THERMALLY-ACTIVATED, HIGH-TEMPERATURE CEMENT SUSPENDING
AGENT
BACKGROUND
[0001] The present invention relates to hydraulic cement suspending agents for use in
high temperature wellbore applications, and methods relating thereto.
[0002] A natural resource such as oil or gas residing in a subterranean formation can be
recovered by drilling a well into the formation. To do so, a wellbore is typically drilled down to
the subterranean formation while circulating a drilling fluid through the wellbore. After the
drilling is terminated, a string of pipe, e.g., casing, is run in the wellbore. Primary cementing is
then usually performed whereby a cementing fluid, usually including water, cement, and
particulate additives, is pumped down through the string of pipe and into the annulus between the
string of pipe and the walls of the wellbore to allow the cementing fluid to set into an
impermeable cement column and thereby seal the annulus. Subsequent secondary cementing
operations, i.e., any cementing operation after the primary cementing operation, may also be
performed. One example of a secondary cementing operation is squeeze cementing whereby a
cementing fluid is forced under pressure to areas of lost integrity in the annulus to seal off those
areas.
[0003] As the bottom hole circulating temperature of a well increases, the viscosity of a
cementing fluid decreases. This decrease in viscosity, which is known as thermal thinning, can
result in settling of the solids in the slurry. Undesirable consequences of the solids settling
include free water and a density gradient in the set cement. To inhibit settling, cement
suspending agents, e.g., crosslinked polymers, can be added to the cementing fluid. As the
cementing fluid temperature increases, the cement suspending agent is thought to increase the
viscosity of the cementing fluid, for example, by breaking crosslinks to release a polymer into
the fluid. One important feature of a cement suspending agent is that it does not adversely affect
low-temperature rheology.
[0004] Existing cement suspending agents, e.g., guar or guar derivatives crosslinked with
borate, delay crosslink breakage sufficiently to allow mixing and pumping of a cement fluid
without imparting an excessively-high viscosity. However, those existing suspending agents are
known to degrade above 300 °F (149 °C). This temperature limitation makes these cement
suspending agents impractical for use in higher temperature applications.
SUMMARY OF THE INVENTION
[0005] The present invention relates to hydraulic cement suspending agents for use in
high temperature wellbore applications, and methods relating thereto.
[0006] According to one aspect of the invention there is provided a method comprising:
providing a cementing fluid comprising an aqueous fluid, a hydraulic cement, and a cement
suspending agent, wherein the cement suspending agent comprises a crosslinked particulate
formed by a reaction comprising a first monofunctional monomer, a primary crosslinker, and a
secondary crosslinker; placing the cementing fluid in a wellbore penetrating a subterranean
formation; and allowing the cementing fluid to set therein.
[0007] In an embodiment, the subterranean formation is about 225 °F (107 °C) to about
600 °F (316 °C).
[0008] In an embodiment, the crosslinked particulate begins to degrade and dissolve
above about 225 °F (107 °C).
[0009] In an embodiment, the method further comprises: placing a spacer fluid
comprising the cement suspending agent in the wellbore before and/or after placing the
cementing fluid in the wellbore.
[0010] In an embodiment, the cement suspending agent is at a different concentration in
the spacer fluid than in the cementing fluid.
[0011] In an embodiment, the first monofunctional monomer comprises a monomer
selected from the group consisting of N,N-dimethylacrylamide, sodium 2-acrylamido-2-
methylpropanesulfonate, 2-acrylamido-2-methylpropanesulfonic acid, N-
(hydroxymethyl)acrylamide, N-(hydroxyethyl)acrylamide, acrylamide, methacrylamide, Nvinylformamide,
l-vinyl-2-pyrrolidinone, N-vinylcaprolactam, N-acryloyl morpholine, Nmethyl-
N-vinylacetamide, N-isopropylacrylamide, N,N-diethylacrylamide, sodium 4-
styrenesulfonate, and vinylsulfonic acid .
[0012] In an embodiment, the primary crosslinker is present in the reaction at about 0.1%
to about 20% by weight of total monomer.
[0013] In an embodiment, the primary crosslinker comprises a crosslinking agent
selected from the group consisting of ethylene diacrylate, polyethylene glycol diacrylate with 2
to 30 ethylene glycol units, polyethylene glycol dimethacrylate with 2 to 30 ethylene glycol
units, glycerol dimethacrylate, triglycerol diacrylate, ethoxylated glycerol diacrylate, ethoxylated
glycerol triacrylate, pentaerythritol tetraacrylate, ethoxylated pentaerythritol tetraacrylate,
pentaerythritol triacrylate, trimethylolpropane triacrylate, and ethoxylated trimethylolpropane
triacrylate, and any combination thereof.
[0014] In an embodiment, the secondary crosslinker is present in the reaction at about
0.005% to about 0.5% by weight of total monomer.
[0015] In an embodiment, the secondary crosslinker comprises a crosslinking agent
selected from the group consisting of N,N '-methylenebisacrylamide, N,N'-(l,2-dihydroxy-l,2-
ethanediyl)bisacrylamide, N,N'-(l,2-ethanediyl)bisacrylamide, and N,N'-[[2,2-
bis(hydroxymethyl)-l,3-propanediyI]bis(oxymethylene)]bisacrylamide, bis(2-
methacryloyl)oxyethyl disulfide, and N,N'-bis(acryloyl)cystamine, and any combination thereof.
