[3] The present invention relates to a thermoplastic
15 resin composition, a method of preparing the same, and a molded article including the same. More particularly, the present invention relates to a thermoplastic resin composition that has excellent mechanical properties such as impact strength, tensile strength, and flexural strength and
20 is capable of replacing a PVC resin by allowing use of existing equipment due to excellent processability and heat
1

resistance thereof; a method of preparing the thermoplastic resin composition; and a molded article including the thermoplastic resin composition.
5 【Background Art】
[4] A polyvinylchloride resin (hereinafter referred to
as "PVC resin") is a general-purpose resin that is inexpensive and has excellent flame retardancy, chemical resistance, and processability. In addition to these
10 advantages, when a polyvinylchloride resin is used, it is
easy to control the hardness of a product. Accordingly,
polyvinylchloride resins are generally applied to exterior
materials for construction, especially window frames.
[5] However, due to the intrinsic nature of PVC resins,
15 reprocessing of PVC resins is difficult, and harmful substances are generated when PVC resins are prepared or discarded. In addition, compared to other resins, PVC resins are vulnerable to thermal deformation due to low heat resistance thereof. Due to these limitations, when
20 manufacturing an outdoor window frame using a PVC resin, the window frame is mainly manufactured in white.
2

[6] Recently, as demand for new building materials and
building materials having a luxurious appearance increases, demand for colored window frames is increasing. Accordingly, to impart a color to a window frame manufactured using a PVC 5 resin, a method of painting the window frame or attaching a film to the window frame is used. However, problems such as scratches or discoloration occur.
[7] Acrylonitrile-styrene-acrylate copolymers
(hereinafter referred to as "ASA resins") have excellent
10 weather resistance, light resistance, chemical resistance, heat resistance, and impact resistance, and thus are widely used in various fields, such as electric/electronic parts, building materials, automobiles, ships, and leisure goods, due to broad applicability thereof.
15 [8] An ASA resin is attracting attention as a resin that
can be used instead of a PVC resin. However, ASA resins have poor processability due to high flowability thereof, and additional costs are incurred due to replacement of an existing extruder for PVC resins. That is, when the type of a
20 resin is changed, the shape of an extruder must also be changed.
3

[9] Therefore, there is growing demand for development of
an ASA resin composition that can be prepared using existing equipment for PVC resins due to excellent processability thereof and is resistant to deformation caused by outdoor 5 radiant heat.
[10] [Related Art Documents] [11] [Patent Documents] [12] KR 10-1444054 B1
10 【Disclosure】
【Technical Problem】
[13] Therefore, the present invention has been made in view of the above problems, and it is one object of the present invention to provide a thermoplastic resin
15 composition that has excellent mechanical properties such as impact strength, tensile strength, and flexural strength and is capable of replacing a PVC resin by allowing use of an existing extruder due to excellent processability and heat resistance thereof; a method of preparing the thermoplastic
20 resin composition; and a molded article including the thermoplastic resin composition.
4

[14] The above and other objects can be accomplished by the present invention described below.
[Technical Solution]
5 [15] In accordance with one aspect of the present invention, provided is a thermoplastic resin composition including 100 parts by weight of a base resin including 0.5 to 45 % by weight of a graft copolymer (A-1) including acrylate rubber having an average particle diameter of 50 to
10 150 nm, an aromatic vinyl compound, and a vinyl cyanide compound, 20 to 80 % by weight of a graft copolymer (A-2) including acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 % by weight of an α-
15 methylstyrene-based copolymer (B) having a weight average
molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10
parts by weight of an ultra-high molecular weight copolymer
(C) having a weight average molecular weight of 1,000,000 to
12,000,000 g/mol.
20 [16]
[17] In accordance with another aspect of the present
5

invention, provided is a method of preparing a thermoplastic resin composition, the method including mixing 100 parts by weight of a base resin including 0.5 to 45 % by weight of a graft copolymer (A-1) including acrylate rubber having an 5 average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide compound, 20 to 8 0 % by weight of a graft copolymer (A-2) including acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 %
10 by weight of an α-methylstyrene-based copolymer (B) having a weight average molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10 parts by weight of an ultra-high molecular weight copolymer (C) having a weight average molecular weight of 1,000,000 to 12,000,000 g/mol, and then preparing pellets
15 using an extrusion kneader having with a size of 10 to 100 pi at 200 to 300 °C using an extrusion kneader.
[18]
[19] In accordance with yet another aspect of the present invention, provided is a molded article including the 20 thermoplastic resin composition.
[20]
6

【Advantageous effects】
[21] The present invention can provide a high-quality thermoplastic resin composition with improved heat resistance and extensional viscosity and low flowability while 5 maintaining mechanical properties such as impact strength, tensile strength, and flexural strength; a method of preparing the thermoplastic resin composition; and a molded article including the thermoplastic resin composition. According to the present invention, the thermoplastic resin
10 composition can be applied to fields, such as exterior materials for construction, that require processability and resistance against deformation caused by outdoor radiant heat. [22] In particular, the thermoplastic resin composition can replace a PVC resin and allows use of an existing
15 extruder, thereby improving economics.
[23]
【Best mode】
[24] Hereinafter, a thermoplastic resin composition, a method of preparing the same, and a molded article including 20 the same according to the present invention will be described in detail.
7

[25] The present inventors confirmed that, when a thermoplastic resin composition was prepared by adding an ultra-high molecular weight copolymer in a predetermined content ratio to a base resin including two types of 5 acrylate-based rubber-aromatic vinyl compound-vinyl cyanide compound graft copolymers each containing acrylate rubber particles having different average particle diameters and an α-methylstyrene-vinyl cyanide copolymer, the prepared thermoplastic resin composition had excellent mechanical
10 properties, was capable of replacing a PVC resin due to excellent heat resistance and processability thereof, and was producible using an existing extruder. Based on these results, the present inventors conducted further studies to complete the present invention.
15 [26]
[27] The thermoplastic resin composition of the present invention will be described as follows.
[28]
[29] The thermoplastic resin composition of the present
20 invention includes 100 parts by weight of a base resin
including 0.5 to 45 % by weight of a graft copolymer (A-1)
8

including acrylate rubber having an average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide compound, 20 to 80 % by weight of a graft copolymer (A-2) including acrylate rubber having an average particle 5 diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 % by weight of an α-methylstyrene-based copolymer (B) having a weight average molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10 parts by weight of an ultra-high molecular weight copolymer
10 (C) having a weight average molecular weight of 1,000,000 to 12,000,000 g/mol. In this case, since the thermoplastic resin composition of the present invention has excellent heat resistance and processability while having excellent mechanical properties such as impact strength, tensile
15 strength, flexural strength, and hardness, the thermoplastic resin composition may replace a PVC resin using an existing extruder.
[30]
[31] Hereinafter, each component constituting the 20 thermoplastic resin composition of the present invention will be described in detail.
9

