was conducted on the thus 5 produced photoelectrochemical cells of Examples 1 to 5 and Comparative Example 1 to 3. The simulated sunlight irradiation experiment was conducted as follows. [0121] (Simulated Sunlight Irradiation Experiment)
A solar simulator manufactured by SERIC Ltd. was used to apply simulated sunlight. The surface of the second semiconductor layer (or the third
10 semiconductor layer) in the semiconductor electrode of each of the
photoelectrochemical cells of Examples 1 to 5 and Comparative Examples 1 to 3 was irradiated with simulated sunlight at an intensity of 1 kW/m2 through the light incident portion of each photoelectrochemical cell. The gas generated on the surface of the counter electrode was collected for 30 minutes. The components of
15 the collected gas were analyzed and the amount of the gas generated was
determined by gas chromatography. Furthermore, the density of the photocurrent flowing between the semiconductor electrode and the counter electrode was measured with an ammeter. The apparent quantum efficiency was calculated using the amount of the gas generated on the counter electrode.
20 [0122] Table 4 below indicates the apparent quantum efficiency measured for each of the photoelectrochemical cells of Examples 1 to 5 and Comparative Examples 1 to
3.
[0123] Table 4

Quantum efficiency
Example 1 20
Example 2 29
Example 3 32
Example 4 35
Example 5 15
Comparative Example 1 6
Comparative Example 2 •
Comparative Example 3 8
25 [0124] As a result of the analysis of the gas collected in the photoelectrochemical cell of the Example 1, it was confirmed that hydrogen was generated on the counter electrode. The rate of hydrogen generation was 1.8 x 10*7 L/s. Furthermore, since the photocurrent flowing between the semiconductor electrode and the counter electrode was 1.2 mA/cm2, it was confirmed that the electrolysis of water was

performed stoichiometrically. The apparent quantum efficiency was about 20%, as calculated using the following formula.
[0125] Apparent quantum efficiency = {(measured photocurrent density [mA/cm2]) / (photocurrent density obtainable by the sunlight to be possibly absorbed in the band 5 gap of the semiconductor material used for the second semiconductor layer [mA/cm2])} x 100
[0126] As a result of the analysis of the gas collected in the photoelectrochemical cell of the Comparative Example 1, it was confirmed that hydrogen was generated on the counter electrode. The rate of hydrogen generation was 7.0 x 10'8 L/s.
10 Furthermore, since the photocurrent flowing between the semiconductor electrode and the counter electrode was 0.42 mA/cm2, it was confirmed that the electrolysis of water was performed stoichiometrically. The apparent quantum efficiency was about 6%, as calculated using the above formula. [0127] As a result of the analysis of the gas collected in the photoelectrochemical
15 cell of the Comparative Example 3, it was confirmed that hydrogen was generated on the counter electrode. The rate of hydrogen generation was 8.5 x 108 L/s. Furthermore, since the photocurrent flowing between the semiconductor electrode and the counter electrode was 0.53 mA/cm2, it was confirmed that the electrolysis of water was performed stoichiometrically. The apparent quantum efficiency was
20 about 8%, as calculated using the above formula.
[0128] In view of these results, it is believed that, in the semiconductor electrode of the photoelectrochemical cell of Example 1, efficient charge separation between the electrons and holes generated by photoexcitation inside the second semiconductor layer reduced the probability of the recombination between the generated electrons
25 and holes. Probably as a result, the photoelectrochemical cell of Example 1 showed a higher apparent quantum efficiency than the cells of Comparative Examples 1 and 3.
[0129] The photoelectrochemical cell of Comparative Example 2 was irradiated with light. Although it was observed that gas was generated on the surface of the
30 counter electrode, the amount of gas generated was too small to be detected. [0130] As indicated in Table 2, in the semiconductor electrode in the photoelectrochemical cell of Comparative Example 2, the Fermi level of the first semiconductor layer (p-type semiconductor layer) on the conductor side was lower than that of the second semiconductor layer (n-type semiconductor layer) on the
35 surface side. Therefore, Schottky barriers were formed at the junction plane between the first semiconductor layer and the second semiconductor layer. Probably, these barriers prevented charge separation between the electrons and