[0016] In an embodiment, the reaction further comprises a second monofunctional
monomer, wherein the second monofunctional monomer and the first monofunctional monomer
are different.
[0017] In an embodiment, the weight ratio of the first monofunctional monomer to the
second monofunctional monomer in the reaction ranges from about 0.1:99.9 to about 99.9:0. 1.
[0018] According to a further aspect of the present invention there is provided a
cementing fluid comprising: an aqueous fluid, a cementitious particulate, and a cement
suspending agent comprising a crosslinked particulate, wherein the crosslinked particulate is
made from a reaction comprising: a first monofunctional monomer, a primary crosslinker, and a
secondary crosslinker.
[0019] In an embodiment, the cementitious particulate is a hydraulic cement.
[0020] In an embodiment, the cementing fluid further comprises a weighting agent, a fine
aggregate particulate, or any combination thereof.
[0021] In an embodiment, the reaction further comprises a second monofunctional
monomer, wherein the first monofunctional monomer and the second monofunctional monomer
are different.
[0022] According to a further aspect of the present invention there is provided a method
comprising: providing a treatment fluid comprising an aqueous fluid, a plurality of particulates,
and a suspending agent, wherein the suspending agent comprises a crosslinked particulate
formed by a reaction comprising a first monofunctional monomer and a primary crosslinker;
placing the treatment fluid in a wellbore penetrating a subterranean formation with a bottom hole
static temperature greater than about 225 °F (107 °C); and allowing a plurality of crosslinks
within the crosslinked particulate to degrade thereby allowing at least some of the polymer to
dissolve and suspend the particulates.
[0023] In an embodiment, the reaction further comprises a second monofunctional
monomer.
[0024] In an embodiment, the reaction further comprises a secondary crosslinker.
[0025] In an embodiment, the treatment fluid is selected from the group consisting of a
cement slurry, a flush fluid, a spacer fluid, and a fracturing fluid.
[0026] According to a further aspect of the present invention there is provided a
treatment fluid comprising an aqueous fluid, a plurality of particulates, and a suspending agent
comprising a crosslinked particulate, wherein the crosslinked particulate is formed by a reaction
comprising a first monofunctional monomer and a primary crosslinker.
[0027] In an embodiment, the suspending agent further comprises a second
monofunctional monomer.
[0028] In an embodiment, the suspending agent further comprises a secondary
crosslinker.
[0029] In an embodiment, the treatment fluid is selected from the group consisting of a
cement slurry, a flush fluid, a spacer fluid, and a fracturing fluid.
[0030] According to a further aspect of the present invention there is provided a method
of producing a cement suspending agent, the method comprising: providing an oil solution
comprising an oil-based solvent and a surfactant; providing a monomer mixture comprising an
aqueous fluid, a first monofunctional monomer, and a primary crosslinker; forming an inverse
suspension with the monomer mixture and the oil solution; reacting the monomer mixture in the
inverse suspension with a free-radical initiator to react to form a crosslinked particulate; and
isolating the crosslinked particulate.
[0031] The features and advantages of the present invention will be readily apparent to
those skilled in the art upon a reading of the description of the preferred embodiments that
follows.
BRIEF DESCRIPTION OF THE DRAWINGS
[0032] The following figures are included to illustrate certain aspects of the present
invention, and should not be viewed as exclusive embodiments. The subject matter disclosed is
capable of considerable modification, alteration, and equivalents in form and function, as will
occur to those skilled in the art and having the benefit of this disclosure.
[0033] Figure 1 is a plot of the experimental conditions and results described in the
Examples section.
[0034] Figure 2 is a plot of the experimental conditions and results described in the
Examples section.
[0035] Figure 3 is a plot of the experimental conditions and results described in the
Examples section.
[0036] Figure 4 is a plot of the experimental conditions and results described in the
Examples section.
[0037] Figure 5 is a plot of the experimental conditions and results described in the
Examples section.
[0038] Figure 6 is a plot of the experimental conditions and results described in the
Examples section.
DETAILED DESCRIPTION
[0039] The present invention relates to hydraulic cement suspending agents for use in
high temperature wellbore applications, and methods relating thereto.
[0040] Of the many advantages of the present invention, the present invention provides
compositions that protect against thermal thinning of cements at elevated temperature, and
methods thereof. The present invention provides cement suspending agents that are useful in
subterranean formations that have bottom hole static temperatures (BHST) of 225 °F (107 °C) or
greater, including those formations that have a bottom hole static temperature in excess of about
400 °F (204 °C). Thus, the applicability of the cement suspending agents of the present
invention encompasses a significantly higher temperature range than other, known cement
suspending agents. The cement suspending agents of the present invention are designed to not
adversely affect the low-temperature viscosity of a treatment fluid. Additionally, the cement
suspending agents of the present invention may be applicable to a wide variety of subterranean
formations and/or wellbore treatments where a particulate suspending aid is needed in high
temperature applications, including in cementing fluids, spacer fluids, flush fluids, and fracturing
fluids. When used in cementing fluids, the cement suspending agents may not adversely affect
the setting time of a cementitious composition or the final strength of a cementitious
composition.