[32]
[33] A-1) Graft copolymer including acrylate rubber, aromatic vinyl compound, and vinyl cyanide compound
[34] For example, the acrylate rubber of the graft 5 copolymer (A-1) may have an average particle diameter of 50 to 150 nm, preferably 60 to 140 nm, more preferably 70 to 140 nm, still more preferably 80 to 140 nm. Within this range, in addition to excellent impact strength, tensile strength, flexural strength, and hardness, a finally prepared
10 thermoplastic resin composition may have excellent processability.
[35] In this specification, average particle diameter may be measured by dynamic light scattering, and specifically, may be measured as an intensity value using a Nicomp 380
15 particle size analyzer (manufacturer: PSS) in a Gaussian mode. As a specific measurement example, a sample is prepared by diluting 0.1 g of latex (TSC: 35 to 50 wt%) 1,000 to 5,000 times with distilled water, i.e., a sample is diluted appropriately so as not to deviate significantly from an
20 intensity setpoint of 300 kHz and is placed in a glass tube. Then, the average particle diameter of the sample is measured
10

using a flow cell in auto-dilution in a measurement mode of dynamic light scattering/intensity 300 kHz/intensity-weight Gaussian analysis. At this time, setting values are as follows: temperature: 23 °C; measurement wavelength: 632.8 nm; 5 and channel width: 10 μsec.
[36]
[37] For example, based on a total weight of the base resin, the graft copolymer (A-1) may be included in an amount of 0.5 to 45 % by weight, preferably 1 to 35 % by weight, 10 more preferably 10 to 25 % by weight. Within this range, balance between mechanical strength and extensional viscosity may be excellent.
[38] For example, the graft copolymer (A-1) may include 40 to 60 % by weight of acrylate rubber, 25 to 45 % by weight of 15 an aromatic vinyl compound, and 5 to 25 % by weight of a vinyl cyanide compound. Within this range, impact strength, tensile strength, flexural strength, and extensional viscosity may be excellent.
[39] As a preferred example, the graft copolymer (A-1) may
20 include 45 to 55 % by weight of acrylate rubber, 30 to 40 %
by weight of an aromatic vinyl compound, and 10 to 20 % by
11

weight of a vinyl cyanide compound. Within this range, impact strength, tensile strength, flexural strength, and extensional viscosity may be excellent.
[40] In this description, a polymer including a certain 5 compound means a polymer prepared by polymerizing the compound, and a unit in the polymer is derived from the compound.
[41]
[42] For example, the graft copolymer (A-1) may be 10 prepared by emulsion polymerization. In this case, mechanical
strength such as tensile strength, impact strength, and
flexural strength may be excellent.
[43] Emulsion graft polymerization methods commonly
practiced in the art to which the present invention pertains 15 may be used as the emulsion polymerization method of the
present invention without particular limitation.
[44]
[45] In this description, for example, the acrylate may
include one or more selected from the group consisting of
20 alkyl acrylates containing an alkyl group having 2 to 8
carbon atoms, and is preferably an alkyl acrylate containing
12

an alkyl group having 4 to 8 carbon atoms, more preferably butyl acrylate or ethylhexyl acrylate.
[46] In this description, for example, the aromatic vinyl
compound may include one or more selected from the group
5 consisting of styrene, α-methylstyrene, m-methylstyrene, p-
methylstyrene, and p-tert-butylstyrene, and is preferably
styrene.
[47] In this description, for example, the vinyl cyanide compound may include one or more selected from the group 10 consisting of acrylonitrile, methacrylonitrile, ethylacrylonitrile, and isopropylacrylonitrile, and is preferably acrylonitrile.
[48]
[4 9] A-2) Graft copolymer including acrylate rubber, 15 aromatic vinyl compound, and vinyl cyanide compound
[50] For example, the acrylate rubber of the graft copolymer (A-2) may have an average particle diameter of 151 to 600 nm, preferably 200 to 500 nm, more preferably 300 to 450 nm, still more preferably 350 to 430 nm. Within this 20 range, in addition to excellent impact strength, tensile strength, flexural strength, and hardness, a finally prepared
13

thermoplastic resin composition may have excellent processability.
[51]
[52] For example, based on a total weight of the base 5 resin, the graft copolymer (A-2) may be included in an amount of 20 to 80 % by weight, preferably 30 to 75 % by weight, more preferably 40 to 70 % by weight. Within this range, balance between mechanical strength and extensional viscosity may be excellent.
10 [53]
[54] For example, the graft copolymer (A-2) may include 40 to 60 % by weight of acrylate rubber, 25 to 45 % by weight of an aromatic vinyl compound, and 5 to 25 % by weight of a vinyl cyanide compound. Within this range, impact strength,
15 tensile strength, flexural strength, and extensional viscosity may be excellent.
[55] As a preferred example, the graft copolymer (A-2) may include 45 to 55 % by weight of acrylate rubber, 30 to 40 % by weight of an aromatic vinyl compound, and 10 to 20 % by
20 weight of a vinyl cyanide compound. Within this range, impact strength, tensile strength, flexural strength, and
14

extensional viscosity may be excellent.
[56]
[57] For example, the graft copolymer (A-2) may be prepared by emulsion polymerization. In this case, mechanical 5 strength such as tensile strength, impact strength, and flexural strength may be excellent.
[58] Emulsion graft polymerization methods commonly practiced in the art to which the present invention pertains may be used as the emulsion polymerization method of the 10 present invention without particular limitation.
[59]
[60] The amount of the graft copolymer (A-1) is preferably less than that of the graft copolymer (A-2). More preferably, the weight ratio of the graft copolymer (A-1) to the graft
15 copolymer (A-2) is 1:3 to 1:5, still more preferably 1:3.3 to 1:4.7. Within this range, balance between mechanical properties and extensional viscosity may be excellent. [61] In this specification, the weight ratio of A to B refers to the weight ratio of A:B.
20 [62]
[63] The types of the acrylate, the aromatic vinyl
15

compound, and the vinyl cyanide compound included in the graft copolymer (A-2) may be the same as the types of the acrylate, the aromatic vinyl compound, and the vinyl cyanide compound included in the graft copolymer (A-1). 5 [64]
[65] B) α-methylstyrene-based copolymer
[66] For example, based on a total weight of the base resin, the α-methylstyrene-based copolymer (B) may be included in an amount of 10 to 45 % by weight, preferably 15
10 to 40 % by weight, more preferably 20 to 35 % by weight. Within this range, since the thermoplastic resin composition of the present invention has excellent heat resistance and processability while having excellent mechanical properties such as impact strength, tensile strength, flexural strength,
15 and hardness, the thermoplastic resin composition may replace a PVC resin using an existing extruder.
[67]
[68] The α-methylstyrene-based polymer (B) may be a heat-resistant copolymer. In this case, a finally prepared 20 thermoplastic resin composition may have heat resistance while maintaining mechanical properties.
16