holes generated by photo excitation inside the second semiconductor layer, resulting in a higher probability of the recombination between the generated electrons and holes, and thus, in a failure to generate hydrogen efficiently
[0131] The same experiment was performed with the photoelectrochemical cells of 5 Examples 2 to 4. As a result, as indicated in Table 3, the cells of Examples 2 to 4 showed apparent quantum efficiencies of 29%, 32%, and 35%, respectively [0132] It could be confirmed from these results that since the ohmic loss derived from the conducting wire was eliminated in the photoelectrochemical cell of Example 3, the apparent quantum efficiency was further improved, compared to the
10 photoelectrochemical cells of Examples 1 and 2.
[0133] The apparent quantum efficiency of the photoelectrochemical cell of Example 5 was 15%, although the apparent quantum efficiency of CdS alone was about 5% in Example 5. It was confirmed from these results that with the use of a semiconductor electrode that includes a plurality of semiconductor layers whose
15 band structure relationships meet the requirements of the present invention, hydrogen can be generated more efficiently than the separate use of these semiconductor materials.
[0134] Photoelectrochemical cells were produced with various combinations of the p-type semiconductor materials indicated in Table 1 so that the structural
20 requirements of the semiconductor electrode of the present invention were met, and the apparent quantum efficiencies thereof were measured. As a result, the highest apparent quantum efficiency was 40%.
[0135] It should be noted that an Na2S03 aqueous solution containing Na2S was used as an electrolyte in each of the photoelectrochemical cells of Examples 1 to 5
25 and Comparative Examples 1 to 3. In view of this, presumably, when the
semiconductor electrode was irradiated with light, the reaction that proceeded in the semiconductor electrode was not an oxygen evolution reaction according to the above-indicated reaction formula (l) but a reaction according to the be low indicated reaction formula (3). Presumably the reaction expressed by the aforementioned
30 reaction formula (2) proceeded in the counter electrode. [0136] Formula (3):
2h++S*" -► S (3)
[0137] BaZro.8lno.2O3a was used for the first semiconductor layer in the 35 photoelectrochemical cell of Example 2, and BaZro.8lno.2O3a was used for the first semiconductor layer in the photoelectrochemical cell of Example 4, but instead,

BaZro.4Ceo.Jno.2O3a may be used. A BaZro.4Ceo.4Ino.2O3a film can be formed, for example, by sputtering. The band edge level of the conduction band and the band edge level of the valence band are indicated in Table 1. A semiconductor electrode using these materials also meets the requirements of the semiconductor electrode of 5 the present invention. This means that the apparent quantum efficiency is
expected to be improved, as is the case with Example 1. It should be noted that the band edge levels of the conduction bands and the band edge levels of the valence bands, and the band gaps of the p-type semiconductors indicated in Table 1 are the actual values measured by UPS, AC-3, or ultraviolet-visible spectroscopy (UV-Vis).
10 In USP, photoelectron spectroscopic measurement was performed in vacuum using a sample obtained by electrodepositing a powder sample on a Pt substrate. In AC-3, photoelectron spectroscopic measurement with an atmospheric photoelectron spectrometer (AC-3, Riken Keiki Co., Ltd.) was performed in the atmosphere using a disk-shaped bulk sample (with a diameter of 12 cm and a thickness of 0.5 cm). In
15 UV-Vis, absorption spectroscopic measurement was performed by a transmission method or a diffuse reflection method also using a disk-shaped bulk sample or a powder sample.
INDUSTRIAL APPLICABILITY
20 [0138] The photoelectrochemical cell and the energy system of the present
invention can improve the quantum efficiency of the hydrogen evolution reaction by irradiation with light, and thus are useful as a domestic power generation system and the like.