[0041] Some embodiments of the present invention provide cementing fluids suitable for
use in a subterranean wellbore comprising an aqueous liquid, a hydraulic cement, and a cement
suspending agent. The cement suspending agent generally comprises a crosslinked particulate
formed by a reaction comprising a first monofunctional monomer, a primary crosslinker, and a
secondary crosslinker. In some embodiments the cementing fluid may then be placed into a
wellbore penetrating a subterranean formation and allowed to set therein.
[0042] Some embodiments of the present invention provide methods comprising
providing an oil solution, which itself comprises an oil-based solvent and a surfactant, and
providing a monomer mixture, which itself comprises an aqueous liquid, a first monofunctional
monomer, and a primary crosslinker. An inverse suspension may then be formed from the
monomer mixture and the oil solution. A crosslinked particulate may be formed by reacting the
monomer mixture in the inverse suspension with a free-radical initiator. The crosslinked
particulates may be further isolated and used in subterranean treatments.
[0043] Other embodiments of the present invention provide methods that provide a
treatment fluid comprising an aqueous liquid, a plurality of particulates, and a suspending agent.
In such methods, the suspending agent generally comprises a crosslinked particulate formed by a
reaction comprising a first monofunctional monomer and a primary crosslinker. In some
embodiments the treatment fluid comprising the crosslinked particulate may be placed in a
wellbore penetrating a subterranean formation with a bottom hole static temperature greater than
about 225 °F (107 °C). The plurality of crosslinks in the crosslinked particulate may be allowed
to degrade, thereby allowing at least some of the polymer to dissolve and suspend the
particulates.
[0044] In some embodiments, a cement suspending agent of the present invention may
comprise a crosslinked particulate, wherein the crosslinked particulate has been formed by a
reaction comprising a first monofunctional monomer, a primary crosslinker, and optionally a
secondary crosslinker. It should be understood that the term "particulate" or "particle," as used
in this disclosure, includes all known shapes of materials, including, but not limited to, spherical
materials, substantially spherical materials, low to high aspect ratio materials, fibrous materials,
polygonal materials (such as cubic materials), and mixtures thereof. In some embodiments, a
crosslinked particulate may be formed from a reaction that comprises a first monofunctional
monomer, a second monofunctional monomer, and a primary crosslinker. In some embodiments,
a crosslinked particulate may comprise a first monofunctional monomer, a second
monofunctional monomer, a primary crosslinker, and a secondary crosslinker. In some
embodiments, a first monofunctional monomer and a second monofunctional monomer may be
different. In some embodiments, a primary crosslinker and a secondary crosslinker may be
different.
[0045] It should be noted that when "about" is provided at the beginning of a numerical
list, "about" modifies each number of the numerical list. It should be noted that in some
numerical listings of ranges, some lower limits listed may be greater than some upper limits
listed. One skilled in the art will recognize that the selected subset will require the selection of
an upper limit in excess of the selected lower limit.
[0046] Suitable monofunctional monomers for use in the present invention may be a
monomer containing a vinyl or vinylidene group that is stable in a polymerized and or
crosslinked form at a high temperature, i.e., above 225 °F (107 °C). As used herein, "stable"
refers to substantially nondegradable on the timescale of the performance requirement. Suitable
monofunctional monomers include N-substituted and N,N-disubstituted acrylamides. Other
suitable monofunctional monomers include N-vinylamides and N-alkyl-N-vinylamides.
Examples of monofunctional monomers include, but are not limited to, N,N-dimethylacrylamide,
sodium 2-acrylamido-2-methylpropanesulfonate, 2-acrylamido-2-methylpropanesuIfonic acid,
N-(hydroxymethyl)acrylamide, N-(hydroxyethyl)acrylamide, acrylamide, methacrylamide, Nvinylformamide,
l-vinyl-2-pyrrolidinone, N-vinylcaprolactam, N-acryloyl morpholine, Nmethyl-
N-vinylacetamide, N-isopropylacrylamide, N,N-diethylacrylamide, sodium 4-
styrenesulfonate, vinylsulfonic acid, and any derivative thereof. It should be noted that a mixture
of monofunctional monomers may also be applicable for use in the present invention.
[0047] In some embodiments, a crosslinked particulate may be formed from a reaction
that comprises a first and a second monofunctional monomer. A ratio of first monofunctional
monomer to second monofunctional monomer may be present in the reaction in an amount
ranging from a lower limit of about 0.1:99.9, 1:99, 5:95, 10:90, 25:75 or 50:50 to an upper limit
of about 99.9:0.1, 99:1, 90:10, 75:25, or 50:50, and wherein the amount may range from any
lower limit to any upper limit and encompass any subset between the upper and lower limits.