[69] Polymers commonly referred to as heat-resistant resins in the art to which the present invention pertains may be used as the heat-resistant copolymer of the present invention without particular limitation. Specifically, the 5 heat-resistant copolymer may refer to a monomer having a higher glass transition temperature (based on polymer) than a styrene monomer, that is, a polymer including a heat-resistant monomer.
[70]
10 [71] For example, the α-methylstyrene-based copolymer (B) may be a copolymer of an α-methylstyrene-based monomer and a vinyl cyanide compound or a copolymer of an α-methylstyrene-based monomer, a vinyl cyanide compound, and an aromatic vinyl compound excluding α-methylstyrene, preferably a
15 copolymer of α-methylstyrene, acrylonitrile, and styrene.
[72] Specifically, the α-methylstyrene-based copolymer (B) may be a copolymer including 50 to 80 % by weight of an α-methylstyrene-based monomer; 20 to 50 % by weight of a vinyl cyanide compound; and 0 to 10 % by weight or greater than 0 %
20 by weight and less than or equal to 10 % by weight of an aromatic vinyl compound excluding α-methylstyrene. In this
17

case, heat resistance may be excellent while maintaining impact strength, and thus decomposition by outdoor radiant heat may be prevented, thereby obtaining a deformation prevention effect. 5 [73] The α-methylstyrene-based copolymer (B) is preferably a copolymer including 50 to 80 % by weight of α-methylstyrene; 20 to 50 % by weight of acrylonitrile; and 0 to 10 % by weight or greater than 0 % by weight and less than or equal to 10 % by weight of styrene. In this case, heat resistance 10 may be excellent while maintaining impact strength, and thus decomposition by outdoor radiant heat may be prevented, thereby obtaining a deformation prevention effect.
[74]
[75] For example, the α-methyl styrene-based monomer may
15 include one or more selected from the group consisting of α-methyl styrene and derivatives thereof. In this case, heat resistance may be excellent. For example, the derivatives of α-methyl styrene may be compounds in which one or more hydrogens of α-methyl styrene are substituted with a
20 substituent such as an akyl group having 1 to 10 carbon atoms and a halogen group, preferably compounds in which one or
18

more hydrogens in the aromatic ring of α-methyl styrene are substituted with a substituent such as an alkyl group having 1 to 10 carbon atoms and a halogen group.
[76] 5 [77] For example, the α-methylstyrene-based copolymer (B) preferably has a weight average molecular weight of 60,000 to 180,000 g/mol, more preferably 80,000 to 120,000 g/mol. Within this range, heat resistance may be excellent while impact strength is maintained.
10 [78] In this specification, weight average molecular weight may be measured using tetrahydrofuran (THF) as an eluate through gel permeation chromatography (GPC, Waters Breeze). In this case, weight average molecular weight is obtained as a relative value to a polystyrene standard (PS)
15 specimen. Specific measurement conditions are as follows: solvent: THF, column temperature: 40 °C, flow rate: 0.3 ml/min, sample concentration: 20 mg/ml, injection amount: 5 µl, column model: 1×PLgel 10 µm MiniMix-B (250×4.6 mm) + 1×PLgel 10 µm MiniMix-B (250×4.6 mm) + 1×PLgel 10 µm MiniMix-
20 B Guard (50×4.6 mm), equipment name: Agilent 1200 series system, Refractive index detector: Agilent G1362 RID, RI
19

temperature: 35 °C, data processing: Agilent ChemStation S/W, and test method (Mn, Mw and PDI): OECD TG 118.
[79]
[80] The α-methylstyrene-based copolymer (B) preferably 5 has a glass transition temperature of 110 to 150 °C, more preferably 110 to 140 °C. Within this range, heat resistance may be excellent.
[81] In this specification, glass transition temperature may be measured at a temperature rise rate of 10 °C/minutes 10 using a Differential Scanning Calorimeter (DSC) (Q100, TA Instruments Co.) according to ASTM D 3418.
[82]
[83] For example, the α-methylstyrene-based copolymer (B) may be prepared by solution polymerization or bulk 15 polymerization. In this case, heat resistance and impact strength may be excellent.
[84] Solution polymerization and bulk polymerization methods commonly practiced in the art to which the present invention pertains may be used in the present invention 20 without particular limitation.
[85]
20

[86] C) Ultra-high molecular weight copolymer having
weight average molecular weight of 1,000,000 to 12,000,000 g/mol
[87] For example, based on 100 parts by weight of the base 5 resin, the ultra-high molecular weight copolymer (C) may be included in an amount of 0.5 to 10 parts by weight, preferably 1 to 7 parts by weight, more preferably 1.5 to 5 parts by weight. Within this range, since the thermoplastic resin composition of the present invention has excellent heat
10 resistance and processability while having excellent mechanical properties such as impact strength, tensile strength, flexural strength, and hardness, the thermoplastic resin composition may replace a PVC resin using an existing extruder.
15 [88]
[89] In this specification, ultra-high molecular weight may be defined as a weight average molecular weight of 1,000,000 to 12,000,000 g/mol. Accordingly, an ultra-high molecular weight copolymer having a weight average molecular
20 weight of 1,000,000 to 12,000,000 g/mol has the same meaning as a copolymer having a weight average molecular weight of
21