35
CLAIMS
1. A photoelectrochemical cell comprising:
a semiconductor electrode including a conductor and a semiconductor layer 5 disposed on the conductor!
a counter electrode connected electrically to the conductor; an electrolyte in contact with surfaces of the semiconductor layer and the counter electrode; and
a container accommodating the semiconductor electrode, the counter 10 electrode and the electrolyte, wherein
a band edge level Ecs of a conduction band, a band edge level Evs of a valence band, and a Fermi level EFS in a surface near-field region of the semiconductor layer, and a band edge level ECJ of a conduction band, a band edge level EVJ of a valence band, and a Fermi level EFJ in a junction plane near-field 15 region of the semiconductor layer with the conductor satisfy relative to a vacuum level, Ecs " EFS > ECJ - EFJ, EFS - Evs < EFJ ' EVJ, ECJ > "4.44 eV, and Evs < "5.67 eV, and
the Fermi level EFS in the surface near-field region of the semiconductor layer and the Fermi level EFJ in the junction plane near-field region of the 20 semiconductor layer with the conductor satisfy relative to the vacuum level, -5.67 eV < EFS < "4.44 eV and -5.67 eV < EFJ < '4.44 eV, respectively.
2. The photoelectrochemical cell according to claim 1, wherein
the semiconductor layer includes first to Nth (N is an integer of 2 or more) 25 semiconductor layers that are disposed in this order on the conductor,
when two adjacent layers selected from the first to Nth semiconductor layers are referred to as a (K-l)th (K is an integer of 2 to N) semiconductor layer and a Kth semiconductor layer from the side of the conductor, a band edge level ECK of a conduction band, a band edge level EVK of a valence band, and a Fermi level EFK 30 of the Kth semiconductor layer, and a band edge level ECCK-I) of a conduction band, a band edge level EVCK-I) of a valence band, and a Fermi level EF(K-I) of the (K-l)th semiconductor layer satisfy relative to the vacuum level, ECK " EFK > EC(K-I) " EF(K-I), EFK • EVK < EF(K-I) • EV(K-I), EC(K-I) > "4.44 eV, and EVK < "5.67 eV, and
the Fermi level EFK of the Kth semiconductor layer and the Fermi level 35 EF(K-I) of the (K-l)th semiconductor layer satisfy relative to the vacuum level, -5.67 eV < EFK < "4.44 eV and -5.67 eV < EF(K-I) < "4.44 eV, respectively

3. The photoelectrochemical cell according to claim 1, wherein the
semiconductor layer includes at least two elements, and at least one of the elements
in the semiconductor layer has a concentration increasing or decreasing along a
thickness direction of the semiconductor layer.
5
4. The photoelectrochemical cell according to claim 1, wherein the
semiconductor layer is composed of at least one selected from the group consisting of
oxide, nitride, and oxynitride.
10 5. The photoelectrochemical cell according to claim 1, wherein the
semiconductor layer contains an oxide containing barium, zirconium and indium as constituent elements, or an oxide containing barium, zirconium, cerium and indium as constituent elements.
15 6. The photoelectrochemical cell according to claim 1, wherein the
semiconductor layer contains at least one selected from perovskite-type oxide semiconductors represented by the following general formulae A and B:
BaZri-xMx03-a (General Formula A) where M denotes at least one element selected from trivalent elements, x denotes a
20 numerical value of more than 0 and less than 1, and a denotes an amount of oxygen deficiency that is a numerical value of more than 0 and less than 1.5; and
BaZrxCeyMi-x-y03-a (General Formula B) where M denotes at least one element selected from trivalent elements, x denotes a numerical value of more than 0 and less than 1, y denotes a numerical value of more
25 than 0 and less than 1, x + y < 1 is satisfied, and a denotes an amount of oxygen deficiency that is a numerical value of more than 0 and less than 1.5.
7. The photoelectrochemical cell according to claim 1, wherein the counter
electrode is disposed on the conductor.
30
8. An energy system comprising:
the photoelectrochemical cell according to claim l;
a hydrogen storage, connected to the photoelectrochemical cell by a first pipe,
for storing hydrogen generated inside the photoelectrochemical cell; and
35 a fuel cell, connected to the hydrogen storage by a second pipe, for
converting the hydrogen stored in the hydrogen storage into electricity.