[0048] Suitable primary crosslinkers for use in the present invention may be a crosslinker
with at least two vinyl or vinylidene groups that form at least one crosslink that is hydrolytically
stable at ambient temperature and hydrolytically unstable at high temperature, i.e., above 225 °F
(107 °C), on the timescale of the well treatment. As used herein, "hydrolytically stable," and any
derivative thereof, indicates stable against hydrolysis. Examples of primary crosslinkers include,
but are not limited to, ethylene diacrylate, polyethylene glycol diacrylate with 2 to 30 ethylene
glycol units, polyethylene glycol dimethacrylate with 2 to 30 ethylene glycol units, glycerol
dimethacrylate, triglycerol diacrylate, ethoxylated glycerol diacrylate, ethoxylated glycerol
triacrylate, pentaerythritol tetraacrylate, ethoxylated pentaerythritol tetraacrylate, pentaerythritol
triacrylate, trimethylolpropane triacrylate, ethoxylated trimethylolpropane triacrylate, and any
derivative thereof. A suitable primary crosslinker may hydrolyze at temperatures ranging from a
lower limit of about 225 °F (107 °C), 275 °F (135 °C), 300 °F (149 °C), 325 °F (163 °C), 350 °F
(177 °C), 400 °F (204 °C), or 450 °F (232 °C) to an upper limit of about 700 °F (371 °C), 650 °F
(343 °C), 600 °F (316 °C), 550 °F (288 °C), 500 °F (260 °C), 450 °F (232 °C), or 400 °F (204
°C), and wherein the temperature may range from any lower limit to any upper limit and
encompass any subset between the upper and lower limits. A primary crosslinker may be present
in the reaction to form a crosslinked particulate in an amount ranging from a lower limit of about
0.1%, 0.5%, 1%, 5%, or 10% by weight of total monomer to an upper limit of about 20%, 15%,
10%, 5%, or 1% by weight of total monomer, and wherein the amount may range from any lower
limit to any upper limit and encompass any subset between the upper and lower limits.
[0049] Suitable secondary crosslinkers for use in the present invention may be any
known bisacrylamide crosslinker that forms at least one crosslink that is hydrolytically unstable
at high temperature, i.e., above 225 °F (107 °C), on the timescale of the well treatment.
Examples of secondary crosslinkers include, but are not limited to, N,N' -
methylenebisacrylamide, N,N'-( ,2-dihydroxy- 1,2-ethanediyl)bisacrylamide, N,N'-( 1,2-
ethanediyl)bisacrylamide, N,N'-[[2,2-bis(hydroxymethyl)-l,3-
propanediyl]bis(oxymethylene)]bisacrylamide, bis(2-methacryloyl)oxyethyl disulfide, N,N'-
bis(acryloyl)cystamine, and any derivative thereof. A suitable secondary crosslinker may
hydrolyze at temperatures ranging from a lower limit of about 225 °F (107 °C), 275 °F (135 °C),
300 °F (149 °C), 325 °F (163 °C), 350 °F (177 °C), 400 °F (204 °C), or 450 °F (232 °C) to an
upper limit of about 700 °F (371 °C), 650 °F (343 °C), 600 F (3 16 °C), 550 °F (288 °C), 500 °F
(260 °C), 450 °F (232 °C), or 400 °F (204 °C), and wherein the temperature may range from any
lower limit to any upper limit and encompass any subset between the upper and lower limits. A
secondary crosslinker may be present in a crosslinked particulate in an amount ranging from a
lower limit of about 0.005%, 0.01%, 0.05%, or 0.1% by weight of total monomer to an upper
limit of about 0.5%, 0.25%, 0.1%, or 0.05% by weight of total monomer, and wherein the
amount may range from any lower limit to any upper limit and encompass any subset between
the upper and lower limits.
[0050] In preferred embodiments, the secondary crosslinker may be hydrolytically stable
to a higher temperature than the primary crosslinker.
[0051] In some embodiments, when the temperature exceeds the temperature at which
the primary and/or secondary crosslinker hydrolyzes, the crosslinker may hydrolyze thereby
allowing the polymer comprising the first and/or second monofunctional monomer to dissolve in
a treatment fluid.
[0052] In some embodiments, a cement suspending agent of the present invention may be
used in a treatment fluid comprising a particulate. In some embodiments, when the primary
and/or secondary crosslinkers hydrolyze, the polymer comprising the first and/or second
monofunctional monomer may dissolve in the treatment fluid thereby inhibiting settling of a
particulate suspended in a treatment fluid. In some embodiments, the cement suspending agents
may be used in a treatment fluid comprising a particulate, wherein the particulate needs to be
maintained in suspension at temperatures greater than about 225 °F (107 °C), 275 °F (135 °C),
300 °F (149 °C), 325 °F (163 °C), 350 °F (177 °C), 400 °F (204 °C), or 450 °F (232 °C).
[0053] A suitable particulate for use in the present invention may be any particulate
suitable for use in a subterranean formation including, but not limited to, cementitious
particulates, weighting agents, proppants, fine aggregate particulates, and any combination
thereof. Suitable particulates for use in the present invention may have a diameter ranging from
a lower limit of about 0.5 m , 1 m h, 10 m , 50 m h , 0.1 mm, or 1 mm to an upper limit of about
10 mm, 1 mm, 0.5 mm, 0.1 mm, or 50 m h, and wherein the diameter may range from any lower
limit to any upper limit and encompass any subset between the upper and lower limits. A
particulate may be present in a treatment fluid in an amount ranging from a lower limit of about
0%, 20%, 30%, 40%, or 50% by weight of treatment fluid to an upper limit of about 90%, 80%,
70%, 60%, 50%, or 40% by weight of treatment fluid, and wherein the amount may range from
any lower limit to any upper limit and encompass any subset between the upper and lower limits.