1,000,000 to 12,000,000 g/mol.
[90]
[91] For example, the ultra-high molecular weight copolymer (C) may be an acrylic-based copolymer (C-1), an 5 aromatic vinyl compound-vinyl cyanide compound copolymer (C-2), or a mixture thereof. In this case, mechanical properties such as impact strength, tensile strength, and flexural strength may be maintained, and flowability may be reduced, thereby improving processability.
10 [92]
[93] For example, the acrylic-based copolymer (C-1) may include an alkyl acrylate-based crosslinked product (i) including a crosslinking agent and 5 to 20 % by weight of an alkyl acrylate monomer; 55 to 90 % by weight of a methyl
15 methacrylate monomer (ii); and 5 to 40 % by weight of one or more (iii) selected from the group consisting of an alkyl acrylate monomer and an alkyl methacrylate monomer. In this case, mechanical properties such as impact strength, tensile strength, and flexural strength may be maintained, and
20 flowability may be reduced, thereby improving processability. [94] The acrylic-based copolymer (C-1) preferably includes
22

an alkyl acrylate-based crosslinked product (i) including a crosslinking agent and 10 to 17 % by weight of an alkyl acrylate monomer; 60 to 80 % by weight of a methyl methacrylate monomer (ii); and 10 to 30 % by weight of one or 5 more (iii) selected from the group consisting of an alkyl acrylate monomer and an alkyl methacrylate monomer. In this case, mechanical properties such as impact strength, tensile strength, and flexural strength may be maintained, and flowability may be reduced, thereby improving processability.
10 [95] For example, the crosslinking agent may include one or more selected from the group consisting of aryl methacrylate, trimethylolpropane, triacrylate, and divinylbenzene. [96] For example, based on 100 parts by weight in total of
15 the monomers used to polymerize the acrylic-based copolymer (C-1), the crosslinking agent may be included in an amount of 0.01 to 0.3 parts by weight. Within this range, extensional viscosity may be improved, and processability may be excellent.
20 [97] For example, the alkyl acrylate-based crosslinked product may have a swelling index of 3 to 10, preferably 4 to
23

9. Within this range, extensional viscosity may be improved, and processability may be excellent.
[98] In this description, to calculate swelling index, acetone is added to 1 g of alkyl acrylate-based crosslinked 5 product powder, stirring is performed at room temperature for 24 hours, centrifugation is performed to obtain a fraction not dissolved in acetone, and then the fraction is dried. Then, the weights of the fraction before and after drying are measured, and swelling index is calculated by substituting 10 the weight values into the following equation.
[99] * Swelling index = Weight before drying after centrifugation/weight after drying after centrifugation
[100]
[101] For example, the alkyl acrylate monomer may have a 15 linear, branched, or cyclic alkyl group having 1 to 18 carbon
atoms, and preferably includes one or more selected from the
group consisting of methyl acrylate, ethyl acrylate, n-butyl
acrylate, lauryl acrylate, stearyl acrylate, 2-ethylhexyl
acrylate, and cyclohexyl acrylate. 20 [102] For example, the alkyl methacrylate monomer may have
a linear or cyclic alkyl group having 2 to 18 carbon atoms,
24

and preferably includes one or more selected from the group consisting of n-butyl methacrylate, lauryl methacrylate, stearyl methacrylate, tridecyl methacrylate i-butyl methacrylate, t-butyl methacrylate, 2-ethylhexylmethacrylate, 5 and cyclohexyl methacrylate.
[103]
[104] For example, the acrylic-based copolymer (C-1) may have a weight average molecular weight of 1,000,000 to 12,000,000 g/mol, preferably 1,000,000 to 9,000,000 g/mol, 10 more preferably 1,000,000 to 6,000,000 g/mol. Within this range, mechanical properties may be excellent, and flowability may be improved.
[105]
[106] For example, the acrylic-based copolymer (C-1) may be 15 prepared by emulsion polymerization, suspension
polymerization, or solution polymerization, preferably
emulsion polymerization. In this case, processability and
impact strength may be excellent.
[107] Emulsion polymerization, suspension polymerization, 20 and solution polymerization commonly practiced in the art to
which the present invention pertains may be used in the
25

present invention without particular limitation.
[108]
[109] A method of preparing the acrylic-based copolymer (C-1) preferably includes a step (i) of preparing an alkyl 5 acrylate-based crosslinked product having a swelling index of 3 to 10 using a crosslinking agent and 5 to 20 % by weight of an alkyl acrylate-based monomer; a step (ii) of preparing a polymer by emulsion-polymerizing 27.5 to 45 % by weight of a methyl methacrylate monomer, 2.5 to 20 % by weight of one or
10 more selected from the group consisting of an alkyl acrylate monomer having an alkyl group having 1 to 18 carbon atoms and an alkyl methacrylate monomer having an alkyl group having 2 to 18 carbon atoms, an emulsifier, a crosslinking agent, a polymerization initiator, and a redox catalyst before or
15 after the step (i) of preparing the alkyl acrylate-based crosslinked product; and a step of terminating emulsion polymerization by adding 27.5 to 45 % by weight of a methyl methacrylate monomer, 2.5 to 20 % by weight of one or more selected from the group consisting of an alkyl acrylate
20 monomer having an alkyl group having 1 to 18 carbon atoms and an alkyl methacrylate monomer having an alkyl group having 2
26

to 18 carbon atoms, an emulsifier, a crosslinking agent, a polymerization initiator, and a redox catalyst to the alkyl acrylate-based crosslinked product prepared in the step (i) and the polymer prepared in the step (ii). In this case, 5 mechanical properties such as impact strength, tensile strength, and flexural strength may be maintained, and flowability may be reduced, thereby improving processability. [110] For example, the step (i) and the step (ii) may be performed in a separate place or reactor.
10 [111]
[112] Based on 100 parts by weight in total of the monomers used to polymerize the acrylic-based copolymer (C-1), the emulsifier may be included in an amount of 0.5 to 5 parts by weight.
15 [113] The types of the emulsifier are not particularly limited. However, the emulsifier may include one or more selected from the group consisting of anionic emulsifiers including aliphatic esters, alkyl benzene sulfonates, alkyl phosphate salts, and dialkyl sulfosuccinates and nonionic
20 emulsifiers including polyoxyethylene alkyl ethers and alkylamine esters.
27

[114] For example, based on 100 parts by weight in total of the monomers used to polymerize the acrylic-based copolymer (C-1), the crosslinking agent may be included in an amount of 0.01 to 0.3 parts by weight. 5 [115] For example, the crosslinking agent may include one or more selected from the group consisting of aryl methacrylate, trimethylolpropane triacrylate, and divinylbenzene, preferably an acrylate-based compound. [116] For example, based on 100 parts by weight in total of 10 the monomers used to polymerize the acrylic-based copolymer (C-1), the polymerization initiator may be included in an amount of 0.0005 to 0.005 parts by weight.
[117] For example, the polymerization initiator may include one or more selected from the group consisting of a water-15 soluble initiator, a fat-soluble initiator, and a redox initiator.
[118] The water-soluble initiator preferably includes one or more selected from the group consisting of potassium persulfate, ammonium persulfate, and sodium persulfate. 20 [119] The fat-soluble initiator preferably includes one or more selected from the group consisting of t-butyl
28

