Claims:1. A low density cleansing composition comprising:
a. soap noodles;
b. at least one carbonate;
c. at least one protic acid having Pka<5; and
d. at least one polymer,
wherein soap noodles weight concentration in said composition is in the range of 89-92%, at least one carbonate weight concentration in said composition is in the range of 0.8-1.2%, at least one protic acid weight concentration in said composition is in the range of 0.5-0.9%, and at least one polymer weight concentration in said composition is in the range of 0.01-0.02%.
2. The composition as claimed in claim 1, wherein
a. said soap noodles weight concentration in said composition is 90.1%;
b. said at least one carbonate weight concentration in said composition is 0.95%;
c. said at least one protic acid weight concentration in said composition is 0.7%; and
d. said at least one polymer weight concentration in said composition is 0.015%.
3. The composition as claimed in any of the claims 1-2, wherein
a. said at least one carbonate is selected from the group consisting of sodium carbonate (soda ash light), sodium bicarbonate, and combinations thereof;
b. said at least one protic acid is selected from the group consisting of citric acid, lactic acid, and combinations thereof;
c. said at least one polymer is selected from the group consisting of high molecular weight polyethylene oxide, acrylic based homopolymer, and combinations thereof.

4. The composition as claimed in any of the claims 1-3, said composition further comprising:
a. titanium dioxide having weight concentration in the range of 0.01-1%;
b. talc having weight concentration in the range of 5-7%;
c. water having weight concentration in the range of 0.5-2%; and
d. fragrance having weight concentration in the range of 0.5-2%.
5. The composition as claimed in claim 4, said composition comprising :
a. titanium dioxide having weight concentration in the range of 0.01-1%;
b. talc having weight concentration in the range of 5-7%;
c. water having weight concentration in the range of 0.5-2%;
d. fragrance having weight concentration in the range of 0.5-2%;
e. soap noodles having weight concentration in the range of 89-92%;
f. soda ash light having weight concentration in the range of 0.8-1.2%;
g. citric acid having weight concentration in the range of 0.5-0.9%; and
h. polyethylene oxide having weight concentration in the range of 0.01-0.02%.
6. The composition as claimed in claim 5, said composition comprising:
a. soap noodles having weight concentration of 90.1%;
b. titanium dioxide having weight concentration of 0.1%;
c. soda ash light having weight concentration of 0.95%;
d. talc having weight concentration of 6.13%;
e. high molecular weight polyethylene oxide having weight concentration of 0.015%;
f. water having weight concentration of 0.905%;
g. citric acid having a weight concentration of 0.7%; and
h. fragrance having weight concentration of 1.1%.
7. The composition as claimed in any of the claims 1-6, wherein said composition has a density in the range of 1.03-1.05g/ml.
8. The composition as claimed in claim 7, wherein said composition has a density of 1.04g/ml.
9. A method of preparing a low density cleansing composition as claimed in any of the claims 1-3, said method comprising;
a. mixing soap noodles, at least one carbonate, and at least one polymer, in a container at about 24°C-26 oC to obtain a first mixture;
b. transferring the first mixture in to a closed system plodder and adding at least one protic acid to obtain a plodded mixture; and
c. passing the plodded mixture through a cone and extruder maintained at a temperature it the range of 40-50°C to obtain said low density cleansing composition.
10. A method of preparing a low density cleansing composition as claimed in any of the claims 4-7, said method comprising:
a. mixing soap noodles, titanium dioxide, soda ash light, talc, high molecular weight polyethylene oxide, water, and fragrance in a container at about 24°C-26 oC to obtain a first mixture;
b. transferring the first mixture in to a closed system plodder and adding citric acid to obtain a plodded mixture; and
c. passing the plodded mixture through a cone and extruder maintained at a temperature it the range of 40-50°C to obtain said low density cleansing composition.
, Description:As Attached