[0054] The terms "cement" and "hydraulic cement" may be used interchangeably in this
application. As used herein, the terms refer to compounds of a cementitious nature that set
and/or harden in the presence of water. Suitable hydraulic cements for use in the present
invention may be any known hydraulic cement including, but are not limited to, a Portland
cement including API classes A, B, C, G, and H; a slag cement; a pozzolana cement; a gypsum
cement; an aluminous cement; a silica cement; a high alkalinity cement; and any combination
thereof. In some embodiments, a cementing fluid may comprise an aqueous liquid, a hydraulic
cement, and a cement suspending agent.
[0055] Suitable weighting agents for use in the present invention may be any known
weighting agent that is a particulate including, but not limited to, barite; hematite; manganese
tetraoxide; galena; silica; siderite; celestite; ilmenite; dolomite; calcium carbonate; and any
combination thereof.
[0056] Suitable proppants for use in the present invention may be any known proppant
including, but not limited to, sand, bauxite, ceramic materials, glass materials, polymer materials,
polytetrafluoroethylene materials, nut shell pieces, cured resinous particulates comprising nut
shell pieces, seed shell pieces, cured resinous particulates comprising seed shell pieces, fruit pit
pieces, cured resinous particulates comprising fruit pit pieces, wood, composite particulates, and
any combination thereof. Suitable composite particulates may comprise a binder and a filler
material wherein suitable filler materials include silica, alumina, fumed carbon, carbon black,
graphite, mica, titanium dioxide, meta-silicate, calcium silicate, kaolin, talc, zirconia, boron, fly
ash, hollow glass microspheres, solid glass, and any combination thereof.
[0057] Suitable fine aggregate particulates for use in the present invention may include,
but are not limited to, fly ash, silica flour, fine sand, diatomaceous earth, lightweight aggregates,
hollow spheres, and any combination thereof.
[0058] Suitable aqueous fluids for use in the present invention may comprise fresh water,
saltwater (e.g., water containing one or more salts dissolved therein), brine (e.g., saturated salt
water), seawater, and any combination thereof. Generally, the water may be from any source,
provided that it does not contain components that might adversely affect the stability and/or
performance of the compositions or methods of the present invention.
[0059] While a number of preferred embodiments described herein relate to cementing
fluids, it is understood that other treatment fluids may also be prepared according to the present
invention including, but not limited to, spacer fluids, drilling fluids, fracturing fluids, and lost
circulation fluids. As referred to herein, the term "spacer fluid" should be understood to mean a
fluid placed within a wellbore to separate fluids, e.g., to separate a drilling fluid within the
wellbore from a cementing fluid that will subsequently be placed within the wellbore.
[0060] In some embodiments, a cement suspending agent may be included in a first fluid
that is placed in a wellbore and/or subterranean formation before and/or after a second fluid,
wherein the second fluid comprises a plurality of particulates and the cement suspending agent.
n some embodiments, the concentration of cement suspending agent may be different in a first
fluid than in a second fluid. In some embodiments, the first fluid may be a spacer fluid and the
second fluid may be a treatment fluid.
[0061] The teachings of the present invention and the methods and compositions of the
present invention may be used in many different types of subterranean treatment operations.
Such operations include, but are not limited to, casing operations, plugging operations, drilling
operations, lost circulation operations, completion operations, and water-blocking operations. In
some embodiments, the suspending aid of the present invention may be used as a secondary
gelling agent in a high-temperature fracturing treatment. The methods and compositions of the
present invention may be used in large-scale operations or pills. As used herein, a "pill" is a type
of relatively small volume of specially prepared treatment fluid placed or circulated in the
wellbore.
[0062] In some embodiments, a cement suspending agent may be used in a wellbore
and/or subterranean formation with a bottom hole static temperature (BHST) ranging from a
lower limit of about 225 °F (107 °C), 275 °F (135 °C), 300 °F (149 °C), 325 °F (163 °C), 350 °F
(177 °C), 400 °F (204 °C), or 450 °F (232 °C) to an upper limit of about 700 °F (371 °C), 650 °F
(343 °C), 600 °F (316 °C), 550 °F (288 °C), 500 °F (260 °C), 450 °F (232 °C), or 400 °F (204
°C), and wherein the temperature may range from any lower limit to any upper limit and
encompass any subset between the upper and lower limits.
[0063] In some embodiments, a cement suspending agent may be provided in wet or dry
form. In some embodiments, a suspending agent may be added to a treatment fluid on-site or
off-site of the wellbore location.
[0064] In some embodiments, a cement suspending agent may be produced by providing
an oil solution comprising an oil-based solvent and a surfactant; providing a monomer mixture
comprising an aqueous liquid and the monomers and the crosslinkers needed for a desired
crosslinked particulate; forming an inverse suspension with the monomer mixture and the oil
solution; and reacting a free-radical initiator with the monomer mixture in the inverse suspension
to form a crosslinked particulate. Without being limited by theory or mechanism, it is believed
that as a crosslinked polymer forms in the inverse suspension it generates crosslinked
particulates. In some embodiments, a crosslinked particulate may be isolated by a method
including, but not limited to, drying either by water-miscible solvent extraction or azeotropic
distillation; followed by filtration or centrifugation to remove the oil-based solvent.