hydroperoxide, cumene hydroperoxide, benzoylperoxide, and lauroyl peroxide.
[120] For example, based on 100 parts by weight in total of the monomers used to polymerize the acrylic-based copolymer 5 (C-1), the redox catalyst may be included in an amount of 0.01 to 0.1 parts by weight.
[121] For example, the redox catalyst may include one or
more selected from the group consisting of sodium
formaldehyde sulfoxylate, disodium
10 ethylenediaminetetraacetate, ferrous sulfate, ethylene sodium diamine tetraacetate, and copper(II) sulfate.
[122] For example, the acrylic-based copolymer copolymer in a latex form prepared by emulsion polymerization may be prepared as an acrylic-based copolymer in a powder form
15 through aggregation, dehydration, and drying steps.
[123]
[124] For example, the aromatic vinyl compound-vinyl cyanide compound copolymer (C-2) may include 60 to 80 % by weight of an aromatic vinyl compound and 20 to 40 % by weight 20 of a vinyl cyanide compound, preferably 65 to 75 % by weight of an aromatic vinyl compound and 25 to 35 % by weight of a
29

vinyl cyanide compound. Within this range, mechanical properties such as impact strength, tensile strength, and flexural strength may be maintained, and flowability may be reduced, thereby improving processability. 5 [125] For example, the aromatic vinyl compound-vinyl cyanide compound copolymer (C-2) may have a weight average molecular weight of 1,000,000 to 12,000,000 g/mol, preferably 1,000,000 to 10,000,000 g/mol, more preferably 1,000,000 to 7,000,000 g/mol, still more preferably 1,000,000 to 6,000,000
10 g/mol, most preferably 1,000,000 to 6,000,000 g/mol. Within this range, processability may be excellent.
[126] The aromatic vinyl compound-vinyl cyanide compound copolymer (C-2) is preferably a styrene-acrylonitrile copolymer. In this case, processability may be excellent.
15 [127] For example, the aromatic vinyl compound-vinyl cyanide compound copolymer (C-2) may be prepared by emulsion polymerization, bulk polymerization, or suspension polymerization, preferably emulsion polymerization. In this case, heat resistance and fluidity may be excellent.
20 [128] When the aromatic vinyl compound and the vinyl cyanide compound are emulsion-polymerized, components, such
30

as an emulsifier, a polymerization initiator, a molecular weight regulator, and deionized water, commonly used in emulsion polymerization, may be added. In addition, emulsion polymerization methods commonly practiced in the art to which 5 the present invention pertains may be used in the present invention without particular limitation.
[129]
[130] The types of the aromatic vinyl compound and the vinyl cyanide compound included in the aromatic vinyl 10 compound-vinyl cyanide compound copolymer (C-2) may be the same as the types of the aromatic vinyl compound and the vinyl cyanide compound included in the graft copolymer (A-1).
[131]
[132] Additives
15 [133] For example, the thermoplastic resin composition may further include one or more selected from the group consisting of an antioxidant, a UV stabilizer, a fluorescent brightening agent, a chain extender, a release agent, a pigment, a dye, an antibacterial agent, a processing aid, a
20 metal deactivator, a smoke suppressant, an inorganic filler, glass fiber, an anti-friction agent, and an anti-wear agent.
31

For example, based on 100 parts by weight of the base resin, each of the additives may be included in an amount of 0.01 to 5 parts by weight, preferably 0.05 to 3 parts by weight, more preferably 0.1 to 2 parts by weight. In this case, the 5 required physical properties of the thermoplastic resin composition of the present invention may be implemented without deterioration in the intrinsic physical properties thereof.
[134]
10 [135] Thermoplastic resin composition
[136] The thermoplastic resin composition preferably has a total rubber content of 25 to 43 % by weight, more preferably 27 to 40 % by weight, still more preferably 30 to 35 % by weight. Within this range, mechanical properties and
15 processability may be excellent.
[137] In the present invention, rubber content is measured using FT-IR.
[138]
[139] For example, when an extensional viscosity fixture
20 (EVF) attached to an ARES rheometer of TA Instruments (New
Castle, Delaware, USA) is used to preheat a specimen having a
32

size of 180×10×7 mm at 190 °C for 30 seconds and measure extensional viscosity after 1 second, the thermoplastic resin composition may have an extensional viscosity of 530,000 to 760,000 Pa•S, preferably 540,000 to 750,000 Pa•S, more 5 preferably 550,000 to 740,000 Pa•S, still more preferably 570,000 to 730,000 Pa•S, most preferably 600,000 to 720,000 Pa•S. Within this range, processability and physical property balance may be excellent, and extruding may be performed using existing PVC equipment.
10 [140] In this specification, extensional viscosity refers to the resistance of fluid when the fluid is deformed by extensional stress. As extensional viscosity increases, the flowability of a molten resin decreases, thereby improving extrusion processability.
15 [141]
[142] For example, the thermoplastic resin composition may have an impact strength (23 °C, 1/4") of 23 kgf•cm/cm or more, preferably 25 kgf•cm/cm or more, more preferably 25 to 42 kgf•cm/cm, still more preferably 27 to 42 kgf•cm/cm as
20 measured according to ASTM D256. Within this range, the balance of all physical properties may be excellent.
33

[143]
[144] For example, the thermoplastic resin composition may
have a tensile strength of 230 kgf/cm2 or more, preferably 250
kgf/cm2 or more, more preferably 250 to 400 kgf/cm2, still
5 more preferably 270 to 380 kgf/cm2, most preferably 300 to 370
kgf/cm2 as measured according to ASTM D638. Within this range, the balance of all physical properties may be excellent. [145] For example, the thermoplastic resin composition may have a flexural strength of 330 kgf/cm2 or more, preferably 10 350 kgf/cm2 or more, more preferably 350 to 700 kgf/cm2, still more preferably 400 to 680 kgf/cm2, most preferably 430 to 650 kgf/cm2 as measured according to ASTM D790. Within this range, the balance of all physical properties may be excellent.
[146]
15 [147] For example, the thermoplastic resin composition may have a hardness of 38 or more, preferably 40 or more, more preferably 40 to 85, still more preferably 45 to 80, most preferably 50 to 75 as measured according to ASTM D785. Within this range, the balance of all physical properties may
20 be excellent.
[148]
34

[149] For example, the thermoplastic resin composition may have a heat resistance of 67 °C or higher, preferably 70 °C or higher, more preferably 70 to 85 °C, still more preferably 75 to 82 °C as measured according to ASTM D648. In this case, 5 the balance of all physical properties may be excellent.
[150]
[151] For example, when a 3T sheet is prepared from the thermoplastic resin composition under the conditions of 200 °C and a molding pressure of 100 kgf/cm2 using a T-die 10 extruder, and then the surface of the sheet is observed with the naked eye, the surface of the sheet is uniform, no shrinkage is observed in the surface of the sheet, and the appearance of the sheet is kept constant.
[152]
15 [153] Method of preparing thermoplastic resin composition
[154] A method of preparing a thermoplastic resin composition according to the present invention includes a step of mixing 100 parts by weight of a base resin including 0.5 to 45 % by weight of a graft copolymer (A-1) including
20 acrylate rubber having an average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide
35

compound, 20 to 80 % by weight of a graft copolymer (A-2) including acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 % by weight of an α-5 methylstyrene-based copolymer (B) having a weight average molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10 parts by weight of an ultra-high molecular weight copolymer (C) having a weight average molecular weight of 1,000,000 to 12,000,000 g/mol, and then preparing pellets using an
10 extrusion kneader with a size of 10 to 100 pi at 200 to 300 °C.
[155] In this case, mechanical properties such as impact strength, tensile strength, flexural strength, and hardness may be excellent. In addition, due to excellent heat
15 resistance and processability, an existing extruder may be used to replace a PVC resin with the thermoplastic resin composition of the present invention.
[156]
[157] The method of preparing the thermoplastic resin
20 composition shares all the technical characteristics of the
above-described thermoplastic resin composition. Accordingly,
36

repeated description thereof will be omitted.
[158]
[159] In the step of preparing pellets using the extrusion kneader, preferably, the extrusion kneader having a size of 5 25 to 75 pi at 200 to 300 °C. More preferably, the extrusion kneader having a size of 30 to 75 pi at 210 to 260 °C. Within this range, stable extrusion is possible and kneading effect may be excellent. At this time, the temperature is temperature set in a cylinder, and pi means outer diameter
10 (unit: mm).
[160] Extrusion kneaders commonly used in the art to which the present invention pertains may be used without particular limitation, and a twin-screw extrusion kneader is preferably used.
15 [161]
[162] Molded article
[163] For example, a molded article of the present invention includes the thermoplastic resin composition of the present invention. In this case, mechanical properties such
20 as impact strength, tensile strength, flexural strength, and hardness may be excellent. In addition, due to excellent heat
37

resistance and processability, an existing extruder may be used to replace a PVC resin with the thermoplastic resin composition of the present invention.
[164] 5 [165] The molded article is preferably an exterior material for construction, specifically, a window frame, a door, a roof, or a fence. In this case, the molded article including the thermoplastic resin composition of the present invention may have quality superior to quality required by the market.
10 [166]
[167] A method of manufacturing the molded article includes a step of mixing 100 parts by weight of a base resin including 0.5 to 45 % by weight of a graft copolymer (A-1) including acrylate rubber having an average particle diameter
15 of 50 to 150 nm, an aromatic vinyl compound, and a vinyl
cyanide compound, 20 to 80 % by weight of a graft copolymer
(A-2) including acrylate rubber having an average particle
diameter of 151 to 600 nm, an aromatic vinyl compound, and a
vinyl cyanide compound, and 10 to 45 % by weight of an α-
20 methylstyrene-based copolymer (B) having a weight average molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10
38

parts by weight of an ultra-high molecular weight copolymer (C) having a weight average molecular weight of 1,000,000 to 12,000,000 g/mol, and then performing kneading and extrusion at 200 to 300 °C to prepare pellets; and a step of sheet-5 molding or injection-molding the prepared pellets at a molding temperature of 180 to 300 °C to manufacture a molded article. In this case, a thermoplastic resin product having excellent processability may be prepared.
[168]
10 [169] As a preferred example, the step of manufacturing a molded article may include a step of sheet-molding the prepared pellets at a molding temperature of 180 to 300 °C. As a more preferred example, the step of manufacturing a molded article may include a step of sheet-molding the
15 prepared pellets under the conditions of a molding temperature of 180 to 300 °C and a molding pressure of 50 to 300 kgf/cm2. In this case, a sheet-molded article having excellent processability and a uniform surface may be easily manufactured.
20 [170] The molding temperature is preferably 190 to 230 °C, more preferably 200 to 220 °C. Within this range, a sheet-39

molded article having excellent processability and a uniform surface may be easily manufactured.
[171] The molding pressure is preferably 50 to 200 kgf/cm2, more preferably 80 to 150 kgf/cm2. Within this range, a 5 sheet-molded article having high impact strength may be easily manufactured.
[172]
[173] As another preferred example, the step of
manufacturing a molded article may include a step of
10 injection-molding the prepared pellets under the conditions of an injection temperature of 200 to 260 °C, an injection pressure of 60 to 100 bar, and a holding pressure of 25 to 55 bar. In this case, an injection-molded article having excellent mechanical properties such as impact strength may
15 be easily manufactured.
[174] The injection temperature is preferably 200 to 230 °C, more preferably 210 to 220 °C. Within this range, an injection-molded article having excellent mechanical properties such as impact strength may be easily manufactured.
20 [175] The injection pressure is preferably 70 to 90 bar, more preferably 75 to 85 bar. Within this range, an
40

injection-molded article having excellent mechanical properties such as impact strength may be easily manufactured. [176] The holding pressure is preferably 30 to 50 bar, more preferably 35 to 50 bar. Within this range, an injection-5 molded article having excellent mechanical properties such as impact strength may be easily manufactured.
[177]
[178] In describing the thermoplastic resin composition of the present invention, the method of preparing the same, and 10 the molded article including the same, it should be noted that other conditions or equipment not explicitly described herein may be appropriately selected within the range commonly practiced in the art without particular limitation.
[179]
15 [180] Hereinafter, the present invention will be described in more detail with reference to the following preferred examples. However, these examples are provided for illustrative purposes only and should not be construed as limiting the scope and spirit of the present invention. In
20 addition, it will be apparent to those skilled in the art that various changes and modifications may be made without
41

departing from the spirit and scope of the present invention, and such changes and modifications are also within the scope of the appended claims.
[181] 5 [182] [Examples]
[183] Materials used in Examples and Comparative Examples below are as follows.
[184] * A-1) Graft copolymer: Butylacrylate-styrene-acrylonitrile copolymer (butylacrylate: 50 % by weight, 10 styrene: 35 % by weight, and acrylonitrile: 15 % by weight) containing acrylate rubber having an average particle diameter of 120 nm
[185] * A-2) Graft copolymer: Butylacrylate-styrene-acrylonitrile copolymer (butylacrylate: 50 % by weight, 15 styrene: 35 % by weight, and acrylonitrile: 15 % by weight) containing acrylate rubber having an average particle diameter of 400 nm
[186] * B) α-methylstyrene-based polymer: Heat-resistant SAN resin (α-methylstyrene: 65 % by weight, acrylonitrile: 20 30 % by weight, and styrene: 5 % by weight, weight average molecular weight: 90,000 g/mol)
42