Alternatively, the crosslinked particulate may be isolated from the oil-based solvent before
drying with air. One skilled in the art, with the benefit of this disclosure, will recognize suitable
procedural variations, including order of addition, to achieve the desired crosslinked particulate.
For example, when reacting the free radical initiator with the monomer mixture, the free radical
initiator may be added to the monomer mixture shortly before forming the inverse emulsion, to
the oil solution before forming the inverse suspension, to the inverse suspension, or any
combination thereof.
[0065] Suitable oil-based solvents may include, but are not limited to, paraffinic
hydrocarbons, aromatic hydrocarbons, olefinic hydrocarbons, petroleum distillates, synthetic
hydrocarbons, and any combination thereof. Examples of a suitable oil-based solvent include
ESCAID® (a low viscosity organic solvent, available from ExxonMobil, Houston, TX).
Suitable surfactants may include, but are not limited to, a HYPERMER® (a nonionic, polymeric
surfactant, available from Croda, Edison, NJ), block copolymers of ethylene oxide and propylene
oxide, block copolymers of butylene oxide and ethylene oxide, sorbitan esters, copolymers of
rnethacrylic acid and C12-C18 alkyl methacrylates, alkylarylsulfonate salts, and any combination
thereof. Suitable free radical initiators may be any water-soluble free radical initiator including,
but not limited to, persulfate salts, organic peroxides, organic hydroperoxides, azo compounds
(e.g. 2,2'-azobis(2-amidinopropane) dihydrochloride), and any combination thereof. One skilled
in the art with the benefit of this disclosure will recognize the plurality of applicable oil-based
solvents, surfactants, and free radical initiators and the appropriate concentrations of each needed
for producing a crosslinked particulate.
[0066] To facilitate a better understanding of the present invention, the following
examples of preferred embodiments are given. In no way should the following examples be read
to limit, or to define, the scope of the invention.
EXAMPLES
[0067] Cement suspending agent synthesis. A 250 L round bottom, 3 necked flask was
fitted with an overhead stirrer and a nitrogen purge. The flask was charged with 100 mL
ESCAID®110 oil-based solvent and 1 mL of HYPERMER ® 1031 polymeric surfactant.
Monomer mixture was prepared by combining 20 g of monofunctional monomer, primary
crosslinking monomer (as indicated), secondary crosslinking monomer (as indicated), water (as
indicated), and 0.2 mL of triethanolamine in a 50 mL beaker. Then 0.2 mL of 10% w/v sodium
persulfate was mixed into the monomer mixture. Immediately after adding the sodium
persulfate, the monomer mixture was added to the three-necked flask and the stimng rate was set
to 200 rpm to form the water-in-oil (inverse phase) suspension. The mixture was stirred until the
reaction was complete, as indicated by a temperature rise followed by cooling to ambient
temperature. The product, a crosslinked particulate, was subsequently isolated by either acetone
extraction or azeotropic distillation, followed by filtration.
[0068] For acetone extraction, the product mixture was poured into approximately 300
mL of acetone to extract the water from the crosslinked particulate. The product was collected
on a Biichner funnel by vacuum filtration. The product was subsequently rinsed with acetone to
remove residual oil and air-dried.
[0069] For azeotropic distillation, approximately 50 mL of heptane was added to the
three-necked flask. The overhead stirrer was replaced with a Dean-Stark trap and reflux
condenser and the flask was fitted with a thermometer and temperature controller. The mixture
was stirred (magnetically) and heated to reflux until the water was distilled from the product.
The resulting dry, crosslinked particulate was separated from the hydrocarbon mixture by
vacuum filtration on a Biichner funnel. The product was rinsed with acetone to remove residual
oil and air-dried.
[0070] Cement suspending agents tested. The following five cement suspending agent
("CSA") compositions were prepared by the above procedures.
Table 1 (CSA-1)
» Monomer mixture:
o 1.984 g EO(l 5) trimethylolpropane triacrylate (Sartomer SR9035)
o .34 g N,N -dimethylacrylamide (Aldrich)
o 10.179 g 50% w/w sodium 2-acrylamido-2-methylpropanesulfonic acid (AMPS)
(Lubrizol AMPS 2405)
• No additional water added.
• Worked up with acetone extraction.
Table 2 (CSA-2)
• Monomer mixture:
o .984 g EO(l 5) trimethylolpropane triacrylate (Sartomer SR9035)
o 15.008 g N,N -dimethylacrylamide (Aldrich)
o 10.005 g 50% w/w sodium AMPS (Lubrizol AMPS 2405)
o 0.30 mL 0.5% w/v N,N '-methylenebisacrylamide (Aldrich)
No additional water added.
Worked up with acetone extraction.
Table 3 CSA-3
Monomer mixture:
o 1.999 g polyethylene glycol diacrylate, Mn = 258 (Aldrich)
o 5.000 g N,N -dimethylacrylamide (Aldrich)
o 10.006 g 50% w/w sodium AMPS (Lubrizol AMPS 2405)
o 0.50 mL 0.5% w/v N N '-methylenebisacrylamide (Aldrich)
No additional water added.
Worked up with acetone extraction.
Table 4 (CSA-4)
Monomer mixture:
o 2.000 g polyethylene glycol diacrylate, Mn = 258 (Aldrich)
o 15.000 g N,N -dimethylacrylamide (Aldrich)
o 9.998 g 50% w/w sodium AMPS (Lubrizol AMPS 2405)
o 0.50 mL 0.5% w/v N,N '-methylenebisacrylamide (Aldrich)
15.099 g additional deionized water added.
Worked up with acetone extraction.
Table 5 (CSA-5)
Monomer mixture:
o 2.004 g polyethylene glycol diacrylate, M = 258 (Aldrich)
o 15.0740 g N N-dimethylacrylamide (Aldrich)
o 0.003 g 50% w/w sodium AMPS (Lubrizol AMPS 2405)
o 0.50 mL 0.5% w/v N,N '-methylenebisacrylamide (Aldrich)
15.006 g additional deionized water added.
Worked up with azeotropic distillation.
[0071] Settling Test. Cement slurries containing the above cement suspending agents
were prepared according to API RP10B, Recommended Practice for Testing Well Cements: 500
g Texas Lehigh Class H cement; 372.3 g weighting agent HI-DENSE® #4 (non-radioactive and
non-magnetic hematite, available from Halliburton Energy Services, Inc.); 1 5 g weighting agent
SSA®-2 (sand, available from Halliburton Energy Services, Inc.); 5 g fluid-loss control agent
HALAD®-413 (synthetic polymer, available from Halliburton Energy Services, Inc.); 5 g
retarder HR®-12 (calcium lignosulfonate and organic acid, available from Halliburton Energy
Services, Inc.); 1.25 g retarder HR®-25 (cement retarder, available from Halliburton Energy
Services, Inc.); 3.75 g cement suspending agent; and 285.6 g tap water.
[0072] The slurry was transferred to a Halliburton high-pressure, high-temperature
consistometer with Chandler modifications for data acquisition. The consistometer was
programmed to heat to a chamber temperature of 350 °F (177 °C) over 90 minutes at a constant
pressure of 2000 psi (1379 N/cm2). Upon reaching 350 °F (177 °C), the temperature and
pressure were held constant for the remainder of the test. After a minimum of 2 hours elapsed
time, the stirrer motor was shut off for 10 minutes, and then restarted. This off/on cycle may be
repeated one or more times, depending on the test. A test is considered successful if the slurry
resumes stirring when restarted. A failed test is indicated by a broken shear pin in the slurry can
drive disk caused by excessive torque from settled cement. Figure 1 provides the experimental
conditions and results of the consistometer screening test for a control cement sample. Figures
2-6 provide the experimental conditions and results of the consistometer screening test for a
cement sample containing cement suspending agents of the present invention.
Sample Setting Test Results
Control (no cement suspending agent) Failed (pin sheared, severe settling)
CSA-1 (Figure 2) Passed (pin did not shear, slight settling)
CSA-2 (Figure 3) Passed (pin did not shear, no settling)
CSA-3 (Figure 4) Passed (pin did not shear, no settling)
CSA-4 (Figure 5) Passed (pin did not shear, no settling)
CSA-5 (Figure 6) Passed (pin did not shear, no settling)
[0073] Therefore, the present invention is well adapted to attain the ends and advantages
mentioned as well as those that are inherent therein. The particular embodiments disclosed
above are illustrative only, as the present invention may be modified and practiced in different
but equivalent manners apparent to those skilled in the art having the benefit of the teachings
herein. Furthermore, no limitations are intended to the details of construction or design herein
shown, other than as described in the claims below. It is therefore evident that the particular
illustrative embodiments disclosed above may be altered, combined, or modified and all such
variations are considered within the scope of the present invention. While compositions and
methods are described in terms of "comprising," "containing," or "including" various
components or steps, the compositions and methods can also "consist essentially of or "consist
of the various components and steps. All numbers and ranges disclosed above may vary by
some amount. Whenever a numerical range with a lower limit and an upper limit is disclosed,
any number and any included range falling within the range is specifically disclosed. In
particular, every range of values (of the form, "from about a to about b," or, equivalently, "from
approximately a to b," or, equivalently, "from approximately a-b") disclosed herein is to be
understood to set forth every number and range encompassed within the broader range of values.
Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and
clearly defined by the patentee. Moreover, the indefinite articles "a" or "an," as used in the
claims, are defined herein to mean one or more than one of the element that it introduces. If
there is any conflict in the usages of a word or term in this specification and one or more patent
or other documents that may be incorporated herein by reference, the definitions that are
consistent with this specification should be adopted.
CLAIMS:
. A method comprising:
providing a cementing fluid comprising an aqueous liquid, a hydraulic cement,
and a cement suspending agent, wherein the cement suspending agent comprises a crosslinked
particulate formed by a reaction comprising a first monofunctional monomer, a primary
crosslinker, and a secondary crosslinker;
placing the cementing fluid in a wellbore penetrating a subterranean formation;
and
allowing the cementing fluid to set therein.