[187] * C-1) Ultra-high molecular weight acrylic-based copolymer: Acrylic copolymer (butylacrylate: 15 % by weight and methylmethacrylate: 85 % by weight) having a weight average molecular weight of 1,000,000 g/mol 5 [188] * C-2) Ultra-high molecular weight SAN copolymer: Styrene-acrylonitrile copolymer (ZB-869, Zibo Huaxing Additives Co.) having a weight average molecular weight of 5,000,000 g/mol
[189]
10 [190] Examples 1 to 11 and Comparative Examples 1 to 9
[191] According to the contents shown in Tables 1 and 2, the components shown in Tables 1 and 2 were introduced into a twin-screw extruder, and kneading and extrusion were performed at a cylinder temperature of 230 °C to prepare
15 pellets. Using the prepared pellets, a 3T sheet was prepared under the conditions of a molding temperature of 200 °C and a molding pressure of 100 kgf/cm2 using a T-die extruder, and then moldability was evaluated. In addition, the prepared pellets were injected at a barrel temperature of 220 °C using
20 an injection machine to prepare a specimen for measuring physical properties, and the impact strength, tensile
43

strength, flexural strength, hardness, heat resistance, and extensional viscosity of the specimen were measured.
[192]
[193] [Test Example] 5 [194] The properties of the specimens prepared in Examples 1 to 11 and Comparative Examples 1 to 9 were measured according to the following methods, and the results are shown in Tables 1 and 2 below.
[195] 10 [196] Measurement methods
[197] * Rubber content (% by weight): Rubber content of
thermoplastic resin composition pellets was measured using
Agilent Cary 660 FT-IR (Agilent Co.).
[198] * Impact strength (kgf•cm/cm): Impact strength was 15 measured under the conditions of a thickness of 1/4" and a
temperature of 23 °C according to ASTM D256.
[199] * Tensile strength (kgf/cm2): Tensile strength was
measured according to ASTM D638.
[200] * Flexural strength (kgf/cm2): Flexural strength was 20 measured according to ASTM D790.
[201] * Hardness: Hardness was measured according to ASTM
44

D785.
[202] * Heat resistance (°C): Heat resistance was measured
under a load of 18.6 kgf according to ASTM D648.
[203] * Extensional viscosity (Pa•S): An extensional 5 viscosity fixture (EVF) attached to an ARES rheometer of TA
Instruments was used to preheat a specimen having a size of
180×10×7 mm at 190 °C for 30 seconds and measure extensional
viscosity after 1 second.
[204] * Sheet moldability: A 3T sheet was prepared under 10 the conditions of a molding temperature of 200 °C and a
molding pressure of 100 kgf/cm2 using a T-die extruder, and
then the surface uniformity and appearance (whether shrinkage
or deformation has occurred) of the sheet were evaluated by
visual observation as follows: 15 [205] ○: Excellent surface uniformity and appearance
[206] A: Excellent surface uniformity or appearance
[207] X: Poor both in surface uniformity and appearance
[208]
[209] [Table 1] ^
Clas sifi cati on Exam
ple
1 Exam
ple
2 Exam
ple
3 Exam
ple
4 Exam
ple
5 Exam
ple
6 Exam
ple
7 Exam
ple
8 Exam
ple
9 Exam
ple
10 Exam
ple
11
A-1) 15 1 35 15 15 15 15 12 15 15 15
A-2) 50 65 30 70 50 50 50 48 50 50 50
45

B) 35 34 35 15 35 35 35 37 35 35 35
C-1) 3 3 3 3 1 5 7 3
C-2) 1 3 7
Rubb er cont ent 32.5 32.5 32.5 8 42.5 32.5 32.5 32.5 30 32.5 32.5 32.5
Impa ct stre ngth 30 35 25 40 30 30 30 28 30 30 30
Tens ile stre ngth 300 280 350 250 300 300 300 360 300 300 300
Flex ural stre ngth 450 420 500 350 450 450 450 620 450 450 450
Hard ness 65 60 65 40 65 65 65 70 65 65 65
Heat resi stan ce 78 80 78 70 78 78 78 80 78 78 78
Exte
nsio
nal
visc
osit
y 670, 000 620, 000 550, 000 660, 000 630, 000 680, 000 700, 000 640, 000 640, 000 680, 000 720, 000
Shee
t
mold
abil
ity o ▲ ▲ ▲ ▲ o o o o o o
[210] [Table 2]

Clas sifi cati on Compa rativ
e
Examp
le 1 Compa rativ
e
Examp
le 2 Compa rativ
e
Examp
le 3 Compa rativ
e
Examp
le 4 Compa rativ
e
Examp
le 5 Compa rativ
e
Examp
le 6 Compa rativ
e
Examp
le 7 Compa rativ
e
Examp
le 8 Compa rativ
e
Examp
le 9
A-1) 15 15 15 25 35 0 50 15 15
A-2) 50 50 20 65 57 75 15 50 50
B) 35 35 65 10 8 25 35 35 35
C-1) 0.1 15 3 1 3 3 3
C-2) 0.1 15
Rubb er cont ent 32.5 32.5 17.5 45 46 37.5 32.5 32.5 32.5
Impa
ct
stre 33 40 15 60 62 35 20 33 40
46

ngth
Tens ile stre ngth 300 300 470 180 170 220 380 300 300
Flex ural stre ngth 460 400 800 300 290 350 500 450 450
Hard ness 62 65 100 55 55 35 65 62 63
Heat resi stan ce 78 78 92 60 62 65 80 78 78
Exte
nsio
nal
visc
osit
y 350,0 00 770,0 00 292,0 00 100,0 00 130,0 00 500,0 00 400,0 00 380,0 00 800,0 00
Shee
t
mold
abil
ity X X X X X ▲ ▲ X X
[211] In Tables 1 and 2, the content of each of A-1), A-2),
and B) is given in % by weight based on the total weight thereof. The content of C) is given in parts by weight based on 100 parts by weight in total of A-1), A-2), and B. 5 [212] As shown in Tables 1 and 2, compared to Comparative Examples 1 to 9, in the case of Examples 1 to 11 according to the present invention, impact strength, tensile strength, flexural strength, and hardness are maintained, heat resistance and extensional viscosity are excellent, and sheet 10 moldability is improved, allowing extrusion using existing PVC equipment. In particular, in the case of Examples 1 and 6
47