2. A method according to claim 1, wherein the subterranean formation is about 225
°F to about 600 °F .
3. A method according to claim 1 or 2, wherein the crosslinked particulate begins to
degrade and dissolve above about 225 °F.
4. A method according to claim 1, 2 or 3 further comprising:
placing a spacer fluid comprising the cement suspending agent in the wellbore
before and/or after placing the cementing fluid in the wellbore.
5. A method according to claim 4, wherein the cement suspending agent is at a
different concentration in the spacer fluid than in the cementing fluid.
6. A method according to any preceding claim, wherein the first monofunctional
monomer comprises a monomer selected from the group consisting of N,V-dimethylacry amide,
sodium 2-acrylamido-2-methylpropanesulfonate, 2-acrylamido-2-methylpropanesulfonic acid, N-
(hydroxymethyl)acrylamide, N-(hydroxyethyl)acrylamide, acrylamide, methacrylamide, Nvinylformamide,
l-vinyl-2-pyrrolidinone, N-vinylcaprolactam, N-acryloyl morpholine, Nmethyl-
N-vinylacetamide, N-isopropylacrylamide, N,N-diethylacrylamide, sodium 4-
styrenesulfonate, and vinylsulfonic acid .
7. A method according to any preceding claim, wherein the primary crosslinker is
present in the reaction at about 0.1% to about 20% by weight of total monomer.
8. A method according to any preceding claim, wherein the primary crosslinker
comprises a crosslinking agent selected from the group consisting of ethylene diacrylate,
polyethylene glycol diacrylate with 2 to 30 ethylene glycol units, polyethylene glycol
dimethacrylate with 2 to 30 ethylene glycol units, glycerol dimethacrylate, triglycerol diacrylate,
ethoxylated glycerol diacrylate, ethoxylated glycerol triacrylate, pentaerythritol tetraacrylate,
ethoxylated pentaerythritol tetraacrylate, pentaerythritol triacrylate, trimethylolpropane
triacrylate, and ethoxylated trimethylolpropane triacrylate, and any combination thereof.
9. A method according to any preceding claim, wherein the secondary crosslinker is
present in the reaction at about 0.005% to about 0.5% by weight of total monomer.
10. A method according to any preceding claim, wherein the secondary crosslinker
comprises a crosslinking agent selected from the group consisting of N,N'-
methylenebisacrylamide, N,N'~( 1,2-dihydroxy- 1,2-ethanediyl)bisacrylamide, N,N'-(\,2-
ethanediyl)bisacrylamide, and N,N'-[[2,2-bis(hydroxymethyl)-l,3-
propanediyl]bis(oxymethylene)]bisacrylamide, bis(2-methacryloyl)oxyethyl disulfide, and N -
bis(acryloyl)cystamine, and any combination thereof.
11. A method according to any preceding claim, wherein the reaction further
comprises a second monofunctional monomer, wherein the second monofunctional monomer
and the first monofunctional monomer are different.
12. A method according to claim 11, wherein the weight ratio of the first
monofunctional monomer to the second monofunctional monomer in the reaction ranges from
about 0.1:99.9 to about 99.9:0.1.
13. A cementing fluid comprising:
an aqueous liquid,
a cementitious particulate, and
a cement suspending agent comprising a crosslinked particulate, wherein the
crosslinked particulate is made from a reaction comprising:
a first monofunctional monomer,
a primary crosslinker, and
a secondary crosslinker.
14. A cementing fluid according to claim 13, wherein the cementing fluid further
comprises a weighting agent, a fine aggregate particulate, or any combination thereof.
15. A cementing fluid according to claim 13 or 14, wherein the reaction further
comprises a second monofunctional monomer, wherein the first monofunctional monomer and
the second monofunctional monomer are different.
16. A method comprising:
providing a treatment fluid comprising an aqueous liquid, a plurality of
particulates, and a suspending agent, wherein the suspending agent comprises a crosslinked
particulate formed by a reaction comprising a first monofunctional monomer and a primary
crosslinker;
placing the treatment fluid in a wellbore penetrating a subterranean formation
with a bottom hole static temperature greater than about 225 F; and
allowing a plurality of crosslinks within the crosslinked particulate to degrade
thereby allowing at least some of the polymer to dissolve and suspend the particulates.
17. A method according to claim 16, wherein the reaction further comprises a second
monofunctional monomer.
18. A method according to claim 16 or 17, wherein the reaction further comprises a
secondary crosslinker.
1 . A method according to claim 16, 17 or 18, wherein the treatment fluid is selected
from the group consisting of a cement slurry, a flush fluid, a spacer fluid, and a fracturing fluid.
20. A method of producing a cement suspending agent, the method comprising:
providing an oil solution comprising an oil-based solvent and a surfactant;
providing a monomer mixture comprising an aqueous liquid, a first
monofunctional monomer, and a primary crosslinker;
forming an inverse suspension with the monomer mixture and the oil solution;
reacting the monomer mixture in the inverse suspension with a free-radical
initiator to form a crosslinked particulate; and
isolating the crosslinked particulate.