to 11, in addition to extensional viscosity, mechanical strength, and heat resistance, sheet moldability is excellent. [213] Specifically, in the case of Comparative Example 1 including the ultra-high molecular weight acrylic-based 5 copolymer (C-1) in an amount less than the range of the present invention, extensional viscosity is low, and sheet moldability is poor. In the case of Comparative Example 2 including an excess of the acrylic-based copolymer (C-1), extensional viscosity is greatly increased, resulting in poor
10 sheet moldability.
[214] In addition, in the case of Comparative Example 3 in which an excess of the copolymer (B) is included and the total rubber content of a thermoplastic resin composition is small, impact strength and extensional viscosity are reduced,
15 and sheet moldability is poor. In the case of Comparative Examples 4 and 5 in which a small amount of the copolymer (B) is included and the total rubber content of a thermoplastic resin composition is excessive, heat resistance and extensional viscosity are reduced, and sheet moldability is
20 poor.
[215] In addition, in the case of Comparative Example 6 not
48

including the resin (A-1), heat resistance is reduced. In the case of Comparative Example 7 in which the contents of the resin (A-1) and the resin (A-2) are out of the range of the present invention, extensional viscosity and impact strength 5 are significantly reduced.
[216] In addition, in the case of Comparative Example 8 including the ultra-high molecular weight SAN-based resin (C-2) in an amount less than the range of the present invention, extensional viscosity is greatly reduced, resulting in poor
10 sheet moldability. In the case of Comparative Example 9 including the ultra-high molecular weight SAN-based resin (C-2) in an amount exceeding the range of the present invention, extensional viscosity is greatly increased, resulting in poor sheet moldability.
15 [217] As a result, in the case of the thermoplastic resin composition of the present invention including 100 parts by weight of a base resin including a graft copolymer including acrylate rubber having an average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide
20 compound; a graft copolymer including acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic
49

vinyl compound, and a vinyl cyanide compound; and an α-methylstyrene-based copolymer having a weight average molecular weight of 60,000 to 180,000 g/mol and an ultra-high molecular weight copolymer having a weight average molecular 5 weight of 1,000,000 to 12,000,000 g/mol in a predetermined amount, mechanical properties are maintained, heat resistance and extensional viscosity are excellent, and sheet moldability is improved, enabling replacement of a PVC resin using existing equipment. 10

WE CLAIMS

A thermoplastic resin composition, comprising:
5 100 parts by weight of a base resin comprising 0.5 to
45 % by weight of a graft copolymer (A-1) comprising acrylate rubber having an average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide compound, 20 to 80 % by weight of a graft copolymer (A-2) comprising
10 acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 % by weight of an α-methylstyrene-based copolymer (B) having a weight average molecular weight of 60,000 to 180,000 g/mol; and
15 0.5 to 10 parts by weight of an ultra-high molecular
weight copolymer (C) having a weight average molecular weight of 1,000,000 to 12,000,000 g/mol.
[Claim 2]
20 The thermoplastic resin composition according to claim
1, wherein the graft copolymer (A-1) and the graft copolymer
51

(A-2) independently comprise 40 to 60 % by weight of acrylate rubber, 25 to 45 % by weight of an aromatic vinyl compound, and 5 to 25 % by weight of a vinyl cyanide compound.
5 [Claim 3]
The thermoplastic resin composition according to claim
1, wherein the α-methylstyrene-based polymer (B) comprises 50
to 80 % by weight of an α-methylstyrene-based compound, 20 to
50 % by weight of a vinyl cyanide compound, and 0 to 10 % by
10 weight of an aromatic vinyl compound excluding α¬
me thylstyrene.
[Claim 4]
The thermoplastic resin composition according to claim 15 1, wherein the ultra-high molecular weight copolymer (C) is an acrylic-based copolymer (C-1), an aromatic vinyl compound-vinyl cyanide compound copolymer (C-2), or a mixture thereof.
[Claim 5]
20 The thermoplastic resin composition according to claim
4, wherein the acrylic-based copolymer (C-1) comprises an
52

alkyl acrylate-based crosslinked product (i) comprising a crosslinking agent and 5 to 20 % by weight of an alkyl acrylate monomer; 55 to 90 % by weight of a methyl methacrylate monomer (ii); and 5 to 40 % by weight of one or 5 more (iii) selected from the group consisting of an alkyl acrylate monomer and an alkyl methacrylate monomer.
【Claim 6】
The thermoplastic resin composition according to claim 10 5, wherein the crosslinking agent comprises one or more selected from the group consisting of aryl methacrylate, trimethylolpropane, triacrylate, and divinylbenzene.
【Claim 7】
15 The thermoplastic resin composition according to claim
5, wherein, based on 100 parts by weight in total of the monomers used to polymerize the acrylic-based copolymer (C-1), the crosslinking agent is comprised in an amount of 0.01 to 0.3 parts by weight.
20
【Claim 8】
53

The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition has a total rubber content of 23 to 43 % by weight as measured by FT-IR.
5 【Claim 9】
The thermoplastic resin composition according to claim 1, wherein, when an extensional viscosity fixture (EVF) attached to an ARES rheometer of TA Instruments (New Castle, Delaware, USA) is used to preheat a specimen having a size of 10 180×10×7 mm at 190 °C for 30 seconds and measure extensional viscosity after 1 second, the thermoplastic resin composition has an extensional viscosity of 530,000 to 760,000 Pa•S.
【Claim 10】
15 The thermoplastic resin composition according to claim
1, wherein the thermoplastic resin composition has an impact strength (23 °C, 1/4") of 23 kgf•cm/cm or more as measured according to ASTM D256.
20 【Claim 11】
54

The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition has a tensile strength of 230 kgf/cm2 or more as measured according to ASTM D638. 5
【Claim 12】
The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition has a flexural strength of 330 kgf/cm2 or more as measured according to ASTM 10 D790.
【Claim 13】
The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition has a heat 15 resistance of 67 °C higher as measured under a load of 18.6 kgf according to ASTM D648.
【Claim 14】
A method of preparing a thermoplastic resin 20 composition, comprising:
55

mixing 100 parts by weight of a base resin comprising 0.5 to 45 % by weight of a graft copolymer (A-1) comprising acrylate rubber having an average particle diameter of 50 to 150 nm, an aromatic vinyl compound, and a vinyl cyanide 5 compound, 20 to 80 % by weight of a graft copolymer (A-2) comprising acrylate rubber having an average particle diameter of 151 to 600 nm, an aromatic vinyl compound, and a vinyl cyanide compound, and 10 to 45 % by weight of an α-methylstyrene-based copolymer (B) having a weight average
10 molecular weight of 60,000 to 180,000 g/mol; and 0.5 to 10
parts by weight of an ultra-high molecular weight copolymer
(C) having a weight average molecular weight of 1,000,000 to
12,000,000 g/mol, and then preparing pellets using an
extrusion kneader with a size of 10 to 100 pi at 200 to
15 300 °C.
[Claim 15]
A molded article, comprising the thermoplastic resin composition according to any one of claims 1 to 13.